KR800000919B1

KR800000919B1 - Producing method of decorations for personal ornaments and furniture

Info

Publication number: KR800000919B1
Application number: KR790002203A
Authority: KR
Inventors: 양영남
Original assignee: 양영남
Priority date: 1979-07-03
Filing date: 1979-07-03
Publication date: 1980-09-10

Abstract

Shellfish and ferrouse mineral are used for broahes or buttons and their mold decorations. Their pieces are impregnated into the colour resin and hardened, and the surface is coated with resin of transparent of semitransparent, and to improve value of product, the surface is grinded flatly for appearance the sculpture and scraped the parts of projecting.

Description

How to make ornaments and upholstery

제1도는 수지를 가열시키는 상태의 단면도.1 is a cross-sectional view of a state in which a resin is heated.

제2도는 패류 및 비 철광석 조각을 함침시킨 수지의 평면도.2 is a plan view of a resin impregnated with shellfish and non-iron ore pieces.

제3도는 패류 및 비철광석 조각을 함침시켜 수지표피층을 형성하는 단면도.3 is a cross-sectional view of impregnating shellfish and pieces of non-ferrous ore to form a resin skin layer.

제4도는 이 발명의 일실시 단면도.4 is a cross-sectional view of one embodiment of the present invention.

제5도는 종래의 장신구 단면도.5 is a cross-sectional view of a conventional ornament.

제6도는 이 발명의 방법으로 완성된 장신구의 실시도.6 is an illustration of ornaments completed by the method of the present invention.

이 발명은 패류(貝類) 및 비철광석을 사용한 부로치, 펜단트, 버클, 머리장식구, 단추 및 가구류의 각종 모형장식, 악기형태의 장식품 등의 제조방법에 관한 것이다.The present invention relates to a method for manufacturing various types of ornaments such as brooch, pendants, buckles, headdresses, buttons and furniture using shellfish and non-ferrous ores, musical instruments and the like.

종래의 장신구나 장식품에 있어서는 반드시 투명수지를 이용하여 필요한 패류나 소라등을 투명수지내에 함침시켜 외부에서 투시할 수 있도록 하였으나, 불투명한 유색수지를 이용한 경우에는 이와같은 외부에서의 투시가 불가능하므로 패류나 비철광석의 조각을 수지가 굳기전에 수지표면에 불균일하게 산재시켜 수지가 굳은 후에 그 표면에 다시 투명수지를 도포하는 방법이 사용되어왔다. 그러나 이와 같이 할 경우에는 수지의 경화시간이 길기 때문에 수지표면에 산재시킨 패류 및 비철광석의 조각들이 수지내로 깊이 함침되어 외부에서 볼 수 없게 매몰되며 이를 방지하기 위하여 수지층을 얇게 할 경우에는 부분적으로 패류나 비철광석의 일부가 수지면보다 높게 돌출되어 조잡품이 되는등의 결점이 있었다.In the case of conventional ornaments or ornaments, the necessary shellfish or seashells must be impregnated in the transparent resin using transparent resin, so that they can be viewed from the outside. B. Nonferrous ore fragments have been unevenly scattered on the resin surface before the resin is hardened, and then the resin is applied to the surface after the resin is hardened. However, in this case, since the curing time of the resin is long, fragments of shellfish and non-ferrous ores scattered on the resin surface are deeply impregnated into the resin and buried invisible from the outside. Part of the shellfish and non-ferrous ores protruded higher than the surface of the water and became a crude product.

이 고안은 종래의 이와 같은 제결점을 시정하기 위하여 유색수지에 패류 및 비철광석의 조각을 함침경화시킨 후 경화된 수지의 상측을 평활한 상태로 연삭하여 투명 또는 반투명의 수지로 표면층을 피복토록 하므로서 매몰된 패류 및 비철광석의 조각이 표출되게 함은 물론 수지면보다 튀어나온 조각돌을 평면상태로 깎아버리게 되어 장신구나 장식품으로서의 가치를 높일 수 있는 장신구 및 장식품을 제공함에 목적이 있다.This design impregnates a piece of shellfish and non-ferrous ore to the colored resin to correct the conventional defects, and then ground the upper side of the cured resin in a smooth state to cover the surface layer with a transparent or translucent resin. The purpose of the present invention is to provide ornaments and ornaments that allow sculptures of buried shellfish and non-ferrous ores to be extruded, as well as scrapping fragments protruding from the surface of the water in a flat state.

이 발명을 첨부된 도면과 함께 상세히 설명하면 다음과 같다.This invention will be described in detail with reference to the accompanying drawings.

이 발명은 상온의 에폭시수지(1)등을 경화제와 혼합하여 용기(2)에 넣고 가열하여 액상으로 되었을 때 패류(3)등을 균일히 뿌려 고체유된 수지판(4)을 용기(2)에서 이탈시켜 그라인더로 갈고 평삭기계로 평활한 표면(5)을 형성하여 필요로 하는 형상의 형판(6)을 잘라낸 후 그 표면에 투명 또는 반투명의 수지(7)를 낙하시켜 100-200℃의 로 속에서 7-8시간에 걸쳐 수지표피층(8)을 형성토록 된 것이다.In the present invention, the epoxy resin (1) at room temperature is mixed with a curing agent, placed in a container (2), and heated to a liquid state. The grinder was removed from the grinder, and the smooth surface 5 was formed with a grinding machine to cut out the template 6 of the required shape, and then the transparent or semi-transparent resin 7 was dropped on the surface of the furnace at 100-200 ° C. The resin epidermal layer 8 was formed over 7-8 hours.

이 방명은 그라인더로 수지(1)를 갈아냄으로서 수지(1)에 매몰되었던 패류(3)나 비철광석이 균일히 표출되며 평삭기계로 재처리하므로서 패류(3) 및 비철광석이 갖는 고유의 색채가 표현되고 또한 투명 또는 반투명의 수지(7)를 예시도면 제3도와 같이 평활한 표면(5)의 상측에서 떨어뜨려서 수지표피층(8)을 형성하기 때문에 수지(7)의 표면장력으로 인하여 자연스러운 라운드형태의 수지표피층이 형성되어 내보 투시가 아름답게 됨은 물론 여러가지 특성을 갖는 수지의 사용이 가능하고 장신구의 종류와 용도에 따라서는 수지표피층(8)을 양면에 형성함이 가능하다.This visitor uses the grinder to grind the resin 1 so that shellfish 3 or non-ferrous ore that has been buried in the resin 1 can be uniformly displayed and reprocessed by a grinding machine, and the original color of shellfish 3 and non-iron ore can be achieved. Natural resin due to the surface tension of the resin 7 because the resin 7 is formed and the transparent or translucent resin 7 is dropped from the upper side of the smooth surface 5 as shown in FIG. The resin skin layer in the form is formed, which makes the perspective view beautiful, as well as the use of a resin having various properties, and the resin skin layer 8 can be formed on both sides depending on the type and use of the jewelry.

또한 장신구 및 패류의 종류에 따라 두께를 얇게 혹은 두텁게 할 수 있는 효과가 있다.In addition, there is an effect that can be thin or thick depending on the type of jewelry and shellfish.

Claims

Epoxy resin (1) at room temperature is mixed with a curing agent, placed in a container (2), and heated to a liquid state when the shell (3) is uniformly sprayed to remove the solidified resin plate (4) from the container (2). The surface of the mold (6) is cut out and the transparent or semi-transparent resin (7) is dropped on the surface to form a smooth surface (5) with a flattening machine. A method for producing ornaments and upholstery characterized in that the resin skin layer (8) is formed over eight hours.