RU2539070C1 - Coloured glaze - Google Patents
Coloured glaze Download PDFInfo
- Publication number
- RU2539070C1 RU2539070C1 RU2014107318/03A RU2014107318A RU2539070C1 RU 2539070 C1 RU2539070 C1 RU 2539070C1 RU 2014107318/03 A RU2014107318/03 A RU 2014107318/03A RU 2014107318 A RU2014107318 A RU 2014107318A RU 2539070 C1 RU2539070 C1 RU 2539070C1
- Authority
- RU
- Russia
- Prior art keywords
- glaze
- kaolin
- cobalt oxide
- calcium borate
- borax
- Prior art date
Abstract
Description
Изобретение относится к промышленности строительных материалов и касается составов глазурей для нанесения на керамические изделия декоративно-художественного и хозяйственно-бытового назначения.The invention relates to the building materials industry and relates to glaze compositions for application to ceramic products for decorative, artistic and household purposes.
Известна цветная глазурь, содержащая, вес.ч.: свинцовый глет 6; кварцевый песок 3; каолин 1; окись кобальта 1 [1].Known colored glaze containing, parts by weight of: lead litharge 6; silica sand 3; kaolin 1; cobalt oxide 1 [1].
Задача изобретения состоит в повышении водостойкости цветной глазури.The objective of the invention is to increase the water resistance of colored glaze.
Технический результат достигается тем, что цветная глазурь, включающая свинцовый глет, кварцевый песок, каолин и окись кобальта, дополнительно содержит борат кальция и буру при следующем соотношении компонентов, вес.ч.: свинцовый глет 4-4,5; кварцевый песок 4-4,5; каолин 0,5-1; окись кобальта 0,3-0,5; борат кальция 0,5-1; бура 0,5-1.The technical result is achieved in that the colored glaze, including lead litharge, quartz sand, kaolin and cobalt oxide, additionally contains calcium borate and borax in the following ratio of components, parts by weight: lead litharge 4-4.5; silica sand 4-4.5; kaolin 0.5-1; cobalt oxide 0.3-0.5; calcium borate 0.5-1; borax 0.5-1.
Составы цветной глазури приведены в таблице.The compositions of colored glaze are given in the table.
В составе глазури может быть использован, например, каолин Просяновского месторождения, характеризующийся следующим химическим составом, мас.%: SiO2 46,02-46,5; TiO2 0,47-0,52; Al2O3 38,69-40,17; Fe2O3 0,55-0,92; CaO 0,05-0,19; п.п.п. 13,34-13,97. Рекомендуется использовать чистые кварцевые пески, с пониженным содержанием соединений железа.The glaze composition can be used, for example, kaolin of the Prosyanovskoye deposit, characterized by the following chemical composition, wt.%: SiO 2 46.02-46.5; TiO 2 0.47-0.52; Al 2 O 3 38.69-40.17; Fe 2 O 3 0.55-0.92; CaO 0.05-0.19; p.p.p. 13.34-13.97. It is recommended to use pure quartz sand with a low content of iron compounds.
Компоненты дозируют в требуемых количествах, смешивают и сплавляют при температуре 1450-1480°C. Расплав гранулируют в воду. Полученную фритту загружают в шаровую мельницу и размалывают мокрым способом до полного прохождения через сетку 008. Подготавливают глазурную суспензию с влажностью 45-50%. Суспензию наносят на поверхность обожженных керамических изделий, которые обжигают вторично при температуре 1000-1100°C. Глазурь образует покрытие, имеющее синюю окраску.The components are dosed in the required quantities, mixed and fused at a temperature of 1450-1480 ° C. The melt is granulated into water. The resulting frit is loaded into a ball mill and milled wet until it passes through the mesh 008. Prepare a glaze suspension with a moisture content of 45-50%. The suspension is applied to the surface of the fired ceramic products, which are fired a second time at a temperature of 1000-1100 ° C. The glaze forms a blue coating.
Источники информацииInformation sources
1. Алферов Л.Г. Технология росписи. Дерево. Металл. Керамика. Ткани. - Ростов-на-Дону: Изд-во «Феникс», 2000. - С.256.1. Alferov L.G. Mural technology. Wood. Metal. Ceramics. Tissues. - Rostov-on-Don: Publishing house "Phoenix", 2000. - P.256.
Claims (1)