MX2021004446A - Lamina de acero recubierta a base de zinc electrolitico de alta resistencia y alta ductilidad y metodo para la produccion de la misma. - Google Patents

Lamina de acero recubierta a base de zinc electrolitico de alta resistencia y alta ductilidad y metodo para la produccion de la misma.

Info

Publication number
MX2021004446A
MX2021004446A MX2021004446A MX2021004446A MX2021004446A MX 2021004446 A MX2021004446 A MX 2021004446A MX 2021004446 A MX2021004446 A MX 2021004446A MX 2021004446 A MX2021004446 A MX 2021004446A MX 2021004446 A MX2021004446 A MX 2021004446A
Authority
MX
Mexico
Prior art keywords
carbides
particle size
average particle
less
steel sheet
Prior art date
Application number
MX2021004446A
Other languages
English (en)
Inventor
Shinjiro Kaneko
Takuya Hirashima
Original Assignee
Jfe Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jfe Steel Corp filed Critical Jfe Steel Corp
Publication of MX2021004446A publication Critical patent/MX2021004446A/es

Abstract

Se proporcionan una lámina de acero recubierta a base de zinc electrolítico de alta resistencia y alta ductilidad que tiene excelente capacidad de flexión y un método para la producción de la misma. Una lámina de acero recubierta a base de zinc electrolítico de alta resistencia y alta ductilidad incluye un recubrimiento a base de zinc electrolítico sobre una superficie de una lámina de acero base, en la cual la lámina de acero base tiene una composición de componentes predeterminada y una microestructura de acero en la cual el porcentaje de área total de una o dos de entre martensita que contiene un carburo que tiene un tamaño de partícula promedio de 50 nm o menos y bainita que contiene un carburo que tiene un tamaño de partícula promedio de 50 nm o menos es de 90% o más en toda la microestructura de acero, el porcentaje de área total de una o dos de entre la martensita que contiene un carburo que tiene un tamaño de partícula promedio de 50 nm o menos y la bainita que contiene un carburo que tiene un tamaño de partícula promedio de 50 nm o menos es de 80% o más en una región que se extiende desde la superficie de la lámina de acero base hasta una profundidad de 1/8 del espesor de la lámina de acero base, y el perímetro total de partículas de carburo individuales que tienen un tamaño de partícula promedio de 50 nm o menos en la martensita que contiene un carburo que tiene un tamaño de partícula promedio de 50 nm o menos y la vainita que contiene un carburo que tiene un tamaño de partícula promedio de 50 nm o menos presentes en la región es de 50 µm/mm2 o más, en la cual la cantidad de hidrógeno difusible en el acero es de 0.20 ppm en masa o menos.
MX2021004446A 2018-10-18 2019-08-06 Lamina de acero recubierta a base de zinc electrolitico de alta resistencia y alta ductilidad y metodo para la produccion de la misma. MX2021004446A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2018196591 2018-10-18
PCT/JP2019/030793 WO2020079926A1 (ja) 2018-10-18 2019-08-06 高延性高強度電気亜鉛系めっき鋼板およびその製造方法

Publications (1)

Publication Number Publication Date
MX2021004446A true MX2021004446A (es) 2021-07-07

Family

ID=70283035

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2021004446A MX2021004446A (es) 2018-10-18 2019-08-06 Lamina de acero recubierta a base de zinc electrolitico de alta resistencia y alta ductilidad y metodo para la produccion de la misma.

Country Status (7)

Country Link
US (1) US12043884B2 (es)
EP (1) EP3828299A4 (es)
JP (1) JP6760521B1 (es)
KR (1) KR102541248B1 (es)
CN (1) CN112867807B (es)
MX (1) MX2021004446A (es)
WO (1) WO2020079926A1 (es)

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20230392226A1 (en) * 2020-10-27 2023-12-07 Jfe Steel Corporation Hot-pressed member, steel sheet for hot pressing, and methods for producing the hot-pressed member and the steel sheet for hot pressing
US20240068065A1 (en) * 2020-12-25 2024-02-29 Jfe Steel Corporation Steel sheet, member, and methods for manufacturing the same
JP7151948B1 (ja) * 2021-06-15 2022-10-12 Ｊｆｅスチール株式会社 高強度亜鉛めっき鋼板および部材ならびにそれらの製造方法
WO2022264585A1 (ja) * 2021-06-15 2022-12-22 Ｊｆｅスチール株式会社 高強度亜鉛めっき鋼板および部材ならびにそれらの製造方法

Family Cites Families (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6149007A (ja) * 1984-08-17 1986-03-10 Nishida Tekko Kk 地下ダム用制水弁装置
JP3993703B2 (ja) 1998-09-03 2007-10-17 新日本製鐵株式会社 加工用薄鋼板の製造方法
JP5418047B2 (ja) 2008-09-10 2014-02-19 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5412182B2 (ja) * 2009-05-29 2014-02-12 株式会社神戸製鋼所 耐水素脆化特性に優れた高強度鋼板
MX360965B (es) * 2009-11-30 2018-11-23 Nippon Steel & Sumitomo Metal Corp Placa de acero de alta resistencia con resistencia a la tracción final de 900 mpa o mas, excelente en resistencia a la fragilizacion por hidrógeno y método de producción de la misma.
WO2011118126A1 (ja) * 2010-03-24 2011-09-29 Ｊｆｅスチール株式会社 超高強度部材の製造方法および使用方法
JP5531757B2 (ja) 2010-04-28 2014-06-25 新日鐵住金株式会社 高強度鋼板
JP5466576B2 (ja) 2010-05-24 2014-04-09 株式会社神戸製鋼所 曲げ加工性に優れた高強度冷延鋼板
KR101253885B1 (ko) 2010-12-27 2013-04-16 주식회사 포스코 연성이 우수한 성형 부재용 강판, 성형 부재 및 그 제조방법
ES2706996T3 (es) 2011-09-30 2019-04-02 Nippon Steel & Sumitomo Metal Corp Chapa de acero de alta resistencia galvanizada por inmersión en caliente con excelente resistencia a la fractura retardada y método para su fabricación
US20170218475A1 (en) 2014-08-07 2017-08-03 Jfe Steel Corporation High-strength steel sheet and method for manufacturing same
MX2017012194A (es) * 2015-03-25 2017-12-15 Jfe Steel Corp Lamina de acero laminada en frio y metodo de fabricacion para la misma.
US10858717B2 (en) 2015-08-11 2020-12-08 Jfe Steel Corporation Material for high strength steel sheets, hot rolled material for high strength steel sheets, hot-rolled and annealed material for high strength steel sheets, high strength steel sheet, high strength hot-dip-coated steel sheet, high strength electroplated steel sheet, and method of manufacturing same
JP6354921B1 (ja) * 2016-09-28 2018-07-11 Ｊｆｅスチール株式会社 鋼板およびその製造方法
MX2019002324A (es) 2016-09-28 2019-07-04 Jfe Steel Corp Lamina de acero y metodo para producir la misma.
WO2018146828A1 (ja) * 2017-02-10 2018-08-16 Ｊｆｅスチール株式会社 高強度亜鉛めっき鋼板及びその製造方法
WO2019003445A1 (ja) 2017-06-30 2019-01-03 Ｊｆｅスチール株式会社 熱間プレス部材およびその製造方法ならびに熱間プレス用冷延鋼板
US11377710B2 (en) 2018-03-30 2022-07-05 Nippon Steel Corporation Steel sheet and manufacturing method therefor

Also Published As

Publication number Publication date
EP3828299A1 (en) 2021-06-02
CN112867807A (zh) 2021-05-28
CN112867807B (zh) 2023-04-21
KR20210060551A (ko) 2021-05-26
WO2020079926A1 (ja) 2020-04-23
JP6760521B1 (ja) 2020-09-23
KR102541248B1 (ko) 2023-06-08
JPWO2020079926A1 (ja) 2021-02-15
US12043884B2 (en) 2024-07-23
EP3828299A4 (en) 2021-06-02
US20210324504A1 (en) 2021-10-21

Similar Documents

Publication Publication Date Title
MX2021004446A (es) Lamina de acero recubierta a base de zinc electrolitico de alta resistencia y alta ductilidad y metodo para la produccion de la misma.
MX2019009513A (es) Lamina de acero galvanizada de alta resistencia y metodo para producir la misma.
MX2021004933A (es) Lamina de acero de alta resistencia y metodo para la fabricacion de la misma.
MX2020009652A (es) Lamina de acero laminada en frio de alta resistencia y metodo de manufacturacion de la misma.
MX2017009015A (es) Lámina de acero chapado de alta resistencia que tiene excelentes propiedades de chapado, trabajabilidad y mayor resistencia a las fracturas, y método para su producción.
MX2021004419A (es) Lamina de acero electrogalvanizada de alta resistencia y alto limite de alargamiento y metodo para la fabricacion de la misma.
MX2016000266A (es) Lamina de acero chapado de alta resistencia que tiene propiedades superiores de chapado, capacidad de manipulacion, y resistencia a la fractura retardada, y metodo de produccion la misma.
MX2020005475A (es) Chapa de acero galvanizada de alta resistencia y metodo para fabricar la misma.
MX2021003895A (es) Lamina de acero laminada en caliente y metodo para fabricar la misma.
MX2020006342A (es) Hoja de acero de alta resistencia y alta formabilidad y metodo de fabricacion.
MX2018009643A (es) Lamina de acero de alta resistencia y metodo para la produccion de la misma.
MX2019013949A (es) Lamina de acero de alta resistencia y su metodo de produccion.
MX2018009164A (es) Lamina de acero galvanizado de alta resistencia y alta relacion de rendimiento y metodo para producir la misma.
MY160065A (en) High-strength galvanized steel sheet nad method of manufacturing the same
MX2021007759A (es) Lamina de acero galvanizada por inmersion en caliente de alta resistencia y metodo para producir la misma.
MX357963B (es) Lamina de acero galvanizado por inmersion en caliente, de alta resistencia, con excelentes caracteristicas mecanicas de corte, lamina de acero galvanizado por inmersion en caliente, aleada, de alta resistencia y metodo para producir dichas laminas.
MX2019004000A (es) Lamina de acero recubierta de metal, metodo de fabricacion de lamina de acero galvanizada por inmersion en caliente, y metodo de fabricacion de lamina de acero galvanizada-recocida aleada.
MX2017009021A (es) Lámina de acero chapado de alta resistencia y método para su producción.
MX2021008505A (es) Lamina de acero de alta resistencia.
MX2019001045A (es) Lamina de acero y metodo para la produccion de la misma.
MX2019009876A (es) Cuerpo estampado en caliente.
MX2021009452A (es) Lamina de acero galvanizada por inmersion en caliente y metodo para producir la misma.
MX2016012708A (es) Chapa de acero laminada en frio de alta resistencia, chapa de acero galvanizada en inmersion en caliente de alta resistencia y chapa de acero galvanfusionado en inmersion en caliente de alta resistencia que tiene excelente ductilidad, abocardabilidad por estiramiento y soldabilidad.
MX2021004105A (es) Lamina de acero laminada en caliente y metodo para fabricar la misma.
MX2016012797A (es) Chapa de acero laminada en frio de alta resistencia, chapa de acero galvanizada en baño caliente de alta resistencia y chapa de acero galvanofusionado en baño caliente de alta resistencia que tiene excelente ductilidad, abocardabilidad por estiramiento y soldabilidad.