KR20120089165A - landscaping facility surface protecting method using natural earth - Google Patents

landscaping facility surface protecting method using natural earth Download PDF

Info

Publication number
KR20120089165A
KR20120089165A KR1020110010829A KR20110010829A KR20120089165A KR 20120089165 A KR20120089165 A KR 20120089165A KR 1020110010829 A KR1020110010829 A KR 1020110010829A KR 20110010829 A KR20110010829 A KR 20110010829A KR 20120089165 A KR20120089165 A KR 20120089165A
Authority
KR
South Korea
Prior art keywords
natural
liquid
powder
soil
mixing
Prior art date
Application number
KR1020110010829A
Other languages
Korean (ko)
Inventor
김창영
지석중
Original Assignee
김창영
(주)태창그린조경
지석중
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김창영, (주)태창그린조경, 지석중 filed Critical 김창영
Priority to KR1020110010829A priority Critical patent/KR20120089165A/en
Publication of KR20120089165A publication Critical patent/KR20120089165A/en

Abstract

PURPOSE: A surface protective process for a natural landscape facility using natural soil is provided to use eco-friendly materials only for protecting roadside trees and flowerpots. CONSTITUTION: A surface protective process for a natural landscape facility using natural soil comprises the following steps: watering the surface of roadside trees and movable or fixable flowerpots, removing the soil on the surface in the thickness of 5-15cm, and pressuring the surface of the soil for firstly hardening; mixing washed silica, zeolite aggregate, pozzolanic aggregate, coco peat, gypsum, nature cellulose fibers, and other materials to obtain a powder material; mixing the powder material with a liquid mixture obtained by diluting a liquid fertilizer undiluted solution with 90-110 times amount of water, and a liquid solidification material to obtain a liquid phase material; mixing 55-65% of powder material and 35-45% of liquid phase material to obtain a surface protective material; spreading the surface protective material on the soil around the roadside trees and movable or fixable flowerpots, and secondly hardening the soil; and curing the spread surface protective material.

Description

자연토를 이용한 자연조경시설 표면보호 공법{landscaping facility surface protecting method using natural earth}Landscaping facility surface protecting method using natural earth}

본 발명은 자연토를 이용한 자연조경시설 표면보호 공법에 관한 것으로서, 보다 상세하게는 가로수 및 화분 등과 같은 자연조경시설을 보호하기 위해 표면에 설치되는 보호판을 친환경적으로 대체하는 자연토를 이용한 자연조경시설 표면보호 공법에 관한 것이다.The present invention relates to a natural landscaping facility surface protection method using natural soils, and more particularly, natural landscaping facilities using natural soils to replace environmentally friendly protection plates installed on the surface to protect natural landscaping facilities such as roadside trees and pots. It relates to a surface protection method.

일반적으로 도로변이나 아파트 주변 산책로, 공원 등지에는 쾌적한 도시 및 주거환경을 조성하기 위하여 가로수 및 화분(이동식 또는 고정식 화분)들이 곳곳에 식재되어 있다. 이러한 가로수들은 차동차들의 배기가스를 흡수 정화하여 신선한 공기를 공급하는 등 환경 정화, 공해방지, 환경미화, 소음방지 등에 커다란 기여를 하고 있다.In general, roadside trees and potted plants (portable or fixed pots) are planted in various places on the roadside, promenades and parks around the apartments to create a pleasant urban and residential environment. These trees have contributed greatly to environmental purification, pollution prevention, environmental beautification and noise prevention by absorbing and purifying the exhaust gas of differential cars to supply fresh air.

가로수 보호커버는 이러한 가로수의 보호를 위해 설치되는 구조물로서, 종래의 가로수 보호커버가 도 1 에 도시된다. 도시된 바와 같이, 종래에는, 가로수가 식재된 지면에 가로수를 둘러싸는 금속재 덮개판(10)이 씌워지고, 덮개판(10)의 외측에 벽돌이나 나무등으로 구성된 경계틀(100)이 설치된다.Roadside protection cover is a structure installed for the protection of the roadside, a conventional roadside protection cover is shown in FIG. As shown, in the related art, a metal cover plate 10 surrounding a roadside tree is covered on a ground in which a roadside is planted, and a boundary frame 100 made of bricks, trees, etc. is installed outside the cover plate 10. .

그러나, 도 2는 안전상의 문제가 있는 가로수 보호 덮개들을 보여주는 도면이다. 예컨대 도 2b와 같이 경계틀(100)이 벽돌로 구성되는 경우에는, 보행자가 지면위로 돌출된 벽돌에 걸려 넘어지거나 하는 사례가 빈번하게 발생하고 있으며, 도 2c와 같이 금속재 덮개가 외부로 이탈되게 될 경우에도 통행의 불편을 주는 문제점이 있었다.However, FIG. 2 is a view showing roadside protective covers having safety problems. For example, when the boundary frame 100 is made of bricks, as shown in Figure 2b, there are frequent occurrences of pedestrians trip over the bricks protruding above the ground, and as shown in Figure 2c the metal cover will be separated to the outside Even when there was a problem of passing inconvenience.

도 3 및 4는 오염된 상태의 가로수 보호 덮개들을 보여주는 도면이다. 도 3 및 4를 참조하면, 종래의 가로수 보호커버는 그레이팅 사이에 각종 오물등이 끼거나 들어가는 문제와, 오염물질이 주변에 쌓이는 문제가 있어 주변경관을 해치며 가로수 등과 같은 식재의 성장을 방해하여 가로수를 고사하는 등의 문제점이 있었다.3 and 4 are diagrams showing the roadside protective cover in a contaminated state. Referring to Figures 3 and 4, the conventional roadside protection cover has a problem that the various dirts, etc. between the grating and the entering, and contaminants accumulate around the harm to the surrounding landscape and hinder the growth of plants such as roadside trees There was a problem such as a row of trees.

상술한 문제점을 해결하기 위한 본 발명의 목적은, 가로수 및 화분 등과 같은 자연조경시설을 보호하기 위해 표면에설치되는 보호판 필요없이 친환경적인 재료만을 이용하여 자연조경시설 표면을 보호할 수 있도록 하는 자연토를 이용한 자연조경시설 표면보호 공법을 제공하는 데 있다.An object of the present invention for solving the above problems, natural soil to protect the surface of the natural landscaping facilities using only environmentally friendly materials without the need for a protective plate installed on the surface to protect the natural landscaping facilities such as roadside trees and pots To provide a surface protection method for natural landscaping facilities.

또한, 본 발명의 다른 목적은, 균일한 시공품질을 유지할 수 있도록 하는 자연토를 이용한 자연조경시설 표면보호 공법을 제공하는 데 있다.In addition, another object of the present invention is to provide a natural landscaping facility surface protection method using natural soil to maintain a uniform construction quality.

상기 목적을 달성하기 위한 본 발명에 따른 자연토를 이용한 자연조경시설 표면보호 공법은, (A) 가로수 또는 이동식 고정식 화분 표면에 물을 살수한 후, 5 ? 15cm 두께로 표층을 겉어 낸 후, 상기 표면에 압력을 가해 1차로 다져주는 시공준비 단계와, (B) 1 ? 5mm 크기의 세척규사 52 ? 56％, 제오라이트 골재 18 ? 22％, 포졸란 골재 8 ? 10％, 야자코코피트 7 ? 8, 석고 4 ? 6％, 10mm 이하규격의 천연 셀룰로스 화이버 2.5 ? 3.5％, 포졸란 분말과 목초액을 배합한 펠릿형 분말재 0.5 ? 1.5％를 포함하는 분말 조성물에, 에테르 전분 0.3 ? 0.5％, MC증점제 0.25 ? 0.35％, 주석산 0.10 ? 0.14％, 공기연행재 0.0001 ? 0.0003％를 포함하는 보조 조성물을 혼합하여 생성된 분말재에, 수목생장 촉진 및 토양개량재인 액상비료 원액 4 ? 6％를 물에 90 ? 110배로 희석한 액상 혼합물 45 ? 55％에 액상 고화재 45 ? 55％를 혼합하여 생성된 액상재를 서로 혼합하되, (C) 상기 분말재는 55 ? 65％로 상기 액상재는 35 ? 45％로 혼합, 반죽하여 표면보호재를 생성하는 단계와, (D) 상기 B 단계를 통해 생성된 표면 보호재를 상기 A 단계를 통해 정리된 상기 모토 표면에 포설한 후, 2차로 다져주는 단계 및 (F) 일정시간이 동안 상기 D 단계를 통해 포설된 상기 표면 보호재를 양생시키는 양생단계를 포함하는 것을 특징으로 한다.Natural landscaping facility surface protection method using a natural soil according to the present invention for achieving the above object, (A) after spraying water on the roadside or mobile fixed potted plant surface, 5? After the surface layer is 15 cm thick, the construction preparation step is performed by applying pressure to the surface to prepare the first step, and (B) 1? 5mm washing silicate 52? 56% Zeolite Aggregate 18? 22%, pozzolan aggregate 8? 10%, palm coco feet 7? 8, plaster 4? 6% natural cellulose fiber 2.5 mm or less 0.5% of pellet type powder material which mixes 3.5% of pozzolanic powder and wood vinegar solution To the powder composition containing 1.5%, ether starch 0.3? 0.5%, MC thickener 0.25? 0.35%, tartaric acid 0.10? 0.14%, Air Entrainment 0.0001? To the powder material produced by mixing the auxiliary composition containing 0.0003%, the liquid fertilizer stock solution 4? 90% 6% in water Liquid mixture diluted 110-fold 45? Liquid solidified material at 55% 45? 55% of the liquid material produced by mixing with each other, but (C) the powder material is 55? 65% of the liquid material is 35? Mixing and kneading at 45% to produce a surface protective material, and (D) placing the surface protective material generated through the B step on the surface of the motto arranged through the A step, and then slicing the second step; F) curing the surface protective material laid through the step D for a predetermined time period.

또한, 본 발명에 따른 자연토를 이용한 자연조경시설 표면보호 공법은, (a) 가로수 또는 이동식 고정식 화분 표면인 모토를 평탄하게 정리하는 시공준비 단계와, (b) 1 ? 5mm 크기의 세척규사 25 ? 29％, 제오라이트 골재 22 ? 26％, 포졸란 골재 22 ? 24％, 야자코코피트 11 ? 13, 석고 7 ? 9％, 10mm 이하규격의 천연 셀룰로스 화이버 4 ? 6％, 포졸란 분말과 목초액을 배합한 펠릿형 분말재 0.5 ? 1.5％를 포함하는 분말 조성물에, 에테르 전분 0.4 ? 0.6％, MC증점제 0.25 ? 0.35％, 주석산 0.140 ? 0.150％, 공기연행재 0.0002 ? 0.0004％를 포함하는 보조 조성물을 혼합하여 생성된 분말재에, 수목생장 촉진 및 토양개량재인 액상비료 원액 4.5 ? 5.5％를 물에 90 ? 110배로 희석한 액상 혼합물 45 ? 55％에 액상 고화재 45 ? 55％를 혼합하여 생성된 액상재를 서로 혼합하되, (c) 상기 분말재는 55 ? 65％로 상기 액상재는 36 ? 40％로 혼합, 반죽하여 표면보호재를 생성하는 단계와, (d) 상기 b 단계를 통해 생성된 표면 보호재를 상기 a 단계를 통해 정리된 상기 모토 표면에 포설하는 단계 및 (f) 일정시간이 동안 상기 d 단계를 통해 포설된 상기 표면 보호재를 양생시키는 양생단계를 포함하는 것을 특징으로 한다.In addition, the natural landscaping facility surface protection method using the natural soil according to the present invention, (a) a construction preparation step for smoothly arranging the motto which is a roadside tree or a mobile fixed potted plant surface, and (b) 1? 5mm cleaning silica 25? 29% Zeolite Aggregate 22? 26%, pozzolan aggregate 22? 24%, palm coco feet 11? 13, plaster 7? 9%, less than 10mm natural cellulose fiber 4? 0.5% of pellet type powder material which blended 6%, pozzolan powder and wood vinegar solution To the powder composition containing 1.5%, ether starch 0.4? 0.6%, MC thickener 0.25? 0.35%, tartaric acid 0.140? 0.150%, Air Entrainment 0.0002? To the powder material produced by mixing the auxiliary composition containing 0.0004%, the liquid fertilizer stock solution 4.5? 90% to 5.5% in water Liquid mixture diluted 110-fold 45? Liquid solidified material at 55% 45? 55% of the liquid material produced by mixing with each other, but (c) the powder material is 55? 65% of the liquid material is 36? Mixing and kneading at 40% to produce a surface protective material; (d) disposing the surface protective material produced in step b on the surface of the motto arranged through step a; and (f) for a predetermined time. It characterized in that it comprises a curing step of curing the surface protective material installed through the step d.

또한, 상기 (D) 단계 또는 (d) 단계는, 상기 모토 표면 상부에 망사형의 보조 매트를 배치하거나, 상기 모토 표면에 포설된 상기 표면 보호재의 상부에 상기 보조 매트가 배치되는 단계를 더 포함하는 것을 특징으로 한다.In addition, the step (D) or (d) further comprises the step of placing the auxiliary mat of the mesh type on the surface of the moto, or the auxiliary mat is disposed on top of the surface protective material installed on the surface of the moto. Characterized in that.

또한, 상기 보조 매트는, 자연소재인 볏짚으로 이루어지며, 정형 또는 부정형태의 망형으로 형성되는 것을 특징으로 한다.In addition, the auxiliary mat is made of a straw straw, which is a natural material, characterized in that formed in a net form of a regular or irregular form.

또한, 상기 액상고화재는, 특수 공중합액상 아크 릴액상 폴리머(Pure-Acrylic Emulsion)47?55％, 리튬 실리 케이트(Lithiym Sithium Silicate)10?15％, 폴리카르복실 산(Polycarbonate Acid) 3?5％ 라우릴 황산 나트륨(SodiumLauryl Sulfate)0.025?0.05％, 글루콘산 나트륨(Sodium Gluconate)2?4％와 표면장력을 감소 처리한 물을 혼합하여 침투 유동성이 좋도록 처리하는 것을 특징으로 한다.In addition, the liquid solid material is a special copolymer liquid acrylic polymer (Pure-Acrylic Emulsion) 47-55%, lithium silicate (Lithiym Sithium Silicate) 10-15%, polycarboxylic acid (Polycarbonate Acid) 3-5 % Sodium Lauryl Sulfate (0.025 ~ 0.05%), Sodium Gluconate (Sodium Gluconate) 2 ~ 4% and the surface tension is reduced by mixing the treated water characterized in that the treatment to improve the fluidity.

또한, 상기 액상고화재는, 셀룰로스 화이버(Cellulose Fiber)2?5％,폴리 비닐 알콜화이버(Poly Vinyl Alcohol Fiber)2?5％를 첨가하는 것을 특징으로 한다.In addition, the liquid solid material is characterized in that the addition of cellulose fiber (Cellulose Fiber) 2-5%, polyvinyl alcohol fiber (2-5%).

또한, 상기 액상고화재는, 혼합수를 제외한 분말 형태로 제조되는 것을 특징으로 한다.In addition, the liquid solidifying material is characterized in that it is produced in the form of powder except the mixed water.

본 발명은, 자연조경시설 표면에 설치되는 금속 또는 합성수지재 보호판 없이도 자연토를 충분한 강도와 내구성을 갖도록 제작할 수 있어, 시공비용을 절감할 수 있고, 환경 친화적이며, 평평하기 때문에 돌출되지 않아 보행자의 안전을 확보할 수 있어 안정성도 좋으며, 분말재와 액상재를 섞어 현장에서 간편하게 사용할 수 있으므로, 작업자들이 사용하는 것이 간편한 장점이 있다.The present invention can produce natural soil with sufficient strength and durability without the metal or synthetic resin protective plate installed on the surface of the natural landscaping facility, can reduce the construction cost, environmentally friendly, flat, so as not to protrude Safety can be ensured, stability is also good, and the powder and liquid materials can be easily mixed in the field, workers have the advantage of easy to use.

또한, 차후 보수가 필요할 경우, 간단하게 적당량을 살수방식으로 도포하여 수명을 증가시킬 수 있어 유지보수가 간편한 장점이 있다.In addition, when the maintenance is required in the future, it is possible to increase the life by simply applying a suitable amount in a spraying method has the advantage of easy maintenance.

또한, 친환경 무기계열 안료를 사용하여 간단한 방법으로 다양한 색상을 연출할 수 있는 효과가 있다.In addition, there is an effect that can produce a variety of colors by a simple method using an environmentally friendly inorganic pigment.

또한, 특별한 기술과 장비가 필요치 않으므로 공공근로 사업 적용시 고령의 작업자들이 작업하는 것이 용이한 장점이 있다.In addition, since there is no need for special skills and equipment, there is an advantage that it is easy for older workers to work when applying for public work projects.

도 1은 종래의 가로수 보호커버를 나타내는 도면이다.
도 2는 도 2는 안전상의 문제가 있는 가로수 보호 덮개들을 보여주는 참고도면이다.
도 3 및 4는 오염된 상태의 가로수 보호 덮개들을 보여주는 도면이다.
도 5는 자연토를 이용한 자연조경시설 표면보호 공법의 블럭도이다.
도 6은 본 발명에 따른 표면 보호재를 모토 상면에 포설한 상태의 단면도이다.
도 7은 본 발명에 따른 표면 보호재와 모토 사이에 보조 매트를 배치한 상태의 단면도이다.
도 8은은 본 발명에 따른 표면 보호재를 가로수에 시공한 상태의 도면이다.1 is a view showing a conventional roadside protective cover.
FIG. 2 is a reference view showing the roadside protective covers of FIG. 2 having safety problems.
3 and 4 are diagrams showing the roadside protective cover in a contaminated state.
5 is a block diagram of a natural landscaping facility surface protection method using natural soil.
6 is a cross-sectional view of the surface protective material according to the present invention placed on the upper surface of the motto.
7 is a cross-sectional view of the auxiliary mat disposed between the surface protective material and the motto according to the present invention.
8 is a view showing a state in which the surface protective material according to the present invention installed on the roadside tree.

이하, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 본 발명을 용이하게 실시할 수 있을 정도로 상세히 설명하기 위하여, 본 발명의 바람직한 실시예를 첨부한 도면을 참조하여 상세하게 설명한다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings so that those skilled in the art can easily carry out the present invention.

물론, 하기에서 본 발명을 설명함에 있어 관련된 공지 기능 또는 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명은 생략될 수 있다.Of course, in the following description of the present invention, if it is determined that the detailed description of the related known functions or configurations may unnecessarily obscure the subject matter of the present invention, the detailed description may be omitted.

도 3은 자연토를 이용한 자연조경시설 표면보호 공법의 블럭도이고, 도 4는 본 발명에 따른 표면 보호재를 모토 상면에 포설한 상태의 단면도이며, 도 5는 본 발명에 따른 표면 보호재와 모토 사이에 보조 매트를 배치한 상태의 단면도이다.Figure 3 is a block diagram of a natural landscaping facility surface protection method using natural soil, Figure 4 is a cross-sectional view of the surface protective material according to the present invention installed on the surface of the motto, Figure 5 is a surface protective material and motto between the present invention It is sectional drawing of the state which has arrange | positioned the auxiliary mat.

도 3 내지 도 5를 참조하면, 본 발명의 일실시예에 따른 자연조경시설 표면보호 공법, 시공준비단계(S110), 분말재와 액상재를 혼합하는 단계(S120), 표면보호재(112)를 생성하는 단계(S130), 표면보호재(112)를 포설하는 단계(S140) 및 양생단계(S140)를 포함한다.3 to 5, the natural landscaping facility surface protection method according to an embodiment of the present invention, the construction preparation step (S110), the step of mixing the powder material and the liquid material (S120), surface protection material 112 It generates a step (S130), the step of laying the surface protection material 112 (S140) and curing step (S140).

상기 시공준비단계(S110)는, 가로수 또는 화초의 표면에 지반을 평탄(돌 고르기 등)하고, 오물, 이물질 등을 제거한 후, 표면에 소량의 물을 살수한 후, 5 ? 15cm 두께로 표층을 걷어 낸다. 이후, 상기 표면에 적당량의 압력을 가해 다져준다. 또한 특수 한 경우에는 바탕면에 50 ? 50 mm규격의 메쉬를 설치 할 수 있으며, 조건이 열악한 경우 사전에 소량의 물에 특수 폴리머를 사전 배합하여 살수 할 수도 있을 것이다.In the construction preparation step (S110), after the ground is flat (stone picking, etc.) on the surface of road trees or flowers, and removes dirt, foreign substances, etc., after spraying a small amount of water on the surface, 5? Roll out the surface layer to a thickness of 15 cm. Thereafter, an appropriate amount of pressure is applied to the surface. Also in special cases 50? 50 mm mesh can be installed and special conditions can be pre-mixed with a small amount of water if the conditions are poor.

그 다음, 분말재와 액상재를 혼합하는 단계(S120)는, 분말재에 액상제를 서로 혼합한다.Next, in step S120 of mixing the powder material and the liquid material, the liquid agent is mixed with the powder material.

여기서 분말재와 액상재의 제조는 사전에 제조된 조성물로, 1 ? 5mm 크기의 세척규사 52 ? 56％, 제오라이트 골재 18 ? 22％, 포졸란 골재 8 ? 10％, 야자코코피트 7 ? 8, 석고 4 ? 6％, 10mm 이하규격의 천연 셀룰로스 화이버 2.5 ? 3.5％, 포졸란 분말과 목초액을 배합한 펠릿형 분말재 0.5 ? 1.5％를 포함하는 분말 조성물에, 에테르 전분 0.3 ? 0.5％, MC증점제 0.25 ? 0.35％, 주석산 0.10 ? 0.14％, 공기연행재 0.0001 ? 0.0003％를 포함하는 보조 조성물을 혼합하여 분말재를 생성한다. 이렇게 생성된 분말재에 수목생장 촉진 및 토양개량재인 액상비료 원액 4 ? 6％를 물에 90 ? 110배로 희석한 액상 혼합물 45 ? 55％에 액상 고화재 45 ? 55％를 혼합하여 생성된 액상재를 서로 혼합하여 생성된 조성물이다.Here, the preparation of the powder and liquid materials is a composition prepared in advance, 1? 5mm washing silicate 52? 56% Zeolite Aggregate 18? 22%, pozzolan aggregate 8? 10%, palm coco feet 7? 8, plaster 4? 6% natural cellulose fiber 2.5 mm or less 0.5% of pellet type powder material which mixes 3.5% of pozzolanic powder and wood vinegar solution To the powder composition containing 1.5%, ether starch 0.3? 0.5%, MC thickener 0.25? 0.35%, tartaric acid 0.10? 0.14%, Air Entrainment 0.0001? Auxiliary composition containing 0.0003% is mixed to produce a powder. Liquid fertilizer stock solution that promotes tree growth and improves soil in the powder material thus produced 4? 90% 6% in water Liquid mixture diluted 110-fold 45? Liquid solidified material at 55% 45? It is a composition produced by mixing the liquid materials produced by mixing 55% with each other.

표면보호재(112)를 생성하는 단계(S130)는, 상기 S120에서 상기 분말재는 55 ? 65％로 상기 액상재는 35 ? 45％로 혼합, 반죽하되, 2 내지 4 분간 믹서에 혼합한 후, 반죽하여 반죽형태의 표면보호재(112)를 생성한다.Generating the surface protection material 112 (S130), the powder material is 55? 65% of the liquid material is 35? Mix and knead at 45%, mix in a mixer for 2 to 4 minutes, then knead to form a dough-like surface protective material 112.

표면보호재(112)를 포설하는 단계(S140)는, 상기 생성된 표면 보호재(112)를 상기 S110 단계를 통해 정리된 상기 모토 표면(111)에 포설한 후, 2차로 다져준다. 이때 2차 다짐은 람마(ton f/blow : 3.4?9.4)로 적어도 15회 이상 충분히 다짐한다(도 6 참조).In the step of installing the surface protection material 112 (S140), the surface protection material 112 is formed on the motto surface 111 arranged through the step S110, and then compacted secondly. At this time, the second compaction is sufficient for at least 15 times as a ramma (ton f / blow: 3.4 to 9.4) (see FIG. 6).

이때. 상기 표면 보호재(112)는 혼합물 이탈방지, 재료분리 방지를 위하여 반드시 보도블럭 등 설치물과 수평을 이루도록 포설하되, 포설 두께(t)는 5cm 내지 15cm 정도로 포설하는데, 두께는 10cm인 것이 가장 바람직하다. 그리고 중앙 부위는 양끝단에서 15 ? 30 각도를 유지하도록 모양을 다지는 것이 바람직하다. 중앙 부위가 15 ? 30 각도를 유지하도록 형성될 경우, 오염물이 쌓이지 않아 오물투기 방지와 별도의 청소가 불필요한 효과가 있다.At this time. The surface protection material 112 is installed so as to be horizontal to the installation, such as the sidewalk block to prevent the separation of the mixture, material separation prevention, the installation thickness (t) is installed in about 5cm to 15cm, the thickness is most preferably 10cm. And the central part is 15? At both ends. It is desirable to compact the shape to maintain 30 angles. 15 is the central area? If it is formed to maintain the 30 angle, there is no effect that the dirt does not accumulate, preventing dirt dumping and separate cleaning.

이때, 추가적으로 상기 표면 보호재(112)를 상기 모토 표면(111)에 포설하기전, 상기 모토 표면(111) 상부에 망사형의 보조 매트(113)를 배치하거나, 상기 모토 표면(111)에 표면 보호재(112)를 포설한 후, 표면 보호재(112) 상부에 보조 매트(113)를 배치하여 사용할 수도 있을 것이다(도 7참조). 도 7에 도시된 바와 같이 망사형의 보조 매트(113)는 자연소재인 볏짚으로 이루어져 환경친화적이며, 차후 토양의 유실 방지와 내구성을 증가시키는 역할을 한다. 이러한 망사형의 보조 매트(113)는 도7a와 같이 구멍이 부정형태로 형성된 것이나, 또는 도 7b와 같이 구멍이 정형으로 형성된 것을 사용할 수 있을 것이다. 또한 보조 매트(113)의 넓이는 50 × 50mm이고, 두께는 10mm인 것이 바람직하다.In this case, before the surface protective material 112 is installed on the moto surface 111, a mesh-type auxiliary mat 113 is disposed on the moto surface 111 or a surface protective material on the moto surface 111. After laying 112, the auxiliary mat 113 may be disposed and used on the surface protection material 112 (see FIG. 7). As shown in FIG. 7, the mesh-type auxiliary mat 113 is made of rice straw which is a natural material, which is environmentally friendly, and serves to prevent loss of soil and increase durability. The mesh-type auxiliary mat 113 may be one in which holes are formed in an irregular shape as shown in FIG. 7A, or one having holes in a shape as shown in FIG. 7B. In addition, it is preferable that the width of the auxiliary mat 113 is 50 x 50 mm, and the thickness is 10 mm.

또한, 표면보호재(112)를 고정화하기 위해 첨가되는 액상고화재는 대한민국 특허 출원번호 10-2010-0104414에 게제된 다기능 액상고화재를 사용하는 것으로, 상기 액상고화재는, 특수 공중합액상 아크 릴액상 폴리머(Pure-Acrylic Emulsion)47?55％, 리튬 실리 케이트(Lithiym Sithium Silicate)10?15％, 폴리카르복실 산(Polycarbonate Acid) 3?5％ 라우릴 황산 나트륨(SodiumLauryl Sulfate)0.025?0.05％, 글루콘산 나트륨(Sodium Gluconate)2?4％와 표면장력을 감소 처리한 물을 혼합하여 침투 유동성이 좋도록 처리하는 것이며, 특히 셀룰로스 화이버(Cellulose Fiber)2?5％,폴리 비닐 알콜화이버(Poly Vinyl Alcohol Fiber)2?5％를 첨가한다.In addition, the liquid solidified material added to fix the surface protective material 112 is to use a multi-functional liquid solidified material disclosed in the Republic of Korea Patent Application No. 10-2010-0104414, the liquid solidified material is a special copolymerized liquid acryl liquid phase Polymer (Pure-Acrylic Emulsion) 47-55%, Lithium Sithium Silicate 10-15%, Polycarbonate Acid 3-5% Sodium Lauryl Sulfate0.025-0.05%, Sodium gluconate (2-4%) and surface tension-reduced water are mixed to provide good permeability and fluidity, especially Cellulose Fiber (2-5%), Poly Vinyl Alcohol Fiber (Poly Vinyl) Alcohol Fiber) 2-5% is added.

이러한 액상고화재 3 내지 5％에 액상비료인 그린원 친환경 유기농자재(농진흥청 목록 공시번호 08-유기-3-112)인 수목생장 촉진 및 토양개량재를 물에 100 ? 300배로 희석하여 다기능 액상고화재에 혼합하여 사용한다. 이러한 액상고화재는 중금속이 함유되어 있지 않은 친환경 액상고화재를 이용하여 시공시 환경오염을 방지하도록 하는 것이다.3 to 5% of the liquid solidified materials to promote the growth of trees and soil improvement materials in the green one eco-friendly organic materials (RDA List Publication No. 08-Organ-3-112), which is a liquid fertilizer in water? Dilute to 300 times and mix into multifunctional liquid solid. Such liquid solids are to prevent environmental pollution during construction using environmentally friendly liquid solids that do not contain heavy metals.

또한, 표면보호재(112)는 통, 배수가 유리한 구조와 규격, 소재로 이루어져 있으며, 중금속등이 포함되어 있지 않고, 토양과 식재에 장기적으로 비료화적인 영향을 제공할 수도 있을 것이다.In addition, the surface protection material 112 is made of a structure, a standard, a material having a favorable drainage, drainage, heavy metals, etc., and may provide a long-term fertilizer effect on soil and planting.

또한, 표면보호재(112) 제조에 사용되는 제오라이트는 흡, 배수 및 비료용도는 물론, 충진재 역할도 하는 재료이며, 포졸란 골재는 천연 광물로 적황토 색상을 가지며 천연 안료로서 토양개선 및 오염을 예방하는 역할을 한다. 그리고 세척규사는 표면보호재(112)의 표면 강도를 높이고 전체적인 구조에 강도를 제공하고 공극을 유지하도록 하는 역할을 한다. 야자코코피트(cocopeat)는 황토색상을 갖는 천연 유기물 소재로 체적중량의 20배의 물을 흡수하는 능력이 있으므로, 배수와 건조시 수분을 공급하여 일정기간동안 천연 분말안료와 보, 배수 유기골재의 역할을 한 후, 퇴비화되는 특징이 있는 재료이다. 또한 포졸란 분말과 목초액 혼합 팰릿형 분말재는 식재물에 영양을 지속적으로 공급하여 식재물에 활성화를 돕는 역할을 하며, 천연 셀롤로스 화이버는 전체의 조성물을 감싸고 고정하며 액상 고화재와 배합시 전체적인 가교 역할을 하여 내구성을 증진시키는 역할을 한다. 석고분말은 조성물의 강도 유지와 시공의 신속성을 갖도록 하는 역할을 한다. In addition, the zeolite used in the manufacture of the surface protective material 112 is a material that serves as a filler, as well as the absorption, drainage and fertilizer use, pozzolan aggregate is a natural mineral with a red ocher earth color, as a natural pigment to prevent soil improvement and pollution Play a role. And the cleaning silica serves to increase the surface strength of the surface protection material 112, to provide strength to the overall structure and to maintain the voids. Coconut is a natural organic material with yellow soil color and has the ability to absorb 20 times the volume weight of water. Therefore, it supplies water during drainage and drying, It is a material that is characterized by being composted after it plays a role. In addition, pozzolanic powder and wood vinegar mixed pellet-type powder supplies nutrition to plants and helps them to be activated. Natural cellulose fibers wrap and fix the entire composition and act as a whole crosslinking when combined with liquid solids. It serves to promote durability. Gypsum powder plays a role of maintaining the strength of the composition and the speed of construction.

또한, 천연광물계, 합성 안료를 사용하며 다양한 색상을 첨가하고 특수폴리머와 결합시 자외선을 차단시킬 수 있도록 할 수 있다. 이러한 색상 안료의 첨가는 일반적인 사항이므로, 상세한 설명은 생략한다.In addition, natural mineral-based, synthetic pigments can be added and various colors can be added and UV rays can be blocked when combined with special polymers. Since the addition of such color pigments is a general matter, detailed description thereof will be omitted.

도 8은 본 발명에 따른 표면 보호재를 가로수에 시공한 상태의 도면이다.8 is a view showing a state in which the surface protective material according to the present invention installed in the roadside tree.

도 8을 참고하면, 양생단계(S140)을 거쳐 일정시간이 지나면 포설된 표면 보호재(112)가 양생되어 일정강도를 갖게 된다. 도 8a는 표면 보호재(112) 하단에 보조 매트(113)가 배치된 상태이고, 도 8b는 표면 보호재(112) 상단에 보조 매트(113)가 배치된 상태이다.Referring to FIG. 8, after a predetermined time passes through the curing step (S140), the installed surface protective material 112 is cured to have a certain strength. 8A illustrates a state in which an auxiliary mat 113 is disposed at the bottom of the surface protection material 112, and FIG. 8B illustrates a state in which the auxiliary mat 113 is disposed on the top of the surface protection material 112.

5mm크기의 세척규사 54％, 제오라이트20％, 포졸란 9％, 야자코코피트 8％, 석고 5, 천연 셀롤로스 3％, 포졸란 분말과 목초액 배합 펠릿형 분말재 1％를 혼합하여 기본 시험을 하였다.A basic test was carried out by mixing 54% of silica sand, 5% zeolite 20%, pozzolane 9%, cococopit 8%, gypsum 5, natural cellulose 3%, pozzolane powder and 1% wood-based powder mixture pellets.

단, 상기 조성물에 0.4％의 에테르 전분(stach ether), 0.3％의 MC증점재(methyl cellulose), 0.12 주석산(tartaric acid), 0.0002 중량의 공기연행재를 기본배합조성물에 추가 사용하였다.However, 0.4% ether starch (stach ether), 0.3% MC thickener (methyl cellulose), 0.12 tartaric acid (tartaric acid), 0.0002 by weight of the air entrainer was used in the composition.

또한, 다기능 액상고화재와 액상비료인 인 그린원 친환경 유기농자재(농진흥청 목록 공시번호 08-유기-3-112)인 수목생장 촉진 및 토량개량재로서 원액을 5％, 물에 100배로 희석한 액상 혼합물을 1:액상고화재 1을 기준으로 제조하였다.In addition, as a multifunctional liquid solids and liquid fertilizer, Green Green, an eco-friendly organic material (RDA Publication No. 08-Organ-3-112), promotes tree growth and improves soil volume by diluting the stock solution by 5% and 100 times in water. A liquid mixture was prepared based on 1: liquid solid 1.

이에, 분말혼합물(분말재)을 100％로 하고 액상혼합물(액상재)을 40％로 하여 분말과 액상 전체를 혼합기에 강제로 배합하여 표면보호재(112)를 생성하여 시험한 결과, 한국건설 생활환경 시험연구원에 시험을 의뢰한 결과, 본 출원인들은 28일 양생된 표면보호재(112)의 압축강도는 19.8n/mm2 (KS L 5105-2007 시험방법)로 나타났다는 것을 확인할 수 있었다. 그러므로 충분한 강도와 내구성을 확보할 수 있다는 것을 본 실험을 통해 다시 확인할 수 있었다.Therefore, the powder mixture (powder material) to 100% and the liquid mixture (liquid material) to 40% by forcibly blending the powder and the whole liquid in the mixer to produce a surface protective material 112, and tested, As a result of requesting the test by the Environmental Testing Institute, the applicants were able to confirm that the compressive strength of the surface protective material 112 cured on the 28th was 19.8n / mm 2 (KS L 5105-2007 test method). Therefore, it was confirmed through this experiment that sufficient strength and durability can be secured.

5mm크기의 세척규사 27％, 제오라이트24％, 포졸란 23％, 야자코코피트 12％, 석고 8％, 천연 셀롤로스 5％, 포졸란 분말과 목초액 배합 펠릿형 분말재 1％를 혼합하여 기본 시험을 하였다.The basic test was carried out by mixing 27% silica sand with 24 mm zeolite, 24% zeolite, 23% pozzolane, 12% palm cocopitite, 8% gypsum, 5% natural cellulose, 1% pozzolanic powder and 1% wood-based powdered pellet powder. .

단, 상기 조성물에 0.5％의 에테르 전분(stach ether), 0.3％의 MC증점재(methyl cellulose), 0.145 주석산(tartaric acid), 0.0003 중량의 공기연행재를 기본배합조성물에 추가 사용하였다.However, 0.5% ether starch (stach ether), 0.3% MC thickener (methyl cellulose), 0.145 tartaric acid (tartaric acid), 0.0003 by weight of the air entrainer was used in the composition.

또한, 다기능 액상고화재와 액상비료인 인 그린원 친환경 유기농자재(농진흥청 목록 공시번호 08-유기-3-112)인 수목생장 촉진 및 토량개량재로서 원액을 5％, 물에 100배로 희석한 액상 혼합물을 1:액상고화재 1.5을 기준으로 제조하였다.In addition, as a multifunctional liquid solids and liquid fertilizer, Green Green, an eco-friendly organic material (RDA Publication No. 08-Organ-3-112), promotes tree growth and improves soil volume by diluting the stock solution by 5% and 100 times in water. Liquid mixtures were prepared based on 1: liquid solid 1.5.

이에, 분말혼합물(분말재)을 100％로 하고 액상혼합물(액상재)을 38％로 하여 분말과 액상 전체를 혼합기에 강제로 배합하여 표면보호재(112)를 생성하여 시험한 결과, 한국건설 생활환경 시험연구원에 시험을 의뢰한 결과, 본 출원인들은 28일 양생된 표면보호재(112)의 압축강도는 13.0n/mm2 (KS L 5105-2007 시험방법)로 나타났다는 것을 확인할 수 있었다. 그러므로 충분한 강도와 내구성을 확보할 수 있다는 것을 본 실험을 통해 다시 확인할 수 있었다.Therefore, the powder mixture (powder material) to 100% and the liquid mixture (liquid material) to 38% by forcibly mixing the powder and the whole liquid in the mixer to produce a surface protective material 112, and tested the results. As a result of requesting the test by the Environmental Testing Institute, the applicants were able to confirm that the compressive strength of the surface protective material 112 cured on the 28th was 13.0n / mm 2 (KS L 5105-2007 test method). Therefore, it was confirmed through this experiment that sufficient strength and durability can be secured.

5mm크기의 세척규사 27％, 제오라이트24％, 포졸란 23％, 야자코코피트 12％, 석고 8％, 천연 셀롤로스 5％, 포졸란 분말과 목초액 배합 펠릿형 분말재 1％를 홉합하여 기본 시험을 하였다.The basic test was performed by mixing 27% of 5mm sized silica sand, 24% zeolite, 23% pozzolane, 12% palm cocopitite, 8% gypsum, 5% natural cellulose, 1% pozzolane powder and 1% powdered wood powder mixture. .

단, 상기 조성물에 0.5％의 에테르 전분(stach ether), 0.3％의 MC증점재(methyl cellulose), 0.145 주석산(tartaric acid), 0.0003 중량의 공기연행재를 기본배합조성물에 추가 사용하였다.However, 0.5% ether starch (stach ether), 0.3% MC thickener (methyl cellulose), 0.145 tartaric acid (tartaric acid), 0.0003 by weight of the air entrainer was used in the composition.

또한, 다기능 액상고화재와 액상비료인 인 그린원 친환경 유기농자재(농진흥청 목록 공시번호 08-유기-3-112)인 수목생장 촉진 및 토량개량재로서 원액을 5％, 물에 100배로 희석한 액상 혼합물을 1:액상고화재 1.5을 기준으로 제조하였다.In addition, as a multifunctional liquid solids and liquid fertilizer, Green Green, an eco-friendly organic material (RDA Publication No. 08-Organ-3-112), promotes tree growth and improves soil volume by diluting the stock solution by 5% and 100 times in water. Liquid mixtures were prepared based on 1: liquid solid 1.5.

이후, 악조건(비, 눈)하에 식재되어 있는 가로 조경수(가로수) 하단에 보조 매트(113)를 배치하고, 그 상부에 본 발명에 따른 표면보호재(112)를 포설(설치)하였다.Subsequently, the auxiliary mat 113 was disposed at the lower side of the horizontal landscape water (horizontal tree) that was planted under bad conditions (rain and snow), and the surface protection material 112 according to the present invention was installed (installed) on the upper side.

이에, 분말혼합물(분말재)을 100％로 하고 액상혼합물(액상재)을 38％로 하여 분말과 액상 전체를 혼합기에 강제로 배합하여 표면보호재(112)를 생성하여 시험한 결과, 한국건설 생활환경 시험연구원에 시험을 의뢰한 결과, 본 출원인들은 28일 양생된 표면보호재(112)의 압축강도는 11.6n/mm2 (KS L 5105-2007 시험방법)로 나타났다는 것을 확인할 수 있었다. 그러므로 충분한 강도와 내구성을 확보할 수 있다는 것을 본 실험을 통해 다시 확인할 수 있었다.Therefore, the powder mixture (powder material) to 100% and the liquid mixture (liquid material) to 38% by forcibly mixing the powder and the whole liquid in the mixer to produce a surface protective material 112, and tested the results. As a result of requesting the test by the Environmental Testing Institute, the applicants were able to confirm that the compressive strength of the surface protective material 112 cured on the 28th was 11.6n / mm 2 (KS L 5105-2007 test method). Therefore, it was confirmed through this experiment that sufficient strength and durability can be secured.

본 발명은 상술한 바람직한 실시예에 한정되지 아니하며 청구범위에서 청구하는 본 발명의 요지를 벗어남이 없이 당해 발명이 속하는 기술분야에서 통상의 지식을 가진 자라면 누구든지 용이하게 변형 실시 가능한 것은 물론이고, 이와 같은 변경은 청구항의 청구범위 기재범위 내에 있게 된다.The present invention is not limited to the above-described preferred embodiments and can be easily modified by anyone of ordinary skill in the art without departing from the gist of the invention claimed in the claims, Such changes are intended to fall within the scope of the claims.

Claims (7)

(A) 가로수 또는 이동식 고정식 화분 표면에 물을 살수한 후, 5 ? 15cm 두께로 표층을 겉어 낸 후, 상기 표면에 압력을 가해 1차로 다져주는 시공준비 단계;
(B) 1 ? 5mm 크기의 세척규사 52 ? 56％, 제오라이트 골재 18 ? 22％, 포졸란 골재 8 ? 10％, 야자코코피트 7 ? 8, 석고 4 ? 6％, 10mm 이하규격의 천연 셀룰로스 화이버 2.5 ? 3.5％, 포졸란 분말과 목초액을 배합한 펠릿형 분말재 0.5 ? 1.5％를 포함하는 분말 조성물에,
에테르 전분 0.3 ? 0.5％, MC증점제 0.25 ? 0.35％, 주석산 0.10 ? 0.14％, 공기연행재 0.0001 ? 0.0003％를 포함하는 보조 조성물을 혼합하여 생성된 분말재에,
수목생장 촉진 및 토양개량재인 액상비료 원액 4 ? 6％를 물에 90 ? 110배로 희석한 액상 혼합물 45 ? 55％에 액상 고화재 45 ? 55％를 혼합하여 생성된 액상재를 서로 혼합하되,
(C) 상기 분말재는 55 ? 65％로 상기 액상재는 35 ? 45％로 혼합, 반죽하여 표면보호재를 생성하는 단계;
(D) 상기 B 단계를 통해 생성된 표면 보호재를 상기 A 단계를 통해 정리된 상기 모토 표면에 포설한 후, 2차로 다져주는 단계; 및
(F) 일정시간이 동안 상기 D 단계를 통해 포설된 상기 표면 보호재를 양생시키는 양생단계;를 포함하는 것을 특징으로 하는 자연토를 이용한 자연조경시설 표면보호 공법.(A) after watering the surface of a tree or mobile stationary pot, 5? After preparing the surface layer to a thickness of 15cm, applying the pressure to the surface to prepare the first step;
(B) 1? 5mm washing silicate 52? 56% Zeolite Aggregate 18? 22%, pozzolan aggregate 8? 10%, palm coco feet 7? 8, plaster 4? 6% natural cellulose fiber 2.5 mm or less 0.5% of pellet type powder material which mixes 3.5% of pozzolanic powder and wood vinegar solution In powder composition containing 1.5%,
Ether starch 0.3? 0.5%, MC thickener 0.25? 0.35%, tartaric acid 0.10? 0.14%, Air Entrainment 0.0001? To the powder material produced by mixing the auxiliary composition containing 0.0003%,
Liquid fertilizer stock solution for promoting tree growth and soil improvement 4? 90% 6% in water Liquid mixture diluted 110-fold 45? Liquid solidified material at 55% 45? 55% of the liquid material produced by mixing with each other,
(C) The powder material is 55? 65% of the liquid material is 35? Mixing and kneading at 45% to produce a surface protective material;
(D) depositing the surface protective material produced in the step B on the surface of the motto arranged in the step A, and then slicing the second step; And
(F) curing the surface protective material laid through the step D for a predetermined time; natural landscaping facility surface protection method using a natural soil comprising a. (a) 가로수 또는 이동식 고정식 화분 표면인 모토를 평탄하게 정리하는 시공준비 단계;
(b) 1 ? 5mm 크기의 세척규사 25 ? 29％, 제오라이트 골재 22 ? 26％, 포졸란 골재 22 ? 24％, 야자코코피트 11 ? 13, 석고 7 ? 9％, 10mm 이하규격의 천연 셀룰로스 화이버 4 ? 6％, 포졸란 분말과 목초액을 배합한 펠릿형 분말재 0.5 ? 1.5％를 포함하는 분말 조성물에,
에테르 전분 0.4 ? 0.6％, MC증점제 0.25 ? 0.35％, 주석산 0.140 ? 0.150％, 공기연행재 0.0002 ? 0.0004％를 포함하는 보조 조성물을 혼합하여 생성된 분말재에,
수목생장 촉진 및 토양개량재인 액상비료 원액 4.5 ? 5.5％를 물에 90 ? 110배로 희석한 액상 혼합물 45 ? 55％에 액상 고화재 45 ? 55％를 혼합하여 생성된 액상재를 서로 혼합하되,
(c) 상기 분말재는 55 ? 65％로 상기 액상재는 36 ? 40％로 혼합, 반죽하여 표면보호재를 생성하는 단계;
(d) 상기 b 단계를 통해 생성된 표면 보호재를 상기 a 단계를 통해 정리된 상기 모토 표면에 포설하는 단계; 및
(f) 일정시간이 동안 상기 d 단계를 통해 포설된 상기 표면 보호재를 양생시키는 양생단계;를 포함하는 것을 특징으로 하는 자연토를 이용한 자연조경시설 표면보호 공법.(a) a construction preparation step for flattening the motto that is a tree or mobile stationary potted surface;
(b) 1? 5mm cleaning silica 25? 29% Zeolite Aggregate 22? 26%, pozzolan aggregate 22? 24%, palm coco feet 11? 13, plaster 7? 9%, less than 10mm natural cellulose fiber 4? 0.5% of pellet type powder material which blended 6%, pozzolan powder and wood vinegar solution In powder composition containing 1.5%,
Ether starch 0.4? 0.6%, MC thickener 0.25? 0.35%, tartaric acid 0.140? 0.150%, Air Entrainment 0.0002? To the powder material produced by mixing the auxiliary composition containing 0.0004%,
Liquid fertilizer undiluted solution 4.5 for tree growth and soil improvement 90% to 5.5% in water Liquid mixture diluted 110-fold 45? Liquid solidified material at 55% 45? 55% of the liquid material produced by mixing with each other,
(c) the powder material is 55? 65% of the liquid material is 36? Mixing and kneading at 40% to produce a surface protective material;
(d) depositing the surface protective material produced in step b on the surface of the motto arranged in step a; And
(F) curing the surface protective material laid through the step d for a predetermined time; natural landscaping facility surface protection method using a natural soil comprising a. 제 1 항 또는 제 2 항에 있어서,
상기 (D) 단계 또는 (d) 단계는,
상기 모토 표면 상부에 망사형의 보조 매트를 배치하거나, 상기 모토 표면에 포설된 상기 표면 보호재의 상부에 상기 보조 매트가 배치되는 단계를 더 포함하는 것을 특징으로 하는 자연토를 이용한 자연조경시설 표면보호 공법.The method according to claim 1 or 2,
Step (D) or (d),
A surface protection of natural landscaping facilities using natural soil further comprises the step of disposing a mesh-type auxiliary mat on the surface of the moto, or the auxiliary mat on the surface of the surface protection material installed on the surface of the moto. Method. 제 3 항에 있어서,
상기 보조 매트는,
자연소재인 볏짚으로 이루어지며, 정형 또는 부정형태의 망형으로 형성되는 것을 특징으로 하는 자연토를 이용한 자연조경시설 표면보호 공법.The method of claim 3, wherein
The auxiliary mat,
Natural landscaping facility surface protection method using natural soil, consisting of rice straw, which is a natural material, is formed in a net form of the form or irregular form. 제 1 항 또는 제 2 항에 있어서,
상기 액상고화재는,
특수 공중합액상 아크 릴액상 폴리머(Pure-Acrylic Emulsion)47?55％, 리튬 실리 케이트(Lithiym Sithium Silicate)10?15％, 폴리카르복실 산(Polycarbonate Acid) 3?5％ 라우릴 황산 나트륨(SodiumLauryl Sulfate)0.025?0.05％, 글루콘산 나트륨(Sodium Gluconate)2?4％와 표면장력을 감소 처리한 물을 혼합하여 침투 유동성이 좋도록 처리하는 것을 특징으로 하는 자연토를 이용한 자연조경시설 표면보호 공법.The method according to claim 1 or 2,
The liquid solidifying material,
Pure Co-Acrylic Emulsion 47 ~ 55%, Lithium Sithium Silicate 10 ~ 15%, Polycarbonate Acid 3 ~ 5% Sodium Lauryl Sulfate ) Surface protection method of natural landscaping facility using natural soil, characterized in that the mixture is treated with 0.025 to 0.05%, sodium gluconate (2-4%) and water with reduced surface tension to improve penetration fluidity. 제 5 항에 있어서,
상기 액상고화재는,
셀룰로스 화이버(Cellulose Fiber)2?5％,폴리 비닐 알콜화이버(Poly Vinyl Alcohol Fiber)2?5％를 첨가하는 것을 특징으로 자연토를 이용한 자연조경시설 표면보호 공법.The method of claim 5, wherein
The liquid solidifying material,
A surface protection method of natural landscaping facility using natural soil, characterized by adding 2-5% of Cellulose Fiber and 2-5% of Poly Vinyl Alcohol Fiber. 제 5 항에 있어서,
상기 액상고화재는,
혼합수를 제외한 분말 형태로 제조되는 것을 특징으로 하는 자연토를 이용한 자연조경시설 표면보호 공법.The method of claim 5, wherein
The liquid solidifying material,
Natural landscaping facility surface protection method using a natural soil, characterized in that the powder is prepared except the mixed water.
KR1020110010829A 2011-02-01 2011-02-01 landscaping facility surface protecting method using natural earth KR20120089165A (en)