RU2001121156A - Заготовка оптического волокна, имеющая барьер для радикала он, и способ ее изготовления - Google Patents
Заготовка оптического волокна, имеющая барьер для радикала он, и способ ее изготовленияInfo
- Publication number
- RU2001121156A RU2001121156A RU2001121156/03A RU2001121156A RU2001121156A RU 2001121156 A RU2001121156 A RU 2001121156A RU 2001121156/03 A RU2001121156/03 A RU 2001121156/03A RU 2001121156 A RU2001121156 A RU 2001121156A RU 2001121156 A RU2001121156 A RU 2001121156A
- Authority
- RU
- Russia
- Prior art keywords
- layer
- refractive index
- core
- optical fiber
- sio
- Prior art date
Links
- 239000003365 glass fiber Substances 0.000 title claims 20
- 238000004519 manufacturing process Methods 0.000 title claims 3
- 229910004298 SiO 2 Inorganic materials 0.000 claims 14
- 238000005253 cladding Methods 0.000 claims 14
- 239000000758 substrate Substances 0.000 claims 9
- 229910005793 GeO 2 Inorganic materials 0.000 claims 7
- 238000009792 diffusion process Methods 0.000 claims 5
- TUJKJAMUKRIRHC-UHFFFAOYSA-N hydroxyl radical Chemical compound [OH] TUJKJAMUKRIRHC-UHFFFAOYSA-N 0.000 claims 5
- 239000000463 material Substances 0.000 claims 5
- 238000000151 deposition Methods 0.000 claims 2
- 230000003287 optical Effects 0.000 claims 2
- 230000035515 penetration Effects 0.000 claims 2
- 241000283707 Capra Species 0.000 claims 1
- 230000015572 biosynthetic process Effects 0.000 claims 1
- 238000005755 formation reaction Methods 0.000 claims 1
- 238000007740 vapor deposition Methods 0.000 claims 1
Claims (20)
1. Заготовка оптического волокна, содержащая трубку-подложку, слой оболочки внутри трубки-подложки, слой сердцевины, размещенный внутри слоя оболочки, имеющий показатель преломления, больший чем показатель преломления слоя оболочки, и увеличивающийся по направлению к центру сердцевины, первый барьер, сформированный между трубкой-подложкой и слоем оболочки посредством осаждения материала с низким коэффициентом диффузии радикала ОН и предназначенный для предотвращения проникновения в слой оболочки радикала ОН, включенного в трубку-подложку, и второй барьер, сформированный между слоем оболочки и слоем сердцевины посредством осаждения материала с низким коэффициентом диффузии радикала ОН, для предотвращения проникновения в слой сердцевины радикала ОН, включенного в слой оболочки.
2. Заготовка оптического волокна по п.1, в которой первый или второй барьер формируется из состава, выбранного из группы, состоящей из SiO2 и SiO2+GeO2.
3. Заготовка оптического волокна по п.1, в которой первый или второй барьер формируется из состава, выбранного из группы, состоящей из SiO2 и SiO2+GeO2.
4. Заготовка оптического волокна по п.1, в которой первый или второй барьер имеет показатель преломления не больший, чем показатель преломления трубки-подложки и слоя сердцевины.
5. Заготовка оптического волокна по п.1, в которой отношение диаметра слоя оболочки к диаметру слоя сердцевины находится в пределах около от 1,1 до 3,0.
6. Заготовка оптического волокна по п.1, в которой показатель преломления на периферии слоя сердцевины находится в пределах приблизительно от 75 до 99% от показателя преломления в центре слоя сердцевины.
7. Способ изготовления заготовки оптического волокна, заключающийся в том, что формируют первый барьер посредством осаждения материала с низким коэффициентом диффузии радикала ОН на внутренней поверхности трубки-подложки, формируют слой оболочки на первом барьере, формируют второй барьер посредством осаждения материала с низким коэффициентом диффузии радикала ОН на слое оболочки и формируют слой сердцевины посредством осаждения так, чтобы он имел показатель преломления, возрастающий по направлению к центру слоя сердцевины, предназначенного для передачи оптического сигнала.
8. Способ по п.7, в котором дополнительно формируют второй барьер посредством осаждения материала с низким коэффициентом диффузии радикала ОН между формированием слоя оболочки и слоя сердцевины.
9. Способ по п.8, в котором первый или второй барьер формируют из состава, выбранного из группы, состоящей из SiO2 и SiO2+GeO2.
10. Заготовка оптического волокна, содержащая цилиндрическую сердцевину, показатель преломления которой плавно возрастает от периферии сердцевины к центру сердцевины, внутренний слой оболочки, окружающий сердцевину, содержащий SiO2 и являющийся свободным от Р2О5, причем показатель преломления внутреннего слоя оболочки меньше показателя преломления сердцевины, средний слой оболочки, окружающий внутренний слой оболочки и содержащий SiO2 и P2O5, причем показатель преломления среднего слоя оболочки меньше показателя преломления сердцевины и приблизительно равен показателю преломления внутреннего слоя оболочки, внешний слой оболочки, окружающий средний слой оболочки, содержащий SiO2 и являющийся свободным от P2O5, причем показатель преломления внешнего слоя оболочки меньше показателя преломления сердцевины и приблизительно равен показателю преломления внутреннего слоя оболочки, и трубку-подложку, окружающую внешний слой оболочки, имеющую показатель преломления выше показателей преломления внутреннего слоя оболочки, среднего слоя оболочки и внешнего слоя оболочки.
11. Заготовка оптического волокна по п.10, в которой внутренний слой оболочки дополнительно содержит GeO2 для регулировки показателя преломления внутреннего слоя оболочки.
12. Заготовка оптического волокна по п.10, в которой внешний слой оболочки дополнительно содержит GeO2 для регулировки показателя преломления внешнего слоя оболочки.
13. Заготовка оптического волокна по п.10, в которой показатель преломления на периферии сердцевины находится в диапазоне от 75 до 99% от показателя преломления в центре сердцевины.
14. Заготовка оптического волокна по п.10, в которой отношение диаметра внешнего слоя оболочки к диаметру слоя сердцевины находится в диапазоне приблизительно от 1,1 до 3,0.
15. Способ изготовления оптического волокна, заключающийся в том, что осаждают методом модифицированного осаждения из газовой фазы внешний слой оболочки, содержащий SiO2 и являющийся свободным от P2O5, на внутренней поверхности трубки-подложки, для создания внешнего слоя оболочки с более низким показателем преломления, чем у трубки-подложки; осаждают средний слой оболочки, содержащий SiO2 и P2O5, на внутренней поверхности внешнего слоя оболочки для создания среднего слоя оболочки с показателем преломления, приблизительно равным показателю преломления внешнего слоя оболочки, осаждают внутренний слой оболочки, содержащий SiO2 и являющийся свободным от Р2O5, на внутренней поверхности среднего слоя оболочки для создания внутреннего слоя оболочки с показателем преломления, приблизительно равным показателю преломления внешнего слоя оболочки и среднего слоя оболочки, осаждают слой сердцевины на внутренней поверхности внутреннего слоя оболочки, имеющий состав, изменяющийся от периферии к центру, для создания сердцевины, имеющей показатель преломления более высокий, чем показатель преломления внешнего слоя оболочки, среднего слоя оболочки и внутреннего слоя оболочки, и имеющий показатель преломления, плавно возрастающий от периферии сердцевины к центру сердцевины для предотвращения оптических потерь, обусловленных термическим напряжением в оптическом волокне, и осуществляют сжатие трубки-подложки с осажденными слоями для формирования заготовки оптического волокна.
16. Способ по п.15, в котором при осаждении внешнего слоя заготовки дополнительно осаждают GeO2 с SiO2 для управления показателем преломления внешнего слоя заготовки.
17. Способ по п.15, в котором при осаждении внутреннего слоя заготовки дополнительно осаждают GeO2 с SiO2 для управления показателем преломления внутреннего слоя заготовки.
18. Способ по п.15, в котором отношение диаметра внешнего слоя заготовки к диаметру слоя сердцевины заготовки оптического волокна находится в диапазоне приблизительно от 1,1 до 3,0.
19. Способ по п.15, в котором показатель преломления на периферии сердцевины заготовки оптического волокна находится в диапазоне от 75 до 99% от показателя преломления в центре сердцевины.
20. Способ по п.15, в котором дополнительно осуществляют быстрое вытягивание заготовки оптического волокна для формирования оптического волокна.