KR20160077348A - Skin care sheet using water soluble microfiber coated with fuctional material and method of manufacturing the same - Google Patents
Skin care sheet using water soluble microfiber coated with fuctional material and method of manufacturing the sameInfo
- Publication number
- KR20160077348A KR20160077348A KR1020140186310A KR20140186310A KR20160077348A KR 20160077348 A KR20160077348 A KR 20160077348A KR 1020140186310 A KR1020140186310 A KR 1020140186310A KR 20140186310 A KR20140186310 A KR 20140186310A KR 20160077348 A KR20160077348 A KR 20160077348A
- Authority
- KR
- South Korea
- Prior art keywords
- microfibers
- water
- sheet
- skin care
- functional material
- Prior art date
Abstract
Description
본 발명은 피부미용 시트에 관한 것으로, 특히 수용성 마이크로 섬유 표면에 피부 미용 등에 효과가 있는 기능성 물질(이하, "기능성 물질"이라 한다)이 코팅된 미용시트 및 그 제조방법에 관한 것이다. More particularly, the present invention relates to a beauty sheet coated with a functional material (hereinafter referred to as "functional material"
종래의 미용시트는 아래 특허문헌 1에 개시되어 알려져 있듯이, 직포나 부직포상에 기능성 물질인 천연추출물, 단백질, 비타민 등의 피부 활성에 도움이 되는 기능성 물질을 함유시켜 주름개선, 미백, 보습효과, 피부 탄력 부여 등의 기능을 가지도록 제조되었다.As known in the following patent document 1, a conventional beauty sheet contains a functional substance which helps skin activity such as a natural extract, a protein, and a vitamin, which is a functional substance, on a woven fabric or a nonwoven fabric to improve wrinkles, whitening, Skin elasticity, and so on.
이들 종래의 미용시트는 피부에 대한 부착성이 낮으며 미용액이 공기에 노출됨으로 인해 야기되는 미용성분들의 변성을 피하기 어렵고 초기에 너무 고농도의 미용성분이 피부와 접촉함으로 인한 피부 자극 발생 소지가 높다는 문제점이 있었다.These conventional beauty sheets have low adhesiveness to the skin and it is difficult to avoid the denaturation of the cosmetic ingredients caused by the exposure of the cosmetic liquid to the air and it is difficult to prevent skin irritation due to too high concentration of cosmetic ingredients .
이를 개선하기 위해 아크릴폴리머, 젤라틴, 무수말레인산 등을 응용한 하이드로젤 매트릭스 점착시트형 제제가 제품화되어 있으나 점착층 형성에 문제가 있어 이를 보완하는 기술 개발이 이루어지고 있다. In order to improve this, a hydrogel matrix adhesive sheet-type preparation using acryl polymer, gelatin, maleic anhydride or the like is commercialized, but there is a problem in formation of an adhesive layer, and technology for complementing the development is being developed.
본 발명은 약물전달체계(Drug delivery system)을 응용한 미용시트를 개발하고자 하는 목적으로 피부 친화 물질로서 수용성 고분자를 채용하여 마이크로 섬유화하고 기능성 물질을 상기 마이크로 섬유에 스며들게 하여 이를 건조된 시트상으로 미용시트를 제조하고 피부 부착전에 수분 미스트를 스프레이하여 미용시트의 점착력을 부여하면서 섬유 표면의 기능성 물질이 피부표면에 직접 접촉하여 흡수되도록 구성한 미용시트를 제공하고자 한다.The present invention aims to develop a beauty sheet using a drug delivery system. The purpose of the present invention is to develop microfibers by adopting a water-soluble polymer as a skin-friendly substance, to impregnate functional materials into the microfibers, The present invention provides a cosmetic sheet comprising a sheet and spraying water mist before adhering the skin, so that the functional material on the surface of the fiber is brought into direct contact with the surface of the skin while giving the adhesive force of the hair sheet.
또한 본 발명은 상기한 미용시트를 제조하는 방법을 제공함에 다른 목적이 있다. Another object of the present invention is to provide a method of manufacturing the above-mentioned beauty sheet.
상기 목적 달성을 위해 본 발명의 미용시트는 수용성 고분자 마이크로 섬유에 기능성 물질이 코팅된 것으로 이루어져 있다. 상기 마이크로 섬유는 섬유의 평균직경이 수 마이크로미터로 형성되며 10~30gsm의 평량을 가지고, 상기 기능성 물질은 마이크로 섬유 중량대비 1~10%로 코팅된 것을 특징으로 한다. In order to achieve the above object, the beauty sheet of the present invention comprises a water-soluble polymer micro fiber coated with a functional material. The microfibers have an average diameter of fibers of several micrometers, a basis weight of 10 to 30 gsm, and the functional material is coated at 1 to 10% of the weight of microfibers.
본 발명의 미용시트를 제조하는 방법으로, 수용성 고분자를 물에 녹여 전기방사하여 마이크로 섬유를 형성하는 전기방사단계; 기능성 물질인 미용물질을 소정의 용제에 녹여 스프레이 또는 함침하여 건조하는 기능성 물질 코팅단계; 소정의 형상으로 커팅하는 미용시트 형성단계를 포함하는 것을 특징으로 하는 미용시트 제조방법을 제공한다. A method for producing a hairdressing sheet of the present invention includes: an electrospinning step of dissolving a water-soluble polymer in water and electrospinning to form microfibers; A functional material coating step of dissolving a cosmetic material, which is a functional material, in a predetermined solvent, followed by spraying or impregnation; And a step of forming a beauty sheet for cutting into a predetermined shape.
본 발명의 미용시트는 피부에 유효한 기능성 물질인 미용물질을 생체 친화형 물질인 수용성 고분자 마이크로 섬유에 코팅하여 종래의 부직포에 기능성 물질을 도포하여 발생된 문제점과 하이드로젤 매트릭스 타입의 미용 패치의 점착력 부여 문제점을 동시에 해결하고 건조 상태의 시트로 제조되어 변질없이 장시간 보존가능하여 장시간 유통 기한의 제한이 없어지며 피부 부착 과정의 애로사항까지 모두 해결한 미용시트를 제공할 수 있다. The beauty sheet of the present invention is a beauty sheet comprising a water-soluble polymer micro-fiber, which is a biocompatible material, which is a functional material effective on the skin, which is coated on the water-soluble polymer micro- And can be stored for a long time without deterioration. Thus, there is no limitation in the expiration date for a long time, and a beauty sheet can be provided which solves all the difficulties of the skin attachment process.
이하, 실시예를 통해 본 발명을 상세히 설명한다. Hereinafter, the present invention will be described in detail with reference to Examples.
일본 쿠라레이사의 PVA를 탈이온수에 28wt%로 가온하면서 4시간이상 교반하여 완전히 녹인후, 이 PVA 수용액을 전기방사 노즐에 통해 전기방사하여 평균직경 2마이크로미터, 10gsm으로 PVA 마이크로 섬유를 형성하였다. 이때 20gsm의 PP 스펀본드를 이형지로 사용하였고 전기방사 조건은 인가전압은 2만볼트, 노즐과 컬렉터와의 거리는 30cm로 하였다.PVA microfibers having an average diameter of 2 micrometers and 10 gsm were formed by dissolving the PVA of KURARAY CO., LTD. In deionized water to 28 wt% with stirring for 4 hours or more and completely dissolving the PVA aqueous solution through an electrospinning nozzle. At this time, a 20 gsm PP spun bond was used as a release paper. The electrospinning conditions were 20,000 volts applied voltage, and the distance between the nozzle and the collector was 30 cm.
에탄올에 기능성 물질인 미용물질로 수용성 콜라겐 10wt%, 패각소성물질 미량 녹여 PVA 마이크로 섬유에 스프레이 코팅한 후 열풍건조하였다. 고형분의 코팅량은 PVA 마이크로 섬유 중량대비 5wt%가 되도록 스프레이량을 조절하였다. 이후 소정 형상으로 커팅하여 미용시트를 제조하였다. 이때 PET투명필름을 같이 놓고 커팅하여 이형지인 PP스펀본드를 제거하였다.10% by weight of water soluble collagen and a small amount of firing agent were dissolved in ethanol as a cosmetic substance, which was a functional substance, and spray-coated on PVA microfibers, followed by hot air drying. The spray amount was adjusted so that the coating amount of the solid content was 5 wt% based on the weight of the PVA microfibers. Thereafter, the sheet was cut into a predetermined shape to produce a beauty sheet. At this time, the PET transparent film was put together and cut to remove the release paper, PP spun bond.
PVA 마이크로 섬유의 평량을 20gsm으로 한 것 이외에는 실시예 1과 동일하게 미용시트를 제조하였다.A cosmetic sheet was prepared in the same manner as in Example 1 except that the basis weight of the PVA microfibers was 20 gsm.
PVA 마이크로 섬유의 평량을 30gsm으로 한 것 이외에는 실시예 1과 동일하게 미용시트를 제조하였다.
A cosmetic sheet was prepared in the same manner as in Example 1 except that the basis weight of the PVA microfibers was 30 gsm.
실시예 1 내지 실시예3의 PET투명필름 위의 미용시트에 수분 미스트를 적량 스프레이하면 수초 이내에 투명하게 변하면서 점착력을 갖게 되며 이를 원하는 피부 부위에 접착하여 시간 경과에 따른 변화를 관찰한 결과 10gsm의 경우 건조시간이 30gsm보다 짧지만 10분 내지 30분의 시간 경과 이후에 하얀색 필름상으로 피막이 형성되었다.When spraying a wet mist on the PET sheet of the PET transparent films of Examples 1 to 3, it turned transparent within a few seconds and adhered to the desired skin region and observed changes with time. As a result, The drying time was shorter than 30 gsm, but a film was formed on the white film after a lapse of 10 to 30 minutes.
이 피막은 손으로 집어 제거하거나 물로 세척할 경우 깨끗하게 제거할 수 있었다. 결국 약물전달체계를 미용시트에 적용하고자 하는 본 발명의 목적에 부합하는 미용시트를 제조할 수 있었다. This coating could be cleanly removed by hand picking or washing with water. As a result, a beauty sheet conforming to the object of the present invention for applying a drug delivery system to a beauty sheet could be produced.
Claims (9)
상기 마이크로 섬유는 피부 친화성 물질의 수용성 고분자를 전기방사하여 얻어진 것을 특징으로 하는 피부미용시트.The method according to claim 1,
Wherein the microfibers are obtained by electrospinning a water-soluble polymer of a skin-affinity substance.
상기 기능성 물질은, 수용성 콜라겐, 패각소성 미세분말, 키토산, 토코페롤, 자일리톨 및 글리세린을 포함한 군에서 선택된 하나 또는 하나 이상의 혼합물인 것을 특징으로 하는 피부미용 시트.The method according to claim 1,
Wherein said functional material is one or a mixture of at least one selected from the group consisting of water-soluble collagen, fine-shell calcined powder, chitosan, tocopherol, xylitol and glycerin.
상기 수용성 고분자는 폴리에틸렌 옥사이드(PEO: poly(ethylene), 폴리비닐피롤리돈(PVP: polyvinylpyrrolidone), CMC, PAA(Polyacrylic acid), 전분 및 히알루론산을 포함한 군에서 선택된 하나 또는 하나 이상의 혼합물을 포함한 것을 특징으로 하는 피부미용 시트. The method according to claim 1,
The water-soluble polymer includes one or a mixture of at least one selected from the group consisting of polyethylene oxide (PEO), polyvinylpyrrolidone (PVP), CMC, polyacrylic acid (PAA), starch and hyaluronic acid Features a skin care sheet.
상기 마이크로 섬유는 10~30 g/㎡ 평량을 가지고, 상기 기능성 물질은 마이크로 섬유의 중량에 대하여 1~10중량%로 코팅되는 것을 특징으로 하는 피부미용 시트. The method according to claim 1,
Wherein the microfibers have a basis weight of 10 to 30 g / m < 2 >, and the functional material is coated at 1 to 10 wt% with respect to the weight of the microfibers.
수용성 고분자를 물에 녹여 전기방사하여 마이크로 섬유를 형성하는 마이크로섬유 형성단계; 및 피부미용에 효능이 있는 기능성 물질을 소정의 용제에 녹인 기능성 물질 용액을 마이크로 섬유에 스프레이 또는 함침하여 건조하는 기능성 물질 코팅단계;를 포함한 것을 특징으로 피부미용 시트의 제조방법. A method for manufacturing a skin-beauty sheet using a water-soluble polymer,
A microfiber forming step of dissolving the water-soluble polymer in water and electrospinning to form microfibers; And a functional material coating step of spraying or impregnating microfibers with a functional material solution dissolved in a predetermined solvent, which is effective for skin care, and drying the microfibers.
상기 수용성 고분자는 폴리에틸렌 옥사이드(PEO: poly(ethylene), 폴리비닐피롤리돈(PVP: polyvinylpyrrolidone), CMC, PAA(Polyacrylic acid), 전분 및 히알루론산을 포함한 군에서 선택된 하나 또는 하나 이상의 혼합물인 것을 특징으로 하는 피부미용 시트의 제조방법.The method according to claim 6,
The water-soluble polymer is one or a mixture of one or more selected from the group consisting of polyethylene oxide (PEO), polyvinylpyrrolidone (PVP), CMC, PAA (polyacrylic acid), starch and hyaluronic acid By weight or less.
상기 기능성 물질은, 수용성 콜라겐, 패각소성 미세분말, 키토산, 토코페롤, 자일리톨 및 글리세린을 포함한 군에서 선택된 하나 또는 하나 이상의 혼합물인 것을 특징으로 하는 피부미용 시트의 제조방법. The method according to claim 6,
Wherein the functional material is one or a mixture of at least one member selected from the group consisting of water-soluble collagen, fine-shell calcined powder, chitosan, tocopherol, xylitol and glycerin.
상기 마이크로 섬유는 10~30 g/㎡ 평량을 가지고, 상기 기능성 물질은 마이크로 섬유의 중량에 대하여 1~10중량%로 코팅하는 것을 특징으로 하는 피부미용 시트의 제조방법. 8. The method of claim 7,
Wherein the microfibers have a basis weight of 10 to 30 g / m < 2 > and the functional material is coated at 1 to 10 wt% with respect to the weight of the microfibers.