KR20220095126A - Gel composition and kit comprising physically crosslinked polymer hyaluronic acid or salt thereof - Google Patents
Gel composition and kit comprising physically crosslinked polymer hyaluronic acid or salt thereof Download PDFInfo
- Publication number
- KR20220095126A KR20220095126A KR1020210183044A KR20210183044A KR20220095126A KR 20220095126 A KR20220095126 A KR 20220095126A KR 1020210183044 A KR1020210183044 A KR 1020210183044A KR 20210183044 A KR20210183044 A KR 20210183044A KR 20220095126 A KR20220095126 A KR 20220095126A
- Authority
- KR
- South Korea
- Prior art keywords
- composition
- hyaluronic acid
- salt
- acid
- molecular weight
- Prior art date
Abstract
Description
본 명세서에는 물리적으로 가교된 고분자 히알루론산 또는 그 염을 고함량으로 포함하는 겔 조성물 및 키트가 개시된다.Disclosed herein are gel compositions and kits comprising physically cross-linked polymeric hyaluronic acid or a salt thereof in a high content.
종래의 유액형태의 화장품 제형에서 점도를 조절하기 위해서는 카보머, 천연 또는 합성 고분자 등을 적용을 고려해왔으나 단순히 선형고분자를 적용할 경우 특이 사용감 구현 측면에서 한계가 있다. 이러한 한계를 극복하기 위하여, 겔화된 수용성 고분자를 활용하여 고점도의 조성물을 제조할 수 있으며, 특히 히알루론산을 이용하여 고점도 조성물을 제조할 수 있다. In order to control the viscosity in the conventional emulsion type cosmetic formulation, it has been considered to apply carbomer, natural or synthetic polymer, etc., but when simply applying a linear polymer, there is a limit in terms of realizing a specific feeling of use. In order to overcome this limitation, a high-viscosity composition can be prepared by using a gelled water-soluble polymer, and in particular, a high-viscosity composition can be prepared using hyaluronic acid.
이 때, 겔화된 히알루론산을 제조하는 다양한 메커니즘이 존재한다. 예컨대, 히알루론산의 화학적 가교 방법으로는, 히알루론산을 개질시켜 브릿지제(bridge agent)를 이용해 가교시키거나(ex: HA-NH2), 히알루론산에 직접 크로스-링커(cross-linker)를 반응시켜 가교시킬 수 있다(ex: HA-BDDE-HA (BDDE : 에테르류)). 다만, 히알루론산을 화학적으로 가교시키는 경우, 화학 제품을 사용하거나, 화학반응 환경을 형성하기 위한 버퍼 사용 시 독성우려 또는 화학반응을 위한 특정 pH 조건 또는 온도 조건이 요구되는 경우가 많아, 합성 후 중화공정이 수반되므로, 공정이 매우 복잡하고 양산성이 떨어질 수 있다. At this time, various mechanisms for producing gelled hyaluronic acid exist. For example, as a chemical crosslinking method of hyaluronic acid, hyaluronic acid is modified and crosslinked using a bridge agent (ex: HA-NH 2 ), or a direct cross-linker is reacted with hyaluronic acid. and cross-linking (ex: HA-BDDE-HA (BDDE: ethers)). However, when chemically crosslinking hyaluronic acid, chemical products or buffers to form a chemical reaction environment are often required for toxicity concerns or specific pH conditions or temperature conditions for chemical reactions, so neutralize after synthesis Since the process is involved, the process may be very complicated and productivity may be poor.
따라서, 화학적 가교제의 사용없이 가교된 히알루론산을 포함하면서도, 고점도를 가지는 조성물의 개발이 요구된다. Therefore, it is required to develop a composition having a high viscosity while including the cross-linked hyaluronic acid without the use of a chemical cross-linking agent.
본 개시의 일 측면에서, 물리적으로 가교된 히알루론산을 포함하여, 기존대비 점도, 끈적임, 점탄성이 높은 유액 형태를 가지며, 히알루론산을 고함량으로 포함하여도 때밀림과 끈적임이 없고 산뜻함이 향상된 겔 조성물을 제공하고자 한다. In one aspect of the present disclosure, including physically cross-linked hyaluronic acid, it has an emulsion form with high viscosity, stickiness, and viscoelasticity compared to the existing ones, and even contains a high content of hyaluronic acid. It is intended to provide a composition.
일 측면에서, 본 명세서는 고분자 히알루론산 또는 그 염, n가 알코올(n은 1 내지 10), 및 산성 pH 조절제를 포함하고, 상기 고분자 히알루론산 또는 그 염은 n가 알코올에 의해 물리적으로 가교되며, pH가 3 이상인, 겔 조성물을 제공한다. In one aspect, the present specification includes a polymeric hyaluronic acid or a salt thereof, an n-hydric alcohol (n is 1 to 10), and an acidic pH adjuster, wherein the polymeric hyaluronic acid or a salt thereof is physically crosslinked by an n-hydric alcohol, , wherein the pH is 3 or higher.
다른 일 측면에서, 본 명세서는 고분자 히알루론산 또는 그 염 및 n가 알코올(n은 1 내지 10)을 포함하여 상기 고분자 히알루론산 또는 그 염이 n가 알코올에 의해 물리적으로 가교되어 포함되는 제1 제; 및 산성 pH 조절제를 포함하는 제2 제;를 포함하고, 상기 제1 제 및 제2 제가 혼합되어 겔이 형성되며, 상기 겔의 pH가 3 이상인, 화장품 키트를 제공한다.In another aspect, the present specification provides a first agent comprising a polymer hyaluronic acid or a salt thereof and an n-hydric alcohol (n is 1 to 10), wherein the polymer hyaluronic acid or a salt thereof is physically cross-linked with an n-hydric alcohol ; and a second agent including an acidic pH adjusting agent; wherein the first agent and the second agent are mixed to form a gel, and the pH of the gel is 3 or more, it provides a cosmetic kit.
일 측면에 있어서, 물리적으로 가교된 히알루론산을 포함하여 사용자들에게 시각적인 베네핏을 주면서도, 도포시 피부 탄력 향상에 대한 인지 효능도 부여할 수 있다. 더불어, 충분한 양의 수분을 담지하여 높은 수분 유지력과 특이 사용감을 줄 수 있다는 장점이 있다.In one aspect, it is possible to provide a visual benefit to users by including physically cross-linked hyaluronic acid, while also providing a cognitive effect for improving skin elasticity when applied. In addition, there is an advantage that it can hold a sufficient amount of moisture to provide high moisture retention and a special feeling of use.
다른 일 측면에 있어서, 본 개시는 유화 조성물 또는 가용화 조성물 모두에 적용이 가능하여, 소비자 타깃, 조성물의 용도 등에 따라 다양한 제형으로 제공할 수 있다.In another aspect, the present disclosure can be applied to both emulsified compositions or solubilized compositions, and can be provided in various formulations according to consumer targets, uses of the composition, and the like.
도 1는 본 개시의 일 실시예에 따른 조성물의 겔링 반응에 따른 점탄성 변화를 측정한 결과이다.
도 2는 pH에 따른 히알루론산 하이드로겔 물성 변화에 관한 그래프이다.
도 3은 본 개시의 일 실시예에 따른 조성물의 보습 효과에 관한 그래프이다.(y축 단위: %)
도 4는 히알루론산 함량에 따른 하이드로겔 물성 변화에 관한 그래프이다.
도 5는 폴리올, 에탄올 첨가에 따른 조성물의 등전점의 이동에 관한 것이다.1 is a result of measuring the change in viscoelasticity according to the gelling reaction of a composition according to an embodiment of the present disclosure.
2 is a graph relating to the change in the physical properties of the hyaluronic acid hydrogel according to the pH.
3 is a graph relating to the moisturizing effect of the composition according to an embodiment of the present disclosure. (Y-axis unit: %)
4 is a graph relating to the change of hydrogel physical properties according to the content of hyaluronic acid.
5 is related to the shift of the isoelectric point of the composition according to the addition of polyol and ethanol.
이하, 하기의 실시예를 통하여 본 개시를 보다 구체적으로 설명한다. 그러나 하기의 실시에는 본 개시에 대한 이해를 돕기 위해 예시의 목적으로만 제공된 것일 뿐, 본 개시의 범주 및 범위가 이에 한정되지 않는다.Hereinafter, the present disclosure will be described in more detail through the following examples. However, the following examples are provided only for the purpose of illustration to help the understanding of the present disclosure, and the scope and scope of the present disclosure are not limited thereto.
본 명세서에서, 어떤 부분이 어떤 구성 요소를 "포함"한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성 요소를 제외하는 것이 아니라 다른 구성 요소를 더 포함할 수 있는 것을 의미한다.In the present specification, when a part "includes" a certain component, this means that other components may be further included rather than excluding other components unless otherwise stated.
이하, 본 개시를 상세히 설명한다.Hereinafter, the present disclosure will be described in detail.
본 개시의 예시적인 구현예들에서는, 고분자 히알루론산 또는 그 염, n가 알코올(n은 1 내지 10) 및 산성 pH 조절제를 포함하고, 상기 고분자 히알루론산 또는 그 염은 n가 알코올에 의해 물리적으로 가교되며, pH가 3 이상인, 겔 조성물을 제공한다. In exemplary embodiments of the present disclosure, it includes a high molecular weight hyaluronic acid or a salt thereof, an n-hydric alcohol (n is 1 to 10) and an acidic pH adjusting agent, and the high molecular weight hyaluronic acid or a salt thereof is physically by n-hydration alcohol. It provides a gel composition that is crosslinked and has a pH of at least 3.
본 명세서 내 "히알루론산(Hyaluronic acid)"이라 함은 음이온성 천연다당류로 염의 형태(salt form)로 존재하며 EWG 등급 1에 해당하는 원료이다. 주로 미생물을 통해 생산 및 정제가 이루어 지는데 사람의 체내 연결조직과 세포외기질에 존재하고, 음이온성 작용기로 인한 수분함유량이 높아 보습제로 많이 사용된다. 히알루론산의 분자 구조는 하기 화학식 1로 표시될 수 있고, 본 명세서에서는 히알루론산의 염의 형태로 포함될 수 있다. In the present specification, "hyaluronic acid" is an anionic natural polysaccharide that exists in salt form and is a raw material corresponding to
[화학식 1][Formula 1]
(상기 x은 1300 ~ 8000이다)(where x is 1300 to 8000)
상기 x의 단위는 mol이다. The unit of x is mol.
본 개시의 일 구현예에서는, 물에 녹거나 분산되어 농후 또는 겔화 효과를 낼 수 있는 친수성 고분자인 히알루론산을 포함하였으며, 산성 용액 내 수소 이온의 존재 하에 히알루론산의 음이온 형태가 프로톤화(protonation) 되며 물성이 강해지는 특성을 이용하였다. In one embodiment of the present disclosure, hyaluronic acid, which is a hydrophilic polymer that can be dissolved or dispersed in water to produce a thickening or gelling effect, is included, and in the presence of hydrogen ions in an acidic solution, the anion form of hyaluronic acid is protonated and the property of strengthening the physical properties was used.
본 개시의 일 실시예는 히알루론산을 화장료 조성물에 적용하기 위해, n가 알코올(n은 1 내지 10) 및/또는 폴리올을 적용하여 히알루론산이 겔과 같은(gel-like) 물성을 띄는, 즉 히알루론산의 용해도를 감소시킬 수 있는 등전점을 pH 3 이상이 되도록 적용하여, 겔화가 이루어진 유액 제형 내용물의 경우 물성면에서 현저히 우수한 효과를 보일 수 있다. In one embodiment of the present disclosure, in order to apply hyaluronic acid to a cosmetic composition, n-hydric alcohol (n is 1 to 10) and/or polyol is applied so that hyaluronic acid has gel-like properties, that is, By applying an isoelectric point capable of reducing the solubility of hyaluronic acid to be
유통화장품 안전관리 기준 상 로션/크림을 포함한 기초 화장용 제품류는 pH 기준이 3.0~9.0으로 되어있어, pH 3 이하에서는 화장료 조성물로 적용이 어려울 수 있다. 이는 피부 pH가 5~6으로 약산성 영역대를 유지하고 있기 때문이며, pH 3 이하로 떨어질 경우 피부에 자극이 될 수 있다. 일 실시예로서, 상기 조성물의 pH는 3 이상, 3.1 이상, 3.2 이상, 3.3 이상, 3.4 이상일 수 있다. According to distribution cosmetic safety management standards, basic cosmetic products including lotions/creams have a pH standard of 3.0 to 9.0, so it may be difficult to apply as a cosmetic composition at a pH of 3 or less. This is because the skin pH is in the weakly acidic range of 5 to 6, and when the pH falls below 3, it may irritate the skin. In one embodiment, the pH of the composition may be 3 or more, 3.1 or more, 3.2 or more, 3.3 or more, 3.4 or more.
일 구현예에서, 상기 고분자 히알루론산의 염은 히알루론산 나트륨일 수 있다. In one embodiment, the salt of the polymer hyaluronic acid may be sodium hyaluronate.
일 구현예에서, 상기 고분자 히알루론산 또는 그 염의 함량은 상기 조성물 총 중량을 기준으로 0.1 내지 5 중량%일 수 있다. 예컨대, 상기 고분자 히알루론산 또는 그 염의 함량은 상기 조성물 총 중량을 기준으로 0.1 중량% 이상, 0.3 중량% 이상, 0.5 중량% 이상, 0.6 중량% 이상, 0.7 중량% 이상, 0.8 중량% 이상, 0.9 중량% 이상, 1.0 중량% 이상, 1.1 중량% 이상, 1.2 중량% 이상, 1.3 중량% 이상, 1.5 중량% 이상, 1.7 중량% 이상, 2 중량% 이상, 3 중량% 이상, 또는 4 중량% 이상일 수 있고, 5 중량% 이하, 4중량% 이하, 3 중량% 이하, 2.5 중량% 이하, 2 중량% 이하, 1.7 중량% 이하, 1.5 중량% 이하, 1.3 중량% 이하, 1.2 중량% 이하, 1.1 중량% 이하, 1 중량% 이하, 0.9 중량% 이하, 0.8 중량% 이하, 0.7 중량% 이하 또는 0.5 중량% 이하일 수 있다. 상기 함량이 0.1 중량% 미만인 경우 보습력이 떨어지고 겔 형성이 어려울 수 있고, 5 중량% 초과인 경우 발림성이 좋지 않을 수 있다. In one embodiment, the content of the polymer hyaluronic acid or its salt may be 0.1 to 5% by weight based on the total weight of the composition. For example, the content of the polymeric hyaluronic acid or its salt is 0.1 wt% or more, 0.3 wt% or more, 0.5 wt% or more, 0.6 wt% or more, 0.7 wt% or more, 0.8 wt% or more, 0.9 wt% based on the total weight of the composition. % or more, 1.0 wt% or more, 1.1 wt% or more, 1.2 wt% or more, 1.3 wt% or more, 1.5 wt% or more, 1.7 wt% or more, 2 wt% or more, 3 wt% or more, or 4 wt% or more, and , 5 wt% or less, 4 wt% or less, 3 wt% or less, 2.5 wt% or less, 2 wt% or less, 1.7 wt% or less, 1.5 wt% or less, 1.3 wt% or less, 1.2 wt% or less, 1.1 wt% or less , 1 wt% or less, 0.9 wt% or less, 0.8 wt% or less, 0.7 wt% or less, or 0.5 wt% or less. If the content is less than 0.1% by weight, the moisturizing power may decrease and gel formation may be difficult, and if it is more than 5% by weight, the spreadability may be poor.
일 구현예에서, 상기 n가 알코올(n은 1 내지 10)은 메탄올, 에탄올, 프로판올 및 부탄올로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있다. 예를 들어, 상기 n가 알코올은 1가 알코올 또는에탄올일 수 있다. In one embodiment, the n-hydric alcohol (n is 1 to 10) may include one or more selected from the group consisting of methanol, ethanol, propanol and butanol. For example, the n-hydric alcohol may be a monohydric alcohol or ethanol.
일 구현예에서, 상기 산성 pH 조절제는 산 및 글루코노락톤(Gluconolactone) 및 과일 추출물로 이루어진 군에서 선택된 하나 이상을 포함할 수 있으나, 스킨케어 제품에 pH를 낮추는 목적이면 제한 없이 사용할 수 있다. 일 실시예로서, 상기 산은 유기산 또는 무기산일 수 있다. 구체적으로, 상기 산은 저분자 히알루론산, 시트릭산, 락틱산, 아스코르빅애씨드, 소듐 피루베이트(sodium pyruvate) 또는 석신산(Succinic acid)에서 선택된 것 일 수 있다. 일 실시예로서, 상기 과일 추출물은 빌베리 열매 추출물(VACCINIUM MYRTILLUS FRUIT EXTRACT), 사탕수수 열매 추출물(SACCHARUM OFFICINARUM EXTRACT), 오렌지 열매 추출물(CITRUS AURANTIUM DULCIS FRUIT EXTRACT) 또는 레몬 열매 추출물(CITRUS LIMON FRUIT EXTRACT) 등에서 선택된 것일 수 있다. In one embodiment, the acidic pH adjusting agent may include at least one selected from the group consisting of acid and gluconolactone and fruit extract, but may be used without limitation as long as it is for the purpose of lowering the pH in skin care products. In one embodiment, the acid may be an organic acid or an inorganic acid. Specifically, the acid may be selected from low molecular weight hyaluronic acid, citric acid, lactic acid, ascorbic acid, sodium pyruvate, or succinic acid. In one embodiment, the fruit extract is bilberry fruit extract (VACCINIUM MYRTILLUS FRUIT EXTRACT), sugar cane fruit extract (SACCHARUM OFFICINARUM EXTRACT), orange fruit extract (CITRUS AURANTIUM DULCIS FRUIT EXTRACT) or lemon fruit extract (CITRUS LIMON FRUIT EXTRACT), etc. may be selected.
일 구현예에서, 상기 산은 저분자 히알루론산을 포함하고, 상기 고분자 히알루론산 또는 그 염의 중량평균분자량은 700 내지 3,000 kDa 이며, 상기 저분자 히알루론산의 중량평균분자량은 2 내지 100 kDa일 수 있고, 또는 상기 고분자 히알루론산 또는 그 염의 중량평균분자량은 1,300 내지 1,700 kDa 이며, 상기 저분자 히알루론산의 중량평균분자량은 3 내지 7 kDa일 수 있다. In one embodiment, the acid includes low molecular weight hyaluronic acid, the weight average molecular weight of the high molecular weight hyaluronic acid or a salt thereof is 700 to 3,000 kDa, and the weight average molecular weight of the low molecular weight hyaluronic acid may be 2 to 100 kDa, or the The high molecular weight hyaluronic acid or its salt may have a weight average molecular weight of 1,300 to 1,700 kDa, and the low molecular weight hyaluronic acid may have a weight average molecular weight of 3 to 7 kDa.
예컨대, 상기 고분자 히알루론산 또는 그 염의 중량평균분자량은 700 kDa 이상, 900 kDa 이상, 1,100 kDa 이상, 1,300 kDa 이상, 1,400 kDa 이상, 1,500 kDa 이상, 또는 1,600 kDa 이상일 수 있고, 3,000 kDa 이하, 2,700 kDa 이하, 2,400 kDa 이하, 2,100 kDa 이하, 1,700 kDa 이하, 1,600 kDa 이하, 1,500 kDa 이하, 또는 1,400 kDa 이하일 수 있으며, 상기 저분자 히알루론산의 중량평균분자량은 2 kDa 이상, 3 kDa 이상, 4 kDa 이상, 5 kDa 이상, 또는 6 kDa 이상일 수 있고, 100 kDa 이하, 50 kDa 이하, 40 kDa 이하, 30 kDa 이하, 20 kDa 이하, 10 kDa 이하, 7 kDa 이하, 6 kDa 이하, 5 kDa 이하, 또는 4 kDa 이하일 수 있다. For example, the weight average molecular weight of the polymer hyaluronic acid or its salt may be 700 kDa or more, 900 kDa or more, 1,100 kDa or more, 1,300 kDa or more, 1,400 kDa or more, 1,500 kDa or more, or 1,600 kDa or more, 3,000 kDa or less, 2,700 kDa or more or less, 2,400 kDa or less, 2,100 kDa or less, 1,700 kDa or less, 1,600 kDa or less, 1,500 kDa or less, or 1,400 kDa or less, and the weight average molecular weight of the low molecular weight hyaluronic acid is 2 kDa or more, 3 kDa or more, 4 kDa or more, 5 kDa or more, or 6 kDa or more, and 100 kDa or less, 50 kDa or less, 40 kDa or less, 30 kDa or less, 20 kDa or less, 10 kDa or less, 7 kDa or less, 6 kDa or less, 5 kDa or less, or 4 kDa or less. may be below.
상기 고분자 히알루론산 또는 그 염의 중량평균분자량이 700 kDa 미만인 경우 보습 효과가 떨어질 수 있고, 상기 저분자 히알루론산의 중량평균분자량이 100 kDa 초과인 경우 피부 투과가 어려울 수 있다.When the weight average molecular weight of the high molecular weight hyaluronic acid or its salt is less than 700 kDa, the moisturizing effect may be reduced, and when the weight average molecular weight of the low molecular weight hyaluronic acid is more than 100 kDa, skin penetration may be difficult.
일 구현예에서, 상기 조성물은 폴리올을 더 포함할 수 있다. 상기 폴리올은 글리세린, 프로필렌글리콜, 부틸렌글리콜, 글리세롤, 에리스리톨, 자일리톨, 말티톨글리세린, 소르비톨, 폴리글리세린, 폴리에틸렌글리콜, 펜탄디올, 및 이소프렌글리콜로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있다. In one embodiment, the composition may further include a polyol. The polyol may include at least one selected from the group consisting of glycerin, propylene glycol, butylene glycol, glycerol, erythritol, xylitol, maltitol glycerin, sorbitol, polyglycerin, polyethylene glycol, pentanediol, and isoprene glycol.
일 구현예에서, 상기 조성물은 폴리올을 더 포함하고, 상기 조성물 전체 중량을 기준으로, 고분자 히알루론산 또는 그 염 0.1 내지 5 중량%; n가 알코올(n은 1 내지 10) 0.1 내지 30 중량%; 산 0.1 내지 10 중량%; 및 폴리올 0.1 내지 30 중량%;를 포함할 수 있다. In one embodiment, the composition further comprises a polyol, based on the total weight of the composition, 0.1 to 5% by weight of a polymer hyaluronic acid or a salt thereof; 0.1 to 30% by weight of an n-hydric alcohol (n is 1 to 10); 0.1 to 10% by weight of acid; and 0.1 to 30% by weight of polyol.
일 구현예에서, 상기 조성물의 점도는 5,000 cps 이상일 수 있다. 예컨대, 5,000 cps 이상, 5,500 cps 이상, 6,000 cps 이상, 6,500cps 이상, 7,000 cps 이상, 7,500 cps 이상, 8000 cps 이상일 수 있고, 50,000 cps 이하일 수 있다. 본 개시의 일 측면에서, 5,000 cps 이상의 고점도를 가지면서도 때밀림과 끈적임이 개선된 조성물을 제공할 수 있다. In one embodiment, the viscosity of the composition may be 5,000 cps or more. For example, 5,000 cps or more, 5,500 cps or more, 6,000 cps or more, 6,500 cps or more, 7,000 cps or more, 7,500 cps or more, 8000 cps or more, and 50,000 cps or less. In one aspect of the present disclosure, it is possible to provide a composition having a high viscosity of 5,000 cps or more while improving smudging and stickiness.
일 구현예에서, 상기 조성물은 가용화제를 더 포함할 수 있다. 가용화제란 물에 용해되지 않는 물질을 가용화하기 위해 사용되는 계면 활성제로, 주로 폴리(옥시에틸렌)알킬에테르, 폴리(옥시에틸렌)알킬페닐에테르 같은 비이온 계면 활성제가 사용된다. 상기 가용화제는 PPG-13-데실테트라데세스-24(PPG-13-DECYLTETRADECETH-24), 폴리글리세릴-6 카프레이트(POLYGLYCERYL-6 CAPRYLATE), POLYGLYCERYL-4 CAPRATE, 폴리글리세릴-5 트리올레이트(POLYGLYCERYL-5 TRIOLEATE), 폴리글리세릴-10 라우레이트(POLYGLYCERYL-10 LAURATE), PEG-60 하이드로제네이티드 캐스트롤 오일(PEG-60 HYDROGENATED CASTOR OIL) 등을 포함할 수 있다.In one embodiment, the composition may further include a solubilizer. A solubilizer is a surfactant used to solubilize substances that are not soluble in water, and nonionic surfactants such as poly(oxyethylene)alkyl ether and poly(oxyethylene)alkylphenyl ether are mainly used. The solubilizer is PPG-13-decyltetradeceth-24 (PPG-13-DECYLTETRADECETH-24), polyglyceryl-6 caprate (POLYGLYCERYL-6 CAPRYLATE), POLYGLYCERYL-4 CAPRATE, polyglyceryl-5 triol POLYGLYCERYL-5 TRIOLEATE, POLYGLYCERYL-10 LAURATE, PEG-60 Hydrogenated Castrol Oil (PEG-60 HYDROGENATED CASTOR OIL), and the like.
일 구현예에서, 상기 조성물 전체 중량을 기준으로 상기 가용화제를 0.01 내지 5 중량% 포함할 수 있고, 예컨대, 상기 가용화제를 0.01 중량% 이상, 0.05 중량% 이상, 0.1 중량% 이상, 0.15 중량% 이상, 0.2 중량% 이상, 0.25 중량% 이상, 0.3 중량% 이상, 0.4 중량% 이상, 0.5 중량% 이상, 1중량% 이상, 2중량% 이상, 3중량% 이상, 또는 4중량% 이상 포함할 수 있고, 5중량% 이하, 4중량% 이하, 3.5중량% 이하, 3중량% 이하, 2.5중량% 이하, 2중량% 이하, 1.5중량% 이하, 1량% 이하, 0.5중량% 이하, 0.1중량% 이하, 또는 0.05 중량% 이하 포함할 수 있다.In one embodiment, based on the total weight of the composition, it may contain 0.01 to 5% by weight of the solubilizing agent, for example, 0.01% by weight or more, 0.05% by weight or more, 0.1% by weight or more, 0.15% by weight of the solubilizing agent or more, 0.2 wt% or more, 0.25 wt% or more, 0.3 wt% or more, 0.4 wt% or more, 0.5 wt% or more, 1 wt% or more, 2 wt% or more, 3 wt% or more, or 4 wt% or more 5 wt% or less, 4 wt% or less, 3.5 wt% or less, 3 wt% or less, 2.5 wt% or less, 2 wt% or less, 1.5 wt% or less, 1 wt% or less, 0.5 wt% or less, 0.1 wt% or less or less, or 0.05 wt% or less.
일 구현예에서, 상기 조성물은 유화 조성물 또는 가용화(solubilization) 조성물일 수 있다. In one embodiment, the composition may be an emulsion composition or a solubilization composition.
일 구현예에서, 상기 조성물은 피부 보습용일 수 있다. In one embodiment, the composition may be for skin moisturizing.
일 구현예에서, 상기 조성물은 화장료 조성물일 수 있다. In one embodiment, the composition may be a cosmetic composition.
일 측면에서, 상기 화장료 조성물의 외형은 화장품학 또는 피부과학적으로 허용 가능한 매질 또는 기제를 함유한다. 이는 국소적용에 적합한 모든 제형으로, 예를 들면, 용액, 겔, 고체, 반죽 무수 생성물, 수상에 유상을 분산시켜 얻은 에멀젼, 현탁액, 마이 크로에멀젼, 마이크로캡슐, 미세과립구 또는, 이온형(리포좀) 및 비이온형의 소낭 분산제의 형태로, 또는 크림, 스킨, 로션, 파우더, 연고, 스프레이 또는 콘실 스틱의 형태로 제공될 수 있다. 이들 조성물은 당해 분야의 통상적인 방법에 따라 제조될 수 있다. 본 개시에 따른 조성물은 또한 포말(foam)의 형태로 또는 압축된 추진제를 더 함유한 에어로졸 조성물의 형태로도 사용될 수 있다.In one aspect, the appearance of the cosmetic composition contains a cosmetically or dermatologically acceptable medium or base. It is available in all formulations suitable for topical application, for example solutions, gels, solids, kneaded dry products, emulsions obtained by dispersing an oily phase in an aqueous phase, suspensions, microemulsions, microcapsules, microgranules or ionic (liposomes). And it may be provided in the form of a non-ionic vesicular dispersant, or in the form of a cream, skin, lotion, powder, ointment, spray or concealer stick. These compositions can be prepared according to conventional methods in the art. The composition according to the present disclosure may also be used in the form of a foam or in the form of an aerosol composition further containing a compressed propellant.
본 개시의 일 실시예에 따른 화장료 조성물은 그 제형에 있어서 특별히 한정되는 바가 없으며, 예를 들면, 앰플, 크림, 유연화장수, 수렴화장수, 영양화장수, 영양크림, 마사지크림, 에센스, 아이크림, 아이에센스, 클렌징크림, 클렌징폼, 클렌징워터, 상기 화장료 조성물을 포함하는 클렌징 티슈, 팩, 바디로션, 바디크림, 바디오일 및 바디에센스 등의 화장품으로 제형화될 수 있다.The cosmetic composition according to an embodiment of the present disclosure is not particularly limited in its formulation, for example, an ampoule, cream, softening lotion, astringent lotion, nourishing lotion, nourishing cream, massage cream, essence, eye cream, eye cream Essence, cleansing cream, cleansing foam, cleansing water, cleansing tissue containing the cosmetic composition, pack, body lotion, body cream, body oil, can be formulated into cosmetics such as body essence.
본 개시의 일 실시예에 따른 제형이 페이스트, 크림 또는 겔인 경우에는 담체 성분으로서 동물섬유, 식물섬유, 왁스, 파라핀, 전분, 트라칸트, 셀룰로오스 유도체, 폴리에틸렌 글리콜, 실리콘, 벤토나이트, 실리카, 탈크 또는 산화아연 등이 이용될 수 있다.When the formulation according to an embodiment of the present disclosure is a paste, cream, or gel, animal fiber, vegetable fiber, wax, paraffin, starch, tracanth, cellulose derivative, polyethylene glycol, silicone, bentonite, silica, talc or oxidation as a carrier component Zinc or the like may be used.
본 개시의 일 실시예에 따른 제형이 스프레이인 경우에는 담체 성분으로서 락토스, 탈크, 실리카, 알루미늄히드록시드, 칼슘 실리케이트 또는 폴리아미드 파우더가 이용될 수 있고, 추가적으로 클로로플루오로히드로카본, 프로판/부탄 또는 디메틸 에테르와 같은 추진체를 포함할 수 있다.When the formulation according to an embodiment of the present disclosure is a spray, lactose, talc, silica, aluminum hydroxide, calcium silicate or polyamide powder may be used as a carrier component, and additionally chlorofluorohydrocarbon, propane/butane or a propellant such as dimethyl ether.
본 개시의 일 실시예에 따른 제형이 용액 또는 유탁액의 경우에는 담체 성분으로서 용매, 용매화제 또는 유탁화제가 이용되고, 예컨대 물, 에탄올, 이소프로판올, 에틸 카보네이트, 에틸 아세테이트, 벤질 알코올, 벤질 벤조에이트, 프로필렌 글리콜, 1,3-부틸글리콜 오일, 글리세롤 지방족 에스테르, 폴리에틸렌 글리콜 또는 소르비탄의 지방산 에스테르가 있다.When the formulation according to an embodiment of the present disclosure is a solution or emulsion, a solvent, solvating agent or emulsifying agent is used as a carrier component, for example, water, ethanol, isopropanol, ethyl carbonate, ethyl acetate, benzyl alcohol, benzyl benzoate. , propylene glycol, 1,3-butyl glycol oil, glycerol fatty esters, fatty acid esters of polyethylene glycol or sorbitan.
본 개시의 일 실시예에 따른 제형이 현탁액인 경우에는 담체 성분으로서 물, 에탄올 또는 프로필렌 글리콜과 같은 액상 희석제, 에톡실화 이소스테아릴 알코올, 폴리옥시에틸렌 소르비톨 에스테르 및 폴리옥시에틸렌 소르비탄 에스테르와 같은 현탁제, 미소결정성 셀룰로오스, 알루미늄 메타히드록시드, 벤토나이트, 아가 또는 트라칸트 등이 이용될 수 있다.When the formulation according to an embodiment of the present disclosure is a suspension, as a carrier component, a liquid diluent such as water, ethanol or propylene glycol, ethoxylated isostearyl alcohol, a suspension such as polyoxyethylene sorbitol ester and polyoxyethylene sorbitan ester agent, microcrystalline cellulose, aluminum metahydroxide, bentonite, agar or tracanth and the like can be used.
본 개시의 일 실시예에 따른 제형이 계면-활성제 함유 클렌징인 경우에는 담체 성분으로서 지방족 알코올 설페이트, 지방족 알코올 에테르 설페이트, 설포숙신산 모노에스테르, 이세티오네이트, 이미다졸리늄 유도체, 메틸타우레이트, 사르코시네이트, 지방산 아미드 에테르 설페이트, 알킬아미도베타인, 지방족 알코올, 지방산 글리세리드, 지방산 디에탄올아미드, 식물성 유, 리놀린 유도체 또는 에톡실화 글리세롤 지방산 에스테르 등이 이용될 수 있다.When the formulation according to an embodiment of the present disclosure is surfactant-containing cleansing, aliphatic alcohol sulfate, aliphatic alcohol ether sulfate, sulfosuccinic acid monoester, isethionate, imidazolinium derivative, methyltaurate, sarco as carrier components Cinate, fatty acid amide ether sulfate, alkylamidobetaine, fatty alcohol, fatty acid glyceride, fatty acid diethanolamide, vegetable oil, linoline derivative or ethoxylated glycerol fatty acid ester and the like can be used.
일 실시예에 따른 본 개시의 조성물은 제형을 그대로 사용할 수 있고, 구체적으로는 점탄성이 좋은 젤리같은 외관을 가질 수 있다. The composition of the present disclosure according to an embodiment may be used as it is, and specifically may have a jelly-like appearance with good viscoelasticity.
본 개시의 일 실시예에 따른 화장료 조성물에는 기능성 첨가물 및 일반적인 화장료 조성물에 포함되는 성분이 추가로 포함될 수 있다. 상기 기능성 첨가물로는 수용성 비타민, 유용성 비타민, 고분자 펩티드, 고분자 다당, 스핑고 지질 및 해초 엑기스로 이루어진 군에서 선택된 성분을 포함할 수 있다.The cosmetic composition according to an embodiment of the present disclosure may further include a functional additive and a component included in a general cosmetic composition. The functional additive may include a component selected from the group consisting of water-soluble vitamins, oil-soluble vitamins, polymer peptides, polymer polysaccharides, sphingolipids, and seaweed extract.
이외에 포함되는 배합 성분으로서는 유지 성분, 보습제, 에몰리엔트제, 계면 활성제, 유기 및 무기 안료, 유기 분체, 자외선 흡수제, 방부제, 살균제, 산화 방지제, 식물 추출물, pH 조정제, 알콜, 색소, 향료, 혈행 촉진제, 냉감제, 제한(制汗)제, 정제수 등을 들 수 있다.Other ingredients included include oils and fats, moisturizers, emollients, surfactants, organic and inorganic pigments, organic powders, UV absorbers, preservatives, bactericides, antioxidants, plant extracts, pH adjusters, alcohols, pigments, fragrances, blood circulation An accelerator, a cooling agent, a limiting agent, purified water, etc. are mentioned.
일 구현예에서, 상기 조성물은 식품 조성물일 수 있다. In one embodiment, the composition may be a food composition.
본 개시의 일 실시예에 따른 식품 조성물은 액상 또는 고체 상태의 제형일 수 있고, 정제, 캡슐제, 연질캡슐제, 환제, 과립제, 음료(드링크제), 다이어트바, 초콜렛, 카라멜 제형 또는 과자류 제형일 수 있으며, 그 제형이 특별히 한정되는 것은 아니다. 본 개시의 일 실시예에 따른 식품 조성물은 상기 유효 성분 외에도 필요에 따라 부형제, 당류, 향료, 색소, 유지류, 단백질 등을 적의 함유할 수 있다.The food composition according to an embodiment of the present disclosure may be a liquid or solid formulation, and may be a tablet, capsule, soft capsule, pill, granule, beverage (drink), diet bar, chocolate, caramel formulation, or confectionery formulation. and the formulation is not particularly limited. The food composition according to an embodiment of the present disclosure may contain, if necessary, excipients, sugars, flavorings, pigments, oils and fats, proteins, and the like in addition to the active ingredients.
일 구현예에서, 상기 조성물은 약학 조성물일 수 있다. In one embodiment, the composition may be a pharmaceutical composition.
본 개시의 일 실시예에 따른 조성물을 의약품에 적용할 경우에는, 본 개시의 일 실시예에서 사용되는 유효성분에 상용되는 무기 또는 유기의 담체를 가하여 반고체 또는 액상의 형태로 비경구 투여제로 제형화할 수 있으며, 본 개시에 따른 상기 약학 조성물은 비경구, 직장, 국소, 경피, 정맥 내, 근육 내, 복강 내, 피하 등으로 투여될 수 있다. When the composition according to an embodiment of the present disclosure is applied to a pharmaceutical, it is formulated as a semi-solid or liquid form for parenteral administration by adding a commercially available inorganic or organic carrier to the active ingredient used in an embodiment of the present disclosure. In addition, the pharmaceutical composition according to the present disclosure may be administered parenterally, rectally, topically, transdermally, intravenously, intramuscularly, intraperitoneally, subcutaneously, or the like.
본 개시의 일 구현예 따른 조성물은 당업계에 널리 알려진 통상적인 방법에 따라 실시함으로써, 유효성분을 용이하게 제형화할 수 있으며, 이 때 계면활성제, 부형제, 착색료, 향신료, 보존료, 안정제, 완충제, 현탁제, 기타 상용하는 보조제를 적당히 사용할 수 있다.The composition according to one embodiment of the present disclosure can be easily formulated by carrying out a conventional method well known in the art, and in this case, a surfactant, excipient, colorant, spice, preservative, stabilizer, buffer, suspension and other commercially available adjuvants may be appropriately used.
본 개시의 일 실시예에 따른 약학 조성물의 유효 성분의 투여 용량은 투여받을 대상의 연령, 성별, 체중, 병리 상태 및 그 심각도, 투여 경로 또는 처방자의 판단에 따라 달라질 것이다. 이러한 인자에 기초한 적당한 용량의 결정은 당업자의 수준 내에 있으며, 이의 1일 투여 용량은 예를 들어 0.1mg/kg/일 내지 100mg/kg/일, 보다 구체적으로는 5mg/kg/일 내지 50mg/kg/일이 될 수 있으나, 이에 제한되는 것은 아니다.The dosage of the active ingredient of the pharmaceutical composition according to an embodiment of the present disclosure will vary depending on the age, sex, weight, pathological condition and severity of the subject to be administered, the route of administration, or the judgment of the prescriber. Determination of an appropriate dose based on these factors is within the level of a person skilled in the art, and its daily dose is for example 0.1 mg/kg/day to 100 mg/kg/day, more specifically 5 mg/kg/day to 50 mg/kg It can be, but is not limited to, /work.
본 개시의 또다른 예시적인 구현예들에서는, 고분자 히알루론산 또는 그 염 및 n가 알코올(n은 1 내지 10)을 포함하여 상기 고분자 히알루론산 또는 그 염이 n가 알코올에 의해 물리적으로 가교되어 포함되는 제1 제; 및 산성 pH 조절제를 포함하는 제2 제;를 포함하고, 상기 제1 제 및 제2 제가 혼합되어 겔이 형성되며, 상기 겔의 pH가 3 이상인, 화장품 키트를 제공한다. In another exemplary embodiment of the present disclosure, the high molecular weight hyaluronic acid or its salt is physically crosslinked with an n-hydric alcohol, including high molecular weight hyaluronic acid or a salt thereof and an n-hydric alcohol (n is 1 to 10) being the first; and a second agent including an acidic pH adjusting agent; wherein the first agent and the second agent are mixed to form a gel, and the pH of the gel is 3 or more, it provides a cosmetic kit.
본 개시의 일 구현예에 따르면, 종래 기술과 달리 냉해동 공법을 적용하지 않고, 단순히 히알루론산을 포함하는 제1 제와 겔의 pH를 조절할 수 있는 산을 포함하는 제2 제를 혼합하는 것만으로 겔을 형성할 수 있으므로, 적용시 간편하게 겔형 조성물을 제조하여 사용할 수 있다. According to one embodiment of the present disclosure, unlike the prior art, without applying the freeze-thaw method, simply mixing the first agent containing hyaluronic acid and the second agent containing the acid capable of adjusting the pH of the gel Since a gel can be formed, a gel-type composition can be conveniently prepared and used when applied.
일 구현예에서, 상기 고분자 히알루론산의 염은 히알루론산 나트륨 일 수 있다.In one embodiment, the salt of the polymer hyaluronic acid may be sodium hyaluronate.
일 구현예에서, 상기 고분자 히알루론산 또는 그 염의 함량은 상기 제1 제 및 제2 제의 총 중량을 기준으로 0.1 내지 5 중량% 일 수 있다.In one embodiment, the content of the polymer hyaluronic acid or its salt may be 0.1 to 5% by weight based on the total weight of the first agent and the second agent.
일 구현예에서, 상기 n가 알코올(n은 1 내지 10)은 메탄올, 에탄올, 프로판올 및 부탄올로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있다.In one embodiment, the n-hydric alcohol (n is 1 to 10) may include one or more selected from the group consisting of methanol, ethanol, propanol and butanol.
일 구현예에서, 상기 산성 pH 조절제는 산, 글루코노락톤(Gluconolactone) 및 과일 추출물로 이루어진 군에서 선택된 하나 이상을 포함할 수 있으나, 스킨케어 제품에 pH를 낮추는 목적이면 제한 없이 사용할 수 있다. 일 실시예로서, 상기 산은 유기산 또는 무기산일 수 있다. 구체적으로, 상기 산은 저분자 히알루론산, 시트릭산, 락틱산, 아스코르빅애씨드, 소듐 피루베이트(sodium pyruvate) 또는 석신산(Succinic acid)에서 선택된 것 일 수 있다. 일 실시예로서, 상기 과일 추출물은 빌베리 열매 추출물(VACCINIUM MYRTILLUS FRUIT EXTRACT), 사탕수수 열매 추출물(SACCHARUM OFFICINARUM EXTRACT), 오렌지 열매 추출물(CITRUS AURANTIUM DULCIS FRUIT EXTRACT) 또는 레몬 열매 추출물(CITRUS LIMON FRUIT EXTRACT) 등에서 선택된 것일 수 있다. In one embodiment, the acidic pH adjusting agent may include at least one selected from the group consisting of acid, gluconolactone, and fruit extract, but may be used without limitation as long as it is for the purpose of lowering the pH in skin care products. In one embodiment, the acid may be an organic acid or an inorganic acid. Specifically, the acid may be selected from low molecular weight hyaluronic acid, citric acid, lactic acid, ascorbic acid, sodium pyruvate, or succinic acid. In one embodiment, the fruit extract is bilberry fruit extract (VACCINIUM MYRTILLUS FRUIT EXTRACT), sugar cane fruit extract (SACCHARUM OFFICINARUM EXTRACT), orange fruit extract (CITRUS AURANTIUM DULCIS FRUIT EXTRACT) or lemon fruit extract (CITRUS LIMON FRUIT EXTRACT), etc. may be selected.
일 구현예에서, 상기 산은 저분자 히알루론산을 포함하고, 상기 고분자 히알루론산 또는 그 염의 중량평균분자량은 700 내지 3,000 kDa 이며, 상기 저분자 히알루론산의 중량평균분자량은 2 내지 100 kDa일 수 있다.In one embodiment, the acid includes low molecular weight hyaluronic acid, the high molecular weight hyaluronic acid or a salt thereof has a weight average molecular weight of 700 to 3,000 kDa, and the weight average molecular weight of the low molecular weight hyaluronic acid may be 2 to 100 kDa.
일 구현예에서, 상기 제1 제는 폴리올을 더 포함할 수 있다.In one embodiment, the first agent may further include a polyol.
일 구현예에서, 상기 키트는 피부 보습용일 수 있다. In one embodiment, the kit may be for skin moisturizing.
이하, 하기의 실시예를 통하여 본 개시를 보다 구체적으로 설명한다. 그러나 하기의 실시에는 본 개시에 대한 이해를 돕기 위해 예시의 목적으로만 제공된 것일 뿐, 본 개시의 범주 및 범위가 이에 한정되지 않는다.Hereinafter, the present disclosure will be described in more detail through the following examples. However, the following examples are provided only for the purpose of illustration to help the understanding of the present disclosure, and the scope and scope of the present disclosure are not limited thereto.
실시예Example
실시예 1 Example 1
하기 표 1과 같은 처방으로 히알루론산 0.1~5 중량%로 실험을 진행하였고 처음부터 모든 원료를 투입하여 제조하는 1-step 공정과 산성용액을 별도로 정제수에 녹여 준비한 후(제2 제) 나머지 용액(제1 제)과 추후 섞어서 제조하는 2-step 공정을 비교하였다. 또한, 실시예 1, 2 그리고 비교예 2에서는 분자량이 다른 히알루론산을 산성 용액으로 적용하였다. Experiments were conducted with 0.1 to 5% by weight of hyaluronic acid with the formulation shown in Table 1 below, and after preparing a 1-step process and an acidic solution prepared by inputting all raw materials from the beginning in purified water (second agent), the remaining solution ( The first agent) and the 2-step process of mixing and manufacturing later were compared. In addition, in Examples 1, 2 and Comparative Example 2, hyaluronic acid having a different molecular weight was applied as an acidic solution.
구체적으로, 실시예 1는 히알루론산 고분자 1 중량%와 히알루론산 저분자 0.5 중량%를 비커 하나에 일괄 투입하여 제조하는 원스텝 공정으로 제조하였으며, 저분자 히알루론산 0.5 중량%가 pH를 떨어뜨리는 역할을 수행한다. 실시예 2는 실시예 1과 동일한 조성으로 제조하되, 제1제 및 제2제로 분리하여 적용하였다(2-step 공정). 실시예 3은 pH 조절제로 저분자 히알루론산 대신 시트르산을 사용한 것을 제외하고는 실시예 2와 동일하게 제조하였다.Specifically, Example 1 was prepared by a one-step process in which 1 wt% of a hyaluronic acid polymer and 0.5 wt% of a low molecular weight hyaluronic acid were batched into one beaker, and 0.5 wt% of a low molecular weight hyaluronic acid serves to lower the pH. . Example 2 was prepared in the same composition as in Example 1, but the first agent and the second agent were separately applied (2-step process). Example 3 was prepared in the same manner as in Example 2, except that citric acid was used instead of low molecular weight hyaluronic acid as a pH adjuster.
비교예 1은 히알루론산 고분자를 처방하지 않은 것을 제외하고는 실시예 3과 동일한 조성과 방법으로 제조하였다. 비교예 2는 에탄올을 포함하지 않은 것을 제외하고는 실시예 1과 동일한 조성과 방법으로 제조하였다. Comparative Example 1 was prepared in the same composition and method as in Example 3, except that the hyaluronic acid polymer was not prescribed. Comparative Example 2 was prepared in the same composition and method as in Example 1, except that ethanol was not included.
하기의 실시예 및 비교예에 사용된 히알루론산은 현대바이오랜드 社의 소듐 히알루론산을 사용하였다.As the hyaluronic acid used in the following Examples and Comparative Examples, sodium hyaluronic acid manufactured by Hyundai Bioland was used.
실시예 1, 2 를 비교한 결과 두 공정 모두 겔링이 가능한 것을 확인할 수 있었다. 또한 산성 용액으로 히알루론산이 아닌 시트르산을 적용한 실시예 3의 경우에도 성공적으로 겔링이 일어나는 것을 확인하였다. 하지만 비교예 1과 같이 고분자 히알루론산 또는 그 염의 골격이 존재하지 않는 경우 겔링이 되지 않았고, 에탄올이 포함되지 않을 경우(비교예 2)는 겔링이 되어도 금방 겔링이 풀리는 양상을 확인할 수 있었다.As a result of comparing Examples 1 and 2, it was confirmed that both processes were capable of gelling. In addition, in the case of Example 3 in which citric acid, not hyaluronic acid, was applied as an acidic solution, it was confirmed that gelling occurred successfully. However, as in Comparative Example 1, when the skeleton of the polymer hyaluronic acid or its salt did not exist, gelling did not occur, and when ethanol was not included (Comparative Example 2), it was confirmed that the gelling was quickly released even after gelling.
실시예 2 - 탄성, 점성 및 점도 측정Example 2 - Elasticity, Viscosity and Viscosity Measurement
상기 실시예에서 제조된 조성물들을 이용하여 탄성 및 점성 정도를 측정하였다. 탄성계수(G') 및 점성계수(G")는 레오미터(Rheometer; Maven, USA)를 사용하였다. 설정 조건은 '진동(Oscillation)', '주파수 스위프(frequency sweep)', '전단 응력(shear stress)'과 같고, 25℃에서 플레이트 타입(Plate type) : 20 mm 플레이트 콘(plate corn)을 사용하여, 1 Pa 로 조정된 진동 응력(oscillation stress), 0.1 ~ 30 Hz의 주파수 범위, 1 Pa 전단 응력, 2mm 갭(gap)에서 측정을 실시하였다. 그 중에서 1Hz때의 G', G"값을 측정하였다. G', G" 측정 샘플은 지름 20mm, 두께 1mm의 디스크 형태의 규격으로 통일하였다.The degree of elasticity and viscosity were measured using the compositions prepared in the above Examples. A rheometer (Maven, USA) was used for the elastic modulus (G') and the viscous modulus (G"). The setting conditions were 'Oscillation', 'frequency sweep', 'shear stress ( shear stress)', plate type at 25°C: using a 20 mm plate corn, oscillation stress adjusted to 1 Pa, frequency range from 0.1 to 30 Hz, 1 Pa shear stress was measured at a gap of 2 mm. Among them, G' and G" values at 1 Hz were measured. The G' and G" measurement samples were standardized in the form of a disk with a diameter of 20 mm and a thickness of 1 mm.
점도는 측정은 브룩필드 LV 비스코미터(Brookfield LV Viscometer), 브룩필드 RV 비스코미터(Brookfield RV Viscometer)를 사용하였다. 스핀들 회전 rpm 및 측정시간은 12 rpm, 2min이며, No. 63 스핀들을 사용해 측정하였다.The viscosity was measured using a Brookfield LV Viscometer and a Brookfield RV Viscometer. Spindle rotation rpm and measurement time are 12 rpm, 2 min, No. Measurements were made using a 63 spindle.
실시예 1의 경우 산성용액(제2 제)과 겔링이 이루어지는 동안 물성의 변화가 일어나게 되는데, 도 1를 참조하면 액상 상태였던 히알루론산 용액이 산성 용액으로 인해 산성화 되면서 탄성계수(G'; Elastic modulus)와 점성계수(G"; Viscos modulus)가 교차하게 되는 지점에서 겔링이 일어났다. 이때의 pH는 3.4이며 히알루론산의 농도는 전체 조성물 중량을 기준으로 1중량%이다.In the case of Example 1, a change in physical properties occurs during gelling with the acidic solution (second agent). Referring to FIG. 1 , the hyaluronic acid solution, which was in a liquid state, is acidified due to the acidic solution, and the elastic modulus (G'; Elastic modulus) ) and the viscous modulus (G"; Viscos modulus), gelling occurred at the intersection. At this time, the pH was 3.4 and the concentration of hyaluronic acid was 1% by weight based on the total weight of the composition.
실시예 3 - pH에 따른 히알루론산 하이드로겔 물성 변화Example 3 - Changes in physical properties of hyaluronic acid hydrogel according to pH
pH 변화에 따른 하이드로겔 물성 변화를 측정한 결과를 하기 표 2 및 도 2에 나타내었다. The results of measuring changes in hydrogel properties according to pH changes are shown in Table 2 and FIG. 2 below.
구체적으로, 실시예 3에서 폴리올 2개와 에탄올을 삭제한 처방이며, 이 때 시트르산의 농도를 달리해가며 pH를 조절하였고, 그 결과 pH 2~3 영역에서 겔의 물성이 높아지는 것을 보여주는 결과이다. Specifically, in Example 3, two polyols and ethanol were omitted, and the pH was adjusted by varying the concentration of citric acid at this time, and as a result, it is a result showing that the physical properties of the gel are increased in the pH 2-3 range.
표 2와 도 2를 통하여, 에탄올, 폴리올이 없으면 pH 2~3에서 겔링이 된다는 것을 알 수 있다. 따라서, 전술한 본 개시의 일 실시예들과 같이 에탄올, 폴리올을 포함하여, pH 3 이상으로 겔링 포인트가 올라갈 수 있고 화장품으로 쓸 수 있다. Through Table 2 and FIG. 2, it can be seen that gelling occurs at pH 2-3 without ethanol and polyol. Therefore, as in the above-described exemplary embodiments of the present disclosure, including ethanol and polyol, the gelling point may rise to
실시예 4 - 보습감 개선 효과Example 4 - Moisture improvement effect
하이드로겔 앰플 적용 시 보습감 개선 효과를 관찰하여 도 3에 나타내었다. 구체적으로, 실시예 1의 조성물을 20~40세 남성 6명 전박에 도포한 후 시간별로 코르네오미터(Corneometer)를 통해 수분유지력을 측정한 결과이다. 시간별로 관찰한 결과, 실시예 1의 조성물을 사용한 경우 보습감이 크개 개선되는 것을 확인할 수 있다. When the hydrogel ampoule was applied, the moisturizing effect was observed and shown in FIG. 3 . Specifically, the composition of Example 1 was applied to the forearms of 6 males aged 20-40 years, and the moisture retention ability was measured by a corneometer for each hour. As a result of observation for each time, it can be confirmed that the moisturizing feeling is greatly improved when the composition of Example 1 is used.
실시예 5 - 히알루론산 함량에 따른 제형의 물성 변화Example 5 - Changes in physical properties of the formulation according to the content of hyaluronic acid
실시예 3과 동일한 조성 및 방법으로 제조하되, 고분자 히알루론산의 함량을 조절하여, 이에 따른 제형의 물성을 관찰하였다. 도 4를 참조하면, 제형 내 히알루론산 함량 설정에 있어서 0.5 내지 0.6 중량% 이상에서 겔의 물성이 큰 폭으로 증가하기 시작하며, 0.8 내지 0.9 중량% 이상부터는 겔의 물성 증가폭이 감소하였다. It was prepared in the same composition and method as in Example 3, but by adjusting the content of the polymer hyaluronic acid, the physical properties of the formulation were observed. Referring to FIG. 4 , when the amount of hyaluronic acid in the formulation is set, the physical properties of the gel start to increase significantly at 0.5 to 0.6% by weight or more, and the increase in the physical properties of the gel decreases from 0.8 to 0.9% by weight or more.
실시예 6 - 등전점 관찰Example 6 - Observation of isoelectric point
실시예 3과 동일한 조성 및 방법으로 제조하되, 글리세롤 및 에탄올 농도를 달리하여, 이에 따른 제형의 물성을 관찰하였다. 구체적으로, 실시예 3 처방에서 고분자 히알루론산을 1 중량%, 에탄올을 4 중량%로 고정한 후, 글리세롤(폴리올)의 함량만 조절한 결과이다. 하기 표 3 및 도 5를 참조하면, 폴리올 함량이 늘어날수록 겔링 포인트(등전점)의 pH가 상승하여, 화장품 제형에 적용할 수 있다는 것을 확인하였다. It was prepared in the same composition and method as in Example 3, but with different concentrations of glycerol and ethanol, and thus the physical properties of the formulation were observed. Specifically, it is the result of adjusting only the content of glycerol (polyol) after fixing the polymer hyaluronic acid to 1% by weight and ethanol to 4% by weight in the formulation of Example 3. Referring to Tables 3 and 5 below, as the polyol content increases, the pH of the gelling point (isoelectric point) increases, confirming that it can be applied to cosmetic formulations.
정리해보면, 본 개시의 일 측면은 고분자 히알루론산 또는 그 염, 산성 pH 조절제, 및 1-10가 알코올의 조합을 포함함으로써 겔링 반응을 통해 특이 제형의 완성도를 높일 수 있다. 본 개시의 일 측면은 제형의 완성 여부를 육안상으로 관찰하는 수준에서 쉽게 평가할 수 있고, 그 물리적인 수치를 측정한 결과 겔화되지 않은 경우와 뚜렷한 차이를 보임을 확인할 수 있다. In summary, one aspect of the present disclosure can increase the degree of completeness of a specific formulation through a gelling reaction by including a combination of high molecular weight hyaluronic acid or a salt thereof, an acidic pH adjuster, and a 1-10 alcohol. One aspect of the present disclosure can be easily evaluated at the level of visually observing whether or not the formulation is completed, and it can be confirmed that the physical value is measured and shows a clear difference from the non-gelled case.
본 개시는 일 실시예로서 다음의 실시형태들을 제공할 수 있다.The present disclosure may provide the following embodiments as an example.
제1실시형태는 고분자 히알루론산 또는 그 염, n가 알코올(n은 1 내지 10) 및 산성 pH 조절제를 포함하고, 상기 고분자 히알루론산 또는 그 염은 n가 알코올에 의해 물리적으로 가교되며, pH가 3 이상인, 겔 조성물을 제공할 수 있다.A first embodiment includes a polymeric hyaluronic acid or a salt thereof, an n-hydric alcohol (n is 1 to 10) and an acidic pH adjuster, wherein the polymeric hyaluronic acid or a salt thereof is physically crosslinked by an n-hydric alcohol, and the pH is 3 or more, a gel composition can be provided.
제2실시형태는, 제1실시형태에 있어서, 상기 고분자 히알루론산의 염은 히알루론산 나트륨인, 겔 조성물을 제공할 수 있다.In the second embodiment, in the first embodiment, the salt of the polymer hyaluronic acid is sodium hyaluronate, it can provide a gel composition.
제3실시형태는, 제1실시형태 또는 제2실시형태에 있어서, 상기 고분자 히알루론산 또는 그 염의 함량은 상기 조성물 총 중량을 기준으로 0.1 내지 5 중량%인, 겔 조성물을 제공할 수 있다.A third embodiment, in the first embodiment or the second embodiment, the content of the polymer hyaluronic acid or its salt is 0.1 to 5% by weight based on the total weight of the composition, it can provide a gel composition.
제4실시형태는, 제1실시형태 내지 제3실시형태 중 어느 하나에 있어서, 상기 산성 pH 조절제는, 저분자 히알루론산, 시트릭산, 락틱산, 아스코르빅애씨드, 소듐 피루베이트(sodium pyruvate) 또는 석신산(Succinic acid)에서 선택되는 산; 글루코노락톤(Gluconolactone); 및 빌베리열매추출물(VACCINIUM MYRTILLUS FRUIT EXTRACT), 사탕수수 열매 추출물(SACCHARUM OFFICINARUM EXTRACT), 오렌지 열매 추출물(CITRUS AURANTIUM DULCIS FRUIT EXTRACT) 또는 레몬 열매 추출물(CITRUS LIMON FRUIT EXTRACT)에서 선택되는 과일 추출물;로 이루어진 군에서 선택되는 하나 이상을 포함하는, 겔 조성물을 제공할 수 있다.In a fourth embodiment, according to any one of the first to third embodiments, the acidic pH adjusting agent is low molecular weight hyaluronic acid, citric acid, lactic acid, ascorbic acid, sodium pyruvate, or an acid selected from succinic acid; Gluconolactone; and a fruit extract selected from VACCINIUM MYRTILLUS FRUIT EXTRACT, SACCHARUM OFFICINARUM EXTRACT, CITRUS AURANTIUM DULCIS FRUIT EXTRACT or CITRUS LIMON FRUIT EXTRACT; It can provide a gel composition comprising one or more selected from.
제5실시형태는, 제1실시형태 내지 제4실시형태 중 어느 하나에 있어서, 상기 산성 pH 조절제는 저분자 히알루론산을 포함하고, 상기 고분자 히알루론산 또는 그 염의 중량평균분자량은 700 내지 3,000 kDa 이며, 상기 저분자 히알루론산의 중량평균분자량은 2 내지 100 kDa인, 겔 조성물을 제공할 수 있다.In a fifth embodiment, in any one of the first to fourth embodiments, the acidic pH adjusting agent comprises low molecular weight hyaluronic acid, and the high molecular weight hyaluronic acid or a salt thereof has a weight average molecular weight of 700 to 3,000 kDa, The low molecular weight hyaluronic acid may have a weight average molecular weight of 2 to 100 kDa, providing a gel composition.
제6실시형태는, 제1실시형태 내지 제5실시형태 중 어느 하나에 있어서, 상기 조성물은 폴리올을 더 포함하는, 겔 조성물을 제공할 수 있다.A sixth embodiment may provide the gel composition according to any one of the first to fifth embodiments, wherein the composition further comprises a polyol.
제7실시형태는, 제1실시형태 내지 제6실시형태 중 어느 하나에 있어서, 상기 조성물은 폴리올을 더 포함하고, 상기 조성물 전체 중량을 기준으로, 고분자 히알루론산 또는 그 염 0.1 내지 5 중량%; n가 알코올(n은 1 내지 10) 0.1 내지 30 중량%; 산성 pH 조절제 0.1 내지 10 중량%; 및 폴리올 0.1 내지 30 중량%;를 포함하는 겔 조성물을 제공할 수 있다.A seventh embodiment, in any one of the first to sixth embodiments, wherein the composition further comprises a polyol, based on the total weight of the composition, 0.1 to 5% by weight of a polymer hyaluronic acid or a salt thereof; 0.1 to 30% by weight of an n-hydric alcohol (n is 1 to 10); 0.1 to 10% by weight of an acidic pH adjusting agent; and 0.1 to 30 wt% of a polyol; may provide a gel composition comprising.
제8실시형태는, 제1실시형태 내지 제7실시형태 중 어느 하나에 있어서, 상기 조성물의 점도는 5,000 cps 이상인, 겔 조성물을 제공할 수 있다.An eighth embodiment may provide the gel composition according to any one of the first to seventh embodiments, wherein the composition has a viscosity of 5,000 cps or more.
제9실시형태는, 제1실시형태 내지 제8실시형태 중 어느 하나에 있어서, 상기 조성물은 유화 조성물 또는 가용화(solubilization) 조성물인, 겔 조성물을 제공할 수 있다.A ninth embodiment may provide the gel composition according to any one of the first to eighth embodiments, wherein the composition is an emulsion composition or a solubilization composition.
제10실시형태는, 제1실시형태 내지 제9실시형태 중 어느 하나에 있어서, 상기 조성물은 피부 보습용인, 겔 조성물을 제공할 수 있다.A tenth embodiment may provide the gel composition according to any one of the first to ninth embodiments, wherein the composition is for skin moisturizing.
제11실시형태는, 제1실시형태 내지 제10실시형태 중 어느 하나에 있어서, 상기 조성물은 화장료 조성물인, 겔 조성물을 제공할 수 있다.An eleventh embodiment may provide a gel composition according to any one of the first to tenth embodiments, wherein the composition is a cosmetic composition.
제12실시형태는, 제1실시형태 내지 제11실시형태 중 어느 하나에 있어서, 상기 조성물은 식품 조성물인, 겔 조성물을 제공할 수 있다.A twelfth embodiment may provide the gel composition according to any one of the first to eleventh embodiments, wherein the composition is a food composition.
제13실시형태는, 제1실시형태 내지 제12실시형태 중 어느 하나에 있어서, 상기 조성물은 약학 조성물인, 겔 조성물을 제공할 수 있다.A thirteenth embodiment may provide the gel composition according to any one of the first to twelfth embodiments, wherein the composition is a pharmaceutical composition.
제14실시형태는, 제1실시형태 내지 제13실시형태 중 어느 하나에 있어서, 고분자 히알루론산 또는 그 염 및 n가 알코올(n은 1 내지 10)을 포함하여 상기 고분자 히알루론산 또는 그 염이 n가 알코올에 의해 물리적으로 가교되어 포함되는 제1 제; 및 산성 pH 조절제를 포함하는 제2 제;를 포함하고, 상기 제1 제 및 제2 제가 혼합되어 겔이 형성되며, 상기 겔의 pH가 3 이상인, 화장품 키트를 제공할 수 있다.In a fourteenth embodiment, according to any one of the first to thirteenth embodiments, the polymeric hyaluronic acid or its salt is n, a first agent that is physically crosslinked with an alcohol; and a second agent comprising an acidic pH adjusting agent; wherein the first agent and the second agent are mixed to form a gel, and the pH of the gel is 3 or more, it is possible to provide a cosmetic kit.
제15실시형태는, 제1실시형태 내지 제14실시형태 중 어느 하나에 있어서, 상기 고분자 히알루론산의 염은 히알루론산 나트륨인, 화장품 키트를 제공할 수 있다.A fifteenth embodiment may provide a cosmetic kit according to any one of the first to fourteenth embodiments, wherein the salt of the polymeric hyaluronic acid is sodium hyaluronate.
제16실시형태는, 제1실시형태 내지 제15실시형태 중 어느 하나에 있어서, 상기 고분자 히알루론산 또는 그 염의 함량은 상기 제1 제 및 제2 제의 총 중량을 기준으로 0.1 내지 5 중량%인, 화장품 키트를 제공할 수 있다.A sixteenth embodiment, in any one of the first to fifteenth embodiments, wherein the content of the polymeric hyaluronic acid or its salt is 0.1 to 5% by weight based on the total weight of the first agent and the second agent , can provide cosmetic kits.
제17실시형태는, 제1실시형태 내지 제16실시형태 중 어느 하나에 있어서, 상기 산성 pH 조절제는, 저분자 히알루론산, 시트릭산, 락틱산, 소듐 피루베이트(sodium pyruvate) 또는 석신산(Succinic acid)에서 선택되는 산; 글루코노락톤(Gluconolactone); 및 빌베리열매추출물(VACCINIUM MYRTILLUS FRUIT EXTRACT), 오렌지추출물 또는 레몬추출물에서 선택되는 과일 추출물;로 이루어진 군에서 선택되는 하나 이상을 포함하는, 화장품 키트를 제공할 수 있다.A seventeenth embodiment, according to any one of the first to sixteenth embodiments, wherein the acidic pH adjusting agent is low molecular weight hyaluronic acid, citric acid, lactic acid, sodium pyruvate or succinic acid ) an acid selected from; Gluconolactone; And a bilberry fruit extract (VACCINIUM MYRTILLUS FRUIT EXTRACT), a fruit extract selected from orange extract or lemon extract; containing one or more selected from the group consisting of, may provide a cosmetic kit.
제18실시형태는, 제1실시형태 내지 제17실시형태 중 어느 하나에 있어서, 상기 산성 pH 조절제는 저분자 히알루론산을 포함하고, 상기 고분자 히알루론산 또는 그 염의 중량평균분자량은 700 내지 3,000 kDa 이며, 상기 저분자 히알루론산의 중량평균분자량은 2 내지 100 kDa인, 화장품 키트를 제공할 수 있다.In an eighteenth embodiment, in any one of the first to seventeenth embodiments, the acidic pH adjusting agent comprises low molecular weight hyaluronic acid, and the high molecular weight hyaluronic acid or a salt thereof has a weight average molecular weight of 700 to 3,000 kDa, The weight average molecular weight of the low molecular weight hyaluronic acid is 2 to 100 kDa, it is possible to provide a cosmetic kit.
제19실시형태는, 제1실시형태 내지 제18실시형태 중 어느 하나에 있어서, 상기 제1 제는 폴리올을 더 포함하는, 화장품 키트를 제공할 수 있다.A nineteenth embodiment may provide the cosmetic kit according to any one of the first to eighteenth embodiments, wherein the first agent further comprises a polyol.
제20실시형태는, 제1실시형태 내지 제19실시형태 중 어느 하나에 있어서, 상기 키트는 피부 보습용인, 화장품 키트를 제공할 수 있다.A twentieth embodiment may provide the cosmetic kit according to any one of the first to nineteenth embodiments, wherein the kit is for skin moisturizing.
Claims (20)
상기 고분자 히알루론산 또는 그 염은 n가 알코올에 의해 물리적으로 가교되며,
pH가 3 이상인, 겔 조성물.Contains high molecular weight hyaluronic acid or a salt thereof, an n-hydric alcohol (n is 1 to 10), and an acidic pH adjuster,
The polymer hyaluronic acid or its salt is physically crosslinked by an n-hydric alcohol,
A gel composition having a pH of 3 or higher.
상기 고분자 히알루론산의 염은 히알루론산 나트륨인, 겔 조성물.According to claim 1,
The salt of the polymeric hyaluronic acid is sodium hyaluronate, a gel composition.
상기 고분자 히알루론산 또는 그 염의 함량은 상기 조성물 총 중량을 기준으로 0.1 내지 5 중량%인, 겔 조성물.According to claim 1,
The content of the polymeric hyaluronic acid or its salt is 0.1 to 5% by weight based on the total weight of the composition, the gel composition.
저분자 히알루론산, 시트릭산, 락틱산, 아스코르빅애씨드, 소듐 피루베이트(sodium pyruvate) 또는 석신산(Succinic acid)에서 선택되는 산;
글루코노락톤(Gluconolactone); 및
빌베리열매추출물(VACCINIUM MYRTILLUS FRUIT EXTRACT), 사탕수수 열매 추출물(SACCHARUM OFFICINARUM EXTRACT), 오렌지 열매 추출물(CITRUS AURANTIUM DULCIS FRUIT EXTRACT) 또는 레몬 열매 추출물(CITRUS LIMON FRUIT EXTRACT)에서 선택되는 과일 추출물;
로 이루어진 군에서 선택되는 하나 이상을 포함하는, 겔 조성물.According to claim 1, wherein the acidic pH adjusting agent,
an acid selected from low molecular weight hyaluronic acid, citric acid, lactic acid, ascorbic acid, sodium pyruvate or succinic acid;
Gluconolactone; and
a fruit extract selected from VACCINIUM MYRTILLUS FRUIT EXTRACT, SACCHARUM OFFICINARUM EXTRACT, CITRUS AURANTIUM DULCIS FRUIT EXTRACT or CITRUS LIMON FRUIT EXTRACT;
A gel composition comprising at least one selected from the group consisting of.
상기 산성 pH 조절제는 저분자 히알루론산을 포함하고,
상기 고분자 히알루론산 또는 그 염의 중량평균분자량은 700 내지 3,000 kDa 이며,
상기 저분자 히알루론산의 중량평균분자량은 2 내지 100 kDa인, 겔 조성물.According to claim 1,
The acidic pH adjusting agent includes low molecular weight hyaluronic acid,
The weight average molecular weight of the polymer hyaluronic acid or its salt is 700 to 3,000 kDa,
The weight average molecular weight of the low molecular weight hyaluronic acid is 2 to 100 kDa, the gel composition.
상기 조성물은 폴리올을 더 포함하는, 겔 조성물.According to claim 1,
The composition further comprises a polyol, the gel composition.
상기 조성물은 폴리올을 더 포함하고,
상기 조성물 전체 중량을 기준으로,
고분자 히알루론산 또는 그 염 0.1 내지 5 중량%;
n가 알코올(n은 1 내지 10) 0.1 내지 30 중량%;
산성 pH 조절제 0.1 내지 10 중량%; 및
폴리올 0.1 내지 30 중량%;
를 포함하는 겔 조성물.According to claim 1,
The composition further comprises a polyol,
Based on the total weight of the composition,
Polymeric hyaluronic acid or its salt 0.1 to 5% by weight;
0.1 to 30% by weight of an n-hydric alcohol (n is 1 to 10);
0.1 to 10% by weight of an acidic pH adjuster; and
0.1 to 30% by weight of a polyol;
A gel composition comprising a.
상기 조성물의 점도는 5,000 cps 이상인, 겔 조성물.According to claim 1,
The viscosity of the composition is at least 5,000 cps, the gel composition.
상기 조성물은 유화 조성물 또는 가용화(solubilization) 조성물인, 겔 조성물.According to claim 1,
The composition is an emulsion composition or a solubilization composition, a gel composition.
상기 조성물은 피부 보습용인, 겔 조성물.According to claim 1,
The composition is for moisturizing the skin, a gel composition.
상기 조성물은 화장료 조성물인, 겔 조성물.According to claim 1,
The composition is a cosmetic composition, a gel composition.
상기 조성물은 식품 조성물인, 겔 조성물.According to claim 1,
The composition is a food composition, a gel composition.
상기 조성물은 약학 조성물인, 겔 조성물.According to claim 1,
The composition is a pharmaceutical composition, a gel composition.
산성 pH 조절제를 포함하는 제2 제;를 포함하고,
상기 제1 제 및 제2 제가 혼합되어 겔이 형성되며,
상기 겔의 pH가 3 이상인, 화장품 키트.a first agent comprising a polymeric hyaluronic acid or a salt thereof and an n-hydric alcohol (n is 1 to 10), wherein the polymeric hyaluronic acid or a salt thereof is physically crosslinked by an n-hydric alcohol; and
a second agent comprising an acidic pH adjusting agent; and
The first agent and the second agent are mixed to form a gel,
The pH of the gel is 3 or more, cosmetic kit.
상기 고분자 히알루론산의 염은 히알루론산 나트륨인, 화장품 키트.15. The method of claim 14,
The salt of the polymer hyaluronic acid is sodium hyaluronate, cosmetic kit.
상기 고분자 히알루론산 또는 그 염의 함량은 상기 제1 제 및 제2 제의 총 중량을 기준으로 0.1 내지 5 중량%인, 화장품 키트.15. The method of claim 14,
The content of the polymeric hyaluronic acid or its salt is 0.1 to 5% by weight based on the total weight of the first agent and the second agent, a cosmetic kit.
저분자 히알루론산, 시트릭산, 락틱산, 소듐 피루베이트(sodium pyruvate) 또는 석신산(Succinic acid)에서 선택되는 산;
글루코노락톤(Gluconolactone); 및
빌베리열매추출물(VACCINIUM MYRTILLUS FRUIT EXTRACT), 오렌지추출물 또는 레몬추출물에서 선택되는 과일 추출물;
로 이루어진 군에서 선택되는 하나 이상을 포함하는, 화장품 키트.15. The method of claim 14, wherein the acidic pH adjusting agent,
an acid selected from low molecular weight hyaluronic acid, citric acid, lactic acid, sodium pyruvate or succinic acid;
Gluconolactone; and
a fruit extract selected from bilberry fruit extract (VACCINIUM MYRTILLUS FRUIT EXTRACT), orange extract or lemon extract;
A cosmetic kit comprising at least one selected from the group consisting of.
상기 산성 pH 조절제는 저분자 히알루론산을 포함하고,
상기 고분자 히알루론산 또는 그 염의 중량평균분자량은 700 내지 3,000 kDa 이며,
상기 저분자 히알루론산의 중량평균분자량은 2 내지 100 kDa인, 화장품 키트.15. The method of claim 14,
The acidic pH adjusting agent includes low molecular weight hyaluronic acid,
The weight average molecular weight of the polymer hyaluronic acid or its salt is 700 to 3,000 kDa,
The weight average molecular weight of the low molecular weight hyaluronic acid is 2 to 100 kDa, cosmetic kit.
상기 제1 제는 폴리올을 더 포함하는, 화장품 키트.15. The method of claim 14,
The first agent further comprises a polyol, cosmetic kit.
상기 키트는 피부 보습용인, 화장품 키트.15. The method of claim 14,
The kit is for skin moisturizing, cosmetic kit.