PL440310A1 - Sposób otrzymywania nanocząstek węglika boru - Google Patents
Sposób otrzymywania nanocząstek węglika boruInfo
- Publication number
- PL440310A1 PL440310A1 PL440310A PL44031022A PL440310A1 PL 440310 A1 PL440310 A1 PL 440310A1 PL 440310 A PL440310 A PL 440310A PL 44031022 A PL44031022 A PL 44031022A PL 440310 A1 PL440310 A1 PL 440310A1
- Authority
- PL
- Poland
- Prior art keywords
- boron
- amorphous
- hours
- boron carbide
- layer
- Prior art date
Abstract
Przedmiotem zgłoszenia jest sposób otrzymywania nanocząstek węglika boru, w procesie syntezy bezpośredniej z proszków boru i węgla, które ogrzewa się w temperaturze 1400 - 1700°C, a następnie rozdrabnia. Sposób charakteryzuje się tym, że w tyglu grafitowym, na podkładce grafitowej, umieszcza się kolejno: warstwę proszku boru amorficznego, a następnie warstwę węgla w postaci amorficznej sadzy, przy czym stosunek boru amorficznego do amorficznej sadzy wynosi 4:1 i całość ogrzewa się przez 10 minut do 4 godzin. Z otrzymanego złoża produktu warstwę znajdującą się najniżej przy dnie tygla, wyróżniającą się jasno-szarą barwą i wykazującą największą zwięzłość i twardość, poddaje się intensywnemu mieleniu elementami stalowymi w środowisku izopropanolu przez okres 6 do 24 godzin, a następnie poddaje trawieniu chemicznemu, stosując kolejno: stężony HCl, następnie stężony HNO<sub>3</sub> i ponownie stężony HCl. Otrzymany proszek poddaje się wielokrotnemu przepłukiwaniu wodą destylowaną, aż do uzyskania pH zawiesiny wynoszącego od 6,5 – 7,5, a w końcowym etapie zawiesinę poddaje się intensywnemu wirowaniu przy ilości obrotów od 5000 do 12000 obr./min, z czasem wirowania wynoszącym od 5 minut do 4 godzin, uzyskując zaokrąglone ziarna węglika boru o wielkości od 50 do 200 nm.
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PL440310A PL440310A1 (pl) | 2022-02-07 | 2022-02-07 | Sposób otrzymywania nanocząstek węglika boru |
EP23154483.4A EP4223694A1 (en) | 2022-02-07 | 2023-02-01 | Method of obtaining boron carbide nanoparticles |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PL440310A PL440310A1 (pl) | 2022-02-07 | 2022-02-07 | Sposób otrzymywania nanocząstek węglika boru |
Publications (1)
Publication Number | Publication Date |
---|---|
PL440310A1 true PL440310A1 (pl) | 2023-08-14 |
Family
ID=85776065
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PL440310A PL440310A1 (pl) | 2022-02-07 | 2022-02-07 | Sposób otrzymywania nanocząstek węglika boru |
Country Status (2)
Country | Link |
---|---|
EP (1) | EP4223694A1 (pl) |
PL (1) | PL440310A1 (pl) |
Family Cites Families (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3914371A (en) | 1973-12-27 | 1975-10-21 | Us Energy | Method for preparing boron-carbide articles |
US4804525A (en) | 1986-04-14 | 1989-02-14 | The Dow Chemical Company | Producing boron carbide |
EP2125663A4 (en) * | 2007-02-22 | 2012-05-23 | Boron Compounds Ltd | PROCESS FOR PRODUCING CERAMIC MATERIALS |
CN105924175B (zh) * | 2016-04-21 | 2019-02-12 | 河北工程大学 | 一种细晶碳化硼陶瓷及其制备方法 |
CN111377449A (zh) * | 2018-12-28 | 2020-07-07 | 内蒙古元瓷新材料科技有限公司 | 一种碳化硼纳米颗粒的制备方法 |
CN110357106B (zh) * | 2019-08-26 | 2022-07-29 | 燕山大学 | 一种制备纳米孪晶碳化硼粉体的方法 |
-
2022
- 2022-02-07 PL PL440310A patent/PL440310A1/pl unknown
-
2023
- 2023-02-01 EP EP23154483.4A patent/EP4223694A1/en active Pending
Also Published As
Publication number | Publication date |
---|---|
EP4223694A1 (en) | 2023-08-09 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
Li et al. | Research of material removal and deformation mechanism for single crystal GGG (Gd3Ga5O12) based on varied-depth nanoscratch testing | |
JP6230106B2 (ja) | 炭化珪素単結晶の製造方法 | |
TW200923146A (en) | Low pressure method of annealing diamonds | |
CN100587118C (zh) | 一种直接在钢材上生长纳米晶氮化铬薄膜的方法 | |
PL440310A1 (pl) | Sposób otrzymywania nanocząstek węglika boru | |
Lv et al. | Effects of calcium sources and magnesium ions on the mechanical behavior of MICP-treated calcareous sand: experimental evidence and precipitated crystal insights | |
JP2011510894A (ja) | ナノダイヤモンドおよび炭素質材料からのナノダイヤモンド様粒子 | |
JP2019515864A (ja) | 多結晶立方晶窒化ホウ素及びその製造方法 | |
Xu et al. | Surface conversion reaction and high efficient grinding of CVD diamond films by chemically mechanical polishing | |
He et al. | Mechanical properties of nano-grain SiO2 glass prepared by spark plasma sintering | |
Zhou et al. | Polishing process of 4H-SiC under different pressures in a water environment | |
CN104862460B (zh) | 高碳铬轴承钢的复合热处理工艺 | |
Abdelsalam et al. | Effects of Al2O3, SiO2 nanoparticles, and g-C3N4 nanosheets on biocement production from agricultural wastes | |
Han et al. | Improvement of biomineralization of Sporosarcina pasteurii as biocementing material for concrete repair by atmospheric and room temperature plasma mutagenesis and response surface methodology | |
CN109943845A (zh) | 一种球化mmc复合涂层材料及其激光熔覆方法 | |
Wu et al. | Microstructure, phase composition and wear properties of iron-based gradient coatings by laser cladding on 65Mn steel | |
Lin et al. | Nanocrystalline diamond particles prepared by high-energy ball milling method | |
RU2223220C2 (ru) | Способ получения алмазных частиц, способ получения алмазных кристаллов и способ получения содержащих алмазные частицы заготовок | |
HUP0401137A2 (hu) | Eljárás kopásálló felületi bevonat készítésére, továbbá kopásálló bevonat készítésére alkalmas anyagösszetétel | |
JP2005075652A (ja) | サイアロン焼結体 | |
Laad | Extraction and characterization of silica from agro-waste for energy applications | |
Zhang et al. | A study of graphitization of free-cutting steel | |
CN104525861B (zh) | 发动机凸轮及其制备方法 | |
Shamelkhanova et al. | The Study of the Role of Fullerene Black Additive during the Modification of Ductile Cast Iron | |
Chen et al. | Recent development in diamond synthesis |