RU2160856C1 - Способ формирования антифрикционного покрытия контактирующих трущихся поверхностей - Google Patents

Способ формирования антифрикционного покрытия контактирующих трущихся поверхностей Download PDF

Info

Publication number
RU2160856C1
RU2160856C1 RU2000110414/28A RU2000110414A RU2160856C1 RU 2160856 C1 RU2160856 C1 RU 2160856C1 RU 2000110414/28 A RU2000110414/28 A RU 2000110414/28A RU 2000110414 A RU2000110414 A RU 2000110414A RU 2160856 C1 RU2160856 C1 RU 2160856C1
Authority
RU
Russia
Prior art keywords
antifriction coating
coating
substance
formation
friction surfaces
Prior art date
Application number
RU2000110414/28A
Other languages
English (en)
Original Assignee
Козлов Владимир Васильевич
Михальченков Владимир Анатольевич
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Козлов Владимир Васильевич, Михальченков Владимир Анатольевич filed Critical Козлов Владимир Васильевич
Priority to RU2000110414/28A priority Critical patent/RU2160856C1/ru
Priority to PCT/RU2000/000471 priority patent/WO2001079717A1/ru
Priority to AU2001217448A priority patent/AU2001217448A1/en
Application granted granted Critical
Publication of RU2160856C1 publication Critical patent/RU2160856C1/ru

Abstract

Изобретение относится к области машиностроения и может быть использовано в узлах трения. Способ формирования антифрикционного покрытия контактирующих трущихся поверхностей заключается в том, что между трущимися поверхностями размещают предварительно механоактивированную смесь размельченного формирующего антифрикционное покрытие вещества со связующим. В качестве формирующего антифрикционное покрытие вещества используют композицию природных минералов, содержащую, мас.%: Mg3Si2O5(OH)4 - 10-60, MgFe2O4 - 10-60, MoS2 - 1-20, сопутствующие редкоземельные элементы - 0,1-10, H2O - не более 5; предварительную механоактивацию можно проводить с пульсацией давления 0,01 - 10 МПа при 100 - 200°С. Технический результат - повышение стабильности, прочности и долговечности антифрикционного покрытия трущихся поверхностей.

Description

Изобретение относится к машиностроению и может быть использовано в узлах трения.
Известен способ формирования антифрикционного покрытия контактирующих трущихся поверхностей, заключающийся в том, что между трущимися поверхностями предварительно размещают механоактивированную смесь природного серпентинита дисперсностью 0,001-1 мкм в количестве 2-4 мас.%, см., например, патент Российской Федерации N2006708 по кл. F 16 C 33/14 от 22.12.92.
Недостатком этого способа является низкое качество образуемого покрытия, которое не обеспечивает достаточную износостойкость трущихся элементов.
Известен также способ формирования антифрикционного покрытия контактирующих трущихся поверхностей, заключающийся в том, что между трущимися поверхностями размещают предварительно механоактивированную смесь размельченного формирующего антифрикционное покрытие вещества со связующим, при этом в качестве такого вещества используют природный серпентинит, содержащий, мас.%:
MgO, CaO - 20 - 60
SiO, Al2O3 - 20 - 60
H2O - 3 - 10
Примеси пород - 3-10
Предварительную механоактивацию производят пульсацией давления 0,1 - 1,0 МПа при 40-100oC, размещение смеси и приработку трущихся поверхностей осуществляют при температуре механоактивации, см. патент Российской Федерации N2006707 по классу F 16 C 33/14 от 03.07.92.
Данное техническое решение принято в качестве прототипа настоящего изобретения.
Недостатком прототипа является неравномерная толщина получаемого антифрикционного покрытия, его нестабильность и недолговечность, особенно в условиях повышенных механических и температурных воздействий, что не позволяет обеспечить высокую износостойкость трущихся поверхностей.
В основу настоящего изобретения положено решение задачи повышения стабильности, прочности и долговечности антифрикционного покрытия трущихся поверхностей, в том числе при интенсивных механических и температурных воздействиях, обеспечение высокой износостойкости этих поверхностей.
Согласно изобретению эта задача решается за счет того, что в способе формирования антифрикционного покрытия контактирующих трущихся поверхностей, заключающемся в том, что между трущимися поверхностями размещают предварительно механоактивированную смесь размельченного формирующего антифрикционное покрытие вещества со связующим, в качестве формирующего антифрикционное покрытие вещества используют композицию природных минералов, содержащую, мас. %: Mg3Si2O5(OH)4 - 10-60; MgFe2O4 - 10-60; MoS2 - 1-20, сопутствующие редкоземельные элементы - 0,1-10, H2O - не более 5; предварительную механоактивацию можно проводить с пульсацией давления 0,01 - 10 МПа при 100-200oC.
Указанные границы параметров определяются следующими условиями. Присутствие в композиции менее 10 или более 60% Mg3Si2O5(OH)4 или MgFe2O4 значительно уменьшает скорость образования антифрикционного покрытия и отрицательно сказывается на его прочности. Уменьшение ниже 1% либо увеличение свыше 20% содержания MoS2 ухудшает антифрикционные качества покрытия. Присутствие в композиции редкоземельных элементов увеличивает коррозионную стойкость покрытия, а наличие в исходной композиции более 10% воды резко снижает ее. Пульсация давления от 0,01 до 10 МПа в процессе механоактивации позволяет достичь высокой степени дисперсности композиции в связующем, что значительно уменьшает скорость седиментации взвеси и тем самым повышает скорость образования и качество антифрикционного покрытия. Температурный диапазон от 100 до 200oC позволяет интенсивно испарять воду в процессе механоактивации, не нарушая структуру связующего.
Заявителем не выявлены какие-либо технические решения, идентичные настоящему изобретению, что позволяет сделать вывод о его соответствии критерию "новизна".
Реализация отличительных признаков изобретения обусловливает возникновение нового эффекта, заключающегося в следующем.
Ионы Mg занимают место ионов Fe в кристаллической решетке поверхностного слоя трущихся деталей ввиду большей активности Mg. При этом образуется основа, на которой формируется металлокерамическое антифрикционное покрытие, включающее три взаимосвязанных слоя: нижний, относительно мягкий, имеющий высокую степень адгезии с защищаемой поверхностью, промежуточный слой, являющийся базой для формирования внешнего слоя, поверхность которого представляет собой таблично-регулярную кристаллическую структуру. Благодаря этому повышается стабильность, прочность и долговечность антифрикционного покрытия, в том числе при повышенных механических и температурных воздействиях, повышается износостойкость трущихся поверхностей.
Заявителем не обнаружены какие-либо источники информации, которые содержали бы сведения о влиянии заявленных отличий на достигаемый результат, в связи с чем можно сделать вывод о его соответствии критерию "изобретательский уровень".
Заявленный способ реализуют следующим образом.
Пример.
В моторное масло с вязкостью по SAF 10W40 внесли 0,5 мас.% порошка, содержащего, мас.%:
Mg3Si2O5(OH)4 - 4O
MgFe2O4 - 40
MoS2 - 12
Редкоземельные элементы - 3
H2O - 5
Смесь механоактивировали между неподвижным и вращающимся перфорированными дисками с зазором 0,01 мм между ними и угловой скоростью до 150 м/с в течение 5 мин. При этом давление резко изменялось от 0,01 до 10 МПа, температура возросла от 20 до 200oC. Механоактивированную смесь ввели между образцом и контртелом машины 2070 СМТ-1 для испытания материалов на трение и износ.
Пары трения скольжения были изготовлены из стали марки 4Х13 твердостью HRC 60-64 по ГОСТ 2789-73. Контактная нагрузка составляла 160 кгс, скорость вращения образца поддерживалась 200 об/мин в течение 5 ч.
В результате прирост массы образца достиг 2,16•10-3 г, что связано с образованием антифрикционного покрытия. При этом коэффициент трения составил 0,01 для образца с покрытием и 0,063 для образца без покрытия. Относительный износ в результате формирования антифрикционного покрытия уменьшился в 52 раза.
Для пролонгации эффекта возможно периодическое внесение формирующего антифрикционное покрытие вещества. При этом периодичность определяется по изменению эксплуатационных параметров машин и механизмов.
Для реализации способа использованы распространенные природные минералы и обычное промышленное оборудование, что обусловливает соответствие изобретения критерию "промышленная применимость".

Claims (1)

1. Способ формирования антифрикционного покрытия контактирующих трущихся поверхностей, заключающийся в том, что между трущимися поверхностями размещают предварительно механоактивированную смесь размельченного формирующего антифрикционное покрытие вещества со связующим, отличающийся тем, что в качестве формирующего антифрикционное покрытие вещества используют композицию природных минералов, содержащую, мас.%:
Mg3Si2O5(OH)4 - 10 - 60
MgFe2О4 - 10 - 60
MoS2 - 1 - 20
Сопутствующие редкоземельные элементы - 0,1 - 10
Н2О - Не более 5
2. Способ по п.1, отличающийся тем, что предварительную механоактивацию проводят с пульсацией давления 0,01 - 10 МПа при 100 - 200oC.
RU2000110414/28A 2000-04-18 2000-04-18 Способ формирования антифрикционного покрытия контактирующих трущихся поверхностей RU2160856C1 (ru)