KR920006450A - 가요성 발포성 도료 조성물 - Google Patents
가요성 발포성 도료 조성물 Download PDFInfo
- Publication number
- KR920006450A KR920006450A KR1019910016914A KR910016914A KR920006450A KR 920006450 A KR920006450 A KR 920006450A KR 1019910016914 A KR1019910016914 A KR 1019910016914A KR 910016914 A KR910016914 A KR 910016914A KR 920006450 A KR920006450 A KR 920006450A
- Authority
- KR
- South Korea
- Prior art keywords
- curable composition
- temperature
- cycle test
- curing
- zinc
- Prior art date
Abstract
내용 없음.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제 1 도는 4W13 I-비임의 10in 단면을 나타내는 동일한 크기의 사시도이다.
제 2 도는 제 1 도의 평면도이다.
Claims (18)
- (a) 폴리에폭시드 수지, (b) 폴리에폭시드 수지를 경화시키기에 적합한 경화제, 및 (c)(ⅰ) 아연, (ⅱ) 붕소, (ⅲ) 인 및 (ⅳ) 열분해시의 팽창 가스의 공급원을 제공하기에 적합한 물질들의 혼합물을 함유한 첨가제 성분을 포함하고 있으며 ; 가열 또는 불꽃에 노출시 탄소질 챠콜을 형성할 수 있으며, 단, 2개의 열전쌍이 표면에 부착되어 있는 4W13 I-비임의 10in(0.254m)의 단면에 비연소된 경화성 조성물을 0.5in(12.7mm)의 두께로 도포하고, 주위 온도에서 16시간동안 경화시키고, 약 60℃에서 5일간 강제 경화시키고, 냉각 사이클 시험을 수행할 때, 비연소된 경화 조성물이 크래킹되지 않고 냉각 사이클 시험중의 최소한 10회 연소 사이클을 통과하는데 충분한 가요성을 갖는 발포성 경화성 조성물(여기서, 상기 냉각 사이클 시험중의 한 사이클은 상기 비임을, 도막 밑에 있는 비임의 표면에 부착된 2개의 열전쌍에 의해 측정된 바와 같이, 강철이 약 0°F(-18℃) 내지 약 -10°F(-23℃)의 온도에 도달하는데 충분한 시간동안 약 0°F(-18℃) 내지 약 -10°F(-23℃)의 온도에서 작동하는 냉동기내에 위치시키고, 상기 비임을 냉동기로부터 꺼낸 다음, 비임의 표면주위로 이동되는 열전쌍에 의해 측정된 바와 같이, 상기 표면 온도가 3분 이내에 110°F(43℃)에 도달할때까지, 히트 건(heat gun)[Alpha Division of Loral Corp. 사제의 모델번호 HG 50146, 14 amp : 팁에서의 최소온도 500°F(260℃)]을 상기 표면으로부터 0.5in(12.7mm)의 간격을 두고 일정하게 통과시키므로써, 상기 표면의 50in2(0.0323m2)면적을 제 1 도 및 제 2 도에 나타난 바와 같이 가온시키고, 주위온도에서 최소한 2시간동안 방치시키는 것을 포함함).
- (a) 가요성 폴리에폭시드 수지, (b) 상기 폴리에폭시드 수지를 경화시키기에 적합한 경화제, 및 (c)(ⅰ) 아연, (ⅱ) 붕소, (ⅲ) 인 및 (ⅳ) 열분해시의 팽창 가스의 공급원을 제공하기에 적합한 물질들의 혼합물을 함유한 첨가제 성분을 포함하고 있으며 : 가열 또는 불꽃에 노출시 탄소질 챠콜을 형성할 수 있으며, 단, 2개의 열전쌍이 표면에 부착되어 있는 4W13 I-비임의 10in(0.254m)의 단면에 비연소된 경화성 조성물을 0.5in(12.7mm)의 두께로 도포하고, 주위 온도에서 16시간동안 경화시키고, 약 60℃에서 5일간 강제 경화시키고, 냉각 사이클 시험을 수행할 때, 비연소된 경화 조성물이 크래킹되지 않고 냉각 사이클 시험중의 최소한 10회 연소 사이클을 통과화는데 충분한 가요성을 갖는 발포성 경화성 조성물(여기서, 상기 냉각 사이클 시험중의 한 사이클은 상기 비임을, 도막 밑에 있는 비임의 표면에 부착된 2개의 열전쌍에 의해 측정된 바와 같이, 강철이 약 0°F(-18℃)내지 약 -10°F(-23℃)의 온도에 도달하는데 충분한 시간동안 약 0°F(-18℃)내지 약 -10°F(-23℃)의 온도에서 작동하는 냉동기내에 위치시키고, 상기 비임을 냉동기로부터 꺼낸 다음, 비임의 표면주위로 이동되는 열전쌍에 의해 측정된 바와 같이, 상기 표면 온도가 3분이내에 110°F(43℃)에 도달할때까지, 히트 건[Alpha Division of Loral Corp. 사제의 모델번호 HG 50146, 14 amp : 팁에서의 최소온도 500°F(260℃)]을 상기 표면으로부터 0.5in(12.7mm)의 간격을 두고 일정하게 통과시키므로써, 상기 표면의 50in2(0.0323m2)면적을 제 1 도 및 제 2 도에 나타나 바와 같이 가온시키고, 주위온도에서 최소한 2시간동안 방치시키는 것을 포함함).
- (a) 폴리에폭시드 수지, (b) 폴리에폭시드 수지를 경화시키기에 적합한 가요성 경화제, 및 (c)(ⅰ) 아연, (ⅱ) 붕소, (ⅲ)인 및 (ⅳ) 열분해시의 팽창 가스의 공급원을 제공하기에 적합한 물질들의 혼합물을 함유한 첨가제 성분을 포함하고 있으며 ; 가열 또는 불꽃에 노출시 탄소질 챠콜을 형성할 수 있으며, 단, 2개의 열전쌍의 표면에 부착되어 있는 4W13 I-비임의 10in(0.254m)의 단면에 비연소된 경화성 조성물을 0.5in(12.7mm)의 두께로 도포하고, 주위 온도에서 16시간동안 경화시키고, 약 60℃에서 5일간 강제 경화시키고, 냉각 사이클 시험을 수행할 때, 비연소된 경화 조성물이 크래킹되지 않고 냉각 사이클 시험중의 최소한 10회 연속 사이클을 통과하는데 충분한 가요성을 갖는 발포성 경화성 조성물(여기서, 상기 냉각 사이클 시험중의 한 사이클은 상기 비임을, 도막 밑에 있는 비임의 표면엔 부착된 2개의 열전쌍에 의해 측정된 바와 같이, 강철이 약 0°F(-18℃)내지 약 -10°F(-23℃)의 온도에 도달하는데 충분한 시간동안 약 0°F(-18℃)내지 약 -10°F(-23℃)의 온도에서 작동하는 냉동기내에 위치시키고, 상기 비임을 냉동기로부터 꺼낸 다음, 비임의 표면주위로 이동되는 열전쌍에 의해 측정된 바와 같이, 상기 표면 온도가 3분 이내에 110°F(43℃)에 도달할때까지, 히트건[Alpha Division of Loral Corp. 사제의 모델번호 HG 50146, 14 amp : 팁에서의 최소온도 500°F(260℃)]을 상기 표면으로부터 0.5in(12.7mm)의 간격을 두고 일정하게 통과시키므로써, 상기 표면의 50in2(0.0323m2) 면적을 제 1 도및 제 2 도에 나타난 바와 같이 가온시키고, 주위온도에서 최소한 2시간동안 방치시키는 것을 포함함).
- (a) 폴리에폭시드와 가요성 산 작용성 폴리에스테르의 에폭시 작용성 부가물, (b) 상기 에폭시 작용성 부가물을 경화시키기에 적합한 경화제, 및 (c)(ⅰ) 아연, (ⅱ) 붕소, (ⅲ)인 및 (ⅳ) 열분해시의 팽창 가스의 공급원을 제공하기에 적합한 물질들의 혼합물을 함유한 첨가제 성분을 포함하고 있으며 ; 가열 또는 불꽃에 노출시 탄소질 챠콜을 형성할 수 있으며, 단, 2개의 열전쌍의 표면에 부착되어 있는 4W13 I-비임의 10in(0.254m)의 단면에 비연소된 경화성 조성물을 0.5in(12.7mm)의 두께로 도포하고, 주위 온도에서 16시간동안 경화시키고, 약 60℃에서 5일간 강제 경화시키고, 냉각 사이클 시험을 수행할 때, 비연소된 경화 조성물이 크래킹되지 않고 냉각 사이클 시험중의 최소한 10회 연속 사이클을 통과하는데 충분한 가요성을 갖는 발포성 경화성 조성물(여기서, 상기 냉각 사이클 시험중의 한 사이클은 상길 비임을, 도막 밑에 있는 비임의 표면엔 부착된 2개의 열전쌍에 의해 측정된 바와 같이, 강철이 약 0°F(-18℃)내지 약 -10°F(-23℃)의 온도에 도달하는데 충분한 시간동안 약 0°F(-18℃)내지 약 -10°F(-23℃)의 온도에서 작동하는 냉동기내에 위치시키고, 상기 비임을 냉동기로부터 꺼낸 다음, 비임의 표면주위로 이동되는 열전쌍에 의해 측정된 바와 같이, 상기 표면 온도가 3분 이내에 110°F(43℃)에 도달할때까지, 히트 건[Alpha Division of Loral Corp. 사제의 모델번호 HG 50146, 14 amp : 팁에서의 최소온도 500°F(260℃)]을 상기 표면으로부터 0.5in(12.7mm)의 간격을 두고 일정하게 통과시키므로써, 상기 표면의 50in2(0.323m2) 면적을 제 1 도 및 제 2 도에 나타난 바와 같이 가온시키고, 주위온도에서 최소한 2시간동안 방치시키는 것을 포함함).
- 제 1 항에 있어서, 상기 경화제와 반응성이 있는 가요성 부연제를 추가로 포함하는 발포성 경화성 조성물.
- 제 4 항에 있어서, 상기 경화제가 모노-, 디- 또는 폴리아크릴레이트, 또는 그의 혼합물과 모노-, 디- 또는 폴리아민 또는 그의 혼합물로부터 제조된 아민 작용성 마이클(Michael)부가물인 발포성 경화성 조성물.
- 제 4 항에 있어서, 상기 부가물을 제조하는데 사용되는 상기 폴리에스테르가 탄소원자 7 내지 16개를 갖는 폴리카복실산 또는 상기 산의 혼합물을 포함한 폴리카복실산 성분, 및 디에틸렌 글리콜 일부를 포함한 폴리올 성분으로부터 제조되는 발포성 경화성 조성물.
- 제 7 항에 있어서, 상기 폴리카복실산 성분이 도데칸디오산 및 아젤레산의 혼합물을 포함하는 발포성 경화성 조성물.
- 제 4 항에 있어서, 상기 경화제가 아민 경화제인 발포성 경화성 조성물.
- 제 9 항에 있어서, 상기 아민이 폴리아미노-폴리아미노인 발포성 경화성 조성물.
- 제 4 항에 있어서, 상기 아연 공급원이 산화 아연, 붕산 아연, 인산 아연 및 탄산 아연으로부터 선택되는 발포성 경화성 조성물.
- 제 4 항에 있어서, 상기 붕소 공급원이 산화 붕소, 붕산 나트륨, 붕산 칼륨, 5붕산 암모늄, 붕산 암모늄 및 붕산 아연으로부터 선택되는 발포성 경화성 조성물.
- 제 4 항에 있어서, 상기 인 공급원이 트리스-2-클로로에틸 포스페이트, 인산, 모노-및 디-암모늄 포스페이트, 멜라민 피로포스페이트, 및 암모늄 폴리포스페이트로부터 선택되는 발포성 경화성 조성물.
- 제 4 항에 있어서, 상기 아연이 상기 폴리에폭시드 수지, 경화제 및 첨가제 성분의 전체 중량을 기준으로 약 0.1 내지 약 25중량%범위의 양으로 존재하는 발포성 경화성 조성물.
- 제 4 항에 있어서, 상기 붕소가 상기 폴리에폭시드 수지, 경화제 및 첨가제 성분의 전체 중량을 기준으로 약 0.1 내지 약 10중량% 범위의 양으로 존재하는 발포성 경화성 조성물.
- 제 4 항에 있어서, 상기 인이 폴리에폭시드 수지, 경화제의 첨가제 성분의 전체 중량을 기준으로 약 0.05내지 약 20중량% 범위의 양으로 존재하는 발포성 경화성 조성물.
- 제 1 항에 있어서, 강화 충진제를 추가로 포함하는 발포성 경화성 조성물.
- (a) 폴리에폭시드와 가용성 산 작용성 폴리에스테르의 에폭시 작용성 부가물, (b) 에폭시 작용성 부가물을 경화시키기에 적합한 경화제, 및 (c)(ⅰ) 아연, (ⅱ) 붕소, (ⅲ)인 및 (ⅳ) 열분해시의 팽창 가스의 공급원을 제공하기에 적합한 물질들의 혼합물을 함유한 첨가제 성분을 포함하고 있으며 ; 가열 또는 불꽃에 노출시 탄소질 챠콜을 형성할 수 있으며, 단, 2개의 열전쌍의 표면에 부착되어 있는 4W13 I-비임의 10in(0.254m)의 단면에 비연소된 경화성 조성물을 0.5in(12.7mm)의 두께로 도포하고, 주위 온도에서 16시간동안 경화시키고, 약 60℃에서 5일간 강제 경화시키고, 냉각 사이클 시험을 수행할 때, 비연소된 경화 조성물이 크래킹되지 않고 냉각 사이클 시험중의 최소한 10회 연속 사이클을 통과하는데 충분한 가요성을 가지며 ; 연소조건에 노출시 발포하는 경화성 조성물이 표면상에 도포되어 있음을 특징으로 하는, 연소조건에 노출시 감소된 온도상승률을 나타내는 기재(여기서, 상기 냉각 사이클 시험중의 한 사이클은 상기 비임을, 도막 밑에 있는 비임의 표면에 부착된 2개의 열전쌍에 의해 측정된 바와 같이, 강철이 약 0°F(-18℃)내지 약 -10°F(-23℃)의 온도에 도달하는데 충분한 시간동안 약 0°F(-18℃)내지 약 -10°F(-23℃)의 온도에서 작동하는 냉동기내에 위치시키고, 상기 비임을 냉동기로부터 꺼낸 다음, 비임의 표면주위로 이동되는 열전쌍에 의해 측정된 바와 같이, 상기 표면 온도가 3분 이내에 110°F(43℃)에 도달할때까지, 히트 건[Alpha Division of Loral Corp. 사제의 모델번호 HG 50146, 14 amp : 팁에서의 최소온도 500°F(260℃)]을 상기 표면으로부터 0.5in(12.7mm)의 간격을 두고 일정하게 통과시키므로써, 상기 표면의 50in2(0.323m2) 면적을 제 1 도 및 제 2 도에 나타난 바와 같이 가온시키고, 주위온도에서 최소한 2시간동안 방치시키는 것을 포함함).※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.