KR102608317B1 - Self-melting wet beauty sheet and its manufacturing method - Google Patents

Self-melting wet beauty sheet and its manufacturing method Download PDF

Info

Publication number
KR102608317B1
KR102608317B1 KR1020230027068A KR20230027068A KR102608317B1 KR 102608317 B1 KR102608317 B1 KR 102608317B1 KR 1020230027068 A KR1020230027068 A KR 1020230027068A KR 20230027068 A KR20230027068 A KR 20230027068A KR 102608317 B1 KR102608317 B1 KR 102608317B1
Authority
KR
South Korea
Prior art keywords
skin
beauty
weight
serum
water
Prior art date
Application number
KR1020230027068A
Other languages
Korean (ko)
Inventor
이병수
Original Assignee
이병수
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이병수 filed Critical 이병수
Priority to KR1020230027068A priority Critical patent/KR102608317B1/en
Application granted granted Critical
Publication of KR102608317B1 publication Critical patent/KR102608317B1/en

Abstract

본 발명은 피부미용 기능을 갖는 수용성 유효성분, 막 형성 수용성 고분자 및 가교제를 용매에 용해한 방사용액의 전기방사에 의해 상호 가교결합(Cross-linking)된 나노멤브레인에 정제수를 함유하지 않은 세럼을 함침하여 미용시트를 제조하되, 상기 세럼은 글리세롤(Glycerol)과 부틸렌글라이콜(Butylene Glycol) 중 하나 이상의 성분이 혼합되고, 세럼이 함침된 미용시트를 피부에 부착시 세럼은 공기 중의 수분과 피부에 존재하는 수분을 흡수하여 미용시트에 공급함으로써 미용시트가 스스로 용융되는 것을 특징으로 하는 자가 용융 습식 미용시트에 관한 것이다.
본 발명은 습식 미용시트의 글리세롤이나 부틸렌글라이콜이 공기 중에서 흡수한 수분과 피부에서 흡수한 수분을 미용시트에 공급하여 미용성분의 가교결합(Cross-linking)이 끊어지면서 스스로 용융된 후 서서히 피부에 흡수되도록 함으로써 기존 미용시트를 사용할 때의 불편함을 개선하고, 빠른 건조로 인해 미용효과가 감소하는 문제를 해결하였다.
The present invention involves impregnating a nanomembrane cross-linked with a serum that does not contain purified water by electrospinning a spinning solution containing a water-soluble active ingredient with a skin-beautifying function, a film-forming water-soluble polymer, and a cross-linking agent dissolved in a solvent. A beauty sheet is manufactured, wherein the serum is a mixture of one or more ingredients of glycerol and butylene glycol, and when the beauty sheet impregnated with the serum is attached to the skin, the serum is present in moisture in the air and on the skin. It relates to a self-melting wet beauty sheet, characterized in that the beauty sheet melts itself by absorbing moisture and supplying it to the beauty sheet.
In the present invention, the glycerol or butylene glycol of the wet beauty sheet supplies moisture absorbed from the air and moisture absorbed from the skin to the beauty sheet, so that the cross-linking of the beauty ingredients is broken and melts on its own, then gradually melts into the skin. By allowing it to be absorbed into the skin, the inconvenience when using existing beauty sheets was improved and the problem of reduced beauty effect due to rapid drying was solved.

Description

자가 용융 습식 미용시트 및 그 제조방법{SELF-MELTING WET BEAUTY SHEET AND ITS MANUFACTURING METHOD} Self-melting wet beauty sheet and its manufacturing method {SELF-MELTING WET BEAUTY SHEET AND ITS MANUFACTURING METHOD}

본 발명은 자가 용융 습식 미용시트 및 그 제조방법에 관한 것으로, 보다 상세하게는 수용성 미용성분의 시트를 피부에 부착하기만 하면 공기 중에서 자연히 흡수된 수분과 피부에 존재하는 수분만으로 미용시트의 가교결합(Cross-linking)이 끊어지면서 미용성분이 피부에 흡수되는 자가 용융 습식 미용시트 및 그 제조방법에 관한 것이다.The present invention relates to a self-melting wet beauty sheet and a method of manufacturing the same. More specifically, by simply attaching a sheet of water-soluble beauty ingredients to the skin, the beauty sheet is cross-linked using only the moisture naturally absorbed from the air and the moisture present in the skin. This relates to a self-melting wet beauty sheet in which beauty ingredients are absorbed into the skin by breaking the cross-linking, and a method of manufacturing the same.

종래의 수용성 미용시트 제품은 대부분이 건조시트로 미용시트를 녹여 피부 내 흡수를 촉진시키기 위해서는 미스트나 세럼, 크림 등 수분이 함유된 액상으로 건조시트를 용해시키는 방식을 사용하였다.Most of the conventional water-soluble beauty sheet products are dry sheets, and in order to promote absorption into the skin, the dry sheet is dissolved in a moisture-containing liquid such as mist, serum, or cream.

최근 콜라겐이 다량 함유된 수용성 미용시트의 예를 들어 보더라도 건조 상태의 콜라겐 시트를 피부에 부착 후 미스트를 분사하여 시트를 녹여 사용하는 방식의 제품이다.Even looking at the recent example of a water-soluble beauty sheet containing a large amount of collagen, it is a product that attaches a dry collagen sheet to the skin and then sprays mist to melt the sheet.

그러나 이러한 방식은 사용 방법에 익숙하지 않은 소비자들의 경우 얇고 습기에 취약한 수용성 미용시트의 특성으로 사용하기도 전에 손의 습기로 인해 일부가 녹거나, 얇은 시트의 경우 자칫하면 찢어지는 등 제품 취급이 어려워 제대로 사용을 하지 못하고 버려지는 경우가 많으며, 소비자의 제품에 대한 불만으로 반품이 빈번하게 발생하는 문제가 있다.However, for consumers who are not familiar with how to use this method, due to the characteristics of water-soluble beauty sheets that are thin and vulnerable to moisture, it is difficult to properly handle the product, such as some melting due to the moisture of the hands before use, or in the case of thin sheets, tearing. There are many cases where products are thrown away without being used, and there is a problem of frequent returns due to consumer dissatisfaction with the product.

또한 수용성 미용성분 시트의 특성 상 미스트나 세럼 등의 액상에 의해 녹는 반응속도가 너무 빠르고 다시 급속하게 건조하게 되므로 녹은 미용성분이 피부에 접촉한 후 수분이 증발하면 피부가 건조해지고 이에 따라 미용효과를 기대할 수가 없어 추가로 미스트를 분사하거나 별도의 보습제를 덧발라야 하는 등 사용이 불편하고 비효율적이었다.In addition, due to the nature of the water-soluble beauty ingredient sheet, the reaction speed of dissolution in liquids such as mist or serum is too fast and it dries quickly again. Therefore, when the moisture evaporates after the dissolved beauty ingredient comes into contact with the skin, the skin becomes dry and the beauty effect is lost. It was inconvenient and inefficient to use, as I had to spray additional mist or apply a separate moisturizer because I couldn't get my hopes up.

대한민국 등록특허 제10-1454421호 ‘자가 용융형 나노섬유로 구성된 미용시트 및 그 제조방법’은 이와 같은 종래의 방식에 의한 미용시트로서, 건조 상태의 미용시트를 피부에 부착 후 미스트를 분사하여 수분을 공급하거나, 세안 후 미용시트를 피부에 부착하여 사용하는 방식이기 때문에 수분에 의해 미용시트가 녹는 반응속도가 너무 빨라 미용성분이 피부에 충분히 흡수되기도 전에 증발해 버리는 문제가 있고, 세안을 하거나 미스트의 분사가 필요하기 때문에 언제 어디서나 간편하게 사용할 수 있는 제품이 아니다.Republic of Korea Patent No. 10-1454421, 'Beauty sheet composed of self-melting nanofibers and its manufacturing method' is a beauty sheet using this conventional method. After attaching a dry beauty sheet to the skin, mist is sprayed to moisturize the skin. Since this method is used by supplying or attaching a beauty sheet to the skin after washing the face, the reaction speed of the beauty sheet melting due to moisture is too fast, so there is a problem that the beauty ingredients evaporate before they are fully absorbed into the skin. Because it requires spraying, it is not a product that can be easily used anytime, anywhere.

대한민국 등록특허 제10-1440318호 ‘피부용 패치 조성물 및 이를 이용한 피부용 패치의 제조방법’은 패치가 수분을 포함하기 때문에 패치를 피부에 부착할 때 끈적이고 손에 달라붙게 되어 패치를 피부에 제대로 붙이기 쉽지 않은 문제가 있다.Republic of Korea Patent No. 10-1440318 'Skin patch composition and method of manufacturing a skin patch using the same' states that since the patch contains moisture, it becomes sticky and sticks to the hand when attached to the skin, making it difficult to properly attach the patch to the skin. There is a problem.

대한민국 공개특허 제10-2011-0074081호 ‘피부질환 개선 또는 피부미용 조성물 및 이의 제조방법’은 에탄올, 정제수 등 수용성 고분자 물질을 용해시킬 수 있는 용제를 별도로 첨가하여 조성물을 제조하는 것으로서, 피부질환 개선 및 피부 미용 기능을 갖는 활성 성분을 투입하고, 활성 성분의 용해도에 따라 유화제 및 첨가제를 첨가하기 때문에 제조가 복잡하며, 보관이 까다로운 문제가 있다.Republic of Korea Patent Publication No. 10-2011-0074081, 'Skin disease improvement or skin care composition and method for manufacturing the same' is to manufacture a composition by separately adding a solvent capable of dissolving water-soluble polymer substances such as ethanol and purified water, thereby improving skin disease. And since active ingredients with skin beauty functions are added and emulsifiers and additives are added depending on the solubility of the active ingredients, manufacturing is complicated and storage is difficult.

대한민국 등록특허 제10-1454421호Republic of Korea Patent No. 10-1454421 대한민국 등록특허 제10-1440318호Republic of Korea Patent No. 10-1440318 대한민국 공개특허 제10-2011-0074081호Republic of Korea Patent Publication No. 10-2011-0074081

본 발명은 상기한 바와 같은 문제점을 해결하기 위한 것으로, 수용성 미용시트에 정제수가 함유되지 않은 세럼을 함침하여 제조한 습식시트로 초기 부착단계에서는 시트형태이나 시간이 지남에 따라 세럼이 함유한 글리세롤이나 부틸렌글라이콜 등 공기 중 수분 흡수 특성을 갖는 미용성분이 공기 중에서 흡수한 수분과 피부에서 흡수한 수분을 미용시트에 공급하여 수용성 성분의 가교결합(Cross-linking)이 풀어짐에 따라 미용성분이 피부에 서서히 흡수되어 사용상의 불편함과 빠른 건조로 인한 미용효과의 감소 등 종래 건조시트의 비효율성을 해결할 수 있는 자가 용융 습식 미용시트 및 그 제조방법을 제공하는 것을 목적으로 한다.The present invention is intended to solve the problems described above, and is a wet sheet manufactured by impregnating a water-soluble beauty sheet with a serum that does not contain purified water. It is in the form of a sheet at the initial attachment stage, but over time, the glycerol or serum contained therein Beauty ingredients that have the property of absorbing moisture from the air, such as butylene glycol, supply the moisture absorbed from the air and the moisture absorbed from the skin to the beauty sheet, and as the cross-linking of the water-soluble ingredients is broken, the beauty ingredients are absorbed into the skin. The purpose is to provide a self-melting wet beauty sheet and a method of manufacturing the same, which can solve the inefficiencies of conventional dry sheets, such as inconvenience in use and reduction of beauty effect due to rapid drying by slowly being absorbed into the body.

상기한 바와 같은 목적을 달성하기 위하여 본 발명에 따른 자가 용융 습식 미용시트는 피부미용 기능을 갖는 수용성 유효성분, 막 형성 수용성 고분자 및 가교제를 용매에 용해한 방사용액의 전기방사에 의해 상호 가교결합(Cross-linking)된 나노멤브레인에 정제수를 함유하지 않은 세럼을 함침하여 미용시트를 제조하되, 세럼은 글리세롤(Glycerol)과 부틸렌글라이콜(Butylene Glycol) 중 하나 이상의 성분이 혼합되고, 세럼이 함침된 미용시트를 피부에 부착시 세럼은 공기 중의 수분과 피부에 존재하는 수분을 흡수하여 미용시트에 공급함으로써 미용시트가 스스로 용융된다.In order to achieve the above-described object, the self-melting wet beauty sheet according to the present invention is cross-linked (cross-linked) by electrospinning of a spinning solution in which a water-soluble active ingredient with a skin care function, a film-forming water-soluble polymer, and a cross-linking agent are dissolved in a solvent. A beauty sheet is manufactured by impregnating the (linking) nanomembrane with a serum that does not contain purified water. The serum is a mixture of one or more ingredients of glycerol and butylene glycol, and the beauty sheet is impregnated with the serum. When the sheet is attached to the skin, the serum absorbs moisture in the air and moisture present on the skin and supplies it to the beauty sheet, causing the beauty sheet to melt itself.

상기 나노멤브레인 100 중량% 중 막 형성 수용성 고분자가 10 ~ 30 중량%를 차지하고, 나머지는 피부미용 기능을 갖는 수용성 유효성분과 가교제로 구성하여 피부 부착 사용시 공기 중에 분포돼 있는 수분과 피부에 존재하는 수분을 자연 흡수하여 가교결합(Cross-linking)이 풀어짐에 따라 나노멤브레인의 결합이 깨지면서 용융되어 수용성 미용성분이 서서히 피부에 흡수된다.Of 100% by weight of the nanomembrane, the film-forming water-soluble polymer accounts for 10 to 30% by weight, and the remainder is composed of water-soluble active ingredients with skin-beautifying functions and a cross-linking agent, which absorbs moisture distributed in the air and moisture present on the skin when used on the skin. As cross-linking is released through natural absorption, the bonds in the nanomembrane are broken and melted, and the water-soluble cosmetic ingredients are gradually absorbed into the skin.

상기 미용시트의 중량이 1m2 당 1.5 내지 7 그램인 것이 바람직하다. 여기서 미용시트는 가교결합된 나노멤브레인에 정제수를 함유하지 않은 세럼을 함침하여 제조한 것으로 사용자의 피부에 부착할 수 있는 최종 제품 형태의 미용시트를 말한다.It is preferable that the weight of the beauty sheet is 1.5 to 7 grams per 1 m 2 . Here, the beauty sheet is manufactured by impregnating a cross-linked nanomembrane with a serum that does not contain purified water, and refers to a beauty sheet in the form of a final product that can be attached to the user's skin.

피부미용 기능을 갖는 수용성 유효성분은 하이드롤라이즈드 콜라겐(Hydrolyzed Collagen), 병풀, 비타민 C, 나이아신아마이드(Niacinamide), 히알루론산(hyaluronic acid), 아데노신(adenosine), 세라마이드(Ceramide) 중에서 선택한 1종 또는 2종 이상의 혼합물을 포함하여 구성하며, 막 형성 수용성 고분자는 폴리비닐알코올(PVA), 폴리비닐피롤리돈(PVP), 풀루란(Pullulan), 아밀로덱스트린(Amylodextrin), 알긴산(Alginic acid) 중에서 선택한 1종 또는 2종 이상의 혼합물을 포함하여 구성하는 것이 바람직하다.The water-soluble active ingredient with skin beauty function is one selected from Hydrolyzed Collagen, Centella asiatica, Vitamin C, Niacinamide, hyaluronic acid, adenosine, and Ceramide. Or, it consists of a mixture of two or more types, and the film-forming water-soluble polymers include polyvinyl alcohol (PVA), polyvinylpyrrolidone (PVP), pullulan, amylodextrin, and alginic acid. It is preferable to include one type or a mixture of two or more types selected from among them.

상기 피부미용 기능을 갖는 수용성 유효성분은 자가 용융되어 피부에 서서히 흡수되며, 상기 막 형성 수용성 고분자는 자가 용융되어 일부는 피부에 흡수되고, 고분자에 해당하는 나머지 일부는 흡수되지 못하고 피부 위에 도포된 후 녹아서 사라지게 된다.The water-soluble active ingredient with the skin care function self-melts and is gradually absorbed into the skin, and the film-forming water-soluble polymer self-melts and part of it is absorbed into the skin, and the remaining part corresponding to the polymer is not absorbed and is applied on the skin. It melts and disappears.

상기 세럼 100 중량% 중 글리세롤이 30 ~ 90 중량%를 차지하고, 나머지는 세럼을 구성하는 기타 성분으로 구성할 수 있다.Of 100% by weight of the serum, glycerol accounts for 30 to 90% by weight, and the remainder may be composed of other ingredients that make up the serum.

상기 세럼 100 중량% 중 부틸렌글라이콜이 30 ~ 90 중량%를 차지하고, 나머지는 세럼을 구성하는 기타 성분으로 구성할 수 있다.Out of 100% by weight of the serum, butylene glycol accounts for 30 to 90% by weight, and the remainder may be composed of other ingredients that make up the serum.

상기 세럼 100 중량% 중 글리세롤과 부틸렌글라이콜이 30 ~ 90 중량%를 차지하고, 나머지는 세럼을 구성하는 기타 성분으로 구성하는 것이 가장 바람직하다.It is most preferable that glycerol and butylene glycol account for 30 to 90 wt% of 100 wt% of the serum, and the remainder is comprised of other ingredients that make up the serum.

이 때 세럼에 포함되는 글리세롤과 부틸렌글라이콜은 30 : 70 내지 40 : 60의 중량비로 혼합하도록 한다.At this time, the glycerol and butylene glycol contained in the serum are mixed at a weight ratio of 30:70 to 40:60.

한편, 상기와 같은 목적을 달성하기 위하여 본 발명에 따른 자가 용융 습식 미용시트의 제조방법은 다음의 단계로 구성된다.Meanwhile, in order to achieve the above object, the manufacturing method of the self-melting wet beauty sheet according to the present invention consists of the following steps.

피부미용 기능을 갖는 수용성 유효성분, 막 형성 수용성 고분자 및 가교제를 용매에 혼합한다.Water-soluble active ingredients with skin-beautifying functions, film-forming water-soluble polymers, and cross-linking agents are mixed in a solvent.

혼합된 방사용액으로 전기방사하여 수용성 나노멤브레인을 제조한다.A water-soluble nanomembrane is manufactured by electrospinning with a mixed spinning solution.

나노멤브레인에 정제수를 함유하지 않은 세럼을 함침하여 미용시트를 제조한다.A beauty sheet is manufactured by impregnating the nanomembrane with serum that does not contain purified water.

패치 형태가 유지되도록 미용시트를 건조 숙성한다.The beauty sheet is dried and aged to maintain the shape of the patch.

이러한 과정을 거쳐 만들어진 자가 용융 습식 미용시트의 일면에는 PET 메쉬 커버를 합포하고, 미용시트의 타면에는 부직포를 부착하여 보관 가능한 최종 제품의 형태로 완성된다.A PET mesh cover is attached to one side of the self-melting wet beauty sheet created through this process, and a non-woven fabric is attached to the other side of the beauty sheet to create a final product that can be stored.

상기 나노멤브레인을 제조하는 단계에서, 나노멤브레인 100 중량% 중 막 형성 수용성 고분자가 10 ~ 30 중량%를 차지하고, 나머지는 피부미용 기능을 갖는 수용성 유효성분과 가교제로 구성하여 피부에 부착 사용시 공기 중에 분포돼 있는 수분과 피부에 존재하는 수분을 자연 흡수하여 가교결합(Cross-linking)이 풀어짐에 따라 나노멤브레인의 결합이 깨지면서 용융되도록 제조된다.In the step of manufacturing the nanomembrane, the film-forming water-soluble polymer accounts for 10 to 30% by weight of 100% by weight of the nanomembrane, and the remainder is composed of a water-soluble active ingredient with a skin care function and a crosslinking agent, which is distributed in the air when attached to the skin and used. It is manufactured so that the bonds in the nanomembrane are broken and melted as cross-linking is released by naturally absorbing moisture present in the skin.

상기 미용시트를 제조하는 단계에서, 세럼 100 중량% 중 글리세롤과 부틸렌글라이콜이 30 ~ 90 중량%를 차지하고, 글리세롤과 부틸렌글라이콜은 30 : 70 내지 40 : 60의 중량비로 혼합되도록 제조된다.In the step of manufacturing the beauty sheet, glycerol and butylene glycol account for 30 to 90 wt% of 100 wt% of serum, and glycerol and butylene glycol are mixed at a weight ratio of 30:70 to 40:60. .

상기 건조 숙성하는 단계에서, 숙성조건은 섭씨50 ~ 70 ℃의 온도로 24 ~ 48 시간 숙성하여 패치로 피부에 부착할 수 있도록 한다.In the dry aging step, the maturation conditions are 24 to 48 hours at a temperature of 50 to 70 degrees Celsius so that it can be attached to the skin as a patch.

이상에서 설명한 바와 같이 상기와 같은 구성을 갖는 본 발명은 습식 미용시트의 글리세롤이나 부틸렌글라이콜이 공기 중에서 흡수한 수분과 피부에서 흡수한 수분을 미용시트에 공급하여 미용성분의 가교결합(Cross-linking)이 끊어지면서 스스로 용융된 후 서서히 피부에 흡수되도록 함으로써 기존 미용시트를 사용할 때의 불편함을 개선하고, 빠른 건조로 인해 미용효과가 감소하는 문제를 해결하였다.As described above, the present invention having the above configuration supplies moisture absorbed from the air by glycerol or butylene glycol of the wet beauty sheet and moisture absorbed from the skin to the beauty sheet to cross-link (Cross-link) the beauty ingredients. By breaking the link, it melts on its own and is gradually absorbed into the skin, thereby improving the inconvenience of using existing beauty sheets and solving the problem of reduced beauty effect due to rapid drying.

또한, 나노멤브레인에 세럼을 함침하여 제조한 미용시트를 패치 형태로 건조 숙성하여 사용자에게 공급하고 미용시트의 세럼은 정제수를 함유하지 않기 때문에 미용시트가 수분 때문에 끈적일 염려가 없어 사용자의 제품 휴대가 편리하며, 피부에 부착하기 위해 손으로 만질 때에도 끈적거리지 않아 제품의 사용이 간편하다.In addition, the beauty sheet manufactured by impregnating the nanomembrane with serum is dried and aged in the form of a patch and supplied to the user. Since the serum in the beauty sheet does not contain purified water, there is no need to worry about the beauty sheet becoming sticky due to moisture, making it easier for the user to carry the product. It is convenient, and the product is easy to use as it does not feel sticky even when touched with the hand to attach it to the skin.

또한, 공기 중에서 흡수한 수분과 피부에서 흡수한 수분을 미용시트에 공급하여 가교결합이 끊어지면서 스스로 용융될 때 피부미용 기능을 갖는 수용성 유효성분, 글리세롤, 부틸렌글라이콜 등이 피부로 천천히 스며들며 이 때 막 형성 수용성 고분자는 서서히 굳어 매우 얇은 막을 형성함으로써 용융된 미용성분들이 공기 중으로 증발하지 않고 피부에 천천히 흡수되도록 도와주기 때문에 기존 제품대비 미용효과가 뛰어나다.In addition, when moisture absorbed from the air and moisture absorbed from the skin is supplied to the beauty sheet and the cross-links are broken and melted on their own, water-soluble active ingredients with skin beauty functions, such as glycerol and butylene glycol, slowly permeate into the skin. Water-soluble polymers that form a film gradually harden to form a very thin film, helping molten beauty ingredients to be slowly absorbed into the skin rather than evaporating into the air, making it more effective than existing products.

도 1은 본 발명에 따른 자가 용융 습식 미용시트의 제조방법의 순서도,
도 2는 본 발명에 따라 제조된 전기방사에 의해 가교결합된 나노멤브레인의 사진,
도 3은 나노멤브레인에 정제수를 함유하지 않은 세럼을 함침하여 제조한 미용시트의 사진,
도 4는 본 발명에 따라 제조된 자가 용융 습식 미용시트의 저면에 부직포를 부착하고, 상면에는 PET 메쉬 커버를 합포하여 사용자가 피부에 부착 사용하기 전완성품의 구성을 나타내는 예시도,
도 5는 본 발명에 따라 제조된 자가 용융 습식 미용시트에 부착된 부직포를 떼어내고 있는 사진.

1 is a flowchart of a method for manufacturing a self-melting wet beauty sheet according to the present invention;
Figure 2 is a photograph of a nanomembrane crosslinked by electrospinning prepared according to the present invention;
Figure 3 is a photograph of a beauty sheet manufactured by impregnating a nanomembrane with a serum that does not contain purified water;
Figure 4 is an example showing the configuration of a finished product before a user attaches it to the skin by attaching a non-woven fabric to the bottom of the self-melting wet beauty sheet manufactured according to the present invention and combining a PET mesh cover to the top,
Figure 5 is a photograph showing the non-woven fabric attached to the self-melting wet beauty sheet manufactured according to the present invention.

본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 첨부되는 도면과 함께 상세하게 후술되는 실시예를 참조하면 명확해질 것이다.The advantages and features of the present invention and methods for achieving them will become clear by referring to the embodiments described in detail below along with the accompanying drawings.

그러나, 본 발명은 이하에서 개시되는 실시예로 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 것이다.However, the present invention is not limited to the embodiments disclosed below, but will be implemented in various different forms.

본 명세서에서 본 실시예는 본 발명의 개시가 완전하도록 하며, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이다.The examples herein are provided to make the disclosure of the present invention complete and to fully inform those skilled in the art of the scope of the invention.

그리고, 본 발명은 청구항의 범주에 의해 정의될 뿐이다.And, the present invention is only defined by the scope of the claims.

따라서, 몇 몇 실시예에서, 잘 알려진 구성 요소, 잘 알려진 동작 및 잘 알려진 기술들은 본 발명이 모호하게 해석되는 것을 피하기 위하여 구체적으로 설명되지 않는다.Accordingly, in some embodiments, well-known components, well-known operations and well-known techniques are not specifically described in order to avoid ambiguous interpretation of the present invention.

또한, 명세서 전체에 걸쳐 동일 참조 부호는 동일 구성 요소를 지칭하고, 본 명세서에서 사용된(언급된) 용어들은 실시예를 설명하기 위한 것이며 본 발명을 제한하고자 하는 것은 아니다.In addition, the same reference numerals refer to the same components throughout the specification, and the terms used (mentioned) in the specification are for explaining embodiments and are not intended to limit the present invention.

본 명세서에서, 단수형은 문구에서 특별히 언급하지 않는 한 복수형도 포함하며, '포함(또는, 구비)한다'로 언급된 구성 요소 및 동작은 하나 이상의 다른 구성요소 및 동작의 존재 또는 추가를 배제하지 않는다.In this specification, the singular also includes the plural unless specifically stated in the phrase, and elements and operations referred to as 'including (or, including)' do not exclude the presence or addition of one or more other elements and operations. .

다른 정의가 없다면, 본 명세서에서 사용되는 모든 용어(기술 및 과학적 용어를 포함)는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 공통적으로 이해될 수 있는 의미로 사용될 수 있을 것이다.Unless otherwise defined, all terms (including technical and scientific terms) used in this specification may be used with meanings that can be commonly understood by those skilled in the art to which the present invention pertains.

또한, 일반적으로 사용되는 사전에 정의되어 있는 용어들은 정의되어 있지 않은 한 이상적으로 또는 과도하게 해석되지 않는다.Additionally, terms defined in commonly used dictionaries are not interpreted ideally or excessively unless they are defined.

이하, 첨부된 도면을 참고로 본 발명의 바람직한 실시예에 대하여 설명한다.Hereinafter, preferred embodiments of the present invention will be described with reference to the attached drawings.

도 1 내지 도 5를 참고하면, 본 발명에 의한 자가 용융 습식 미용시트는 다음과 같은 방법으로 제조한다.Referring to Figures 1 to 5, the self-melting wet beauty sheet according to the present invention is manufactured by the following method.

피부미용 기능을 갖는 수용성 유효성분, 막 형성 수용성 고분자 및 가교제를 용매에 혼합하는 단계(S100)Step of mixing water-soluble active ingredients with skin-beautifying properties, film-forming water-soluble polymer, and cross-linking agent in a solvent (S100)

피부미용 기능을 갖는 수용성 유효성분, 막 형성 수용성 고분자 및 가교제를 용매에 함께 혼합하여 방사용액을 준비한다.A spinning solution is prepared by mixing a water-soluble active ingredient with a skin care function, a water-soluble film-forming polymer, and a crosslinking agent together in a solvent.

피부미용 기능을 갖는 수용성 유효성분은 하이드롤라이즈드 콜라겐(Hydrolyzed Collagen), 병풀, 비타민 C, 나이아신아마이드(Niacinamide), 히알루론산(hyaluronic acid), 아데노신(adenosine), 세라마이드(Ceramide) 중에서 선택한 1종 또는 2종 이상의 혼합물을 포함하여 구성하는 것이 바람직하나, 피부미용 기능을 갖는 저분자의 수용성 유효성분에 해당하는 다른 성분을 혼합하여 구성할 수도 있다.The water-soluble active ingredient with skin beauty function is one selected from Hydrolyzed Collagen, Centella asiatica, Vitamin C, Niacinamide, hyaluronic acid, adenosine, and Ceramide. Alternatively, it is preferable to include a mixture of two or more types, but it may also be composed by mixing other ingredients that correspond to low-molecular-weight, water-soluble active ingredients with skin care functions.

막 형성 수용성 고분자는 폴리비닐알코올(PVA), 폴리비닐피롤리돈(PVP), 풀루란(Pullulan), 아밀로덱스트린(Amylodextrin), 알긴산(Alginic acid) 중에서 선택한 1종 또는 2종 이상의 혼합물을 포함하여 구성하는 것이 바람직하나, 수용성의 막 형성 고분자에 해당하는 다른 성분을 혼합하여 구성할 수도 있다.Film-forming water-soluble polymers include one or a mixture of two or more selected from polyvinyl alcohol (PVA), polyvinylpyrrolidone (PVP), pullulan, amylodextrin, and alginic acid. It is preferable to configure it as such, but it can also be configured by mixing other components corresponding to water-soluble film-forming polymers.

피부미용 기능을 갖는 수용성 유효성분은 자가 용융되어 피부에 서서히 흡수되며, 막 형성 수용성 고분자는 자가 용융되어 일부는 피부에 흡수되고, 고분자에 해당하는 나머지 일부는 흡수되지 못하고 피부 위에 도포된 후 녹아서 사라지게 된다.Water-soluble active ingredients with skin care functions self-melt and are gradually absorbed into the skin, while film-forming water-soluble polymers self-melt and some are absorbed into the skin, while the remaining part, which corresponds to polymers, is not absorbed and melts and disappears after being applied on the skin. do.

용매는 물이나 알코올 또는 이들을 혼합하여 사용할 수 있는데, 본 발명에서는 물을 사용하였다.The solvent can be water, alcohol, or a mixture thereof, and water was used in the present invention.

가교제는 TSA(para-toluene sulfonic acid), 폴리우레아-co-포름알데히드(poly(urea-co-formaldehyde), TMPTMA(tri-methylopropane trimethacrylate), DVB(Divinylbenzene), 보론산(boric acid), 글루타 알데하이드(glutaraldehyde) 중에서 선택된 어느 하나를 사용할 수 있다. 본 발명에서는 TSA를 사용하였다.Crosslinking agents include TSA (para-toluene sulfonic acid), poly(urea-co-formaldehyde), TMPTMA (tri-methylopropane trimethacrylate), DVB (Divinylbenzene), boric acid, and gluta. Any one selected from aldehydes (glutaraldehyde) can be used. In the present invention, TSA was used.

일반적으로 고분자 물질을 용해할 때 가열 교반하면서 방사용액을 제조하고 상온으로 냉각한 후 가교제를 첨가하여 방사용액이 가교화 반응이 일어나지 않는 범위에서 가교제를 투입하는 것이 바람직하다.In general, when dissolving a polymer material, it is desirable to prepare a spinning solution while heating and stirring, cool it to room temperature, and then add the crosslinking agent to a range where a crosslinking reaction does not occur in the spinning solution.

따라서 본 발명에서도 방사용액 제조 시 가교제의 투입은 피부미용 기능을 갖는 수용성 유효성분과 막 형성 수용성 고분자를 물에 용해한 후 최종 단계에서 실시하는 것이 바람직하다.Therefore, in the present invention as well, when preparing the spinning solution, it is preferable that the addition of the crosslinking agent is carried out in the final step after dissolving the water-soluble active ingredient with skin-beautifying function and the water-soluble film-forming polymer in water.

혼합된 방사용액으로 전기방사하여 수용성 나노멤브레인을 제조하는 단계 (S200)Step of producing a water-soluble nanomembrane by electrospinning with a mixed spinning solution (S200)

방사용액의 전기방사에 의해 상호 가교결합(Cross-linking)된 나노멤브레인을 준비한다. 방사용액에 고전압을 가해줌으로써 고분자 jet이 분출되어 용매가 휘발되면서 나노스케일의 직경을 갖는 나노멤브레인이 얻어진다.Prepare cross-linked nanomembranes by electrospinning the spinning solution. By applying high voltage to the spinning solution, a polymer jet is ejected, the solvent is volatilized, and a nanomembrane with a nanoscale diameter is obtained.

도 2를 참고하면, 전기방사에 의해 가교결합된 콜라겐 건식 나노멤브레인의 모습을 나타낸다. 도 2는 피부미용 기능을 갖는 수용성 유효성분으로 하이드롤라이즈드 콜라겐(Hydrolyzed Collagen)을 사용하고, 막 형성 수용성 고분자는 폴리비닐알코올(PVA)을 사용하고, 가교제는 TSA(para-toluene sulfonic acid)를 사용하여 방사용액으로 전기방사하여 건식 나노멤브레인을 제조한 것이다. 나노화이버의 직경은 200㎚(0.2㎛) 이다.Referring to Figure 2, it shows the collagen dry nanomembrane cross-linked by electrospinning. Figure 2 shows that hydrolyzed collagen is used as a water-soluble active ingredient with skin beauty function, polyvinyl alcohol (PVA) is used as a film-forming water-soluble polymer, and TSA (para-toluene sulfonic acid) is used as a cross-linking agent. A dry nanomembrane was manufactured by electrospinning with a spinning solution. The diameter of the nanofiber is 200㎚ (0.2㎛).

도 2를 참고하면, 건식 나노멤브레인 100 중량% 중 막 형성 수용성 고분자가 10 ~ 30 중량%를 차지하고, 나머지는 피부미용 기능을 갖는 수용성 유효성분과 가교제로 구성하여 피부 부착 사용시 공기 중에 분포돼 있는 수분과 피부에 존재하는 수분을 자연 흡수하여 가교결합(Cross-linking)이 풀어짐에 따라 나노멤브레인의 결합이 깨지면서 용융된다.Referring to Figure 2, out of 100% by weight of the dry nanomembrane, the film-forming water-soluble polymer accounts for 10 to 30% by weight, and the remainder is composed of water-soluble active ingredients with skin-beautifying functions and a cross-linking agent, so that when used on the skin, the moisture distributed in the air and As the moisture present in the skin is naturally absorbed and the cross-linking is released, the bonds of the nanomembrane are broken and melted.

구체적으로, 건식 나노멤브레인 100 중량% 중 막 형성 수용성 고분자 10 ~ 30 중량%, 가교제 1 ~ 2 중량%를 혼합하여 구성하고, 나머지는 피부미용 기능을 갖는 수용성 유효성분을 혼합하여 구성한다. 가교제가 1 중량% 미만일 경우 충분한 가교가 이루어지지 않으며, 가교제가 2 중량%를 초과할 경우 가교제의 함량이 지나치게 많아 가교반응에 참여하지 않는 가교제가 많아지게 된다. 막 형성 수용성 고분자가 10 중량% 미만일 경우 시트의 형태가 제대로 유지되지 않는 문제가 있으며, 막 형성 수용성 고분자가 30 중량%를 초과할 경우 시트의 강도가 높아져 3~4시간이 지나도 시트가 용융되지 않는 문제가 발생한다.Specifically, the dry nanomembrane is made by mixing 10 to 30 wt% of film-forming water-soluble polymer and 1 to 2 wt% of cross-linking agent out of 100 wt% of the dry nanomembrane, and the remainder is made by mixing water-soluble active ingredients with skin care functions. If the crosslinking agent is less than 1% by weight, sufficient crosslinking is not achieved, and if the crosslinking agent is more than 2% by weight, the content of the crosslinking agent is too high, resulting in many crosslinking agents not participating in the crosslinking reaction. If the film-forming water-soluble polymer is less than 10% by weight, the sheet does not maintain its shape properly. If the film-forming water-soluble polymer exceeds 30% by weight, the strength of the sheet increases and the sheet does not melt even after 3 to 4 hours. A problem arises.

피부미용 기능을 갖는 수용성 유효성분은 주로 저분자이기 때문에 수분에 의해 녹는 정도가 민감하므로 저 중량(1.5 ~ 5.0 그램)의 시트라 하더라도 어느 정도 시트의 형태를 유지하기 위해 20중량% 정도의 막 형성 수용성 고분자를 사용하고, 나머지는 피부미용 기능을 갖는 수용성 유효성분 78 ~ 79중량%, 가교제 1 ~ 2 중량%를 혼합하여 사용하는 것이 가장 바람직하다.Since water-soluble active ingredients with skin care functions are mainly low molecules, they are sensitive to the degree to which they dissolve in moisture, so even for sheets of low weight (1.5 to 5.0 grams), about 20% by weight of water-soluble film is required to form a film to maintain the shape of the sheet to some extent. It is most desirable to use a polymer and mix the remainder with 78 to 79% by weight of a water-soluble active ingredient with skin-beautifying properties and 1 to 2% by weight of a crosslinking agent.

나노멤브레인에 정제수를 함유하지 않은 세럼을 함침하여 미용시트를 제조하는 단계(S300)Step of manufacturing a beauty sheet by impregnating the nanomembrane with serum that does not contain purified water (S300)

도 2의 건식 나노멤브레인에 정제수를 함유하지 않은 세럼을 함침하여 도 3의 미용시트를 제조한다. 세럼에 정제수가 포함되면 나노멤브레인이 녹아버리기 때문에 정제수를 함유하지 않은 세럼을 함침한다.The beauty sheet of Figure 3 is manufactured by impregnating the dry nanomembrane of Figure 2 with a serum that does not contain purified water. If the serum contains purified water, the nanomembrane will dissolve, so it is impregnated with a serum that does not contain purified water.

세럼은 글리세롤(Glycerol)과 부틸렌글라이콜(Butylene Glycol) 중 하나 이상의 성분이 혼합되고, 세럼이 함침된 미용시트를 피부에 부착시 세럼은 공기 중의 수분과 피부에 존재하는 수분을 흡수하여 미용시트에 공급함으로써 미용시트가 스스로 용융되도록 한다.Serum is a mixture of one or more of Glycerol and Butylene Glycol, and when a beauty sheet impregnated with serum is attached to the skin, the serum absorbs the moisture in the air and the moisture present on the skin, forming a beauty sheet. By supplying it to, the beauty sheet is allowed to melt on its own.

본 발명에서는 세럼을 함침하는 것으로 설명하고 있으나, 세럼 대신에 에센스를 함침하는 경우도 본 발명의 보호범위에 속한다. 세럼과 에센스는 단지 농도에서 차이가 있을 뿐이며, 세럼은 에센스보다 좀 더 짙은 느낌의 제형을 말한다.In the present invention, impregnation with serum is described, but impregnation with essence instead of serum also falls within the scope of protection of the present invention. The difference between serum and essence is only in concentration, and serum is a formulation that has a slightly thicker feel than essence.

글리세롤과 부틸렌글라이콜은 기본적으로 보습제 기능을 하는 점에서 일치한다. 그러나 사용감은 조금 다른데, 글리세린은 조금 뻑뻑한 느낌이 있고, 부틸렌글라이콜은 조금 더 부드러운 느낌이 있다.Glycerol and butylene glycol are basically similar in that they function as moisturizers. However, the feeling of use is a little different; glycerin has a slightly thicker feel, while butylene glycol has a slightly softer feel.

수분 함유 및 보습 기능은 글리세롤이 안정성 면에서 더 뛰어나지만 부틸렌글라이콜도 인체에 축적되지 않으며 독성 또한 가지지 않아 안전한 성분으로 분류되어 많이 사용되고 있다.Glycerol has better water retention and moisturizing properties in terms of stability, but butylene glycol does not accumulate in the human body and is not toxic, so it is classified as a safe ingredient and is widely used.

또한, 부틸렌글라이콜은 좋은 용매로 사용된다. 즉, 부틸렌클라이콜은 보습 기능을 하면서도 재료들이 잘 섞이게 만들어 준다.Additionally, butylene glycol is used as a good solvent. In other words, butylene glycol has a moisturizing function and helps the ingredients mix well.

글리세롤은 부틸렌글라이콜보다는 다른 물질을 섞어주는 능력이 떨어진다. 그래서 세럼에 글리세롤이나 부틸렌글라이콜 중 어느 하나만 혼합해서 사용해도 되지만, 두 가지를 적절히 섞어서 사용할 때 공기 중 수분과 피부에 존재하는 수분을 흡수하여 미용시트에 공급하여 미용시트가 자가 용융되도록 하는데 더욱 좋은 효과를 발휘한다.Glycerol has a lower ability to mix other substances than butylene glycol. So, you can mix either glycerol or butylene glycol with the serum, but when you mix the two properly, it absorbs moisture in the air and moisture existing on the skin and supplies it to the beauty sheet, allowing the beauty sheet to self-melt. It has good effect.

위에서 설명한 것처럼 글리세롤과 부틸렌글라이콜 중 한가지만 세럼에 혼합해서 사용해도 습식 미용시트의 형성 및 자가 용융에 문제가 없다.As explained above, there is no problem with the formation and self-melting of the wet beauty sheet even if only one of glycerol and butylene glycol is mixed with the serum.

세럼은 글리세롤과 부틸렌글라이콜 외에 다른 수분흡수 특성이 있는 히알루론산, 소듐PCA, 프로필렌글리콜(Propylene Glycol), 세라마이드 (Ceramides), 스쿠알란 (Squalane), 판테놀 (Panthenol) 등의 보습제 물질들도 혼합하여 사용 가능하나, 글리세롤과 부틸렌글라이콜이 수분흡수 능력과 사용 효율이 가장 뛰어나며, 다량 함유 시에도 피부 자극 또는 부작용 및 경제성 등의 문제가 없었다.In addition to glycerol and butylene glycol, serum is a mixture of moisturizing substances with other moisture absorption properties such as hyaluronic acid, sodium PCA, propylene glycol, ceramides, squalane, and panthenol. Although it can be used, glycerol and butylene glycol have the best moisture absorption ability and usage efficiency, and even when contained in large amounts, there are no problems such as skin irritation, side effects, or economic feasibility.

본 발명에서 글리세롤 또는 부틸렌글라이콜 중 어느 하나만 혼합하여 사용시 또는 글리세롤과 부틸렌글라이콜 두 가지를 혼합하여 사용시 세럼의 나머지 성분은 히알루론산을 혼합하는 것을 예로 설명하고 있으나, 히알루론산 외에 위에서 예로 든 세럼에 혼합 가능한 다른 수분흡수 특성이 있는 물질을 혼합하여 사용하는 것도 가능하며 본 발명의 보호범위에서 제외하지 않는다.In the present invention, when using a mixture of either glycerol or butylene glycol, or when using a mixture of both glycerol and butylene glycol, the remaining ingredient of the serum is explained as a mixture of hyaluronic acid. However, in addition to hyaluronic acid, It is also possible to mix and use substances with other moisture-absorbing properties that can be mixed with the serum and are not excluded from the scope of protection of the present invention.

세럼 100 중량% 중 글리세롤이 30 ~ 90 중량%를 차지하도록 하고, 나머지는 히알루론산을 혼합하였다. 공기 중 수분이 많이 포함되어 있는 않은 경우는 글리세롤이 50 중량% 미만일 경우 공기 중 수분 흡수 능력이 떨어져 1시간이 지나도 습식 미용시트에서 자가 용융이 잘 일어나지 않았다. 그러나 여름철과 같이 실내 습도가 높아 공기 중 수분이 많이 포함되어 있는 경우는 글리세롤이 30중량% 이상 50중량% 이하의 범위에서도 자가 용융이 잘 일어났다.Glycerol accounted for 30 to 90% by weight of 100% by weight of serum, and the remainder was mixed with hyaluronic acid. In cases where there is a lot of moisture in the air, if glycerol is less than 50% by weight, the ability to absorb moisture in the air is low and self-melting does not occur well in the wet beauty sheet even after 1 hour. However, when the indoor humidity is high and the air contains a lot of moisture, such as in the summer, self-melting occurs easily even when the glycerol is in the range of 30% by weight to 50% by weight.

그리고 글리세롤이 90 중량%를 초과하는 경우 습식 미용시트가 뻣뻣해지는 현상이 발생하였다.And when glycerol exceeded 90% by weight, the wet beauty sheet became stiff.

세럼 100 중량% 중 부틸렌글라이콜이 30 ~ 90 중량%를 차지하도록 하고, 나머지는 히알루론산을 혼합하였다. 글리세롤과 마찬가지로 공기 중 수분이 많이 포함되어 있는 않은 경우는 부틸렌글라이콜이 50 중량% 미만일 경우 공기 중 수분 흡수 능력이 떨어져 1시간이 지나도 습식 미용시트에서 자가 용융이 잘 일어나지 않았다. 그러나 여름철과 같이 실내 습도가 높아 공기 중 수분이 많이 포함되어 있는 경우는 부틸렌글라이콜이 30중량% 이상 50중량% 이하의 범위에서도 자가 용융이 잘 일어났다.Out of 100% by weight of serum, butylene glycol accounted for 30 to 90% by weight, and the remainder was mixed with hyaluronic acid. As with glycerol, when there is a lot of moisture in the air, if butylene glycol is less than 50% by weight, the ability to absorb moisture in the air is reduced, so self-melting does not occur in wet beauty sheets even after 1 hour. However, when the indoor humidity is high and the air contains a lot of moisture, such as in the summer, self-melting occurs easily even in the range of 30% by weight to 50% by weight of butylene glycol.

그리고 부틸렌글라이콜이 90 중량%를 초과하는 경우 지나치게 끈적여 미용시트로 적합하지 않았다.And if butylene glycol exceeds 90% by weight, it is too sticky and is not suitable as a beauty sheet.

세럼 100 중량% 중 글리세롤과 부틸렌글라이콜이 30 ~ 90 중량%를 차지하도록 하고, 나머지는 히알루론산을 혼합하였다. 이 경우가 글리세롤 또는 부틸렌글라이콜 하나만 혼합하는 경우보다 시트의 감촉도 가장 부드럽고 끈적이지 않았다. 그리고 피부의 촉촉함을 지속하는 자가 용융 효과도 가장 뛰어났다.Out of 100% by weight of serum, glycerol and butylene glycol accounted for 30 to 90% by weight, and the remainder was mixed with hyaluronic acid. In this case, the sheet felt softer and was not sticky compared to the case where only glycerol or butylene glycol was mixed. And the self-melting effect that maintains skin moisture was also the most outstanding.

공기 중 수분이 많이 포함되어 있는 않은 경우는 글리세롤과 부틸렌글라이콜이 45 중량% 미만일 경우 공기 중의 수분을 충분히 흡수하지 못하여 습식 미용시트에서 자가 용융이 잘 일어나지 않았다. 그러나 여름철과 같이 실내 습도가 높아 공기 중 수분이 많이 포함되어 있는 경우는 글리세롤과 부틸렌글라이콜이 30중량% 이상 45중량% 이하의 범위에서도 자가 용융이 잘 일어났다.In cases where there is a lot of moisture in the air, if glycerol and butylene glycol are less than 45% by weight, self-melting does not occur well in wet beauty sheets because moisture in the air cannot be sufficiently absorbed. However, when the indoor humidity is high and the air contains a lot of moisture, such as in the summer, self-melting occurs easily even in the range of 30% by weight to 45% by weight of glycerol and butylene glycol.

그리고 글리세롤과 부틸렌글라이콜이 90%를 초과하는 경우 미용시트는 잘 녹으나 지나치게 끈적여 미용시트로 적합하지 않았다.And if glycerol and butylene glycol exceeded 90%, the beauty sheet dissolved easily, but was too sticky and was not suitable as a beauty sheet.

구체적으로, 글리세롤과 부틸렌글라이콜은 30 : 70 내지 40 : 60의 중량비로 혼합될 때 미용시트의 감촉, 피부에 부착시 쪼그라들지 않고 펴지는 정도, 피부의 촉촉함을 지속하는 자가 용융의 효과가 뛰어났다.Specifically, when glycerol and butylene glycol are mixed at a weight ratio of 30:70 to 40:60, the texture of the beauty sheet, the extent to which it spreads rather than shrinks when attached to the skin, and the self-melting effect that maintains skin moisture are improved. Excellent.

다시 말해서, 글리세롤 대비 부틸렌글라이콜을 더 많이 혼합할 때 미용시트의 감촉, 피부에 부착하여 사용시 잘 펴지는 정도 그리고 미용시트가 공기 중의 수분을 흡수하여 자가 용융시 피부 촉촉함의 지속시간 등의 모든 면에서 우수한 효과를 나타냈다.In other words, when mixing more butylene glycol compared to glycerol, all factors such as the texture of the beauty sheet, the extent to which it spreads well when attached to the skin, and the duration of skin moisture when the beauty sheet absorbs moisture in the air and self-melts, etc. It showed excellent effects in this regard.

도 4 및 도 5를 참고하면, 자가 용융 습식 미용시트의 중량이 1m2 당 1.5 내지 7 그램, 두께는 0.003 내지 0.015mm 가 되도록 제조한다.Referring to Figures 4 and 5, the self-melting wet beauty sheet is manufactured so that the weight is 1.5 to 7 grams per 1 m 2 and the thickness is 0.003 to 0.015 mm.

자가 용융 습식 미용시트의 중량이 1m2 당 1.5 그램보다 작고, 두께가 0.003 mm 보다 작으면 미용시트를 피부에 부착 후 부직포를 미용시트에서 떼어낼 때 미용시트가 찢어지는 경우가 발생할 뿐만 아니라, 세럼이 공기 중의 수분과 피부에 존재하는 수분을 흡수하여 미용시트에 공급하여 미용시트가 스스로 용융되더라도 피부에 흡수되는 수분의 양이 적어 피부미용의 효과가 떨어진다.If the weight of the self-melting wet beauty sheet is less than 1.5 grams per 1 m 2 and the thickness is less than 0.003 mm, not only may the beauty sheet be torn when the non-woven fabric is removed from the beauty sheet after attaching the beauty sheet to the skin, but also the serum This absorbs the moisture in the air and the moisture existing on the skin and supplies it to the beauty sheet. Even if the beauty sheet melts on its own, the amount of moisture absorbed into the skin is small, reducing the skin beauty effect.

그리고 자가 용융 습식 미용시트의 중량이 1m2 당 7 그램보다 크고, 두께가 0.015 mm 보다 크면 세럼이 공기 중의 수분과 피부에 존재하는 수분을 흡수하여 미용시트에 공급함으로써 미용시트가 용융될 때 3~4시간이 지나도 시트가 잘 녹지 않고 남아있어 미관상 좋지 않은 문제가 있다.And if the weight of the self-melting wet beauty sheet is greater than 7 grams per 1 m 2 and the thickness is greater than 0.015 mm, the serum absorbs moisture in the air and moisture existing on the skin and supplies it to the beauty sheet, so when the beauty sheet melts, it takes 3~ Even after 4 hours, the sheet does not dissolve well and remains, causing an unsightly problem.

대기의 수분 등을 흡수해서 녹이는 자가 용융 습식 미용시트의 반복 테스트 결과 미용시트의 중량은 평방미터 당 중량 2 ~ 5그램 (두께 약 0.004 ~ 0.007mm)정도 규격의 시트로 제작할 때 가장 문제가 없고 좋은 효과를 나타냈다.As a result of repeated testing of a self-melting wet beauty sheet that absorbs and melts atmospheric moisture, the weight of the beauty sheet is the most problem-free and best when manufactured as a sheet with a standard weight of 2 to 5 grams per square meter (thickness of approximately 0.004 to 0.007 mm). It showed effect.

패치 형태가 유지되도록 미용시트를 건조 숙성하는 단계(S400)Step of drying and aging the beauty sheet to maintain the shape of the patch (S400)

숙성조건은 섭씨 50 ~ 70 ℃의 온도로 24 ~ 48 시간 숙성하여 패치로 피부에 부착할 수 있도록 한다.The ripening conditions are 50 to 70 degrees Celsius for 24 to 48 hours so that it can be attached to the skin as a patch.

도 4를 참고하면, 이러한 과정을 거쳐 만들어진 콜라겐 습식 미용시트는 탄성을 가지는 시트 패치로 겉면인 PET 메쉬 커버를 걷어내고 부직포와 콜라겐 습식 미용시트를 피부면에 부착한 후 부직포를 제거하면 두께 약 0.005mm 나노 콜라겐 습식 미용시트가 투명한 상태로 피부에 강력히 부착되며 시간이 지나면서 시트 패치의 두께가 얇아지고 특히 가운데 부분부터 녹아 없어지면서 가장자리까지 녹게 되어 패치의 형태는 없어지고 일부 잔여물이 남게되며 이를 토너 등을 이용하여 두드려서 다 녹이게 된다.Referring to Figure 4, the collagen wet beauty sheet made through this process is an elastic sheet patch. The outer PET mesh cover is removed and the non-woven fabric and collagen wet beauty sheet are attached to the skin surface. When the non-woven fabric is removed, the thickness is about 0.005. The mm nano collagen wet beauty sheet is transparent and strongly adheres to the skin. As time goes by, the thickness of the sheet patch becomes thinner, especially from the center and melts to the edges, so the shape of the patch disappears and some residue remains. Tap it with toner, etc. to dissolve it.

실시예 및 비교예Examples and Comparative Examples

이하, 실시예 및 비교예를 들어 본 발명을 구체적으로 설명한다. 본 발명이 속하는 분야의 평균적 기술자는 아래 실시예에 기재된 조성 외에 여러 가지 다른 형태로 본 발명을 변경할 수 있으며, 이하 실시예에서는 본 발명을 예시할 따름이지 본 발명의 기술적 사상의 범위를 아래 실시예의 범위로 한정하기 위한 의도로 해석해서는 안 된다.Hereinafter, the present invention will be described in detail through examples and comparative examples. An average person skilled in the field to which the present invention pertains can modify the present invention into various other forms in addition to the composition described in the examples below. The examples below only illustrate the present invention, but the scope of the technical idea of the present invention is described in the examples below. It should not be interpreted as an intention to limit the scope.

[실시예 1][Example 1]

(1) 피부미용 기능을 갖는 수용성 유효성분은 하이드롤라이즈드 콜라겐(Hydrolyzed Collagen)이 약 72% 중량비, 막 형성 고분자인 폴리비닐알코올(PVA) 약 27% 중량비, 가교제는 TSA 약 1% 중량비가 혼합(1) The water-soluble active ingredient with skin beauty function is Hydrolyzed Collagen at about 72% weight ratio, polyvinyl alcohol (PVA), a film-forming polymer, at about 27% weight ratio, and the cross-linking agent is TSA at about 1% weight ratio. mix

(2) 글리세롤 80중량%, 히알루론산 20중량%를 혼합한 정제수를 함유하지 않은 세럼을 함침(2) Impregnation with a serum containing no purified water mixed with 80% by weight of glycerol and 20% by weight of hyaluronic acid.

전기방사를 거쳐 제조된 나노섬유 멤브레인을 평방미터 당 4그램의 평량을 가지며 방사용액은 전기방사에 용매로 사용되는 순수물과 시트 구성 성분인 피부미용 기능을 갖는 수용성 유효성분은 하이드롤라이즈드 콜라겐(Hydrolyzed Collagen)이 약 72% 중량비, 막 형성 고분자인 폴리비닐알코올(PVA) 약 27% 중량비, 가교제는 TSA 약 1% 중량비가 혼합되며, 나노시트 전기방사 시 방사판으로 P. P. Spunbond 부직포 40그램를 투입하고 그 위에 콜라겐과 폴리비닐알코올을 전기방사하여 수용성 콜라겐 건조시트(도 2)를 제조한다.The nanofiber membrane manufactured through electrospinning has a basis weight of 4 grams per square meter, and the spinning solution is pure water used as a solvent for electrospinning, and the water-soluble active ingredient with skin beautification function, which is a component of the sheet, is hydrolyzed collagen. (Hydrolyzed Collagen) is mixed at a weight ratio of about 72%, polyvinyl alcohol (PVA), a film-forming polymer, is mixed at a weight ratio of about 27%, and the crosslinker is mixed at a weight ratio of about 1% TSA. When electrospinning nanosheets, 40 grams of P. P. Spunbond nonwoven fabric is added as a spinning plate. Then, collagen and polyvinyl alcohol are electrospun on top of it to produce a water-soluble collagen dry sheet (Figure 2).

수용성 콜라겐 건조시트에 공기 중 수분흡수성이강한 글리세롤 80중량%, 히알루론산 20중량%를 혼합한 정제수를 함유하지 않은 세럼을 함침시킨다.The water-soluble collagen drying sheet is impregnated with a serum containing no purified water mixed with 80% by weight of glycerol and 20% by weight of hyaluronic acid, which have strong moisture absorption in the air.

콜라겐 습식시트를 제조하는 단계에는 앞의 전기방사 제조된 건조시트의 부직포 반대면에 PET 메쉬 커버를 접착하지 않은 상태로 합포하고(도 4), 3겹 시트의 메쉬면에 정제수 등 수분이 포함되지 않은 세럼을 롤러를 이용하여 표면에 코팅작업한다.In the step of manufacturing a collagen wet sheet, a PET mesh cover is laminated on the non-woven opposite side of the electrospun dry sheet without adhering to it (Figure 4), and the mesh side of the 3-ply sheet does not contain moisture such as purified water. Coat the surface with the unused serum using a roller.

세럼은 점도를 3,000cps ~ 5,000cps 정도로 흐름성이 좋도록 하며 너무 과하게 액상을 도포하면 촉감이나 시트의 용해가 잘 안되는 경우가 있으므로 1kg 당 양 20m2 ~ 25m2 정도 도포하였다(도 4).The serum has a viscosity of about 3,000 cps to 5,000 cps for good flowability. If too much liquid is applied, the feel or dissolution of the sheet may be difficult, so about 20 m 2 to 25 m 2 per 1 kg was applied (Figure 4).

세럼 함침작업을 마치면 시트의 내구성을 강화하여 패치 형태가 유지되도록 하기 위해 건조 숙성을 한다. 숙성조건은 섭씨 55 ~ 60 ℃의 온도로 30 ~ 36시간 숙성하였다.After the serum impregnation work is completed, dry aging is performed to strengthen the durability of the sheet and maintain the shape of the patch. The aging conditions were 55 to 60 degrees Celsius for 30 to 36 hours.

이러한 과정을 거쳐 만들어진 콜라겐 습식시트(도 4)는 탄성을 가지는 시트 패치로 겉면인 PET 메쉬 커버를 걷어내고 부직포와 콜라겐 시트(자가 용융 습식 미용시트)를 피부면에 부착한 후 부직포를 제거하였으며 시간에 따른 자가 용융의 효과를 확인하였다.The collagen wet sheet (Figure 4) made through this process is an elastic sheet patch, the outer PET mesh cover is removed, the non-woven fabric and collagen sheet (self-melting wet beauty sheet) are attached to the skin surface, the non-woven fabric is removed, and the non-woven fabric is removed over time. The effect of self-melting was confirmed.

대기 중의 습도가 높거나 온도가 높은 경우에는 평균적인 데이터를 얻기가 힘들고 습도가 50% 이하이고 실내 온도가 21℃ 이하 인 경우에는 착용자의 피부의 건성 지성 정도에 따라 시트의 용융 정도가 달라지는데 지성의 경우에는 피부의 습기와 유분으로 인해 시트의 용융에 영향이 적은 반면 건성인 경우에는 시트가 공기 중의 습기를 흡착하여도 피부에 바로 공급이 되어 시트의 용융 조건에 수분함유량이 미치지 못하여 시트가 녹기보다는 견고하게 피부에 남아있기 때문에 실험 조건은 섭씨 21도, 습도 50%를 기준으로 하여 자가 용융의 효과를 확인하였다.When the humidity in the air is high or the temperature is high, it is difficult to obtain average data, and when the humidity is less than 50% and the room temperature is less than 21℃, the degree of melting of the sheet varies depending on the dryness or oiliness of the wearer's skin. In the case of dry skin, moisture and oil from the skin have little effect on the melting of the sheet, whereas in the case of dry skin, even if the sheet absorbs moisture in the air, it is supplied directly to the skin, so the moisture content does not meet the melting conditions of the sheet, so rather than melting the sheet. Because it remains firmly on the skin, the experimental conditions were 21 degrees Celsius and 50% humidity to confirm the effect of self-melting.

[실시예 2][Example 2]

(1) 피부미용 기능을 갖는 수용성 유효성분은 하이드롤라이즈드 콜라겐(Hydrolyzed Collagen)이 약 79% 중량비, 막 형성 고분자인 폴리비닐알코올(PVA) 약 20% 중량비, 가교제는 TSA 약 1% 중량비가 혼합(1) The water-soluble active ingredient with skin beauty function is Hydrolyzed Collagen at about 79% weight ratio, polyvinyl alcohol (PVA), a film-forming polymer, at about 20% weight ratio, and the cross-linking agent is TSA at about 1% weight ratio. mix

(2) 부틸렌글라이콜 80중량%, 히알루론산 20중량%를 혼합한 정제수를 함유하지 않은 세럼을 함침(2) Impregnation with a serum containing no purified water mixed with 80% by weight of butylene glycol and 20% by weight of hyaluronic acid.

전기방사를 거쳐 제조된 나노섬유 멤브레인을 평방미터 당 4그램의 평량을 가지며 방사용액은 전기방사에 용매로 사용되는 순수물과 시트 구성 성분인 피부미용 기능을 갖는 수용성 유효성분은 하이드롤라이즈드 콜라겐(Hydrolyzed Collagen)이 약 79% 중량비, 막 형성 고분자인 폴리비닐알코올(PVA) 약 20% 중량비, 가교제는 TSA 약 1% 중량비가 혼합되며, 나노시트 전기방사 시 방사판으로 P. P. Spunbond 부직포 40그램를 투입하고 그 위에 콜라겐과 폴리비닐알코올을 전기방사하여 수용성 콜라겐 건조시트(도 2)를 제조한다.The nanofiber membrane manufactured through electrospinning has a basis weight of 4 grams per square meter, and the spinning solution is pure water used as a solvent for electrospinning, and the water-soluble active ingredient with skin beautification function, which is a component of the sheet, is hydrolyzed collagen. (Hydrolyzed Collagen) is mixed at a weight ratio of about 79%, polyvinyl alcohol (PVA), a film-forming polymer, is mixed at a weight ratio of about 20%, and the crosslinking agent is mixed at a weight ratio of about 1% TSA. When electrospinning nanosheets, 40 grams of P. P. Spunbond nonwoven fabric is added as a spinning plate. Then, collagen and polyvinyl alcohol are electrospun on top of it to produce a water-soluble collagen dry sheet (Figure 2).

수용성 콜라겐 건조시트에 공기 중 수분흡수성이강한 부틸렌글라이콜 80중량%, 히알루론산 20중량%를 혼합한 정제수를 함유하지 않은 세럼을 함침시킨다.The water-soluble collagen drying sheet is impregnated with a serum containing no purified water mixed with 80% by weight of butylene glycol and 20% by weight of hyaluronic acid, which have strong moisture absorption in the air.

콜라겐 습식시트를 제조하는 단계에는 앞의 전기방사 제조된 건조시트의 부직포 반대면에 PET 메쉬 커버를 접착하지 않은 상태로 합포하고(도 4), 3겹 시트의 메쉬면에 정제수 등 수분이 포함되지 않은 세럼을 롤러를 이용하여 표면에 코팅작업한다.In the step of manufacturing a collagen wet sheet, a PET mesh cover is laminated on the non-woven opposite side of the electrospun dry sheet without adhering to it (Figure 4), and the mesh side of the 3-ply sheet does not contain moisture such as purified water. Coat the surface with the unused serum using a roller.

나머지는 실시예 1과 동일하게 실시하였다.The rest was carried out in the same manner as Example 1.

[실시예 3][Example 3]

(1) 피부미용 기능을 갖는 수용성 유효성분은 하이드롤라이즈드 콜라겐(Hydrolyzed Collagen)이 약 69% 중량비, 막 형성 고분자인 폴리비닐알코올(PVA) 약 30% 중량비, 가교제는 TSA 약 1% 중량비가 혼합(1) The water-soluble active ingredient with skin beauty function is Hydrolyzed Collagen at about 69% weight ratio, polyvinyl alcohol (PVA), a film-forming polymer, at about 30% weight ratio, and the cross-linking agent is TSA at about 1% weight ratio. mix

(2) 글리세롤과 부틸렌글라이콜 80중량%, 히알루론산 20중량%를 혼합한 정제수를 함유하지 않은 세럼을 함침. 이때 글리세롤과 부틸렌글라이콜의 중량비는 30 : 70의 비율로 혼합(2) Impregnate with a serum containing no purified water mixed with 80% by weight of glycerol and butylene glycol and 20% by weight of hyaluronic acid. At this time, the weight ratio of glycerol and butylene glycol is mixed at a ratio of 30:70.

전기방사를 거쳐 제조된 나노섬유 멤브레인을 평방미터 당 4그램의 평량을 가지며 방사용액은 전기방사에 용매로 사용되는 순수물과 시트 구성 성분인 피부미용 기능을 갖는 수용성 유효성분은 하이드롤라이즈드 콜라겐(Hydrolyzed Collagen)이 약 69% 중량비, 막 형성 고분자인 폴리비닐알코올(PVA) 약 30% 중량비, 가교제는 TSA 약 1% 중량비가 혼합되며, 나노시트 전기방사 시 방사판으로 P. P. Spunbond 부직포 40그램를 투입하고 그 위에 콜라겐과 폴리비닐알코올을 전기방사하여 수용성 콜라겐 건조시트(도 2)를 제조한다.The nanofiber membrane manufactured through electrospinning has a basis weight of 4 grams per square meter, and the spinning solution is pure water used as a solvent for electrospinning, and the water-soluble active ingredient with skin beautification function, which is a component of the sheet, is hydrolyzed collagen. (Hydrolyzed Collagen) is mixed at a weight ratio of about 69%, polyvinyl alcohol (PVA), a film-forming polymer, is mixed at a weight ratio of about 30%, and the crosslinker is mixed at a weight ratio of about 1% TSA. When electrospinning nanosheets, 40 grams of P. P. Spunbond nonwoven fabric is added as a spinning plate. Then, collagen and polyvinyl alcohol are electrospun on top of it to produce a water-soluble collagen dry sheet (Figure 2).

수용성 콜라겐 건조시트에 공기 중 수분흡수성이강한 글리세롤과 부틸렌글라이콜 80중량%, 히알루론산 20중량%를 혼합한 정제수를 함유하지 않은 세럼을 함침시킨다. 이때 글리세롤과 부틸렌글라이콜의 중량비는 30 : 70의 비율로 혼합하였다.The water-soluble collagen drying sheet is impregnated with a serum that does not contain purified water, which is a mixture of 80% by weight of glycerol and butylene glycol and 20% by weight of hyaluronic acid, which have strong moisture absorption in the air. At this time, the weight ratio of glycerol and butylene glycol was mixed at a ratio of 30:70.

콜라겐 습식시트를 제조하는 단계에는 앞의 전기방사 제조된 건조시트의 부직포 반대면에 PET 메쉬 커버를 접착하지 않은 상태로 합포하고(도 4), 3겹 시트의 메쉬면에 정제수 등 수분이 포함되지 않은 세럼을 롤러를 이용하여 표면에 코팅작업한다.In the step of manufacturing a collagen wet sheet, a PET mesh cover is laminated on the non-woven opposite side of the electrospun dry sheet without adhering to it (Figure 4), and the mesh side of the 3-ply sheet does not contain moisture such as purified water. Coat the surface with the unused serum using a roller.

나머지는 실시예 1과 동일하게 실시하였다.The rest was carried out in the same manner as Example 1.

[실시예 4][Example 4]

(1) 피부미용 기능을 갖는 수용성 유효성분은 하이드롤라이즈드 콜라겐(Hydrolyzed Collagen)이 약 82% 중량비, 막 형성 고분자인 폴리비닐알코올(PVA) 약 17% 중량비, 가교제는 TSA 약 1% 중량비가 혼합(1) The water-soluble active ingredient with skin beauty function is Hydrolyzed Collagen at about 82% by weight, polyvinyl alcohol (PVA), a film-forming polymer, at about 17% by weight, and the cross-linking agent is TSA at about 1% by weight. mix

(2) 글리세롤과 부틸렌글라이콜 80중량%, 히알루론산 20중량%를 혼합한 정제수를 함유하지 않은 세럼을 함침. 이때 글리세롤과 부틸렌글라이콜의 중량비는 40 : 60의 비율로 혼합(2) Impregnate with a serum containing no purified water mixed with 80% by weight of glycerol and butylene glycol and 20% by weight of hyaluronic acid. At this time, the weight ratio of glycerol and butylene glycol is mixed at a ratio of 40:60.

전기방사를 거쳐 제조된 나노섬유 멤브레인을 평방미터 당 4그램의 평량을 가지며 방사용액은 전기방사에 용매로 사용되는 순수물과 시트 구성 성분인 피부미용 기능을 갖는 수용성 유효성분은 하이드롤라이즈드 콜라겐(Hydrolyzed Collagen)이 약 82% 중량비, 막 형성 고분자인 폴리비닐알코올(PVA) 약 17% 중량비, 가교제는 TSA 약 1% 중량비가 혼합되며, 나노시트 전기방사 시 방사판으로 P. P. Spunbond 부직포 40그램를 투입하고 그 위에 콜라겐과 폴리비닐알코올을 전기방사하여 수용성 콜라겐 건조시트(도 2)를 제조한다.The nanofiber membrane manufactured through electrospinning has a basis weight of 4 grams per square meter, and the spinning solution is pure water used as a solvent for electrospinning, and the water-soluble active ingredient with skin beauty function, which is a component of the sheet, is hydrolyzed collagen. (Hydrolyzed Collagen) is mixed at a weight ratio of about 82%, polyvinyl alcohol (PVA), a film-forming polymer, is mixed at a weight ratio of about 17%, and the crosslinker is mixed at a weight ratio of about 1% TSA. When electrospinning nanosheets, 40 grams of P. P. Spunbond nonwoven fabric is added as a spinning plate. Then, collagen and polyvinyl alcohol are electrospun on top of it to produce a water-soluble collagen dry sheet (Figure 2).

수용성 콜라겐 건조시트에 공기 중 수분흡수성이강한 글리세롤과 부틸렌글라이콜 80중량%, 히알루론산 20중량%를 혼합한 정제수를 함유하지 않은 세럼을 함침시킨다. 이때 글리세롤과 부틸렌글라이콜의 중량비는 40 : 60의 비율로 혼합하였다.The water-soluble collagen drying sheet is impregnated with a serum that does not contain purified water, which is a mixture of 80% by weight of glycerol and butylene glycol and 20% by weight of hyaluronic acid, which have strong moisture absorption in the air. At this time, glycerol and butylene glycol were mixed at a weight ratio of 40:60.

콜라겐 습식시트를 제조하는 단계에는 앞의 전기방사 제조된 건조시트의 부직포 반대면에 PET 메쉬 커버를 접착하지 않은 상태로 합포하고(도 4), 3겹 시트의 메쉬면에 정제수 등 수분이 포함되지 않은 세럼을 롤러를 이용하여 표면에 코팅작업한다.In the step of manufacturing a collagen wet sheet, a PET mesh cover is laminated on the non-woven opposite side of the electrospun dry sheet without adhering to it (Figure 4), and the mesh side of the 3-ply sheet does not contain moisture such as purified water. Coat the surface with the unused serum using a roller.

나머지는 실시예 1과 동일하게 실시하였다.The rest was carried out in the same manner as Example 1.

[비교예 1] [Comparative Example 1]

피부미용 기능을 갖는 수용성 유효성분은 하이드롤라이즈드 콜라겐(Hydrolyzed Collagen)이 약 91% 중량비, 막 형성 고분자인 폴리비닐알코올(PVA) 약 8% 중량비, 가교제는 TSA 약 1% 중량비가 혼합The water-soluble active ingredient with skin-beautifying properties is about 91% by weight of Hydrolyzed Collagen, about 8% by weight of polyvinyl alcohol (PVA), a film-forming polymer, and about 1% by weight of TSA as a cross-linking agent.

나머지는 실시예 1과 동일하게 실시하였다.The rest was carried out in the same manner as Example 1.

[비교예 2] [Comparative Example 2]

피부미용 기능을 갖는 수용성 유효성분은 하이드롤라이즈드 콜라겐(Hydrolyzed Collagen)이 약 63% 중량비, 막 형성 고분자인 폴리비닐알코올(PVA) 약 36% 중량비, 가교제는 TSA 약 1% 중량비가 혼합The water-soluble active ingredient with skin-beautifying properties is about 63% by weight of Hydrolyzed Collagen, about 36% by weight of polyvinyl alcohol (PVA), a film-forming polymer, and about 1% by weight of TSA as a cross-linking agent.

나머지는 실시예 2와 동일하게 실시하였다.The rest was carried out in the same manner as Example 2.

[비교예 3] [Comparative Example 3]

글리세롤 25중량%, 히알루론산 75중량%를 혼합한 정제수를 함유하지 않은 세럼을 함침Impregnated with a serum containing no purified water mixed with 25% by weight of glycerol and 75% by weight of hyaluronic acid.

나머지는 실시예 1과 동일하게 실시하였다.The rest was carried out in the same manner as Example 1.

[비교예 4] [Comparative Example 4]

글리세롤 95중량%, 히알루론산 5중량%를 혼합한 정제수를 함유하지 않은 세럼을 함침Impregnated with a serum containing no purified water mixed with 95% by weight of glycerol and 5% by weight of hyaluronic acid.

나머지는 실시예 1과 동일하게 실시하였다.The rest was carried out in the same manner as Example 1.

[비교예 5] [Comparative Example 5]

부틸렌글라이콜 25중량%, 히알루론산 75중량%를 혼합한 정제수를 함유하지 않은 세럼을 함침Impregnated with a serum that does not contain purified water mixed with 25% by weight of butylene glycol and 75% by weight of hyaluronic acid.

나머지는 실시예 2와 동일하게 실시하였다.The rest was carried out in the same manner as Example 2.

[비교예 6] [Comparative Example 6]

부틸렌글라이콜 95중량%, 히알루론산 5중량%를 혼합한 정제수를 함유하지 않은 세럼을 함침Impregnated with a serum that does not contain purified water mixed with 95% by weight of butylene glycol and 5% by weight of hyaluronic acid.

나머지는 실시예 2와 동일하게 실시하였다.The rest was carried out in the same manner as Example 2.

[비교예 7] [Comparative Example 7]

글리세롤과 부틸렌글라이콜 25중량%, 히알루론산 75중량%를 혼합한 정제수를 함유하지 않은 세럼을 함침. 이때 글리세롤과 부틸렌글라이콜의 중량비는 30 : 70의 비율로 혼합Impregnated with a serum that does not contain purified water mixed with 25% by weight of glycerol and butylene glycol and 75% by weight of hyaluronic acid. At this time, the weight ratio of glycerol and butylene glycol is mixed at a ratio of 30:70.

나머지는 실시예 3과 동일하게 실시하였다.The rest was carried out in the same manner as Example 3.

[비교예 8] [Comparative Example 8]

글리세롤과 부틸렌글라이콜 80중량%, 히알루론산 20중량%를 혼합한 정제수를 함유하지 않은 세럼을 함침. 이때 글리세롤과 부틸렌글라이콜의 중량비는 60 : 40의 비율로 혼합Impregnated with a serum containing no purified water mixed with 80% by weight of glycerol and butylene glycol and 20% by weight of hyaluronic acid. At this time, the weight ratio of glycerol and butylene glycol is mixed at a ratio of 60:40.

나머지는 실시예 4와 동일하게 실시하였다.The rest was carried out in the same manner as in Example 4.

[실험 결과][Experiment result]

상기의 방법으로 제조된 실시예 1~4 및 비교예 1~8의 미용시트를 가로 5cm, 세로 5cm의 크기로 각각 절단하여 신체 건강한 남, 녀 20명에게 2~4시간 동안 사용하게 하였고, 사용 후 효과에 대하여 설문조사를 실시하였다. 점수의 척도는 1점에서 5점까지로 하고, 1점은 "아니다," 3점은 "보통이다," 5점은 "매우 그렇다"로 설문에 표기하도록 하였다. 아래의 표 1은 남, 녀 20명의 설문조사 결과의 평균점수를 나타낸다.The beauty sheets of Examples 1 to 4 and Comparative Examples 1 to 8 prepared by the above method were cut into pieces of 5 cm in width and 5 cm in length, and were used by 20 healthy men and women for 2 to 4 hours. A survey was conducted regarding the after-effects. The score scale was 1 to 5, with 1 being “no,” 3 being “average,” and 5 being “very much.” Table 1 below shows the average scores of the survey results of 20 men and women.

다음의 표 1에서 볼 수 있듯이, 실시예 1~4는 자가용융, 보습지속력, 막형성에서 좋은 효과를 보여주었으며, 시트끈적임과 시트뻣뻣함의 정도는 양호하였다. 그리고 일정시간(2~4시간)이 지난 후 시트가 용융되어 피부에 흡수되어 미관도 양호한 것으로 나타났다.As can be seen in Table 1 below, Examples 1 to 4 showed good effects in self-melting, moisturizing retention, and film formation, and the degree of sheet stickiness and sheet stiffness was good. And after a certain period of time (2 to 4 hours), the sheet melted and was absorbed into the skin, showing good aesthetics.

특히, 실시예 1, 실시예 2 보다 글리세롤과 부틸렌글라이콜을 혼합하여 사용한 실시예 3 및 실시예 4의 경우가 전체적인 효과가 더 뛰어난 것을 확인할 수 있었다.In particular, it was confirmed that the overall effect was better in Examples 3 and 4, which used a mixture of glycerol and butylene glycol, than in Examples 1 and 2.

비교예 1은 막 형성 고분자인 PVA 함량이 본 발명의 기준치보다 부족하여 막이 제대로 형성되지 않았다. 자가용융은 되었으나 막이 잘 형성되지 않아 보습에 문제를 보였다.In Comparative Example 1, the film was not formed properly because the content of PVA, a film-forming polymer, was less than the standard value of the present invention. It was self-melting, but the film was not formed well, causing problems with moisturizing.

비교예 2는 막 형성 고분자인 PVA 함량이 본 발명의 기준치를 초과하여 막이 강하게 형성되었다. 자가용융, 보습지속력 등에서 효과가 떨어졌으며, 일정시간이 지난 후 시트의 모습도 변화하지 않고 남아있는 문제가 있었다.In Comparative Example 2, the content of PVA, a film-forming polymer, exceeded the standard value of the present invention, so a strong film was formed. It was less effective in terms of self-melting and moisturizing retention, and there was a problem with the appearance of the sheet remaining unchanged after a certain period of time.

비교예 3은 세럼에 포함된 글리세롤의 함량이 본 발명의 기준치보다 부족한 경우이다. 이 경우 자가용융, 보습지속력 등의 효과가 떨어졌다.Comparative Example 3 is a case where the content of glycerol contained in serum is less than the standard value of the present invention. In this case, the effects of self-melting and moisturizing retention were reduced.

비교예 4는 세럼에 포함된 글리세롤의 함량이 본 발명의 기준치를 초과하는 경우이다. 이 경우 시트가 뻣뻣해질 뿐만 아니라 제품의 전체적인 완성도 역시 부족하였다.Comparative Example 4 is a case where the content of glycerol contained in serum exceeds the standard value of the present invention. In this case, not only did the sheet become stiff, but the overall completion of the product was also lacking.

비교예 5는 세럼에 포함된 부틸렌글라이콜의 함량이 본 발명의 기준치보다 부족한 경우이다. 비교예 6은 세럼에 포함된 부틸렌글라이콜의 함량이 본 발명의 기준치를 초과하는 경우이다. 비교예 5, 6 역시 전체적인 효과에서 제품의 완성도가 떨어졌다. 특히 비교예 6은 부틸렌글라이콜의 과다 함량 때문에 시트의 끈적임 정도가 높았다.Comparative Example 5 is a case where the content of butylene glycol contained in the serum is less than the standard value of the present invention. Comparative Example 6 is a case where the content of butylene glycol contained in the serum exceeds the standard value of the present invention. Comparative Examples 5 and 6 also showed poor product perfection in terms of overall effect. In particular, in Comparative Example 6, the degree of stickiness of the sheet was high due to the excessive content of butylene glycol.

비교예 7은 세럼에 포함된 글리세롤과 부틸렌글라이콜의 함량이 본 발명의 기준치보다 부족한 경우이다. 이 경우 공기 중 수분을 충분히 흡수하지 못하여 자가 용융이 잘 일어나지 않았고, 보습이 제대로 지속되지 못하였다.Comparative Example 7 is a case where the content of glycerol and butylene glycol contained in the serum is less than the standard value of the present invention. In this case, self-melting did not occur easily due to insufficient absorption of moisture in the air, and moisturizing did not last properly.

비교예 8은 세럼에 포함된 글리세롤과 부틸렌글라이콜의 전체 함량은 문제가 없으나, 글리세롤이 부틸렌글라이콜보다 더 많이 포함된 경우이다. 이 경우 다른 비교예들보다는 효과가 양호하였으나, 실시예 1 내지 실시예 4 보다는 떨어지는 것을 확인하였다.Comparative Example 8 is a case where there is no problem with the total content of glycerol and butylene glycol contained in the serum, but glycerol is contained in greater amounts than butylene glycol. In this case, the effect was better than other comparative examples, but it was confirmed that it was inferior to Examples 1 to 4.

상술한 바와 같이, 본 발명은 본 발명은 공기 중에서 흡수한 수분과 피부에서 흡수한 수분을 미용시트에 공급하여 가교결합이 끊어지면서 스스로 용융될 때 피부미용 기능을 갖는 수용성 유효성분, 글리세롤, 부틸렌글라이콜 등이 피부로 천천히 스며들며 이때 막 형성 수용성 고분자는 자가 용융되어 일부는 피부에 흡수되고, 고분자에 해당하는 나머지 일부는 흡수되지 못하고 피부 위에 도포된 후 녹아서 사라짐으로써 기존 제품대비 미용효과가 뛰어난 자가 용융 습식 미용시트를 제공한다.As described above, the present invention supplies moisture absorbed from the air and moisture absorbed from the skin to the beauty sheet, and when the crosslink is broken and melts on its own, water-soluble active ingredients, glycerol, and butylene glycol, which have a skin beauty function, are applied to the beauty sheet. Lycol, etc. slowly permeate into the skin, and at this time, the film-forming water-soluble polymer self-melts and part of it is absorbed into the skin, while the remaining part, which corresponds to the polymer, is not absorbed and melts and disappears after being applied on the skin, making it a self-made product with superior beauty effects compared to existing products. We provide melt wet beauty sheets.

본 발명에 개시된 실시예는 본 발명의 기술 사상을 한정하기 위한 것이 아니라, 설명하기 위한 것이고, 이러한 실시예에 의하여 본 발명의 기술 사상의 범위가 한정되는 것도 아니다. 본 발명의 보호 범위는 특허청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.The embodiments disclosed in the present invention are not intended to limit the technical idea of the present invention, but are for explanation, and the scope of the technical idea of the present invention is not limited by these examples. The scope of protection of the present invention should be interpreted in accordance with the scope of the patent claims, and all technical ideas within the equivalent scope should be interpreted as being included in the scope of rights of the present invention.

Claims (12)

피부미용 기능을 갖는 수용성 유효성분, 막 형성 수용성 고분자 및 가교제를 용매에 용해한 방사용액의 전기방사에 의해 상호 가교결합(Cross-linking)된 나노멤브레인에 정제수를 함유하지 않은 세럼을 함침하여 미용시트를 제조하되,
상기 세럼은 글리세롤(Glycerol)과 부틸렌글라이콜(Butylene Glycol) 중 하나 이상의 성분이 혼합되고, 세럼이 함침된 미용시트를 피부에 부착시 세럼은 공기 중의 수분과 피부에 존재하는 수분을 흡수하여 미용시트에 공급함으로써 미용시트가 스스로 용융되고,
상기 나노멤브레인 100 중량% 중 막 형성 수용성 고분자가 10 ~ 30 중량%, 가교제가 1 중량%를 차지하고, 나머지는 피부미용 기능을 갖는 수용성 유효성분으로 구성하여 피부 부착 사용시 공기 중에 분포돼 있는 수분과 피부에 존재하는 수분을 자연 흡수하여 가교결합(Cross-linking)이 풀어짐에 따라 나노멤브레인의 결합이 깨지면서 용융되며,
상기 피부미용 기능을 갖는 수용성 유효성분은 자가 용융되어 피부에 서서히 흡수되며, 상기 막 형성 수용성 고분자는 자가 용융되어 일부는 피부에 흡수되고, 일부는 피부 위에 도포된 후 사라지고,
상기 세럼 100 중량% 중 글리세롤이 30 ~ 90 중량%를 차지하고, 나머지는 히알루론산이 차지하도록 혼합한 것을 특징으로 하는 자가 용융 습식 미용시트.
A beauty sheet is made by impregnating a nanomembrane that is mutually cross-linked by electrospinning of a spinning solution containing water-soluble active ingredients with skin beauty functions, film-forming water-soluble polymers, and a cross-linking agent dissolved in a solvent, with a serum that does not contain purified water. Manufacturing,
The serum is a mixture of one or more ingredients of glycerol and butylene glycol, and when a beauty sheet impregnated with the serum is attached to the skin, the serum absorbs moisture in the air and moisture present on the skin to provide beauty care. By supplying it to the sheet, the beauty sheet melts on its own.
Among 100% by weight of the nanomembrane, the film-forming water-soluble polymer accounts for 10 to 30% by weight, the crosslinking agent accounts for 1% by weight, and the remainder is composed of water-soluble active ingredients with skin care functions, so that when used on the skin, the moisture distributed in the air and the skin As cross-linking is released by naturally absorbing the moisture present in the nanomembrane, the bonds are broken and melted.
The water-soluble active ingredient with the skin care function self-melts and is gradually absorbed into the skin, and the film-forming water-soluble polymer self-melts, some of which is absorbed into the skin, and some of which disappear after being applied on the skin,
A self-melting wet beauty sheet, characterized in that glycerol accounts for 30 to 90% by weight of 100% by weight of the serum, and hyaluronic acid accounts for the remainder.
삭제delete 청구항 1에 있어서,
상기 미용시트의 중량이 1m2 당 1.5 내지 7 그램인 것을 특징으로 하는 자가 용융 습식 미용시트.
In claim 1,
A self-melting wet beauty sheet, characterized in that the weight of the beauty sheet is 1.5 to 7 grams per 1 m 2 .
청구항 1에 있어서,
피부미용 기능을 갖는 수용성 유효성분은 하이드롤라이즈드 콜라겐(Hydrolyzed Collagen), 병풀, 비타민 C, 나이아신아마이드(Niacinamide), 히알루론산(hyaluronic acid), 아데노신(adenosine), 세라마이드(Ceramide) 중에서 선택한 1종 또는 2종 이상의 혼합물을 포함하여 구성하며, 막 형성 수용성 고분자는 폴리비닐알코올(PVA), 폴리비닐피롤리돈(PVP), 풀루란(Pullulan), 아밀로덱스트린(Amylodextrin), 알긴산(Alginic acid) 중에서 선택한 1종 또는 2종 이상의 혼합물을 포함하여 구성하는 것을 특징으로 하는 자가 용융 습식 미용시트.
In claim 1,
The water-soluble active ingredient with skin beauty function is one selected from Hydrolyzed Collagen, Centella asiatica, Vitamin C, Niacinamide, hyaluronic acid, adenosine, and Ceramide. Or, it consists of a mixture of two or more types, and the film-forming water-soluble polymers include polyvinyl alcohol (PVA), polyvinylpyrrolidone (PVP), pullulan, amylodextrin, and alginic acid. A self-melting wet beauty sheet comprising one or a mixture of two or more selected from among.
삭제delete 피부미용 기능을 갖는 수용성 유효성분, 막 형성 수용성 고분자 및 가교제를 용매에 용해한 방사용액의 전기방사에 의해 상호 가교결합(Cross-linking)된 나노멤브레인에 정제수를 함유하지 않은 세럼을 함침하여 미용시트를 제조하되,
상기 세럼은 글리세롤(Glycerol)과 부틸렌글라이콜(Butylene Glycol) 중 하나 이상의 성분이 혼합되고, 세럼이 함침된 미용시트를 피부에 부착시 세럼은 공기 중의 수분과 피부에 존재하는 수분을 흡수하여 미용시트에 공급함으로써 미용시트가 스스로 용융되고,
상기 나노멤브레인 100 중량% 중 막 형성 수용성 고분자가 10 ~ 30 중량%, 가교제가 1 중량%를 차지하고, 나머지는 피부미용 기능을 갖는 수용성 유효성분으로 구성하여 피부 부착 사용시 공기 중에 분포돼 있는 수분과 피부에 존재하는 수분을 자연 흡수하여 가교결합(Cross-linking)이 풀어짐에 따라 나노멤브레인의 결합이 깨지면서 용융되며,
상기 피부미용 기능을 갖는 수용성 유효성분은 자가 용융되어 피부에 서서히 흡수되며, 상기 막 형성 수용성 고분자는 자가 용융되어 일부는 피부에 흡수되고, 일부는 피부 위에 도포된 후 사라지고,
상기 세럼 100 중량% 중 부틸렌글라이콜이 30 ~ 90 중량%를 차지하고, 나머지는 히알루론산이 차지하도록 혼합한 것을 특징으로 하는 자가 용융 습식 미용시트.
A beauty sheet is made by impregnating a nanomembrane that is mutually cross-linked by electrospinning of a spinning solution containing water-soluble active ingredients with skin beauty functions, film-forming water-soluble polymers, and a cross-linking agent dissolved in a solvent, with a serum that does not contain purified water. Manufacturing,
The serum is a mixture of one or more ingredients of glycerol and butylene glycol, and when a beauty sheet impregnated with the serum is attached to the skin, the serum absorbs moisture in the air and moisture present on the skin to provide beauty care. By supplying it to the sheet, the beauty sheet melts on its own.
Among 100% by weight of the nanomembrane, the film-forming water-soluble polymer accounts for 10 to 30% by weight, the crosslinking agent accounts for 1% by weight, and the remainder is composed of water-soluble active ingredients with skin care functions, so that when used on the skin, the moisture distributed in the air and the skin As cross-linking is released by naturally absorbing the moisture present in the nanomembrane, the bonds are broken and melted.
The water-soluble active ingredient with the skin care function self-melts and is gradually absorbed into the skin, and the film-forming water-soluble polymer self-melts, some of which is absorbed into the skin, and some of which disappear after being applied on the skin,
A self-melting wet beauty sheet, characterized in that butylene glycol accounts for 30 to 90% by weight of 100% by weight of the serum, and hyaluronic acid accounts for the remainder.
피부미용 기능을 갖는 수용성 유효성분, 막 형성 수용성 고분자 및 가교제를 용매에 용해한 방사용액의 전기방사에 의해 상호 가교결합(Cross-linking)된 나노멤브레인에 정제수를 함유하지 않은 세럼을 함침하여 미용시트를 제조하되,
상기 세럼은 글리세롤(Glycerol)과 부틸렌글라이콜(Butylene Glycol) 중 하나 이상의 성분이 혼합되고, 세럼이 함침된 미용시트를 피부에 부착시 세럼은 공기 중의 수분과 피부에 존재하는 수분을 흡수하여 미용시트에 공급함으로써 미용시트가 스스로 용융되고,
상기 나노멤브레인 100 중량% 중 막 형성 수용성 고분자가 10 ~ 30 중량%, 가교제가 1 중량%를 차지하고, 나머지는 피부미용 기능을 갖는 수용성 유효성분으로 구성하여 피부 부착 사용시 공기 중에 분포돼 있는 수분과 피부에 존재하는 수분을 자연 흡수하여 가교결합(Cross-linking)이 풀어짐에 따라 나노멤브레인의 결합이 깨지면서 용융되며,
상기 피부미용 기능을 갖는 수용성 유효성분은 자가 용융되어 피부에 서서히 흡수되며, 상기 막 형성 수용성 고분자는 자가 용융되어 일부는 피부에 흡수되고, 일부는 피부 위에 도포된 후 사라지고,
상기 세럼 100 중량% 중 글리세롤과 부틸렌글라이콜이 30 ~ 90 중량%를 차지하고, 나머지는 히알루론산이 차지하도록 혼합하며, 글리세롤과 부틸렌글라이콜은 30 : 70 내지 40 : 60의 중량비로 혼합되는 것을 특징으로 하는 자가 용융 습식 미용시트.
A beauty sheet is made by impregnating a nanomembrane that is mutually cross-linked by electrospinning of a spinning solution containing water-soluble active ingredients with skin beauty functions, film-forming water-soluble polymers, and a cross-linking agent dissolved in a solvent, with a serum that does not contain purified water. Manufacturing,
The serum is a mixture of one or more ingredients of glycerol and butylene glycol, and when a beauty sheet impregnated with the serum is attached to the skin, the serum absorbs moisture in the air and moisture present on the skin to provide beauty care. By supplying it to the sheet, the beauty sheet melts on its own.
Among 100% by weight of the nanomembrane, the film-forming water-soluble polymer accounts for 10 to 30% by weight, the crosslinking agent accounts for 1% by weight, and the remainder is composed of water-soluble active ingredients with skin care functions, so that when used on the skin, the moisture distributed in the air and the skin As cross-linking is released by naturally absorbing the moisture present in the nanomembrane, the bonds are broken and melted.
The water-soluble active ingredient with the skin care function self-melts and is gradually absorbed into the skin, and the film-forming water-soluble polymer self-melts, some of which is absorbed into the skin, and some of which disappear after being applied on the skin,
Out of 100% by weight of the serum, glycerol and butylene glycol account for 30 to 90% by weight, and the remainder is mixed so that hyaluronic acid accounts for, and glycerol and butylene glycol are mixed at a weight ratio of 30:70 to 40:60. A self-melting wet beauty sheet characterized in that.
삭제delete 피부미용 기능을 갖는 수용성 유효성분, 막 형성 수용성 고분자 및 가교제를 용매에 혼합하는 단계;
혼합된 방사용액으로 전기방사하여 수용성 나노멤브레인을 제조하는 단계;
나노멤브레인에 정제수를 함유하지 않은 세럼을 함침하여 미용시트를 제조하는 단계; 및
패치 형태가 유지되도록 미용시트를 건조 숙성하는 단계;를 포함하되,
상기 나노멤브레인을 제조하는 단계에서,
나노멤브레인 100 중량% 중 막 형성 수용성 고분자가 10 ~ 30 중량%, 가교제가 1 중량%를 차지하고, 나머지는 피부미용 기능을 갖는 수용성 유효성분으로 구성하여 피부에 부착 사용시 공기 중에 분포돼 있는 수분과 피부에 존재하는 수분을 자연 흡수하여 가교결합(Cross-linking)이 풀어짐에 따라 나노멤브레인의 결합이 깨지면서 상기 피부미용 기능을 갖는 수용성 유효성분은 자가 용융되어 피부에 서서히 흡수되며, 상기 막 형성 수용성 고분자는 자가 용융되어 일부는 피부에 흡수되고, 일부는 피부 위에 도포된 후 사라지도록 제조되고,
상기 미용시트를 제조하는 단계에서,
상기 세럼 100 중량% 중 글리세롤과 부틸렌글라이콜이 30 ~ 90 중량%를 차지하고, 나머지는 히알루론산이 차지하도록 혼합하며, 글리세롤과 부틸렌글라이콜은 30 : 70 내지 40 : 60의 중량비로 혼합되며,
상기 세럼이 함침된 미용시트를 피부에 부착시 세럼은 공기 중의 수분과 피부에 존재하는 수분을 흡수하여 미용시트에 공급함으로써 미용시트가 스스로 용융되는 것을 특징으로 하는 자가 용융 습식 미용시트의 제조방법.
Mixing a water-soluble active ingredient with a skin care function, a film-forming water-soluble polymer, and a crosslinking agent in a solvent;
Preparing a water-soluble nanomembrane by electrospinning with a mixed spinning solution;
Manufacturing a beauty sheet by impregnating the nanomembrane with a serum that does not contain purified water; and
Including the step of drying and aging the beauty sheet to maintain the shape of the patch,
In the step of manufacturing the nanomembrane,
Out of 100% by weight of nanomembrane, the film-forming water-soluble polymer accounts for 10 to 30% by weight, the cross-linking agent accounts for 1% by weight, and the remainder is composed of water-soluble active ingredients with skin care functions. When attached to the skin, the moisture distributed in the air and the skin are absorbed. As the cross-linking is released by naturally absorbing the moisture present in the nanomembrane, the bonds in the nanomembrane are broken, and the water-soluble active ingredient with the skin care function self-melts and is gradually absorbed into the skin, and the film-forming water-soluble polymer It is manufactured so that it self-melts and some is absorbed into the skin, and some disappears after being applied on the skin.
In the step of manufacturing the beauty sheet,
Out of 100% by weight of the serum, glycerol and butylene glycol account for 30 to 90% by weight, and hyaluronic acid accounts for the remainder, and glycerol and butylene glycol are mixed at a weight ratio of 30:70 to 40:60. ,
A method of manufacturing a self-melting wet beauty sheet, characterized in that when the beauty sheet impregnated with the serum is attached to the skin, the serum absorbs moisture in the air and moisture existing on the skin and supplies it to the beauty sheet, thereby causing the beauty sheet to melt itself.
삭제delete 삭제delete 청구항 9에 있어서,
상기 건조 숙성하는 단계에서,
숙성조건은 섭씨 50 ~ 70 ℃의 온도로 24 ~ 48 시간 숙성하는 것을 특징으로 하는 자가 용융 습식 미용시트의 제조방법.
In claim 9,
In the dry aging step,
A method of manufacturing a self-melting wet beauty sheet, characterized in that the aging condition is aging for 24 to 48 hours at a temperature of 50 to 70 ° C.
KR1020230027068A 2023-02-28 2023-02-28 Self-melting wet beauty sheet and its manufacturing method KR102608317B1 (en)