KR20120010094A - 다공성 경량 불연성 구조체 - Google Patents

다공성 경량 불연성 구조체 Download PDF

Info

Publication number
KR20120010094A
KR20120010094A KR1020110014511A KR20110014511A KR20120010094A KR 20120010094 A KR20120010094 A KR 20120010094A KR 1020110014511 A KR1020110014511 A KR 1020110014511A KR 20110014511 A KR20110014511 A KR 20110014511A KR 20120010094 A KR20120010094 A KR 20120010094A
Authority
KR
South Korea
Prior art keywords
layer
porous
porous lightweight
skin layer
lightweight non
Prior art date
Application number
KR1020110014511A
Other languages
English (en)
Inventor
윤선영
Original Assignee
윤선영
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 윤선영 filed Critical 윤선영
Priority to KR1020110014511A priority Critical patent/KR20120010094A/ko
Priority to KR1020110042075A priority patent/KR101846304B1/ko
Priority to PCT/KR2011/004660 priority patent/WO2012011677A2/ko
Publication of KR20120010094A publication Critical patent/KR20120010094A/ko

Abstract

본 발명은 다공성 경량 불연성 구조체에 관한 것으로서, 본 발명에 따른 다공성 경량 불연성 구조체는 흙으로 형성한 표피층과 메인층를 포함하는 것을 그 구성상의 특징으로 한다.
본 발명에서 제안하고 있는 다공성 경량 불연성 구조체에 따르면, 표피층, 보강리브 및 메인층를 불연성 재질인 흙으로 제작하고, 상기 메인층에 공동을 형성하여 경량화, 단열성 및 방음성이 향상시키고, 보강리브에 의해 압축강도 및 휨강도를 증대시킬 수 있다.

Description

다공성 경량 불연성 구조체{POROUS LIGHTWEIGHT FIRE RESISTANT STRUCTURAL BODY}
본 발명은 다공성 경량 불연성 구조체에 관한 것으로서, 보다 상세하게는 흙으로 제조되는 특정 형태의 물체에 다공질을 형성하여 경량화하고 단열성 및 방음성을 향상시키며, 보강리브를 설치하여 압축강도 및 휨강도를 증대시킬 수 있는 다공성 경량 불연성 구조체에 관한 것이다.
일반적으로 건축물 내벽이나 칸막이 등의 용도로 발포 폴리스틸렌 폼, 석고보드, 샌드위치 패널 등의 패널이 많이 사용되고 있다. 이러한 건축용 패널은 차폐성이 우수하지만 통기성이 부족하며, 환경호르몬과 같은 유해물질이 배출되기도 하는 문제점이 있다. 또한 석고보드는 단열성과 방음성도 만족할만한 수준이 되지 못하고, 발포 폴리스틸렌 폼은 쉽게 연소되며 연소시 유독가스를 발생시키기 때문에 사용이 규제되고 있다.
한편 최근 들어 친환경적이고 건강에 유익한 천연자재로 제조되는 건축용 패널의 수요도 늘고 있는데, 주로 목재, 천연 대리석, 옥, 황토, 세라믹 등이 주재료로 이용되고 있다. 그런데 이러한 천연자재로 제조된 건축용 패널의 경우에는 경량이고, 단열성, 불연성, 방음성, 방수성 등의 성질이 두루두루 요구되는 건축 자재의 요구 성능을 모두 만족시키기 어렵고, 가격 또한 비싸다는 문제점이 있다.
천연재료 중에 비교적 가격이 저렴하고, 다른 재료와의 혼합 등의 방법으로 건축자재의 요구 성능을 구현하기 쉬운 재료로서 대표적인 것이 황토이다. 황토를 이용한 건축용 패널은 다음과 같은 것들이 제안된 바 있다.
대한민국 등록특허 제375321호에는 황토를 분쇄하여 1차 소성시킨 황토를 선별하여 분말상 황토와 입자상 황토로 구분한 후 분말상 황토와 입자상 황토 그리고 점토와 규조토를 섞어 황토혼합물을 만들고, 다시 발포형 폴리스틸렌 수지와 적당량의 물을 첨가하고 균일하게 혼합되도록 교반하여 패널을 성형 제조한 후, 건조와 1000?1100℃ 범위에서 소성 단계를 거쳐 제조되는 건축 내장재용 다공성 패널에 대한 기술이 설명되어 있다.
이러한 황토 다공성 패널은 기공에 의한 중량 감소로 다루기가 쉬워 시공이 편리하고, 단열, 방음 및 습도 조절의 효과가 좋으며, 황토색 특유의 미관을 지니므로 마감재로도 사용이 가능한 다목적 용도의 내장재로 사용할 수 있다.
반면에 다공질을 형성하기위하여 발포형 폴리스틸렌 수지를 사용하고 있기 때문에 소성시 발포형 폴리스틸렌 수지가 연소하여 유독가스를 발생하는 문제점이 있을 뿐만 아니라, 전체적으로 강도가 약하기 때문에 취급 및 시공시 파손의 우려가 크고, 하중이 작용하지 않는 곳에만 사용할 수 있기 때문에 사용용도가 내장 마감재 정도로 한정되는 문제점이 있다.
다른 예로서 대한민국 등록특허 제391704호에서는 황토를 건조하여 가루로 분쇄한 후 펄프, 벤토나이트, 활성탄 가루를 배합한 배합토를 그늘에서 20 일간 숙성시키고, 숙성된 배합토를 물로 반죽하여 압출롤러에 의하여 일정 두께의 패널로 생산하여 다시 그늘에서 20일간 자연 건조시킨 후, 다공의 공기층이 형성되도록 270?300℃에서 소성 처리하는 소성과정을 거쳐 제조되는 건축용 황토 패널에 대한 기술이 설명되어 있다.
이렇게 제조된 건축용 황토 패널은 소성시 생성된 공기층 때문에 통기성을 가지며 패널의 내부에 포함된 활성탄 가루가 공기를 정화하는 등의 효과를 갖는다.
하지만 황토, 펄프, 벤토나이트, 활성탄 가루를 배합하여 압출성형 후 소성하는 형태로 제조됨에 따라 상기 소재들을 견고하게 응집할 수 있는 바인더가 없는 관계로 강도가 매우 약하여 쉽게 파손되는 현상이 발생되는 단점이 있을 뿐만 아니라, 또한 내부의 공기층은 단순히 소성시 함유된 수분의 증발에 의하여 형성되는 극히 미세한 것이므로, 단열이나 방음 등의 효과는 그렇게 크지 않다는 문제점이 있다.
본 발명은 상기한 종래 건축용 패널들을 형성하는 구조체가 가지는 문제점을 해결하고자 하는 것으로서, 구조체를 불연성 재질인 흙을 이용하여 다층 구조로 제조하되 내부에 공동을 형성하여 중량이 감소되며, 강도와 단열성 및 방음성은 우수하고, 제조비용은 저렴한 다공성 경량 불연성 구조체을 제공하는 것을 과제로 한다.
상기한 과제를 해결하기 위하여 본 발명의 다공성 경량 불연성 구조체는 공동입자를 배합한 반죽된 흙을 소정의 형상으로 성형 후 소성하여 공동입자를 탄화 또는 용융시킴으로서 다공질이 형성되도록 한 구조체에 있어서, 상기 구조체를 다층 구조로 형성하되 공동입자의 탄화 또는 용융에 의하여 형성되는 다공질이 다층 구조의 일부 층 또는 전체 층에 형성되도록 구성한 것이다.
그리고 구조체의 다층구조는 바깥쪽의 표피층과 표피층 안쪽의 메인층으로 이루어지는데, 통상 표피층은 공동입자를 함유하지 않는 반죽된 흙으로 형성하고 메인층은 공동입자를 함유하는 반죽된 흙으로 형성하게 된다.
이에 더하여 메인층을 다시 다층 구조로 형성할 수 있으며, 이때 표피층의 가장 먼 쪽에 형성된 층으로부터 표피층의 가장 가까운 쪽에 형성된 층으로 갈수록 각 층에 형성된 공동의 크기가 점차적으로 작아지도록 형성하는 것이 바람직하다.
그리고 메인층에는 표피층과 연결된 보강리브를 더 형성하여 구조체의 강도를 보강할 수도 있다. 이 때 보강리브의 일단이 연결된 표피층에는 상기 보강리브의 길이방향을 따라 보강리브의 폭보다 더 큰 폭을 갖게 형성하는 체결부에 나사 등을 쉽게 박아 넣을 수 있도록 구성함으로써 벽체 등에 쉽게 고정 할 수 있도록 한다.
한편 본 발명의 구조체는 건축용 패널이나 타일 등의 용도로 사용할 수 있도록 판형으로 형성될 수 있으며, 온돌 패널 등의 용도로 사용하고자 할 때에는 구조체가 서로 연속적으로 연결될 수 있는 다면체로 형성하는 것이 좋다. 또한 구조체를 중공 원통형으로 형성하여 파이프의 외주면을 감싸도록 함으로써 파이프의 보온 또는 보냉 용도로 사용할 수도 있다.
온돌 패널 등에 사용하기 위하여 구조체를 다면체로 형성한 경우에는 바닥면과 측면은 표피층을 형성하고 상부면은 메인층이 노출되도록 형성하며, 그 노출면에는 홈부를 형성하여 온수 파이프 등을 배관할 수 있도록 한다. 이 때 노출면의 상부에는 분리되는 구조의 표피층, 즉 덮개층(덮개 패널)이 더 설치되는 것이 바람직하다.
그리고 파이프 보온 보냉용으로 사용하기 위하여 구조체를 중공 원통형으로 형성한 경우에는 파이프를 길이 방향으로 분할할 수 있는 구조로 형성하여 파이프에 쉽게 탈착 할 수 있도록 하는 것이 좋다.
또한 본 발명의 다층 구조를 이루는 구조체를 형성하는데 적합한 흙의 종류는 점토, 황토, 실트. 백토 또는 고령토 등이며, 다층 구조를 형성할 때 필요한 성질을 얻기 위하여 각 층마다 다른 종류의 흙을 사용하거나 교호로 사용할 수 있으며, 모두 동일한 흙을 사용할 수도 있다. 또 필요에 따라서는 서로 다른 종류의 흙을 혼합하여 사용하는 것도 가능하다.
그리고 소성된 상기 다층 구조의 구조체 외표면에는 금속판, 시트지 또는 유약으로 형성되는 마감층을 형성할 수 있으며, 금속판이나 시트지 등을 사용하는 경우에는 접착제를 이용하여 구조체 외표면에 부착할 수 있다.
본 발명에서 제안하고 있는 다공성 경량 불연성 구조체는 불연성 재질이면서 가장 흔한 재료인 흙으로 제작하므로 제조비용이 저렴하고, 다공질을 형성하므로 대단히 가볍고 단열성 및 방음성이 우수하여 건물의 내?외장재, 바닥재 또는 천장재, 칸막이, 파이프 단열재 등의 다양한 용도로 사용할 수 있는 효과가 있다.
구조체 안쪽은 공동의 크기가 커서 무게 감소효과가 크며, 표면 쪽으로 공동의 크기가 점점 작아지도록 구성하여, 흙 종류로 형성된 구조체의 강도 부족 문제가 해결되는 효과가 있다.
구조체의 표피층에 공동을 형성하지 않는 경우 표면의 강도가 매우 높아져 파손의 우려가 줄어들며, 구조체 외표면에 금속판이나 시트지 등으로 마감층을 형성할 때 필요한 접착제 도포시 접착제가 구조체 내부로 스며들어 접착력이 떨어지는 현상을 방지할 수 있다. 또한 마감층을 유약을 발라 처리할 때도 유약이 구조체 내부로 과도하게 스며들어가는 현상을 방지하는 효과를 거둘 수 있다.
이아 같이 본 발명의 구조체에 유약이나 금속판 시트지 등으로 형성되는 마감층을 더 형성하면 더 미려한 형태의 제품을 제조할 수 있다
한편 본 발명의 보강리브는 구조체의 흙 종류로 성형된 구조체가 갖는 취약한 압축강도 및 휨강도를 개선할 수 있으며, 보강리브의 일단에 보강리브의 길이방향을 따라 형성한 체결부는 나사, 못 등의 결합부재를 이용하여 벽면 등에 설치함에 있어 패널이 파손되는 것을 방지하고 아울러 시공을 용이하게 할 수 있는 효과를 얻을 수 있다.
한편 본 발명은 주재료가 흙이므로 성형 자유도가 높아 다양한 형태의 구조체를 제조할 수 있는데, 상부에 배관을 삽입할 수 있는 홈부를 형성한 다면체로 성형하는 경우 건물 바닥면 난방공사 시공에 적합한 온돌 패널로 사용할 수 있고, 중공 원통형으로 성형하는 경우에는 파이프의 보온 보냉을 위한 단열재로 사용할 수 있다.
또한 사용하는 흙도 점토, 황토, 실트. 백토 또는 고령토 등 반죽이 가능한 입자크기를 갖는 것이라면 어느 것이든 자유롭게 사용할 수 있다. 따라서 흙의 종류에 따라 지니고 있는 고유의 성질을 자유롭게 이용할 수 있고, 또 두 종류 이상의 흙을 혼합하여 필요한 성질을 갖는 흙을 제조하여 사용하는 것도 자유롭다.
도 1은 본 발명 실시예1의 부분 사시도이다.
도 2는 보강리브가 형성된 본 발명 실시예1의 부분 사시도이다.
도 3은 본 발명 실시예2의 부분 사시도이다.
도 4는 마감층이 형성된 본 발명 실시예2의 부분 사시도이다.
도 5는 본 발명 실시예3의 단면도이다.
도 6은 본 발명 실시예3에서 덮개층을 제거한 상태의 사시도이다.
도 7은 도 6에서 곡선형 홈부가 더 형성된 상태의 사시도이다.
도 8은 본 발명 실시예4의 부분 사시도이다.
이하에서는 첨부된 도면들을 참조하여, 본 발명의 실시예1에 따른 다공성 경량 불연성 구조체에 대하여 상세하게 설명하기로 한다.
도 1은 실시예1의 일부를 도시한 사시도이다.
실시예1의 다공성 경량 불연성 구조체는 정방형 또는 직방형의 패널 형태로 제조될 수 있다. 상기 패널은 바깥쪽의 표피층(110)과 안쪽의 메인층(140)으로 이루어진 다층 구조를 기본 구성으로 한다.
또한 표피층(110)의 외부에는 마감층(160)을 추가로 형성할 수 있다. 마감층(160)은 금속판, 시트지 또는 유약 등으로 형성할 수 있으며, 금속판이나 시트지 등을 사용하는 경우에는 난연성 접착제를 이용하여 표피층(110)에 부착할 수 있다.
그리고 마감층(160)의 양끝에는 구조체 내측을 향하여 소정 깊이로 구부린 굽힘부(161)를 형성하는 것이 바람직하다. 굽힘부(161)는 본 실시예1의 패널을 연속하여 조립할 때 패널과 패널 사이의 접촉이 미려하게 이루어지도록 한다.
표피층(110)은 불연성 재질인 흙을 반죽하여 성형한다. 이 때 흙은 비교적 입자가 고운 것을 사용하는데, 예를 들면 점토, 황토, 실트. 백토 또는 고령토 등과 같은 것이 있다. 특히 점토는 주변에서 가장 흔하게 구할 수 있으므로 경제성을 갖는다.
메인층(140)은 다양한 크기의 공동입자를 배합한 흙을 반죽하여 성형한다. 메인층(140)에 사용하는 흙은 상기 표피층(110)과 동일한 것이어도 좋고, 물성이 다른 것을 사용할 수도 있다.
상기 공동입자는 구조체를 제조하는 과정에서 내부에 다공질을 형성하기위하여 배합하는 입자를 총칭하여 이르는 말로서, 톱밥, 목탄, 발포성수지 등이 이에 해당한다.
본 발명의 구조체는 메인층(140)과 표피층(110)을 각각의 금형에서 제조하여 이를 적층하는 방법으로 제조할 수 있으며, 다중사출금형을 이용하여 각층을 동시에 사출하면서 적층하는 방법으로 제조할 수도 있다.
상기 방법으로 적층된 메인층(140)과 표피층(110)은 소성과정을 거치게 된다. 통상 흙성분에는 유리질 성분이 포함되어 있으며 소성과정에서 이 유리질이 용융된다. 그리고 상기 메인층(140)과 표피층(110) 사이의 경계면에서 용융된 유리질이 접착제 역할을 하여 각 층을 서로 접합시키게 된다. 만일 유리질 성분이 부족한 흙이 재료로 사용되는 경우에는 흙을 반죽할 때 별도로 유리질을 첨가할 수 있다.
한편 상기 소성과정에서 공동입자는 탄화 또는 용융되므로, 공동입자가 배합된 메인층(140)은 내부에 무수히 많은 공동이 형성되어 다공질이 된다. 이러한 다공질 구조 때문에 구조체는 무게가 가벼워지며 단열성, 방음성이 향상된다.
한편 메인층(140)은 외측에서 내측으로 갈수록 공동의 크기가 큰 다공질을 갖는 다층구조로 형성할 수 있다. 이 경우 상기 메인층(140)의 내부 공동의 크기를 모두 크게 형성한 경우보다 강한 강도를 갖도록 할 수 있으며, 내부 공동의 크기를 모두 작게 형성한 경우보다는 상기 공동에 더 많은 공기를 내포할 수 있게 되므로 단열성, 방음성을 더욱 향상시킬 수 있다.
보강리브(130)도 판 형상으로 형성하고, 상기 표피층(110)과 동일한 재료를 사용하여 성형하여도 좋고, 물성이 다른 흙을 사용할 수 도 있다.
그리고 도 2 도시된 바와 같이 실시예1은 상하부 표피층(110) 사이에 다수의 보강리브(130)를 소정 간격으로 형성할 수 있다 있다. 이 때 보강리브(130)는 구조체의 길이 방향을 따라 길게 형성하는 것이 바람직하다.
상기와 같은 구조에 의해 상하부 표피층(110)과 보강리브(130)는 내부에 공간부가 형성되는데, 이 공간부에 메인층(140)이 형성된다.
보강리브(130)는 구조체의 강도를 보강하는 지지하는 지지프레임 역할을 한다. 즉 다공질의 메인층(140)은 압축하중이나 휨 하중에 매우 취약하며, 메인층(140)을 단순히 표피층(110)으로 덮은 구조체 역시 압축하중이나 휨 하중에 약하다. 따라서 보강리브(130)를 설치하여 구조체에 가해지는 하중에 저항하는 압축강도 및 휨강도를 증가시킴으로써, 구조체가 쉽게 파손되는 것을 방지할 수 있다.
또한, 상기 메인층(140)은 보강리브(130)를 좌우 양측을 메우고 있으므로 보강리브(130)를 지지하는 역할을 하게 된다. 가령, 구조체의 표피층(110)에 압축하중 또는 휨하중이 가하지는 경우에, 상기 메인층(140)은 상기 보강리브(130)의 좌우 양측을 지지하여 상기 보강리브(130)가 좌굴(buckling)되는 것을 방지하게 된다.
결국 상기 메인층(140)과 보강리브(130)의 상보효과에 의하여 구조체(100) 전체의 압축강도 및 휨강도가 개선된다.
상기 메인층(140), 표피층(110)(120), 보강리브(130) 상호간의 결합력은 소성과정에서 용융된 유리질에 의하여 증대시킬 수 있다.
또한 상기 메인층(140)을 공동의 크기를 달리하는 복수 층으로 형성한 경우에도, 소성과정에서 각각의 층은 인접하는 층과 흙에 포함된 유리질이 용융되어 상호 접합되므로 일체화 된다.
상기와 같은 실시예1의 다공성 경량 불연성 구조체(100)는 패널 형태이므로 건물의 내?외장재 및 바닥재로 사용하기 적합하다.
도 3은 실시예2의 일부를 도시한 사시도이다.
실시예2의 다공성 경량 불연성 구조체(100)는 건축물의 내ㅇ외장용 패널로 사용되는 형태를 도시한 것이다.
실시예2는 실시예1과 마찬가지로 다층 구조, 즉 바깥쪽의 표피층(110)과 안쪽의 메인층(140)으로 이루어지는 것을 기본 구성으로 하며, 다수의 보강리브(130)가 소정 간격으로 더 형성될 수 있다.
실시예2의 구조체(100)의 재질 및 제조과정은 실시예1과 동일하다.
다만 실시예2는 구조체 측면이 맞물려 조립될 수 있도록 'ㄱ'자와 'ㄴ'자 형상으로 대향하도록 형성하는 특징이 있다. 이렇게 구조체의 양측면이 맞물리도록 하면 연속적인 조립 작업을 신속하게 수행할 수 있다.
맞물림 구조는 상기 'ㄱ'자와 'ㄴ'자 형상 이외에 요철 형상이나 쐐기 형상 등의 다양한 형상으로 형성할 수 있다.
또한 실시예2는 도 3에 도시된 것처럼, 구조체의 표피층(110) 중 어느 일면에 나사나 못 등의 결합부재(150)가 체결되는 체결부(131)를 형성할 수 있다. 이때 체결부(131)는 상기 표피층(110)과 접하는 보강리브(130)의 일단에 형성하는 것이 좋다.
그리고 체결부(131)는 보강리브(130)의 폭보다 더 큰 폭을 가지도록 형성하고, 나사나 못 등의 길이를 수용할 수 있도록 표피층의 두께 보다 두껍게 형성하는 것이 바람직하다.
체결부(131)는 상기 보강리브(130)를 따라 구조체의 길이방향으로 길게 형성할 수 있으며, 나사, 못 등의 결합부재(150)에 의해 파손되지 않는 강도를 가지도록 형성한다.
체결부(131)는 결합부재(150)를 사용하여 구조체를 건물의 벽면 등에 고정할 때 이용된다.
도 4는 도3에 도시된 실시예2의 표피층(110)의 외부에 마감층(160)을 추가로 형성한 상태를 도시한 것이다. 마감층(160)의 재질이나 형성방법은 실시예1과 동일하다.
도 5는 본 발명의 실시예3의 단면도이다.
실시예3의 다공성 경량 불연성 구조체(100')은 건축물의 내장 패널, 바람직하게는 난방용 내장 패널로 사용되는 형태를 도시한 것이다.
실시예3은 실시예1과 마찬가지로 다층 구조, 즉 바깥쪽의 표피층(110)과 안쪽의 메인층(140)으로 이루어지는 것을 기본 구성으로 하며, 다수의 보강리브(130)가 소정 간격으로 더 형성될 수 있다.
그리고 상기 메인층(140')의 상면에는 온돌 패널의 길이방향을 따라 직선 또는 곡선모양의 홈부(141')를 형성한다. 상기 홈부(141')에는 파이프 또는 호스가 삽입 설치된다. 파이프 또는 호스의 설치된 패널의 상부는 덮개층(120')을 추가로 설치하여 덮을 수 있다.
실시예3의 구조체(100')의 재질 및 제조과정은 실시예1과 동일하다.
또한 표피층(110')과 보강리브(130')의 구성 및 효과 역시 실시예1에서 설명한 바와 같다.
실시예3의 구조체(100')가 바닥재로 사용되는 경우, 상기 메인층(140')의 상면에 형성된 홈부(141')에는 난방용 파이프나 호스를 삽입하여 난방 패널로 사용할 수 있다.
즉 도6에 도시된 직선형 홈부(141')를 갖는 구조체(100')와 도7에 도시된 곡선형 홈부(141')를 갖는 구조체(100')을 각각의 홈부가 이어지도록 연속하여 바닥면에 배치하고, 상기 홈부(141')에 맞추어 파이프나 호스를 삽입함으로써 배관작업을 용이하게 할 수 있다.
상기 메인층(140')은 외측에서 내측으로 갈수록 공동의 크기가 큰 다공질을 갖는 다층구조로 형성할 수 있다.
또한 홈부(141')가 형성된 층에 공동이 가장 큰 다공질을 형성하고 표피층(110') 및 보강리브(130') 쪽으로 갈수록 공동이 점점 작아지도록 다공질 층을 형성할 수도 있는데, 이 경우 다층구조를 형성하기가 용이해 지는 장점이 있다.
상기 메인층(140')에 형성된 다공질은 난방용 파이프의 열이 건물의 바닥으로 전도되는 것을 차단한다.
덮개층(120')는 표피층(110)과 동일한 재료를 사용할 수 있으며, 흑운모 등과 같이 축열성이 좋은 재료를 판재 형태로 가공하여 제조하여도 좋다.
도 8은 다공성 경량 불연성 구조체(100)를 파이프 단열재로 사용하는 형태의 실시예4를 도시한 것이다.
실시예4는 실시예1과 마찬가지로 다층 구조, 즉 바깥쪽의 표피층(110)과 안쪽의 메인층(140)으로 이루어지는 것을 기본 구성으로 하며, 파이프(170)의 외주면을 감쌀 수 있는 중공 원통형 구조를 갖는다.
바람직하게는 도8에 도시된 것처럼 상기 원통형이 좌우 한 쌍으로 분할 형성되는 것이 좋으며, 마주보는 분할면은 서로 맞물려 쉽게 조립될 수 있도록 단차를 형성 한다.
상기 맞물림 구조는 단차 형상 이외에 요철 형상이나 쐐기 형상 등의 다양한 형상으로 형성할 수 있다.
실시예4의 표피층(110)과 메인층(140)의 재질 및 제조과정 및 구조는 실시예1과 동일하며, 표피층(110)의 외부에 실시예1과 같이 마감층을 추가로 형성하여도 좋다.
이상 설명한 본 발명은 본 발명이 속한 기술분야에서 통상의 지식을 가진 자에 의하여 다양한 변형이나 응용이 가능하며, 본 발명에 따른 기술적 사상의 범위는 아래의 특허청구범위에 의하여 정해져야 할 것이다.
100, 100': 구조체 110, 110': 표피층
120': 덮개층 130, 130': 보강리브
131: 체결부 140, 140': 메인층
141': 홈부 150 : 결합부재
160 : 마감층 170 : 파이프

Claims (13)

  1. 공동입자를 배합한 반죽된 흙을 소정의 형상으로 성형 후 소성하여 공동입자를 탄화 또는 용융시킴으로써 다공질이 형성되도록 한 구조체에 있어서,
    상기 구조체는 다층 구조로 이루어지고,
    상기 공동입자의 탄화 또는 용융에 의하여 형성되는 다공질이 상기 다층 구조의 일부 층 또는 전체 층에 형성되어 있는 것을 특징으로 하는 다공성 경량 불연성 구조체.
  2. 청구항 1에 있어서,
    상기 구조체의 다층구조는 바깥쪽의 표피층과 표피층 안쪽의 메인층으로 이루어지되,
    상기 표피층은 공동입자를 함유하지 않는 반죽된 흙으로 형성되고,
    상기 메인층은 공동입자를 함유하는 반죽된 흙으로 형성되는 것을 특징으로 하는 다공성 경량 불연성 구조체.
  3. 청구항 2에 있어서,
    상기 메인층은 다시 다층 구조를 이루고 있고, 표피층의 가장 먼 쪽에 형성된 층으로부터 표피층의 가장 가까운 쪽에 형성된 층으로 갈수록 각 층에 형성된 공동의 크기가 점차적으로 작아지도록 형성한 것을 특징으로 하는 다공성 경량 불연성 구조체.
  4. 청구항 3에 있어서,
    상기 메인층에는 표피층과 연결된 보강리브가 형성되어 있는 것을 특징으로 하는 다공성 경량 불연성 구조체.
  5. 청구항 1 내지 청구항 4 중 어느 한 항에 있어서,
    상기 구조체는 판형으로 형성되는 것을 특징으로 하는 다공성 경량 불연성 구조체.
  6. 청구항 1 내지 청구항 4 중 어느 한 항에 있어서,
    상기 구조체는 서로 연속적으로 연결될 수 있는 다면체로 형성되는 것을 특징으로 하는 다공성 경량 불연성 구조체.
  7. 청구항 1 내지 청구항 4 중 어느 한 항에 있어서,
    상기 구조체는 중공 원통형으로 형성되는 것을 특징으로 하는 다공성 경량 불연성 구조체.
  8. 청구항 4에 있어서,
    상기 보강리브의 일단이 연결된 표피층에는 상기 보강리브의 길이방향을 따라 형성하고, 상기 보강리브의 폭보다 더 큰 폭을 갖는 체결부를 형성한 것을 특징으로 하는 다공성 경량 불연성 구조체.
  9. 청구항 6에 있어서,
    상기 다면체의 구조체는,
    바닥면과 측면은 표피층이 형성되고, 상부면은 메인층이 노출되며, 그 노출면에는 홈부를 형성한 것을 특징으로 하는 다공성 경량 불연성 구조체.
  10. 청구항 9에 있어서,
    상기 노출면의 상부에는 분리되는 구조의 표피층이 설치되는 것을 특징으로 하는 다공성 경량 불연성 구조체.
  11. 청구항 7에 있어서,
    상기 구조체는 중공 원통형의 길이 방향으로 분할되는 구성을 갖는 것을 특징으로 하는 것을 특징으로 하는 다공성 경량 불연성 구조체.
  12. 청구항 1 내지 청구항 4 중 어느 한 항에 있어서,
    상기 다층 구조를 이루는 구조체를 형성하는 흙은 각 층별로 점토, 황토, 실트. 백토 또는 고령토 중에 어느 하나이거나 혼합 된 것을 특징으로 하는 다공성 경량 불연성 구조체.
  13. 청구항 1 내지 청구항 4 중 어느 한 항에 있어서,
    소성된 상기 다층 구조의 구조체 외표면에는 금속판, 시트지 또는 유약으로 형성되는 마감층이 더 포함되는 것을 특징으로 하는 다공성 경량 불연성 구조체.
KR1020110014511A 2010-07-20 2011-02-18 다공성 경량 불연성 구조체 KR20120010094A (ko)