MX384876B - Método para producir un acero de alta resistencia laminado en caliente con conformabilidad del reborde elástico y rendimiento de fatiga del borde excelentes - Google Patents

Método para producir un acero de alta resistencia laminado en caliente con conformabilidad del reborde elástico y rendimiento de fatiga del borde excelentes

Info

Publication number
MX384876B
MX384876B MX2019003292A MX2019003292A MX384876B MX 384876 B MX384876 B MX 384876B MX 2019003292 A MX2019003292 A MX 2019003292A MX 2019003292 A MX2019003292 A MX 2019003292A MX 384876 B MX384876 B MX 384876B
Authority
MX
Mexico
Prior art keywords
edge
hot
producing
strength steel
rolled high
Prior art date
Application number
MX2019003292A
Other languages
English (en)
Spanish (es)
Other versions
MX2019003292A (es
Inventor
Andrew Paul Vass
Maxim Peter Aarnts
Paul Joseph Bellina
Rolf Arjan Rijkenberg
Original Assignee
Tata Steel Ijmuiden Bv
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tata Steel Ijmuiden Bv filed Critical Tata Steel Ijmuiden Bv
Publication of MX2019003292A publication Critical patent/MX2019003292A/es
Publication of MX384876B publication Critical patent/MX384876B/es

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/52—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for wires; for strips ; for rods of unlimited length
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/005—Heat treatment of ferrous alloys containing Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/008—Heat treatment of ferrous alloys containing Si
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/24—Ferrous alloys, e.g. steel alloys containing chromium with vanadium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/60—Ferrous alloys, e.g. steel alloys containing lead, selenium, tellurium, or antimony, or more than 0.04% by weight of sulfur
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/001—Austenite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/004—Dispersions; Precipitations
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
MX2019003292A 2016-09-22 2017-09-22 Método para producir un acero de alta resistencia laminado en caliente con conformabilidad del reborde elástico y rendimiento de fatiga del borde excelentes MX384876B (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP16190061 2016-09-22
PCT/EP2017/074072 WO2018055098A1 (en) 2016-09-22 2017-09-22 A method of producing a hot-rolled high-strength steel with excellent stretch-flange formability and edge fatigue performance

Publications (2)

Publication Number Publication Date
MX2019003292A MX2019003292A (es) 2019-05-20
MX384876B true MX384876B (es) 2025-03-14

Family

ID=57083103

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2019003292A MX384876B (es) 2016-09-22 2017-09-22 Método para producir un acero de alta resistencia laminado en caliente con conformabilidad del reborde elástico y rendimiento de fatiga del borde excelentes

Country Status (10)

Country Link
US (1) US11242579B2 (enExample)
EP (1) EP3516085B1 (enExample)
JP (1) JP7077309B2 (enExample)
KR (1) KR102473782B1 (enExample)
CN (1) CN109790595B (enExample)
BR (1) BR112019002826B1 (enExample)
CA (1) CA3034549A1 (enExample)
ES (1) ES2808342T3 (enExample)
MX (1) MX384876B (enExample)
WO (1) WO2018055098A1 (enExample)

Families Citing this family (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019215132A1 (en) 2018-05-08 2019-11-14 Tata Steel Ijmuiden B.V. Steel strip, sheet or blank having improved formability and method to produce such strip
CN109147873B (zh) * 2018-07-13 2021-09-21 江西理工大学 一种预测微合金钢焊接粗晶区晶粒尺寸的方法
PT3927858T (pt) * 2019-02-18 2022-10-27 Tata Steel Ijmuiden Bv Aço de alta resistência com propriedades mecânicas melhoradas
CZ308471B6 (cs) * 2019-08-19 2020-09-02 Západočeská Univerzita V Plzni Způsob výroby ocelových dílů z AHS oceli řízeným lokálním ochlazováním médiem, využívající tvorbu vícefázové struktury s přerušovaným chlazením na požadované teplotě
EP4118250A1 (en) 2020-03-13 2023-01-18 Tata Steel IJmuiden B.V. Hot rolled steel strip having improved properties
KR102397583B1 (ko) * 2020-09-25 2022-05-13 주식회사 포스코 연신율이 우수한 고강도 후물 열연강판 및 그 제조방법
DE102021104584A1 (de) 2021-02-25 2022-08-25 Salzgitter Flachstahl Gmbh Hochfestes, warmgewalztes Stahlflachprodukt mit hoher lokaler Kaltumformbarkeit sowie ein Verfahren zur Herstellung eines solchen Stahlflachprodukts
US20260028705A1 (en) * 2022-08-09 2026-01-29 Tata Steel Ijmuiden B.V. Hot-rolled high-strength steel strip
KR20240080209A (ko) * 2022-11-28 2024-06-07 주식회사 포스코 다단프레스 성형성이 우수한 열연강판 및 이의 제조방법
EP4663804A1 (en) 2024-06-14 2025-12-17 voestalpine Stahl GmbH Micro-alloyed hot rolled strip with improved formability, up to 700 mpa
EP4663803A1 (en) 2024-06-14 2025-12-17 voestalpine Stahl GmbH Micro-alloyed hot rolled strip with improved formability, above 700 mpa
EP4703482A1 (de) 2024-09-03 2026-03-04 ThyssenKrupp Steel Europe AG Warmgewalztes stahlflachprodukt und verfahren zu seiner herstellung

Family Cites Families (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3945180B2 (ja) * 2000-04-13 2007-07-18 住友金属工業株式会社 穴広げ性および延性が優れた高強度合金化溶融亜鉛めっき鋼板および高強度鋼板と、それらの製造方法
WO2002036840A1 (fr) 2000-10-31 2002-05-10 Nkk Corporation Tole d"acier laminee a chaud presentant une resistance elevee a la traction et procede de fabrication
JP3887300B2 (ja) 2002-11-12 2007-02-28 新日本製鐵株式会社 成形性と溶接後処理性に優れた高強度鋼板
JP4555694B2 (ja) * 2005-01-18 2010-10-06 新日本製鐵株式会社 加工性に優れる焼付け硬化型熱延鋼板およびその製造方法
JP4819489B2 (ja) * 2005-11-25 2011-11-24 Ｊｆｅスチール株式会社 一様伸び特性に優れた高強度鋼板およびその製造方法
JP4803108B2 (ja) 2007-05-21 2011-10-26 住友金属工業株式会社 高強度熱延鋼板及びその製造方法
US8657970B2 (en) 2008-03-26 2014-02-25 Nippon Steel & Sumitomo Metal Corporation Hot-rolled steel sheet excellent in fatigue properties and stretch-flange formability and method for manufacturing the same
KR101109953B1 (ko) * 2008-09-29 2012-02-24 현대제철 주식회사 연신율과 신장플랜지성이 우수한 고장력 열연강판 및 그 제조방법
JP5041083B2 (ja) * 2010-03-31 2012-10-03 Ｊｆｅスチール株式会社 加工性に優れた高張力溶融亜鉛めっき鋼板およびその製造方法
JP5041084B2 (ja) * 2010-03-31 2012-10-03 Ｊｆｅスチール株式会社 加工性に優れた高張力熱延鋼板およびその製造方法
BR112013023633A2 (pt) 2011-03-18 2016-12-13 Nippon Steel & Sumitomo Metal Corp chapa de aço laminada a quente com excelente capacidade de conformação por prensagem e seu método de produção
JP5838796B2 (ja) * 2011-12-27 2016-01-06 Ｊｆｅスチール株式会社 伸びフランジ性に優れた高強度熱延鋼板およびその製造方法
JP5994356B2 (ja) * 2012-04-24 2016-09-21 Ｊｆｅスチール株式会社 形状凍結性に優れた高強度薄鋼板およびその製造方法
CA2872728C (en) * 2012-05-08 2018-11-06 Tata Steel Ijmuiden B.V. Automotive chassis part made from high strength formable hot rolled steel sheet
JP5821864B2 (ja) * 2013-01-31 2015-11-24 Ｊｆｅスチール株式会社 バーリング加工性に優れた高強度熱延鋼板およびその製造方法
EP2954074B1 (en) 2013-02-11 2018-10-31 Tata Steel IJmuiden BV A high-strength hot-rolled steel strip or sheet with excellent formability and fatigue performance and a method of manufacturing said steel strip or sheet
US20160068937A1 (en) * 2013-04-15 2016-03-10 Jfe Steel Corporation High-strength hot-rolled steel sheet and method for producing the same (as amended)
KR20150025952A (ko) 2013-08-30 2015-03-11 현대제철 주식회사 고강도 열연도금강판 및 그 제조 방법
KR102079968B1 (ko) * 2015-07-31 2020-02-21 닛폰세이테츠 가부시키가이샤 고강도 열연 강판
KR102010358B1 (ko) 2018-07-02 2019-08-14 김경훈 형강 파일 인발기

Also Published As

Publication number Publication date
KR20190058476A (ko) 2019-05-29
CN109790595A (zh) 2019-05-21
CA3034549A1 (en) 2018-03-29
WO2018055098A1 (en) 2018-03-29
BR112019002826A2 (pt) 2019-05-21
CN109790595B (zh) 2021-01-26
US11242579B2 (en) 2022-02-08
US20190352736A1 (en) 2019-11-21
JP2019533082A (ja) 2019-11-14
EP3516085A1 (en) 2019-07-31
KR102473782B1 (ko) 2022-12-02
JP7077309B2 (ja) 2022-05-30
ES2808342T3 (es) 2021-02-26
BR112019002826B1 (pt) 2022-12-13
MX2019003292A (es) 2019-05-20
EP3516085B1 (en) 2020-07-08

Similar Documents

Publication Publication Date Title
MX2019003292A (es) Método para producir un acero de alta resistencia laminado en caliente con conformabilidad del reborde elástico y rendimiento de fatiga del borde excelentes.
TR201906728T4 (tr) Mükemmel germe ile flanş şekillendirilebilirliğine sahip sıcak haddelenmiş yüksek dayanımlı haddeleme ile biçimlendirilebilir bir çelik levha ve söz konusu çeliğin üretilmesine yönelik bir yöntem.
PL2907886T3 (pl) Blacha stalowa cienka walcowana na gorąco o dużej wytrzymałości mająca maksymalną wytrzymałość na rozciąganie wynoszącą 980 MPa lub więcej oraz mająca doskonałą utwardzalność przy wypalaniu i wiązkość w niskiej temperaturze
MX2018014325A (es) Metodo para producir una hoja de acero twip que tiene una microestructura austenitica.
MX2020006445A (es) Lamina de acero de alta resistencia que tiene excelentes propiedades de impacto y formabilidad y metodo para manufacturarla.
EP3279363A4 (en) HIGH-STRENGTH COLD-ROLLED STEEL SHEET HAVING EXCELLENT WORKABILITY AND COLLISION CHARACTERISTICS AND HAVING TENSILE STRENGTH OF 980 MPa OR MORE, AND METHOD FOR PRODUCING SAME
MX2018009735A (es) Lamina de acero de alta resistencia y metodo para fabricar la misma.
PL3394300T3 (pl) Sposób wytwarzania blachy stalowej o wysokiej wytrzymałości, mającej ulepszoną ciągliwość i odkształcalność oraz otrzymana blacha stalowa
MX387894B (es) Lamina de acero de alta resistencia y metodo de produccion para la misma, y metodo de produccion para lamina de acero galvanizada de alta resistencia.
MX2017009931A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma.
MX2016008809A (es) Miembro formado en caliente y proceso para manufacturar el mismo.
MX355894B (es) Lamina de acero, lamina de acero chapada, y metodo para producir la misma.
MX2016009745A (es) Lamina de acero laminada en frio de alta resistencia y metodo para la fabricacion de la misma.
UA120059C2 (uk) Основа кузова транспортного засобу і кузов транспортного засобу
MX2019002337A (es) Lamina de acero de alta resistencia y metodo para su fabricacion.
MX394890B (es) Lámina de acero laminada en caliente de alta resistencia y método de fabricación de la misma.
UA113529C2 (xx) Мартенситні сталі з міцністю при розтягуванні 1700-2200 мпа
MX2017009930A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma.
MX2017009935A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma.
BR112017019947A2 (pt) chapa de aço para prensagem a quente e método para produção da mesma
MX2019010315A (es) Producto semiacabado plano de acero, procedimiento para la produccion de un componente y uso.
MX378644B (es) Acero y metodo para fabricarlo.
MX2016007589A (es) Metodo para producir acero inxoidable duplex de alta resistencia.
SE1650923A1 (en) An elongate weld and a beam having such a weld
MX2015009890A (es) Una tira o lamina de acero de alta resistencia laminada de caliente con excelente conformabilidad y rendimiento y un metodo de fabricacion de dicha tira o lamina de acero.