KR930019756A - 열가소성 수지 조성물의 제조방법 - Google Patents
열가소성 수지 조성물의 제조방법 Download PDFInfo
- Publication number
- KR930019756A KR930019756A KR1019920004805A KR920004805A KR930019756A KR 930019756 A KR930019756 A KR 930019756A KR 1019920004805 A KR1019920004805 A KR 1019920004805A KR 920004805 A KR920004805 A KR 920004805A KR 930019756 A KR930019756 A KR 930019756A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- hours
- compound
- resin composition
- rubber elastomer
- Prior art date
Abstract
본 발명은 가교 고무 탄성체(R) 10∼60중량%와 단량체 혼합물 40∼90중량%를 그라프트 중합시켜 얻은 수지조성물(A) 30∼90중량%와 2종 이상의 단량체 화합물을 증합시켜 얻은 수지상 공중합체 (B) 10∼70중량%를 고무탄성체의 함량이 5∼45중량%가 되도록 조정하여 염석하므로써 내후성이 특히 우수한 열가소성 수지 조성물에 제조하는 방법에 관한것으로서, 상기 고무 탄성체(R)은 알킬기의 탄소수가 1∼10일 아크릴산 알킬 에스테르 화합물 70∼99중량%, 스티렌, 아크릴로 니트릴, 메탈 메타크릴레이트에서 선택된 적어도 1종 이상의 단량체 1∼30중량%와 분자중에 이중 결합을 2개이상 갖는 가교성 단량체 0.01∼10중량%(합계 100중량%)의 혼합물을 이온 교환수, 유화제 등이 존재하는 수성 에멀젼에서 괴황산칼륨-아왕산타느륨계, 과항산칼륨-아황산나트륨-Fe 화합물계, 고황산칼륨-아황산나트륨계, 과황산나트-Fe 화합물계, 과황산칼륨-아황산타느륨-피로인산나트륨계에서 선택된 수용성 산화 환원 개시제를 이용하여 정해진 순서대로 투입하여 40℃이하의 저온에서 3∼8시간 동안 1차 증합하고, 60∼80℃로 온도를 승온하여 2∼5시간 동안 숙성하여 얻은 것임을 특징으로 한다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (1)
- 가교 고무 탄성체(R) 10∼60중량%(고형분으로서)와 방향족 비닐화합물, 시안화 비닐화합물, 메타크릴산 알킬에스테르로 이루어진 군에서 선택된 적어도 2종 이상의 단량체 혼합물 40∼90중량%(합계100중량%)를 이온교환수, 유화제, 개시제, 분자량 조절제등이 존재하는 수성 에멀젼중에서 60∼80℃로 3∼8시간 유화 그라프트 중합시켜 얻은 그라프트 수지 조성물(A)30∼90와 방향족 비닐화합물, 시안화 비닐화합물, 메타크릴산 알킬에스트레로 이루어진군에서 선택된 적어도 2종 상의 단량체를 이온교환수, 유화제, 개시제, 분자량 조절제등이 존재하는 수성 에멀젼에서 60∼80℃로3∼8시간 중합시켜 얻은 고유 점도(Ⅰ,Ⅴ)가 0.4∼0.9인 수지상 공중합체(B) 10∼70중량%를 라텍스상으로 혼합하여 가교 고무 탄성체의 함량이 5∼45중량%가 되도록 조성한후 염석을 행하여 열가소성 수지조성물을 제조하는방법에 있어서, 상기 가교 고무 탄성체(R)은 알킬기의 탄소수가 1∼10인 아크릴산 알킬 에스테르 화합물 70∼99중량%, 스티렌, 아크릴로 니트릴, 메틸 메타크릴레이트에서 선택된 적어도 1종 이상의 단량체 1∼30중량%와 분자중에 이중 결합을 2개 이상 갖는 가교성 0.01∼10중량%(합계 100중량%)로 이루어진 혼합물줄 1∼40중량%를 먼저 이온 교환수, 유화제 등의 존재하에 완전히 분산시킨 수성 에멀젼에 과황산칼륨-아황산나트륨, 과황산칼륨-아황산나트-Fe 화합물, 과황산칼륨-아황산타느륨-피로인산나트륨 등에서 선태고딘 수용성 산호 원 개시제 1또는 2종을 첨가하여 교반 한 후 다시 상기 개시제 1종 또는 2종을 가하여 40℃이하의 저온에서 2시간 동아 ㄴ시드 중합한 후 잔량의 단량체 혼합물을 동일 온도에서 3∼6시간동안 연속투입하여 중합시킨 후, 이어서 60∼80℃로 온도를 승온하여 2∼5시간 동안 숙성하여 얻은 것임을 특징으로 하는 열가소성 수지 조성물의 제조방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.