KR20220072001A - 무수축 미장 몰탈 조성물 및 그 시공방법 - Google Patents

무수축 미장 몰탈 조성물 및 그 시공방법 Download PDF

Info

Publication number
KR20220072001A
KR20220072001A KR1020200157589A KR20200157589A KR20220072001A KR 20220072001 A KR20220072001 A KR 20220072001A KR 1020200157589 A KR1020200157589 A KR 1020200157589A KR 20200157589 A KR20200157589 A KR 20200157589A KR 20220072001 A KR20220072001 A KR 20220072001A
Authority
KR
South Korea
Prior art keywords
weight
composition
shrinkage
plastering mortar
mortar
Prior art date
Application number
KR1020200157589A
Other languages
English (en)
Other versions
KR102609216B1 (ko
Inventor
심용래
유덕상
Original Assignee
심용래
유덕상
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 심용래, 유덕상 filed Critical 심용래
Priority to KR1020200157589A priority Critical patent/KR102609216B1/ko
Publication of KR20220072001A publication Critical patent/KR20220072001A/ko
Application granted granted Critical
Publication of KR102609216B1 publication Critical patent/KR102609216B1/ko

Abstract

본 발명은 무수축 미장 몰탈 조성물 및 그 시공방법에 관한 것으로서, 콘크리트 균열부위의 보수가 보다 신속하게 이루어짐과 함께 부착력을 개선시키고 수축 현상을 방지하는 효과를 나타내기 위한 것이다.
이를 실현하기 위한 본 발명의 무수축 미장 몰탈 조성물은, 규사 40~60중량%, 포틀랜드 시멘트, 20~40중량%, CSA(칼슘설포알루미네이트) 1~10중량%, 탄소분말 1~10중량%, 폴리우레아 1~5중량%, 무수석고 1~5중량%, 분말수지 1~3중량%, 탄산칼슘 1~3중량%의 혼합 조성을 이루는 것을 특징으로 한다.

Description

무수축 미장 몰탈 조성물 및 그 시공방법{Non-shrink plastering mortar composition and its construction method}
본 발명은 무수축 미장 몰탈에 관한 것으로서, 더욱 상세하게는 콘크리트 벽면이나 바닥 균열부위, 각종 PC보수 및 미장사춤용으로 사용되는 무수축 미장 몰탈 조성물 및 그 시공방법에 관한 것이다.
일반적으로 콘크리트 구조물에서 열화 등에 의해 콘크리트에 균열이 발생하여 시간이 지나게 되면 콘크리트의 압축강도와 철근의 인장강도가 점차 떨어지게 되고, 균열 부위로 통해 노출된 콘크리트는 중성화 현상이 진행되어 철근의 부식이 일어난다. 이러한 철근의 부식 현상이 심해지면 콘크리트 구조물이 결국 붕괴될 수도 있다.
따라서, 콘크리트 구조물이 열화 되어 균열이 발생하면 조속하게 열화된 부위를 보수할 필요가 있다.
이러한 균열은 시멘트가 응결되는 과정에서 수축에 의해 발생하는 것으로, 시멘트의 구성성분, 시멘트의 분말도, 물의 양 등에 가장 큰 영향을 받는다. 시멘트의 수축균열을 방지하기 위해 건조수축을 보상하는 정도로 팽창할 수 있는 팽창시멘트를 사용하는 방법이 알려져 있다.
그런데 지금까지 알려진 팽창시멘트는 그 제조과정이 복잡하고 부착력이 낮으며, 환경오염물질이 함유되어 있어서 인체에 유해성이 작용하는 등의 문제점이 있었다.
대한민국 특허등록 제1862594호(2018.05.24.등록) 대한민국 특허등록 제307090호(2001.08.17.등록)
본 발명은 상기한 종래 기술에서의 문제점을 개선하기 위해 제안된 것으로서, 기존 제품에 비하여 작업효율이 개선되고 건조 수축이 적으며 부착력이 우수한 혼합 조성을 이루는 무수축 미장 몰탈을 제공함으로써 몰탈 제품의 신뢰성을 향상시키도록 하는데 목적이 있다.
상기 목적을 이루기 위한 본 발명의 무수축 몰탈 조성물은, 규사 40~60중량%, 포틀랜드 시멘트, 20~40중량%, CSA(칼슘설포알루미네이트) 1~10중량%, 탄소분말 1~10중량%, 폴리우레아 1~5중량%, 무수석고 1~5중량%, 분말수지 1~3중량%, 탄산칼슘 1~3중량%의 혼합 조성을 이루는 것을 특징으로 한다.
이러한 본 발명의 무수축 미장 몰탈은, 콘크리트 균열부위의 보수가 보다 신속하게 이루어짐과 함께 부착력을 개선시키고 수축 현상을 방지하는 효과를 나타내게 된다.
특히, 몰탈 재료의 유동성 및 속건성이 개선되어 보다 보수 효율을 향상시키는 이점을 나타낸다
도 1은 본 발명의 일 실시 예에 따른 무수축 미장 몰탈 시공과정 순서도.
이하, 본 발명의 구체적인 실시 예를 살펴보기로 한다.
본 발명의 실시 예는 여러 가지 형태로 변형될 수 있으며, 본 발명의 범위가 아래에서 상세히 설명하는 실시 예로 한정되는 것으로 해석되어서는 안 된다. 본 실시 예는 당 업계에서 평균적인 지식을 가진 자에게 본 발명을 더욱 완전하게 설명하기 위하여 제공되는 것이다.
따라서, 본 상세한 설명에서 표현한 기술특징 등은 더욱 명확한 설명을 강조하기 위해서 과장되어 표현될 수 있다. 또한, 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 공지 기술의 기능 및 구성에 관한 상세한 설명은 생략될 수 있다.
먼저, 본 발명의 일 실시 예에 따른 무수축 미장 몰탈 조성물을 살펴보면 다음과 같다.
본 실시 예에서의 몰탈 조성은, 규사 40~60중량%, 포틀랜드 시멘트, 20~40중량%, CSA(칼슘설포알루미네이트) 1~10중량%, 탄소분말 1~10중량%, 폴리우레아 1~5중량%, 무수석고 1~5중량%, 분말수지 1~3중량%, 탄산칼슘 1~3중량%의 비율로 혼합 조성을 이루도록 하였다.
이때, 혼합 조성물 중 탄소분말은 몰탈의 색상을 기존 제품에 비해 콘크리트색에 유사하도록 나타내고, 폴리우레아는 몰탈층의 탄력성을 향상시키며, 분말수지는 부착력을 증가시키고 수축을 방지하는 기능을 수행하게 된다.
이와 같은 조성을 이루는 무수축 미장 몰탈의 시공과정 및 그에 따른 작용효과를 살펴보면 다음과 같다.
본 발명의 몰탈 조성물은 콘크리트 벽면이나 바닥 균열부위, 각종 PC보수 및 미장사춤 용도로 사용이 이루어지게 되며, 사용 시 물과 적절한 비율로 혼합하여 페이스트 상태로 사용이 이루어지게 된다.
즉, 도 1의 순서도에서와 같이 미장 몰탈을 콘크리트 균열부위에 바르거나 주입 후 5~10분 동안 히터봉 등을 이용하여 70~90℃의 열을 몰탈 표면에 가하게 된다.
이후, 몰탈 표면에 벤질알코올이 혼합된 약액을 분사하여 박막의 코팅층을 형성시키게 된다.
이때 분사되는 약액은 카보머 20~40중량%, 벤질알코올 10~30중량%, 디에틸에테르 10~30중량%, 플루오르화가돌리늄 10~30중량% 비율의 혼합 조성을 이룸이 바람직하다.
이와 같은 과정을 통해 시공이 이루어지게 되면 균열 부위에 충전된 본 발명의 무수축 미장 몰탈로 인하여, 콘크리트 균열부위의 보수가 보다 신속하게 이루어짐과 함께 가열 작용에 따른 부착력을 개선시키고 수축 현상을 방지하는 효과를 나타내게 된다.
특히, 몰탈 표면에 약액 코팅층이 형성되어지게 되면 카보머 및 벤질알코올 작용으로 인해 급격한 몰탈의 보호 기능이 수행되어 몰탈 재료의 유동성 및 속건성이 개선되고, 디에틸에테르는 코팅층의 점도를 유지하여 전체적으로 균일한 박막의 두께로 약액 코팅층이 형성되도록 하며, 플루오르화가돌리늄은 몰탈 표면의 오염방지 및 살균 기능을 수행하는 이점을 나타낸다.
한편, 본 발명의 다른 실시 예로는 상기 무수축 몰탈 조성물에 산화세슘, 벤토나이트, 폴리유산, 브로민, 이산화규소, 알릴 메타크릴레이트가 각각 1~3중량%의 비율로 첨가된다.
즉 이때에는 규사 40~60중량%, 포틀랜드 시멘트, 20~40중량%, CSA(칼슘설포알루미네이트) 1~10중량%, 탄소분말 1~10중량%, 폴리우레아 1~5중량%, 무수석고 1~5중량%로 혼합이 이루어짐과 함께 분말수지, 탄산칼슘, 산화세슘, 벤토나이트, 폴리유산, 브로민, 이산화규소, 알릴 메타크릴레이트 성분이 각각 1~3중량%로 첨가됨이 바람직하다.
이와 같은 조성을 이루게 되면 몰탈의 변색 및 내부 공극 발생을 방지하여 몰탈 품질을 향상시킬 수 있게 된다.
특히, 산화세슘은 몰탈의 내화성을 강화하여 백화 현상을 방지하고, 벤토나이트 및 폴리유산은 수팽창력 향상과 함께 부착력을 강화하여 입자 상호간의 안정적인 결합상태를 이루게 되며, 브로민 및 이산화규소는 몰탈 내구성 및 강도 향상에 따른 크랙 발생을 방지하고, 알릴 메타크릴레이트는 CSA 성분의 활성화에 따른 수축 방지효과를 극대화할 수 있게 된다.
그리고 상기에서 본 발명의 특정한 실시 예가 설명 및 도시되었지만 본 발명의 무수축 미장 몰탈 기술은 당업자에 의해 다양하게 변형되어 실시될 수 있음은 자명한 일이다.
예를 들면, 상기 실시 예에서는 무수축 몰탈의 특정한 성분 혼합 조성이 설명되었으나 필요에 따라서는 기능성 향상을 위한 추가적인 기타성분이 혼합될 수 있게 된다.
또한, 시공과정에 있어서도 건조시간이나 온도 등은 현장 상황 및 계절에 따라 세팅될 수 있게 된다.
따라서 이와 같은 변형된 실시 예들은 본 발명의 기술적 사상이나 범위로부터 개별적으로 이해되어져서는 안되며, 이와 같은 변형된 실시 예들은 본 발명의 첨부된 특허청구범위 내에 포함된다 해야 할 것이다.

Claims (5)

  1. 규사 40~60중량%, 포틀랜드 시멘트, 20~40중량%, CSA(칼슘설포알루미네이트) 1~10중량%, 탄소분말 1~10중량%, 폴리우레아 1~5중량%, 무수석고 1~5중량%, 분말수지 1~3중량%, 탄산칼슘 1~3중량%의 혼합 조성을 이루는 것을 특징으로 하는 무수축 미장 몰탈 조성물.
  2. 청구항 1에 있어서,
    상기 조성물에는 산화세슘 및 벤토나이트가 각각 1~3중량%의 비율로 추가 첨가된 것을 특징으로 하는 무수축 미장 몰탈 조성물.
  3. 청구항 2에 있어서,
    상기 조성물에는 폴리유산, 브로민, 이산화규소, 알릴 메타크릴레이트가 첨가된 것을 특징으로 하는 무수축 미장 몰탈 조성물 시공방법.
  4. 청구항 1 내지 청구항 3중 어느 한 항의 조성을 이루는 미장 몰탈을 콘크리트 균열부위에 주입 후 5~10분 동안 70~90℃의 열을 가한 후, 몰탈 표면에 벤질알코올이 혼합된 액상의 약액을 분사하여 박막의 코팅층을 형성시키는 것을 특징으로 하는 무수축 미장 몰탈 조성물 시공방법.
  5. 청구항 4에 있어서,
    상기 분사되는 액상의 약액은 카보머, 벤질알코올, 디에틸에테르, 플루오르화가돌리늄의 혼합 조성을 이루는 것을 특징으로 하는 무수축 미장 몰탈 조성물 시공방법.
KR1020200157589A 2020-11-23 2020-11-23 무수축 미장 몰탈 조성물 및 그 시공방법 KR102609216B1 (ko)