KR930000706A - 용융도금의 강대상에 도포중량을 제어하기 위한 방법 - Google Patents
용융도금의 강대상에 도포중량을 제어하기 위한 방법 Download PDFInfo
- Publication number
- KR930000706A KR930000706A KR1019920011048A KR920011048A KR930000706A KR 930000706 A KR930000706 A KR 930000706A KR 1019920011048 A KR1019920011048 A KR 1019920011048A KR 920011048 A KR920011048 A KR 920011048A KR 930000706 A KR930000706 A KR 930000706A
- Authority
- KR
- South Korea
- Prior art keywords
- high frequency
- frequency current
- current conductive
- conductive path
- steel strip
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 자계강도(H) 및 강대의 자속밀도(B) 사이의 관계를 나타내는 대표적인 도면,
제2도는 본 발명의 방법을 실시하기 위한 장치의 예를 나타내는 측면도,
제3도는 제2도에 나타난 장치의 정면도.
Claims (16)
- 도금욕조(4)으로 부터 인양되는 강대(S)의 일측면과 타측명에 근접하여, 각각이 상기 도금욕조에서 강대표면과 평행하게 되도록 적어도 한쌍의 고주파 도전경로(S)를 위치시키는 단계와, 상기 강대내에서 반대위상의 고주파 전류가 유기되도록 상기 적어도 한쌍의 고주파 전류도전경로를 통하여 상기 강대를 자기적으로 포화시키는데 충분한 세기의 고주파전류를 흐르게 하고 강대의 표면에 작용하는 자기압력력이 상기 유기된 고주파전류와 상기 고주파 전류도전경로내의 고주파 전류와의 상호작용에 의하여 발생되도록 하는 단계를 구비한 용융 강대상에서 도포중량을 제어하기 위한 방법.
- 제1항에 있어서, 상기 적어도 한쌍의 고주파전류도전경로를 위치시키는 단계는 상기 고주파전류 도전경로가 상기 강대를 통하여 상호 대향될 수 있도록 적어도 한쌍의 고주파 전류도전 경로를 위치시키는 것을 포함하고, 상기 고주파 전류를 흐르게 하는 단계는 적어도 한쌍의 고주파 전류 도전경로를 통하여 동일 위상의 고주파 전류를 흐르게 하는 것을 포함함을 특징으로 하는 방법.
- 제1항에 있어서, 상기 적어도 한쌍의 고주파 전류도전경로를 위치시키는 단계는 상기 고주파전류도전경로의 각각이 상대에 대하여 상측 및 하측으로 편의되어 위치될 수 있도록 적어도 2쌍의 고주파 전류도전경로를 배치하는 것을 포함하도록 함을 특징으로 하는 방법.
- 제1항에 있어서, 강대를 대향하고 있는 측면을 제외한 상기 고주파 전류도전경로는 전자석 물질(2)에 의하여 둘러싸여지도록 함을 특징으로 하는 방법.
- 제1항에 있어서, 상기 고주파 전류도전경로는 고주파 전류도전경로가 강대의 단부와 대향하고 있는 부위에서 강대의 이동방향에 따라 굴곡부(11)를 가지도록 함을 특징으로 하는 방법.
- 제1항에 있어서, 상기 고주파 전류도전경로는 전길이에서 강대의 폭방향으로 경사지게 한 것을 특징으로 하는 방법.
- 제1항에 있어서, 강대의 단부와 대향하고 있는 상기 고주파전류도전경로의 부위가 강대의 폭방향으로 경사지게 됨을 특징으로 한 방법.
- 제2항에 있어서, N극과 S극이 서로 대향되도록 적어도 하나의 자석(5)의 N극과 S극을 설치하고, 강대의 폭방향이 적어도 한쌍의 고주파 전류도전경로에 조정하여 상기 강대의 양단부 외측으로 상기 자석의 N극과 S극 사이에 위치되어서 상기 강대가 상기 자석에 의하여 자기적으로 포화되도록 하는 단계를 더 구비함을 특징으로 한 방법.
- 제8항에 있어서, 상기 고주파 전류도전경로는 한쌍의 고주파 도전경로는 상측 고주파 전류도전경로이고, 나머지 다른 한쌍은 하측 고주파 전류도전경로이고 높이 방향으로 설치된 두쌍의 고주파 전류도전경로이고, 상기 자석은 하나의 자석은 상측 고주파 도전경로의 상측부에 근접하여서, 나머지 다른 하나의 자석은 하측 고주파도전 경로의 하측부에 근접하여 위치되는 2개의 자석임을 특징으로 하는 방법.
- 제8항에 있어서, 상기 고주파 전류도전경로는 한쌍의 고주파 전류도전경로는 상측의 고주파 전류도전경로이고, 나머지 다른 한쌍의 고주파 도전경로는 하측의 고주파 전류도전경로이며, 높이 방향으로 설치된 2쌍의 고주파 전류도전경로이고, 상기 자석은 상측의 고주파 전류도전경로와 하측의 고주파 전류도전경로 사이에 위치되는 하나의 자석임을 특징으로 하는 방법.
- 제8항에 있어서, 상기 자석은 전자석임을 특징으로 하는 방법.
- 제8항에 있어서, 상기 자석은 영구자석임을 특징으로 하는 방법.
- 제1항에 있어서, 도금욕조의 외측으로 인양되는 강대의 양측면에 근접하여 와이핑노즐을 위치시키고, 상기 도금욕조의 외측으로 인양되는 강대로 와이핑 노즐로 부터 가스를 분사시키도록 하는 단계를 더 구비하도록 함을 특징으로 하는 방법.
- 제1항에 있어서 상기 적어도 한쌍의 고주파 전류도전경로를 위치시키는 단계는 와이핑 노즐의 노즐부위에 상기 고주파 전류도전경로를 위치시키는 것을 포함함을 특징으로 한 방법.
- 도금욕조(4)의 외측으로 인양되는 강대(5)의 일측면과 타측면의 각각에 근접하고 상기 도금욕조위의 강대의 포면과 각각 평행하게 되도록 고주파 전류 도전경로(1a, 1b)를 위치시키고 상기 강대의 일측면에 근접한 고주파 전류도전 경로가 상기 강대의 타측면에 근접하여 있는 고주파 전류도전경로를 대향하며, 상기 강대는 상기 고주파 전류도전경로 사이에 위치되도록 하는 단계와 N극과 S극이 서로 대향될 수 있도록 상기 고주파 전류도전경로에 근접하고 강대 양단부의 외측으로 자석(5)의 N극과 S극을 배치시켜서, 폭방향이 적어도 한쌍의 고주파 전류도전경로의 양단부 외측으로 N극과 S극 사이에 위치되도록 한 단계와, 반대위상의 고주파전류가 유기되도록 상기 고주파 도전경로를 통하여 동일 위상의 고주파 전류를 흘려서 강대의 표면상에 작용하는 자기압력력이 상기 유기된 고주파 전류와 상기 고주파 전류도전경로의 고주파 전류와의 상호작용에 의하여 발생되도록 하는 단계를 구비한 용융도금 강대상의 도포중량을 제어하기 위한 방법.
- 도금욕조(4)으로부터 인양되는 강대(S)의 양측면에 근접하여 와이핑노즐(8)을 위치시키는 단계와, 각각의 고주파 도전경로가 도금욕조 위에서 강대의 표면의 각각에 평행하게 되도록 와이핑 노즐에 고주파 전류도전경로 (1a,1b)를 위치시키는 단계와 상기 도금욕조에서 인양되는 강대상으로 와이핑 노즐에서 가스를 분사시키는 단계와, 강대내에서 반대위상의 고주파전류를 유기하도록 상기 고주파 도전경로를 통하여 자기적으로 강대를 포화시키는데 충분한 세기의 고주파 전류를 흘려서 강대의 표면상에 작용하는 자기압력력이 유기된 고주파 전류와, 상기 고주파 전류도전경로의 고주파 전류의 상호작용에 의하여 발생되는 단계를 구비한 용융도금 강대상에서 도포중량을 제어하기 위한 방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.