RU2012139823A - Новый пенобетон - Google Patents
Новый пенобетон Download PDFInfo
- Publication number
- RU2012139823A RU2012139823A RU2012139823/03A RU2012139823A RU2012139823A RU 2012139823 A RU2012139823 A RU 2012139823A RU 2012139823/03 A RU2012139823/03 A RU 2012139823/03A RU 2012139823 A RU2012139823 A RU 2012139823A RU 2012139823 A RU2012139823 A RU 2012139823A
- Authority
- RU
- Russia
- Prior art keywords
- foam concrete
- water
- foaming agent
- sulfate
- concrete according
- Prior art date
Abstract
1. Пенобетон с плотностью от 200 до 800 кг/м, содержащий по массе относительно общей массы бетона:- цемент;- воду;- от 0,01 до 5% добавки, снижающей водопотребность, пластификатора или суперпластификатора;- от 0,45 до 5%, пенообразователя относительно количества воды;- водорастворимую соль кальция, обладающую растворимостью в воде при 20°С более 2 г/100 мл;содержащий неорганические частицы размером от 0,1 до 300 мкм;при этом отношение пенообразователя к соли кальция составляет от 0,3 до 0,8; пенобетон содержит 10 мас.% или более шлака.2. Пенобетон по п.1, в котором неорганические частицы включают карбонат кальция, тонкий кремнеземный порошок, шлак, зольную пыль, пуццолан, стекло, кремнийсодержащие наполнители и их смеси.3. Пенобетон по п.1 или 2, плотность которого составляет от 300 до 700 кг/м.4. Пенобетон по п.1 или 2, отличающийся тем, что пенообразователь выбран из группы, в которую входят алкилсульфонат, алкилэфирсульфонат, гидроксиалкилэфирсульфонат, альфа-олефинсульфонат, алкилбензолсульфонат, алкилсульфат, алкилэфирсульфат, гидроксиалкилэфирсульфат, альфа-олефинсульфат и алкилбензолсульфат или их смеси.5. Пенобетон по п.1 или 2, отличающийся тем, что пенообразователь представляет собой алкилсульфат или алкилэфирсульфат формулыCH-(ОСНСН)-OSOMв которой n равно от 8 до 14, группа CHявляется нормальной или разветвленной, m составляет от 0 до 15, М означает щелочной металл.6. Пенобетон по п.1 или 2, отличающийся тем, что пенообразователь представляет собой нормальный или разветвленный алкилэфирсульфат формулы (1), указанной в п.5, в которой n равно от 10 до 15, m - от 1 до 6.7. Пенобетон по п.1 или 2, отличающийся тем, что пенообразователь представляет собой смесь а
Claims (15)
1. Пенобетон с плотностью от 200 до 800 кг/м3, содержащий по массе относительно общей массы бетона:
- цемент;
- воду;
- от 0,01 до 5% добавки, снижающей водопотребность, пластификатора или суперпластификатора;
- от 0,45 до 5%, пенообразователя относительно количества воды;
- водорастворимую соль кальция, обладающую растворимостью в воде при 20°С более 2 г/100 мл;
содержащий неорганические частицы размером от 0,1 до 300 мкм;
при этом отношение пенообразователя к соли кальция составляет от 0,3 до 0,8; пенобетон содержит 10 мас.% или более шлака.
2. Пенобетон по п.1, в котором неорганические частицы включают карбонат кальция, тонкий кремнеземный порошок, шлак, зольную пыль, пуццолан, стекло, кремнийсодержащие наполнители и их смеси.
3. Пенобетон по п.1 или 2, плотность которого составляет от 300 до 700 кг/м3.
4. Пенобетон по п.1 или 2, отличающийся тем, что пенообразователь выбран из группы, в которую входят алкилсульфонат, алкилэфирсульфонат, гидроксиалкилэфирсульфонат, альфа-олефинсульфонат, алкилбензолсульфонат, алкилсульфат, алкилэфирсульфат, гидроксиалкилэфирсульфат, альфа-олефинсульфат и алкилбензолсульфат или их смеси.
5. Пенобетон по п.1 или 2, отличающийся тем, что пенообразователь представляет собой алкилсульфат или алкилэфирсульфат формулы
CnH2n+1-(ОСН2СН2)m-OSO3M
в которой n равно от 8 до 14, группа CnH2n+1 является нормальной или разветвленной, m составляет от 0 до 15, М означает щелочной металл.
6. Пенобетон по п.1 или 2, отличающийся тем, что пенообразователь представляет собой нормальный или разветвленный алкилэфирсульфат формулы (1), указанной в п.5, в которой n равно от 10 до 15, m - от 1 до 6.
7. Пенобетон по п.1 или 2, отличающийся тем, что пенообразователь представляет собой смесь алкилэфирсульфата и алкилсульфата.
8. Пенобетон по п.1 или 2, отличающийся тем, что водорастворимая соль кальция выбрана из группы, в которую входят хлорид кальция, формиат кальция, нитрат кальция и их смеси.
9. Способ получения пенобетона по п.1, отличающийся тем, что он включает:
(а) смешивание
- цемента;
- воды;
- от 0,01 до 5% добавки, снижающей водопотребность, пластификатора или суперпластификатора;
- от 0,45 до 5% пенообразователя относительно количества воды;
- водорастворимой соли кальция, обладающей растворимостью в воде при 20°С более 2 г/100 мл;
- неорганических частиц размером от 0,1 до 300 мкм,
при этом отношение пенообразователя к соли кальция составляет от 0,3 до 0,8;
(b) подачу газа в смесь, полученную на стадии (а), с целью образования пенобетона; и необязательно
(c) формование пенобетона и обеспечение его схватывания.
10. Способ по п.9, отличающийся тем, что пенобетон, полученный на стадии (b), формуют и оставляют для схватывания с целью получения преформы; эту преформу нарезают на блоки.
11. Способ по п.9 или 10, отличающийся тем, что он не включает стадию автоклавирования.
12. Способ по п.9 или 10, в котором время до схватывания на стадии (с) составляет от 1 до 7 ч.
13. Способ получения пенобетона по п.9 или 10, отличающийся тем, что после стадии (с) пенобетон оставляют для затвердевания в атмосфере с регулируемой влажностью, относительная влажность которой превышает 80%.
14. Применение пенобетона по любому из пп.1-8 в строительстве.
15. Пенобетон по любому из пп.1-8 определенной формы.