RU1801945C - Method of sodium silicate production showing molar ratio @@@=2, not less - Google Patents
Method of sodium silicate production showing molar ratio @@@=2, not lessInfo
- Publication number
- RU1801945C RU1801945C SU904905412A SU4905412A RU1801945C RU 1801945 C RU1801945 C RU 1801945C SU 904905412 A SU904905412 A SU 904905412A SU 4905412 A SU4905412 A SU 4905412A RU 1801945 C RU1801945 C RU 1801945C
- Authority
- RU
- Russia
- Prior art keywords
- molar ratio
- sodium silicate
- less
- mixture
- production showing
- Prior art date
Description
В источниках научно-технической информации описан способ получени высокомодульного жидкого стекла, включающий смешение аморфной двуокиси кремни с раствором низкомодульного жидкого стекла при нагревании от 40 до 100° С в течение времени, необходимого дл получени однородного процесса.Scientific and technical information sources describe a method for producing high-modulus liquid glass, comprising mixing amorphous silicon dioxide with a solution of low-modulus liquid glass by heating from 40 to 100 ° C for the time required to obtain a homogeneous process.
Однако известный признак нагревани смеси до 100° С способствует образованию поликристаллических силикатов натри , что снижает стабильность раствора и приводит к потери св зующих свойств продукта.However, the well-known sign of heating the mixture to 100 ° C promotes the formation of polycrystalline sodium silicates, which reduces the stability of the solution and leads to a loss of the binding properties of the product.
00
55
Claims (1)