RU2107670C1 - Finishing composition - Google Patents
Finishing composition Download PDFInfo
- Publication number
- RU2107670C1 RU2107670C1 RU96110762A RU96110762A RU2107670C1 RU 2107670 C1 RU2107670 C1 RU 2107670C1 RU 96110762 A RU96110762 A RU 96110762A RU 96110762 A RU96110762 A RU 96110762A RU 2107670 C1 RU2107670 C1 RU 2107670C1
- Authority
- RU
- Russia
- Prior art keywords
- composition
- zinc oxide
- polyacrylamide
- chalk
- sodium tetraborate
- Prior art date
Abstract
Description
Изобретение относится к области строительных материалов, а именно к отдельным материалам для заделки щелей, трещин, углублений на деревянных, бетонных и оштукатуренных поверхностях, для ремонта деревянных изделий, для лепки и формования всевозможных поделок, объемных изображений при оформлении стендов, выставок, при отделке и оформлении интерьеров в помещениях, ремонте деревянной мебели и т.д. The invention relates to the field of building materials, namely, to individual materials for sealing cracks, cracks, indentations on wooden, concrete and plastered surfaces, for repairing wooden products, for sculpting and molding all kinds of crafts, three-dimensional images when decorating stands, exhibitions, decoration and interior decoration, repair of wooden furniture, etc.
Известна композиция [1] для отделочных работ следующего состава, мас.%:
Полиакриламид - 1,5 - 3
Мел - 10 - 30
Целлюлоза - 8 - 13
Оксид цинка - 2 - 3
Вода - Остальное
Указанный состав не обладает достаточной пластичностью, прочностью и формообразующей способностью.Known composition [1] for finishing work of the following composition, wt.%:
Polyacrylamide - 1.5 - 3
Chalk - 10 - 30
Cellulose - 8 - 13
Zinc oxide - 2 - 3
Water - Else
The specified composition does not have sufficient ductility, strength and shape-forming ability.
Наиболее близкой к предлагаемому техническому решению является композиция для отделочных работ [2] следующего состава, мас.%:
Полиакриламид - 1,5 - 3
Мел - 10 - 30
Оксид цинка - 1,0 - 3,0
Отходы бумажного производства - 15 - 25
Вода - Остальное
Известный состав имеет низкую адгезию к деревянным, бетонным и оштукатуренным поверхностям, недостаточную прочность и в процессе хранения изменяет свой цвет.Closest to the proposed technical solution is a composition for finishing work [2] of the following composition, wt.%:
Polyacrylamide - 1.5 - 3
Chalk - 10 - 30
Zinc Oxide - 1.0 - 3.0
Papermaking waste - 15 - 25
Water - Else
The known composition has low adhesion to wooden, concrete and plastered surfaces, insufficient strength and during storage changes color.
Задачей изобретения является создание средства, обладающего повышенной прочностью, высокими адгезионными свойствами к деревянным, бетонным, оштукатуренным поверхностям и стабильного по цвету при хранении. The objective of the invention is to provide a tool with high strength, high adhesive properties to wooden, concrete, plastered surfaces and color stable during storage.
Задача решается за счет того, что в композиции изменен процентный состав основных компонентов и дополнительно введен тетраборат натрия, при следующем соотношении компонентов, мас.%:
Полиакриламид - 1,5 - 3,0
Мел - 15 - 30
Оксид цинка - 1,0 - 2,0
Отходы бумажного производства - 10,0 - 15,0
Тетраборат натрия - 0,5 - 1,0
Вода - Остальное
В качестве связующего предложенная отделочная композиция содержит полиакриламид (ПАА), представляющий собой белый порошок без запаха, легко растворимый в воде и нерастворимый в спирте, эфирах и других органических растворителях. ПАА не токсичен, используется в промышленности для очистки промышленных и питьевых вод, для шлихтования пряжи перед ткачеством и выпускается промышленностью в виде 6-10%-ного водного геля по ТУ 6-01-1049-81 или ТУ 6-02-00209912-32-93. В качестве наполнителя состав содержит мел, выпускаемый, например, по ГОСТ 12085-73. Оксид цинка вводится для устранения расслоения состава и выделения на его поверхности различных веществ, растворимых в ПАА и попавших в него при производстве и транспортировке. Выпускается по ГОСТ 10262-73. Оксид цинка может быть заменен цинковыми белилами, представляющими собой порошкообразный продукт белого цвета, выпускаемый по ГОСТ 202-84. Отходы бумажного производства, называемые "скопом", вводятся в качестве целлюлозного наполнителя, придающего составу пластичность и формообразующую способность. Скоп получается в процессе улова и отжима на вакуум-фильтрах из сточных вод бумажного производства тонких фракций, размером 0,005-2,000 мм, бумажной массы и имеет следующий состав, мас.%:
Древесная целлюлоза - 15 - 20
Каолин - 5,0 - 10
Глинозем - 0,7 - 1,0
Канифоль - 0,05 - 0,3
Вода - Остальное
Тетраборат натрия используется для стабилизации цвета состава при хранении. В процессе хранения поверхность состава изменяется по цвету от белого до желто-коричневого, в результате чего ухудшается товарный внешний вид продукта. При добавлении тетрабората в состав сохраняется его белый цвет в течение длительного хранения. Выпускается по ГОСТ 8429-77.The problem is solved due to the fact that in the composition the percentage composition of the main components is changed and sodium tetraborate is additionally introduced, in the following ratio of components, wt.%:
Polyacrylamide - 1.5 - 3.0
Chalk - 15 - 30
Zinc oxide - 1.0 - 2.0
Papermaking waste - 10.0 - 15.0
Sodium tetraborate - 0.5 - 1.0
Water - Else
As a binder, the proposed finishing composition contains polyacrylamide (PAA), which is an odorless white powder, readily soluble in water and insoluble in alcohol, ethers and other organic solvents. PAA is non-toxic, it is used in industry for the treatment of industrial and drinking water, for sizing yarn before weaving and is produced by the industry in the form of a 6-10% aqueous gel according to TU 6-01-1049-81 or TU 6-02-00209912-32 -93. As a filler, the composition contains chalk produced, for example, according to GOST 12085-73. Zinc oxide is introduced to eliminate the separation of the composition and the release on its surface of various substances soluble in PAA and trapped in it during production and transportation. Available in accordance with GOST 10262-73. Zinc oxide can be replaced with zinc whitewash, which is a white powder product, produced in accordance with GOST 202-84. Papermaking waste called “osprey” is introduced as a cellulosic filler to impart plasticity and shape-forming ability to the composition. Osprey is obtained in the process of catching and spinning on vacuum filters from wastewater of paper production of fine fractions, size 0.005-2,000 mm, paper pulp and has the following composition, wt.%:
Wood pulp - 15 - 20
Kaolin - 5.0 - 10
Alumina - 0.7 - 1.0
Rosin - 0.05 - 0.3
Water - Else
Sodium tetraborate is used to stabilize the color of the composition during storage. During storage, the surface of the composition changes in color from white to tan, as a result of which the marketable appearance of the product worsens. When tetraborate is added to the composition, its white color is retained for long-term storage. Available in accordance with GOST 8429-77.
Композиция нетоксична при изготовлении и использовании. Готовят ее по несложной технологии. Весь процесс осуществляется в смесителе с Z-образными мешалками (типа СМ-400, СМ-800) следующим образом. В смеситель при непрерывной работе мешалок постепенно (порциями) загружают влажные бумажные отходы, после чего производят их мокрый перетир в смесителе в течение 20-30 мин. В процессе мокрого перетира происходит разбивание и перетир отдельных алгомерированных комочков - отходов бумажной массы на отдельные волокна. Затем в смеситель заливают гелеобразный полиакриламид с последующим перемешиванием в течение 30 мин. В полученную смесь загружают мел, оксид цинка, тетраборат натрия и смесь перемешивают до получения однородной пластичной массы. The composition is non-toxic in the manufacture and use. Prepare it for simple technology. The whole process is carried out in a mixer with Z-shaped mixers (type SM-400, SM-800) as follows. During continuous operation of the mixers, wet paper wastes are loaded into the mixer (in batches), after which they are wet milled in the mixer for 20-30 minutes. In the process of wet mashing, the individual algomerized lumps — waste paper pulp — are broken and milled into individual fibers. Then gelled polyacrylamide is poured into the mixer, followed by stirring for 30 minutes. Chalk, zinc oxide, sodium tetraborate are loaded into the resulting mixture and the mixture is stirred until a homogeneous plastic mass is obtained.
Примеры конкретного выполнения изобретения при различных соотношениях компонентов и их физико-химические показатели приведены в табл. 1 и 2. Examples of specific embodiments of the invention for various ratios of components and their physico-chemical characteristics are given in table. 1 and 2.
Благодаря своим свойствам состав может найти широкое применение при разнообразных строительных и отделочных работах, например при:
восстановлении поврежденных поверхностей, исправлении дефектов на изделиях из древесно-стружечных и древесно-волокнистых плит;
оформлении интерьеров;
заделке углублений, щелей, трещин на бетонных, деревянных, оштукатуренных поверхностях;
отделке и ремонте мебели, реставрации музейных экспонатов;
изготовлении всевозможных лепных изделий, поделок, игрушек;
приклеивании керамических плиток, в качестве дюбелей и др.Due to its properties, the composition can be widely used in a variety of construction and finishing works, for example, when:
restoration of damaged surfaces, correction of defects on products from chipboard and fiberboard;
interior design;
sealing cavities, cracks, cracks on concrete, wooden, plastered surfaces;
decoration and repair of furniture, restoration of museum exhibits;
the manufacture of all kinds of stucco products, crafts, toys;
gluing ceramic tiles, as dowels, etc.
Claims (1)
Полиакриламид - 1,5 - 3,0
Мел - 15 - 30
Оксид цинка - 1,0 - 2,0
Отходы бумажного производства - 10 - 15
Тетраборат натрия - 0,5 - 1,0
Вода - ОстальноеиComposition for finishing work, including polyacrylamide, chalk, zinc oxide, paper waste and water, characterized in that it additionally contains sodium tetraborate in the following ratio, wt.%:
Polyacrylamide - 1.5 - 3.0
Chalk - 15 - 30
Zinc oxide - 1.0 - 2.0
Papermaking waste - 10 - 15
Sodium tetraborate - 0.5 - 1.0
Water - Rest