KR20110110387A - Rubberized asphalt membrane and felt sheet complex waterproofing material for the exterior waterproofing of the concrete structure - Google Patents
Rubberized asphalt membrane and felt sheet complex waterproofing material for the exterior waterproofing of the concrete structure Download PDFInfo
- Publication number
- KR20110110387A KR20110110387A KR1020100029664A KR20100029664A KR20110110387A KR 20110110387 A KR20110110387 A KR 20110110387A KR 1020100029664 A KR1020100029664 A KR 1020100029664A KR 20100029664 A KR20100029664 A KR 20100029664A KR 20110110387 A KR20110110387 A KR 20110110387A
- Authority
- KR
- South Korea
- Prior art keywords
- asphalt
- rubber
- waterproofing
- weight
- waterproofing material
- Prior art date
Abstract
본 발명은 속건성 아스팔트 화합물, 합성고무접착제, 합성고분자수지 접착제, 천연광물질섬유, 기타 기능성 첨가제등을 주원료로 한 고무아스팔트 도막방수재를 겔(gel) 상태로 제조하여 1회의 도포작업만으로도 1mm정도의 두께를 충족할 수 있을 뿐만 아니라 벽면에서 1mm정도 도포시에도 흘러내리지 않게 시공이 가능하고, 상기 고무아스팔트 도막방수재에 더하여 인장성능과 내균열성이 보강된 아스팔트 펠트시트를 겔상의 고무아스팔트 도막방수층 위에 연속 깔기작업을 수행함으로써 신뢰적인 방수성능을 확보하고 방수시공을 간편하게 행할 수 있는 콘크리트 구조물의 외부방수를 위한 고무아스팔트 도막 및 펠트시트 복합방수재에 관한 것이다.
본 발명은 스트레이트 런 아스팔트(Straight Run Asphalt), 블로운 아스팔트(Blown Asphalt) 또는 스트레이트 런 아스팔트와 블로운 아스팔트를 혼합한 아스팔트 중 선택된 하나와 석유용제를 혼합한 속건성 아스팔트화합물(Quick Drying Asphalt Compound)을 주원료로 하되, 상기 속건성 아스팔트 화합물 60~80중량%에 아스팔트 개질제로서의 합성고무 접착제 5~15중량%, 접착강화제로서의 합성고분자수지 접착제 5~10중량%, 천연 광물질 필러류 5~15중량%, 천연셀룰로우즈 섬유 3~5중량% 및 기타 분산제, 산화방지제등의 기능성 첨가제 0.5~1중량%를 혼합하여 겔상태로 제조된 고무아스팔트 도막방수재; 및 상기 고무아스팔트 도막방수재의 상부에 연속으로 깔아 도포하는 아스팔트 펠트시트를 포함하는 콘크리트 구조물의 외부방수를 위한 고무아스팔트 도막 및 펠트시트 복합방수재를 제공한다.The present invention is a rubber asphalt coating waterproofing material made of a fast-drying asphalt compound, synthetic rubber adhesive, synthetic polymer resin adhesive, natural mineral fiber, other functional additives, etc. as a main raw material in a gel (gel) state of about 1mm only one coating operation Not only can satisfy the requirements, but it can be installed so that it does not flow down even when it is applied about 1mm from the wall surface, and in addition to the rubber asphalt coating waterproofing material, an asphalt felt sheet reinforced with tensile performance and crack resistance is continuously formed on a gel-like rubber asphalt coating waterproofing layer. The present invention relates to a rubber asphalt coating film and a felt sheet composite waterproofing material for external waterproofing of a concrete structure that can ensure reliable waterproofing performance and easily perform waterproofing by carrying out a laying operation.
The present invention relates to a quick dry asphalt compound (Quick Drying Asphalt Compound) in which one selected from a straight run asphalt, a blow asphalt (Blown Asphalt) or asphalt mixed with a straight run asphalt and blown asphalt and a petroleum solvent. The main raw material, but 60 to 80% by weight of the fast-drying asphalt compound 5 to 15% by weight of synthetic rubber adhesive as asphalt modifier, 5 to 10% by weight of synthetic polymer resin adhesive as an adhesive strengthening agent, 5 to 15% by weight of natural mineral fillers, natural Rubber asphalt coating waterproofing material prepared in a gel state by mixing 3 to 5% by weight of cellulose fibers and 0.5 to 1% by weight of other functional additives such as dispersants and antioxidants; And it provides a rubber asphalt coating film and felt sheet composite waterproofing material for the external waterproofing of the concrete structure, including an asphalt felt sheet that is continuously spread on the upper portion of the rubber asphalt coating waterproofing material.
Description
본 발명은 건축물의 옥상, 지하 주차장의 상부 슬래브, 지하외벽, 지하기초바닥 및 지하 콘크리트 구조물 등과 같은 콘크리드 구조물의 비노출형 외부방수공사에 적용되는 도막 및 시트 복합방수재에 관한 것으로, 더욱 상세하게는 겔(Gel) 상태의 점성을 유지하는 아스팔트 도막 방수기능과 접착기능을 함께 부여한 고무아스팔트 도막방수재와, 상기 도막방수재의 상부에 방수성이 뛰어나며 도막방수재와도 완전한 접착을 이룰 수 있는 아스팔트 펠트시트를 조합함으로써 신뢰성있는 방수성능을 구현하며, 아스팔트 시트 방수층의 들뜸, 박리현상 등의 문제점을 개선함과 동시에 시공성을 향상시킬 수 있는 콘크리트 구조물의 외부방수를 위한 고무아스팔트 도막 및 펠트시트 복합방수재에 관한 것이다.
The present invention relates to a coating and sheet composite waterproofing material that is applied to non-exposed external waterproofing of concrete structures such as roof tops of buildings, upper slabs of underground parking lots, underground exterior walls, underground basement floors, and underground concrete structures. Combination of rubber asphalt coating waterproofing material that provides both waterproof and adhesive function of asphalt coating film to maintain viscosity of gel state, and asphalt felt sheet which is excellent in waterproofness on top of the coating material and can achieve perfect adhesion with coating waterproofing material. The present invention relates to a rubber asphalt coating film and felt sheet composite waterproofing material for external waterproofing of concrete structures, which can improve reliability and at the same time improve the workability of the asphalt sheet waterproofing layer by implementing reliable waterproofing performance.
일반적으로, 건축구조물의 옥상이나 지하 주차장의 상부 슬래브 또는 지하외벽 등의 지하 콘크리트 구조물의 외부방수를 행하는 전통적인 방수시공방법으로는 석유화학계열에서 얻은 고체의 블로운 아스팔트, 아스팔트 펠트, 아스팔트 루핑을 주성분으로 하여 만든 방수재를 이용하여 겹층시공을 행하는 아스팔트 8층방수공법이 있는데, 상기 방수시공방법은 공사현장에서 고체의 아스팔트를 고온(220~250℃)가열용융시에 발생되는 연기와 냄새에 의한 환경공해문제가 있으며, 겹층시공으로 작업공종이 복잡할 뿐만 아니라, 지하방수에서 수직외벽면의 경우 용융된 아스팔트의 흘러내림으로 인해 시공이 불가능한 문제점이 있다.In general, the traditional waterproofing method for waterproofing underground concrete structures such as roof top of building structures, upper slabs of underground parking lots or underground outer walls is mainly composed of solid blown asphalt, asphalt felt and asphalt roofing obtained from petrochemical series. There is an 8-layer waterproofing method for asphalt layered construction using a waterproofing material made of water. The waterproof construction method is an environment due to smoke and odor generated during high temperature (220 ~ 250 ℃) heating and melting of solid asphalt at a construction site. There is a pollution problem, and the construction work is not only complicated by layered construction, but also in the case of the vertical outer wall surface in the underground waterproofing, there is a problem that construction is impossible due to the flow of molten asphalt.
이러한 문제점을 개선하여 최근에 널리 사용되고 있는 방수공법은 도1에 도시된 바와 같이 폴리에스터 부직포 혹은 폴리프로필렌(P.P) 직포등의 합성수지를 중심보강재로 하여 양면에 SBS고무아스팔트 콤파운드를 일정두께로 피복시키고, 상부표면은 규사 또는 폴리에칠렌 필름을 접착 성형하고, 하부표면에는 폴리에칠렌 필름이나 실리콘 박리지를 부착하여 자체접착력을 갖게 만든 롤(ROLL)형의 방수시트를 이용한 개량 아스팔트시트 방수공법이다. The waterproofing method, which is widely used in recent years to improve this problem, is coated with SBS rubber asphalt compound on both sides with synthetic resin such as polyester nonwoven fabric or polypropylene (PP) woven fabric as the main reinforcement as shown in FIG. The upper surface is an improved asphalt sheet waterproofing method using a roll (ROLL) type waterproof sheet made by adhesive molding a silica sand or a polyethylene film, and a lower surface by attaching a polyethylene film or a silicone release paper to have a self adhesive force.
이 밖에, 유기 고분자 재료인 폴리우레탄 수지와 정제타르를 혼합한 탄성고무성분의 도막방수재를 사용하는 타르우레탄 도막방수공법, 수용성 고무아스팔트 도막방수공법, 벤토나이트 시트방수공법등이 제안되어 현재 사용되고 있다.In addition, a tar urethane coating waterproofing method using an elastic rubber coating waterproofing material in which a polyurethane resin, which is an organic polymer material, and refined tar is mixed, a water-soluble rubber asphalt coating waterproofing method, a bentonite sheet waterproofing method, and the like have been proposed and currently used.
상기에서 제시된 각각의 방수시공방법에서, 현장에서 가장 많이 적용되고 있는 아스팔트 시트 방수시공방법의 경우, 바탕면 처리- 프라이머 도포- 아스팔트 방수시트 깔기- 방수층 보호몰탈- 누름콘크리트 타설순으로 시공을 수행하고 있으며, 아스팔트 방수시트의 연결 이음매부위는 토우치를 사용하여 열용융접합방법을 행하고 있다.In each of the waterproof construction methods presented above, in the case of the asphalt sheet waterproof construction method that is most applied in the field, the construction is carried out in the order of ground treatment-primer coating-laying asphalt waterproof sheet-waterproof layer protective mortar-pressed concrete In addition, the connecting seam of the asphalt waterproof sheet is subjected to a hot melt welding method using a torch.
이러한 일련의 공정을 수행하는 아스팔트 시트 방수공법은 시공이 간편하여 공기를 단축할 수 있으며, 신장력이 우수하고 유연성있는 방수층을 형성할 수 있는 효과가 있는 반면에, 콘크리트 바탕면과의 접착력 부족으로 바탕면과의 들뜸이나 박리현상이 발생하고, 방수시트간 이음부의 열용융접합으로 인한 이음부의 수밀성저하로 빈번한 하자가 발생하고 있으며, 하자 발생시 결함부위의 발견이 어렵고, 보수비가 과다하게 소요되는 문제점을 내포하고 있다.Asphalt sheet waterproofing method that performs such a series of processes can be shortened by easy construction, and has the effect of forming an excellent stretch force and flexible waterproof layer, while the lack of adhesion to the concrete base surface Lifting and peeling of the surface occurs, and frequent defects occur due to the watertightness of the joints caused by the heat welding of the joints between the waterproof sheets, and when defects occur, it is difficult to find defects and excessive repair costs are required. It is implicated.
상기한 바와 같은 문제점을 극복하기 위하여 본원출원인은 도막방수재와 방수시트를 결합하여 방수성능을 개선하고 하자발생을 최소화하며, 공기를 단축할 수 있는 여러 특허들을 제안한 바 있다. 이들 도막 및 시트 이중방수공법으로 제안된 특허들의 일례로서 특허 제0571292호의 방수용 아스팔트 접착제 조성물과 그를 이용한 아스팔트 시트방수 시공방법, 특허 제0607154호의 고무아스팔트 도막 및 펠트 적층방수재 및 그의 시공방법, 특히 제0533231호의 도막방수층 보강을 위한 스트레치 고무아스팔트 펠트 및 그를 이용한 도막 및 펠트 적층방수재 등이 제안된 바 있다.In order to overcome the problems described above, the present applicant has proposed a number of patents that can combine the waterproof film and the waterproof sheet to improve the waterproof performance, minimize the occurrence of defects, and shorten the air. As an example of the patents proposed by these coating and sheet double waterproofing methods, the waterproof asphalt adhesive composition of Patent No. 0571292 and the asphalt sheet waterproofing method using the same, the rubber asphalt coating film and the felt laminated waterproofing material of Patent No. 0607154, and the construction method thereof, in particular, 0533231 Stretch rubber asphalt felt for reinforcing the coating waterproof layer of the arc and coating film and felt laminated waterproofing material using the same have been proposed.
상기에서 제시된 특허들은 빗물이나 습기등의 침투를 완전히 방지하기 때문에 방수층의 들뜸이나 박리가 발생되지 않으며, 콘크리트 피도체에 대한 강력한 접착력 및 탄력성, 신축성으로 도막방수층을 형성하여 콘크리트 크랙에 따른 저항력을 가지면서 간단한 시공으로 도막 및 시트이중방수효과를 극대화할 수 있는 것을 요지로 하고 있다. 상기 특허들의 필수구성인 고무아스팔트 도막방수재는 속성 경화되는 특징을 가지고 있으며, 도막방수기능 외에 접착기능으로 콘크리트 바탕면과의 접착성을 극대화하면서 방수시트와의 결합을 견고히 할 수 있으므로, 방수성능을 제고시키고, 프라이머 도포작업을 생략할 수 있어 공기를 단축시킬 수 있는 것에 큰 장점이 있다. Since the patents mentioned above completely prevent the infiltration of rainwater or moisture, there is no lifting or peeling of the waterproof layer. Its main purpose is to maximize the waterproofing effect of coating and sheet by simple construction. The rubber asphalt coating waterproofing material, which is an essential component of the patents, has the property of being hardened, and in addition to the waterproofing of the coating, it is possible to firmly bond with the waterproof sheet while maximizing the adhesiveness with the concrete surface by the adhesive function, thereby providing waterproof performance. There is a great advantage in that it is possible to shorten the air can be eliminated, the primer coating operation.
그러나, 이들 특허들에서 제시된 고무아스팔트 도막방수재의 경우 점도가 상온에서 80~100포이즈(poise) 정도의 묽은 액상 타입으로 이루어져 있어 콘크리트 바닥면에는 유용하게 적용될 수 있는 반면에, 벽체면 방수시에는 도막방수재가 흘러내려 작업이 어려운 문제점이 있다. 또한, 상기 도막방수재가 액상타입이므로 로울러나 붓 등으로 1회 도포시 얇은 피막정도의 두께를 갖는 도막방수층을 형성하기 때문에 현장에서 요구하는 일정 두께의 도막방수층 형성을 위해서는 1차 도포하여 건조시킨 후, 2차, 3차 도포를 수차례 시행하여야 하며, 이에 따른 작업시간이 많이 소요되는 문제점을 내포하고 있다.
However, the rubber asphalt coating waterproofing material proposed in these patents is composed of a thin liquid type with a viscosity of about 80 to 100 poise at room temperature, so that it can be usefully applied to concrete floors. There is a problem that the work is difficult because the waterproof material flows down. In addition, since the coating waterproofing material is a liquid type, a coating film waterproofing layer having a thickness of thin film is formed at the time of application with a roller or a brush. Second, third and third application should be carried out several times, which implies a problem that requires a lot of work time.
따라서, 본 발명은 상기의 제반 문제점을 해결하기 위하여 제안된 것으로서, 속건성 아스팔트 화합물, 합성고무접착제, 합성고분자수지 접착제, 천연광물질 필러, 천연셀룰로오즈 섬유, 기타 기능성 첨가제등을 주원료로 한 고무아스팔트 도막방수재를 흘러내리지 않는 겔(gel) 상태로 제조함으로써 1회의 도포작업만으로도 1mm정도의 도막 두께를 형성하며, 벽면에도 1mm정도 두께로 도포시 흘러내리지 않는 도막방수층 형성이 가능하고, 상기 고무아스팔트 도막방수층 위에 인장성능과 내균열성이 보강된 아스팔트 펠트시트의 연속 깔기작업을 수행함으로써 신뢰적인 방수성능을 확보하고 방수시공을 간편하게 행할 수 있는 콘크리트 구조물의 외부방수를 위한 고무아스팔트 도막 및 펠트시트 복합방수재를 제공함에 그 목적이 있다.Therefore, the present invention has been proposed to solve the above problems, the rubber asphalt coating waterproofing material mainly made of fast-drying asphalt compound, synthetic rubber adhesive, synthetic polymer resin adhesive, natural mineral filler, natural cellulose fiber, other functional additives, etc. It is manufactured in a gel state that does not flow down to form a coating film thickness of about 1mm with only one coating operation, it is possible to form a coating film waterproof layer that does not flow down when applied to a wall thickness of about 1mm, on the rubber asphalt coating film By providing continuous waterproofing of asphalt felt sheet reinforced with tensile performance and crack resistance, it provides rubber asphalt coating film and felt sheet composite waterproofing material for external waterproofing of concrete structure which can secure reliable waterproof performance and can easily perform waterproof construction. Has its purpose.
또한, 본 발명은 일반 아스팔트 시트 방수공법이 가지고 있는 방수층의 들뜸, 박리현상 등의 문제점을 개선함과 동시에, 도포기구를 이용하여 고무아스팔트 도막방수재를 바탕면에 도포 시공함으로써 균등한 두께의 도막방수층을 형성할 수 있으며, 이에 더하여 아스팔트 펠트시트를 시트 레이어(Sheet Layer)기구를 이용하여 연속작업으로 깔아줌과 동시에 균일한 하중분포로 눌러주는 기계화시공으로 균질한 방수층의 고품질을 확보할 수 있고, 방수시공에 따른 공기를 단축할 수 있는 콘크리트 구조물의 외부방수를 위한 고무아스팔트 도막 및 펠트시트 복합방수재를 제공함에 다른 목적이 있다.
In addition, the present invention improves the problems such as lifting, peeling phenomenon, etc. of the waterproof layer of the general asphalt sheet waterproofing method, and at the same time by coating the rubber asphalt coating waterproofing material on the base surface by using a coating device, the coating layer of the uniform thickness In addition, it is possible to secure the high quality of the homogeneous waterproof layer by the mechanized construction of pressing the asphalt felt sheet in a continuous operation using a sheet layer mechanism and simultaneously pressing it with a uniform load distribution. Another object is to provide a rubber asphalt coating film and felt sheet composite waterproofing material for external waterproofing of concrete structures that can shorten the air due to waterproof construction.
상기 목적을 달성하기 위하여 본 발명은, 스트레이트 런 아스팔트(Straight Run Asphalt), 블로운 아스팔트(Blown Asphalt) 또는 스트레이트 런 아스팔트와 블로운 아스팔트를 혼합한 아스팔트 화합물중 선택된 하나의 속건성 아스팔트 화합물을 주원료로 하되, 상기 속건성 아스팔트 화합물 60~80중량%에 아스팔트 개질제로서의 합성고무 접착제 5~15중량%, 접착강화제로서의 합성고분자수지 접착제5~10중량%, 천연 광물질 필러류 5~15중량%, 천연셀룰로우즈 섬유 3~5중량% 및 기타 분산제, 산화방지제 등의 기능성 첨가제 0.5~1중량%를 혼합하여 겔상태로 제조된 고무아스팔트 도막방수재; 및 상기 고무아스팔트 도막방수재의 상부에 연속으로 깔아 도포하는 아스팔트 펠트시트를 포함하는 콘크리트 구조물의 외부방수를 위한 고무아스팔트 도막 및 펠트시트 복합방수재를 제공한다.In order to achieve the above object, the present invention, a straight run asphalt (Straight Run Asphalt), blown asphalt (Blown Asphalt) or a fast-drying asphalt compound selected from a mixture of straight run asphalt and blown asphalt as a main raw material 60 to 80% by weight of the quick-drying asphalt compound, 5 to 15% by weight of synthetic rubber adhesive as asphalt modifier, 5 to 10% by weight of synthetic polymer resin adhesive as adhesive strengthening agent, 5 to 15% by weight of natural mineral fillers, natural cellulose Rubber asphalt coating waterproofing material prepared in a gel state by mixing 3 to 5% by weight of fibers and 0.5 to 1% by weight of other functional additives such as dispersants and antioxidants; And it provides a rubber asphalt coating film and felt sheet composite waterproofing material for the external waterproofing of the concrete structure, including an asphalt felt sheet that is continuously spread on the upper portion of the rubber asphalt coating waterproofing material.
본 발명의 제1 실시예에서는 1차 고무아스팔트 도막방수재 도포에 의한 도막방수층 위에 아스팔트 펠트시트 깔기로서 도막 및 펠트시트 복합방수층을 형성할 수 있다.In the first embodiment of the present invention, the coating film and the felt sheet composite waterproof layer may be formed by laying the asphalt felt sheet on the coating waterproof layer by applying the primary rubber asphalt coating waterproofing material.
본 발명의 제2 실시예에서는 상기한 제1 실시예의 구성인 고무아스팔트 도막방수재의 상부에 스트레치 아스팔트 펠트(Stretchy Asphalt Felt)가 가로(또는 세로)방향으로 깔려지고, 그 위에 2차 고무아스팔트 도막방수재가 도포되며, 상기 2차 고무아스팔트 도막방수재상에 아스팔트 펠트시트가 세로(또는 가로)방향으로 깔리는 것을 특징으로 하는 고무아스팔트 도막 및 펠트시트 적층 복합방수재를 제공한다. In the second embodiment of the present invention, stretch asphalt felt (Stretchy Asphalt Felt) is laid in the horizontal (or longitudinal) direction on top of the rubber asphalt waterproofing material, which is the configuration of the first embodiment, and the secondary rubber asphalt coating waterproofing material thereon. Is applied, and the asphalt asphalt sheet and felt sheet laminated composite waterproof material, characterized in that the asphalt felt sheet is laid in the longitudinal (or horizontal) direction on the secondary rubber asphalt coating waterproofing material.
상기한 본 발명의 제1 및 제2 실시예에서, 상기 속건성 아스팔트 화합물의 성분 중 아스팔트와 석유용제의 혼합비율은 아스팔트 65~85중량% : 석유용제 15~35중량% 인 것을 특징으로 한다. In the first and second embodiments of the present invention, the mixing ratio of asphalt and petroleum solvent among the components of the fast-drying asphalt compound is characterized in that the asphalt 65 to 85% by weight: 15 to 35% by weight petroleum solvent.
상기 합성고무 접착제는 이소부틸렌계 고무, 폴리이소부틸렌계 고무 또는 이소부틸렌계고무와 폴리이소부틸렌계 고무의 혼합물중 선택된 하나의 물질에 석유용제를 소정 비율로 혼합하되 이때, 상기 물질과 석유용제간의 혼합비율은 25~35중량% : 65~75중량%로 한 것을 특징으로 한다.The synthetic rubber adhesive may be mixed with a petroleum solvent in a predetermined ratio with a material selected from isobutylene rubber, polyisobutylene rubber, or a mixture of isobutylene rubber and polyisobutylene rubber at a predetermined ratio. The mixing ratio is 25 to 35% by weight: characterized in that 65 to 75% by weight.
상기 합성고분자수지 접착제는 요소수지 또는 송진에 석유용제를 혼합하되, 이때 요소수지 또는 송진과 석유용제간의 혼합비율은 25~35중량% : 65~75중량%로 한 것을 특징으로 한다.The synthetic polymer resin adhesive is mixed with petroleum solvent in urea resin or rosin, wherein the mixing ratio between urea resin or rosin and petroleum solvent is characterized in that 25 to 35% by weight: 65 to 75% by weight.
상기 천연광물질 필러는 해포석(sepiolite), 규회석, 탄산칼슘, 규사, 천연석분말이 혼합된 무기질 필러와 천연셀룰로오즈 섬유로는 펄프섬유가 사용된다.As the natural mineral filler, pulp fibers are used as inorganic fillers and natural cellulose fibers in which lysate (sepiolite), wollastonite, calcium carbonate, silica sand, and natural stone powder are mixed.
상기 아스팔트 펠트시트는 상부면이 폴리에스터 부직포를 아스팔트에 함침시켜 제조한 스트레치 아스팔트 펠트로 이루어지고, 하부면에는 상기 고무아스팔트 도막방수재와 일체화되도록 고무아스팔트 콤파운드로 이루어진 것을 특징으로 한다.The asphalt felt sheet is made of a stretch asphalt felt prepared by impregnating a polyester nonwoven fabric on asphalt, and the bottom surface is made of a rubber asphalt compound to be integrated with the rubber asphalt coating waterproofing material.
상기 스트레치 아스팔트 펠트는 폴리에스터 부직포를 아스팔트에 함침시켜 인장성능과 내균열성을 보강한 것을 특징으로 한다. 또한, 상기 스트레치 아스팔트 펠트(Stretchy Asphalt Felt)에 사용되는 폴리에스터 부직포는 70~140g/㎡인 것을 특징으로 한다.
The stretch asphalt felt is characterized by reinforcing polyester nonwoven fabric in asphalt to reinforce tensile performance and crack resistance. In addition, the polyester nonwoven fabric used in the stretch asphalt felt (Feetchy Asphalt Felt) is characterized in that 70 ~ 140g / ㎡.
전술한 바와 같이 본 발명에 따르면 다음과 같은 효과가 있다.As described above, the present invention has the following effects.
첫째, 고무아스팔트 도막 방수 및 접착기능을 갖는 겔상의 고무아스팔트 도막방수재를 콘크리트 바탕면위에 도포함과 동시에 아스팔트 펠트시트를 연속으로 깔아 일체화한 도막 및 펠트시트복합방수층을 형성함으로써, 아스팔트 펠트시트 방수층과 콘크리트 바탕면과의 들뜸이나 박리현상이 없으며 특히, 인력 시공에 의한 방수공사에서 흔히 발생될 수 있는 시공 부주의에 의한 하자발생빈도를 최소화할 수 있고, 콘크리트 바탕면과 완전히 접착된 도막 및 펠트시트 복합방수층 아래로 누수된 물이 흘러 다닐 수 없기 때문에 방수공사 시공 부주의에 의해 발생된 하자발생의 결함부위 발견이 쉽고, 부분 보수시공이 간편하다.First, by applying a gel-like rubber asphalt coating waterproofing material having a rubber asphalt coating waterproofing and adhesion function on the concrete base surface, and simultaneously assembling asphalt felt sheet to form a composite coating layer and a felt sheet composite waterproofing layer, thereby forming an asphalt felt sheet waterproof layer and There is no lifting or peeling phenomenon with the concrete base surface, and it is possible to minimize the frequency of defects caused by carelessness, which can be commonly generated in waterproof construction by manpower construction, and it is a composite film and felt sheet fully adhered to the concrete base surface. Since the leaked water cannot flow under the waterproofing layer, it is easy to find defects of defects caused by carelessness of waterproofing construction, and partial repair and construction is easy.
둘째, 겔 상의 고무아스팔트 도막방수재 도포와 동시에 아스팔트 펠트시트 깔기의 연속작업으로 작업공정이 단순하여 시공성이 우수하고, 동절기 시공이 가능하다.Second, the work process is simple due to the continuous work of laying the asphalt felt sheet and at the same time to apply the rubber asphalt coating waterproofing material on the gel, and the construction is excellent in winter.
셋째, 콘크리트 바탕면위에 도포되는 아스팔트 도막방수재를 1회의 도포작업만으로 0.8~1.2mm정도 두께의 도막방수층을 형성할 수 있으며, 이에 따른 작업시간을 단축할 수 있다. 또한, 상기 고무아스팔트 도막방수재가 겔타입으로 제조되어 접착성이 뛰어나 벽체면에도 흘러내리지 않는 도막 두께로 시공이 가능하다. Third, it is possible to form a waterproof layer of 0.8 ~ 1.2mm thick by only one coating operation of the asphalt coating waterproofing material to be applied on the concrete base surface, thereby reducing the work time. In addition, since the rubber asphalt coating waterproofing material is manufactured in a gel type, the rubber asphalt coating waterproofing material is excellent in adhesiveness, and thus construction can be performed with a coating thickness that does not flow down to the wall surface.
넷째, 겔상의 고무아스팔트 도막방수층과 인장 및 인열강도가 우수한 아스팔트 펠트시트의 복합방수층 형성후에 수평바닥면의 경우 별도의 방수층 보호몰탈이나 방수층 보호재의 설치가 필요없이 방수층 누름콘크리트 타설작업만으로 마감을 행할 수 있다. 이에 따라 시공공정을 줄여 공사비의 절감 및 공사기간을 단축할 수 있다. Fourth, after forming a composite waterproof layer of gel-like rubber asphalt coating waterproofing layer and asphalt felt sheet with excellent tensile and tear strength, the horizontal floor can be finished by only waterproofing layer pressing concrete without installing additional waterproofing layer protection mortar or waterproofing layer protection material. I can do it. Accordingly, the construction process can be reduced, thereby reducing the construction cost and shortening the construction period.
다섯째, 콘크리트 바탕면에 고무아스팔트 도막방수재를 도포기구를 이용하여 1회의 도포로 균일한 두께의 도막방수층을 형성하고, 그 위에 시트 레이어(Sheet Layer)기구를 사용하여 롤(Roll)형태의 아스팔트 펠트시트를 깔아주면서 펠트시트 위를 균일하중으로 눌러줌으로써 시공을 간편하게 할 수 있고, 기계화시공으로 균등한 방수층의 품질확보와 시공의 간편성으로 방수공사 기간을 단축할 수 있다.
Fifth, the rubber asphalt coating waterproofing material is applied to the concrete base surface using a coating device to form a coating film waterproofing layer having a uniform thickness, and using the sheet layer mechanism thereon, a roll-shaped asphalt felt The construction can be simplified by pressing the felt sheet on the felt sheet while spreading the sheet, and the waterproofing period can be shortened by ensuring the quality of the waterproof layer and simplicity of construction by mechanized construction.
도1은 일반적인 아스팔트 방수시트의 구성도.
도2는 본 발명에 의한 고무아스팔트 도막 및 펠트시트 복합방수재의 제1 실시예 구성을 나타낸 시공단면도.
도3a 및 도3b는 도2에 도시된 아스팔트 펠트시트의 구성을 나타낸 사시도 및 단면도.
도4는 본 발명에 의한 고무아스팔트 도막 및 펠트시트 복합방수재의 제2 실시예 구성을 나타낸 시공단면도.
도5은 제2 실시예에 사용된 스트레치 아스팔트 펠트의 구성을 나타낸 사시도.1 is a block diagram of a general asphalt waterproof sheet.
Figure 2 is a cross-sectional view showing the construction of a first embodiment of a rubber asphalt coating film and a felt sheet composite waterproofing material according to the present invention.
Figures 3a and 3b is a perspective view and a cross-sectional view showing the configuration of the asphalt felt sheet shown in FIG.
Figure 4 is a cross-sectional view showing the construction of a second embodiment of the rubber asphalt coating film and the felt sheet composite waterproofing material according to the present invention.
5 is a perspective view showing the configuration of the stretch asphalt felt used in the second embodiment;
이하, 첨부된 도2 내지 도5를 참조하여 본 발명의 실시예를 상세히 설명한다. Hereinafter, embodiments of the present invention will be described in detail with reference to FIGS. 2 to 5.
본 발명에 의한 콘크리트 구조물의 외부방수를 위한 고무아스팔트 도막 및 펠트시트 복합방수재는 고무아스팔트 도막방수재가 속성경화성을 가지면서 겔상태로 제조되어 콘크리트 바탕면뿐만 아니라, 벽체면에도 1회의 도포작업만으로 일정두께의 도막방수층을 형성할 수 있으며, 작업공정을 단순화하여 시공성이 우수해지도록 구현한 것이다.Rubber asphalt coating film and felt sheet composite waterproofing material for waterproofing the concrete structure according to the present invention is a rubber asphalt coating waterproofing material is produced in a gel state while having a hardening property, not only the concrete base surface, but only one coating operation on the wall surface The thickness of the coating layer can be formed, and the work process is simplified to realize excellent workability.
도2는 본 발명에 의한 고무아스팔트 도막 및 펠트시트의 복합방수재의 제1실시예 구성을 나타낸 시공단면도이고, 도3a 및 도3b는 도2에 도시된 아스팔트 펠트시트의 구성을 나타낸 사시도 및 단면도이다.Figure 2 is a cross-sectional view showing the construction of a first embodiment of a composite waterproof material of rubber asphalt coating film and felt sheet according to the present invention, Figures 3a and 3b is a perspective view and a cross-sectional view showing the configuration of the asphalt felt sheet shown in FIG. .
도면에 도시한 바와 같이 본 발명의 제1 실시예는 스트레이트 런 아스팔트(Straight Run Asphalt), 블로운 아스팔트(Blown Asphalt) 또는 스트레이트 런 아스팔트와 블로운 아스팔트를 혼합한 아스팔트 화합물 중 선택된 하나와 석유용제를 혼합한 속건성 아스팔트 화합물을 주원료로 하되, 상기 속건성 아스팔트 화합물 60~80중량%에 아스팔트 개질제로서의 합성고무 접착제 5~15중량%, 접착강화제로서의 합성고분자수지 접착제 5~10중량% 및 점도증가를 위하여 첨가되는 천연 광물질 필러류 5~15중량%, 증점효과를 발휘하고 점도를 증가시키며, 벽체면 도포시 흐름방지효과를 나타내는 천연 셀룰로오즈 섬유 3~5%와 기타 분산제, 산화방지제 등의 기능성 첨가제 0.5~1중량%를 혼합하여 겔(Gel)상태로 제조된 고무아스팔트 도막방수재; 및 상기 고무아스팔트 도막방수재의 상부에 연속으로 깔아 2차방수를 수행하는 아스팔트 펠트시트를 포함한다. As shown in the drawings, a first embodiment of the present invention is a petroleum solvent selected from a straight run asphalt (Straight Run Asphalt), blown asphalt (Blown Asphalt) or asphalt compound mixed with a straight run asphalt and blown asphalt The mixed quick-drying asphalt compound is used as a main raw material, and the fast-drying asphalt compound is added to 60 to 80% by weight of synthetic rubber adhesive 5 to 15% by weight as an asphalt modifier, 5 to 10% by weight of synthetic polymer adhesive as an adhesive reinforcing agent and viscosity increase. 5 ~ 15% by weight of natural mineral fillers, 3 ~ 5% of natural cellulose fiber showing the thickening effect and increasing the viscosity, and the flow preventing effect when applying the wall surface, and 0.5 ~ 1 functional additives such as dispersing agents and antioxidants Rubber asphalt coating waterproofing material prepared in a gel state by mixing the weight%; And an asphalt felt sheet which is continuously laid on top of the rubber asphalt coating waterproofing material to perform secondary waterproofing.
상기와 같이 구성된 본 발명의 제1 실시예에서는 고무아스팔트 도막방수재 도포와 아스팔트 펠트시트 깔기의 연속시공으로 도막 및 펠트시트 복합방수층을 형성할 수 있다.In the first embodiment of the present invention configured as described above, the coating film and the felt sheet composite waterproof layer can be formed by continuous application of the rubber asphalt coating waterproofing material coating and asphalt felt sheet laying.
상기한 조성비로 제조되는 겔상태의 고무아스팔트 도막방수재는 톱니형 고무흙손 도포공구를 사용하여 균일한 두께(본 실시예에서는 약 1mm)로 콘크리트 바탕면에 도포될 수 있고, 벽체면의 경우에도 톱니형 고무흙손을 이용하여 도포하게 된다. Gel-based rubber asphalt coating waterproofing material produced at the above composition ratio can be applied to the concrete base surface with a uniform thickness (about 1 mm in this embodiment) using a toothed rubber trowel coating tool, even in the case of wall surface It is applied using a rubber trowel.
도4는 본 발명에 의한 고무아스팔트 도막 및 시트의 복합방수재의 제2 실시예 구성을 나타낸 시공단면도이고, 도5는 제2 실시예에 사용된 스트레치 아스팔트 펠트의 구성을 나타낸 사시도이다.Fig. 4 is a construction sectional view showing the construction of the second embodiment of the composite waterproofing material of the rubber asphalt coating film and the sheet according to the present invention. Fig. 5 is a perspective view showing the construction of the stretch asphalt felt used in the second embodiment.
도면에 도시한 바와 같이 본 발명의 제2 실시예는 상기한 제1 실시예의 구성인 고무아스팔트 도막방수재를 바탕면위에 1차 도포하고, 상기 1차 고무아스팔트 도막방수재의 상부에 스트레치 아스팔트 펠트(Stretchy Asphalt Felt)가 가로(또는 세로)방향으로 깔려지고, 그 위에 상기 1차 도막방수재와 동일한 구성인 2차 고무아스팔트 도막방수재가 도포되며, 상기 2차 고무아스팔트 도막방수재상에 아스팔트 펠트시트가 세로(또는 가로)방향으로 도포된 구조로 이루어져 있다. As shown in the drawing, the second embodiment of the present invention is first applied on the base surface of the rubber asphalt coating waterproofing material, which is the configuration of the first embodiment, and stretch asphalt felt (Stetchy) on top of the primary rubber asphalt coating waterproofing material Asphalt Felt) is laid in the horizontal (or longitudinal) direction, and a secondary rubber asphalt coating waterproofing material having the same structure as the primary coating waterproofing material is applied thereon, and an asphalt felt sheet is vertically formed on the secondary rubber asphalt coating waterproofing material. Or transversely).
상기에서 제시한 본 발명의 제1 및 제2 실시예에서, 고무아스팔트 도막방수재는 상온에서 180~220포이즈(poise)정도의 겔타입으로 제조됨으로써 톱니형 고무흙손을 사용하여 고무아스팔트 도막방수재의 도포시에 1회 도포로서 0.8~1.2mm 두께의 도막방수층을 형성할 수 있어 작업시간을 단축할 수 있다.In the first and second embodiments of the present invention presented above, the rubber asphalt coating waterproofing material is manufactured in a gel type of about 180 to 220 poise at room temperature, thereby applying rubber asphalt coating waterproofing material using a toothed rubber trowel. With a single coating at a time, a water-proof coating layer of 0.8 to 1.2 mm thickness can be formed, thereby reducing work time.
본 발명의 제1 및 제2 실시예에서 제시된 구성에 대하여 좀더 상세하게 설명하면 다음과 같다.Referring to the configuration shown in the first and second embodiments of the present invention in more detail as follows.
먼저, 도막방수재의 주원료인 속건성 아스팔트 화합물에는 석유용제가 혼합된다. 상기한 속건성 아스팔트 화합물은 저온에서 콘크리트 바탕면과의 접착성을 부여하기 위한 것으로, 이때의 아스팔트와 석유용제간의 혼합비율은 아스팔트 화합물 65~85중량% : 석유용제 15~35중량%로 하는 것이 바람직하다. First, a petroleum solvent is mixed with the quick-drying asphalt compound which is the main raw material of the coating waterproofing material. The fast-drying asphalt compound is for imparting adhesion to the concrete base surface at low temperature, wherein the mixing ratio between asphalt and petroleum solvent is preferably 65 to 85% by weight asphalt compound: 15 to 35% by weight petroleum solvent. Do.
아스팔트는 상온에서 고체 상태로 되어있다. 따라서, 상온에서 상기 아스팔트에 합성고무, 합성고분자 수지접착제 및 광물질필러류 등을 첨가할 때, 혼합성을 좋게 하기 위하여 아스팔트와 석유용제를 혼합하여 액상형태로 조성하게 된다. 상기한 아스팔트와 석유용제간의 혼합비율중 석유용제의 혼합비율이 15중량% 미만일 경우 아스팔트 화합물의 높은 점도로 이소부틸렌계고무 또는 무기질 필러와 혼합성이 떨어져 균질성 확보가 어려워지고, 35중량%이상일때는 아스팔트 화합물 점도가 묽어져 혼합성은 양호하나 고무아스팔트 도막방수층의 두께 확보가 어려워 방수 성능이 저하되는 문제점이 있다.Asphalt is solid at room temperature. Therefore, when synthetic rubber, synthetic polymer resin adhesive, mineral fillers, etc. are added to the asphalt at room temperature, asphalt and petroleum solvent are mixed to form a liquid form in order to improve the mixing property. When the mixing ratio of the petroleum solvent is less than 15% by weight in the mixing ratio between the asphalt and the petroleum solvent, it is difficult to secure homogeneity due to the high viscosity of the asphalt compound and the incompatibility with the isobutylene rubber or the inorganic filler. As the asphalt compound viscosity is diminished, the mixing property is good, but it is difficult to secure the thickness of the rubber asphalt coating layer.
상기 합성고무 접착제는 이소부틸렌계 고무, 폴리이소부틸렌계 고무 또는 이소부틸렌계고무와 폴리이소부틸렌계 고무의 혼합물중 선택된 하나의 이소부틸렌계 물질에 석유용제를 소정 비율로 혼합하되 이때, 상기 물질과 석유용제간의 혼합비율은 25~35중량% : 65~75중량%로 하는 것이 바람직하다.The synthetic rubber adhesive may be mixed with an isobutylene-based material selected from isobutylene-based rubber, polyisobutylene-based rubber, or a mixture of isobutylene-based rubber and polyisobutylene-based rubber in a predetermined ratio. The mixing ratio between the petroleum solvents is preferably 25 to 35% by weight: 65 to 75% by weight.
이소부틸렌계 고무는 고체상태로 형성되어 있으며, 이는 아스팔트 화합물과 혼합할때 속건성 아스팔트 화합물의 석유용제가 용해력이 낮아 장시간 혼합을 하여야 하는 단점이 있기 때문에 상기한 바와 같은 혼합비율이 제시된 것이다. 즉, 이소부틸렌계 고무 25중량% 미만일때는 혼합성은 좋으나 석유 용제 함량이 많아 아스팔트 화합물의 점도가 묽어 도막 방수층의 두께 확보가 되지 않는 문제가 있다. 또한, 35중량% 이상일때는 높은 점도로 아스팔트 화합물과 다른 원료와의 혼합성이 떨어질 수 있다. 이소부틸렌계 고무 또는 폴리이소부틸렌계 고무와 혼합되는 석유용제는 방향족 탄화수소계 석유용제를 사용하는 것이 바람직하다.The isobutylene-based rubber is formed in a solid state, and since the petroleum solvent of the fast-drying asphalt compound has low solubility in mixing with the asphalt compound, the mixing ratio is suggested as described above. That is, when the isobutylene-based rubber is less than 25% by weight, the mixing properties are good, but the petroleum solvent content is high, so that the viscosity of the asphalt compound is thin and there is a problem in that the thickness of the coating layer is not secured. In addition, when the content is 35% by weight or more, the asphalt compound may have poor compatibility with other raw materials. The petroleum solvent mixed with isobutylene rubber or polyisobutylene rubber is preferably an aromatic hydrocarbon petroleum solvent.
상기 합성고무 접착제는 크랙에 대한 대응력과 내열성 및 콘크리트 바탕면과의 접착성을 부여하기 위한 것으로, 상기 합성고무 접착제의 혼합비율중 5중량% 미만일 경우에는 신장률과 접착강도가 저하되고, 15중량% 이상으로 투입될 경우에는 신장률이 너무 커서 오히려 접착강도가 저하될 우려가 있으며 비용이 상승하여 경제성을 해치는 문제점이 있다.The synthetic rubber adhesive is intended to impart coping with heat and heat resistance and adhesion to the concrete base surface, and when the mixing ratio of the synthetic rubber adhesive is less than 5% by weight, the elongation and adhesive strength are lowered and 15% by weight. In the case of the above-mentioned injection, the elongation rate is too large, and there is a concern that the adhesive strength may be lowered, and the cost may increase, thereby impairing economic efficiency.
상기 합성고분자수지 접착제는 요소수지 또는 송진을 석유용제에 용해한 것을 혼합하되, 이때. 상기 요소수지 또는 송진과 석유용제간의 혼합비율은 25~35중량% : 65~75중량%로 하는 것이 바람직하다.The synthetic polymer adhesive is mixed with urea resin or rosin dissolved in petroleum solvent, but at this time. The mixing ratio between the urea resin or rosin and petroleum solvent is preferably 25 to 35% by weight: 65 to 75% by weight.
요소수지는 상온에서 고체상태의 알갱이 형태로서 요소수지나 송진 단독으로는 속건성 아스팔트 화합물과 균일하게 혼합할 수 없어 석유용제를 혼합하게 된 것이다. 상기 요소수지와 석유용제의 혼합비율중 요소수지가 25중량% 미만일때는 도막 방수재가 콘크리트면과의 초기 접착성이 약해 흘러내리는 성질이 있으며 요소수지가 35중량%이상일때는 요소수지의 강성에 의하여 도막방수재가 콘크리트 크랙에 대응하지 못하고 균열이 발생하는 문제점이 있다. 요소수지 또는 송진과 혼합되는 석유 용제는 방향족 탄화 수소계 석유용제를 사용하는 것이 바람직하다.Urea resin is a solid granule at room temperature, and urea resin or rosin alone cannot be uniformly mixed with fast-drying asphalt compound, so petroleum solvent is mixed. When the urea resin is less than 25% by weight of the mixing ratio of the urea resin and the petroleum solvent, the coating film waterproofing material has a weak initial adhesiveness with the concrete surface, and when the urea resin is 35% by weight or more, There is a problem that the crack does not correspond to the concrete crack cracking material. Petroleum solvents mixed with urea resins or rosin are preferably aromatic hydrocarbon-based petroleum solvents.
상기 합성고분자수지 접착제는 접착력을 보강하고 인장강도, 내열성을 보강하기 위한 것으로, 이 성분의 혼합비율중 5중량% 미만으로 첨가될 경우 인장강도와 접착력이 약해지고, 10중량% 이상으로 첨가될 경우 강도가 커서 방수층에 크랙의 발생가능성이 큰 문제점이 있다.The synthetic polymer resin adhesive is to reinforce the adhesive strength and to strengthen the tensile strength and heat resistance, the tensile strength and adhesive strength is weakened when added to less than 5% by weight of the mixing ratio of this component, the strength when added to 10% by weight or more There is a large problem that the occurrence of cracks in the waterproof layer is large.
상기 아스팔트 화합물, 합성고무 접착제, 합성고분자 접착제의 제조에 사용되는 석유용제로는 솔벤트 또는 아로마틱계 용제가 사용될 수 있다.Solvent or aromatic solvent may be used as the petroleum solvent used in the production of the asphalt compound, synthetic rubber adhesive, synthetic polymer adhesive.
상기 천연광물질 필러는 해포석(sepiolite), 규회석, 탄산칼슘, 규사등이 사용되며, 천연셀룰로우즈 섬유로는 펄프섬유가 사용된다.The natural mineral filler is used in the form of haemulite (sepiolite), wollastonite, calcium carbonate, silica sand, etc., pulp fiber is used as the natural cellulose fibers.
상기 천연광물질 필러는 합성고무 접착제와 혼합되어 크랙에 대한 대응력을 부여하고, 또 접착강도를 증가시킬 수 있도록 하기 위한 것으로, 상기 천연광물질 필러의 혼합비율중 5중량% 미만일 경우에는 1회 도포에서 요구하는 도막두께의 형성이 어렵고, 15중량% 이상으로 투입될 경우에는 도막방수층에 균열이 발생하여 방수성능이 저하되는 문제점이 있다.The natural mineral filler is to be mixed with the synthetic rubber adhesive to give a crack resistance and to increase the adhesive strength, if less than 5% by weight of the mixing ratio of the natural mineral filler required in one application It is difficult to form the coating film, and if it is added at 15% by weight or more, there is a problem that the crack occurs in the coating film waterproofing layer and the waterproof performance is lowered.
상기 아스팔트 펠트시트(Asphalt Felt sheet)는 도3a 및 도3b에 도시한 바와 같이 폴리에스터 부직포를 아스팔트에 함침시켜 인장성능과 내균열성을 보강한 스트레치 아스팔트 펠트를 상부면으로 하고, 상기 스트레치 아스팔트 펠트의 하부면에 소정 두께의 고무아스팔트 콤파운드를 피복시킨 구조로 이루어진다.Asphalt felt sheet (Asphalt Felt sheet) is as shown in Figure 3a and 3b as the upper surface of the stretch asphalt felt reinforced with tensile performance and crack resistance by impregnating the polyester nonwoven fabric in asphalt, the stretch asphalt felt It consists of a structure in which a rubber asphalt compound of a predetermined thickness is coated on the lower surface of the.
본 발명의 실시예에서 상기 고무아스팔트 콤파운드는 아스팔트에 SBS(Styrene Butadiene Styrene) 고무가 혼합된 구조를 제시한다. 또한, 상기 고무아스팔트 콤파운드의 두께는 대략 1~3mm로 한다. 또한, 상기 고무아스팔트 콤파운드층 하부면에는 폴리에스터 부직포(PET 부직포), 폴리프로필렌 부직포(PP 부직포) 또는 이형필름 중 선택된 하나가 부착되어 있다. 상기 아스팔트 복합펠트시트의 최하부면이 폴리에스터 부직포로 이루어질 경우 단위면적당 질량이 40~60g/㎡인 것을 사용한다. In an embodiment of the present invention, the rubber asphalt compound presents a structure in which SBS (Styrene Butadiene Styrene) rubber is mixed with asphalt. In addition, the thickness of the rubber asphalt compound is approximately 1 to 3 mm. In addition, one selected from a polyester nonwoven fabric (PET nonwoven fabric), a polypropylene nonwoven fabric (PP nonwoven fabric), or a release film is attached to the lower surface of the rubber asphalt compound layer. When the lowermost surface of the asphalt composite felt sheet is made of a polyester nonwoven fabric, a mass per unit area of 40 to 60 g / m 2 is used.
상기 아스팔트 펠트시트 상부면의 스트레치 아스팔트 펠트는 폴리에스터 부직포를 아스팔트에 함침시켜 습기와 물의 침투를 방지하며 내구성이 뛰어나 아스팔트 펠트시트의 상부면에서 또다른 방수기능을 구현하게 된다.The stretch asphalt felt of the upper surface of the asphalt felt sheet is impregnated with polyester nonwoven fabric to prevent moisture and water penetration, and has excellent durability to implement another waterproof function on the upper surface of the asphalt felt sheet.
상기 스트레치 아스팔트 펠트는 폴리에스터 부직포를 아스팔트에 함침시켜 인장성능과 내균열성을 보강한 것을 사용한다. 또한 상기 스트레치 아스팔트 펠트는 도5에 도시한 바와 같이, 펠트와 펠트간의 겹침부위를 나타내는 오버랩 라인(over lap line)표시가 되어 있어 도막방수재상에 펠트를 깔아 도포할 때, 펠트의 겹침부위 시공을 정밀하게 할 수 있다. The stretch asphalt felt is used by impregnating a polyester nonwoven fabric in asphalt to reinforce tensile performance and crack resistance. In addition, as shown in Fig. 5, the stretch asphalt felt has an overlap lap line indicating the overlapping portion between the felt and the felt, and when the felt is laid on the coating waterproofing material, the overlapping portion of the felt is applied. I can do it precisely.
상기 아스팔트 펠트시트 구조 및 스트레치 아스팔트 펠트(Stretchy Asphalt Felt)에 사용되는 폴리에스터 부직포는 단위면적당 70~140g/㎡인 것을 사용하되, 바람직하기로는 단위면적당 100g/㎡인 것을 사용하는 것이다.Polyester nonwoven fabric used in the asphalt felt sheet structure and stretch asphalt felt (Stretchy Asphalt Felt) is used in the 70 ~ 140g / ㎡ per unit area, preferably to use 100g / ㎡ per unit area.
상기에서 제시된 스트레치 아스팔트 펠트 및 아스팔트 펠트시트는 고무아스팔트 도막방수층 위에 쉽게 깔 수 있도록 통상 롤(Roll) 형태로 제조된다.The stretch asphalt felt and the asphalt felt sheet presented above are usually manufactured in roll form so as to be easily laid on the rubber asphalt coating waterproof layer.
본 발명에 의한 고무아스팔트 도막방수재 및 아스팔트 펠트시트의 품질기준은 하기의 [표1]과 같다. Quality standards of rubber asphalt coating waterproofing material and asphalt felt sheet according to the present invention are shown in Table 1 below.
고무아스팔트 도막방수재
Rubber Asphalt Waterproofing Material
ASTM D2823 시험기준(Asphalt Roof Coatings)
ASTM D2823 Test Criteria (Asphalt Roof Coatings)
아스팔트 펠트시트
Asphalt Felt Sheet
KSF 4917 시험기준(개량 아스팔트 방수시트)
KSF 4917 test standard (improved asphalt waterproof sheet)
본 발명의 제1 실시예인 탄성이 뛰어난 고무아스팔트 도막방수층과 아스팔트 펠트시트층 구조와, 제2 실시예인 1차 고무아스팔트 도막방수재와 인장성능과 내균열성이 보강된 스트레치 아스팔트 펠트층, 2차 고무아스팔트 도막방수재 및 아스팔트 펠트시트층 구조는 적층시공으로 방수층을 형성함으로써 진동이 심한 콘크리트 구조물의 방수에 적합하게 사용될 수 있고, 콘크리트 구조체의 미세한 균열발생에 대한 대응성이 매우 우수하다. 또한, 적층방수공법의 특성으로 방수시공할 콘크리트 바탕면 정리가 간편하고, 고무아스팔트 도막방수재 도포와 아스팔트 펠트시트의 연속 깔기 작업으로 시공성이 우수하다. 이 밖에 돌출이 많은 복잡한 구조물에서도 무이음매의 방수층을 형성하고, 아스팔트의 가열없이 상온시공으로 시공성이 매우 간편하다.Rubber asphalt coating waterproofing layer and asphalt felt sheet layer structure having excellent elasticity, which is the first embodiment of the present invention, and primary asphalt asphalt coating waterproofing material which is the second embodiment, and stretch asphalt felt layer and secondary rubber reinforced with tensile performance and crack resistance Asphalt coating waterproofing material and asphalt felt sheet layer structure can be used for the waterproofing of the concrete structure with a lot of vibration by forming a waterproof layer in the laminated construction, and excellent response to the occurrence of minute cracks of the concrete structure. In addition, it is easy to clean up the concrete surface to be waterproofed due to the characteristics of the laminated waterproof method, and excellent workability by applying rubber asphalt coating waterproofing material and continuous laying of asphalt felt sheet. In addition, even in a complex structure with many protrusions, a seamless waterproof layer is formed, and construction is very easy by using at room temperature without heating the asphalt.
특히, 본 발명은 적층(5층) 방수층 형성에서 5번째 작업공정이 스트레치 아스팔트 펠트시트 대신에 일정 두께를 나타내는 아스팔트 펠트시트를 깔아줌으로써 적층방수층의 두께를 3mm 이상으로 형성할 수 있으며, 아스팔트 펠트시트 하부면의 고무아스팔트 콤파운드가 고무아스팔트 도막방수재와 완전한 접착효과를 나타낸다. In particular, the present invention can form the thickness of the laminated waterproof layer to 3mm or more by laying the asphalt felt sheet showing a certain thickness instead of the stretch asphalt felt sheet in the fifth (5 layer) waterproof layer formation, asphalt felt sheet The rubber asphalt compound of the lower surface shows a perfect adhesion effect with the rubber asphalt coating waterproofing material.
하기에서는 본 발명에 의한 고무아스팔트 도막 및 펠트시트 복합방수재의 시공예를 설명한다.Hereinafter, a construction example of the rubber asphalt coating film and the felt sheet composite waterproofing material according to the present invention will be described.
먼저, 방수공사를 시공할 콘크리트 구조물의 바탕 표면을 가능한 한 깨끗하고 편평하게 한다. 콘크리트 구조물 상판의 경우 콘크리트 표면은 가능한 건조해야 하며 바탕면에 묻어 있는 기름, 흙, 레이턴스 등의 이물질을 깨끗하게 제거하고 요철 부위는 면정리를 수행한다. First, make the base surface of the concrete structure to be waterproofed as clean and flat as possible. In the case of the concrete deck, the concrete surface should be as dry as possible. The foreign substances such as oil, soil, and latencies on the surface should be removed cleanly, and the irregularities will be cleaned.
바탕면 정리 작업이 끝난 후, 방수 시공할 바탕면 전체에 아스팔트 프라이머를 1평방미터당 0.3ℓ정도로 도포한다. After finishing the ground surface, apply asphalt primer about 0.3ℓ per 1 square meter to the entire surface to be waterproofed.
위의 아스팔트 프라이머 도포 경화후에 1차 도막방수재인 고무아스팔트 도막방수재를 소정 두께로 도포하여 고무아스팔트 도막방수층을 형성한다. 이때, 상기 고무아스팔트 도막방수재는 아스팔트 펠트시트의 폭만큼 바탕면에 도포한다. After the above asphalt primer coating curing, the rubber asphalt coating waterproofing material, which is the primary coating waterproofing material, is applied to a predetermined thickness to form a rubber asphalt coating waterproofing layer. At this time, the rubber asphalt coating waterproofing material is applied to the base surface by the width of the asphalt felt sheet.
여기서, 상기 1차 도막방수재인 고무아스팔트 도막방수재의 뛰어난 접착력에 의해 콘크리트 바탕면에 완전 접착되기 때문에 상기 아스팔트 프라이머 도포 공정은 생략할 수도 있다.Here, the asphalt primer coating process may be omitted because it is completely adhered to the concrete base surface by the excellent adhesion of the rubber asphalt coating waterproofing material which is the primary coating waterproofing material.
상기 도포과정에 이어 연속하여, 1차 도포된 고무아스팔트 도막방수층위에 롤 형상으로 감긴 아스팔트 펠트시트를 시트 레이어(sheet layer) 기구를 이용하여 연속으로 깔아주면서 균일하중으로 눌러주어 고무아스팔트 도막방수층 위에 아스팔트 펠트시트를 밀착시킨다.Subsequent to the coating process, the asphalt felt sheet wound in a roll shape on the first applied rubber asphalt coating waterproofing layer was spread by using a sheet layer mechanism, and then pressed with a uniform load, thereby providing asphalt on the rubber asphalt coating waterproofing layer. Adhere the felt sheet.
상기한 시공과정을 통하여 상기 아스팔트 펠트시트 하부면의 고무아스팔트 콤파운드가 고무아스팔트 도막방수층과 완전하게 접착되어 일체화됨으로써 도막 및 펠트시트의 복합방수층을 형성하게 된다.Through the construction process, the rubber asphalt compound of the lower surface of the asphalt felt sheet is completely bonded with the rubber asphalt coating waterproof layer to form a composite waterproof layer of the coating film and the felt sheet.
다음, 아스팔트 펠트시트간의 겹침시공시, 오버랩 표시부에 부착된 이형필름을 제거하면서 연결 아스팔트 펠트시트를 오버랩표시부에 겹쳐 깔아주며 시공한다.Next, when the overlapping construction between the asphalt felt sheets, the connecting asphalt felt sheet is overlapped with the overlap display portion while removing the release film attached to the overlap display portion.
상기 아스팔트 펠트시트간의 연결이음 끝단부위에는 아스팔트 매스틱(본원출원인에 의해 등록된 제0278173호)으로 보강도포하여 연결이음부의 수밀성을 강화한다. At the end of the connection joint between the asphalt felt sheet is reinforced with an asphalt mastic (0278173 registered by the present applicant) to enhance the watertightness of the connection joint.
상기 고무아스팔트 도막방수재 도포와 아스팔트 펠트시트 깔기 시공이 완료되면 방수층 위에 방수층 절연 폴리에틸렌 필름을 깔고 방수층 누름콘크리트를 타설하여 마감 시공을 수행한다.When the coating of the rubber asphalt waterproofing material and the laying of the asphalt felt sheet are completed, the waterproofing layer insulation polyethylene film is laid on the waterproofing layer, and the waterproofing layer press concrete is poured to finish the construction.
상기와 같이 구성되어 시공되는 본 발명은 건축구조물의 옥상지하기초 바닥지하외벽 및 지하주차장 상부 슬라브방수와 지하철 지하차도, 전력구, 통신구 등의 공동구와 같은 지하콘크리트 구조물의 외부방수에 적용할 수 있으며, 이 외에 방수가 필요한 모든 콘크리트 구조물 방수에 적용할 수 있다.The present invention constructed and constructed as described above can be applied to the exterior waterproofing of underground concrete structures such as the rooftop subsurface basement outer wall of the building structure and the upper slab waterproofing of the underground parking lot, and the underground tunnels, power holes, communication holes, etc. In addition, it can be applied to waterproofing all concrete structures requiring waterproofing.
이상에서 설명한 본 발명은 전술한 실시예 및 첨부된 도면에 의해 한정되는 것이 아니고, 본 발명의 기술적 사상을 벗어나지 않는 범위 내에서 여러 가지 치환, 변형 및 변경이 가능함은 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 있어 명백할 것이다.
The present invention described above is not limited to the above-described embodiment and the accompanying drawings, and various substitutions, modifications, and changes are possible within the scope without departing from the technical spirit of the present invention. It will be evident to those who have knowledge of.
Claims (16)
상기 고무아스팔트 도막방수재의 상부에 연속으로 깔아 도포하는 아스팔트 펠트시트를 포함하는 콘크리트 구조물의 외부방수를 위한 고무아스팔트 도막 및 펠트시트 복합방수재.
Straight run asphalt (Straight Run Asphalt), Blown Asphalt (Blown Asphalt) or one of the asphalt compounds mixed with straight run asphalt and blown asphalt, and the fast-drying asphalt compound mixed with petroleum solvent as the main raw material, 60 to 80% by weight, 5-15% by weight of synthetic rubber adhesive as asphalt modifier, 5-10% by weight of synthetic polymer resin adhesive as adhesive strengthening agent, 5-15% by weight of natural mineral fillers, thickening effect, increase viscosity Rubber asphalt coating waterproofing material prepared in a gel state by mixing 3 to 5% by weight of natural cellulose fibers showing a flow preventing effect when applying the wall surface; And
Rubber waterproofing coating and felt sheet composite waterproofing material for the external waterproofing of the concrete structure including an asphalt felt sheet that is continuously spread on the upper portion of the rubber asphalt coating waterproofing material.
상기 고무아스팔트 도막방수재는 분산제, 산화방지제 등의 기능성 첨가제 0.5~1중량%가 더 첨가되는 것을 특징으로 하는 콘크리트 구조물의 외부방수를 위한 고무아스팔트 도막 및 펠트시트 복합방수재.
The method of claim 1,
The rubber asphalt coating waterproofing material is a rubber asphalt coating film and felt sheet composite waterproofing material for external waterproofing of the concrete structure, characterized in that 0.5 ~ 1% by weight of functional additives, such as dispersing agent, antioxidant.
상기 고무아스팔트 도막방수재는 상온에서 180~220포이즈(poise) 정도의 겔(Gel)타입으로 제조되는 것을 특징으로 하는 콘크리트 구조물의 외부방수를 위한 고무아스팔트 도막 및 펠트시트 복합방수재.
The method of claim 1,
The rubber asphalt coating waterproofing material is a rubber asphalt coating film and felt sheet composite waterproofing material for external waterproofing of a concrete structure, characterized in that the gel (gel) type of about 180 ~ 220 poise at room temperature.
상기 고무아스팔트 도막방수재와 아스팔트 펠트시트를 교번적으로 적층되는 것을 특징으로 하는 콘크리트 구조물의 외부방수를 위한 고무아스팔트 도막 및 펠트시트 복합방수재.
The method according to any one of claims 1 to 3,
The rubber asphalt coating film and felt sheet composite waterproofing material for external waterproofing of the concrete structure, characterized in that the rubber asphalt coating waterproofing material and the asphalt felt sheet is alternately laminated.
상기 1차 고무아스팔트 도막방수재의 상부에 깔려지며, 폴리에스터 부직포를 아스팔트에 함침시켜 인장성능과 내균열성을 보강한 스트레치 아스팔트 펠트(Stretchy Asphalt Felt);
상기 1차 고무아스팔트 도막방수재와 동일한 조성물로 이루어져 상기 스트레치 아스팔트 펠트의 상부에 도포되는 2차 고무아스팔트 도막방수재; 및
상기 2차 고무아스팔트 도막방수재의 상부에 연속으로 깔려 도포되는 아스팔트 펠트시트를 포함하는 콘크리트 구조물의 외부방수를 위한 고무아스팔트 도막 및 펠트시트 복합방수재.
One of selected from straight run asphalt, blown asphalt or blown asphalt and a mixture of straight run asphalt and blown asphalt, and a fast-drying asphalt compound mixed with a petroleum solvent as a main raw material, the fast-drying asphalt compound 60 ~ 80% by weight of synthetic rubber adhesive 5-15% by weight of asphalt modifier, 5-10% by weight of synthetic polymer resin adhesive as adhesive strengthening agent, 5-15% by weight of natural mineral fillers, thickening effect, increasing the viscosity 3 ~ 5% by weight of natural cellulose fibers and 0.5 ~ 1% by weight of functional additives such as dispersants and antioxidants, which are applied to the surface of the wall, are applied in the form of gel and applied to the concrete surface Primary rubber asphalt coating waterproofing material;
Stretch asphalt felt is laid on the upper portion of the primary rubber asphalt coating waterproofing material, and reinforced with tensile performance and crack resistance by impregnating a polyester nonwoven fabric on asphalt;
A secondary rubber asphalt coating waterproofing material made of the same composition as the primary rubber asphalt coating waterproofing material and applied to an upper portion of the stretch asphalt felt; And
Rubber waterproofing coating and felt sheet composite waterproofing material for the external waterproofing of the concrete structure including an asphalt felt sheet is continuously spread on the upper portion of the secondary rubber asphalt coating waterproofing material.
상기 속건성 아스팔트 화합물의 성분 중 아스팔트와 석유용제의 혼합비율은 아스팔트 65~85중량% : 석유용제 15~35중량% 인 것을 특징으로 하는 속건성 아스팔트 화합물을 주성분으로 하는 콘크리트 구조물의 외부방수를 위한 고무아스팔트 도막 및 펠트시트 복합방수재.
The method according to any one of claims 1 to 3, 5,
The mixing ratio of asphalt and petroleum solvent among the components of the fast-drying asphalt compound is 65 to 85% by weight asphalt: 15 to 35% by weight of petroleum solvent, rubber asphalt for external waterproofing of the concrete structure mainly composed of the fast-drying asphalt compound Coating and felt sheet composite waterproofing material.
상기 합성고무 접착제는 이소부틸렌계 고무, 폴리이소부틸렌계 고무 또는 이소부틸렌계고무와 폴리이소부틸렌계 고무의 혼합물중 선택된 하나의 물질에 석유용제를 소정 비율로 혼합하되 이때, 상기 물질과 석유용제간의 혼합비율은 25~35중량% : 65~75중량%로 한 것을 특징으로 하는 콘크리트 구조물의 외부방수를 위한 고무아스팔트 도막 및 펠트시트 복합방수재.
The method according to any one of claims 1 to 3, 5,
The synthetic rubber adhesive may be mixed with a petroleum solvent in a predetermined ratio with a material selected from isobutylene rubber, polyisobutylene rubber, or a mixture of isobutylene rubber and polyisobutylene rubber at a predetermined ratio. The mixing ratio is 25 to 35% by weight: rubber asphalt coating film and felt sheet composite waterproofing material for external waterproofing of the concrete structure, characterized in that it was 65 to 75% by weight.
상기 합성고분자수지 접착제는 요소수지 또는 송진을 석유용제에 혼합한 것으로 혼합하되, 이때 요소수지 또는 송진과 석유용제간의 혼합비율은 25~35중량% : 65~75중량%로 한 것을 특징으로 하는 콘크리트 구조물의 외부방수를 위한 고무아스팔트 도막 및 펠트시트 복합방수재.
The method according to any one of claims 1 to 3, 5,
The synthetic polymer resin adhesive is mixed with urea resin or rosin mixed with petroleum solvent, wherein the mixing ratio between urea resin or rosin and petroleum solvent is 25 to 35% by weight: 65 to 75% by weight concrete Rubber asphalt coating film and felt sheet composite waterproofing material for waterproofing the structure.
상기 천연광물질 필러는 해포석(sepiolite), 규회석, 탄산칼슘, 규사 중 선택된 하나의 물질로 이루어지고, 천연셀룰로오즈 섬유는 펄프섬유로 이루어진 것을 특징으로 하는 콘크리트 구조물의 외부방수를 위한 고무아스팔트 도막 및 펠트시트 복합방수재.
The method according to any one of claims 1 to 3, 5,
The natural mineral filler is made of one material selected from haemulite (sepiolite), wollastonite, calcium carbonate, silica sand, natural cellulose fiber is made of pulp fiber rubber asphalt coating film and felt sheet for external waterproofing Composite waterproofing.
상기 아스팔트 펠트시트는 상부면이 폴리에스터 부직포를 아스팔트에 함침시켜 제조한 스트레치 아스팔트 펠트로 이루어지고, 하부면에는 상기 고무아스팔트 도막방수재와 조합되도록 고무아스팔트 콤파운드로 이루어진 것을 특징으로 하는 콘크리트 구조물의 외부방수를 위한 고무아스팔트 도막 및 펠트시트 복합방수재.
The method according to any one of claims 1 to 3, 5,
The asphalt felt sheet is made of a stretch asphalt felt prepared by impregnating a polyester nonwoven fabric on asphalt, and a lower surface of the asphalt felt sheet is made of rubber asphalt compound so as to be combined with the rubber asphalt coating waterproofing material. Rubber asphalt coating film and felt sheet composite waterproofing material.
상기 스트레치 아스팔트 펠트는 폴리에스터 부직포를 아스팔트에 함침시켜 인장성능과 내균열성을 보강한 것을 특징으로 하는 콘크리트 구조물의 외부방수를 위한 고무아스팔트 도막 및 펠트시트 복합방수재.
The method of claim 10,
The stretch asphalt felt is a rubber asphalt coating film and felt sheet composite waterproofing material for external waterproofing of the concrete structure, characterized in that the polyester non-woven fabric is impregnated into the asphalt to strengthen the tensile performance and crack resistance.
상기 스트레치 아스팔트 펠트(Stretchy Asphalt Felt)에 사용되는 폴리에스터 부직포가 70 ~ 140g/㎡인 것을 특징으로 하는 콘크리트 구조물의 외부방수를 위한 고무아스팔트 도막 및 펠트시트 복합방수재.
The method of claim 10,
Rubber asphalt coating film and felt sheet composite waterproofing material for external waterproofing of the concrete structure, characterized in that the polyester non-woven fabric used in the stretch asphalt felt (Stretchy Asphalt Felt) is 70 ~ 140g / ㎡.
상기 아스팔트 펠트시트의 고무아스팔트 콤파운드는 아스팔트에 SBS(Styrene Butadiene Styrene) 고무가 혼합된 것을 특징으로 하는 콘크리트 구조물의 외부방수를 위한 고무아스팔트 도막 및 펠트시트 복합방수재.
The method of claim 10,
Rubber asphalt compound of the asphalt felt sheet is a rubber asphalt coating film and felt sheet composite waterproofing material for external waterproofing of the concrete structure, characterized in that SBS (Styrene Butadiene Styrene) rubber is mixed with asphalt.
상기 스트레치 아스팔트 펠트는 일측면에 소정 폭의 오버랩 라인(over lap line)표시가 되어 있는 것을 특징으로 하는 콘크리트 구조물의 외부방수를 위한 고무아스팔트 도막 및 펠트시트 복합방수재.
The method of claim 5, wherein
The stretch asphalt felt rubber asphalt coating film and felt sheet composite waterproofing material for waterproofing the exterior of the concrete structure, characterized in that the one side is marked with an overlap line (overlap line) of a predetermined width.
상기 아스팔트 펠트시트의 일측 상부에 오버랩(over lap) 표시부가 형성되어 있으며, 이 오버랩 표시부 상에 이형필름이 부착되어 있는 것을 특징으로 하는 콘크리트 구조물의 외부방수를 위한 고무아스팔트 도막 및 펠트시트 복합방수재.
The method of claim 10,
An overlap display part is formed on an upper portion of the asphalt felt sheet, and a release film is attached to the overlap display part. The rubber asphalt coating film and the felt sheet composite waterproofing material for external waterproofing of the concrete structure.
상기 복합 아스팔트 펠트시트의 저면에 폴리에스터 부직포(PET 부직포), 폴리프로필렌 부직포(PP 부직포) 또는 이형필름 중 선택된 하나가 설치된 것을 특징으로 하는 콘크리트 구조물의 외부방수를 위한 고무아스팔트 도막 및 펠트시트 복합방수재.The method of claim 10,
Rubber asphalt coating film and felt sheet composite waterproofing material for external waterproofing of a concrete structure, characterized in that selected one of a polyester nonwoven fabric (PET nonwoven fabric), polypropylene nonwoven fabric (PP nonwoven fabric) or a release film is installed on the bottom surface of the composite asphalt felt sheet .