KR20190111760A - 내화 성능이 향상된 결로방지용 복합단열판넬 및 그 제조방법 - Google Patents
내화 성능이 향상된 결로방지용 복합단열판넬 및 그 제조방법 Download PDFInfo
- Publication number
- KR20190111760A KR20190111760A KR1020190024002A KR20190024002A KR20190111760A KR 20190111760 A KR20190111760 A KR 20190111760A KR 1020190024002 A KR1020190024002 A KR 1020190024002A KR 20190024002 A KR20190024002 A KR 20190024002A KR 20190111760 A KR20190111760 A KR 20190111760A
- Authority
- KR
- South Korea
- Prior art keywords
- composite
- synthetic resin
- resin hollow
- flame retardant
- insulation panel
- Prior art date
Abstract
본 발명은 내화 성능이 향상된 결로방지용 복합단열판넬 및 그 제조방법에 관한 것이다.
본 발명에 따른 내화 성능이 향상된 결로방지용 복합단열판넬은 난연 성능과 결로방지에 유용한 통기성을 제공하도록 다수개의 통공을 가지며 양면에 표면 개질 처리가 된 제1 및 제2 복합합성수지 중공판과, 상기 제1 및 제2 복합합성수지 중공판의 일면에 형성되는 불연성 코팅층과, 상기 제1 및 제2 복합합성수지 중공판의 타면에 형성되는 열경화성 접착제층과, 양면에 수용성 난연 접착제가 도포된 후 난연 부직포가 부착되며 상기 제1 및 제2 복합합성수지 중공판의 열경화성 접착제층과 접착되는 난연 2급의 준불연성 페놀폼계 단열재로 구성되며, 보수의 용이성과 도장, 벽지 마감의 용이성 및 설치공정의 단순화로 제품 경쟁력을 향상시키고 또한 내화 성능이 난연 등급에서 난연 2급의 준불연 등급으로 대폭 강화된 것을 특징으로 하는 것이다.
본 발명에 따른 내화 성능이 향상된 결로방지용 복합단열판넬은 난연 성능과 결로방지에 유용한 통기성을 제공하도록 다수개의 통공을 가지며 양면에 표면 개질 처리가 된 제1 및 제2 복합합성수지 중공판과, 상기 제1 및 제2 복합합성수지 중공판의 일면에 형성되는 불연성 코팅층과, 상기 제1 및 제2 복합합성수지 중공판의 타면에 형성되는 열경화성 접착제층과, 양면에 수용성 난연 접착제가 도포된 후 난연 부직포가 부착되며 상기 제1 및 제2 복합합성수지 중공판의 열경화성 접착제층과 접착되는 난연 2급의 준불연성 페놀폼계 단열재로 구성되며, 보수의 용이성과 도장, 벽지 마감의 용이성 및 설치공정의 단순화로 제품 경쟁력을 향상시키고 또한 내화 성능이 난연 등급에서 난연 2급의 준불연 등급으로 대폭 강화된 것을 특징으로 하는 것이다.
Description
관련된 출원에 대한 크로스-
레퍼런스
본 발명은 이 출원에 인용된 모든 다른 레퍼런스들과 함께 전체적으로 모든 목적을 위해 레퍼런스로 합체되는 것으로, 2018년 3월 23일자로 출원된 대한민국 특허출원 번호 10-2018-0033614의 우선권 이익을 청구한다.
기술분야
본 발명은 내화 성능이 향상된 결로방지용 복합단열판넬 및 그 제조방법에 관한 것으로서, 보다 상세하게는 난연 성능과 결로방지에 유용한 통기성을 제공하도록 다수개의 통공을 가지며 양면에 표면 개질 처리가 된 제1 및 제2 복합합성수지 중공판과, 상기 제1 및 제2 복합합성수지 중공판의 일면에 형성되는 불연성 코팅층과, 상기 제1 및 제2 복합합성수지 중공판의 타면에 형성되는 열경화성 접착제층과, 양면에 수용성 난연 접착제가 도포된 후 난연 부직포가 부착되며 상기 제1 및 제2 복합합성수지 중공판의 열경화성 접착제층과 접착되는 난연 2급의 준불연성 페놀폼계 단열재로 구성되며, 보수의 용이성과 도장, 벽지 마감의 용이성 및 설치공정의 단순화로 제품 경쟁력을 향상시키고 또한 내화 성능이 난연 등급에서 난연 2급의 준불연 등급으로 대폭 강화된 내화성능이 향상된 결로방지용 복합단열판넬에 관한 것이다.
주지된 바와 같이, 건축물에 있어 내부와 외부 사이의 온도 차이가 심한 경우에 건축 재료의 열전달을 최소화하여 건축물 외부의 기온과 관계없이 실내 기온을 일정하게 유지해주기 위하여 단열재가 사용되고 있다. 상기 단열재는 내부에 미세한 기공(공기층)이 많은 재료가 사용되어 단열성능을 향상시킨다.
또한, 상기 단열재는 동절기에 실내와 실외의 기온이 현격히 차이가 발생되어 건축물의 외주부 중 단열성능이 부족한 부분의 표면 온도가 노점온도 이하로 떨어지면 그 표면에 물방울이 발생하는 결로현상이 발생될 수 있다. 상기 결로현상은 벽지 또는 페인트 등 내수 성능이 취약한 실내마감 재료로 처리된 부분이 부패되거나 인체에 유해한 곰팡이 등이 발생하게 되어, 실내환경을 크게 훼손시키는 문제가 있었다.
이에, 상기한 단열성능을 향상시키고 결로현상을 방지시키기 위하여 다양한 형태의 결로방지용 단열판넬 및 그 제조방법이 제안되고 있다.
상기 결로방지용 단열판넬은 설치방법에 따라 선시공 공법과 후시공 공법으로 구분된다.
상기 선시공 공법에는 내부 옹벽 및 천정부 결로방지 단열판, 지하층 및 최상층 결로방지 단열판 등 거푸집에 선시공하여 콘트리트를 타설함으로써, 벽면 및 천정과 일체로 상기 결로방지 단열판을 형성시키는 공법이다.
상기 후시공 공법에는 신발장 및 붙박이장 후변부 단열마감판, 발코니 다용도실 벽면부 단열마감판, 내부 옹벽의 단열마감판 등 기존 벽면에 시공하여 벽면 및 천정을 형성시키는 공법이다.
그 중에서 종래 일반적으로 사용되는 결로방지용 단열판의 사시도가 도 1에 도시되어 있으며, 이에 대해 설명하면 다음과 같다.
도시된 바와 같이, 결로현상 방지 및 단열 향상을 위하여 폴리프로필렌(PP) 수지로 제조된 합성수지 중공판(12)에 열가소성 수지 접착제를 사용하여 스티렌계 발포성 합성수지(14)를 결합시킨 복합 단열판넬(10)이 제조된다.
그러나, 상기 스티렌계 발포성 합성수지(14)를 결합시키는 상기 접착제로 사용되는 열가소성 수지는 열에 약하여 일정 온도 상승시 이탈됨으로써 상기 합성수지 중공판(12)으로부터 스티렌계 발포성 합성수지(14)가 쉽게 떨어지는 단점이 있다.
또한, 합성수지 중공판(12)의 표면에 코로나 열처리나 부직포 융착 등을 하여 벽지, 페인트 등의 마감처리가 용이하도록 하였으나, 합성수지 중공판(12)에 시멘트가 쉽게 부착되지 않고 표면강도가 약하여 건설공사 현장에서 합성수지 중공판(12)의 파손이 심하고 시멘트 등으로 보수할 수 없어 설치비용이 가중되는 문제가 발생하였으며, 합성수지 중공판이 열에 약하여 직사광선이 직접 전달되는 앞쪽발코니에는 적용하기 어려운 단점이 있다.
또한 합성수지 중공판의 표면 개질을 수행하지 아니한 상태에서 몰탈을 도포, 제조하면, 표면에 몰탈이 부착되지 않고 이탈되는 문제점이 발생하고 있다.
또한, 합성수지 중공판(12)을 제조하기 위하여 통상 폴리프로필렌(PP) 수지가 사용되었으나, 상기 폴리프로필렌 수지는 프로필렌의 중합체로서 밀도가 0.9~0.91이며, 결정도는 크지만 성형한 후에는 70% 이하로 저하되고 탄소와 수소로만 이루어져 있어 전기적 성질이 우수한 반면에, 첫째 합성수지와 스티로폼과 같은 서로 다른 물성을 합지하는 과정에서 이물질 부착에 따른 복합 단열판넬(10)의 휨 발생으로 인하여 제품의 결함이 발생되어 성능이 저하되는 문제가 있었고, 둘째 열에 약하기 때문에 수축 및 팽창이 빈번하게 발생되어 복합 단열판넬(10)을 제조할 때 휨,이탈 등이 발생되고, 셋째 외부의 충격에 의해 쉽게 파손되는 문제점들이 있었다.
본 발명은 상기한 문제점을 해결하기 위하여 된 것으로서, 본 발명의 목적은건물 공사 수행시 별도의 방습층을 구비하지 않고 마감과 방습공사를 한번에 수행하며 단열재의 두께감소, 벽체 두께감소 등에 따른 공사원가절감이 가능하고, 준불연 성능을 만족시키면서 단열판넬의 파손시 시멘트 등으로 그 보수가 용이하도록 하고, 단열판넬 내부로 수분이 침투하더라도 복합합성수지 중공판과 단열재가 쉽게 떨어지지 않도록 하고, 벽체 또는 천장에 잘 부착될 수 있으며, 내화 성능이 난연 등급에서 준불연 등급으로 대폭 강화된 것을 특징으로 하는 내화성능이 향상된 결로방지용 복합단열판넬 및 그 제조방법을 제공하는 데 그 목적이 있다.
본 발명에 따른 내화성능이 향상된 결로방지용 복합단열판넬의 특징은, 건축물의 소정 부위에 부착되어 단열성능 향상과 결로현상 방지 및 곰팡이 발생을 방지토록 하는 결로방지용 복합단열판넬에 있어서, 난연 성능과 결로방지에 유용한 통기성을 제공하도록 다수개의 통공을 가지며 양면에 표면 개질 처리가 된 제1 및 제2 복합합성수지 중공판과, 상기 제1 및 제2 복합합성수지 중공판의 일면에 형성되는 불연성 코팅층과, 상기 제1 및 제2 복합합성수지 중공판의 타면에 형성되는 열경화성 접착제층과, 양면에 수용성 난연 접착제가 도포된 후 난연 부직포가 부착되며 상기 제1 및 제2 복합합성수지 중공판의 열경화성 접착제층과 접착되는 난연 2급의 준불연성 페놀폼계 단열재로 구성되며, 내화 성능이 난연 등급에서 난연 2급의 준불연 등급으로 대폭 강화된 것에 있다.
또한, 본 발명에 따른 내화성능이 향상된 결로방지용 복합단열판넬의 제조방법의 특징은, 건축물의 소정 부위에 부착되어 단열성능 향상과 결로현상 방지 및 곰팡이 발생을 방지토록 하는 결로방지용 복합단열판넬의 제조방법에 있어서, 폴리프로필렌 수지와 탈크를 포함하여 이루어진 복합수지 원료에 난연제 및 UV 안정제를 첨가하고 혼합하여 융해하는 단계, 상기 혼합 융해 원료로 소정의 압출기에서 다수의 통공을 가지는 복합합성수지 중공판으로 제조하는 단계, 상기 복합합성수지 중공판의 양면을 표면 개질 처리하는 단계, 상기 표면 개질 처리된 복합합성수지 중공판을 25 ~ 30℃로 24시간 동안 양생하여 절단하는 단계, 상기 양생하여 절단된 제1 및 제2 복합합성수지 중공판의 일면에 유,무기질 접착제를 도포하여 내화 성능을 난연 등급에서 난연 2급의 준불연 등급으로 향상시킬 수 있는 불연성 무기질 코팅층을 형성하는 단계, 상기 일면에 불연성 무기질 코팅층이 형성된 제1 및 제2 복합합성수지 중공판의 타면에 열경화성 접착제를 도포하여 열경화성 접착제층을 형성하는 단계, 페놀폼계 단열재의 양면에 수용성 난연 접착제를 도포한 후 난연 부직포를 부착하는 단계, 상기 제1 및 제2 복합합성수지 중공판의 열경화성 접착제층 사이에 상기 페놀폼계 단열재를 접착하는 단계, 상기 접착된 복합단열판넬을 건조실에서 25 ~ 30℃로 24시간 동안 건조시키는 단계, 상기 건조된 복합단열판넬의 제1 및 제2 복합합성수지 중공판과 페놀폼계 단열재의 접착 틈새를 접착제로 밀봉하는 단계로 이루어지는 것에 있다.
본 발명에 따른 내화성능이 향상된 결로방지용 복합단열판넬에 의하면, 건축물의 소정 부위에 부착되어 단열성능 향상과 결로현상 방지 및 곰팡이 발생을 방지토록 하는 결로방지용 복합단열판넬에 있어서, 난연 성능과 결로방지에 유용한 통기성을 제공하도록 다수개의 통공을 가지며 양면에 표면 개질 처리가 된 제1 및 제2 복합합성수지 중공판과, 상기 제1 및 제2 복합합성수지 중공판의 일면에 형성되는 불연성 코팅층과, 상기 제1 및 제2 복합합성수지 중공판의 타면에 형성되는 열경화성 접착제층과, 양면에 수용성 난연 접착제가 도포된 후 난연 부직포가 부착되며 상기 제1 및 제2 복합합성수지 중공판의 열경화성 접착제층과 접착되는 난연 2급의 준불연성 페놀폼계 단열재로 구성되며, 내화 성능이 난연 등급에서 난연 2급의 준불연 등급으로 대폭 강화된 결로방지용 복합단열판넬이 제공됨으로써, 건물 공사 수행시 별도의 방습층을 구비하지 않고 마감과 방습공사를 한번에 수행하며 단열재의 두께감소, 벽체 두께감소 등에 따른 공사 원가절감이 가능하다. 또한, 준불연 성능을 만족시키면서 단열판넬의 파손시 시멘트 등으로 그 보수가 용이하도록 하고, 단열판넬 내부로 수분이 침투하더라도 복합합성수지 중공판과 단열재가 쉽게 떨어지지 않도록 하고, 벽체 또는 천장에 잘 부착될 수 있게 된다. 또한, 내화 성능이 난연 등급에서 난연 2급의 준불연 등급으로 대폭 강화되게 되는 것이다.
도 1은 종래기술에 따른 결로방지용 복합단열판넬을 보인 사시도,
도 2는 본 발명에 따른 내화 성능이 향상된 결로방지용 복합단열판넬을 보인 사시도,
도 3은 도 2의 'A'부 확대 사시도,
도 4는 본 발명에 따른 내화 성능이 향상된 결로방지용 복합단열판넬의 제조과정을 보인 흐름도이다
도 2는 본 발명에 따른 내화 성능이 향상된 결로방지용 복합단열판넬을 보인 사시도,
도 3은 도 2의 'A'부 확대 사시도,
도 4는 본 발명에 따른 내화 성능이 향상된 결로방지용 복합단열판넬의 제조과정을 보인 흐름도이다
이하, 본 발명의 바람직한 실시예를 첨부된 도면을 참조하여 설명하면 다음과 같다.
도 2는 본 발명에 따른 내화 성능이 향상된 결로방지용 복합단열판넬을 보인 사시도이다.
도 3은 도 2의 A부 확대 사시도이다.
도시된 바와 같이, 제1 및 제2 복합합성수지 중공판(22)(23)은 내장재로서의 필요한 표면강도를 갖는 폴리프로필렌(PP) 수지 및 탈크 등으로 되는 복합수지 원료에 난연제 및 UV 안정제가 첨가되어 혼합, 융해되어 제조된다. 또한, 결로방지에 유용한 성능인 통기성을 가지도록 다수개의 통공(28)이 구비된다. 또한, 상기 제1 및 제2 복합합성수지 중공판(22)(23)의 양면은 코로나 열처리 또는 부직포 등의 열융착에 의한 표면 개질 처리가 된다. 상기 제1 및 제2 복합합성수지 중공판(22)(23)의 일면에 유,무기질 접착제가 도포되어 내화 성능이 난연 등급에서 난연 2급의 준불연 등급으로 향상되는 불연성 무기질 코팅층(30)이 형성된다. 상기 제1 및 제2 복합합성수지 중공판(22)(23)의 타면에 우레탄 및 에폭시계 열경화성 접착제가 도포되어 열경화성 접착제층(26)이 형성된다. 페놀폼계 단열재(24)의 양면에 수용성 난연 접착제가 도포된 후 난연 부직포(32)가 부착된다. 이와같이 된 준불연성 페놀폼계 단열재가 상기 제1 및 제2 복합합성수지 중공판(22)(23)의 열경화성 접착제층(26)과 접착된다.
이렇게 하여 내화 성능이 난연 등급에서 난연 2급의 준불연 등급으로 대폭 강화된 내화 성능이 향상된 결로방지용 복합단열판넬(20)이 제공된다.
한편, 상기 복합합성수지 중공판(22),(23)은 폴리플로필렌 수지만으로도 제조된다.
또한, 상기 복합합성수지 중공판(22),(23)과 페놀폼계 단열재(24)를 접착하는데 있어서는 무용제형의 에폭시계 접착제 및 우레탄계 접착제가 사용된다. 상기 에폭시 및 우레탄계 접착제는 수분 및 열에 강하기 때문에 콘트리트 벽체 또는 천정에 함유된 수분 성분이 침투하는 것을 막을 수 있으며, 무수축성이고 변형이 발생되지 않아 본 발명에 따른 결로방지용 복합단열판넬(20)의 평판을 확보하는데 적합하다.
또한, 상기 불연성 코팅층(30)은 유,무기질을 충진제로 하여 구성되는 접착제가 사용되며 일반 몰탈이나 시멘트 등은 복합합성수지 중공판에 직접 부착이 난해하며, 유,무기질 접착제는 복합단열판넬(20)의 표면강도 증대와 내화성능(준불연 등급)이 강화되도록 구성되는 바, 시멘트, 질석, 모래, 규사, 석고 등 무기질 성분과 아크릴, 초산비닐 등 유기질 성분이 혼합된 접착제가 사용된다.
이어, 본 발명에 따른 내화 성능이 향상된 결로방지용 복합단열판넬의 제조방법을 도 4를 참조하여 설명한다.
여기에서, 본 발명에 적용된 복합수지 원료는 동일한 기능 및 성분, 효과가 제공되는 범위 내에서 다른 공급업체의 원료가 적용될 수 있음은 물론이고, 또한 원료 공급양도 변화될 수 있다.
먼저, 폴리프로필렌 수지와 탈크등을 포함하는 복합수지 원료에 난연제 및 UV 안정제를 첨가하고 혼합하여 압출성형 기기에서 설정 온도를 220℃로 한 상태로 융해시키고(S100), 다수개의 통공(28)이 일체로 형성되는 제1 및 제2 복합합성수지 중공판(22)(23)을 제조한다(S102). 이때, 상기 혼합원료의 중량비 대비 난연제는 8~10％, UV 안정제는 3~5％가 첨가된다.
다음으로, 상기 복합합성수지 중공판(22)(23)의 양면에 대해 표면 개질 처리공정이 수행된다(S104). 이 표면 개질 처리는 2가지 방법이 채택되며 그 첫째로는 상기 복합합성수지 중공판(22)(23)의 양면에 코로나 열처리기구(성진기기, EMS 202)에 의하여 코로나 열처리가 수행되고, 다른 방법으로는 부직포를 열융착하여 수행된다. 상기 코로나 열처리는 복합합성수지 중공판(22)(23)의 표면에 존재하는 유막을 제거하며 상기 표면에 미세한 요철을 발생시켜 타물질과의 부착력이 향상되도록 표면 개질 처리를 하는 것이고 부직포 열융착 처리는 복합합성수지 중공판(22)(23)의 표면에 부직포 등을 열융착하여 타물질과의 부착력을 향상시키는 것이다.
여기에서, 상기 표면 개질 처리는 플라스틱 일부의 재질에 에너지가 강한 단파장의 자외선을 인가하여 플라스틱 표면의 화학 결합을 절단시키면, 상기 플라스틱 표면의 극성이 높아져서 극성이 다른 물질 즉, 도료, 착색제, 코팅제 등이 부착되기 쉽도록 처리하는 것을 말하며, 본 발명에서는 코로나 열처리에 의하여 수행된다.
이와 같이, 표면 개질 처리가 완료된 복합합성수지 중공판(22)(23)은 자체적으로 갖는 수축 및 팽창현상을 방지하도록 대략 24시간 동안 25℃ ~ 30℃(바람직하게는 28℃)의 온도에 의해 양생되고, 소정 규격에 맞게 프레스 공정으로 절단된다(S106).
상기 복합합성수지 중공판(22)(23)의 프레스 공정이 완료된 후에는, 상기 제1 및 제2 복합합성수지 중공판(22)(23)의 일면에 유,무기질을 충진제로 사용하는 접착제를 1~3mm 도포하여 불연성 무기질 코팅층(30)을 형성한다(S108). 여기에서, 특히 견운모계의 무기질 성분이 포함되어 내화 성능이 강화되는 것이다. 본 발명에서는 유,무기질 접착제로서 나래텍의 NR100 접착제를 사용하였다. 상기 불연성 코팅층(30)에 사용되는 접착제는 시멘트, 질석, 모래, 규사, 석고 등의 무기질 및 아크릴, 초산비닐 등의 유기질의 혼합물로 이루어지며 상기 유,무기질 성분의 함량은 접착제의 중량비 대비 약 6:4로 하는 것이 바람직하다. 여기에서, 상기 유,무기질 접착제가 사용되어 코팅층이 형성되는 것은 시멘트 또는 몰타르와의 부착력을 향상시켜서 임의의 건설현장에서 사용된 복합단열판넬(20)이 파손되더라도 시멘트 또는 몰타르를 발라 상기 파손된 부분을 용이하게 보수하기 위함과 건축자재로서의 내화성능향상 및 표면강도 증대가 그 목적이다.
다음으로, 상기 복합합성수지 중공판(22)(23)의 타면에 아크릴수지 접착제를 1차 도포하고 수분과 열에 강한 우레탄계 및 에폭시계의 접착제를 도포하여 열경화성 접착제층(26)을 형성한다(S110). 이때, 상기 혼합원료의 중량비 대비 4~6％의 접착제가 도포되어 접착제층이 형성된다.
다음으로, 준불연 성능의 페놀폼계 단열재(24)의 양면에 이물질 부착 능력 증대를 위해 수용성 접착제가 도포된 후 난연 부직포(32)가 부착된다(S112).
상기 제1 및 제2 복합합성수지 중공판(22),(23)의 열경화성 접착제층(26) 사이에 상기 준불연 성능의 페놀폼계 단열재(24)가 접착된다(S114).
본 발명에서는 나래텍의 NR200, NR300 접착제가 사용되었다. 상기 열경화성 접착제는 무수축성이며 변형이 없어 콘크리트 벽체 또는 천정이 함유한 수분 성분이 침투하는 것을 방지할 수 있음은 물론 복합단열판넬(20)의 평판을 확보하는데 적합하다.
이와 같이 하여 상기 제1 및 제2 복합합성수지 중공판(22),(23)에 페놀폼계 단열재(24)가 부착된 후에, 접착력 증대를 위하여 건조실에서 24시간 동안 25℃ ~ 30℃(바람직하게는 28℃)의 온도로서 접착 건조가 행해진다(S116).
마지막으로, 상기 제1 및 제2 복합합성수지 중공판(22),(23)과 상기 페놀폼계 단열재(24) 부착시에 발생되는 접착 틈새를 접착제로서 밀봉한다(S118). 이때, 상기 접착제에 의한 밀봉공정은 부착력 증대와 함께 콘크리트의 수분침투를 예방하여 복합단열판넬(20)의 내구성을 향상시킬수 있게 된다.
이로써, 페놀폼계 단열재(24)의 양면에 각각 열경화성 접착제층(26)을 개재하여 상기 제1 및 제2 복합합성수지 중공판(22)(23)이 접착되고 또한 상기 제1 및 제2 복합합성수지 중공판(22)(23)의 타면에 불연성 무기질 코팅층(30)이 형성된 내화 성능이 향상된 결로방지용 복합단열판넬(20)이 완성되는 것이다.
한편, 본 발명은 상술한 특정의 바람직한 실시예에 한정되지 아니하며, 청구범위에서 청구하는 본 발명의 요지를 벗어남이 없이 당해 발명이 속하는 기술분야에서 통상의 지식을 가진 자라면 누구든지 다양한 변경 또는 변형 실시가 가능할 것이다.
10 : 단열판넬 12 : 합성수지 중공판
14 : 스티로폼
20 : 복합단열판넬 22, 23 : 복합합성수지 중공판
24 : 페놀폼계 단열재 26 : 열경화성 접착제층
28 : 통공 30 : 불연성 코팅층
32 : 난연 부직포
14 : 스티로폼
20 : 복합단열판넬 22, 23 : 복합합성수지 중공판
24 : 페놀폼계 단열재 26 : 열경화성 접착제층
28 : 통공 30 : 불연성 코팅층
32 : 난연 부직포
Claims (6)
- 건축물의 소정 부위에 부착되어 단열성능 향상과 결로현상 방지 및 곰팡이 발생을 방지토록 하는 결로방지용 복합단열판넬에 있어서,
난연 성능과 결로방지에 유용한 통기성을 제공하도록 다수개의 통공을 가지며 양면에 표면 개질 처리가 된 제1 및 제2 복합합성수지 중공판과,
상기 제1 및 제2 복합합성수지 중공판의 일면에 형성되는 불연성 코팅층과,
상기 제1 및 제2 복합합성수지 중공판의 타면에 형성되는 열경화성 접착제층과,
양면에 수용성 난연 접착제가 도포된 후 난연 부직포가 부착되며 상기 제1 및 제2 복합합성수지 중공판의 열경화성 접착제층과 접착되는 난연 2급의 준불연성 페놀폼계 단열재로 구성되며,
내화 성능이 난연 등급에서 난연 2급의 준불연 등급으로 대폭 강화된 것을 특징으로 하는
내화성능이 향상된 결로방지용 복합단열판넬. - 제 1항에 있어서,
상기 표면 개질 처리는 코로나 열처리 또는 부직포 열융착인 것을 특징으로 하는
내화성능이 향상된 결로방지용 복합단열판넬. - 제1항 또는 제2항에 있어서,
상기 불연성 코팅층은 견운모를 주성분으로 하는 무기질 코팅층인 것을 특징으로 하는
내화성능이 향상된 결로방지용 복합단열판넬. - 건축물의 소정 부위에 부착되어 단열성능 향상과 결로현상 방지 및 곰팡이 발생을 방지토록 하는 결로방지용 복합단열판넬의 제조방법에 있어서,
폴리프로필렌 수지와 탈크를 포함하여 이루어진 복합수지 원료에 난연제 및 UV 안정제를 첨가하고 혼합하여 융해하는 단계,
상기 혼합 융해 원료로 소정의 압출기에서 다수의 통공을 가지는 복합합성수지 중공판으로 제조하는 단계,
상기 복합합성수지 중공판의 양면을 표면 개질 처리하는 단계,
상기 표면 개질 처리된 복합합성수지 중공판을 25 ~ 30℃로 24시간 동안 양생하여 절단하는 단계,
상기 양생하여 절단된 제1 및 제2 복합합성수지 중공판의 일면에 유,무기질 접착제를 도포하여 내화 성능을 난연 등급에서 난연 2급의 준불연 등급으로 향상시킬 수 있는 불연성 무기질 코팅층을 형성하는 단계,
상기 일면에 불연성 무기질 코팅층이 형성된 제1 및 제2 복합합성수지 중공판의 타면에 열경화성 접착제를 도포하여 열경화성 접착제층을 형성하는 단계,
페놀폼계 단열재의 양면에 수용성 난연 접착제를 도포한 후 난연 부직포를 부착하는 단계,
상기 제1 및 제2 복합합성수지 중공판의 열경화성 접착제층 사이에 상기 페놀폼계 단열재를 접착하는 단계,
상기 접착된 복합단열판넬을 건조실에서 25 ~ 30℃로 24시간 동안 건조시키는 단계,
상기 건조된 복합단열판넬의 제1 및 제2 복합합성수지 중공판과 페놀폼계 단열재의 접착 틈새를 접착제로 밀봉하는 단계로 이루어지는 것을 특징으로 하는
내화성능이 향상된 결로방지용 복합단열판넬의 제조방법. - 제4항에 있어서,
상기 표면 개질 처리는 코로나 열처리 또는 및 부직포 열융착인 것을 특징으로 하는
내화성능이 향상된 결로방지용 복합단열판넬의 제조방법. - 제4항 또는 제5항에 있어서,
상기 불연성 코팅층은 견운모를 주성분으로 하는 무기질 코팅층인 것을 특징 으로 하는
내화성능이 향상된 결로방지용 복합단열판넬의 제조방법.