CN109790595B - 一种具有优异的外卷边成形性和边缘疲劳性能的热轧高强度钢的制备方法 - Google Patents

一种具有优异的外卷边成形性和边缘疲劳性能的热轧高强度钢的制备方法 Download PDF

Info

Publication number
CN109790595B
CN109790595B CN201780058098.8A CN201780058098A CN109790595B CN 109790595 B CN109790595 B CN 109790595B CN 201780058098 A CN201780058098 A CN 201780058098A CN 109790595 B CN109790595 B CN 109790595B
Authority
CN
China
Prior art keywords
ferrite
hec
steel
tensile strength
hot
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201780058098.8A
Other languages
English (en)
Chinese (zh)
Other versions
CN109790595A (zh
Inventor
R·A·赖肯伯格
M·P·阿尔恩特斯
P·J·贝利纳
A·P·瓦斯
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tata Steel Ijmuiden BV
Original Assignee
Tata Steel Ijmuiden BV
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tata Steel Ijmuiden BV filed Critical Tata Steel Ijmuiden BV
Publication of CN109790595A publication Critical patent/CN109790595A/zh
Application granted granted Critical
Publication of CN109790595B publication Critical patent/CN109790595B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/52—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for wires; for strips ; for rods of unlimited length
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/005—Heat treatment of ferrous alloys containing Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/008—Heat treatment of ferrous alloys containing Si
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0205—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/24—Ferrous alloys, e.g. steel alloys containing chromium with vanadium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/60—Ferrous alloys, e.g. steel alloys containing lead, selenium, tellurium, or antimony, or more than 0.04% by weight of sulfur
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/001—Austenite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/004—Dispersions; Precipitations
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
CN201780058098.8A 2016-09-22 2017-09-22 一种具有优异的外卷边成形性和边缘疲劳性能的热轧高强度钢的制备方法 Active CN109790595B (zh)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
EP16190061.8 2016-09-22
EP16190061 2016-09-22
PCT/EP2017/074072 WO2018055098A1 (en) 2016-09-22 2017-09-22 A method of producing a hot-rolled high-strength steel with excellent stretch-flange formability and edge fatigue performance

Publications (2)

Publication Number Publication Date
CN109790595A CN109790595A (zh) 2019-05-21
CN109790595B true CN109790595B (zh) 2021-01-26

Family

ID=57083103

Family Applications (1)

Application Number Title Priority Date Filing Date
CN201780058098.8A Active CN109790595B (zh) 2016-09-22 2017-09-22 一种具有优异的外卷边成形性和边缘疲劳性能的热轧高强度钢的制备方法

Country Status (10)

Country Link
US (1) US11242579B2 (enExample)
EP (1) EP3516085B1 (enExample)
JP (1) JP7077309B2 (enExample)
KR (1) KR102473782B1 (enExample)
CN (1) CN109790595B (enExample)
BR (1) BR112019002826B1 (enExample)
CA (1) CA3034549A1 (enExample)
ES (1) ES2808342T3 (enExample)
MX (1) MX384876B (enExample)
WO (1) WO2018055098A1 (enExample)

Families Citing this family (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3791000B1 (en) 2018-05-08 2023-08-09 Tata Steel IJmuiden B.V. Steel strip, sheet or blank having improved formability and method to produce such strip
CN109147873B (zh) * 2018-07-13 2021-09-21 江西理工大学 一种预测微合金钢焊接粗晶区晶粒尺寸的方法
JP2022520485A (ja) 2019-02-18 2022-03-30 タタ、スティール、アイモイデン、ベスローテン、フェンノートシャップ 機械的特性が改善された高強度鋼
CZ2019542A3 (cs) * 2019-08-19 2020-09-02 Západočeská Univerzita V Plzni Způsob výroby ocelových dílů z AHS oceli řízeným lokálním ochlazováním médiem, využívající tvorbu vícefázové struktury s přerušovaným chlazením na požadované teplotě
US12385114B2 (en) 2020-03-13 2025-08-12 Tata Steel Ijmuiden B.V. Hot rolled steel strip having improved properties
KR102397583B1 (ko) * 2020-09-25 2022-05-13 주식회사 포스코 연신율이 우수한 고강도 후물 열연강판 및 그 제조방법
DE102021104584A1 (de) 2021-02-25 2022-08-25 Salzgitter Flachstahl Gmbh Hochfestes, warmgewalztes Stahlflachprodukt mit hoher lokaler Kaltumformbarkeit sowie ein Verfahren zur Herstellung eines solchen Stahlflachprodukts
CN119677880A (zh) * 2022-08-09 2025-03-21 塔塔钢铁艾默伊登有限责任公司 热轧高强度钢带材
KR20240080209A (ko) * 2022-11-28 2024-06-07 주식회사 포스코 다단프레스 성형성이 우수한 열연강판 및 이의 제조방법
EP4663803A1 (en) 2024-06-14 2025-12-17 voestalpine Stahl GmbH Micro-alloyed hot rolled strip with improved formability, above 700 mpa
EP4663804A1 (en) 2024-06-14 2025-12-17 voestalpine Stahl GmbH Micro-alloyed hot rolled strip with improved formability, up to 700 mpa

Family Cites Families (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3945180B2 (ja) * 2000-04-13 2007-07-18 住友金属工業株式会社 穴広げ性および延性が優れた高強度合金化溶融亜鉛めっき鋼板および高強度鋼板と、それらの製造方法
CA2395901C (en) 2000-10-31 2006-07-18 Nkk Corporation High strength hot rolled steel sheet and method for manufacturing the same
JP3887300B2 (ja) 2002-11-12 2007-02-28 新日本製鐵株式会社 成形性と溶接後処理性に優れた高強度鋼板
JP4555694B2 (ja) * 2005-01-18 2010-10-06 新日本製鐵株式会社 加工性に優れる焼付け硬化型熱延鋼板およびその製造方法
JP4819489B2 (ja) * 2005-11-25 2011-11-24 Ｊｆｅスチール株式会社 一様伸び特性に優れた高強度鋼板およびその製造方法
JP4803108B2 (ja) 2007-05-21 2011-10-26 住友金属工業株式会社 高強度熱延鋼板及びその製造方法
BRPI0822384B1 (pt) 2008-03-26 2020-06-09 Nippon Steel & Sumitomo Metal Corp folha de aço laminada a quente excelente em propriedades de fadiga e formabilidade de flange por esticamento, e método para a fabricação da mesma
KR101109953B1 (ko) * 2008-09-29 2012-02-24 현대제철 주식회사 연신율과 신장플랜지성이 우수한 고장력 열연강판 및 그 제조방법
JP5041084B2 (ja) * 2010-03-31 2012-10-03 Ｊｆｅスチール株式会社 加工性に優れた高張力熱延鋼板およびその製造方法
JP5041083B2 (ja) * 2010-03-31 2012-10-03 Ｊｆｅスチール株式会社 加工性に優れた高張力溶融亜鉛めっき鋼板およびその製造方法
US10428409B2 (en) 2011-03-18 2019-10-01 Nippon Steel Corporation Hot-rolled steel sheet with excellent press formability and production method thereof
JP5838796B2 (ja) * 2011-12-27 2016-01-06 Ｊｆｅスチール株式会社 伸びフランジ性に優れた高強度熱延鋼板およびその製造方法
JP5994356B2 (ja) * 2012-04-24 2016-09-21 Ｊｆｅスチール株式会社 形状凍結性に優れた高強度薄鋼板およびその製造方法
CA2872728C (en) 2012-05-08 2018-11-06 Tata Steel Ijmuiden B.V. Automotive chassis part made from high strength formable hot rolled steel sheet
JP5821864B2 (ja) * 2013-01-31 2015-11-24 Ｊｆｅスチール株式会社 バーリング加工性に優れた高強度熱延鋼板およびその製造方法
BR112015018058A2 (pt) * 2013-02-11 2017-07-18 Tata Steel Ijmuiden Bv tira ou chapa de aço laminada a quente de alta resistência com excelente capacidade de conformação e performance de fadiga e método de produção da mencionada tira ou chapa
WO2014171062A1 (ja) * 2013-04-15 2014-10-23 Ｊｆｅスチール株式会社 高強度熱延鋼板およびその製造方法
KR20150025952A (ko) 2013-08-30 2015-03-11 현대제철 주식회사 고강도 열연도금강판 및 그 제조 방법
BR112018000633A2 (pt) * 2015-07-31 2018-09-18 Nippon Steel & Sumitomo Metal Corporation chapa de aço laminada a quente de alta resistência
KR102010358B1 (ko) 2018-07-02 2019-08-14 김경훈 형강 파일 인발기

Also Published As

Publication number Publication date
JP7077309B2 (ja) 2022-05-30
BR112019002826A2 (pt) 2019-05-21
EP3516085B1 (en) 2020-07-08
EP3516085A1 (en) 2019-07-31
MX384876B (es) 2025-03-14
JP2019533082A (ja) 2019-11-14
CN109790595A (zh) 2019-05-21
KR102473782B1 (ko) 2022-12-02
US11242579B2 (en) 2022-02-08
BR112019002826B1 (pt) 2022-12-13
KR20190058476A (ko) 2019-05-29
CA3034549A1 (en) 2018-03-29
MX2019003292A (es) 2019-05-20
ES2808342T3 (es) 2021-02-26
US20190352736A1 (en) 2019-11-21
WO2018055098A1 (en) 2018-03-29

Similar Documents

Publication Publication Date Title
CN109790595B (zh) 一种具有优异的外卷边成形性和边缘疲劳性能的热轧高强度钢的制备方法
EP3584337B1 (en) High strength hot-rolled steel sheet and method for producing same
CN108350542B (zh) 具有优异的拉伸凸缘成形性的热轧高强度可轧制成形钢片材和制造所述钢的方法
KR102226643B1 (ko) 강판 및 그 제조 방법
EP2824210B1 (en) High-strength cold-rolled steel sheet and process for manufacturing same
JP6852736B2 (ja) 溶融亜鉛めっき冷延鋼板
JP6628682B2 (ja) 加工性に優れた高強度ステンレス鋼板およびその製造方法
CN113166893B (zh) 耐久性优异的高强度钢材及其制造方法
JP4901623B2 (ja) 打ち抜き穴広げ性に優れた高強度薄鋼板およびその製造方法
US12049687B2 (en) High-strength steel having high yield ratio and excellent durability, and method for manufacturing same
KR102098482B1 (ko) 내충돌 특성이 우수한 고강도 강판 및 이의 제조방법
US20230120827A1 (en) High strength steel sheet and method of producing same
JP7168137B1 (ja) 高強度鋼板およびその製造方法
US12180571B2 (en) High-strength cold rolled steel sheet and galvannealed steel sheet having excellent burring property, and manufacturing method therefor
KR102485003B1 (ko) 성형성 및 표면품질이 우수한 고강도 도금강판 및 그 제조방법
CN117083408A (zh) 高强度钢板及其制造方法
WO2024057670A1 (ja) 鋼板、部材およびそれらの製造方法
WO2024057669A1 (ja) 鋼板、部材およびそれらの製造方法

Legal Events

Date Code Title Description
PB01 Publication
PB01 Publication
SE01 Entry into force of request for substantive examination
SE01 Entry into force of request for substantive examination
GR01 Patent grant
GR01 Patent grant