KR20130123133A - A towel having the function of massage of skin - Google Patents

Abstract

The present invention relates to a scrubber fabric having a skin massage function. The scrubber fabric is woven with a woven yarn obtained by primary twisting of two strands of fiber yarns having 30-300 denier at 1200-2700 TPM in a direction of S or Z, and secondary complex twisting of the primary twisted two strands of fiber yarns while one strand thereof is twisted at 600-1300 TPM in a direction of Z or S. The woven yarn is used to weave the scrubber fabric by using a weaving machine. Here, files with a length of 2-10 mm are further formed on one surface of the scrubber fabric by using a file forming machine, thereby reducing the friction of the scrubber fabric with the skin of a user, so that the rubber fabric is provided as a towel having smooth feeling. Alternatively, only the primary twisted fiber yarns are used to weave the scrubber fabric, without secondary complex twisting, and then a file formation surface, in which files with a length of 5 mm or smaller are generated, is further formed on one surface or both surfaces of the rubber fabric.

Description

A TOWEL HAVING THE FUNCTION OF MASSAGE OF SKIN}

The present invention relates to a fabric of a wheat flour tool having a skin massage function, and more particularly, by applying to the user's skin to improve the problems of conventional wheat towel, and give a cushioning skin massage feeling in addition to the wheat flour function The present invention relates to the provision of a towel having a constitution in which the cleaning and massage effects are simultaneously provided.

Towels or gloves for use in showers and baths are used to fabricate a grime-free cloth as a separate component from general fabrics.

Most towels, such as shower towels and gloves, use viscose yarn as a means to impart roughness without causing pain to the skin so that the body's time can be removed by mechanical friction. Most of the construction is manufactured.

In the case of the conventional fabric of the milling tool of such a configuration, when used by being processed with a towel or a glove or the like, the structure in which the projected projections contact the body to impart friction and thereby remove the dirt or the projections exert excessive force on the body Recently, there is a problem that does not meet the consumer's desire for gentle cleaning.

In view of these problems, the inventors and applicants of the present application filed under Patent Application No. 10-1999-0054032 and registered as of April 26, 2002, 'The method of composite yarn processing for skin massage fiber yarn' of Patent No. 10-0334464. In,

The present invention relates to a composite yarn processing method of fiber yarn for skin massage, and it is the purpose of knitting fibers and gloves with the same fiber yarn to prevent the skin from being damaged due to friction when used for skin massage.

In this application, the loop-shaped fiber yarn structure provides excellent ventilation and cushioning with the skin, so that when it is on the skin and foreign matter, the foreign matter falls off and the damage of the skin is eliminated. The setting work can be eliminated and dye can be obtained to obtain a high-quality skin massage fabric.

In the earlier application, in order to achieve this purpose, two strands of 70-150 denier fibers were twisted at 1200-2700 TPM in the primary S direction or the Z direction, respectively, and one strand of two strands of the primary twisted yarn was twisted. The 600-1300TPM discloses the technical structure which processed by 2nd composite twisting in the Z direction or the S direction.

In the case of knitting in the form of a knitted fabric or a glove having a looped structure for skin massage using the fiber yarn of the present application, the knitted knitted fabric or the glove is densely ventilated due to the loop shape and the loop structure is The fabric, which is knitted with loop-fiber fibers when friction with the skin does not occur, has ventilation and cushions to remove the damage to the skin. It has been proposed a configuration having an effect that is easily separated.

In the applicant's source as described above, two strands of 70-150 denier fiber yarns are twisted at 1200-2700TPM in the primary S direction or Z direction, respectively, in order to form a loop-shaped fiber yarn structure, and the primary yarns It is judged that two strands of fiber yarn with 600-1300TPM in the second or second composite yarn are processed to be suitable for pushing the body's adherent time.Towels, gloves, and towels are used as a grime tool. It is manufactured as a structure, etc., and is actually used widely.

However, in recent years, most of the bath facilities are spread in each home, and a simple body washing with a shower or the like is used in most cases, and it is very rare to push the time routinely at home.

Therefore, the above-described configuration of the source of the above-mentioned source composition is very rough to be used as a shower towel or bath towel which does not push in spite of various advantages, and is not suitable because it gives excessive friction to the user's skin. No proved to be.

In view of these problems, the inventor of the present invention adopts a technical desirable effect of the previous application as it is, a configuration suitable for use in the shower, that is, a light skin massage function and a cleaning function by cushioning the skin when the user's body is washed. At the same time, it provides a fabric suitable for wheat flour tools having a skin massage function of improved effect by further devising a constitution.

When the fabric of the wheat flour tool having a skin massage function according to the configuration of the present invention is used as a towel, gloves, etc., various characteristics of the source of the inventor

Minimizes the damage of the skin caused by friction, makes it easy to remove the dirt, and because of the looped fiber structure, the ventilation condition is excellent and the cushioning with the skin has a good time to remove the dirt and foreign matter on the skin While the effect that the damage of the disappears just has,

The present invention provides a configuration suitable as a towel for a shower or a bath having a configuration capable of soft cleaning by imparting a cushioning feeling without impairing the user's skin.

1 is a process flow diagram for manufacturing a fabric of wheat flour using a massage function of the first embodiment to which the technique of the present invention is applied.
Figure 2 is a schematic diagram showing the pile formation of the fabric of wheat flour using the skin massage function applied technology of the present invention.
Figure 3 is an explanatory diagram showing the fabric of the wheat flour using the skin massage function applied technology of the present invention.
Figure 4 is a photograph showing the pile forming surface in the fabric of the wheat flour using the skin massage function applied technology of the present invention.
Figure 5 is a photograph showing the pile non-forming surface in the fabric of the wheat flour using the skin massage function applied technology of the present invention.
Figure 6 is a perspective view of a glove configured using the fabric of the wheat flour using the skin massage function applied technology of the present invention.

Hereinafter, with reference to the accompanying drawings and photos will be described a preferred configuration and operation of the present invention for achieving the above object.

1 is a process flow chart for manufacturing the configuration of the first embodiment of the fabric of the wheat flour using the skin massage function applied technology of the present invention, Figure 2 is a file of the fabric of the wheat flour using a skin massage function applied technology of the present invention Figure 3 is a schematic diagram showing the formation, Figure 3 is an explanatory view showing the fabric of the wheat flour tool having a skin massage function to which the technique of the present invention is applied, Figure 4 is a file forming of the fabric of the wheat flour tool having a skin massage function to which the technique of the present invention is applied Photograph showing the surface, Figure 5 is a photograph showing the non-formed surface of the fabric of the wheat flour milling tool having a skin massage function to which the technique of the present invention is applied.

[First Embodiment]

A first preferred embodiment of the present invention is the invention of the use of the fiber yarn manufactured in the composite yarn processing method of the 'applicant's skin massage fiber yarn of Patent No. 10-0334464 of the applicant,

Two strands of 70-150 denier fibers are twisted at 1200-2700 TPM in the primary S direction or Z direction, respectively, and as shown in FIG. 3, the two strands of primary yarns S1 and S2 are twisted. One strand of 600-1300TPM is processed by the secondary composite yarn in the Z direction or the S direction to be used as the weaving yarn of the fabric of the wheat flour tool having basic skin massage function.

In the crew, two strands of 70-150 denier fiber yarns were twisted at 1200-2700 TPM in the primary S direction or Z direction, respectively, but 30 to 300 denier in the user's feedback response following its use. It has been found that the primary yarns using the fiber yarn are in the range of obtaining the same effect.

Therefore, the process for manufacturing the fabric of the wheat flour using the skin massage function of the present invention, as shown in Figure 1, as follows.

Two strands of 30 to 300 denier fibers are twisted at 1200-2700TPM in the primary S or Z direction, respectively, and one strand of two strands of primary twisted yarn (S1, S2) is 600-1300TPM. As a weaving yarn, a second composite twisted and processed in the Z direction or the S direction is adopted (100).

Using the weaving yarn as described above, weaving fabric (T) for the milling tool using a weaving machine.

The file forming surface (FS) for generating the file (F: file) in the range of 2 ~ 10mm in length on one surface is put into the conventional file forming machine (FM) for the woven fabric for milling tool. (120)

For the user's convenience, for example, 80 * 20 cmm in length and width, and the edge of the pile forming surface (FS) for which the pile-forming surface (FS) is generated, and the edges are sewn (E) and the entire towel (W) (130).

In the above manufacturing process, the pile forming machine FM is a conventional processing machine, and as shown in FIG. 2, the pile milling material T is put into the pile forming machine FM mounted to reciprocate the blade K as shown in FIG. 2. F) is raised.

As shown in the enlarged photograph of the portion A of the towel W of FIG. 3 showing the pile forming machine FM on which the pile F of FIG. 4 is formed, a part of the twisted fiber yarn is cut and raised as the pile F, thereby smoothing friction. It can be seen that it forms a surface.

Preferably, the pile forming surface (FS) is formed on any one surface of the milling tool fabric (T) and the other surface is the pile non-forming surface (NF) by exposing and weaving a combustible fiber yarn such as a prior application as it is used for milling and It can be used in combination for washing soap.

FIG. 4 is an enlarged view of a portion A of the towel W of FIG. 3 showing the pile forming machine FM on which the pile F is formed, and FIG. 5 is a diagram made of combustible work such as a prior application of the pile non-forming surface NF. It is an enlarged view of part B of 3.

[Second Embodiment]

The second preferred embodiment of the present invention uses a fiber yarn manufactured in the 'composite yarn processing method of the fiber yarn for skin massage' of Patent No. 10-0334464 of the applicant of the applicant,

Weaving only the first fiber yarn without the second composite yarn using only the first yarn twisted by twisting two strands of 30 to 300 denier fibers in the primary S direction or the Z direction at 1200-2700 TPM, respectively. As a speaker.

Only the primary twisted fiber yarn is used to weave the fabric for milling tools.

The file forming surface FS is formed in the range of the length of 5 mm or less in the file (F: file) on one surface by inputting to the conventional file forming machine (FM) for the woven fabric for milling tools.

For the user's convenience, for example, 80 * 20 cmm in length and width is cut and the corners are finished with a punching edge (G). (W), or as shown in Fig. 6 constitutes a grit-shaped gripping groove (G).

[Third Embodiment]

In a third preferred embodiment of the present invention, in the case of rayon, two strands of 30 to 300 denier fibers are used in the primary S direction or Z direction, respectively, in the range of 50 to 2,400 TPM in the case of rayon. Using only the first twisted fiber yarn by selectively selecting and twisting according to the length and denier value of rayon,

Experimental results have shown that it is preferable to prepare only the primary fiber yarns as weaving yarns without the secondary composite yarns to prepare the fabric for milling use of the grains (T).

[Fourth Embodiment]

In a fourth preferred embodiment of the present invention, if the fiber used is a kind of chemical yarn,

When wound in a zigzag shape and treated by heat setting, it was found that, as in the above embodiment, the pile may be formed by weaving only a single yarn without a twisting process.

That is, 30 ~ 300 denier chemical yarns are wound in a perm shape and thermally set, and the winding yarn value is taken within the range of 50 ~ 2,400 TPM, but as the length of the file becomes longer, the value of TPM should be increased. Of course.

While the fabric of the wheat flour using the skin massage function produced by various methods as described above retains all the effects of the fiber yarn of the applicant's source,

The pile is formed to act like a number of cilia (纖毛) to form a smooth use surface to give a cushion to the user and to have an optimal configuration to use as a towel for a variety of purposes, such as using a mil or shower or bath.

F: file
FS: File Formation Surface
T: Towel Fabric

Claims (5)

Two strands of 30 to 300 denier fibers are twisted at 1200-2700TPM in the primary S or Z direction, respectively, and one strand of two strands of primary twisted yarn (S1, S2) is 600-1300TPM. In the fabric of the wheat flour tool having a skin massage function of weaving the second composite yarn in the Z direction or the S direction to the weaving yarn;
Using the weaving yarn (S), weaving the milling tool fabric (T) using a weaving machine,
As a towel (W) to form a soft (F: file) of 2 ~ 10mm in length with a file forming machine (FM) on one side of the fabric for the use of the milling tool (T) to reduce friction on the user's skin Fabric of wheat flour tool having a skin massage function, characterized in that provided. Weaving two strands of 30 to 300 denier fibers by 1200-2700TPM in the primary S-direction or Z-direction, respectively, using only the primary twisted yarn, and only the primary yarn without the secondary composite yarn Weaving as a weaving machine for weaving the milling tool (T)
It has a skin massage function, characterized in that to form a file forming surface (FS) for generating a file (F: file) in the range of the length of 5 mm or less on one surface or both surfaces with respect to the fabric for milling tool (T) Fabric of wheat grinder. 3. The method of claim 2,
In the case of the rayon yarn, two strands of 30 to 300 denier fibers are selected and twisted according to the length of the pile and the rayon denier within the range of 50 to 2,400 TPM in the primary S direction or the Z direction, respectively. By using only the first twisted fiber yarn, the fabric of the flour milling tool having a skin massage function, characterized in that the fabric for the flour milling material (T). In the case of a chemical yarn that is woven for the milling use fabric (T), the yarn of the chemical yarn of 30 to 300 deniers is wound into a perm shape and thermally set, and the winding yarn value is in the range of 50 to 2,400 TPM. Assemble and weave a fabric for the use of grain mill (T),
Forming a file on one or both sides of the flour milling material fabric (T), the longer the length of the pile, the fabric of the wheat flour tool having a skin massage function, characterized in that to increase the value of the TPM. The method according to claim 1, 2 or 4,
The pile forming surface (FS) generated in the milling tool fabric (T) may be applied to one or both sides of the milling tool fabric (T),
The dough mill material (T) is a dough mill having a skin massage function, characterized in that it can be molded into a towel or gloves as a milling tool.