KR20120085480A - a solid fuel manufactured by toilet garbage and a manufacturing method thereof - Google Patents

a solid fuel manufactured by toilet garbage and a manufacturing method thereof Download PDF

Info

Publication number
KR20120085480A
KR20120085480A KR1020110006825A KR20110006825A KR20120085480A KR 20120085480 A KR20120085480 A KR 20120085480A KR 1020110006825 A KR1020110006825 A KR 1020110006825A KR 20110006825 A KR20110006825 A KR 20110006825A KR 20120085480 A KR20120085480 A KR 20120085480A
Authority
KR
South Korea
Prior art keywords
solid fuel
waste
toilet waste
toilet
mixture
Prior art date
Application number
KR1020110006825A
Other languages
Korean (ko)
Inventor
정석원
Original Assignee
정석원
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 정석원 filed Critical 정석원
Priority to KR1020110006825A priority Critical patent/KR20120085480A/en
Publication of KR20120085480A publication Critical patent/KR20120085480A/en

Abstract

PURPOSE: Solid fuel and a method for preparing the same are provided to reduce environmental pollution by preventing the generation of harmful gas generated from the combustion of fossil fuel. CONSTITUTION: A method for preparing solid fuel includes the following: impurities are eliminated from bathroom waste to remain papers(S1); the bathroom water is pulverized(S2); a calorie adjusting agent and a coagulating agent are mixed with the pulverized product to obtain a mixed product(S3); the mixed product is dried at high temperatures(S4); the dried product is pulverized(S5); and the pulverized dried product is extruded or compressed to be formed into pre-determined shapes(S6).

Description

화장실 폐기물을 이용한 고형연료 및 이를 제조하는 제조방법{a solid fuel manufactured by toilet garbage and a manufacturing method thereof}Solid fuel manufactured by toilet waste and manufacturing method thereof

본 발명은 화력으로 사용되는 고형연료에 관한 것으로서, 더 구체적으로는 화장실에서 사용하고 버려지는 화장실 폐기물을 이용하여 제조되는 고형연료 및 이를 제조하는 제조방법에 관한 것이다.The present invention relates to a solid fuel to be used for thermal power, and more particularly to a solid fuel produced using the toilet waste that is used and discarded in the toilet and a manufacturing method for producing the same.

산업사회의 발전으로 기술력의 향상과 생활의 편리함 등 여러가지 이로운 점이 있는 반면, 무분별한 발전으로 인해 환경오염이라는 문제가 발생하고 있다.The development of industrial society has various advantages such as improvement of technology and convenience of life, while the problem of environmental pollution is caused by indiscriminate development.

이러한, 환경오염은 생활의 편리함을 제공하기 위한 1회용 제품들을 늘어남에 따라 더욱 가속화되고 있다.This environmental pollution is accelerating as more and more disposable products to provide the convenience of life.

1회용 제품들은 예컨대, 음료를 담을 수 있는 페티(P.T)병, 생리대, 기저귀 등의 생활 폐기물이 많은 부분을 차지하고 있으며, 생활 폐기물 중에서 재사용이 가능한 것은 재활용을 하지만 재사용이 불가능한 것들은 매립하거나 소각하는 형태로 폐기되어 환경오염을 유발하고 있다.Disposable products occupy a large portion of household waste, such as PET bottles, sanitary napkins, and diapers, which can hold beverages. Among them, reusable ones are recycled but non-reusable ones are buried or incinerated. It is disposed of and causes environmental pollution.

따라서, 근래에는 버려지는 생활 폐기물을 재활용할 수 있도록 생활 폐기물을 연료화시키는 방법이 제시되고 있다.Therefore, in recent years, a method of fueling household wastes has been proposed to recycle the household wastes discarded.

예컨대, 생활폐기물을 연료화시키는 방법 중에는 한국공개특허 제2006-82063호의 폐휴지를 이용한 고형연료의 제조방법이 개시되어 있다.For example, among the methods for fueling domestic waste, a method for producing solid fuel using waste paper waste is disclosed in Korean Patent Laid-Open No. 2006-82063.

폐휴지를 이용한 고형연료의 제조방법은 표백액에 폐휴지를 표백하는 공정, 폐휴지의 이물질을 제거하는 공정, 폐휴지를 탈수하는 공정, 폐휴지에 물을 넣고 교합하여 세척 및 탈수하는 공정, 표백제를 제거하여 재생 원료를 만들고 석탄분말60％및 목분10％을 혼합하는 공정, 성형공정, 건조공정을 거쳐 고형연료를 제조하게 된다. 이러한 폐휴지를 이용한 고형연료는 폐휴지를 재사용할 수 있어 환경오염을 방지할 수 있다.The method of manufacturing solid fuel using waste paper is a process of bleaching waste paper in bleach solution, removing foreign matters from waste paper, dehydrating waste paper, washing and dehydrating by putting water in waste paper Bleach is removed to make recycled raw materials, and solid fuel is produced through a process of mixing 60% of coal powder and 10% of wood powder, forming process and drying process. Solid fuel using such waste paper waste can be recycled waste paper can prevent environmental pollution.

하지만, 폐휴지를 이용한 고형연료는 표백액을 사용하여 폐휴지를 표백하기 때문에 사용된 표백액을 폐기하는 과정에서 환경오염이 발생되며, 주된 성분이 폐휴지가 아니라 석탄분말이기 때문에 고형연료의 연소시 화석연료와 같이 이산화황, 일산화탄소 등 유해물질이 발생하는 문제점이 있다.However, solid fuel using waste paper bleaches waste paper using bleach solution, so environmental pollution occurs in the process of discarding used bleach solution, and combustion of solid fuel because the main component is coal powder, not waste paper waste. Hazardous substances such as sulfur dioxide and carbon monoxide are generated, such as fossil fuel.

또한, 석탄분말이 함유되어 고형연료를 취급할 때, 석탄분진이 발생하고, 석탄분진이 묻어날 뿐만 아니라, 석탄분말 때문에 무게가 무거워 취급이 난해한 문제점이 있었다.In addition, when handling the solid fuel containing coal powder, not only coal dust is generated, coal dust is buried, but because of the heavy weight of the coal powder has a problem that handling is difficult.

본 발명은 전술한 바와 같은 문제점을 해결하기 위한 것으로서, 본 발명이 해결하고자 하는 과제는 버려지는 폐기물을 사용하여 제조비용이 저렴하며, 화석연료보다 높은 열량과 유해가스의 발생이 적을 뿐만 아니라, 분진이 발생하지 않으며, 무게가 가벼워 취급이 용이한 고형연료를 제공하는 것이다.The present invention is to solve the problems as described above, the problem to be solved by the present invention is a low manufacturing cost by using the waste is discarded, not only generates less calories and harmful gas than fossil fuel, dust This does not occur, it is to provide a solid fuel that is light in weight and easy to handle.

상기한 과제를 해결하기 위한 본 발명의 실시예에 따른 화장실 폐기물을 이용한 고형연료의 제조방법은 화장실 폐기물에서 종이류만 남도록 이물질을 제거하는 단계, 상기 이물질이 제거된 화장실 폐기물을 파쇄하는 단계, 상기 파쇄된 화장실 폐기물에 열량조절제 및 응고제를 혼합하여 혼합체를 구성하는 단계, 상기 혼합체를 고온에서 건조하는 단계, 상기 건조하는 단계에서 건조된 상기 혼합체를 분쇄하는 단계, 상기 분쇄된 혼합체를 압출 또는 압착하여 임의의 형상으로 성형하는 단계를 포함한다.Solid fuel manufacturing method using a toilet waste according to an embodiment of the present invention for solving the above problems is to remove the foreign matter so that only paper remains in the toilet waste, the step of crushing the toilet waste from which the foreign matter is removed, the shredding Mixing the calorie control agent and the coagulant to the toilet waste to form a mixture, drying the mixture at a high temperature, pulverizing the dried mixture in the drying step, extruding or compressing the pulverized mixture optionally Molding to the shape of.

상기 응고제는 물에 곡물가루를 혼합한 것일 수 있다.The coagulant may be a mixture of grain flour in water.

상기 열량조절제는 폐타이어 실밥일 수 있다.The calorie control agent may be waste tire seams.

상기 혼합체를 고온에서 건조하는 단계에서는 100℃ 이상 150℃ 이하의 온도에서 30시간 이상 40 시간 이하의 시간 동안 건조될 수 있다.In the step of drying the mixture at a high temperature may be dried for more than 30 hours 40 hours or less at a temperature of more than 100 ℃ 150 ℃.

본 발명의 실시예에 따른 화장실 폐기물을 이용한 고형연료는 연소 시 화력을 발생하는 고형연료에 있어서, 화장실 폐기물이 70중량％ 내지 90중량％, 열량을 조절하는 열량조절제가 1중량％ 내지 20중량％ 및 상기 열량조절제와 상기 화장실 폐기물을 응고시키는 응고제를 0.1중량％ 내지 10중량％을 포함하고, 건조 후의 수분 함량은 15중량％ 내지 25중량％일 수 있다.Solid fuel using toilet waste according to an embodiment of the present invention is a solid fuel that generates thermal power when burning, 70% to 90% by weight of toilet waste, 1% to 20% by weight of the calorific agent for adjusting the calorie And 0.1 wt% to 10 wt% of the calorific agent and the coagulant for coagulating the toilet waste, and the moisture content after drying may be 15 wt% to 25 wt%.

상기 열량조절제는 폐타이어 실밥일 수 있다.The calorie control agent may be waste tire seams.

상기 응고제는 물과 곡물가루의 혼합물인 것일 수 있다.The coagulant may be a mixture of water and grain flour.

본 발명에 따르면, 폐기물을 사용하여 고형연료를 제조함으로써, 제조비용을 감소시킬 수 있으며, 매립되는 폐기물의 발생을 줄일 수 있을 뿐만 아니라, 화석연료에서 연소 시 발생되는 유해가스의 발생이 적어 환경오염을 감소시킬 수 있다.According to the present invention, by manufacturing the solid fuel by using the waste, it is possible to reduce the manufacturing cost, to reduce the generation of landfilled waste, and to reduce the generation of harmful gases generated during combustion in fossil fuel, environmental pollution Can be reduced.

또한, 주된 성분이 종이류인 화장실 폐기물이기 때문에, 무게가 가볍고 뿐만 아니라 열량이 높으며, 분진이 발생하지 않아 취급이 용이한 이점이 있다.In addition, since the main component is a toilet waste, which is paper, it is light in weight and high in calories, and there is an advantage in that it is easy to handle because no dust is generated.

도 1은 본 발명의 실시예에 따른 화장실 폐기물을 이용한 고형연료를 개략적으로 도시한 사시도이다.
도 2는 본 발명의 실시예에 따른 화장실 폐기물을 이용한 고형연료의 제조방법을 개략적으로 도시한 도면이다.1 is a perspective view schematically showing a solid fuel using toilet waste according to an embodiment of the present invention.
2 is a view schematically showing a method of manufacturing solid fuel using toilet waste according to an embodiment of the present invention.

이하, 첨부된 도면을 참조하여 본 발명의 실시예를 상세히 설명하도록 한다.Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings.

먼저, 본 발명의 실시예에 따른 화장실 폐기물을 고형연료(100)는 그 주된 구성물이 화장실 폐기물이다. 여기서, 화장실 폐기물은 화장실에서 가장 많이 사용되는 종이류 예컨대, 화장지, 생리대, 기저귀 등의 폐기물을 의미한다.First, the toilet waste in accordance with an embodiment of the present invention solid fuel 100, the main component is the toilet waste. Here, the toilet waste refers to waste papers most commonly used in the toilet, for example, toilet paper, sanitary napkin, and diaper.

화장실 폐기물은 대부분 재사용되지 않고 매립되기 때문에 환경오염이 발생하며, 화장실 폐기물이 하루에 버려지는 량은 그 수를 헤아릴 수 없을 정도로 많기 때문에 화장실 폐기물을 이용하여 고형연료(100)를 제작함으로써, 환경오염을 방지하고자 한다.Because most of the toilet waste is landfilled and not reused, environmental pollution occurs, and since the amount of toilet waste is discarded a day is innumerable, the solid fuel 100 is produced by using the toilet waste, thereby causing environmental pollution. To prevent this.

도 1에 도시된 바와 같이, 본 발명의 실시예에 따른 화장실 폐기물을 고형연료(100)는 화장실 폐기물을 포함할 수 있다. 이 화장실 폐기물은 고형연료(100)의 주된 성분으로 연소시 화력을 발생할 수 있다. 한편, 화장실 폐기물은 화장실에서 사용되고 버려지는 화장지, 생리대, 기저귀가 될 수 있다.As shown in Figure 1, the toilet waste solid fuel 100 according to an embodiment of the present invention may include toilet waste. This toilet waste is a main component of the solid fuel 100, and may generate fire power when burned. On the other hand, toilet waste may be toilet paper, sanitary napkins, diapers used and discarded in the toilet.

그리고, 화장실 폐기물은 70중량％ 내지 90중량％이하를 포함할 수 있다. 여기서, 화장실 폐기물이 90중량％를 초과하면 고형연료(100)가 쉽게 부서지며, 70％중량％ 미만이면 화력이 미미하여 연료로서의 가치가 떨어진다.In addition, the toilet waste may include 70% by weight to 90% by weight or less. Here, when the toilet waste exceeds 90% by weight, the solid fuel 100 is easily broken, and when it is less than 70% by weight, the thermal power is insignificant and the value as a fuel is lowered.

본 발명의 실시예에 따른 화장실 폐기물을 고형연료(100)는 열량조절제를 포함할 수 있다. 이 열량조절제는 화장실 폐기물과 혼합되어 고형연료(100)의 열량을 조절할 수 있다. 이때 열량조절제는 화장실 폐기물과 혼합되는 혼합비율이 높아질수록 더 높은 열량을 발생시킬 수 있다.The solid waste fuel toilet 100 according to the embodiment of the present invention may include a calorie control agent. This calorie control agent can be mixed with the toilet waste to control the calorie of the solid fuel (100). In this case, the calorie control agent may generate higher calories as the mixing ratio of the toilet waste is increased.

예컨대, 열병합 발전소, 소성로 등과 같은 높은 화력이 요구될 때에는 열량조절제의 혼합비율이 높은 고형연료(100)를 사용하고, 농작물 재배단지와 같이 낮은 화력이 요구될 때에는 열량조절제의 혼합비율이 낮은 고형연료(100)가 사용될 수 있다.For example, when a high thermal power such as a cogeneration plant or a kiln is required, the solid fuel 100 having a high mixing ratio of calorie control agent is used, and a solid fuel having a low mixing ratio of calorie control agent when low thermal power is required, such as a crop planting complex. 100 may be used.

한편, 열량조절제는 폐타이어 실밥으로 구현될 수 있다. 여기서, 타이어는 일반적으로 철사로 골격을 형성하며, 철사의 외면에 고무를 가류하여 제조된다. 이때, 골격을 이루는 철사와 고무 사이에 고무가 철사에 견고히 고착될 수 있도록 실이 감기게 된다.On the other hand, calorie control agent may be implemented in waste tire seams. Here, the tire is generally made of wire to form a skeleton, and is manufactured by vulcanizing rubber on the outer surface of the wire. At this time, the thread is wound between the wire forming the skeleton and the rubber so that the rubber can be firmly fixed to the wire.

이렇게 구성된 타이어는 파손되거나 마모되어 폐기할 때, 철사는 재사용이 가능하지만 고무는 재사용이 불가능하기 때문에 철사와 고무를 분리하여 폐기를 한다. 이때, 고무를 폐기하기 전 고무 사이에 삽입된 실을 분리하는 형태로 폐타이어 실밥을 얻을 수 있다.When the tire is thus configured to be broken or worn out, the wire is reusable but rubber is not reusable. At this time, the waste tire seams can be obtained in the form of separating the thread inserted between the rubber before discarding the rubber.

따라서, 열량조절제로 폐타이어 실밥을 사용함으로써, 버려지는 폐기물의 량을 줄일 수 있어 환경오염을 감소시킬 수 있다.Therefore, by using the waste tire seams as a calorific control agent, the amount of waste discarded can be reduced, thereby reducing environmental pollution.

아울러, 열량조절제는 1중량％ 내지 20중량％가 화장실 폐기물에 포함될 수 있다. 여기서, 열량조절제가 20중량％를 초과할 경우, 화력이 너무 높고 연소속도가 빨라 연소 시 고형연료(100)의 소모량이 상승되며, 열량조절제가 1중량％미만일 경우, 열량조절제의 비율이 미미하여 화력에 영향을 미치지 못한다.In addition, the calorific control agent may be included in the toilet waste 1% to 20% by weight. Here, when the caloric control agent exceeds 20% by weight, the thermal power is too high and the combustion speed is fast, the consumption of the solid fuel 100 during combustion increases, and when the caloric control agent is less than 1% by weight, the ratio of the caloric control agent is inferior to the thermal power Does not affect.

본 발명의 실시예에 따른 화장실 폐기물을 고형연료(100)는 응고제를 포함할 수 있다. 이 응고제는 화장실 폐기물과 열량조절제의 응고력을 견고하게 하여 고형연료(100)의 성형 후 고형연료(100)가 부서지는 것을 방지할 수 있다.The solid fuel 100 of the toilet waste according to the embodiment of the present invention may include a coagulant. The coagulant hardens the coagulation power of the toilet waste and the calorific control agent to prevent the solid fuel 100 from breaking after the solid fuel 100 is molded.

한편, 응고제는 물과 곡물가루의 혼합물일 수 있다. 이때, 곡물가루는 밀가루인 것이 바람직하고, 물과 곡물가루의 혼합비율은 1:1인 것이 바람직하다.On the other hand, the coagulant may be a mixture of water and grain flour. At this time, the grain flour is preferably wheat flour, and the mixing ratio of water and grain flour is preferably 1: 1.

여기서, 밀가루는 제분공장에서 밀을 제분 시 공기 중에 날리는 형태로 제분공장에 쌓여 버려지거나 유통기한이 지난 밀가루가 사용될 수 있다. 따라서, 버려지는 밀가루를 사용하기 때문에 고형연료(100)의 제조비용을 감소시킬 수 있다.Here, the flour may be used in the flour mill is stacked in the mill or the expiration date in the form of flying in the air at the mill mill. Therefore, since the flour is discarded, the manufacturing cost of the solid fuel 100 can be reduced.

그리고 응고제는 화장실 폐기물에 0.1중량％ 내지 10중량％가 혼합될 수 있다. 여기서 응고제가 0.1중량％ 미만으로 혼합될 경우에는 응고제의 혼합량이 적어 고형연료(100)가 쉽게 부서질 수 있으며, 응고제의 혼합량이 10중량％를 초과하여 혼합될 경우에는 고형연료(100)의 경도가 강해 고형연료(100)의 착화 시 착화 시간이 오래 걸리는 문제점이 있다.And the coagulant may be mixed with 0.1 to 10% by weight in the toilet waste. Here, when the coagulant is mixed in less than 0.1% by weight, the amount of coagulant is mixed so that the solid fuel 100 may be easily broken. In the case where the coagulant is mixed in excess of 10% by weight, the hardness of the solid fuel 100 may be reduced. There is a problem that the ignition time takes a long time when the ignition of the solid fuel 100 is strong.

이렇게 구성된 본 발명의 실시예에 따른 화장실 폐기물을 고형연료(100)는 매립되고 버려지는 폐기물을 연료로 사용함으로써, 매립되는 폐기물을 감소시켜 환경오염을 감소시킬 수 있을 뿐만 아니라 연소 시 화석연료와 같이 일산화탄소, 이산화황과 같은 유해가스의 발생이 낮아 환경오염을 줄일 수 있다.By using the toilet waste according to the embodiment of the present invention configured as the solid fuel 100 as fuel, the waste that is buried and discarded can reduce the landfill waste and reduce environmental pollution as well as fossil fuel during combustion. It is possible to reduce environmental pollution due to low generation of harmful gases such as carbon monoxide and sulfur dioxide.

또한, 종이류 및 열량조절제가 첨가되어 발열량이 높으며, 버려지는 화장실 폐기물, 폐타이어 실밥, 그리고 밀가루 등을 사용함으로써, 제조비용을 대폭 낮출 수 있다.In addition, the amount of heat generated by the addition of papers and calorie control is high, by using the discarded toilet waste, waste tire seams, flour, etc., it is possible to significantly reduce the manufacturing cost.

한편, 이러한 구성을 가지는 고형연료(100)는 하기와 같은 방법으로 제조될 수 있다.On the other hand, the solid fuel 100 having such a configuration can be manufactured by the following method.

도 2에 도시된 바와 같이, 본 발명의 실시예에 따른 화장실 폐기물을 고형연료(100)의 제조방법은 먼저, 화장실 폐기물의 이물질을 선별하는 단계(S1)를 거칠 수 있다. 즉, 이 단계(S1)에서는 화장실에서 수거된 화장실 폐기물을 선별기에 넣어 종이류인 화장지, 생리대, 기저귀만 남도록 그 외의 이물질을 제거할 수 있다.As shown in FIG. 2, the method for manufacturing the toilet waste solid fuel 100 according to the embodiment of the present invention may first go through a step (S1) of sorting foreign matter from the toilet waste. That is, in this step (S1) it is possible to remove the other foreign matter so that only toilet paper, sanitary napkin, diapers, which are papers, are put in the toilet waste collected in the toilet.

여기서, 선별기는 복수의 관통 홈이 형성된 평판을 모터로 진동시키고, 평판의 상부에 화장실 폐기물을 올려놓아 화장실 폐기물이 평판을 지나면서 평판의 진동에 의해 복수의 홈을 통해 이물질이 평판의 하부로 떨어지도록 구성될 수 있다.Here, the sorter vibrates the plate formed with a plurality of through grooves by a motor, and puts toilet waste on the top of the plate so that the toilet waste passes through the plate, and foreign matters fall into the lower portion of the plate by the vibration of the plate. It can be configured to.

그리고, 이물질이 제거된 화장실 폐기물은 가공이 용이하도록 임의의 크기로 파쇄되는 단계(S2)를 거칠 수 있다. 이때, 화장실 폐기물이 파쇄되는 크기는 대략 1cm 내지 3cm로 파쇄될 수 있다.In addition, the toilet waste from which foreign matters are removed may be crushed to an arbitrary size (S2) to facilitate processing. At this time, the size of the toilet waste may be shredded to about 1cm to 3cm.

한편, 화장실 폐기물이 파쇄될 때에는 파쇄기에 의해 파쇄될 수 있으며, 파쇄기는 모터에 의해 복수의 칼날이 회전하고, 그 회전하는 칼날의 사이에 화장실 이물질이 삽입되어 파쇄되는 형태로 구성될 수 있다.On the other hand, when the toilet waste is crushed may be crushed by a crusher, the crusher may be configured in such a way that a plurality of blades are rotated by the motor, toilet foreign matter is inserted and crushed between the rotating blades.

또한, 파쇄된 화장실 폐기물은 열량조절제와 응고제를 혼합하여 혼합체를 구성하는 단계(S3)를 거칠 수 있다. 이 단계(S3)에서는 파쇄된 화장실 폐기물로 제조된 고형연료(100)의 열량을 조절할 수 있도록 열량조절제를 혼합하고, 고형연료(100)가 성형 후 쉽게 부서지는 것을 방지하기 위해 응고제도 함께 혼합하여 혼합체를 구성할 수 있다.In addition, the crushed toilet waste may go through the step (S3) of mixing the caloric control agent and the coagulant to form a mixture. In this step (S3) by mixing the calorific control agent to adjust the calorie of the solid fuel (100) made of crushed toilet waste, by mixing the coagulant also to prevent the solid fuel (100) is easily broken after molding The mixture can be constructed.

그리고, 화장실 폐기물에 열량조절제 및 응고제가 혼합하여 구성된 혼합체를 건조시키는 단계(S4)를 거칠 수 있다. 이 단계(S4)에서는 고열을 발생하는 건조실에 혼합체를 넣어 내부에 열을 가하는 형태로 화장실 폐기물을 건조할 수 있다.Then, the calorific control agent and the coagulant may be mixed with the toilet waste to dry the mixture (S4). In this step (S4) it is possible to dry the toilet waste in the form of applying the heat to the mixture in the drying chamber that generates high heat.

이때, 혼합체가 건조되는 조건은 100℃ 이상 150℃ 이하의 온도에서 건조될 수 있으며, 30시간 이상 40시간 이하의 시간 동안 건조될 수 있다.At this time, the conditions under which the mixture is dried may be dried at a temperature of 100 ° C or more and 150 ° C or less, and may be dried for 30 hours or more and 40 hours or less.

여기서, 건조온도가 100℃ 미만일 경우, 건조 온도가 낮아 건조시간이 오래 걸리며, 150℃를 초과할 경우, 주된 원료인 화장실 폐기물이 불에 탈 수 있다. 그리고 건조시간이 30시간 미만일 경우, 건조 시간이 적어 일가 건조가 되지 않는 부분이 발생하며, 40시간을 초과할 경우, 혼합체가 너무 건조되어 고형연료(100)의 성형 시 고형연료(100)가 쉽게 부서질 수 있다.Here, when the drying temperature is less than 100 ℃, the drying temperature is low, it takes a long time to dry, if it exceeds 150 ℃, the toilet waste, the main raw material can be burned. And when the drying time is less than 30 hours, there is less drying time occurs a part that does not dry, if more than 40 hours, the mixture is too dry, the solid fuel (100) easily when forming the solid fuel (100) Can break.

한편, 혼합체가 건조되었을 때의 수분의 함량은 15중량％ 이상 25중량％ 이하의 범위를 가질 수 있다. 여기서, 수분의 함량은 혼합체를 구성하는 화장실 폐기물 뿐만 아니라 화장실 폐기물과 함께 혼합된 열량조절제 및 응고제에 함유된 수분을 모두 포함한다.On the other hand, the moisture content when the mixture is dried may have a range of 15% by weight or more and 25% by weight or less. Here, the moisture content includes not only the toilet waste constituting the mixture but also all the moisture contained in the caloric control agent and the coagulant mixed with the toilet waste.

아울러, 혼합체의 수분의 함량이 15중량％ 미만인 경우, 수분의 함량이 미미하여 고형연료(100)를 연소하였을 때, 단시간 내에 고형연료(100)가 타버리기 때문에 지속적인 열을 공급하기 어려우며, 수분의 함량이 25중량％를 초과한 경우, 수분의 함량이 높아 고형연료(100)가 착화되지 않는 문제점이 발생할 수 있다.In addition, when the moisture content of the mixture is less than 15% by weight, when the solid fuel 100 is burned due to the insignificant water content, it is difficult to supply continuous heat because the solid fuel 100 burns within a short time, and the water content When the content exceeds 25% by weight, a problem may occur in that the solid fuel 100 does not ignite due to high moisture content.

그리고, 건조실에서 건조된 혼합체는 미립자로 분쇄하는 단계(S5)를 거칠 수 있다. 이 단계(S5)에서는 혼합체의 성형이 용이하도록 파쇄될 때의 크기보다 더 작은 크기 예컨대, 가루와 같은 작은 크기로 분쇄할 수 있다.In addition, the mixture dried in the drying chamber may be subjected to the step (S5) of grinding into fine particles. In this step S5, the mixture can be ground to a size smaller than the size when the mixture is crushed, for example, a small size such as powder.

한편, 혼합체를 분쇄할 때에는 분쇄기에 넣어 분쇄할 수 있는데, 이 분쇄기는 예컨대, 공지의 믹서기와 같이 임의로 형성된 통 안에 모터에 의해 회전하는 칼날이 설치되고, 이 칼날의 회전에 의해 화장실 폐기물이 분쇄되도록 구성될 수 있다.On the other hand, when the mixture is pulverized, it can be put in a pulverizer and pulverized. In this pulverizer, for example, a blade formed by a motor is installed in an arbitrarily formed cylinder such as a known mixer, so that the toilet waste is pulverized by the rotation of the blade. Can be configured.

이렇게 분쇄된 혼합체는 임의의 형상으로 고형연료(100)를 성형하는 단계(S6)를 거칠 수 있다. 이 단계(S6)에서는 화장실 폐기물을 사용자가 사용하기 편리하거나 불이 쉽게 착화 될 수 있는 형상으로 고형연료(100)를 형성할 수 있다.The pulverized mixture may be subjected to the step S6 of forming the solid fuel 100 into an arbitrary shape. In this step (S6) it is possible to form the solid fuel 100 in a shape that the toilet waste can be convenient for the user or easily ignited.

고형연료(100)는 고형연료(100)의 중앙으로 공기가 용이하게 유통될 수 있도록 내부가 빈 기둥형상으로 형성되는 것이 바람직하다(도 1 참조).The solid fuel 100 is preferably formed in a hollow columnar shape so that air can be easily distributed to the center of the solid fuel 100 (see FIG. 1).

아울러, 혼합체는 압출기 또는 압착기로 압출 또는 압착하는 형태로 임의의 형상으로 성형될 수 있다. 여기서, 압출기 또는 압착기는 공지의 구성이므로 상세한 설명은 생략한다.In addition, the mixture may be molded into any shape in the form of extrusion or compression by an extruder or a compactor. Here, since an extruder or a compactor is a well-known structure, detailed description is abbreviate | omitted.

따라서, 본 발명의 실시예에 따른 화장실 폐기물을 고형연료(100)는 폐기물을 사용하여 제조되기 때문에 제조단가를 대폭 낮출 수 있으며, 화석연료와 같이 연소 시 이산화황, 일산화탄소 같은 유해가스의 발생을 뿐만 아니라 매립되는 폐기물의 양을 줄여 환경오염을 감소시킬 수 있다.Therefore, the solid waste fuel according to the embodiment of the present invention, the solid fuel 100 is manufactured using the waste, so that the manufacturing cost can be significantly reduced, and not only generation of harmful gases such as sulfur dioxide and carbon monoxide during combustion, such as fossil fuel, Environmental pollution can be reduced by reducing the amount of waste that is landfilled.

또한, 주된 성분이 화장실 폐기물 즉, 종이류이기 때문에 열량이 높을 뿐만 아니라, 무게가 가볍고 분진 같은 것이 묻어나지 않아 취급이 용이하다.In addition, since the main component is toilet waste, that is, paper, not only is high in calories, but also light in weight and dust-free, which is easy to handle.

이상에서는 본 발명의 바람직한 실시예를 설명하였으나, 본 발명의 범위는 이 같은 특정 실시예에만 한정되지 않으며, 해당분야에서 통상의 지식을 가진 자라면 본 발명의 특허청구범위 내에 기재된 범주 내에서 적절하게 변경이 가능할 것이다.Although the preferred embodiment of the present invention has been described above, the scope of the present invention is not limited only to this specific embodiment, and those skilled in the art are appropriately within the scope described in the claims of the present invention. Changes will be possible.

100: 화장실 폐기물을 이용한 고형연료
S1: 이물질 제거 S2: 파쇄
S3: 혼합 S4: 건조
S5: 분쇄 S6: 성형100: solid fuel using toilet waste
S1: remove foreign substance S2: shred
S3: Mixed S4: Dry
S5: grinding S6: molding

Claims (7)

화장실 폐기물에서 종이류만 남도록 이물질을 제거하는 단계,
상기 이물질이 제거된 화장실 폐기물을 파쇄하는 단계,
상기 파쇄된 화장실 폐기물에 열량조절제 및 응고제를 혼합하여 혼합체를 구성하는 단계,
상기 혼합체를 고온에서 건조하는 단계,
상기 건조하는 단계에서 건조된 상기 혼합체를 분쇄하는 단계,
상기 분쇄된 혼합체를 압출 또는 압착하여 임의의 형상으로 성형하는 단계를 포함하는 것을 특징으로 하는 화장실 폐기물을 이용한 고형연료의 제조방법.Removing debris so that only paper remains in the toilet waste,
Crushing the toilet waste from which the foreign substances have been removed;
Mixing the calorie control agent and the coagulant with the crushed toilet waste to form a mixture,
Drying the mixture at a high temperature,
Pulverizing the dried mixture in the drying step,
And extruding or pressing the pulverized mixture to form a shape into an arbitrary shape. 제1항에 있어서,
상기 응고제는 물에 곡물가루를 혼합한 것을 특징으로 하는 화장실 폐기물을 이용한 고형연료의 제조방법.The method of claim 1,
The coagulant manufacturing method of a solid fuel using a toilet waste, characterized in that the grain powder mixed with water. 제1항에 있어서,
상기 열량조절제는 폐타이어 실밥인 것을 특징으로 하는 화장실 폐기물을 이용한 고형연료의 제조방법.The method of claim 1,
The calorie control method for producing a solid fuel using the toilet waste, characterized in that the waste tire seams. 제1항에 있어서,
상기 혼합체를 고온에서 건조하는 단계에서는 100℃ 이상 150℃ 이하의 온도에서 30시간 이상 40 시간 이하의 시간 동안 건조되는 것을 특징으로 하는 화장실 폐기물을 이용한 고형연료의 제조방법.The method of claim 1,
In the step of drying the mixture at a high temperature, a solid fuel using a toilet waste, characterized in that the drying for 30 hours or more and 40 hours or less at a temperature of more than 100 ℃ 150 ℃. 연소 시 화력을 발생하는 고형연료에 있어서,
화장실 폐기물이 70중량％ 내지 90중량％, 열량을 조절하는 열량조절제가 1중량％ 내지 20중량％ 및 상기 열량조절제와 상기 화장실 폐기물을 응고시키는 응고제를 0.1중량％ 내지 10중량％을 포함하고,
건조 후의 수분 함량은 15중량％ 내지 25중량％인 것을 특징으로 하는 화장실 폐기물을 이용한 고형연료.In solid fuels that generate fire power during combustion,
70 wt% to 90 wt% of toilet waste, 1 wt% to 20 wt% of calorie controlling agent to control calories, and 0.1 wt% to 10 wt% of coagulant coagulating the calorific agent and the toilet waste,
The moisture content after drying is 15 to 25 weight% solid fuel using the toilet waste characterized by the above-mentioned. 제5항에 있어서,
상기 열량조절제는 폐타이어 실밥인 것을 특징으로 하는 화장실 폐기물을 이용한 고형연료.The method of claim 5,
The calorie control solid fuel using toilet waste, characterized in that the waste tire seams. 제5항에 있어서,
상기 응고제는 물과 곡물가루의 혼합물인 것을 특징으로 하는 화장실 폐기물을 이용한 고형연료.The method of claim 5,
The coagulant is a solid fuel using a toilet waste, characterized in that the mixture of water and grain flour.
KR1020110006825A 2011-01-24 2011-01-24 a solid fuel manufactured by toilet garbage and a manufacturing method thereof KR20120085480A (en)