RU2478741C1

RU2478741C1 - Method for obtaining tissues of crepe weaves

Info

Publication number: RU2478741C1
Application number: RU2011148039/12A
Authority: RU
Inventors: Галина Ивановна Толубеева; Виктор Алексеевич Толубеев
Priority date: 2011-11-28
Filing date: 2011-11-28
Publication date: 2013-04-10

Abstract

FIELD: textiles, paper.

SUBSTANCE: in the claimed method of obtaining tissues of crepe weaves the R₀×R_y threads are added on the area of rapport, which is filled only with weft or only with warp overlaps numbered from bottom to top in ascending order, warp or weft single overlaps with the numbers from the generated one-dimension array of the list of possible numbers of added single overlaps, which is a random permutation of the integer numbers in the range [1, 2, …, R₀×R_y] to achieve the desired values of parameters of obtained crepe weaves.

EFFECT: creation of new crepe weaves providing obtaining crepe close texture fabric surface without rhytmicity of the pattern both on the entire area of rapport and its individual sections, control and prevention of occurring of long horizontal and vertical layers of the same overlaps during the production of crepe weave.

3 tbl, 4 dwg

Description

Изобретение относится к производству текстильных материалов и касается изготовления тканей креповых переплетений, вырабатываемых на ткацких станках из пряжи обычной крутки.The invention relates to the production of textile materials and for the manufacture of crepe weave fabrics produced on looms from ordinary twist yarn.

Назначение креповых переплетений ткани, относящихся к классу мелкоузорчатых, подклассу комбинированных - получение мелкозернистой креповой поверхности ткани без попеременного использования в утке ткани полотняного переплетения нитей повышенной креповой крутки левого и правого направлений.The purpose of crepe weaves of fabric belonging to the class of fine-knitted, combined subclass is to obtain a fine-grained crepe surface of the fabric without alternating use of plain weave of threads of increased crepe twist left and right in the weft of the fabric.

Известен способ получения тканей креповых переплетений совмещением двух и более переплетений, когда на площади раппортов R_o×R_y нитей, найденных как наименьшее общее кратное раппортов совмещаемых исходных переплетений, строится первое переплетение, независимо от него строится второе, третье и так далее переплетения, причем, при совмещении основных перекрытий первого и последующих переплетений или оставляют основное перекрытие, осуществляя принцип совмещение-сложение, или заменяют его на уточное - принцип совмещение-вычитание, получая в итоге два различных креповых переплетения [Дружинская О.И. Разработка автоматизированных методов построения заправочных рисунков тканей комбинированных переплетений // Диссертация на соискание ученой степени к.т.н. - М.: МГТУ им. А.Н.Косыгина, 2007, с.52].There is a method of obtaining crepe weave fabrics by combining two or more weaves, when the first weave is constructed on the area of rapport R _o × R _{y of} threads found as the smallest common multiple of the repeat weights of the combined initial weaves, independently the second, third and so on weaves are constructed, moreover , when combining the main floors of the first and subsequent weaves, either leave the main floor, implementing the principle of combination-addition, or replace it with the weft one - the principle of combination-subtraction, getting as a result, two different crepe weaves [O. Druzhinskaya Development of automated methods for constructing filling patterns of fabrics of combined weaves // Thesis for the degree of candidate of technical sciences - M.: MSTU. A.N. Kosygina, 2007, p. 52].

Известен также способ получения тканей креповых переплетений совмещением двух и более переплетений при попеременном использовании принципов совмещения-сложения и совмещения-вычитания на отдельных нитях раппорта с задаваемыми различными чередованиями обоих принципов [Патент 2374368 C2 РФ, МПК⁶ D03D 23/00. Способ получения тканей креповых переплетений / Малецкая С.В., Малецкий В.В.; заявитель и патентообладатель Государственное образовательное учреждение высшего профессионального образования «Ульяновский государственный технический университет». №2008102914/12; заявл. 25.01.2008; опубл. 27.11.2009, 7 с.: 4 ил.].There is also a method of obtaining crepe weave fabrics by combining two or more weaves with the alternate use of the principles of combining-addition and combining-subtraction on separate threads of rapport with various alternations of both principles that can be set [Patent 2374368 C2 of the Russian Federation, IPC ⁶ D03D 23/00. A method of obtaining crepe weave fabrics / Maletskaya S.V., Maletsky V.V .; Applicant and patent holder State educational institution of higher professional education “Ulyanovsk State Technical University”. No. 2008102914/12; declared 01/25/2008; publ. November 27, 2009, 7 p.: 4 ill.].

Анализ принятого в аналогах способа совмещения двух и более переплетений показывает, что он представляет собой способ добавления основных перекрытий второго, третьего и так далее переплетений к исходному первому переплетению на площади расчетного раппорта R_o×R_y нитей.An analysis of the method of combining two or more weaves adopted in analogues shows that it is a method of adding the main overlaps of the second, third and so on weaves to the initial first weave on the area of the calculated rapport R _o × R _{y of} threads.

Недостатками способов-аналогов является то, что при получении тканей креповых переплетений способом совмещения двух и более переплетений как отдельного использования принципов совмещение-сложение и совмещение-вычитание, так и их последовательного чередования, не всегда предотвращает появление в получаемом креповом переплетении ритмичных рисунков, данный способ не всегда дает возможность получить мелкозернистую поверхность ткани, допускает появление чрезмерно длинных основных и уточных настилов, например имеются основные и уточные настилы, составляющие 11 перекрытий. Кроме того, способ получения креповых переплетений тканей путем совмещения двух и более переплетений не дает возможность контролировать при получении переплетения максимальную и среднюю длину основных и уточных настилов.The disadvantages of the analogue methods is that when obtaining crepe weave fabrics by combining two or more weaves, as a separate use of the principles of combination-addition and combination-subtraction, and their sequential alternation, does not always prevent the appearance of rhythmic patterns in the resulting crepe weave, this method does not always make it possible to obtain a fine-grained surface of the fabric, allows the appearance of excessively long main and weft flooring, for example, there are basic and weft decking, is 11 floors. In addition, the method of obtaining crepe weave fabrics by combining two or more weaves does not make it possible to control the maximum and average lengths of the main and weft floorings when receiving weaves.

За прототип принят способ получения тканей креповых переплетений добавлением к заданному переплетению, построенному на площади принятого раппорта R_o×R_y нитей, основных или уточных перекрытий произвольно или по какому-либо закону [Мартынова А.А., Слостина Г.Л., Власова Н.А. Строение и проектирование тканей. М.: РИО МГТА им. А.Н.Косыгина, 1999, с.89].The prototype adopted a method of obtaining crepe weave fabrics by adding to a given weave built on the area of the accepted rapport R _o × R _{y of} threads, weft or weft overlaps arbitrarily or according to some law [Martynova A.A., Slostina G.L., Vlasova ON. The structure and design of fabrics. M .: RIO MGTA them. A.N. Kosygina, 1999, p. 89].

Недостатком прототипа является то, что добавление к построенному на площади раппорта R_o×R_y нитей исходному переплетению произвольно или по какому-либо закону основных или уточных перекрытий не всегда дает возможность получить креповую мелкозернистую поверхность ткани, в большинстве случаев полученное креповое переплетение на отдельных участках раппорта сохраняет закономерности исходного переплетения, приводя к появлению ритмичных рисунков, добавление чрезмерного числа перекрытий приводит к появлению недопустимо длинных основных и уточных настилов, также нет возможности контроля максимальной и средней длин основных и уточных настилов в ходе построения переплетения.The disadvantage of the prototype is that the addition to the initial weave built on the area of the rapport R _o × R _y of stitches arbitrarily or according to some law of the main or weft overlap does not always make it possible to obtain a crepe fine-grained surface of the fabric, in most cases, crepe weave in individual sections rapport preserves the patterns of initial weaving, leading to the appearance of rhythmic patterns, the addition of an excessive number of overlaps leads to the appearance of unacceptably long main and weft flooring, there is also no possibility of controlling the maximum and average lengths of the main and weft flooring during the construction of weaving.

Техническим результатом заявляемого способа получения тканей креповых переплетений является расширение ассортимента тканей путем создания новых креповых переплетений, обеспечивающих получение креповой мелкозернистой поверхности ткани с отсутствием ритмичности рисунка как на всей площади раппорта, так и его отдельных участках, контроль и предотвращение появления в ходе получения крепового переплетения недопустимо длинных горизонтальных и вертикальных настилов одноименных перекрытий.The technical result of the proposed method for producing crepe weave fabrics is to expand the assortment of fabrics by creating new crepe weaves that provide crepe fine-grained fabric surface with no rhythm in the pattern both over the entire rapport area and its individual sections, and it is unacceptable to control and prevent the appearance of crepe weave long horizontal and vertical floorings of the same floor.

Указанный технический результат достигается тем, что в способе получения тканей креповых переплетений, заключающемся в добавлении на известной площади раппорта R_o×R_y нитей основных или уточных перекрытий по определенному закону, согласно изобретению, принимают максимально допустимые величины настилов одноименных перекрытий по основе f_кр.omax и по утку f_кp.ymax, пределы средней длины перекрытий по основе f_кр.o и по утку f_кр.y, пределы коэффициента связанности переплетения по основе K_no и по утку K_ny, заполняют раппорт переплетения одними уточными или одними основными настилами, последовательно снизу-вверх и слева-направо нумеруют все перекрытия раппорта получаемого крепового переплетения, генерируют одномерный массив p, представляющий собой случайную перестановку из целых чисел в пределах [1, 2, …, R_o×R_y] и являющийся перечнем возможных номеров основных или уточных перекрытий крепового переплетения, постепенно добавляют к уточным настилам основные перекрытия или к основным настилам уточные перекрытия по принятому закону случайной перестановки целых чисел, определяют фактическую максимальную длину горизонтальных и вертикальных настилов одноименных перекрытий, после получения крепового переплетения с длиной вертикальных и горизонтальных основных и уточных настилов, не превышающих максимально возможные, находят сумму всех пересечек по основе Σt_o и по утку Σt_y, среднее на нить число пересечек по основе t_o и по утку t_y, средние длины перекрытий по основе f_o и по утку f_y, коэффициенты связанности переплетения по основе K_no и по утку K_ny по известным зависимостям, сравнивают фактические значения параметров переплетения с заданными, анализируют полученное креповое переплетение, принимают решение о продолжении или прекращении добавления перекрытий; для получения переплетений креповых тканей путем постепенного добавления уточных перекрытий к основным настилам на площади раппорта R_o×R_y нитей всю последовательность действий повторяют, получают переплетения, негативные по отношению к переплетениям, полученным добавлением основных перекрытий к уточным настилам, причем значения параметров переплетений-негативов равны значениям параметров переплетений, полученных добавлением основных перекрытий.The specified technical result is achieved by the fact that in the method for producing crepe weave fabrics, which consists in adding, on a known rapport area R _o × R _y, yarns of warp or weft floors according to a certain law, according to the invention, the maximum allowable flooring values of the same floors on the basis of f _cr are adopted _{. omax} and weft f _cr.ymax , the limits of the average length of the overlap on the basis of f _cr.o and the weft f _cr.y , the limits of the coefficient of weave connectivity on the basis of K _no and the weft K _ny , fill the weave pattern one by one single or single main floorings, sequentially from bottom to top and from left to right, number all overlapping patterns of the resulting crepe weave, generate a one-dimensional array p, which is a random permutation of integers within [1, 2, ..., R _o × R _y ] and which is a list of possible numbers of the main or weft overlaps of the crepe weave, gradually add to the weft decks the main floors or to the main decks of the weft according to the adopted law of random rearrangement of integers, determine the fact ical maximum length of vertical and horizontal decks of similar overlap, after receiving crepe weave with the length of vertical and horizontal warp and weft decking not exceeding the maximum possible, finding the sum of all peresechek warp Σt _o and weft Σt _y, mean on the thread number peresechek on the basis of t _o and weft t _y, the average length of overlap on the basis of f _o and weft f _y, relatedness weave coefficients K _no warp and weft K _ny using known relationships, comparing the actual values of parameters CONTINUE? eteniya with predetermined analyzed resulting crepe weave, decide whether to continue or terminate the addition of overlap; to obtain crepe weaves by gradually adding weft overlaps to the main floors on the R _o × R _y rapport area of the threads, the whole sequence of actions is repeated, weaves that are negative with respect to weaves obtained by adding the main floors to the weft floors, and the values of the negatives equal to the values of the parameters of weaves obtained by adding the main floors.

Указанный технический результат - создание новых креповых переплетений, обеспечивающих получение мелкозернистой поверхности ткани с отсутствием ритмичности рисунка и чрезмерно длинных вертикальных и горизонтальных настилов одноименных перекрытий - достигается, с одной стороны, за счет использования при формировании перечня возможных номеров добавляемых одиночных перекрытий крепового переплетения случайных перестановок целых чисел в пределах [1, 2, …, R_o×R_y], получаемых с помощью табличного или программного датчика, с другой стороны, за счет постепенного добавления одиночных перекрытий к настилам противоположного знака перекрытий только в случае, если добавляемое перекрытие не приводит к появлению одноименного вертикального или горизонтального настила чрезмерной длины, что является контролем и предотвращением получения недопустимо длинных настилов одноименных перекрытий. Кроме того, после получения очередного варианта (иногда единственного) крепового переплетения выполняют расчет и оценку его параметров и принимают решение о продолжении или прекращении получения вариантов тканей креповых переплетений.The specified technical result - the creation of new crepe weaves, providing a fine-grained surface of the fabric with no rhythm in the pattern and excessively long vertical and horizontal floorings of the same name overlapping - is achieved, on the one hand, by using random permutations of integer crepes in the formation of the list of possible numbers of added single overlap crepe webs numbers within [1, 2, ..., R _o × R _y ] obtained using a table or software sensor, on the other hand, due to the gradual addition of single floors to floorings of the opposite sign of floorings only if the added flooring does not lead to the appearance of the same vertical or horizontal flooring of excessive length, which is the control and prevention of obtaining unacceptably long floorings of the same floor. In addition, after receiving the next version (sometimes the only one) of the crepe weave, they calculate and evaluate its parameters and decide on whether to continue or stop receiving crepe weave fabric options.

На фиг.1 изображены креповые переплетения, полученные способом прототипа, путем добавления основных перекрытий: 1-а) добавлением к полотняному переплетению на площади раппорта 8×8 нитей основных перекрытий по закону неправильного четырехнитного сатина, построенного на переплетении нечетных нитей основы с четными нитями утка; 1-б) произвольным добавлением двух основных перекрытий к переплетению, представленному на фиг.1-а; на фиг. 2 представлена последовательность построения вариантов креповых переплетений по заявленному способу путем добавления основных одиночных перекрытий к уточным настилам на площади раппорта 8×8 нитей: 2-а) площадь раппорта 8×8 нитей, заполненная длинными уточными настилами; 2-б) номера перекрытий раппорта; 2-в) и 2-г) промежуточные креповые переплетения, не удовлетворяющее заданным условиям; 2-д)-2-и) креповые переплетения, удовлетворяющие заданным условиям; на фиг. 3 представлены креповые переплетения, полученные по заявленному способу путем добавления уточных перекрытий к основным настилам на площади раппорта 8×8 нитей: 3-а) площадь раппорта 8×8 нитей, заполненная длинными основными настилами; 3-б) номера перекрытий раппорта; 3-в)-3-ж) показаны переплетения, негативные по отношению к переплетениям, представленным на фиг.2-г-2-з; на фиг.4 - пример крепового переплетения, полученного по заявленному способу: 4-а) добавлением основных перекрытий к уточным настилам; 4-б) добавлением уточных перекрытий к основным настилам. Figure 1 shows the crepe weave obtained by the prototype method, by adding the main floors: 1-a) adding to the plain weave on the rapport area 8 × 8 threads of the main floors according to the law of irregular four-strand sateen, built on the weaving of odd warp threads with even weft threads ; 1-b) the arbitrary addition of two main overlap to the weave shown in figure 1-a; in FIG. 2 shows the sequence of constructing crepe weave variants according to the claimed method by adding basic single ceilings to the weft floors on a rapport area of 8 × 8 threads: 2-a) the rapport area of 8 × 8 threads filled with long weft floors; 2-b) numbers of overlappings of rapport; 2-c) and 2-d) intermediate crepe weaves that do not satisfy the given conditions; 2-d) -2-i) crepe weaves that satisfy the given conditions; in FIG. 3 shows the crepe weaves obtained by the claimed method by adding weft overlaps to the main floors on the area of rapport of 8 × 8 threads: 3-a) the area of the rapport of 8 × 8 threads filled with long main floors; 3-b) numbers of overlappings of rapport; 3-c) -3-g) shows weaves that are negative with respect to the weaves shown in Fig.2-g-2-s; figure 4 is an example of a crepe weave obtained by the claimed method: 4-a) by adding basic overlap to the weft flooring; 4-b) by adding weft ceilings to the main flooring.

Пример практического осуществления способа.An example of the practical implementation of the method.

Получают возможные варианты ткани крепового переплетения с раппортами по основе и по утку, равными 8×8 нитей, предварительно обобщают опыт получения тканей креповых переплетений. В табл. 1 приведены значения средней длины перекрытий по основе f_o, по утку f_y, максимальной длины настилов одноименных перекрытий по основе f_omax, по утку f_ymax, коэффициент связанности переплетения, рассчитываемый по методике Г.И.Толубеевой, по основе K_no и по утку K_ny двух креповых переплетений, полученных по способу прототипа (фиг.1).Possible crepe weave fabric variants are obtained with rapport on the warp and weft equal to 8 × 8 threads, preliminary the experience of obtaining crepe weave fabrics is generalized. In the table. 1 shows the values of the average length of the ceilings on the basis of f _o , on the weft f _y , the maximum length of the floorings of the same floors on the basis of f _omax , on the weft f _ymax , the coefficient of interlocking, calculated according to the method of G.I. Tolubeeva, according to K _no and according to duck K _ny two crepe weaves obtained by the method of the prototype (figure 1).

Таблица 1Table 1 Номер крепаCrepe number f_o f _o f_y f _y f_omax f _omax f_ymax f _ymax K_no K _no K_ny K _ny Креп фиг.1-аCrepe figure 1-a 1,14291,1429 1,14291,1429 33 33 0,89290.8929 0,89290.8929 Креп фиг.1-бCrepe figure 1-b 1,23081,2308 1,23081,2308 33 33 0,82990.8299 0,82990.8299

По значениям параметров креповых переплетений, представленных в табл.1, принимают пределы необходимой величины средней длины перекрытий по основе f_кр.о=[1,1…2,0] и по утку f_кр.y=[1,1…2,0], принимают значение максимальной длины перекрытий по основе и по утку f_кр.оmax=/f_кр._ymax=3 перекрытия, пределы значений коэффициента связанности переплетения К_кр.no=К_кр.ny=[0,6…0,9], заполняют раппорт 8×8 нитей уточными настилами (фиг.2-а), последовательно, как показано на фиг.2-б, снизу-вверх и слева-направо нумеруют все перекрытия раппорта получаемого крепового переплетения, генерируют одномерный массив p возможных номеров основных перекрытий крепового переплетения, представляющий собой случайную перестановку из целых чисел в пределах [1, 2, …, 64], с помощью функции p=randperm(n) в среде программирования MATLAB:According to the values of the crepe weave parameters presented in Table 1, the limits of the required value of the average length of the ceilings on the basis of f _cr.o = [1.1 ... 2.0] and the weft f _cr.y = [1.1 ... 2, take 0], take the value of the maximum length of the ceilings on the basis and on the duck f _cr.Omax = / f _cr . _ymax = 3 overlap, the limits of the values of the coefficient of interconnection of the weave K _cr.no = K _cr.ny = [0.6 ... 0.9], fill the rapport of 8 × 8 threads with weft floors (Fig.2-a), sequentially, as shown figure 2-b, from bottom to top and from left to right, number all overlappings of the rapport of the resulting crepe weave, generate a one-dimensional array p of possible numbers of the main overlap of the crepe weave, which is a random permutation of integers within [1, 2, ..., 64 ], using the p = randperm (n) function in the MATLAB programming environment:

наносят основные перекрытия на уточные перекрытия раппорта с номерами, соответствующими числам одномерного массива p, контролируя при этом длину горизонтальных и вертикальных настилов одноименных перекрытий. На фиг.2-в показано нанесение первых 32-х основных перекрытий с номерами до перекрытия №38 (номера нанесенных перекрытий в сгенерированной последовательности для наглядности обведены кружком), анализируя полученное креповое переплетение (фиг.2-в) видим, что максимальная длина горизонтальных и вертикальных основных настилов f_omax нe превышает заданную f_кр.оmах, равную трем перекрытиям, максимальная длина уточных настилов f_ymax равна четырем перекрытиям (этот уточный настил расположен на второй основной нити), превышает заданную f_кр.ymax, равную трем перекрытиям, что свидетельствует о необходимости продолжить добавление основных перекрытий на плоскость раппорта; далее необходимо поместить основное перекрытие №38, как показано на фиг.2-г, это невозможно, так как на третьей уточной нити будет получен основной настил из четырех перекрытий, что недопустимо по условию задачи; продолжим дальнейшее добавление основных перекрытий; номера перекрытий, нанести которые невозможно, не обведены кружком, нанесение основного перекрытия №14 (оно для наглядности обведено квадратом) ликвидирует последний настил, превышающий максимально возможную длину, добавление основных перекрытий можно остановить; полученное креповое переплетение представлено на фиг.2-д, находят сумму всех пересечек по основе Σt_o=38 и по утку Σt_y=38, по известным формулам рассчитывают среднее число пересечек по основе t_o и по утку t_y, средние длины перекрытий по основе f_o и по утку f_y, по известной методике Г.И.Толубеевой определяют коэффициенты связанности переплетения по основе K_no и по утку K_ny. Параметры крепового переплетения, представленного на фиг.2-д, приведены в табл.2.apply the main floors to weft rapport floors with numbers corresponding to the numbers of the one-dimensional array p, while controlling the length of the horizontal and vertical floorings of the same floors. Figure 2-c shows the application of the first 32 main floors with numbers to floor No. 38 (the numbers of the applied floors in the generated sequence are circled for clarity), analyzing the crepe weave obtained (Figure 2-c), we see that the maximum horizontal length and vertical main decking f _omax ne f _kr.omah exceeds a predetermined, three overlaps equal to the maximum length of weft decking f _ymax is equal to four overlaps (weft this flooring is located on the second main thread) exceeds a predetermined _kr.ymax f equal renovated floors, highlighting the need to continue to add to the main overlap in the plane rapport; then it is necessary to place the main floor No. 38, as shown in Fig. 2d, this is impossible, since the main flooring of four floors will be obtained on the third weft thread, which is unacceptable by the condition of the problem; we will continue to add further main floors; the numbers of overlappings that cannot be applied are not circled, the application of the main floor No. 14 (it is surrounded by a square for clarity) eliminates the last flooring exceeding the maximum possible length, the addition of main floors can be stopped; the obtained crepe weave is shown in Fig.2-e, find the sum of all intersections on the basis of Σt _o = 38 and weft Σt _y = 38, according to well-known formulas, calculate the average number of intersections on the basis of t _o and weft t _y , the average lengths of floors on the basis of f _o and weft f _y , according to the well-known method of G.I. Tolubeeva, the coefficients of weaving connectivity are determined on the basis of K _no and weft K _ny . The crepe weave parameters shown in Fig.2-e are given in table.2.

Таблица 2table 2 Номер крепаCrepe number f_o f _o f_y f _y f_omax f _omax f_ymax f _ymax K_no K _no K_ny K _ny Креп фиг.2-дCrepe Fig. 2-d 1,68421.6842 1,68421.6842 33 33 0,63710.6371 0,63710.6371 Креп фиг.3-вCrepe 3-c Креп фиг.2-еCrepe fig. 2 1,60001,6000 1,68421.6842 33 33 0,66220.6622 0,64030.6403 Креп фиг.3-гCrepe 3-g Креп фиг.2-жCrepe fig. 2-g 1,68421.6842 1,68421.6842 33 33 0,63510.6351 0,63510.6351 Креп фиг.3-дCrepe Fig. 3-d Креп фиг.2-зCrepe fig.2-z 1,68421.6842 1,77781,7778 33 33 0,63040.6304 0,60850.6085 Креп фиг.3-еCrepe Fig. 3 Креп фиг.2-иCrepe Fig. 2 1,68421.6842 1,77781,7778 33 33 0,63100.6310 0,60910.6091 Креп фиг.3-жCrepe 3-g

Сравнение фактических значений параметров переплетения с необходимыми показывает соответствие полученного переплетения заданным условиям, принимают решение о продолжении или прекращении добавления перекрытий. Если принимают решение продолжить получение вариантов креповых переплетений, следующим на плоскость раппорта необходимо поместить перекрытие №32, что невозможно, так как на восьмой уточной нити появляется основной настил из 6 перекрытий, а на четвертой основной нити - основной настил из 7 перекрытий, что недопустимо по условию задачи, перекрытие №6 поместить на плоскость раппорта крепового переплетения нельзя по тем же причинам, далее помещают перекрытие №12, получают креповое переплетение, представленное на фиг. 2-е, параметры которого приведены в табл.2, поместить перекрытия с номерами №23, №9 и №63 нельзя по условию задачи, далее помещают перекрытие №45, как показано на фиг.2-ж, параметры этого крепового переплетения также приведены в табл.3, нанести перекрытия №41 и №37 нельзя, далее, поместив перекрытие №59, получают креповое переплетение, представленное на фиг.2-з, из оставшегося ряда перекрытий возможно нанесение перекрытия №17, полученное при этом креповое переплетение представлено на рис.2-и, параметры переплетений - в табл.3. Анализ полученных креповых переплетений показывает, что заданным условиям удовлетворяют пять вариантов тканей, во всех пяти переплетениях полностью отсутствует ритмичность рисунков, максимальная длина основных и уточных настилов вдоль обеих систем нитей не превышает заданную и равна 3 перекрытиям, в ходе получения креповых переплетений контролируют их параметры и имеют возможность принять обоснованное решение о прекращении получения вариантов креповых переплетений.A comparison of the actual values of the weave parameters with the necessary ones shows the correspondence of the obtained weave to the given conditions, they decide to continue or stop adding overlap. If you decide to continue receiving crepe weave options, then next to the rapport plane you need to put overlap No. 32, which is impossible, since the main flooring of 6 floors appears on the eighth weft thread and the main flooring of 7 floors appears on the fourth main thread, which is unacceptable the condition of the problem, overlap No. 6 cannot be placed on the crepe weave repeat plane for the same reasons, then overlap No. 12 is placed, and the crepe weave shown in FIG. 2, the parameters of which are given in Table 2, it is impossible to place the overlap with the numbers No. 23, No. 9 and No. 63 according to the condition of the problem, then place the overlap No. 45, as shown in figure 2-g, the parameters of this crepe weave are also given in table 3, overlapping No. 41 and No. 37 cannot be applied, then, placing overlapping No. 59, the crepe weave shown in Fig. 2-c is obtained, overlapping No. 17 is possible from the remaining row of ceilings, the crepe weave obtained is presented in Fig. 2, the parameters of weaving are shown in Table 3. An analysis of the crepe weaves obtained shows that five fabric options satisfy the given conditions, the rhythm of the patterns is completely absent in all five weaves, the maximum length of the main and weft floorings along both yarn systems does not exceed the specified one and is equal to 3 overlaps.In the process of obtaining crepe weaves, their parameters are controlled and have the opportunity to make an informed decision to stop receiving crepe weave options.

При получении переплетений креповых тканей путем постепенного добавления уточных перекрытий к основным настилам, показанным на фиг. 3-а, на площади раппорта 8×8 нитей, с номерами перекрытий, показанными на фиг. 3-б, с той же сгенерированной последовательностью возможных номеров добавляемых одиночных перекрытий, всю последовательность действий сохраняют, получают переплетения, негативные по отношению к рассмотренным. Пример получения креповых переплетений путем постепенного добавления одиночных уточных перекрытий к основным настилам представлен на фиг.3, по условиям рассмотренного примера также получают пять вариантов креповых переплетений, представленных на фиг.3-в-3-ж, являющихся негативами креповых переплетений, показанных на фиг.2-д-2-и, причем, значения параметров переплетений-негативов равны значениям параметров переплетений, полученных добавлением основных перекрытий к уточным настилам.Upon receipt of crepe weave by gradually adding weft overlaps to the main floorings shown in FIG. 3-a, in the repeat area of 8 × 8 threads, with the overlap numbers shown in FIG. 3-b, with the same generated sequence of possible numbers of added single floors, the entire sequence of actions is saved, weaves are received that are negative in relation to the ones considered. An example of obtaining crepe weaves by gradually adding a single weft overlap to the main flooring is shown in FIG. 3, according to the conditions of the considered example, five variants of crepe weaves shown in FIGS. 3-c-3-g, which are negatives of crepe weaves shown in FIG. .2-d-2-and, moreover, the values of the parameters of weaves-negatives are equal to the values of the parameters of weaves obtained by adding the main floors to the weft flooring.

На фиг.4-а и 4-б представлены креповые переплетения, полученные заявленным способом путем добавления одиночных основных перекрытий к уточным настилам и одиночных уточных перекрытий к основным настилам с заданными пределами средних и максимальных длин перекрытий по основе и по утку и коэффициентов связанности переплетения по основе и по утку из предыдущего примера со следующей, сгенерированной с помощью функции p=randperm(64) в среде программирования MATLAB, случайной перестановкой номеров перекрытий:Figures 4-a and 4-b show crepe weaves obtained by the claimed method by adding single main floors to weft flooring and single weft floors to main flooring with specified limits of average and maximum lengths of overlap on the base and along the weft and the coefficients of weave connectivity for based on the weft from the previous example with the following generated by using the p = randperm (64) function in the MATLAB programming environment, by randomly rearranging the numbers of overlappings:

Номера перекрытий, нанести которые возможно, обведены кружком, нанесение одиночного перекрытия №62, обведенного квадратом, ликвидирует последний настил, превышающий максимально возможную длину, получают при добавлении одиночных основных перекрытий переплетение, показанное на фиг. 4-а, одиночных уточных перекрытий - 4-б, нанесение любого из оставшихся трех перекрытий приводит к превышению максимально допустимой по условию задачи длины настилов. Данная случайная перестановка целых чисел в пределах [1, 2, …, 64] позволяет получить только одно креповое переплетение добавлением основных перекрытий и одно негативное переплетение при добавлении уточных перекрытий, удовлетворяющих заданным условиям, параметры этих креповых переплетений приведены в табл.3.The numbers of the overlappings, which can be circled, applying a single overlap No. 62, circled by a square, eliminates the last flooring exceeding the maximum possible length; when adding single main overlaps, the weaving shown in FIG. 4-a, single weft overlaps - 4-b, applying any of the remaining three overlaps leads to exceeding the maximum allowable floor lengths for the task. This random permutation of integers within [1, 2, ..., 64] allows you to get only one crepe weave by adding basic overlappings and one negative weave when adding weft overlaps that satisfy the given conditions, the parameters of these crepe weaves are given in Table 3.

Таблица 3Table 3 Номер крепаCrepe number f_o f _o f_y f _y f_omax f _omax f_ymax f _ymax K_no K _no K_ny K _ny Креп фиг.4-аCrepe 4-a 1,60001,6000 1,52381,5238 33 33 0,67100.6710 0,69290.6929 Креп фиг.4-бCrepe Fig. 4-b

В переплетениях полностью отсутствует ритмичность рисунка, максимальная длина основных и уточных настилов вдоль обеих систем нитей не превышает заданную, равную трем, т.е. контролируются их параметры.In the interweaving, the rhythm of the pattern is completely absent, the maximum length of the main and weft decks along both systems of threads does not exceed a predetermined one equal to three, i.e. their parameters are controlled.

Claims

A method of obtaining crepe weave fabrics, which consists in adding, on a known rapport area R _o × R _y, yarns of warp or weft floors according to a certain law, characterized in that the maximum allowable values of flooring of the same name are taken on the basis of f _cr.omax and weft f _{cr. ymax} , the limits of the average length of the ceilings on the basis of f _cr.o and on the weft f _cr.u , the limits of the coefficient of connectedness of the weave on the basis of K _no and on the weft K _ny , fill the weave pattern with one weft or one main flooring, sequentially with bottom-up and left-to-right numbers all overlapping rapports of the resulting crepe weave, generate a one-dimensional array p, which is a random permutation of integers within [1, 2, ..., R _o × R _y ] and is a list of possible basic or weft numbers crepe weave overlays, gradually add basic overlaps to weft decks or weft overlaps to main decks according to the accepted law of random rearrangement of integers, determine the actual maximum horizontal and vertical lengths s of similar flooring slabs, after receiving crepe weave with vertical and horizontal length of the warp and weft decking not exceeding the maximum possible, are based on the sum of all Σt _o peresechek and weft Σt _y, the average number of the yarn on the basis peresechek t _o and for weft t _y , average lengths of overlap on the basis of f _o and for weft f _y , the coefficients of connectedness of weaves on the basis of K _no and on weft K _ny according to known dependencies, compare the actual values of the parameters of weave with the given ones, analyze the resulting crepe e interweaving, decide on the continuation or termination of the addition of overlappings; to obtain crepe weaves by gradually adding weft overlaps to the main floors on the R _o × R _y rapport area of the threads, the whole sequence of actions is repeated, weaves that are negative with respect to weaves obtained by adding the main floors to the weft floors, and the values of the negatives equal to the values of the parameters of weaves obtained by adding the main floors.