RU2018144021A - Способ гидроконверсии тяжелого углеводородного сырья в суспензии - Google Patents
Способ гидроконверсии тяжелого углеводородного сырья в суспензии Download PDFInfo
- Publication number
- RU2018144021A RU2018144021A RU2018144021A RU2018144021A RU2018144021A RU 2018144021 A RU2018144021 A RU 2018144021A RU 2018144021 A RU2018144021 A RU 2018144021A RU 2018144021 A RU2018144021 A RU 2018144021A RU 2018144021 A RU2018144021 A RU 2018144021A
- Authority
- RU
- Russia
- Prior art keywords
- eleven
- integer
- range
- pmo
- simo
- Prior art date
Links
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J27/00—Catalysts comprising the elements or compounds of halogens, sulfur, selenium, tellurium, phosphorus or nitrogen; Catalysts comprising carbon compounds
- B01J27/14—Phosphorus; Compounds thereof
- B01J27/186—Phosphorus; Compounds thereof with arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
- B01J27/188—Phosphorus; Compounds thereof with arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium with chromium, molybdenum, tungsten or polonium
- B01J27/19—Molybdenum
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper
- B01J23/76—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
- B01J23/84—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36 with arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
- B01J23/85—Chromium, molybdenum or tungsten
- B01J23/88—Molybdenum
- B01J23/882—Molybdenum and cobalt
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper
- B01J23/76—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
- B01J23/84—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36 with arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
- B01J23/85—Chromium, molybdenum or tungsten
- B01J23/88—Molybdenum
- B01J23/883—Molybdenum and nickel
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/90—Regeneration or reactivation
- B01J23/94—Regeneration or reactivation of catalysts comprising metals, oxides or hydroxides of the iron group metals or copper
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J27/00—Catalysts comprising the elements or compounds of halogens, sulfur, selenium, tellurium, phosphorus or nitrogen; Catalysts comprising carbon compounds
- B01J27/02—Sulfur, selenium or tellurium; Compounds thereof
- B01J27/04—Sulfides
- B01J27/047—Sulfides with chromium, molybdenum, tungsten or polonium
- B01J27/049—Sulfides with chromium, molybdenum, tungsten or polonium with iron group metals or platinum group metals
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J27/00—Catalysts comprising the elements or compounds of halogens, sulfur, selenium, tellurium, phosphorus or nitrogen; Catalysts comprising carbon compounds
- B01J27/02—Sulfur, selenium or tellurium; Compounds thereof
- B01J27/04—Sulfides
- B01J27/047—Sulfides with chromium, molybdenum, tungsten or polonium
- B01J27/051—Molybdenum
- B01J27/0515—Molybdenum with iron group metals or platinum group metals
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/04—Mixing
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/20—Sulfiding
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
- C10G45/00—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds
- C10G45/02—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds to eliminate hetero atoms without changing the skeleton of the hydrocarbon involved and without cracking into lower boiling hydrocarbons; Hydrofinishing
- C10G45/04—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds to eliminate hetero atoms without changing the skeleton of the hydrocarbon involved and without cracking into lower boiling hydrocarbons; Hydrofinishing characterised by the catalyst used
- C10G45/06—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds to eliminate hetero atoms without changing the skeleton of the hydrocarbon involved and without cracking into lower boiling hydrocarbons; Hydrofinishing characterised by the catalyst used containing nickel or cobalt metal, or compounds thereof
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
- C10G45/00—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds
- C10G45/02—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds to eliminate hetero atoms without changing the skeleton of the hydrocarbon involved and without cracking into lower boiling hydrocarbons; Hydrofinishing
- C10G45/04—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds to eliminate hetero atoms without changing the skeleton of the hydrocarbon involved and without cracking into lower boiling hydrocarbons; Hydrofinishing characterised by the catalyst used
- C10G45/06—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds to eliminate hetero atoms without changing the skeleton of the hydrocarbon involved and without cracking into lower boiling hydrocarbons; Hydrofinishing characterised by the catalyst used containing nickel or cobalt metal, or compounds thereof
- C10G45/08—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds to eliminate hetero atoms without changing the skeleton of the hydrocarbon involved and without cracking into lower boiling hydrocarbons; Hydrofinishing characterised by the catalyst used containing nickel or cobalt metal, or compounds thereof in combination with chromium, molybdenum, or tungsten metals, or compounds thereof
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
- C10G45/00—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds
- C10G45/02—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds to eliminate hetero atoms without changing the skeleton of the hydrocarbon involved and without cracking into lower boiling hydrocarbons; Hydrofinishing
- C10G45/14—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds to eliminate hetero atoms without changing the skeleton of the hydrocarbon involved and without cracking into lower boiling hydrocarbons; Hydrofinishing with moving solid particles
- C10G45/16—Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds to eliminate hetero atoms without changing the skeleton of the hydrocarbon involved and without cracking into lower boiling hydrocarbons; Hydrofinishing with moving solid particles suspended in the oil, e.g. slurries
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
- C10G47/00—Cracking of hydrocarbon oils, in the presence of hydrogen or hydrogen- generating compounds, to obtain lower boiling fractions
- C10G47/02—Cracking of hydrocarbon oils, in the presence of hydrogen or hydrogen- generating compounds, to obtain lower boiling fractions characterised by the catalyst used
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J2523/00—Constitutive chemical elements of heterogeneous catalysts
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
- C10G2300/00—Aspects relating to hydrocarbon processing covered by groups C10G1/00 - C10G99/00
- C10G2300/20—Characteristics of the feedstock or the products
- C10G2300/201—Impurities
- C10G2300/205—Metal content
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
- C10G2300/00—Aspects relating to hydrocarbon processing covered by groups C10G1/00 - C10G99/00
- C10G2300/20—Characteristics of the feedstock or the products
- C10G2300/201—Impurities
- C10G2300/205—Metal content
- C10G2300/206—Asphaltenes
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
- C10G2300/00—Aspects relating to hydrocarbon processing covered by groups C10G1/00 - C10G99/00
- C10G2300/70—Catalyst aspects
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Organic Chemistry (AREA)
- Materials Engineering (AREA)
- Oil, Petroleum & Natural Gas (AREA)
- General Chemical & Material Sciences (AREA)
- Catalysts (AREA)
- Production Of Liquid Hydrocarbon Mixture For Refining Petroleum (AREA)
Claims (84)
1. Способ гидроконверсии в суспензии тяжелого углеводородного сырья в присутствии водорода и по меньшей мере одного диспергированного твердого катализатора, причем указанный, по меньшей мере один, диспергированный твердый катализатор получают из по меньшей мере одной соли гетерополианиона, объединяющей молибден и по меньшей мере один металл, выбранный из кобальта и никеля, в структуре типа Страндберга, типа Кеггина, лакунарнойго структуре типа Кеггина или замещеннойго лакунарнойго структуре типа Кеггина.
2. Способ по п. 1, причем по меньшей мере одна соль гетерополианиона соответствует:
следующей формуле M(6-x)/2HxP2MomWnO23 (I), в которой:
- M означает катион Ni2+ или катион Co2+,
- H означает водород,
- x представляет собой целое число в интервале от 0 до 2,
- P означает фосфор,
- Mo означает молибден,
- W означает вольфрам,
- m представляет собой целое число в интервале от 1 до 5,
- n представляет собой целое число в интервале от 0 до 4,
- m+n=5,
- O означает кислород,
- структура HxP2MomWnO23 является отрицательно заряженным гетерополианионом, причем его заряд равен x-6; или
следующей формуле CpXx/2AgMomWnX'zOyHh (II), в которой:
- C означает катион H+ и/или катион четвертичного аммония, замещенного или незамещенного,
- p представляет собой целое число в интервале от 0 до 6,
- X означает катион Ni2+ или катион Co2+,
- x представляет собой целое число в интервале от 0 до 11,
- p+x представляет собой целое число в интервале от 3 до 11,
- A означает фосфор, или кремний, или бор,
- g равно 0 или 1,
- Mo означает молибден,
- W означает вольфрам,
- m представляет собой целое число в интервале от 1 до 12,
- n представляет собой целое число в интервале от 0 до 11,
- m+n=9, или 11, или 12,
- X' означает элемент группы VIII периодической системы элементов,
- z равно 0 или 1,
- x+z представляет собой целое число, большее или равное 1,
- O означает кислород,
- y представляет собой целое число, равное 34, или 39, или 40,
- H означает водород,
- h представляет собой целое число в интервале от 0 до 3, и
- структура AgMomWnX'zOyHh является отрицательно заряженным гетерополианионом, причем его заряд равен -(p+x).
3. Способ по п. 1 или 2, в котором по меньшей мере одна соль гетерополианиона соответствует:
следующей формуле M(6-x)/2HxP2MomWnO23 (I), в которой:
- M означает катион Ni2+ или катион Co2+,
- H означает водород,
- x представляет собой целое число в интервале от 0 до 2,
- P означает фосфор,
- Mo означает молибден,
- W означает вольфрам,
- m представляет собой целое число в интервале от 3 до 5,
- n представляет собой целое число в интервале от 0 до 2,
- m+n=5,
- O означает кислород,
- структура HxP2MomWnO23 является отрицательно заряженным гетерополианионом, причем его заряд равен x-6; или
следующей формуле CpXx/2AgMomWnX'zOyHh (II), в которой:
- C означает катион H+ и/или катион четвертичного аммония, замещенного или незамещенного,
- p есть целое число в интервале от 0 до 2,
- X означает катион Ni2+ или катион Co2+,
- x представляет собой целое число в интервале от 3 до 8,
- p+x представляет собой целое число в интервале от 3 до 8,
- A означает фосфор или кремний,
- g равно 0 или 1,
- Mo означает молибден,
- W означает вольфрам,
- m представляет собой целое число в интервале от 9 до 12,
- n представляет собой целое число в интервале от 0 до 3,
- m+n=11 или 12,
- X' означает никель или кобальт,
- z равно 0 или 1,
- O означает кислород,
- y представляет собой целое число, равное 39 или 40,
- H означает водород,
- h представляет собой целое число в интервале от 0 до 2, и
- структура AgMomWnX'zOyHh является отрицательно заряженным гетерополианионом, причем его заряд равен -(p+x).
4. Способ по любому из предыдущих пунктов, причем указанная по меньшей мере одна соль гетерополианиона выбрана из следующих солей: Co2H2P2Mo5O23, Co5/2HP2Mo5O23, Co3P2Mo5O23, Ni2H2P2Mo5O23, Ni5/2HP2Mo5O23, Ni3P2Mo5O23, Ni3/2PMo12O40, Ni2SiMo12O40, Ni3Mo12O40H2, Ni4SiMo11O39, Ni7/2PMo11O39, Ni3SiMo11NiO40H2, Ni3PMo11NiO40H, Co3/2PMo12O40, Co2SiMo12O40, Co3Mo12O40H2, Co4SiMo11O39, Co7/2PMo11O39, Co3SiMo11CoO40H2, Co3SiMo11NiO40H2, Ni3SiMo11CoO40H2, Co3PMo11CoO40H, Co3PMo11NiO40H и Ni3PMo11CoO40H.
5. Способ по любому из предыдущих пунктов, причем указанная по меньшей мере одна соль гетерополианиона выбрана из следующих солей:: Ni2H2P2Mo5O23, Ni5/2HP2Mo5O23, Ni3P2Mo5O23, Ni4SiMo11O39, Ni7/2PMo11O39, Ni3SiMo11NiO40H2, Ni3PMo11NiO40H, Co4SiMo11O39, Co7/2PMo11O39, Co3SiMo11CoO40H2, Co3SiMo11NiO40H2, Ni3SiMo11CoO40H2, Co3PMo11CoO40H, Co3PMo11NiO40H и Ni3PMo11CoO40H.
6. Способ по любому из предыдущих пунктов, причем указанная по меньшей мере одна соль гетерополианиона выбрана из Ni2H2P2Mo5O23, Ni5/2HP2Mo5O23, Ni3P2Mo5O23, Ni4SiMo11O39, Ni7/2PMo11O39, Ni3SiMo11NiO40H2 и Ni3PMo11NiO40H.
7. Способ по любому из предыдущих пунктов, включающий по меньшей мере одну из следующих стадий:
a) приготовление водного раствора, содержащего по меньшей мере одну соль гетерополианиона,
b) предварительное смешение водного раствора с углеводородным маслом с получением разбавленной смеси предшественника,
c) смешение водного раствора, полученного на стадии a), или разбавленной смеси предшественника, полученной на стадии b), с тяжелым углеводородным сырьем для образования активной смеси, и
d) осуществление стадии гидроконверсии тяжелого углеводородного сырья путем введения указанного водного раствора, полученного на стадии a), или указанной разбавленной смеси предшественника, полученной на стадии b), или указанной активной смеси, полученной на стадии c), непосредственно в реактор гидроконверсии в суспензии или выше него по потоку.
8. Способ по любому из предыдущих пунктов, дополнительно включающий термическую обработку по меньшей мере одной соли гетерополианиона для образования по меньшей мере одного диспергированного твердого катализатора.
9. Способ по п. 8, где термическая обработка проводится в присутствии по меньшей мере одного сернистого соединения.
10. Способ по любому из предыдущих пунктов, где концентрация молибдена в указанном по меньшей мере одном диспергированном твердом катализаторе составляет от 10 до 10000 масс.ч./млн от веса тяжелого углеводородного сырья на входе в реактор.
11. Способ по любому из предыдущих пунктов, где стадия гидроконверсии проводится при абсолютном давлении от 2 до 38 МПа, и/или при температуре от 300°C до 500°C, и/или при объемной часовой скорости (VVHr) сырья, отнесенной к полному объему реактора, от 0,05 до 10 ч-1, и/или при количестве водорода, смешиваемого с тяжелым углеводородным сырьем, от 50 до 5000 нормальных кубических метров (Нм3) на кубический метр (м3) жидкого тяжелого углеводородного сырья.
12. Способ по любому из предыдущих пунктов, в котором гидроконверсию осуществляют в присутствии диспергированных твердых частиц.
13. Способ по п. 12, причем диспергированные твердые частицы выбраны из оксида алюминия, оксида кремния, алюмосиликата, диоксида титана, углерода, угля и кокса.
14. Способ по любому из предыдущих пунктов, в котором тяжелое углеводородное сырье содержит углеводороды, по меньшей мере 50 вес.% которых имеет температуру кипения выше 300°C, и по меньшей мере 1 вес.% которых имеет температуру кипения выше 540°C, серу при содержании более 0,1 вес.%, металлы при содержании более 20 масс.ч./млн и асфальтены C7 при содержании более 1 масс.%, в расчете на полный вес тяжелого углеводородного сырья.
15. Применение соли гетерополианиона для гидроконверсии в суспензии тяжелого углеводородного сырья в суспензионном реакторе, причем соль гетерополианиона объединяет молибден и по меньшей мере один металл, выбранный из кобальта и никеля, в структуре типа Страндберга, типа Кеггина, лакунарной структуре типа Кеггина или замещенной лакунарной структуре типа Кеггина.