RU2018108045A - Способ повышения вязкости при разрушении полиизоцианурат-содержащих продуктов реакции - Google Patents

Способ повышения вязкости при разрушении полиизоцианурат-содержащих продуктов реакции Download PDF

Info

Publication number
RU2018108045A
RU2018108045A RU2018108045A RU2018108045A RU2018108045A RU 2018108045 A RU2018108045 A RU 2018108045A RU 2018108045 A RU2018108045 A RU 2018108045A RU 2018108045 A RU2018108045 A RU 2018108045A RU 2018108045 A RU2018108045 A RU 2018108045A
Authority
RU
Russia
Prior art keywords
curable composition
paragraphs
mass
composition according
weight
Prior art date
Application number
RU2018108045A
Other languages
English (en)
Other versions
RU2018108045A3 (ru
RU2715566C2 (ru
Inventor
Стив Андре ВАУТТЕРС
Original Assignee
ХАНТСМЭН ИНТЕРНЭШНЛ ЭлЭлСи
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ХАНТСМЭН ИНТЕРНЭШНЛ ЭлЭлСи filed Critical ХАНТСМЭН ИНТЕРНЭШНЛ ЭлЭлСи
Publication of RU2018108045A publication Critical patent/RU2018108045A/ru
Publication of RU2018108045A3 publication Critical patent/RU2018108045A3/ru
Application granted granted Critical
Publication of RU2715566C2 publication Critical patent/RU2715566C2/ru

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/02—Polymeric products of isocyanates or isothiocyanates of isocyanates or isothiocyanates only
    • C08G18/022—Polymeric products of isocyanates or isothiocyanates of isocyanates or isothiocyanates only the polymeric products containing isocyanurate groups
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/40—High-molecular-weight compounds
    • C08G18/4009—Two or more macromolecular compounds not provided for in one single group of groups C08G18/42 - C08G18/64
    • C08G18/4045—Mixtures of compounds of group C08G18/58 with other macromolecular compounds
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/08—Processes
    • C08G18/09—Processes comprising oligomerisation of isocyanates or isothiocyanates involving reaction of a part of the isocyanate or isothiocyanate groups with each other in the reaction mixture
    • C08G18/092—Processes comprising oligomerisation of isocyanates or isothiocyanates involving reaction of a part of the isocyanate or isothiocyanate groups with each other in the reaction mixture oligomerisation to isocyanurate groups
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/08—Processes
    • C08G18/16—Catalysts
    • C08G18/161—Catalysts containing two or more components to be covered by at least two of the groups C08G18/166, C08G18/18 or C08G18/22
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/08—Processes
    • C08G18/16—Catalysts
    • C08G18/22—Catalysts containing metal compounds
    • C08G18/225—Catalysts containing metal compounds of alkali or alkaline earth metals
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/30—Low-molecular-weight compounds
    • C08G18/32—Polyhydroxy compounds; Polyamines; Hydroxyamines
    • C08G18/3203—Polyhydroxy compounds
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/40—High-molecular-weight compounds
    • C08G18/48—Polyethers
    • C08G18/4833—Polyethers containing oxyethylene units
    • C08G18/4837—Polyethers containing oxyethylene units and other oxyalkylene units
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/40—High-molecular-weight compounds
    • C08G18/48—Polyethers
    • C08G18/4833—Polyethers containing oxyethylene units
    • C08G18/4837—Polyethers containing oxyethylene units and other oxyalkylene units
    • C08G18/4845—Polyethers containing oxyethylene units and other oxyalkylene units containing oxypropylene or higher oxyalkylene end groups
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/40—High-molecular-weight compounds
    • C08G18/48—Polyethers
    • C08G18/4854—Polyethers containing oxyalkylene groups having four carbon atoms in the alkylene group
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/65—Low-molecular-weight compounds having active hydrogen with high-molecular-weight compounds having active hydrogen
    • C08G18/66—Compounds of groups C08G18/42, C08G18/48, or C08G18/52
    • C08G18/6666—Compounds of group C08G18/48 or C08G18/52
    • C08G18/667—Compounds of group C08G18/48 or C08G18/52 with compounds of group C08G18/32 or polyamines of C08G18/38
    • C08G18/6674—Compounds of group C08G18/48 or C08G18/52 with compounds of group C08G18/32 or polyamines of C08G18/38 with compounds of group C08G18/3203
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
    • C08G18/72—Polyisocyanates or polyisothiocyanates
    • C08G18/73—Polyisocyanates or polyisothiocyanates acyclic
    • C08G18/735—Polyisocyanates or polyisothiocyanates acyclic containing one isocyanate or isothiocyanate group linked to a primary carbon atom and at least one isocyanate or isothiocyanate group linked to a tertiary carbon atom
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
    • C08G18/72—Polyisocyanates or polyisothiocyanates
    • C08G18/74—Polyisocyanates or polyisothiocyanates cyclic
    • C08G18/75—Polyisocyanates or polyisothiocyanates cyclic cycloaliphatic
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
    • C08G18/72—Polyisocyanates or polyisothiocyanates
    • C08G18/74—Polyisocyanates or polyisothiocyanates cyclic
    • C08G18/76—Polyisocyanates or polyisothiocyanates cyclic aromatic
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
    • C08G18/72—Polyisocyanates or polyisothiocyanates
    • C08G18/74—Polyisocyanates or polyisothiocyanates cyclic
    • C08G18/76—Polyisocyanates or polyisothiocyanates cyclic aromatic
    • C08G18/7614—Polyisocyanates or polyisothiocyanates cyclic aromatic containing only one aromatic ring
    • C08G18/7621—Polyisocyanates or polyisothiocyanates cyclic aromatic containing only one aromatic ring being toluene diisocyanate including isomer mixtures
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G2115/00—Oligomerisation
    • C08G2115/02—Oligomerisation to isocyanurate groups
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G2120/00—Compositions for reaction injection moulding processes
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K11/00—Use of ingredients of unknown constitution, e.g. undefined reaction products
    • C08K11/005—Waste materials, e.g. treated or untreated sewage sludge
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K3/00—Use of inorganic substances as compounding ingredients
    • C08K3/01—Use of inorganic substances as compounding ingredients characterized by their specific function
    • C08K3/013—Fillers, pigments or reinforcing additives
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K7/00—Use of ingredients characterised by shape
    • C08K7/02—Fibres or whiskers
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K7/00—Use of ingredients characterised by shape
    • C08K7/22—Expanded, porous or hollow particles
    • C08K7/24—Expanded, porous or hollow particles inorganic
    • C08K7/28—Glass

Landscapes

  • Chemical & Material Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Polyurethanes Or Polyureas (AREA)

Claims (26)

1. Реакционноспособная отверждаемая композиция для изготовления полиизоцианурат-содержащих продуктов, имеющих температуру стеклования (Tg)>100°C, измеряемую согласно стандарту ASTM D 4065-1, получаемая комбинированием и смешиванием при изоцианатном индексе, равном, по меньшей мере, 100:
а) по меньшей мере, 40% масс. полиизоцианатов, в расчете на общую массу отверждаемой композиции, и
b) 1-30% масс. политетрагидрофурана (P-THF), имеющего среднюю молекулярную массу в диапазоне 1000-5000 г/моль в качестве агента, повышающего ударную вязкость, в расчете на общую массу отверждаемой композиции, и
с) по меньшей мере, 20% масс. низкомолекулярных полиолов, имеющих среднечисловую молекулярную массу <1000 г/моль, в расчете на общую массу отверждаемой композиции, и
d) каталитической композиции тримеризации, и
e) необязательно дополнительных добавок и/или вспомогательных соединений,
где % масс. ароматических колец углеводородов в отверждаемой композиции (ароматичность) составляет, по меньшей мере, 25% масс., в расчете на общую массу реакционноспособной отверждаемой композиции.
2. Отверждаемая композиция по п. 1, где количество полиизоцианатов в отверждаемой композиции составляет предпочтительно, по меньшей мере, 50% масс. полиизоцианатов, более предпочтительно, по меньшей мере, 60% масс. полиизоцианатов, в расчете на общую массу реакционноспособной отверждаемой композиции.
3. Отверждаемая композиция по любому из пп. 1-2, где ароматичность отверждаемой композиции составляет >30% масс., предпочтительно >35% масс., и более предпочтительно ≥50% масс., в расчете на общую массу реакционноспособной отверждаемой композиции.
4. Отверждаемая композиция по любому из пп. 1-3, где низкомолекулярные полиолы включают в себя ароматические полиолы, предпочтительно ароматические полиэфирполиолы на основе сложных эфиров, и более предпочтительно ароматические полиэфирдиолы на основе сложных эфиров.
5. Отверждаемая композиция по любому из пп. 1-4, где низкомолекулярные полиолы включают в себя диолы, имеющие молекулярную массу (MW) ниже 1000 г/моль, выбираемые из алкиленгликолей и/или оксиалкиленгликолей.
6. Отверждаемая композиция по любому из пп. 1-5, где диолы выбирают из полиэтиленгликоля и/или полипропиленгликоля -(1,2) и -(1,3), полибутиленгликоля -(1,4) и -(2,3), полигександиола -(1,6), полиоктандиола -(1,8) и их смесей.
7. Отверждаемая композиция по любому из пп. 1-6, где количество P-THF в отверждаемой композиции находится в диапазоне от 1% масс. до 25% масс., предпочтительно от 1% масс. до 15% масс., более предпочтительно от 1% масс. до 10% масс., в расчете на общую массу реакционноспособной отверждаемой полиизоцианатной композиции, и, где молекулярная масса P-THF находится в диапазоне 1000-3000, предпочтительно в диапазоне 1000-2000 г/моль.
8. Отверждаемая композиция по любому из пп. 1-7, где полиизоцианаты выбирают из алифатических, циклоалифатических, арилалифатических и, предпочтительно, ароматических полиизоцианатов, таких как толуол-диизоцианат в форме его 2,4- и 2,6-изомеров и их смесей, дифенилметан-диизоцианаты и их разновидности, и смеси дифенилметан-диизоцианатов (MDI) и также их олигомеры, которые имеют изоцианатную функциональность более 2.
9. Отверждаемая композиция по любому из пп. 1-8, где каталитическую композицию тримеризации выбирают из солей щелочных и/или щелочноземельных металлов и органических карбоновых кислот, предпочтительно имеющих 1-12 атомов углерода, таких как ацетат калия или 2-этилгексаноат калия, как например, ацетат калия, гексаноат калия, этилгексаноат калия, октаноат калия, лактат калия, этоксид натрия, формиат натрия, формиат калия, ацетат натрия, бензоат калия и их смеси.
10. Отверждаемая композиция по любому из пп. 1-9, где каталитическую композицию тримеризации выбирают из композиции, содержащей галогенид лития, предпочтительно LiCl, эпоксидную смолу и необязательно соединение мочевины.
11. Отверждаемая композиция по любому из пп. 1-10, где каталитическую композицию тримеризации используют в количестве от 0,001 до 10% масс., предпочтительно от 0,1 до 5% масс., наиболее предпочтительно 0,5-2,0% масс., в расчете на общую массу отверждаемой композиции.
12. Отверждаемая композиция по любому из пп. 1-11, где вспомогательные соединения выбирают из изоцианат-нереакционноспособных растворителей, поверхностно-активных веществ, скавенджеров, таких как алкил-ортоформиат и, в частности, три-изопропил-ортоформиат, противомикробных агентов, агентов, повышающих огнестойкость, противодымных агентов, УФ-стабилизаторов, окрашивающих агентов, пластификаторов, агентов, облегчающих выемку изделий из формы, модификаторов реологических свойств, смачивающих агентов, диспергирующих агентов и наполнителей.
13. Отверждаемая композиция по любому из пп. 1-12, где вспомогательные соединения включают материалы-наполнители, которые выбирают из древесной щепы, древесных опилок, древесной стружки, древесных пластинок; бумаги и картона, нарезанных или наслоенных; песка, вермикулита, глины, цемента и других силикатов; размолотого каучука (резины), размолотых термопластиков, размолотых термоотверждающихся материалов; сотовых материалов из любого материала, такого как картон, алюминий, древесина и пластики; металлических частиц и пластин; коры в форме частиц или в виде слоев; природных волокон, таких как льняные, пеньковые и лубяные волокна; синтетических волокон, таких как полиамидные, полиолефиновые, полиарамидные, поли(сложный эфир)ные и углеродные волокна; минеральных волокон, таких как стекловолокна и волокна каменной ваты; минеральных наполнителей, таких как BaSO4 and CaCO3; наночастиц, таких как глины, неорганические оксиды и угли; стеклянных гранул, размолотого стекла, полых стеклянных бусин; вспененных или вспениваемых гранул; необработанных или обработанных отходов, таких как измельченные, нарубленные, раздробленные или размолотые отходы и, в частности, летучая зола; тканых и нетканых текстильных материалов; и комбинаций двух или более материалов, выбираемых из упомянутых материалов.
14. Способ изготовления отверждаемой композиции по любому из пп. 1-13, который включает в себя комбинирование и смешивание ингредиентов (а)-(е) при давлении окружающей среды и при температуре от 5°С до 45°С и более предпочтительно от 5°С до 30°С.
15. Способ изготовления полиизоцианурат-содержащих материалов, имеющих температуру стеклования (Tg) > 100°С, измеренную согласно стандарту ASTM D 4065-1, и повышенное значение вязкости при разрушении G1c > 500 Дж/м2, полученное измерением согласно стандарту ISO 13586, где упомянутый способ включает в себя, по меньшей мере, стадии обеспечения протекания реакции в отверждаемой композиции по любому из п.п. 1-13 при изоцианатном индексе, равном, по меньшей мере, 100, и при температуре отверждения выше 50°С и предпочтительно выше 80°С.
16. Способ изготовления полиизоцианурат-содержащих материалов по п. 15, где упомянутый способ представляет собой периодический, полунепрерывный или непрерывный процесс, инжекционный, экструзионный, пултрузионный процесс формования или процесс формования, такой как процесс компрессионного (прямого) прессования, процесс литьевого прессования полимера, процесс формования с помощью вакуума, процесс пропитки связующим, процесс препрегирования.
17. Способ изготовления полиизоцианурат-содержащих материалов по любому из пп. 15-16, где изоцианатный индекс находится в диапазоне от 100 и вплоть до 15000, предпочтительно в диапазоне 100-500, более предпочтительно в диапазоне 100-300.
18. Способ изготовления полиизоцианурат-содержащих материалов по любому из пп. 15-17, где температура отверждения находится в диапазоне от 50°С до 350°С и наиболее предпочтительно в диапазоне от 90°С до 250°С.
19. Полиизоцианурат-содержащий материал, полученный способом по любому из пп. 15-18, имеющий температуру стеклования > 100°С, измеренную согласно стандарту ASTM D 4065-1, значение вязкости при разрушении G1c > 1000 Дж/м2, полученное измерением согласно стандарту ISO 13586, предпочтительно G1c > 1500 Дж/м2, и/или значение ударной вязкости K1c > 2 МПа⋅м1/2, полученное измерением согласно стандарту ISO 13586.
20. Полиизоцианурат-содержащий материал, полученный способом по любому из пп. 15-18, имеющий температуру стеклования > 150°С, измеренную согласно стандарту ASTM D 4065-1, значение вязкости при разрушении G1c > 500 Дж/м2, полученное измерением согласно стандарту ISO 13586, более предпочтительно G1c > 600 Дж/м2, и/или значение ударной вязкости K1c > 1 МПа⋅м1/2, полученное измерением согласно стандарту ISO 13586.
RU2018108045A 2015-08-07 2016-05-26 Способ повышения вязкости при разрушении полиизоцианурат-содержащих продуктов реакции RU2715566C2 (ru)