RU2478085C1 - Crude mixture for making sculpture (versions) - Google Patents

Crude mixture for making sculpture (versions) Download PDF

Info

Publication number
RU2478085C1
RU2478085C1 RU2011139926/03A RU2011139926A RU2478085C1 RU 2478085 C1 RU2478085 C1 RU 2478085C1 RU 2011139926/03 A RU2011139926/03 A RU 2011139926/03A RU 2011139926 A RU2011139926 A RU 2011139926A RU 2478085 C1 RU2478085 C1 RU 2478085C1
Authority
RU
Russia
Prior art keywords
starch
gypsum binder
crude mixture
sculpture
dry milk
Prior art date
Application number
RU2011139926/03A
Other languages
Russian (ru)
Inventor
Юлия Алексеевна Щепочкина
Original Assignee
Юлия Алексеевна Щепочкина
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Юлия Алексеевна Щепочкина filed Critical Юлия Алексеевна Щепочкина
Priority to RU2011139926/03A priority Critical patent/RU2478085C1/en
Application granted granted Critical
Publication of RU2478085C1 publication Critical patent/RU2478085C1/en

Abstract

FIELD: chemistry.
SUBSTANCE: invention relates to composition of a crude mixture which can be used to make sculpture. According to one of the versions, the crude mixture for making sculpture contains gypsum binder, starch, cast iron shavings ground until full passage through sieve 008, and dry milk, with the following ratio of components, wt %: cast iron shavings 8.0-12.0; gypsum binder 82.0-86.0; dry milk 2.0-4.0; starch 2.0-4.0. In another version, the crude mixture for making sculpture contains gypsum binder, starch and dry milk, with the following ratio of components, wt %: gypsum binder 92.0-96.0; dry milk 2.0-4.0; starch 2.0-4.0.
EFFECT: sharp contours of the article made from the crude mixture, as well as easier processing of the surface of the sculpture.
2 cl, 2 tbl

Description

Изобретение касается состава сырьевой смеси, которая может быть использована для изготовления скульптуры.The invention relates to the composition of the raw mixture, which can be used to make sculptures.

Известна сырьевая смесь для изготовления скульптуры, содержащая гипсовое вяжущее и крахмал [1].Known raw mix for the manufacture of sculptures containing gypsum binder and starch [1].

Задачей изобретения является облегчение последующей обработки поверхности скульптуры, полученной из сырьевой смеси.The objective of the invention is to facilitate subsequent processing of the surface of the sculpture obtained from the raw mix.

Технический результат достигается тем, что сырьевая смесь для изготовления скульптуры, включающая гипсовое вяжущее и крахмал, дополнительно содержит стружку чугунную, измельченную до полного прохождения через сетку 008, и сухое молоко при следующем соотношении компонентов, мас.%: стружка чугунная 8,0-12,0; гипсовое вяжущее 82,0-86,0; сухое молоко 2,0-4,0; крахмал 2,0-4,0.The technical result is achieved in that the raw mixture for the manufacture of sculptures, including gypsum binder and starch, additionally contains pig-iron shavings, crushed until completely passing through the mesh 008, and milk powder in the following ratio of components, wt.%: Pig-iron shavings 8.0-12 0; gypsum binder 82.0-86.0; milk powder 2.0-4.0; starch 2.0-4.0.

Технический результат достигается также тем, что сырьевая смесь для изготовления скульптуры, включающая гипсовое вяжущее и крахмал, дополнительно содержит сухое молоко при следующем соотношении компонентов, мас.%: гипсовое вяжущее 92,0-96,0; сухое молоко 2,0-4,0; крахмал 2,0-4,0.The technical result is also achieved by the fact that the raw mixture for the manufacture of sculptures, including gypsum binder and starch, additionally contains milk powder in the following ratio of components, wt.%: Gypsum binder 92.0-96.0; milk powder 2.0-4.0; starch 2.0-4.0.

В таблицах 1 и 2 приведены примеры предложенной сырьевой смеси для изготовления скульптуры.Tables 1 and 2 show examples of the proposed raw mix for making sculptures.

Таблица 1Table 1 КомпонентыComponents Состав, мас.%:Composition, wt.%: 1one 22 Стружка чугуннаяCast iron shavings 8,08.0 12,012.0 Гипсовое вяжущееGypsum binder 86,086.0 82,082.0 Сухое молокоPowdered milk 2,02.0 4,04.0 КрахмалStarch 4,04.0 2,02.0

Таблица 2table 2 КомпонентыComponents Состав, мас.%:Composition, wt.%: 1one 22 Гипсовое вяжущееGypsum binder 96,096.0 92,092.0 Сухое молокоPowdered milk 2,02.0 4,04.0 КрахмалStarch 2,02.0 4,04.0

Приготовление сырьевой смеси поясняется примерами.The preparation of the raw mix is illustrated by examples.

1. Компоненты дозируют в требуемых количествах. Стружку чугунную измельчают (до полного прохождения через сетку 008). Стружку чугунную, гипсовое вяжущее (марок Г-2 - Г-7), сухое молоко, крахмал смешивают, добавляют воду и еще раз смешивают. Количество воды подбирают экспериментальным путем до достижения нормальной густоты смеси (диаметр расплыва 180±5 мм). Полученную смесь укладывают в формы и оставляют до отверждения.1. The components are dosed in the required quantities. The pig-iron shavings are crushed (until they completely pass through mesh 008). Cast-iron shavings, gypsum binders (grades G-2 - G-7), milk powder, starch are mixed, water is added and mixed again. The amount of water is selected experimentally until a normal density of the mixture is reached (spreading diameter 180 ± 5 mm). The resulting mixture is placed in molds and left to cure.

2. Компоненты дозируют в требуемых количествах. Гипсовое вяжущее (марок Г-2 - Г-7), сухое молоко, крахмал смешивают, добавляют воду и еще раз смешивают. Количество воды подбирают экспериментальным путем до достижения нормальной густоты смеси (диаметр расплыва лепешки 180±5 мм). Полученную смесь укладывают в формы и оставляют до отверждения.2. The components are dosed in the required quantities. Gypsum binder (grades G-2 - G-7), milk powder, starch are mixed, water is added and mixed again. The amount of water is selected experimentally to achieve normal density of the mixture (the diameter of the spread of the cake 180 ± 5 mm). The resulting mixture is placed in molds and left to cure.

После извлечения из формы скульптуру покрывают мыловаром и сушат. Просушенное изделие покрывают нитролаком, слегка подкрашивая углубления желтой масляной краской.After removing from the mold, the sculpture is covered with soap and dried. The dried product is coated with nitro-varnish, slightly tinting the recesses with yellow oil paint.

Источник информацииThe source of information

1. RU 2409530, 2011.1. RU 2409530, 2011.

Claims (2)

1. Сырьевая смесь для изготовления скульптуры, включающая гипсовое вяжущее и крахмал, отличающаяся тем, что дополнительно содержит стружку чугунную, измельченную до полного прохождения через сетку 008, и сухое молоко при следующем соотношении компонентов, мас.%:
стружка чугунная 8,0-12,0 гипсовое вяжущее 82,0-86,0 сухое молоко 2,0-4,0 крахмал 2,0-4,0
1. The raw material mixture for the manufacture of sculptures, including gypsum binder and starch, characterized in that it further comprises pig-iron shavings, crushed until completely passing through the mesh 008, and milk powder in the following ratio of components, wt.%:
cast iron shavings 8.0-12.0 gypsum binder 82.0-86.0 powdered milk 2.0-4.0 starch 2.0-4.0
2. Сырьевая смесь для изготовления скульптуры, включающая гипсовое вяжущее и крахмал, отличающаяся тем, что дополнительно содержит сухое молоко при следующем соотношении компонентов, мас.%:
гипсовое вяжущее 92,0-96,0 сухое молоко 2,0-4,0 крахмал 2,0-4,0
2. The raw material mixture for the manufacture of sculptures, including gypsum binder and starch, characterized in that it additionally contains milk powder in the following ratio, wt.%:
gypsum binder 92.0-96.0 powdered milk 2.0-4.0 starch 2.0-4.0
RU2011139926/03A 2011-09-30 2011-09-30 Crude mixture for making sculpture (versions) RU2478085C1 (en)