Abstract

The present invention relates to a manufacturing method for a cloisonne ceramic, which maximizes the decoration and artistry of a cloisonne ceramic by using a cloisonne decoration technique. The manufacturing method for a cloissonne ceramic comprises: a water repellent agent process for spreading a water repellent agent on a space where is to be decorated by cloisonne; an adhesive process for spreading a gauze or a hemp cloth on the space where is to be decorated by cloisonne using an adhesive; a drying process for naturally drying the attached cloth; a rough sketch process for drawing a rough sketch on the ceramic after the cloth is dried; a building-up process for expressing a cubic effect by mixing the rough sketch with whitewash, glue, and paint; a coloring process for performing a coloring work after the building-up process; a cashew process for spreading cashew on the colored drawing and drying the cashew; a re-gold leafing process for performing a re-gold leafing work which attaches gold leafs after the cashew process; a coating process for performing a coating work after the re-gold leafing work and finishing all works. The present invention maximizes the decoration and artistry of the ceramic by freely applying all colors to the ceramic regardless of the strain and discoloration of the ceramic during a plasticizing process. [Reference numerals] (1) Water repellent agent process;(2) Adhesive process;(3) Drying process;(4) Rough sketch process;(5) Building-up process;(6) Coloring process;(7) Cashew process;(8) Re-gold leafing process;(9) Coating process

Description

The Manufacturing Method for a Ceramic Cloisonne

The present invention relates to a method of producing cloisonne pottery that maximizes decorativeness and artistry by using cloisonne decorating techniques by the method.

In the manufacture of ceramics, which are closely related to our lives, glaze is applied to the surface of the ceramics in order to enhance the strength and enhance the resistance to water and chemicals by enhancing the strength and removing the absorbency. Although it was difficult to maximize the decorativeness and artistry of pottery by applying glaze alone, in the manufacture of improved cloisonne pottery, there are still deformities and discolorations during the firing process. There are many restrictions on the expression of colors other than limited colors such as red, blue, and white.

In the manufacturing method of cloisonne pottery, there are still many properties such as deformation and discoloration during the firing process, and in particular, there are many limitations on the expression of colors other than limited colors such as red, blue and white. In addition, this also had a problem that the work process is long, a lot of time and manufacturing costs increase.

The present invention has been made to solve the above problems,

Its subject matter is

Water repellent process (1st process), adhesive process (2nd process), drying process (3rd process), sketch process (4th process), embossing process (5th process), coloring process (6th process), cashew It is composed of nine steps of the process (seventh process), the cutting process (the eighth process), and the finishing coating process (the ninth process), which is not only related to deformation and discoloration in the firing process of the ceramic, It is a revolutionary production method of cloisonne pottery that has the characteristics to maximize the decorativeness and artistry of pottery by allowing all colors to be applied freely to pottery.

The present invention relates to a method of manufacturing a cloisonne pottery that maximizes decorativeness and artistry, which is free from deformation and discoloration during the firing process, and can be applied freely to ceramics, and also to a manufacturing method. This simple and short working time can reduce the production cost, and in particular, significantly reduce the occurrence of defects, which is very practical and economical effect.

The present invention relates to a production method of cloisonne ceramics (극대화) to maximize the decorativeness and artistry by using the cloisonne ornament technique according to the present.

This will be described in detail with reference to the drawings.

How to make it

。 1st process (water repellent process)-In the process of making pottery, make a space in pottery where all or part of cloth can be decorated with cloisonne. After scratching, apply a water repellent to prevent the glaze from penetrating the scratch, and then put it in a kiln and heat it at 1200-1300 ℃ for 24 hours.

。 2nd process (adhesive process) -A gauze cloth or burlap cloth is glued to the space to be decorated with cloisonne on ceramics with adhesive.

。 3rd process (drying process) -After bonding cloth with adhesive, let it dry for about 24 hours.

。 4th process (Draft process)-When the glued cloth is dried, draw a sketch on the ceramics.

。 5th process (Embossing process)-To express the three-dimensional effect by using the mixture of whistle, glue and pigment in the sketch, the figure is embossed to make it look smooth. Allow to dry naturally for 24 hours after the embossing process.

。 6th process (coloring process) -When the embossing process is completed, color work is performed. Allow to dry for 6 hours after coloring.

。 7th process (cashew process) -When the coloring process is completed, apply the curcuits (lacquer) evenly on the colored painting twice and let it dry naturally for 24 hours.

。 8th process (cutting process)-When the cashew process is completed, perform the cutting operation to attach gold leaf.

。 9th process (coating process) -When the cutting work is completed, finish all the work by coating 2 ~ 3 times to protect the above picture.

The present invention is not only related to deformation, discoloration in the firing process of the ceramic, but also to allow all colors to be applied freely to ceramics, there is a feature that can maximize the decorativeness and artistry of ceramics.

1 is a process diagram according to the present invention

* Drawing code

1-water repellent process (first process) 2-adhesive process (second process) 3-drying process (third process)

4-Draw process (4th process) 5-Elevation process (5th process) 6-Color process (6th process)

7-cashew process (7th process) 8-rolling process (8th process) 9-coating process (ninth process)

Claims (1)

In the production of cloisonne pottery, Water-repellent process that creates a space for the cloth to be decorated with cloisonne, scratches it so that the adhesive can stick to the space, then applies a water repellent to the scratch, and then puts it in a kiln and heats it at 1200-1300 ℃ for 24 hours. 1 step), Glue cloth or burlap cloth in the space to be decorated with cloisonne on the porcelain using adhesive (Second step), Drying process for natural drying for about 24 hours after adhering the cloth with adhesive (Step 3) ), When the glued fabric is dried, the sketching process (the fourth process), which draws the sketch on the ceramics, is a mixture of whistle, glue, and pigment, and the embossing process is dried for 24 hours after embossing to express the three-dimensional effect on the sketch. (5th process), the coloration process (the 6th process) which is dried for about 6 hours after the coloring work when the embossing process is completed, and the curch (lacquer) is applied twice on the painted picture when the coloring process is completed. The cashew process (the seventh process), which is evenly applied and dried for 24 hours, the carpentry process (the eighth process) which performs the gold cutting operation to attach the gold leaf when the cashew process is completed; Method of producing a cloisonne pottery characterized in that the production in the order of the coating step (ninth step) to finish all the work.