KR20190065709A - 원적외선과 음이온이 방출되는 건강벨트 - Google Patents
원적외선과 음이온이 방출되는 건강벨트 Download PDFInfo
- Publication number
- KR20190065709A KR20190065709A KR1020170165152A KR20170165152A KR20190065709A KR 20190065709 A KR20190065709 A KR 20190065709A KR 1020170165152 A KR1020170165152 A KR 1020170165152A KR 20170165152 A KR20170165152 A KR 20170165152A KR 20190065709 A KR20190065709 A KR 20190065709A
- Authority
- KR
- South Korea
- Prior art keywords
- belt
- infrared rays
- ceramic
- oxide
- wearer
- Prior art date
Abstract
본 발명은 원적외선과 음이온이 방출되는 건강벨트에 관한 것으로 그 구성의 특징으로서, 적어도 착용자의 허리를 감싸는 길이와 폭을 가지고, 양단을 여미어 밀착되게 착용되는 벨트; 상기 벨트의 내면에 착용자의 척추와 배꼽에 각각 밀착되어 원적외선과 음이온을 방출하는 세라믹; 및 상기 세라믹의 내면에 착용자의 신체에 따라 위치가 변경되도록 벨트로부터 탈·부착을 유도하는 조절수단;을 포함하여 이루어진다.
이에 따라 본 발명은, 원적외선과 음이온을 다량 방출하는 세라믹을 벨트에 부착시켜 착용만으로도 혈액순환과 신진대사를 촉진시키는 효과가 있다.
이에 따라 본 발명은, 원적외선과 음이온을 다량 방출하는 세라믹을 벨트에 부착시켜 착용만으로도 혈액순환과 신진대사를 촉진시키는 효과가 있다.
Description
본 발명은 건강의 증진을 도모하도록 허리에 착용하는 벨트에 관한 것으로, 보다 구체적으로는 원적외선과 음이온을 다량 방출하는 세라믹을 벨트에 부착시켜 착용만으로도 혈액순환과 신진대사를 촉진시키는 건강벨트에 관한 것이다.
벨트나 복대는 주로 착용자의 허리에 둘러메져 체형을 교정하는 목적으로 하는 압박용과 특정 질환이나 건강을 개선을 목적으로 하는 온열(찜질)용으로 구분된다.
여기서 온열용은 대표적으로 전기에너지로 발열하는 히터수단들이 내장된 벨트들이 있다. 하지만 전기에너지를 사용해야 되므로 이동이 불편할 뿐만 아니라 저온 화상 등의 부작용이 발생하는 문제점이 있다.
따라서 이를 개선하기 위한 일환으로, 대한민국 등록특허공보 제10-1436095호 (발명의 명칭: 그래핀 발열 복대), 대한민국 등록특허공보 제10-1556077호 (고안의 명칭: 발열기능이 있는 건강벨트)와 같이 피부와 접촉하는 부위에 토르마린 볼이 내장한 발열벨트를 제안하고 있다.
이러한 벨트는 토르마린 볼을 내장함으로써 전기에너지 없이도 착용자의 체온에 의한 지속적인 발열과 함께 원적외선과 음이온을 방출하여 혈액개선과 각종 통증완화 및 지방층을 감소시키는 효과를 제공하였다.
그러나 발열성 광물인 토르마린과 실리콘 및 고무 등을 혼합하여 제작한 토르마린 볼을 복대의 내측 표면에 형성하는 경우, 단순히 토르마린에 의한 발열 효과밖에 볼 수 없기 때문에 발열이 나타나는 시간이 오래 걸리는 것은 물론, 발열로 인한 인체에 유익한 파장이 피부 깊숙이 도달하지 못한 아쉬운 점이 있었다.
이에 따라 본 발명은 상기와 같은 종래의 문제점을 근본적으로 해결하기 위한 것으로서, 허리와 배꼽 주위를 원적외선과 음이온을 다량 방출하는 세라믹을 착용자의 피부와 직접적으로 접촉시킴으로서 원적외선과 음이온을 집중적으로 방사시켜 전반적인 혈액순환을 개선시켜 각종 질병을 예방하고 완화시킬 수 있는 원적외선과 음이온이 방출되는 건강벨트를 제공하려는데 그 목적이 있다.
이러한 목적을 달성하기 위해 본 발명은 원적외선과 음이온이 방출되는 건강벨트에 있어서: 적어도 착용자의 허리를 감싸는 길이와 폭을 가지고, 양단을 여미어 밀착되게 착용되는 벨트; 상기 벨트의 내면에 착용자의 척추와 배꼽에 각각 밀착되어 원적외선과 음이온을 방출하는 세라믹; 및 상기 세라믹의 내면에 착용자의 신체에 따라 위치가 변경되도록 벨트로부터 탈·부착을 유도하는 조절수단;을 포함하여 이루어지는 것을 특징으로 한다.
이때, 본 발명에 의한 상기 세라믹은 척추와 배꼽에 밀착 가능한 크기로 성형된 소지에 이산화규소(SiO2), 알루미나(Al2O3), 산화철(Fe2O3), 산화칼슘(CaO), 산화마그네슘(MgO), 산화나트륨(Na2O), 산화칼륨(K2O), 이산화티타늄(TiO2)으로 조성된 유약을 표면에 도포한 다음, 분당 50℃의 승온 속도로 850~1100℃로 소성한 것을 특징으로 한다.
또한, 본 발명에 의한 상기 유약은 65~80중량% 이산화규소(SiO2), 10~15중량% 알루미나(Al2O3), 3~6중량% 산화철(Fe2O3), 0.5~0.8중량% 산화칼슘(CaO), 1.2~1.5중량% 산화마그네슘(MgO), 1.0~1.5중량% 산화나트륨(Na2O), 2.0~3.0중량% 산화칼륨(K2O), 0.5~1.0중량% 이산화티타늄(TiO2)으로 조성된 혼합물을 볼밀로 30~120분간 교반하고, 교반된 혼합물을 75~90℃로 8~10시간 건조한 다음, 건조된 혼합물을 용융되게 열처리하고, 용융물을 급속 냉각한 덩어리를 알코올 용매 하에서 볼밀로 30~60분간 분쇄하고, 분쇄된 분말에 건조한 다음, 물과 1:1 중량비율로 혼합한 것을 특징으로 한다.
또한, 본 발명에 의한 상기 건조된 혼합물은 분당 10℃의 승온 속도로 900℃까지 승온한 이후에 30~60분간 1차 용융하고, 재차 1450℃까지 승온한 다음 1~2시간 2차 융융하는 열처리과정을 거친 것을 특징으로 한다.
또한, 본 발명에 의한 상기 조절수단은 벨트와 세라믹이 맞물리는 일면에 벨크로 또는 스냅단추 또는 접착제 중 어느 하나가 택일하여 구성된 것을 특징으로 한다.
한편, 이에 앞서 본 명세서 및 특허청구범위에 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정해서 해석되어서는 아니 되며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다. 따라서 본 명세서에 기재된 실시예와 도면에 도시된 구성은 본 발명의 가장 바람직한 일 실시예에 불과할 뿐이고, 본 발명의 기술적 사상을 모두 대변하는 것은 아니므로, 본 출원시점에 있어서 이들을 대체할 수 있는 다양한 균등물과 변형예들이 있을 수 있음을 이해하여야 한다.
이상의 구성 및 작용에서 설명한 바와 같이, 본 발명은 허리와 배꼽 주위를 원적외선과 음이온을 다량 방출하는 세라믹을 착용자의 피부와 직접적으로 접촉시킴으로서 원적외선과 음이온을 집중적으로 방사시켜 전반적인 혈액순환을 개선시켜 각종 질병을 예방하고 완화시킬 수 있는 효과를 제공한다.
도 1은 본 발명에 따른 건강벨트를 나타내는 사시도.
도 2 및 도 3은 본 발명에 따른 세라믹을 나타내는 사진
도 4는 본 발명에 따른 건강벨트를 나타내는 사진.
도 2 및 도 3은 본 발명에 따른 세라믹을 나타내는 사진
도 4는 본 발명에 따른 건강벨트를 나타내는 사진.
이하, 첨부된 도면을 참조하여 본 발명에 따른 바람직한 실시예를 상세하게 설명한다.
본 발명은 건강의 증진을 도모하도록 허리에 착용하는 벨트에 관련되며, 도 1 및 도 4처럼 벨트(10)와 세라믹(20) 그리고 조절수단(30)을 주요 구성으로 하는 원적외선과 음이온이 방출되는 건강벨트이다.
먼저, 본 발명에 따른 벨트(10)는 도 1처럼 적어도 착용자의 허리를 감싸는 길이와 폭을 가지고, 양단을 여미어 밀착되게 착용된다. 즉, 벨트(10)는 착용자의 허리에 둘러지는 내·외피와, 내·외피의 테두리에 감싸져 일체로 박음질되는 마감천과, 내·외피의 양단을 여미어 착용시키는 벨크로로 구성된다.
내피는 착용자의 피부에 밀착되는 것으로 자극을 주지 않은 부드러운 섬유재로 이루어지고, 외피는 외부로부터 단열성을 지닌 섬유재나 피혁재로 이루어진다. 이러한 내·외피는 허리를 충분히 감싸서 둘러지는 길이와 폭으로 재단된다. 재단된 내·외피의 일면에는 양단이 서로 맞물려 여미도록 벨크로가 각각 재봉된다.
이어서 본 발명에 따른 세라믹(20)은 도 1 및 도 4처럼 벨트(10)의 내면에 착용자의 척추와 배꼽에 각각 밀착되어 원적외선과 음이온을 방출한다. 이러한 세라믹(20)은 척추용과 배꼽용으로 구분될 수 있다.
척추용은 도 2처럼 척추와 함께 그 주변으로 원적외선과 음이온이 고르게 분산될 수 있도록 작은 단추형(21)을 복수로 배열된다. 배꼽용은 도 3처럼 배꼽을 중심으로 소정 반경에 원적외선과 음이온이 집중될 수 있도록 원반형(25)을 단일로 구성한다. 여기서 원반형(25)은 배꼽에 삽입 또는 밀착될 수 있도록 중앙에 돌기(25a)를 구성하는 것이 좋다.
이때, 세라믹(20)은 단추형(21)과 원반형(25)으로 성형된 소지에 유약을 표면에 도포한 다음, 분당 50℃의 승온 속도로 850~1100℃로 소성한 것이다. 여기서 유약은 65~80중량% 이산화규소(SiO2), 10~15중량% 알루미나(Al2O3), 3~6중량% 산화철(Fe2O3), 0.5~0.8중량% 산화칼슘(CaO), 1.2~1.5중량% 산화마그네슘(MgO), 1.0~1.5중량% 산화나트륨(Na2O), 2.0~3.0중량% 산화칼륨(K2O), 0.5~1.0중량% 이산화티타늄(TiO2)로 조성된 혼합물이다.
본 발명의 유약을 조성하는 성분 중 이산화규소는 원적외선과 음이온을 방출하는 특성을 가지도록 하는 역할을 한다. 이러한 이산화규소와 기타 첨가물은 적절한 조성비도 중요하지만, 소지의 표면에 균일하게 도포할 수 있게 물에 고르게 분산되는 콜로이드 상태로 전환시키는 것이 매우 중요하다
즉, 위에서 언급한 혼합비로 준비된 혼합물을 볼밀로 30~120분간 교반하여 균일하게 혼합한다. 그리고 교반된 혼합물을 오븐에 넣고, 75~90℃에서 8~10시간 건조한다. 이어서 건조된 혼합물을 분당 10℃의 승온 속도로 900℃까지 승온하고, 900℃를 유지한 상태에서 30~60분간 1차 용융한다.
그리고 분당 10℃의 승온 속도로 재차 1450℃까지 승온한 상태에서 1~2시간 2차 융융한다. 이어서 용융물을 물에 담금질로 급속 냉각하여 덩어리(프릿, Frit) 형태로 형성한다. 그리고 덩어리를 알코올 용매 하에서 볼밀로 30~60분간 분쇄하고, 자연 또는 열풍으로 건조한다. 마지막으로 건조된 분말을 물과 1:1 중량비율로 혼합하면, 소지에 도포할 유약이 완성되는 것이다.
마지막으로 본 발명에 따른 조절수단(30)은 도 1처럼 세라믹(20)의 내면에 착용자의 신체에 따라 위치가 변경되도록 벨트(10)로부터 탈·부착을 유도한다. 즉, 조절수단(30)은 벨트(10)와 세라믹(20)이 맞물리는 일면에 벨크로 또는 스냅단추 또는 접착제 중 어느 하나가 택일하여 구성된다. 따라서 착용자의 허리 사이즈나 특정 질환에 따라 세라믹(20)을 원하는 부위에 위치할 수 있도록 자유롭게 조절할 수가 있다.
이하, 구체적인 실시예를 살펴보고 본 발명의 유약이 가진 실질적인 효과가 유효함을 알아보고자 한다.
<실험예>
본 실험은 유약을 조성하는 혼합비율에 따라 원적외선의 방사율 정도를 알아보기 위해 아래 표 1과 같은 시료별 원적외선 방사율과 방사에너지를 측정하였다. 그리고 측정된 방사율 중 가장 높은 실시예를 지름50mm, 두께5mm 석고 소지에 도포하여 가스가마에서 온도별 소성한 다음, 원적외선 방사율과 방사에너지를 측정하였다.
<시료제작>
| SiO2 | Al2O3 | Fe2O3 | CaO | MgO | Na2O | K2O | TiO2 | |
| 실시예1 | 61.26 | 22.90 | 12.40 | 0.05 | 0.61 | 0.43 | 0.94 | 1.41 |
| 실시예2 | 66.26 | 18.60 | 8.31 | 0.13 | 2.00 | 0.53 | 3.44 | 0.73 |
| 실시예3 | 74.22 | 15.70 | 5.29 | 0.20 | 0.66 | 0.61 | 2.73 | 0.59 |
| 실시예4 | 71.49 | 18.50 | 4.69 | 0.10 | 0.55 | 0.51 | 3.75 | 0.41 |
| 실시예5 | 65.44 | 20.60 | 9.78 | 0.10 | 0.79 | 0.54 | 1.76 | 0.99 |
| 실시예6 | 70.00 | 16.50 | 4.82 | 1.06 | 1.26 | 2.30 | 3.56 | 0.50 |
| 실시예7 | 69.37 | 16.80 | 8.15 | 0.16 | 1.56 | 0.58 | 2.58 | 0.80 |
| 실시예8 | 59.56 | 31.70 | 5.93 | 0.22 | 0.56 | 0.59 | 0.86 | 0.58 |
| 실시예9 | 64.34 | 25.30 | 14.70 | 0.59 | 1.17 | 0.56 | 3.71 | 2.36 |
| 실시예10 | 67.97 | 18.50 | 8.14 | 0.10 | 1.17 | 0.64 | 2.68 | 0.80 |
| 실시예11 | 72.80 | 14.60 | 5.68 | 0.68 | 1.48 | 1.39 | 2.67 | 0.70 |
(단위: 중량%)
준비된 혼합물을 볼밀로 60분간 교반하고, 교반된 혼합물을 80℃에서 10시간 건조하였다. 그리고 건조된 혼합물을 분당 10℃의 승온 속도로 900℃까지 승온하고, 900℃를 유지한 상태에서 60분간 용융한 다음, 분당 10℃의 승온 속도로 재차 1450℃까지 승온한 상태에서 2시간 융융하였다.
이어서 용융물을 물에 담금질로 급속 냉각하여 덩어리(프릿, Frit) 형태로 형성하고, 형성된 덩어리를 알코올 용매 하에서 볼밀로 30분간 분쇄하고, 자연 또는 열풍으로 건조하였다. 마지막으로 건조된 분말을 물과 1:1 중량비율로 혼합한 유약을 실시예별로 완성하였다.
<실험결과1>
| Emission (5~20㎛) |
Emission energy (W/㎡·㎛, ℃) |
|
| 실시예1 | 0.915 | 3.53×102 |
| 실시예2 | 0.912 | 3.52×102 |
| 실시예3 | 0.911 | 3.51×102 |
| 실시예4 | 0.916 | 3.53×102 |
| 실시예5 | 0.919 | 3.54×102 |
| 실시예6 | 0.916 | 3.53×102 |
| 실시예7 | 0.917 | 3.54×102 |
| 실시예8 | 0.919 | 3.54×102 |
| 실시예9 | 0.917 | 3.54×102 |
| 실시예10 | 0.920 | 3.55×102 |
| 실시예11 | 0.917 | 3.54×102 |
실시예별로 시료를 측정한 결과, 전체적으로 원적외선 방사율이 0.916으로 매우 높은 편이었으며, 그 중에서 실시예8이 0.920으로 가장 높은 방사율로 측정되었고, 실시예3이 0.911로 가장 낮은 방사율로 측정되었다.
<실험결과2>
| Emission (5~20㎛) |
Emission energy (W/㎡·㎛, ℃) |
|
| 1230℃ | 0.920 | 3.55×102 |
| 1250℃ | 0.917 | 3.54×102 |
| 1270℃ | 0.914 | 3.52×102 |
원적외선 방사율이 가장 높은 실시예8을 온도별로 소성하여 다시 측정한 결과, 1230℃에서 소성한 소지에서 0.920으로 시료와 동일한 원적외선 방사율이 측정되었다.
본 발명은 기재된 실시예에 한정되는 것은 아니고, 본 발명의 사상 및 범위를 벗어나지 않고 다양하게 수정 및 변형할 수 있음은 이 기술의 분야에서 통상의 지식을 가진 자에게 자명하다. 따라서 그러한 변형예 또는 수정예들은 본 발명의 특허청구범위에 속한다 해야 할 것이다.
10: 벨트
20: 세라믹
21: 단추형
25: 원반형
25a: 돌기
30: 조절수단
20: 세라믹
21: 단추형
25: 원반형
25a: 돌기
30: 조절수단
Claims (5)
- 원적외선과 음이온이 방출되는 건강벨트에 있어서:
적어도 착용자의 허리를 감싸는 길이와 폭을 가지고, 양단을 여미어 밀착되게 착용되는 벨트;
상기 벨트의 내면에 착용자의 척추와 배꼽에 각각 밀착되어 원적외선과 음이온을 방출하는 세라믹; 및
상기 세라믹의 내면에 착용자의 신체에 따라 위치가 변경되도록 벨트로부터 탈·부착을 유도하는 조절수단;을 포함하여 이루어지는 것을 특징으로 하는 원적외선과 음이온이 방출되는 건강벨트. - 제1항에 있어서,
상기 세라믹은 척추와 배꼽에 밀착 가능한 크기로 성형된 소지에 이산화규소(SiO2), 알루미나(Al2O3), 산화철(Fe2O3), 산화칼슘(CaO), 산화마그네슘(MgO), 산화나트륨(Na2O), 산화칼륨(K2O), 이산화티타늄(TiO2)으로 조성된 유약을 표면에 도포한 다음, 분당 50℃의 승온 속도로 850~1100℃로 소성한 것을 특징으로 하는 원적외선과 음이온이 방출되는 건강벨트. - 제2항에 있어서,
상기 유약은 65~80중량% 이산화규소(SiO2), 10~15중량% 알루미나(Al2O3), 3~6중량% 산화철(Fe2O3), 0.5~0.8중량% 산화칼슘(CaO), 1.2~1.5중량% 산화마그네슘(MgO), 1.0~1.5중량% 산화나트륨(Na2O), 2.0~3.0중량% 산화칼륨(K2O), 0.5~1.0중량% 이산화티타늄(TiO2)으로 조성된 혼합물을 볼밀로 30~120분간 교반하고, 교반된 혼합물을 75~90℃로 8~10시간 건조한 다음, 건조된 혼합물을 용융되게 열처리하고, 용융물을 급속 냉각한 덩어리를 알코올 용매 하에서 볼밀로 30~60분간 분쇄하고, 분쇄된 분말에 건조한 다음, 물과 1:1 중량비율로 혼합한 것을 특징으로 하는 원적외선과 음이온이 방출되는 건강벨트. - 제3항에 있어서,
상기 건조된 혼합물은 분당 10℃의 승온 속도로 900℃까지 승온한 이후에 30~60분간 1차 용융하고, 재차 1450℃까지 승온한 다음 1~2시간 2차 융융하는 열처리과정을 거친 것을 특징으로 하는 원적외선과 음이온이 방출되는 건강벨트. - 제1항에 있어서,
상기 조절수단은 벨트와 세라믹이 맞물리는 일면에 벨크로 또는 스냅단추 또는 접착제 중 어느 하나가 택일하여 구성된 것을 특징으로 하는 원적외선과 음이온이 방출되는 건강벨트.