MX2022012143A - Chapa de acero, miembro y metodo para producirlos. - Google Patents

Chapa de acero, miembro y metodo para producirlos.

Info

Publication number
MX2022012143A
MX2022012143A MX2022012143A MX2022012143A MX2022012143A MX 2022012143 A MX2022012143 A MX 2022012143A MX 2022012143 A MX2022012143 A MX 2022012143A MX 2022012143 A MX2022012143 A MX 2022012143A MX 2022012143 A MX2022012143 A MX 2022012143A
Authority
MX
Mexico
Prior art keywords
steel sheet
concentration
mpa
less
âμm
Prior art date
Application number
MX2022012143A
Other languages
English (en)
Inventor
Tatsuya Nakagaito
Shunsuke Yamamoto
Katsuya Hoshino
Hidekazu Minami
Yoshiyasu Kawasaki
Lingling Yang
Shotaro TERASHIMA
Yuki Takeda
Original Assignee
Jfe Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jfe Steel Corp filed Critical Jfe Steel Corp
Publication of MX2022012143A publication Critical patent/MX2022012143A/es

Abstract

Se proporciona una chapa de acero con una tensión de rotura (TS) de 780 MPa o más y menos de 1180 MPa, una alta fluencia (YS), alta ductilidad, alta capacidad de rebordeo por estiramiento (capacidad de expansión de orificio), buenas propiedades de fatiga y alta resistencia a la LME, un miembro y un método para producirlos. Una chapa de acero de acuerdo con la presente invención tiene una composición química específica y una microestructura de acero específica, donde en una región dentro de 4.9 µm en una dirección del espesor desde una superficie de la chapa de acero, una región con una concentración de Si no mayor de un tercio de la concentración de Si en la composición química de la chapa de acero y con una concentración de Mn no mayor de un tercio de la concentración de Mn en la composición química de la chapa de acero tiene un espesor de 1.0 µm o más, la concentración más baja de Si LSi y la concentración más baja de Mn LMn en la región dentro de 4.9 µm en la dirección del espesor desde la superficie de la chapa de acero y una concentración de Si TSi y una concentración de Mn TMn en la posición en un cuarto del espesor de la chapa de acero satisfacen la siguiente fórmula (1) y la chapa de acero tiene una tensión de rotura de 780 MPa o más y menos de 1180 MPa. LSi + LMn = (TSi + TMn)/4 (1).
MX2022012143A 2020-03-31 2021-03-25 Chapa de acero, miembro y metodo para producirlos. MX2022012143A (es)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2020062803 2020-03-31
JP2020122183 2020-07-16
PCT/JP2021/012661 WO2021200579A1 (ja) 2020-03-31 2021-03-25 鋼板、部材及びそれらの製造方法

Publications (1)

Publication Number Publication Date
MX2022012143A true MX2022012143A (es) 2022-10-18

Family

ID=77929371

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2022012143A MX2022012143A (es) 2020-03-31 2021-03-25 Chapa de acero, miembro y metodo para producirlos.

Country Status (7)

Country Link
US (1) US20230129828A1 (es)
EP (1) EP4130323A4 (es)
JP (3) JP7001202B1 (es)
KR (1) KR20220145390A (es)
CN (1) CN115349028B (es)
MX (1) MX2022012143A (es)
WO (1) WO2021200579A1 (es)

Families Citing this family (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2022149502A1 (ja) * 2021-01-07 2022-07-14 日本製鉄株式会社 鋼板及びその製造方法
WO2023118350A1 (en) * 2021-12-24 2023-06-29 Tata Steel Nederland Technology B.V. High strength steel strip or sheet excellent in ductility and bendability, manufacturing method thereof, car or truck component
WO2024150820A1 (ja) * 2023-01-13 2024-07-18 日本製鉄株式会社 溶接継手
WO2024150817A1 (ja) * 2023-01-13 2024-07-18 日本製鉄株式会社 鋼板及びめっき鋼板
WO2024150822A1 (ja) * 2023-01-13 2024-07-18 日本製鉄株式会社 鋼板及びめっき鋼板
WO2024150824A1 (ja) * 2023-01-13 2024-07-18 日本製鉄株式会社 溶接継手
WO2024157552A1 (ja) * 2023-01-26 2024-08-02 Ｊｆｅスチール株式会社 亜鉛めっき鋼板および部材、ならびに、それらの製造方法
WO2024202804A1 (ja) * 2023-03-31 2024-10-03 Ｊｆｅスチール株式会社 鋼板、部材およびそれらの製造方法

Family Cites Families (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4964494B2 (ja) 2006-05-09 2012-06-27 新日本製鐵株式会社 穴拡げ性と成形性に優れた高強度鋼板及びその製造方法
JP4924730B2 (ja) * 2009-04-28 2012-04-25 Ｊｆｅスチール株式会社 加工性、溶接性および疲労特性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
JP4737319B2 (ja) * 2009-06-17 2011-07-27 Ｊｆｅスチール株式会社 加工性および耐疲労特性に優れた高強度合金化溶融亜鉛めっき鋼板およびその製造方法
BR112013006143B1 (pt) * 2010-09-16 2018-12-18 Nippon Steel & Sumitomo Metal Corporation chapa de aço de alta resistência e chapa de aço revestida com zinco de alta resistência que têm excelente ductilidade e capacidade de estiramento-flangeamento e método de fabricação das mesmas
JP5858032B2 (ja) * 2013-12-18 2016-02-10 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
EP3287539B1 (en) 2015-04-22 2019-12-18 Nippon Steel Corporation Plated steel sheet
JP6524810B2 (ja) * 2015-06-15 2019-06-05 日本製鉄株式会社 耐スポット溶接部破断特性に優れた鋼板及びその製造方法
JP2017066508A (ja) * 2015-10-02 2017-04-06 株式会社神戸製鋼所 熱間プレス用亜鉛めっき鋼板および熱間プレス成形品の製造方法
KR101758485B1 (ko) * 2015-12-15 2017-07-17 주식회사 포스코 표면품질 및 점 용접성이 우수한 고강도 용융아연도금강판 및 그 제조방법
JP6875914B2 (ja) * 2016-05-30 2021-05-26 株式会社神戸製鋼所 高強度鋼板およびその製造方法
CN110268083B (zh) * 2017-02-10 2021-05-28 杰富意钢铁株式会社 高强度镀锌钢板及其制造方法
JP6428970B1 (ja) * 2017-03-30 2018-11-28 Ｊｆｅスチール株式会社 ホットプレス部材およびその製造方法
EP3663425B1 (en) * 2017-07-31 2024-03-06 Nippon Steel Corporation Hot-dip galvanized steel sheet
CN111247264A (zh) * 2017-10-20 2020-06-05 杰富意钢铁株式会社 高强度钢板及其制造方法
CN111492075B (zh) 2017-12-15 2021-10-12 日本制铁株式会社 钢板、热浸镀锌钢板和合金化热浸镀锌钢板

Also Published As

Publication number Publication date
EP4130323A1 (en) 2023-02-08
CN115349028B (zh) 2024-03-26
JP2022024145A (ja) 2022-02-08
CN115349028A (zh) 2022-11-15
JP7001202B1 (ja) 2022-02-03
JP2022023086A (ja) 2022-02-07
EP4130323A4 (en) 2023-08-30
JP7044197B2 (ja) 2022-03-30
KR20220145390A (ko) 2022-10-28
WO2021200579A1 (ja) 2021-10-07
US20230129828A1 (en) 2023-04-27
JPWO2021200579A1 (es) 2021-10-07

Similar Documents

Publication Publication Date Title
MX2022012143A (es) Chapa de acero, miembro y metodo para producirlos.
MX2022012144A (es) Chapa de acero, miembro y metodo para producirlos.
MX2019009803A (es) Lamina de acero laminada en caliente de alta resistencia y metodo para producir la misma.
MX2021004419A (es) Lamina de acero electrogalvanizada de alta resistencia y alto limite de alargamiento y metodo para la fabricacion de la misma.
MX2011012371A (es) Lamina de acero de alta resistencia, lamina de acero bañada en caliente, y lamina de acero bañada en caliente aleada que tienen excelentes caracteristicas a la fatiga, alargamiento y colision y metodo de fabricacion para tales laminas de acero.
MX2018009643A (es) Lamina de acero de alta resistencia y metodo para la produccion de la misma.
MX2013002893A (es) Chapa delgada de acero laminada en caliente de alta resistencia que tiene excelente resistencia a la fatiga y metodo para fabricar la misma.
MX2019006862A (es) Producto de acero plano laminado en caliente y metodo para la produccion del mismo.
MX2016012584A (es) Chapa de acero galvanizado en baño caliente aleado de alta resistencia con excelente manejabilidad y mayor resistencia de las fracturas, y metodo para su produccion.
MX360332B (es) Lamina de acero galvanizado de alta resistencia, excelente en su capacidad de combado y metodo de fabricacion de la misma.
TW200940717A (en) High strength steel sheet having superior ductility and method for manufacturing the same
MX2017001529A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma, y metodo de produccion para lamina de acero galvanizada de alta resistencia.
WO2018123356A1 (ja) 高強度鋼板および高強度電気亜鉛めっき鋼板
MX2018011687A (es) Lamina de acero y lamina de acero chapeada, metodo para la produccion de lamina de acero laminada en caliente, metodo para la produccion de lamina de acero extra-dura laminada en frio, metodo para la produccion de lamina tratada termicamente, metodo para la produccion de lamina de acero, y metodo para la produccion de lamina de acero chapeada.
MX2011009340A (es) Lamina de acero galvanizado de alta resistencia que tiene excelente formabilidad y metodo para manufacturar la misma.
MX2017009021A (es) Lámina de acero chapado de alta resistencia y método para su producción.
MX2023011533A (es) Lamina de acero, miembro, y metodo para producir la lamina de acero, y metodo para producir el miembro.
MX2016014060A (es) Lamina de acero de alta resistencia y metodo para la fabricacion de la misma.
MX2017011993A (es) Lamina de acero para prensado en caliente y metodo para producir la misma.
MX2021009067A (es) Miembro prensado en caliente, chapa de acero laminada en frio para miembro prensado en caliente, y metodo para producir los mismos.
MX2021000992A (es) Lamina de acero recubierta laminada en caliente de alta resistencia.
WO2018117450A8 (ko) 저온인성 및 후열처리 특성이 우수한 내sour 후판 강재 및 그 제조방법
MX2024002282A (es) Lamina de acero de alta resistencia, lamina de acero recubierta o chapada de alta resistencia, metodos de produccion de la misma, y miembro.
JPH07252592A (ja) 成形性、低温靭性及び疲労特性に優れた熱延高強度鋼板
UA84195C2 (ru) Сталь для механических изделий, способ производства механических изделий с использованием этой стали и механические изделия, произведенные этим способ