KR20200113478A - Water-Soluble Jade Extract and Preparation Method Thereof - Google Patents
Water-Soluble Jade Extract and Preparation Method Thereof Download PDFInfo
- Publication number
- KR20200113478A KR20200113478A KR1020190033709A KR20190033709A KR20200113478A KR 20200113478 A KR20200113478 A KR 20200113478A KR 1020190033709 A KR1020190033709 A KR 1020190033709A KR 20190033709 A KR20190033709 A KR 20190033709A KR 20200113478 A KR20200113478 A KR 20200113478A
- Authority
- KR
- South Korea
- Prior art keywords
- jade
- soluble
- water
- nano
- extract
- Prior art date
Abstract
Description
본 발명은 나노분산 수용화 옥 추출물 제조 방법 및 그 제조방법으로 제조된 수용화 옥 추출물을 유효성분으로 포함하는 화장료 조성물을 제공하는 것을 그 목적으로 한다.An object of the present invention is to provide a method for preparing a nano-dispersed soluble jade extract and a cosmetic composition comprising a soluble jade extract prepared by the method as an active ingredient.
전자파의 일종인 원적외선은 인체에 가장 유익한 파장인 8~16㎛를 갖고 있으며, 인체에 흡수 될 때 일반 열보다 80배나 깊은 피부심층(4~5cm)까지 침투하여, 각종 병원균등의 사멸에 도움을 줄 수 있다. 또한, 원적외선은 인체 내 세포를 구성하는 수분과 단백질 분자에 방사되어 1분에 약 2,000번씩 미세한 진동으로 공진시켜 세포의 활동을 왕성하게 한다. 세포활동 과정에서 열에너지를 발생시키면서 체온을 높이는 작용을 하는데, 체온이 높아지면 미세혈관이 확장되고 혈액 순환이 활성화되면서 신진대사가 강화되며, 조직 재생력이 증가하면서 혈관 내 혈전을 분해하고 혈액순환을 촉진한다. 혈액이 맑아지므로 수소이온농도(pH)를 향상시켜 체질을 산성에서 약알칼리성으로 개선시키는 능력을 강화시키고 또한 정신건강에 도움이 되는 이완작용으로 성인병의 원인인 스트레스 해소에도 효과가 있다.Far-infrared rays, a kind of electromagnetic wave, have a wavelength of 8~16㎛, which is the most beneficial to the human body, and when absorbed into the human body, it penetrates into the deep skin layer (4~5cm) 80 times deeper than normal heat, helping to kill various pathogens. Can give. In addition, far-infrared rays are radiated to water and protein molecules that make up the cells of the human body, and resonate with minute vibrations about 2,000 times per minute to energize the cells. In the process of cell activity, it generates heat energy and increases body temperature.When body temperature rises, microvessels expand and blood circulation is activated, enhancing metabolism, increasing tissue regeneration, decomposing blood clots in blood vessels, and promoting blood circulation. do. Since the blood becomes clear, it strengthens the ability to improve the constitution from acid to weak alkali by improving the hydrogen ion concentration (pH). Also, it is effective in relieving stress, which is the cause of adult diseases, with a relaxation action that is beneficial to mental health.
원적외선이 인체에 미치는 효과는 피하 층의 온도상승, 미세혈관의 확장, 혈액순환의 촉진, 혈액과 인체와 기타 조직과의 신진대사 강화, 혈액장애의 일소, 조직의 재생능력이나 항 경련능력의 증가 등으로 나타나며 동시에 지각 신경의 이상 흥분억제, 자율신경의 기능 조정효과도 있는 것으로 밝혀졌다. 원적외선(far infrared ray)은 하나의 열 파장으로 사람 피부표면에 복사된 원적외선은 인체 중 물의 진동파장과 거의 비슷하여, 공명(共鳴: resonance) 또는 공진(共振: vibration)작용으로 일반 열이 도달할 수 없는 부위까지 도달하는 특징이 있다.The effects of far-infrared rays on the human body include an increase in the temperature of the subcutaneous layer, expansion of microvessels, promotion of blood circulation, enhancement of metabolism between blood and human body and other tissues, elimination of blood disorders, increase in tissue regeneration ability or anticonvulsant ability. It was found to have the effect of suppressing abnormal excitability of the perceptual nerve and adjusting the function of the autonomic nerve at the same time. Far infrared ray is a single thermal wavelength, and the far infrared ray radiated to the surface of human skin is almost similar to the vibration wavelength of water in the human body, so that general heat can reach it through resonance or vibration. It has the characteristic of reaching areas that cannot be reached.
옥은 광석 자체에서 생육 광선인 5-20㎛의 원적외선을 다량으로 방출하는 성질을 갖는다. 이러한 옥에서 방출되는 원적외선은 신체 내의 불포화지방산, 과산화지질, 오염된 물 등의 중합 고리에 강력하게 작용한다. 옥에서 방출되는 원적외선에 의해 이들 오염 성분들의 이중, 삼중의 결합이 분리되므로 인체의 생리 활성 작용이 증대되고 촉진된다.Jade has the property of emitting a large amount of far-infrared rays of 5-20㎛, which is a growing ray from the ore itself. The far-infrared rays emitted from these jades act strongly on the polymerized rings of unsaturated fatty acids, peroxide lipids, and contaminated water in the body. Since the double and triple bonds of these contaminants are separated by far-infrared rays emitted from the jade, the physiological activity of the human body is increased and promoted.
예로부터 사용된 옥의 종류로는 마노, 유리, 호박, 석웅황, 비취, 천하석옥, 황옥 등이 있다. 옥은 경옥(硬玉)과 연옥(軟玉)으로 구분된다. 경옥은 휘석족(煇石族, pyroxene family)에 속하는 납 휘석조 광물로서, 규산, 산화 알루미늄 및 소다(soda)로 구성된 단사정계(單斜晶系) 물질이고, 그 경도는 수정과 같은 치밀한 덩어리이며, 빛은 흑색, 청록, 녹색이고, 투명 또는 반투명한 성질을 갖는다. 연옥(Nephrite Jade)은 이노규산염(Inosilicates)의 단사정계 휘섬석(煇閃石) 광물체로 고토질 대리암 중 사문석화 초염기성 연옥(蛇紋石化超鹽氣性 軟玉)으로 나뉘어진다. 연옥의 품질은 그의 미세한 구조 즉, 투각섬석-양기석 정자가 속조(束組)와 섬유로 되는 조세(粗細)한 정도로 결정되며, 섬유가 극히 가늘수록 품질이 좋은 것으로 알려져 있다.The types of jade used since ancient times include agate, glass, amber, seokwoonghwang, jade, cheonhaseokok, and topaz. Jade is divided into jadeite (硬玉) and purgatory (軟玉). Jadeite is a lead pyroxene mineral belonging to the pyroxene family, and is a monoclinic material composed of silicic acid, aluminum oxide and soda, and its hardness is a dense mass like crystal. And the light is black, cyan, green, and has a transparent or translucent property. Nephrite Jade is a monoclinic fissile mineral of Inosilicates, and is divided into serpentine superbasic purgatory among the paleo-soil marbles. The quality of purgatory is determined by its fine structure, that is, the fine structure of openwork-yanggiseok spermatozoa, and the finer the fiber is, the finer the fiber is, the better the quality is known.
옥은 그 희소성으로 인하여 상기와 같은 탁월한 의학적 효능이 있는 것으로 알려져 있음에도 대부분 목걸이, 반지, 팔찌 등의 일부 신변장식용 보석 장신구로만 한정적으로 이용되고 있다. 또한, 옥은 고가품이기 때문에 옥을 이용한 일반 생활용품으로의 개발은 상대적으로 미약한 실정이다. Although jade is known to have excellent medical effects as described above due to its scarcity, it is mostly used only as a jewelry accessory for personal decoration such as necklaces, rings, and bracelets. Also, since jade is a high-priced product, the development of jade as a general household product is relatively weak.
이러한 옥의 이용을 위해 분말 상태로 가공하여 사용하고 있으나, 화장품 등에 적용하기 위해서는 옥 분말이 화장료 내에 분산이 어려운 문제점이 있다. 또한, 옥의 원적외선과 음이온 방사 효과를 증가시킬 필요가 있다. 또한, 옥 분말에서는 석면 등이 검출되는 경우가 있어 이를 방지할 필요가 있다.In order to use such jade, it is processed and used in a powder state, but there is a problem in that jade powder is difficult to disperse in cosmetics for application to cosmetics. In addition, there is a need to increase the far-infrared and negative ion radiation effects of jade. In addition, since asbestos may be detected in jade powder, it is necessary to prevent this.
본 발명은 상기와 같은 문제점을 해결하기 위하여, 옥으로부터 발산되는 원적외선이나 음이온 등을 최대로 발휘하여 옥의 효능을 배가시키면서, 화장료내에 분산 효율을 향상시킬 수 있는 나노분산 수용화 옥 추출물 및 그 제조 방법을 제공하는 것을 목적으로 한다.In order to solve the above problems, the present invention maximizes the far-infrared rays or anions emitted from the jade to increase the efficacy of jade, while improving the dispersion efficiency in cosmetics, and a nano-dispersed soluble jade extract and a method for producing the same It aims to provide.
본 발명의 일 실시예에 따르면,According to an embodiment of the present invention,
분말옥을 정제하는 단계(S10);Purifying powdered jade (S10);
상기 S10 단계에서 정제된 분말 옥에 물을 가하고 교반하는 단계(S20);Adding water to and stirring the powder jade purified in step S10 (S20);
상기 S20 단계에서 교반된 액체를 초음파 처리하는 단계(S30); 및Ultrasonicating the liquid stirred in the step S20 (S30); And
상기 S30 단계에서 초음파 처리된 액체에서 수용화되지 않은 옥가루를 거르는 단계(S40)를 포함하는 것을 특징으로 하는 나노분산 수용화 옥 추출물 제조 방법을 제공한다.It provides a method for producing a nano-dispersed water-soluble jade extract, characterized in that it comprises a step (S40) of filtering the jade powder not soluble in the sonicated liquid in the step S30.
상기 S40 단계에서 옥가루가 걸러진 액체를 나노 분쇄기를 이용하여 분쇄하는 단계(S50)를 추가로 포함하는 것을 특징으로 한다.It characterized in that it further comprises a step (S50) of pulverizing the liquid from which the jade powder has been filtered using a nano-pulverizer in step S40.
상기 S10 단계는, The step S10,
상기 분말옥에 물을 가해 침적 시킨 후 100 내지 300 RPM으로 10분간 교반하는 단계(S10-1);Adding water to the powdered jade and immersing it, and then stirring at 100 to 300 RPM for 10 minutes (S10-1);
상기 S10-1 단계에서 교반한 후 30분간 방치하는 단계(S10-2);Stirring in the step S10-1 and leaving it for 30 minutes (S10-2);
물 표면에 뜨는 이물질을 제거하고 아래 침적된 분말옥을 분리하는 단계(S10-3); 및Removing foreign substances floating on the water surface and separating the powdered jade deposited below (S10-3); And
상기 S10-3 단계에서 분리된 침적된 분말옥을 60℃ 열풍 건조하는 단계(S10-4)를 포함하는 것을 특징으로 한다.It characterized in that it comprises a step (S10-4) of drying the deposited powdered jade separated in step S10-3 with hot air at 60°C.
상기 S20 단계에서, 100℃ 내지 121℃ 온도, 15lb psi 압력에서 1시간 교반하는 것을 특징으로 한다.In the step S20, characterized in that stirring for 1 hour at a temperature of 100 ℃ to 121 ℃, 15lb psi pressure.
상기 S30 단계에서, 1시간동안 40KHz 초음파로 처리하는 것을 특징으로 한다.In step S30, it is characterized in that the treatment is performed with 40KHz ultrasonic waves for 1 hour.
본 발명의 다른 실시예에 따르면 상기 제조 방법으로 추출된 수용화 옥 추출물을 유효 성분으로 포함하는 화장료 조성물을 제공한다.According to another embodiment of the present invention, there is provided a cosmetic composition comprising the water-soluble jade extract extracted by the above manufacturing method as an active ingredient.
본 발명의 다른 실시예에 따르면, 유연화장수, 영양화장수, 수분크림, 영양크림, 마사지크림, 에센스, 앰플, 젤, 아이크림, 클렌징크림, 클렌징폼, 클렌징워터, 팩, 스프레이 및 파우더로 이루어진 군에서 선택된 하나 이상으로 제형화된 화장료 조성물을 제공할 수 있다.According to another embodiment of the present invention, the group consisting of softening lotion, nutritional lotion, moisture cream, nutrition cream, massage cream, essence, ampoule, gel, eye cream, cleansing cream, cleansing foam, cleansing water, pack, spray and powder A cosmetic composition formulated with one or more selected from can be provided.
본 발명의 실시 예에 따르면, 옥으로부터 발산되는 원적외선이나 음이온 등을 최대로 발휘하여 옥의 효능을 배가시키면서, 화장료내에 분산 효율을 향상시킬 수 있는 나노분산 수용화 옥 추출물 제조 방법 및 화장료 조성물을 제공할 수 있다.According to an embodiment of the present invention, it is possible to provide a nano-dispersed water-soluble jade extract manufacturing method and a cosmetic composition capable of improving the dispersion efficiency in cosmetics while maximizing far-infrared rays or anions emitted from jade to increase the efficacy of jade. I can.
도 1 은 본 발명의 일 실시예에 따른 수용화옥 추출물 제조방법을 나타낸 흐름도이다.
도 2 는 본 발명의 실시예에 따라 제조된 수용화옥 추출물을 포함하는 마스크팩의 석면 검출 시험 결과를 나타내는 도면이다.
도 3 는 본 발명의 실시예에 따라 제조된 수용화옥 추출물을 포함하는 마스크팩의 원적외선 시험 성적서를 나타내는 도면이다.
도 4 는 본 발명의 실시예에 따라 제조된 수용화옥 추출물을 포함하는 마스크팩의 음이온 시험 성적서를 나타내는 도면이다.1 is a flow chart showing a method for preparing a soluble hwaok extract according to an embodiment of the present invention.
Figure 2 is a view showing the results of the asbestos detection test of the mask pack containing the extract prepared according to an embodiment of the present invention.
Figure 3 is a view showing a far-infrared test report of the mask pack containing the extract prepared in accordance with an embodiment of the present invention.
4 is a view showing an anion test report of a mask pack containing an extract prepared according to an embodiment of the present invention.
본 발명의 실시 예에 따른 나노분산 수용화 옥 추출물 제조 방법은 분말 옥광석 정제 단계, 분말옥의 수용화(solable) 및 활성화 단계, 및 옥 수용화액 분리단계를 포함한다.A method for preparing a nano-dispersed water-soluble jade extract according to an embodiment of the present invention includes a step of purifying powdered jade ore, a step of solable and activating powdered jade, and a step of separating an aqueous jade solution.
1. 분말 옥 광석의 정제단계1. Purification step of powdered jade ore
분말 옥은 광석 옥을 분쇄하여 분말화하거나 분말 상태의 옥광석 가루를 사용한다. 분말화의 방법은 광물파쇄기(Crusher, 3-야나 mill등)나 막자 등으로 진행할 수 있으며, 이때 분말 옥입자는 메쉬망(80mesh)을 사용하여 80mesh이하로 분쇄된 것을 사용하는 것이 바람직하다.Powdered jade is pulverized by pulverizing ore jade, or powdered jade ore powder is used. The method of pulverization can be carried out with a mineral crusher (Crusher, 3-Yana mill, etc.) or a mortar, and it is preferable to use the powder jade particles crushed to less than 80 mesh using a mesh net (80 mesh).
1kg의 불균질 분말 상태의 광석옥을 물을 가해 침적시킨 후 100~300 rpm으로 10분간 교반해 준 후 30분 동안 방치한다.1 kg of heterogeneous powdered ore jade was immersed by adding water, stirred at 100 to 300 rpm for 10 minutes, and left for 30 minutes.
물 표면에 뜨는 이물질을 먼저 제거하고 아래 침적된 분말옥만을 분리한다. Foreign matter floating on the water surface is first removed, and only the powder jade deposited below is separated.
침적된 분말옥은 60℃ 이상에서 열풍건조 등의 방법으로 건조하여 960g의 분말옥을 수득한다.The deposited powdered jade is dried by a method such as hot air drying at 60℃ or higher to obtain 960g of powdered jade.
2. 분말옥의 수용화 및 활성화 단계2. Water solubility and activation step of powdered jade
옥 분말 300g당 500mL의 물을 가하고 Stainless Steel Bomber에 투입한 후 121℃, 15lb psi 압력 조건에서 1시간 동안 교반한다.500mL of water per 300g of jade powder was added, put into a stainless steel bomber, and stirred for 1 hour at 121℃ and 15lb psi pressure.
이후 옥가루와 상층액을 같이 1시간동안 40KHz 초음파 처리한다.After that, the jade powder and the supernatant are ultrasonically treated for 1 hour at 40 KHz.
3. 옥 수용화 액의 분리단계3. Separation step of jade aqueous solution
초음파 처리된 옥가루 및 상층액을 먼저 부직포망을 이용하여 가용되지 않은 옥가루를 1차로 거른 후, 0.2um 필터를 이용하여 수용화된 옥 추출물 477mL을 수득한다.First, the sonicated jade powder and the supernatant were first filtered through a non-woven fabric to filter out unsoluble jade powder, and then 477 mL of the soluble jade extract was obtained using a 0.2 um filter.
4. 옥 수용화액을 나노 사이즈로 분쇄하는 단계4. The step of pulverizing the jade aqueous solution into nano size
옥가루가 걸러진 옥 수용화액을 나노 분쇄기에 투입하여 나노 사이즈로 분쇄하여 옥 나노 분산 수용액을 수득한다. 나노분쇄기는 습식 나노입자 분쇄기를 사용하는 것이 바람직하다. 수용화된 옥 입자를 나노 사이즈로 분쇄하여 피부에 효과적으로 분산 흡수될 수 있게 된다. 나노분쇄기는 RETSCH 사의 High Energy Ball Mill Emax, Kotobuki 습식 나노입자 분쇄기, THINKY 사의 arm-310 등을 사용할 수 있다.The jade aqueous solution from which jade powder has been filtered is added to a nano pulverizer and pulverized to a nano size to obtain a jade nano-dispersed aqueous solution. It is preferable to use a wet nanoparticle pulverizer for the nano pulverizer. The soluble jade particles can be pulverized into nano-sized so that they can be effectively dispersed and absorbed into the skin. The nano pulverizer can be used with RETSCH's High Energy Ball Mill Emax, Kotobuki's wet nanoparticle pulverizer, and THINKY's arm-310.
* 성능시험결과* Performance test result
도 2는 상기 제조 방법에 의해 제조된 수용화된 옥 추출물을 포함하는 마스크팩에 대한 석면 검사 결과를 나타낸다. 도 2와 같이 석면 검사 시험법(KS L 5300:2009)으로 검사하였을 때 석면이 검출되지 않았다. 즉, 일반 옥 분말에 검출 위험이 있는 석면이 수용화된 옥 추출물에서는 검출되지 않음을 확인할 수 있다. 따라서, 화장료 등에 안전하게 적용할 수 있다.2 shows the results of the asbestos test for the mask pack containing the soluble jade extract prepared by the above manufacturing method. Asbestos was not detected when tested by the asbestos test method (KS L 5300:2009) as shown in FIG. 2. That is, it can be confirmed that asbestos, which is at risk of detection in general jade powder, is not detected in the soluble jade extract. Therefore, it can be safely applied to cosmetics and the like.
본 발명에 따른 수용화된 옥 추출물의 성능을 나타내기 위하여, 일반 제조방법으로 제조된 대조군과의 성능차이를 비교 실험하였다. 대조군은 다음과 같은 방법으로 제조하였다.In order to show the performance of the soluble jade extract according to the present invention, the difference in performance with the control prepared by the general manufacturing method was compared and tested. The control was prepared by the following method.
(1)pH 비교(1) pH comparison
pH를 식품의약품안전처 기능성화품 기준 및 시험방법 일반시험법 VI-2, 제제의 pH항에 따라 시험하여 다음의 결과를 얻었으며, pH에 대해서는 시험군(본특허방법)및 대조군과의 차이가 거의 없었다.The pH was tested in accordance with the Ministry of Food and Drug Safety's Functional Product Standards and Test Method General Test Method VI-2, the pH of the formulation, and the following results were obtained, and the difference between the test group (this patent method) and the control group was There was little.
(2)음이온 발생량 비교(2) Comparison of anion generation amount
도 4는 본 발명의 실시예에 따라 제조된 옥 추출물을 포함하는 마스크팩의 음이온 발생 결과를 측정한 시험성적서를 나타낸다. 도시되는 바와 같이, 기준시험법 KFIA-FI-1042에 따라 전하입자 측정장치를 이용하여 측정대상물에서 방출되는 음이온을 단위체적당 ion수로 측정하였을 때 본 발명의 실시예의 음이온 발생량이 대조군 대비 높은 것을 확인할 수 있었다.Figure 4 shows a test report measuring the negative ions generation results of the mask pack containing the jade extract prepared according to an embodiment of the present invention. As shown, it can be confirmed that the amount of anion generated in the examples of the present invention is higher than that of the control when the anions emitted from the measurement object are measured as the number of ions per unit volume using a charged particle measuring device according to the reference test method KFIA-FI-1042. there was.
(ion/cc)Negative ions
(ion/cc)
(3)원적외선 발생량 비교(3) Comparison of far-infrared rays generation
도 3은 본 발명의 실시예에 따라 제조된 옥 추출물을 포함하는 마스크팩의 원적외선 발생 결과를 측정한 시험성적서를 나타낸다. 도시되는 바와 같이, 기준시험법 KFIA-FI-1005에 따라 FT-IR을 이용하여 원적외선을 측정한 결과 본 발명의 실시예의 음이온 발생량이 높은 것을 확인하였다.Figure 3 shows a test report measuring the far-infrared generation results of the mask pack containing the jade extract prepared according to an embodiment of the present invention. As shown, as a result of measuring the far-infrared rays using FT-IR according to the reference test method KFIA-FI-1005, it was confirmed that the amount of negative ions generated in the examples of the present invention was high.
본 발명은 피부의 미용에 도움이 되는 음이온 및 원적외선을 화장품 제품에 함유할 수 있도록 풍부한 옥을 수용화 제조방법에 관한 것으로서, 분말화 된 광석옥을 침습 정제하는 단계와, 상기 정제된 옥가루에 열, 초음파 등의 에너지를 주어 원적외선 방출을 향상시키는 단계 및 수용화되지 않은 옥가루를 분리하는 수용화 정제 단계를 포함하는 것을 특징으로 한다.The present invention relates to a manufacturing method of water-soluble jade so that a cosmetic product can contain negative ions and far-infrared rays that are useful for the beauty of the skin, the step of invasively purifying powdered ore jade, and heat to the purified jade powder. It characterized in that it comprises a step of improving the far-infrared emission by applying energy such as ultrasonic waves, and a water-soluble purification step of separating the unwatered jade powder.
본 발명은 옥 추출물을 수용화하여 침전물 없이 사용가능하며, 옥이 가지는 음이온 또는 원적외선 방출 특징을 가지는 추출물로서, pH가 6~8 범위로 다양한 화장품 제형에 적용가능할 수 있다The present invention can be used without sediment by water-soluble jade extract, as an extract having anion or far-infrared emission characteristics of jade, and may be applicable to various cosmetic formulations with a pH ranging from 6 to 8
Claims (6)
상기 S10 단계에서 정제된 분말 옥에 물을 가하고 교반하는 단계(S20);
상기 S20 단계에서 교반된 액체를 초음파 처리하는 단계(S30);
상기 S30 단계에서 초음파 처리된 액체에서 수용화되지 않은 옥가루를 거르는 단계(S40); 및
상기 S40 단계에서 옥가루가 걸러진 옥 수용화액을 나노 분쇄기에 투입하여 나노 사이즈로 분쇄하는 단계(S50);여 를 포함하는 것을 특징으로 하는 나노분산 수용화 옥 추출물 제조 방법.Purifying powdered jade (S10);
Adding water to and stirring the powder jade purified in step S10 (S20);
Ultrasonicating the liquid stirred in the step S20 (S30);
Filtering the jade powder that is not soluble in the sonicated liquid in step S30 (S40); And
In the step S40, the step of pulverizing the jade aqueous solution from which the jade powder has been filtered into a nano-sized nano-sized (S50); Method for producing a nano-dispersed water-soluble jade extract comprising a.
상기 S10 단계는,
상기 분말옥에 물을 가해 침적 시킨 후 100 내지 300 RPM으로 10분간 교반하는 단계(S10-1);
상기 S10-1 단계에서 교반한 후 30분간 방치하는 단계(S10-2);
물 표면에 뜨는 이물질을 제거하고 아래 침적된 분말옥을 분리하는 단계(S10-3); 및
상기 S10-3 단계에서 분리된 침적된 분말옥을 60℃ 열풍 건조하는 단계(S10-4)를 포함하는 나노분산 수용화 옥 추출물 제조 방법.The method of claim 1,
The step S10,
Adding water to the powdered jade and immersing it, and then stirring at 100 to 300 RPM for 10 minutes (S10-1);
Stirring in the step S10-1 and leaving it for 30 minutes (S10-2);
Removing foreign substances floating on the water surface and separating the powdered jade deposited below (S10-3); And
A method for preparing a nano-dispersed soluble jade extract comprising the step of drying the deposited powdered jade separated in step S10-3 with hot air at 60°C (S10-4).
상기 S20 단계에서, 100℃ 내지 121℃ 온도, 15lb psi 압력에서 1시간 교반하는 것을 특징으로 하는 나노분산 수용화 옥 추출물 제조 방법.The method of claim 1,
In the step S20, a method for preparing a nano-dispersed water-soluble jade extract, characterized in that stirring for 1 hour at a temperature of 100° C. to 121° C. and a pressure of 15 lb psi.
상기 S30 단계에서, 1시간동안 40KHz 초음파로 처리하는 것을 특징으로 하는 나노분산 수용화 옥 추출물 제조 방법.The method of claim 1,
In the step S30, the method for producing a nano-dispersed soluble jade extract, characterized in that the treatment with 40KHz ultrasonic waves for 1 hour.
유연화장수, 영양화장수, 수분크림, 영양크림, 마사지크림, 에센스, 앰플, 젤, 아이크림, 클렌징크림, 클렌징폼, 클렌징워터, 팩, 스프레이 및 파우더로 이루어진 군에서 선택된 하나 이상으로 제형화된 화장료 조성물.
The method of claim 5,
Cosmetics formulated with one or more selected from the group consisting of softening lotion, nutrient lotion, moisture cream, nutrition cream, massage cream, essence, ampoule, gel, eye cream, cleansing cream, cleansing foam, cleansing water, pack, spray and powder Composition.