RU2329217C1 - Glaze - Google Patents

Glaze Download PDF

Info

Publication number
RU2329217C1
RU2329217C1 RU2006146112/03A RU2006146112A RU2329217C1 RU 2329217 C1 RU2329217 C1 RU 2329217C1 RU 2006146112/03 A RU2006146112/03 A RU 2006146112/03A RU 2006146112 A RU2006146112 A RU 2006146112A RU 2329217 C1 RU2329217 C1 RU 2329217C1
Authority
RU
Russia
Prior art keywords
glaze
cao
pbo
sio
bao
Prior art date
Application number
RU2006146112/03A
Other languages
Russian (ru)
Inventor
Юли Алексеевна Щепочкина (RU)
Юлия Алексеевна Щепочкина
Original Assignee
Юлия Алексеевна Щепочкина
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Юлия Алексеевна Щепочкина filed Critical Юлия Алексеевна Щепочкина
Priority to RU2006146112/03A priority Critical patent/RU2329217C1/en
Application granted granted Critical
Publication of RU2329217C1 publication Critical patent/RU2329217C1/en

Abstract

FIELD: chemistry.
SUBSTANCE: invention pertains to glaze compositions and can be used in making face tiles. The glaze consists of the following components in the given percentage mass ratios: SiO2 40.0-46.0; Al2O3 4.0-6.0; CaO 4.0-6.0; K2O 1.0-2.0; Na2O 1.0-2.0; B2O3 8.0-10.0; PbO 22.0-25.0; ZnO 4.0-6.0; TiO2 4.0-6.0; BaO 1.0-2.0.
EFFECT: increased frost resistance of the glaze.
1 tbl

Description

Изобретение относится к области технологии силикатов, в частности к составам фриттованных глазурей, используемых в производстве облицовочной плитки.The invention relates to the field of technology of silicates, in particular to compositions of fritted glazes used in the manufacture of facing tiles.

Известна глазурь, включающая, мас.%: SiO2 45,57; Al2O3 6,57; CaO 3,79; K2O 1,79; Na2O 7,2; B2O3 15,39; PbO 20,57; Fe2O3 0,08; MgO 0,04 /1/.Known glaze, including, wt.%: SiO 2 45.57; Al 2 O 3 6.57; CaO 3.79; K 2 O 1.79; Na 2 O 7.2; B 2 O 3 15.39; PbO 20.57; Fe 2 O 3 0.08; MgO 0.04 / 1 /.

Известна глазурь, содержащая, мас.%: SiO2 40,25-43,53; Al2O3 10,34-12,98; CaO 0,36-0,39; Fe2O3 0,27-0,29; K2O 1,54-1,95; Na2O 5,65-6,89; B2O3 6,59-7,97; MnO2 4,0-5,0; PbO 20,0-25,0; ZnO 4,0-5,0 /2/.Known glaze containing, in wt.%: SiO 2 40.25-43.53; Al 2 O 3 10.34-12.98; CaO 0.36-0.39; Fe 2 O 3 0.27-0.29; K 2 O 1.54-1.95; Na 2 O, 5.65-6.89; B 2 O 3 6.59-7.97; MnO 2 4.0-5.0; PbO 20.0-25.0; ZnO 4.0-5.0 / 2 /.

Цель изобретения - повышение морозостойкости глазури.The purpose of the invention is to increase frost resistance of glaze.

Цель достигается тем, что в состав глазури дополнительно вводят TiO2 и BaO при следующем соотношении компонентов, мас.%: SiO2 40,0-46,0; Al2O3 4,0-6,0; CaO 4,0-6,0; K2O 1,0-2,0; Na2O 1,0-2,0; B2O3 8,0-10,0; PbO 22,0-25,0; ZnO 4,0-6,0; TiO2 4,0-6,0; BaO 1,0-2,0.The goal is achieved by the fact that TiO 2 and BaO are additionally added to the glaze in the following ratio of components, wt.%: SiO 2 40.0-46.0; Al 2 O 3 4.0-6.0; CaO 4.0-6.0; K 2 O 1.0-2.0; Na 2 O 1.0-2.0; B 2 O 3 8.0-10.0; PbO 22.0-25.0; ZnO 4.0-6.0; TiO 2 4.0-6.0; BaO 1.0-2.0.

В таблице приведены составы глазури.The table shows the glaze compositions.

ТаблицаTable СоставStructure Компоненты, мас.%:Components, wt.%: Морозостойкость, циклыFrost resistance cycles SiO2 SiO 2 Al2O3 Al 2 O 3 CaOCao K2OK 2 O Na2ONa 2 O B2O3 B 2 O 3 PbOPbo ZnOZno TiO2 TiO 2 BaOBao 1one 40,040,0 6,06.0 4,04.0 1,01,0 2,02.0 10,010.0 25,025.0 6,06.0 4,04.0 2,02.0 290±10290 ± 10 22 43,043.0 5,05,0 5,05,0 1,51,5 1,51,5 9,09.0 23,523.5 5,05,0 5,05,0 1,51,5 290±10290 ± 10 33 46,046.0 4,04.0 6,06.0 2,02.0 1,01,0 8,08.0 22,022.0 4,04.0 6,06.0 1,01,0 290±10290 ± 10

Фритту варят при 1300-1350°C, расплав гранулируют. Фритту размалывают с добавкой 0,1% буры, 47,5% воды. Размалывают до остатка не более 0,2% на сетке №0056. Глазурную суспензию наносят на изделия, сушат и обжигают при 950-1000°С.The frit is boiled at 1300-1350 ° C, the melt is granulated. The frit is ground with the addition of 0.1% borax, 47.5% water. Grind to a residue of not more than 0.2% on mesh No. 0056. The glaze suspension is applied to the products, dried and fired at 950-1000 ° C.

Источники информацииInformation sources

1. Орлов Е.И. Глазури, эмали, керамические краски и массы. - М. - Л.: Комиссариат местной промышленности РСФСР, 1938. - С.14.1. Orlov E.I. Glazes, enamels, ceramic paints and masses. - M. - L .: Commissariat of local industry of the RSFSR, 1938. - P. 14.

2. Авторское свидетельство СССР №1039906, С03С 9/00, 1983.2. USSR author's certificate No. 1039906, С03С 9/00, 1983.

Claims (1)

Глазурь, содержащая SiO2, Al2О3, CaO, K2O, Na2O, В2O3, PbO, ZnO, отличающаяся тем, что дополнительно содержит TiO2 и ВаО при следующем соотношении компонентов, мас.%: SiO2 40,0-46,0; Al2О3 4,0-6,0; CaO 4,0-6,0; K2O 1,0-2,0; Na2O 1,0-2,0; В2О3 8,0-10,0; PbO 22,0-25,0; ZnO 4,0-6,0; TiO2 4,0-6,0; ВаО 1,0-2,0.Glaze containing SiO 2 , Al 2 O 3 , CaO, K 2 O, Na 2 O, B 2 O 3 , PbO, ZnO, characterized in that it additionally contains TiO 2 and BaO in the following ratio, wt.%: SiO 2 40.0-46.0; Al 2 O 3 4.0-6.0; CaO 4.0-6.0; K 2 O 1.0-2.0; Na 2 O 1.0-2.0; B 2 O 3 8.0-10.0; PbO 22.0-25.0; ZnO 4.0-6.0; TiO 2 4.0-6.0; BaO 1.0-2.0.
RU2006146112/03A 2006-12-25 2006-12-25 Glaze RU2329217C1 (en)