KR20230092035A - 콘크리트 구조물용 친환경, 저온 경화성, 고내구성, 무용제형 에폭시 수지계 방수방식재 조성물 - Google Patents
콘크리트 구조물용 친환경, 저온 경화성, 고내구성, 무용제형 에폭시 수지계 방수방식재 조성물 Download PDFInfo
- Publication number
- KR20230092035A KR20230092035A KR1020210179365A KR20210179365A KR20230092035A KR 20230092035 A KR20230092035 A KR 20230092035A KR 1020210179365 A KR1020210179365 A KR 1020210179365A KR 20210179365 A KR20210179365 A KR 20210179365A KR 20230092035 A KR20230092035 A KR 20230092035A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- agent
- epoxy resin
- agents
- Prior art date
Abstract
본 발명은 콘크리트 구조물용 친환경, 저온 경화성, 고내구성의 무용제형 에폭시 수지계 방수방식재 조성물을 제공하는 것으로, 조성물은 주제와 경화제를 포함한다. 주제는, 비스페놀-F형 에폭시수지 55 내지 65 중량부, 탈크, 황산바륨, 견운모, 백운모, 실리카로 이루어지는 군에서 선택되는 1종 또는 2종 이상의 혼합물인 체질안료 20 내지 30 중량부, 유리 박편의 글라스 플레이크(Glass flake) 1 내지 5 중량부, 부착력 증강제 1 내지 5 중량부, 실란 커플링에이전트, 습윤·분산제, 소포·탈포제, 레벨링제, 침강방지제 및 흐름방지제로 이루어진 군에서 선택된 1종 또는 2종 이상의 혼합물인 첨가제 5 내지 10 중량부를 포함한다. 경화제는, 변성 지환족아민 40 내지 50 중량부, 폴리아마이드 15 내지 25 중량부, 페날카민 5 내지 15 중량부, 경화촉진제 5 내지 10 중량부, 습윤·분산제, 소포·탈포제, 레벨링제, 침강방지제 및 흐름방지제로 이루어진 군에서 선택된 1종 또는 2종 이상의 혼합물인 첨가제 2 내지 10 중량부를 포함한다. 여기서, 사용 시 주제와 및 경화제는 1 : 0.3 ~ 0.6 중량부의 중량 비율로 혼합되어 사용된다.
Description
본 발명은 동절기 저온에서도 경화건조가 가능한 콘크리트 구조물용 친환경, 저온 경화성, 및 고내구성의 무용제형 에폭시 수지계 방수방식재 조성물에 관한 것으로서, 상세히는 비스페놀-F형 에폭시수지와 변성 지환족 폴리아민, 폴리아마이드, 페날카민(Phenalkamine)계 경화제 및 기능성 무기 재료를 첨가하여 콘크리트 구조물용 방수·방식 도료를 제조함으로써 내수성, 내염수성, 내화학성, 내마모성, 내스크래치성 등 내식성이 우수한 도막을 형성하게 되는 콘크리트 구조물용 친환경 에폭시 수지계 방수·방식재 조성물에 관한 것이다.
에폭시수지 도료는 일반적으로 상·하수도관 등 강관용 도료, 철 구조물 등의 강재용 도료, 선박용 도료, 중방식 도료 및 콘크리트 구조물용 방수·방식 도료로써 산업 전반에 가장 광범위하게 사용된다.
일반적으로 비스페놀 A에 에피클로로하이드린의 중·축합 반응을 통하여 액상 BPA형 에폭시수지를 제조하여 많이 사용되며, 비스페놀 A와 ECH(Epichloro Hydrin)의 몰비를 조절하여 분자량 및 에폭시 당량에 따른 제품의 용도에 맞게 사용된다.
하지만 일반적으로 사용되는 에폭시수지의 경우 점도가 상온 25℃에서 25,000cps로 도료 제조시에 다량의 톨루엔, 자이렌 및 알코올류 등의 휘발성 유기 용제가 사용되며, 이로 기인하여 대기 환경 오염 및 작업자 인체에 유해한 결과를 초래한다.
또한, 이러한 액상 에폭시수지로 제조된 도료를 사용하는 경우, 에폭시 경화제와 경화 반응 후 생성된 도막이 취성을 가져 외부의 충격에 의해 쉽게 도막이 균열되고 그에 따라 외부 환경에 피도장물이 노출되어 구조물 등에 부식 등의 큰 결함을 야기한다.
뿐만 아니라 동절기 저온에서의 도장 작업시 건조 지연으로 인한 도막의 처짐과 변색 등 외관 결함과 부착성 불량으로 인한 도막의 품질 저하와 시공성 불량으로 인한 비용 증가 등 여러 가지 문제점이 상존한다.
최근 휘발성 유기 화합물(volatile organic compounds; VOC) 사용 규제에 따른 휘발성 유기 용제의 사용량이 규제되고 있는 실정이어서 이러한 문제를 해결할 수 있는 친환경, 고내구성의 무용제형 타입의 콘크리트 구조물용 방수·방식재에 대한 요청이 시급한 실정이다.
본 발명은 동절기 저온에서도 경화건조가 가능한 콘크리트 구조물용 친환경, 저온 경화성, 및 고내구성의 무용제형 에폭시 수지계 방수방식재 조성물을 제공하기 위한 것으로서, 비스페놀-F형 에폭시수지와 변성지환족 폴리아민, 폴리아마이드, 페날카민(Phenalkamine)계 경화제 및 기능성 무기 재료를 첨가하여 콘크리트 구조물용 방수·방식 도료를 제공함으로써 내수성, 내염수성, 내화학성, 내마모성, 내스크래치성 등 내식성이 우수한 도막을 형성하게 되는 친환경적, 무용제형, 저온 경화건조 가능한 콘크리트 구조물용 방수·방식재 조성물을 제공하기 위한 것이다.
또한, 본 발명에 따른 콘크리트 구조물용 친환경, 고내구성의 무용제형 에폭시 수지계 방수방식재 조성물은, 기능성 무기 재료를 함유함으로써 1회에 도막 두께 300㎛ 이상 도장이 가능하고, 인체에 유해한 휘발성 유기화합물(VOC)을 함유하지 않아, 용제의 휘발에 따른 환경 파괴, 생산설비의 오염, 인체에 대한 유해성 등의 문제가 없는 환경친화적이며, 치밀한 도막을 형성하여 구조물의 장기 내구성을 확보할 수 있는 기능성 무기 재료를 함유한 저온 경화형 친환경 고내구성의 무용제형 세라믹 에폭시 방수·방식재 조성물을 제공하기 위한 것이다.
본 발명은 상·하수도, 농업용수, 콘크리트 구조물 등의 수처리 및 폐수처리 시설물 등의 방수·방식에 사용되고, 주차장 등 바닥용 도료, 결로방지 도료, 내마모성 및 내스크래치성 도료로 사용이 가능하다.
상술한 과제를 해결하기 위하여 본 발명에 따른 콘크리트 구조물용 친환경, 저온 경화성, 고내구성의 무용제형 에폭시 수지계 방수방식재 조성물은, 주제와 경화제를 포함한다.
여기서, 주제는, 비스페놀-F형 에폭시수지 55 내지 65 중량부, 탈크, 황산바륨, 견운모, 백운모, 실리카로 이루어지는 군에서 선택되는 1종 또는 2종 이상의 혼합물인 체질안료 20 내지 30 중량부, 유리 박편의 글라스 플레이크(Glass flake) 1 내지 5 중량부, 부착력 증강제 1 내지 5 중량부, 실란 커플링에이전트, 습윤·분산제, 소포·탈포제, 레벨링제, 침강방지제 및 흐름방지제로 이루어진 군에서 선택된 1종 또는 2종 이상의 혼합물인 첨가제 5 내지 10 중량부를 포함한다.
경화제는, 변성 지환족아민 40 내지 50 중량부, 폴리아마이드 15 내지 25 중량부, 페날카민 5 내지 15 중량부, 경화촉진제 5 내지 10 중량부, 습윤·분산제, 소포·탈포제, 레벨링제, 침강방지제 및 흐름방지제로 이루어진 군에서 선택된 1종 또는 2종 이상의 혼합물인 첨가제 2 내지 10 중량부를 포함한다.
여기서, 사용 시 주제와 및 경화제는 1 : 0.3 ~ 0.6 중량부의 중량 비율로 혼합되어 사용된다.
본 발명에 따른 콘크리트 구조물용 친환경, 저온 경화성, 고내구성의 무용제형 에폭시 수지계 방수방식재 조성물은 비스페놀-F형 에폭시수지에 기능성 무기 재료와 페날카민(Phenalkamine) 등의 경화제가 첨가되어 제조되므로 동절기 저온에서도 경화건조가 가능하며, 내수성, 내염수성, 내화학성, 내마모성, 내스크래치성 등 내식성이 우수한 도막을 형성할 수 있고, 우수한 부착력을 얻을 수 있으며, 일반 에폭시 수지에 비해 인장강도, 굴곡강도, 내충격성 등에서 우수한 물성과 우수한 저온 경화성능을 얻을 수 있다.
또한, 1회에 도막 두께 300㎛ 이상 도장이 가능하고, 인체에 유해한 휘발성 유기화합물(VOC)을 함유하지 않아 환경 친화적이며, 그에 따라 용제의 휘발에 따른 환경 파괴, 생산설비의 오염, 인체에 대한 유해성 등의 문제가 없으며, 치밀한 도막을 형성하여 콘크리트 구조물의 장기 내구성을 확보할 수 있다.
이하 본 발명에 대하여 상세히 설명한다.
본 발명에 따른 동절기 저온에서도 경화건조가 가능한 콘크리트 구조물용 친환경, 고내구성의 무용제형 에폭시 수지계 방수방식재 조성물은 주제와 경화제의 2액형(2 성분형)으로서 본 발명의 바람직한 실시예들에 따라 각각 다음과 같은 조성을 갖는다:
비스페놀-F형 에폭시수지 55 내지 65 중량부, 색상안료 1 내지 5 중량부, 체질안료 20 내지 30 중량부, 글라스 플레이크(Glass flake) 1 내지 5 중량부, 부착력 증강제 1 내지 5 중량부, 첨가제 5 내지 10 중량부를 포함하는 주제; 및
변성 지환족아민 40 내지 50 중량부, 폴리아마이드 15 내지 25 중량부, 페날카민 5 내지 15 중량부, 경화촉진제 5 내지 10 중량부, 지르코늄옥사이드(ZrO2) 10 내지 20 중량부, 첨가제 2 내지 10 중량부를 포함하는 경화제;를 포함하여 조성된다.
여기서, 주제와 및 경화제는 1 : 0.3 ~ 0.6 중량부의 중량 비율로 혼합되어 콘크리트 구조물의 방수 방식을 위해 사용될 수 있다.
이하에서는 본 발명에 따른 방수 방식재 조성물을 구성하는 원료들 각각에 대하여 상세히 설명한다.
먼저, 주제를 이루는 원료 성분들을 보면, 비스페놀 F형 에폭시 수지는 비스페놀 A형 에폭시 수지의 분자 가운데 CH3 대신에 H가 있는 수지로서, 비스페놀 A형에 비해 저점도이며 가소성이 우수하며 고반응성이다. 전기전자재료로서 내열성 및 기계적 물성이 좋게 하기 위하여 필러의 고충진화가 지향되면서 저점도 에폭시수지가 개발 출시되고 있는데, 이러한 저점도 에폭시수지로서 비스페놀 F형 에폭시수지가 널리 알려져 있다. 비스페놀-F형 에폭시수지로는 에폭시 당량(EEW) 160∼180, 점도(Viscosity)는 25℃에서 600∼7,000cps 인 것을 사용한다.
일반적으로 에폭시수지로서 비스페놀 A형 에폭시수지가 널리 알려져 있고, 고형 에폭시수지로서는 비스페놀 A형 에폭시수지를 축합반응을 하여 분자량을 증대시킨 것이 사용되고 있으나 톨루엔, 자일렌 및 알코올류 등의 휘발성 유기용제를 첨가하여 용해시킨 후 사용하게 됨에 따라 대기 환경오염과 작업자 인체 유해성의 문제가 초래된다.
색상안료는 본 발명에 따른 콘크리트 구조물용 친환경, 고내구성의 무용제형 에폭시 수지계 방수·방식재 조성물에 포함되어 특정한 색상을 내기 위한 것으로, 이산화티타늄, 카본블랙, 프탈로시아닌그린, 프탈로시아닌블루로 이루어진 군에서 선택된 1종 또는 2종 이상의 혼합물인 유기·무기 안료가 사용될 수 있다.
체질안료는 도막의 내수성, 내화학성 및 기계적 특성 등을 강화하기 위하여 포함될 수 있는데, 탈크, 황산바륨, 견운모, 백운모, 실리카로 이루어지는 군에서 선택되는 1종 또는 2종 이상의 혼합물을 사용할 수 있다.
글라스 플레이크(Glass flake)는 편상의 세라믹계인 유리 박편이며, 콘크리트 구조물용 방수·방식재 도막의 내수성, 내염수성, 내화학성, 내마모성 및 내스크래치성 등의 물성을 증진시키기 위하여 사용될 수 있다.
부착력 증강제는 실란 커플링에이전트(Silane Coupling Agent) 계열로서, 2-(3,4 epoxycyclohexyl)ethyltrimethoxysilane, 3-Glycidoxypropyl methyldimethoxysilane, 3-Glycidoxypropyl trimethoxysilane, 3-Glycidoxypropyl methyldiethoxysilane, 3-Glycidoxypropyl triethoxysilane 중에서 1종 또는 2종 이상의 혼합물을 사용한다.
첨가제는 주제에 포함되어 주제의 물성을 안정화시키기 위하여 포함될 수 있는데, 실란 커플링에이전트, 습윤·분산제, 소포·탈포제, 레벨링제, 침강방지제 및 흐름방지제로 이루어진 군에서 선택된 1종 또는 2종 이상의 혼합물이 사용될 수 있다.
다음으로, 경화제는 변성 지환족아민, 폴리아마이드, 페날카민, 경화촉진제, 지르코늄옥사이드(ZrO2) 및 첨가제를 포함하는데, 본 발명에서 상기 주제 및 상기 경화제는 1 : 0.3 ~ 0.6 중량부의 중량 비율로 혼합되어 사용될 수 있다.
경화제의 조성 비율은 변성 지환족아민 40 내지 50 중량부, 폴리아마이드 15 내지 25 중량부, 페날카민 5 내지 15 중량부, 경화촉진제 5 내지 10 중량부, 지르코늄옥사이드(ZrO2) 10 내지 20 중량부, 첨가제 2 내지 10 중량부의 중량 비율로 조성된다.
변성지환족아민은 전 아민가(Total Amine value) 200∼550, 활성수소당량(Active Hydrogen Equivalent Weight) 50∼120 인 것을 사용한다.
폴리아마이드는 지방산(Fatty acid)과 TETA(Triethylenetetramine) 등의 아민과의 중·축합 반응으로 제조되며, 전 아민가(Total Amine value) 100∼450, 활성수소당량(Active Hydrogen Equivalent Weight) 60∼250 인 것을 사용한다.
페날카민(Phenalkamine)은 캐슈너트 쉘 액체(CNSL)로부터 합성될 수 있고, 폴리아마이드(저 독성, 우수한 유연성 및 내화학성)의 특성과 지방족 아민(빠른 경화, 우수한 내화학성)의 특성을 동시에 갖는다.
또한, 페날카민은 저온에서 뛰어난 경화 특성을 가지고 있으며, 이러한 특성 때문에 페날카민은 해양, 산업 유지 보수 및 토목공학 응용 분야에서 널리 사용되고 있다.
또한, 페날카민은 저온에서의 경화 특성(35°F), 비임계 혼합비(넓은 범위의 혼합비), 우수한 내수성, 유연성 및 다양한 유형의 에폭시 수지와의 우수한 혼화성(호환성), 불충분한 표면처리면에 대해서도 우수한 접착력을 가지며, 거의 모든 에폭시 도장에 적합한 경화제로서 기능할 수 있다.
더욱 상세하게 설명하면, 페닐카민(Phenalkamine)은 속건형이며 저온 경화성이 우수하고 습도가 높은 상황에서 우수한 성능을 발휘하는데, 페날카민을 포함하는 경화제의 가장 큰 장점은 뛰어난 저온 경화 성능을 갖는다는 것이다.
예를 들어, 동절기에 에폭시 도료를 도장할 때 발생하는 가장 큰 문제점으로 느린 경화로 인한 후속 공정 지연 및 도막 품질 저하를 들 수 있는데(저온에서 에폭시의 경화가 장기간 지연되면 주제와 경화제가 반응하지 않은 상태로 엉기게 되고 이것은 시간이 지나도 반응하지 않는다), 본 발명에서는 페날카민을 함유하는 경화제를 사용함으로써 이러한 현상들을 개선할 수 있다.
또한, 페날카민을 포함하는 경화제는 도장 초기의 수분에 강하다는 장점을 갖는데, 폐날카민 분자 특유의 소수성(Hydorphobic)은 물 분자와의 접촉에 의한 영향을 최소화하여 약간의 수분이 잔존하는 소재 위에도 도장이 가능하게 된다.
경화촉진제로는 도데실 페놀(Dodecyl Phenol), 3급 아민류(예 : Tris-2,4,6-dimethylaminomethyl phenol) 등을 사용한다.
지르코늄옥사이드(ZrO2)는 산과 알칼리에서도 거의 녹지 않고, 고온의 물속에서의 내식성은 다른 금속에 비해 월등히 우수하고, 기계적 특성 및 열전도도가 기존의 스테인레스 스틸계 및 티타늄계 소재와 유사한 특징이 있다.
즉, 지르코늄옥사이드(ZrO2)는 파인 세라믹스의 한 종류로서 하얀 결정질의 산화물로, 이것은 금속에 가장 가까운 세라믹 소재로서 우수한 기계적 성질로 인해 금속류의 단점을 보완하여 대체할 수 있는 소재이다. 또한, 밀도가 높고 열팽창률이 금속에 가까워서 금속과의 접합이 가능한 장점이 있다.
경화제의 첨가제는 경화제에 포함되어 경화제의 물성을 안정화시키기 위하여 포함될 수 있는데, 습윤·분산제, 소포·탈포제, 레벨링제, 침강방지제 및 흐름방지제로 이루어진 군에서 선택된 1종 또는 2종 이상의 혼합물이 사용될 수 있다.
이하, 본 발명에 따른 콘크리트 구조물용 친환경, 고내구성의 무용제형 에폭시 수지계 방수방식재 조성물에 대한 실시예 및 비교예를 들어 본 발명을 더욱 구체적으로 설명하기로 한다.
< 실시예 >
주제 및 경화제를 1:0.5의 중량 비율로 혼합하여 콘크리트 구조물용 친환경, 고내구성의 방수·방식재 조성물을 제조하였다.
이때, 상기 주제는 비스페놀 F형 에폭시수지 60 중량부, 색상안료 3 중량부, 체질안료 25 중량부, 글라스 플레이크(Glass flake) 3 중량부, 부착력 증강제 2.5 중량부 및 습윤·분산제로 구성된 첨가제 6.5 중량부의 중량 비율로 혼합하여 제조하였다.
또한, 상기 경화제는 변성 지환족아민 45 중량부, 폴리아마이드 20 중량부, 페날카민 10 중량부, 경화촉진제 7 중량부, 지르코늄옥사이드(ZrO2) 15 중량부 및 습윤·분산제로 구성된 첨가제 3 중량부의 중량 비율로 혼합하여 제조하였다.
< 비교예 >
시중에 판매되고 있는 콘크리트 구조물용 방수·방식재인 일반 에폭시수지 도료를 준비한 후 이를 비교예에 따른 에폭시수지 도료로 사용하였다.
1. 내화학성시험, 내수성시험 및 염수분무시험 결과
상기 실시예 및 비교예에 따른 콘크리트 구조물 방수·방식용 에폭시수지 도료의 내화학성시험, 내수성시험 및 염수분무시험을 수행하였고, 그 결과를 하기의 [표 1]에 나타내었다.
구분 | 실시예 | 비교예 | |
내화학성시험
(15일, 침적시험) |
5%-H2SO4 | 이상없음. 미세하게 변색됨 |
변색 심함, 미세 수포(Blister)
발생 |
5%-H3PO4 | 이상없음. 미세하게 변색됨 |
변색 심함, 미세 수포(Blister)
발생 |
|
5%-NaOH | 이상없음. 미세하게 변색됨 | 변색 심함 | |
5%-NaCl | 이상없음 | 미세하게 변색됨 | |
5%-EtOH | 이상없음 | 미세하게 변색됨 | |
내수성시험(1,000시간 침적시험)) | 이상없음 | 수포 발생 및 발청됨 | |
염수분무시험(500시간)) | 이상없음 | 수포 발생 및 발청됨 |
내화학성시험은 5종의 시약을 5% 수용화하여 15일간 침적시험을 실시하였다.
내수성시험은 50℃의 항온수조에 시험편을 침적하여 실시하였으며, 염수분무시험은 KS D-9502, Salt Spray Test로 실시하였다.
상기 [표 1]을 참조하면, 본 발명의 실시예에 따른 콘크리트 구조물용 친환경, 저온 경화성, 고내구성 방수·방식재 조성물을 사용하여 콘크리트 구조물에 적용한 경우, 비교예에 비하여 내화학성시험, 내수성시험 및 염수분무시험에서의 성능이 우수한 것을 확인할 수 있다.
2. 도막 물성시험 결과
상기 실시예 및 비교예에 따른 콘크리트 구조물용 방수·방식재의 인장강도, 굴곡강도, 내충격성, 내마모성, 연필경도, 수증기 투과율 등의 물성을 측정하였고, 그 결과를 하기의 [표 2]에 나타내었다.
구분 | 실시예 | 비교예 |
인장강도(MPa) | 46.8 | 35.2 |
굴곡강도(MPa) | 66.8 | 49.9 |
내충격성(500g×1/2inch×50cm) | 이상없음 | 미세크랙 발생 |
내마모성(mg) | 75 | 129 |
연필경도 | 4H 이상 | 2H |
수증기 투과율(g/m 2 *?*24hr) | 0.07 | 0.15 |
상기 [표 2]를 참조하면, 본 발명의 실시예에 따른 콘크리트 구조물용 친환경, 고내구성 방수·방식재 조성물을 사용하여 콘크리트 구조물에 적용한 경우, 일반 에폭시수지 도료(비교예)에 비해 인장강도, 굴곡강도, 내충격성, 내마모성, 연필경도, 수증기 투과율 등의 물성이 우수한 것을 확인할 수 있었다.
3. 저온 경화성능 시험 결과
상기 실시예 및 비교예 각각에 따른 에폭시수지 도료의 온도별 건조시간을 측정하여 저온 경화성능을 시험하였고, 그 결과를 하기의 [표 3]에 나타내었다.
온도
(℃) |
고화건조(시간) | |
실시예 | 비교예 | |
0℃ | 40.0 | 72.0 |
5℃ | 25.0 | 48.0 |
25℃ | 8.5 | 19.0 |
상기 [표 3]을 참조하면, 본 발명의 실시예에 따른 방수·방식재 조성물은 비교예에 따른 에폭시수지 도료와 비교하여 저온경화성능(5℃, 고화건조시간)이 25시간(hrs)으로 월등히 우수함을 확인할 수 있었다.
따라서, 본 발명의 실시예에 따른 에폭시 수지계 방수방식재 조성물을 도료로 사용하는 경우, 시공 시간이 약 1/2 정도 단축될 수 있음을 확인할 수 있다.
Claims (3)
- 비스페놀-F형 에폭시수지 55 내지 65 중량부, 탈크, 황산바륨, 견운모, 백운모, 실리카로 이루어지는 군에서 선택되는 1종 또는 2종 이상의 혼합물인 체질안료 20 내지 30 중량부, 유리 박편의 글라스 플레이크(Glass flake) 1 내지 5 중량부, 부착력 증강제 1 내지 5 중량부, 실란 커플링에이전트, 습윤·분산제, 소포·탈포제, 레벨링제, 침강방지제 및 흐름방지제로 이루어진 군에서 선택된 1종 또는 2종 이상의 혼합물인 첨가제 5 내지 10 중량부를 포함하는 주제; 및
변성 지환족아민 40 내지 50 중량부, 폴리아마이드 15 내지 25 중량부, 페날카민 5 내지 15 중량부, 경화촉진제 5 내지 10 중량부, 습윤·분산제, 소포·탈포제, 레벨링제, 침강방지제 및 흐름방지제로 이루어진 군에서 선택된 1종 또는 2종 이상의 혼합물인 첨가제 2 내지 10 중량부를 포함하는 경화제;를 포함하며,
여기서, 주제와 및 경화제는 1 : 0.3 ~ 0.6 중량부의 중량 비율로 혼합되어 사용되는 것을 특징으로 하는 콘크리트 구조물용 친환경, 저온 경화성, 고내구성의 무용제형 에폭시 수지계 방수방식재 조성물. - 제1항에 있어서,
상기 경화제는 지르코늄옥사이드(ZrO2) 10 내지 20 중량부를 더 포함하는 것을 특징으로 하는 콘크리트 구조물용 친환경, 저온 경화성, 고내구성의 무용제형 에폭시 수지계 방수방식재 조성물. - 제1항에 있어서,
비스페놀-F형 에폭시수지는 에폭시 당량(EEW) 160∼180, 점도(Viscosity)는 25℃에서 600∼7,000cps 인 것을 특징으로 하는 콘크리트 구조물용 친환경, 저온 경화성, 고내구성 무용제형 에폭시 수지계 방수방식재 조성물.