KR20190139627A - Waterproof sheet, complex waterproofing layer comprising thereof and manufacturing method of the same - Google Patents

Waterproof sheet, complex waterproofing layer comprising thereof and manufacturing method of the same Download PDF

Info

Publication number
KR20190139627A
KR20190139627A KR1020180066315A KR20180066315A KR20190139627A KR 20190139627 A KR20190139627 A KR 20190139627A KR 1020180066315 A KR1020180066315 A KR 1020180066315A KR 20180066315 A KR20180066315 A KR 20180066315A KR 20190139627 A KR20190139627 A KR 20190139627A
Authority
KR
South Korea
Prior art keywords
waterproof
layer
waterproof layer
sheet
composite
Prior art date
Application number
KR1020180066315A
Other languages
Korean (ko)
Inventor
배문옥
배장원
Original Assignee
배문옥
배장원
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 배문옥, 배장원 filed Critical 배문옥
Priority to KR1020180066315A priority Critical patent/KR20190139627A/en
Publication of KR20190139627A publication Critical patent/KR20190139627A/en

Abstract

The present invention provides a waterproof sheet, which has a modified asphalt compound waterproof layer and a tarpaulin sheet waterproof layer, a complex waterproof layer having the same, and a construction method thereof. According to the present invention, the complex waterproof layer is easy for identifying leakage defect portions and is capable of partial repair.

Description

방수시트, 이를 포함하는 복합 방수층 및 이의 시공방법{Waterproof sheet, complex waterproofing layer comprising thereof and manufacturing method of the same}Waterproof sheet, composite waterproofing layer comprising same and manufacturing method of the same}

본 발명은 공동 주택의 지하 주차장 상부 슬라브 방수 및 건축물의 옥상 방수, 지하철, 지하차도 공동구(전력구, 통신구) 등과 같은 지하 콘크리트 구조물의 외부 방수에 이용될 수 있는 개질 아스팔트 콤파운드 방수층 및 타포린 시트 방수층을 포함하는 방수시트, 이를 포함하는 복합 방수층 및 이의 시공 방법에 관한 것이다. The present invention is a modified asphalt compound waterproofing layer and tarpaulin sheet waterproofing layer that can be used for waterproofing the upper slabs of underground parking lots of apartment houses and roofing waterproofing of buildings, underground concrete structures such as subways, underground joints (power ports, communication ports), etc. It relates to a waterproof sheet, a composite waterproof layer comprising the same and a construction method thereof.

1900년대 이후 국내에서 건축 구조물의 옥상, 지하 기초바닥 및 지하외벽, 지하 주차장 상부 슬라브 방수와 지하철 지하차도 공동구(전력구, 통신구)등의 지하 콘크리트 구조물 외부 방수에 적용되어온 방수자재와 방수공법들의 종류를 분류해보면, 1910년~1970년대까지는 고체의 아스팔트를 공사현장에서 가열 용융하며 방수 바탕면에 도포와 동시에 아스팔트 펠트 또는 아스팔트 루핑을 적층시키는 방법으로 시공되는 열공법의 ‘아스팔트 3겹 8층 방수공법’이 일반적으로 적용되었다.Since the 1900's, waterproof materials and construction methods have been applied to the waterproofing of roof structures, underground foundation floors and basement walls of underground construction structures, upper slabs of underground parking lots, and the exterior waterproofing of underground concrete structures such as subway tunnels and public areas. According to the classification, 'Asphalt 3-ply 8-layer waterproofing' of the thermal method, which is constructed by heating and melting solid asphalt at the construction site from 1910 to 1970s, and applying asphalt felt or asphalt roofing at the same time as applying it to the waterproof surface. Public Law 'was generally applied.

상기 ‘아스팔트 3겹 8층 방수공법’은 1910년대에 일본으로부터 아스팔트를 도입하여 국내에 처음 적용되기 시작하였으며, 8층의 적층방수 시공으로서 방수층의 두께가 비교적 두꺼워, 방수 안전성이 있어 70여년 이상의 오랜 기간동안 적용실적을 나타내었으나, 고체의 블로운 아스팔트(Blown Asphalt)를 공사 현장에서 고온(220~250℃) 가열 용융 시에 발생되는 연기와 냄새 등으로 인한 환경공해 발생문제, 작업 시 작업인부들의 빈번한 화상사고 발생 위험문제, 아스팔트를 고온 가열 용융한 액상 상태에서의 도포로서 수직 벽체면에의 도포 시공 어려움과 3겹 8층의 방수 시공에 따르는 복잡한 작업공정으로서 방수 기능공의 특별한 시공 숙련도가 요구되며, 시공 인건비가 많이 소요되는 단점이 있다. Asphalt three-ply eight-layer waterproofing method was first applied to Korea after introducing asphalt from Japan in the 1910s, and the eight-layer laminated waterproof construction has a relatively thick thickness of waterproof layer, and it has waterproof safety for more than 70 years. Although the application results were shown during this period, environmental pollution caused by smoke and odor generated by melting solid blown asphalt (Blown Asphalt) at high temperature (220 ~ 250 ℃) at the construction site, The problem of frequent burn accidents, the application of the asphalt in a liquid state heated and melted at high temperature, and the complicated construction process due to the difficulty of application on the vertical wall surface and the waterproof construction of three layers and eight layers. However, there is a disadvantage that a lot of construction labor costs.

‘아스팔트 3겹 8층 방수’의 오랜 기간 적용실적으로 방수성능의 우수성은 어느 정도 검증되었으나, 1980년대 이후 인건비의 상승과 환경공해 발생 문제점으로 인해 점진적으로 ‘아스팔트 3겹 8층방수’의 공사현장 적용이 어려워졌으며,As a result of the long-term application of 'Asphalt 3-ply 8-layer waterproofing', the superiority of waterproof performance has been proven to some extent.However, since the 1980s, due to the increase in labor cost and environmental pollution, the construction site of 'Asphalt 3-ply 8-layer waterproofing' has been gradually constructed. Difficult to apply,

이에 대한 대안으로 1970년대 후반 아스팔트 시트 방수재가 외국으로부터 수입되어 처음 적용되기 시작하였으며, 1980년대부터 아스팔트 시트 방수재가 국내에서 생산 보급되기 시작하여, 종래의 ‘아스팔트 3겹 8층 방수’에 비교하여 훨씬 간편한 시공성과 경제성으로 인해 급속히 널리 보급되기 시작하였다. As an alternative to this, asphalt sheet waterproofing material was imported from foreign countries in the late 1970s and applied for the first time, and asphalt sheet waterproofing material began to be produced and distributed in Korea in the 1980s, and compared with the conventional asphalt 3-ply 8-layer waterproofing. Due to the ease of construction and economic feasibility, it is rapidly spreading widely.

하지만 상기 ‘아스팔트 시트 방수’의 문제점으로는 아스팔트 시트 방수층이 콘크리트 바탕면과의 접착력 부족에 의한 방수층의 들뜸 현상 발생, 방수시트 겹침 연결 이음부위를 토우치(Torch) 사용 가열 용융 접합 시, 고무 아스팔트 콤파운드의 연소, 산화에 의한 방수시트 연결 이음부위의 수밀성 부족으로 이음부를 통한 누수사고가 빈번한 문제점이 발생되었으며, 또한 방수시트 연결 이음부위로 통해 누수된 물이 시트 방수층 아래로 흘러 다니면서 콘크리트 구조체 취약부위 여러 개소에서 누수현상이 발생되어 보수범위가 광범위하며, 보수비용이 과다하게 소요되는 커다란 단점을 나타내며 1990년 이후로는 국내 건설업체들이 ‘아스팔트 시트방수’의 적용을 기피하는 현상이 발생되었다. However, the problem of the asphalt sheet waterproofing is that the asphalt sheet waterproofing layer is lifted due to the lack of adhesion to the concrete base surface, and the rubber asphalt when the heat-melt-bonding of the waterproof sheet overlap connection joints uses a torch. Due to the lack of watertightness of the joints of the waterproof sheet due to the combustion and oxidation of the compound, water leakage accidents occurred frequently through the joints. Also, water leaked through the joints of the waterproof sheet flows down the waterproof layer of the concrete structure, and thus is weak in concrete structures. Leakage has occurred in several places, resulting in a wide range of repairs and excessive repair costs, and since 1990, domestic construction companies have avoided the application of 'asphalt sheet waterproofing'.

KS F 3211에서 규정하는 건설용 도막 방수재 중 ‘우레탄계 도막방수’와 ‘고무 아스팔트계 도막방수’등은 로울러나 붓을 사용하는 간편한 도포 시공방법으로서 시공성이 좋으며, 방수층의 신장력이 우수하여 콘크리트 구조체의 미세 균열에도 대응하는 장점이 있으나, 콘크리트 바탕면의 평활도에 따라 균등한 두께의 도막 방수층 형성 어려움이 있으며 방수층의 경화과정에 부분적인 에어포켓(air pocket) 발생현상으로 전체 도막 방수층 중 결함부위가 여러 곳에서 발생하는 단점이 있다. Among the coating waterproofing materials specified in KS F 3211, 'urethane-based waterproofing' and 'rubber asphalt-based waterproofing' are easy to apply by using rollers or brushes, and they have good workability and excellent extension of waterproof layer. Although there is an advantage to cope with fine cracks, it is difficult to form a coating waterproof layer with an even thickness according to the smoothness of the concrete base surface, and there are several air pockets in the curing process of the waterproof layer. There are disadvantages that occur in places.

상기의 설명에서와 같이 방수자재와 방수 공법별로 각각의 장단점을 가지고 있으나, 방수공사 시공이 작업 인부들의 인력에 의한 시공으로서 시공 부주의에 의한 하자 발생 또한 빈번하다는 것은 공통적인 문제점으로 지적될 수 있다. As described in the above description, each material has advantages and disadvantages for each waterproofing method and waterproofing method. However, it may be pointed out that the waterproofing work is frequently caused by carelessness of construction workers due to manpower of workers.

이와 같은 시공 부주의에 의한 방수하자 발생을 최소화하기 위하여 2000년대 이후부터는 방수 공사비가 다소 많이 소요되더라도 종래의 ‘시트방수’나 ‘도막방수’의 단층 방수공법을 보완하여 도막방수와 시트방수를 결합한 도막 및 시트 이중방수 또는 시트와 도막의 결합으로 이루어지는 복합 방수공법 등이 개발되어 적용되고 있는 현실이다. In order to minimize the occurrence of waterproofing defects due to such carelessness of construction, even though waterproof construction cost is somewhat high since 2000s, the single layer waterproofing method of the 'sheet waterproofing' or 'film waterproofing' is supplemented to combine the film waterproofing and sheet waterproofing. And a composite waterproof method consisting of a double waterproof sheet or a combination of the sheet and the coating film has been developed and applied.

한국 공개특허공보 제10-2005-0027200호Korean Unexamined Patent Publication No. 10-2005-0027200

본 발명의 목적은 개질 아스팔트 콤파운드 방수층; 및 상기 개질 아스팔트 콤파운드 방수층 상부면에 구비된 타포린 시트를 포함하는 타포린 시트 방수층;을 포함하는 방수시트를 제공하는 것이다. An object of the present invention is a modified asphalt compound waterproof layer; And a tarpaulin sheet waterproof layer including a tarpaulin sheet provided on an upper surface of the modified asphalt compound waterproof layer.

또한 본 발명의 목적은 상기 방수시트; 및 상기 방수시트 하부면에 구비된 고무 아스팔트 도막 방수층을 포함하는 복합 방수층을 제공하는 것이다. In addition, an object of the present invention is the waterproof sheet; And it is to provide a composite waterproof layer comprising a rubber asphalt coating waterproofing layer provided on the lower surface of the waterproof sheet.

마지막으로 본 발명의 목적은 바탕면을 정리하는 제1단계; 방수하자 발생 취약 부위의 방수층을 보강하는 제2단계; 상기 바탕면 상부면에 고무 아스팔트 도막 방수재 조성물을 도포하여 고무 아스팔트 도막 방수층을 형성하는 제3단계; 상기 고무 아스팔트 도막 방수층 상부면에 상기 방수시트를 부착하는 제4단계; 및 상기 제4단계는 상기 고무 아스팔트 도막 방수층 상부면에 2 이상의 방수시트를 부착하는 경우, 상기 방수시트의 연결 이음 부위의 수밀성을 보강하는 제5단계;를 포함하고, 상기 방수시트들은 겹침 이음으로 연결하며, 상기 겹침 폭은 50 ㎜ 이상인 것인 복합 방수층의 시공 방법을 제공하는 것이다. Finally, the object of the present invention is the first step of arranging the base surface; A second step of reinforcing a waterproof layer of a water-resistant flaw-prone area; A third step of forming a rubber asphalt coating waterproofing layer by applying a rubber asphalt coating waterproofing composition to the upper surface of the base surface; A fourth step of attaching the waterproof sheet to an upper surface of the rubber asphalt coating waterproofing layer; And a fourth step of reinforcing the watertightness of the connection joint portion of the waterproof sheet when attaching two or more waterproof sheets to the upper surface of the rubber asphalt coating waterproofing layer. The waterproof sheets include overlapping joints. To connect, the overlap width is to provide a construction method of the composite waterproof layer is 50 mm or more.

상기의 목적을 달성하기 위하여, 본 발명자는 방수의 안정성과 내구성이 뛰어난 방수시트, 콘크리트 바탕면에 완전히 접착되는 상기 방수시트를 포함하는 복합 방수층 및 이의 시공방법을 제공한다. In order to achieve the above object, the present invention provides a waterproof sheet having excellent waterproof stability and durability, a composite waterproof layer including the waterproof sheet completely adhered to the concrete base surface, and a construction method thereof.

이하, 본 명세서에 대하여 더욱 상세하게 설명한다.Hereinafter, this specification is demonstrated in detail.

본 명세서에서 어떤 부분이 어떤 구성요소를 "포함" 한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성요소를 제외하는 것이 아니라 다른 구성 요소를 더 포함할 수 있는 것을 의미한다. In the present specification, when a part "includes" a certain component, this means that the component may further include other components, except for the case where there is no description to the contrary.

방수시트Waterproof sheet

본 발명은 개질 아스팔트 콤파운드 방수층; 및 The present invention is a modified asphalt compound waterproof layer; And

상기 개질 아스팔트 콤파운드 방수층 상부면에 구비된 타포린 시트를 포함하는 타포린 시트 방수층;을 포함하는 방수시트를 제공한다. It provides a waterproof sheet comprising a; tarpaulin sheet waterproof layer including a tarpaulin sheet provided on the upper surface of the modified asphalt compound waterproof layer.

본 발명의 일 구현예에 있어서, 상기 타포린 시트 방수층은, 폴리에스터 부직포; 상기 폴리에스터 부직포 상부면에 구비된 타포린 시트; 및 상기 타포린 시트 상부면에 구비된 폴리에틸렌 필름을 포함하고, 상기 폴리에스터 부직포는 상기 개질 아스팔트 콤파운드 방수층과 접하여 구비된다.In one embodiment of the invention, the tarpaulin sheet waterproof layer, Polyester nonwoven fabric; A tarpaulin sheet provided on an upper surface of the polyester nonwoven fabric; And a polyethylene film provided on an upper surface of the tarpaulin sheet, wherein the polyester nonwoven fabric is provided in contact with the modified asphalt compound waterproof layer.

더욱 구체적으로 상기 방수시트는 타포린 시트 방수층의 하부면에 개질 아스팔트 콤파운드를 일정 두께로 피복시켜 제조할 수 있다. 더욱 구체적으로 상기 방수시트는 타포린 시트 방수층의 하부면에 개질 아스팔트 콤파운드를 0.5 mm 내지 1.5 mm의 두께로 피복시켜 제조할 수 있다. More specifically, the waterproof sheet may be manufactured by coating a modified asphalt compound on a lower surface of the tarpaulin sheet waterproof layer to a predetermined thickness. More specifically, the waterproof sheet may be prepared by coating a modified asphalt compound on the lower surface of the tarpaulin sheet waterproof layer to a thickness of 0.5 mm to 1.5 mm.

본 발명에 따른 방수시트는 겹층 방수층으로서 방수 안전성과 방수층의 내구성이 탁월한 특성이 있다. The waterproof sheet according to the present invention has excellent properties of waterproof safety and durability of the waterproof layer as a layer waterproof layer.

도 3은 본 발명의 일 구현예에 따른 방수시트의 구조도를 나타낸 도이다. 구체적으로, 본 발명의 개질 아스팔트 콤파운드 방수층; 상기 개질 아스팔트 콤파운드 방수층 상부면에 타포린 시트 방수층이 구비되고, 상기 개질 아스팔트 콤파운드 방수층 하부면에 폴리에스터 부직포 또는 이형필름이 구비된다. 3 is a view showing the structure of a waterproof sheet according to an embodiment of the present invention. Specifically, the modified asphalt compound waterproof layer of the present invention; A tarpaulin sheet waterproof layer is provided on an upper surface of the modified asphalt compound waterproof layer, and a polyester nonwoven fabric or a release film is provided on a lower surface of the modified asphalt compound waterproof layer.

또한, 상기 타포린 시트 방수층은 폴리에스터 부직포, 상기 폴리에스터 부직포 상부면에 구비된 타포린 시트, 상기 타포린 시트 상부면에 폴리에틸렌 필름 구체적으로 고밀도 폴리에틸렌(HDPE) 필름이 구비된다. The tarpaulin sheet waterproof layer may include a polyester nonwoven fabric, a tarpaulin sheet provided on an upper surface of the polyester nonwoven fabric, and a polyethylene film, specifically a high density polyethylene (HDPE) film, on the upper surface of the tarpaulin sheet.

도 4는 본 발명의 일 구현예에 따른 방수시트의 형상도 및 단면도를 나타낸 도이다. Figure 4 is a view showing the shape and cross-sectional view of the waterproof sheet according to an embodiment of the present invention.

구체적으로, 본 발명에 따른 방수시트는 폴리에스터 부직포, 상기 폴리에스터 부직포 상부면에 구비된 타포린 시트, 상기 타포린 시트 상부면에 폴리에틸렌 필름이 구비된 타포린 시트 방수층을 포함하고, 상기 타포린 시트 방수층의 폴리에스터 부직포 하부면에 개질 아스팔트 콤파운드 방수층이 구비되며, 상기 개질 아스팔트 콤파운드 방수층 하부면에 폴리에스터 부직포가 구비된다. Specifically, the waterproof sheet according to the present invention comprises a polyester nonwoven fabric, a tarpaulin sheet provided on the upper surface of the polyester nonwoven fabric, a tarpaulin sheet waterproof layer provided with a polyethylene film on the upper surface of the tarpaulin sheet, the poly of the tarpaulin sheet waterproof layer A modified asphalt compound waterproof layer is provided on the lower surface of the ester nonwoven fabric, and a polyester nonwoven fabric is provided on the lower surface of the modified asphalt compound waterproof layer.

본 발명에 있어서, 상기 타포린 시트는 가볍고 유연성을 가짐과 동시에 인장성능 및 인열성능이 탁월하여 타포린 시트를 포함하는 타포린 시트 방수층의 하부면에 구비된 개질 아스팔트 콤파운드 방수층을 완전히 보호할 수 있다. In the present invention, the tarpaulin sheet is light and flexible, and at the same time excellent in tensile and tear performance can completely protect the modified asphalt compound waterproof layer provided on the lower surface of the tarpaulin sheet waterproof layer including the tarpaulin sheet.

본 발명에 있어서, 상기 개질 아스팔트 콤파운드 방수층은 일반 아스팔트에 고무 계열의 고분자 개질재인 SBS(Styrene Butadiene Styrene Block Copolymer)를 결합시켜 품질을 개량한 아스팔트를 이용하여 형성된 방수층을 의미한다. In the present invention, the modified asphalt compound waterproof layer refers to a waterproof layer formed by using asphalt improved in quality by combining SBS (Styrene Butadiene Styrene Block Copolymer), a rubber-based polymer modifier, to general asphalt.

본 발명에 있어서, 상기 타포린 시트 방수층에 포함된 폴리에틸렌 필름은 당업계에서 공지된 필름을 사용할 수 있으며, 구체적으로 고밀도 폴리에틸렌(HDPE) 필름을 사용할 수 있다. In the present invention, the polyethylene film included in the tarpaulin sheet waterproof layer may use a film known in the art, and specifically, a high density polyethylene (HDPE) film may be used.

본 발명의 일 구현예에 있어서, 상기 타포린 시트 방수층에 포함된 폴리에스터 부직포의 질량은 30 g/㎡ 내지 60 g/㎡ 이고, 상기 타포린 시트의 질량은 100 g/㎡ 내지 220 g/㎡이다. 상기 타포린 시트 방수층에 포함된 폴리에스터 부직포는 타포린 시트 하부면에 피복되는 개질 아스팔트 콤파운드층이 타포린 시트와의 박리현상이 없이 완전히 접합하도록 하는 역할을 한다. In one embodiment of the present invention, the mass of the polyester nonwoven fabric included in the tarpaulin sheet waterproof layer is 30 g / ㎡ to 60 g / ㎡, the mass of the tarpaulin sheet is 100 g / ㎡ to 220 g / ㎡. The polyester nonwoven fabric included in the tarpaulin sheet waterproof layer serves to completely bond the modified asphalt compound layer coated on the lower surface of the tarpaulin sheet without peeling from the tarpaulin sheet.

또 하나의 일 구현예에 있어서, 상기 타포린 시트 방수층에 포함된 상기 폴리에틸렌 필름의 두께는 30 μm 내지 60 μm이다. In another embodiment, the thickness of the polyethylene film included in the tarpaulin sheet waterproof layer is 30 μm to 60 μm.

또 하나의 일 구현예에 있어서, 상기 방수시트는 상기 개질 아스팔트 콤파운드 방수층 하부면에 폴리에스터 부직포 또는 이형 필름을 더 구비할 수 있다. In another embodiment, the waterproof sheet may further include a polyester nonwoven fabric or a release film on the lower surface of the modified asphalt compound waterproof layer.

본 발명의 일 구현예에 있어서, 상기 개질 아스팔트 콤파운드 방수층 하부면에 폴리에스터 부직포가 접하여 구비되고, 상기 개질 아스팔트 콤파운드 방수층 하부면에 구비된 폴리에스터 부직포의 질량은 60 g/㎡ 내지 120 g/㎡일 수 있다. 상기 개질 아스팔트 콤파운드 방수층 하부면에 구비된 폴리에스터 부직포는 후술하는 방수시트 하부면에 구비되는 고무 아스팔트 도막 방수층과 완전한 접합을 이루도록 한다. In one embodiment of the present invention, the polyester nonwoven fabric is provided in contact with the lower surface of the modified asphalt compound waterproof layer, the mass of the polyester nonwoven fabric provided on the lower surface of the modified asphalt compound waterproof layer is 60 g / ㎡ to 120 g / ㎡ Can be. Polyester nonwoven fabric provided on the lower surface of the modified asphalt compound waterproof layer to achieve a complete bonding with the rubber asphalt coating waterproof layer provided on the lower surface of the waterproof sheet to be described later.

또 다른 구현예에 있어서, 상기 개질 아스팔트 콤파운드 방수층 하부면에 이형 필름이 구비되고, 상기 복합 방수층은 자착식 구조(Self Adhesive Type)일 수 있다. In another embodiment, a release film is provided on a lower surface of the modified asphalt compound waterproof layer, and the composite waterproof layer may be a self adhesive type.

본 발명에 따른 방수시트는 KS F 2622(멤브레인 방수층의 방수성능 평가시험 방법)에서 규정하는 패임 저항성 시험, 충격 저항성 시험, 내피로성 시험을 충족한다. The waterproof sheet according to the present invention satisfies the pitting resistance test, the impact resistance test, and the fatigue resistance test specified in KS F 2622 (Test method for evaluating the waterproof performance of the membrane waterproof layer).

복합 방수층Composite waterproofing layer

본 발명은 또한 상기 방수시트; 및 The present invention also the waterproof sheet; And

상기 방수시트 하부면에 구비된 고무 아스팔트 도막 방수층을 포함하는 복합 방수층을 제공한다. It provides a composite waterproof layer comprising a rubber asphalt coating waterproof layer provided on the bottom surface of the waterproof sheet.

본 명세서에서 복합 방수층에 포함된 상기 방수시트는 전술한 내용과 동일하다. The waterproof sheet included in the composite waterproof layer in the present specification is the same as described above.

구체적으로, 본 발명은 방수시트; 및 상기 방수시트 하부면에 구비된 고무 아스팔트 도막 방수층을 포함하고, Specifically, the present invention is a waterproof sheet; And a rubber asphalt coating waterproofing layer provided on the lower surface of the waterproof sheet,

상기 방수시트는 개질 아스팔트 콤파운드 방수층; 및 상기 개질 아스팔트 콤파운드 방수층 상부면에 구비된 타포린 시트를 포함하는 타포린 시트 방수층을 포함하며, The waterproof sheet is a modified asphalt compound waterproof layer; And a tarpaulin sheet waterproof layer including a tarpaulin sheet provided on an upper surface of the modified asphalt compound waterproof layer.

상기 타포린 시트 방수층은 폴리에스터 부직포; 상기 폴리에스터 부직포 상부면에 구비된 타포린 시트; 및 상기 타포린 시트 상부면에 구비된 폴리에틸렌 필름을 포함하고, 상기 폴리에스터 부직포는 상기 개질 아스팔트 콤파운드 방수층과 접하여 구비될 수 있다. The tarpaulin sheet waterproof layer is a polyester nonwoven fabric; A tarpaulin sheet provided on an upper surface of the polyester nonwoven fabric; And a polyethylene film provided on an upper surface of the tarpaulin sheet, and the polyester nonwoven fabric may be provided in contact with the modified asphalt compound waterproof layer.

상기 방수시트의 개질 아스팔트 콤파운드 방수층은 상기 고무 아스팔트 도막 방수층에 접하여 구비되거나, 상기 개질 아스팔트 콤파운드 방수층과 상기 고무 아스팔트 도막 방수층 사이에 폴리에스터 부직포가 추가로 구비될 수 있다. The modified asphalt compound waterproofing layer of the waterproof sheet may be provided in contact with the rubber asphalt coating waterproofing layer, or a polyester non-woven fabric may be further provided between the modified asphalt compound waterproofing layer and the rubber asphalt coating waterproofing layer.

본 발명의 일 구현예에 있어서, 상기 고무 아스팔트 도막 방수층 상부면에 2 이상의 방수시트가 구비될 수 있다. 이 경우, 2 이상의 방수시트 연결 이음은 겹침 이음으로 연결하고, 상기 방수시트의 겹침 폭은 50 mm 이상이다. In one embodiment of the present invention, two or more waterproof sheets may be provided on the upper surface of the rubber asphalt coating waterproofing layer. In this case, two or more waterproof sheet connection joints are connected by overlapping joints, and the overlap width of the waterproof sheet is 50 mm or more.

또한, 상기 방수시트의 겹침 연결 이음 부위 상부면에 방수테이프가 추가적으로 구비되거나, 고무 아스팔트 도막 방수재 조성물을 두께 2.0 mm 내지 3.0mm 및 폭 5.0 mm 정도로 도포할 수 있다. 상기 방수테이프 또는 고무 아스팔트 도막 방수재 조성물은 방수시트 사이의 연결 이음 부위의 수밀성을 보강하는 역할을 할 수 있다. In addition, the waterproof tape may be additionally provided on the upper surface of the overlap connection joint portion of the waterproof sheet, or the rubber asphalt coating waterproofing composition may be applied to a thickness of 2.0 mm to 3.0 mm and a width of 5.0 mm. The waterproof tape or rubber asphalt coating waterproofing composition may serve to reinforce the watertightness of the connection joint between the waterproof sheets.

도 1은 본 발명의 일 구현예에 따른 복합 방수층의 단면도를 나타낸 도이다. 구체적으로 도 1에서와 같이 본 발명은 프라이머층 상부에 고무 아스팔트 도막 방수층이 구비되고, 상기 고무 아스팔트 도막 방수층 상부면에 방수시트가 구비될 수 있다. 또한, 2 이상의 방수시트는 겹침 이음으로 연결되고, 상기 방수시트 겹침 연결 이음 부위 상부에 연결 이음 부위의 수밀성을 보강하기 위하여 방수테이프 또는 고무 아스팔트 도막 방수재 조성물을 도포할 수 있다. 1 is a cross-sectional view of a composite waterproofing layer according to an embodiment of the present invention. Specifically, as shown in FIG. 1, the present invention may include a rubber asphalt coating waterproofing layer on the primer layer, and a waterproof sheet on the upper surface of the rubber asphalt coating waterproofing layer. In addition, two or more waterproof sheets are connected by overlapping joints, and the waterproof tape or rubber asphalt coating waterproofing composition may be applied to reinforce the watertightness of the connection joints on the waterproof sheet overlapping joint joints.

상기 방수시트는 전술한 바와 같이 개질 아스팔트 콤파운드 방수층; 및 상기 개질 아스팔트 콤파운드 방수층 상부면에 구비된 타포린 시트를 포함하는 타포린 시트 방수층을 포함한다. The waterproof sheet is a modified asphalt compound waterproof layer as described above; And a tarpaulin sheet waterproof layer including a tarpaulin sheet provided on an upper surface of the modified asphalt compound waterproof layer.

도 2는 본 발명의 일 구현예에 따른 복합 방수층의 구성도를 나타낸 도이다. 구체적으로 도 2에서와 같이 본 발명은 프라이머층 상부에 고무 아스팔트 도막 방수층이 구비되고, 상기 고무 아스팔트 도막 방수층 상부면에 타포린 시트 방수층 및 개질 아스팔트 콤파운드 방수층을 포함하는 방수시트가 구비된다. 2 is a view showing the configuration of the composite waterproof layer according to an embodiment of the present invention. Specifically, as shown in FIG. 2, the present invention is provided with a rubber asphalt coating waterproofing layer on the primer layer, and a waterproof sheet including a tarpaulin sheet waterproofing layer and a modified asphalt compound waterproofing layer on the upper surface of the rubber asphalt coating waterproofing layer.

본 발명에서 상기 고무 아스팔트 도막 방수층은, 속건성 아스팔트 화합물 45 중량% 내지 70 중량%; 합성고무 개질제 3 중량% 내지 10 중량%; 가소제 2 중량% 내지 5 중량%; 요변성증점제 2 중량% 내지 5 중량%; 산화방지제 0.5 중량% 내지 1.0 중량%; 및 광물질안정제 20 중량% 내지 35 중량%;를 포함하는 겔(gel) 형상의 고무 아스팔트 도막 방수재 조성물로 형성된다. The rubber asphalt coating waterproofing layer in the present invention, 45% by weight to 70% by weight quick-drying asphalt compound; 3 to 10 weight percent synthetic rubber modifier; 2 to 5 weight percent plasticizer; 2 to 5 weight percent of thixotropic thickener; 0.5 wt% to 1.0 wt% antioxidant; And 20 wt% to 35 wt% of a mineral stabilizer. It is formed of a gel-like rubber asphalt coating waterproofing composition.

상기 겔 형상의 고무 아스팔트 도막 방수재 조성물로 형성된 고무 아스팔트 도막 방수층은 콘크리트 바탕면과 뛰어난 접착력을 나타내며, 2 ㎜ 정도 두께의 도막 방수층 형성 후 6시간 이내에 도막 방수층의 표면이 불점착의 지촉 건조 상태로 경화된다. The rubber asphalt coating waterproofing layer formed of the gel-like rubber asphalt coating waterproofing composition exhibits excellent adhesion with the concrete base surface, and the surface of the coating waterproofing layer hardens to a non-tack-contact dry state within 6 hours after the formation of the coating waterproofing layer having a thickness of about 2 mm. do.

또한, 겔 형상의 고무 아스팔트 도막 방수재 조성물은 상기 조성물에 함유된 석유 용제의 증발에 의한 경화 과정에서 콘크리트 바탕면과 더욱 완전한 접착을 이루며, 상기 고무 아스팔트 도막 방수층 상부면에 부착되는 방수시트의 개량 아스팔트 콤파운드 방수층과도 완전한 접착을 이루어 콘크리트 바탕면과의 들뜸이나 박리현상이 없이 전면 접착되어 일체화된 복합 방수층을 형성할 수 있다. In addition, the gel-like rubber asphalt coating waterproofing composition is more fully bonded to the concrete base surface during the curing process by evaporation of the petroleum solvent contained in the composition, the improved asphalt of the waterproof sheet attached to the upper surface of the rubber asphalt coating waterproofing layer Complete bonding with the compound waterproof layer is possible to form an integrated composite waterproof layer by bonding the entire surface without lifting or peeling with the concrete base surface.

본 발명의 일 구현예에 있어서, 상기 속건성 아스팔트 화합물은, 스트레이트 런 아스팔트(Straight Run Asphalt)와 석유용제의 혼합물; 및 블로운 아스팔트(Blown Asphalt)와 석유용제의 혼합물을 혼합한 것이다. In one embodiment of the present invention, the quick-drying asphalt compound, a mixture of straight run asphalt (Straight Run Asphalt) and petroleum solvent; And a mixture of blown asphalt (Blown Asphalt) and a petroleum solvent.

또 하나의 구현예에 있어서, 상기 속건성 아스팔트 화합물은, 상기 스트레이트 런 아스팔트와 석유용제의 혼합물과 상기 블로운 아스팔트와 석유용제의 혼합물을 60 중량% 내지 85 중량% : 15 중량% 내지 40 중량%의 비율로 혼합한 것이다. In another embodiment, the quick-drying asphalt compound, the mixture of the straight run asphalt and petroleum solvent and the mixture of the blown asphalt and petroleum solvent 60 to 85% by weight of 15 to 40% by weight of It is mixed in proportion.

더욱 구체적으로, 상기 스트레이트 런 아스팔트와 석유용제는 70 중량% 내지 85 중량% : 15 중량% 내지 30 중량%의 비율로 혼합되고, 상기 블로운 아스팔트와 석유용제는 60 중량% 내지 80 중량% : 20 중량% 내지 40 중량%의 비율로 혼합하되, 상기 스트레이트 런 아스팔트와 석유용제의 혼합물과 상기 블로운 아스팔트와 석유용제의 혼합물을 60 중량% 내지 85 중량% : 15 중량% 내지 40 중량%의 비율로 혼합한다. More specifically, the straight run asphalt and petroleum solvent is mixed in a ratio of 70% to 85% by weight: 15% by weight to 30% by weight, and the blown asphalt and petroleum solvent are 60% by weight to 80% by weight: 20 A mixture of the weight ratio of 40% by weight to 40% by weight, wherein the mixture of the straight run asphalt and petroleum solvent and the mixture of the blown asphalt and petroleum solvent 60 to 85% by weight: 15 to 40% by weight Mix.

본 발명에 있어서 상기 석유 용제는 솔벤트(solvent), 자이렌(xylene) 또는 솔벤트와 자이렌의 혼합물일 수 있다. In the present invention, the petroleum solvent may be a solvent, xylene, or a mixture of solvent and xylene.

상기 블로운 아스팔트와 석유용제의 혼합물이 40 중량%을 초과하는 경우, 아스팔트 화합물의 경화 속도는 빨라지나, 경화 후에 아스팔트가 딱딱해지는 문제점이 있다. When the mixture of the blown asphalt and the petroleum solvent exceeds 40% by weight, the curing speed of the asphalt compound is faster, but there is a problem that the asphalt becomes hard after curing.

본 발명에 있어서, 상기 합성고무 개질제는 고무 아스팔트 도막 방수층의 신장율 증대와 콘크리트 바탕면의 미세균열 발생에 대한 대응성과 내열성 및 접착성을 부여하기 위한 것으로 3 중량% 미만으로 첨가될 경우 신장율과 접착강도가 저하되고, 10 중량%를 초과하여 첨가될 경우 신장율이 너무 커져서 오히려 접착강도가 저하될 수 있으며 제조원가가 상승되는 문제점이 있다. In the present invention, the synthetic rubber modifier is to increase the elongation of the rubber asphalt coating waterproofing layer and to provide responsiveness and heat resistance and adhesion to the occurrence of microcracks of the concrete base surface, when added to less than 3% by weight elongation and adhesive strength Is lowered, and when added in excess of 10% by weight, the elongation is too large, the adhesive strength may be lowered, and there is a problem that the manufacturing cost is increased.

또한 상기 합성고무 개질제는 이소부틸렌-이소프렌 고무(Isobutene-Isoprene Rubber), PIB고무(Poly Isobutylene Rubber), 폴리부텐(Polybutene) 및 석유수지(Petroleum Resin)로 이루어진 군에서 1 또는 2 이상 선택될 수 있다. In addition, the synthetic rubber modifier may be selected from the group consisting of isobutylene-isoprene rubber (Isobutene-Isoprene Rubber), PIB rubber (Poly Isobutylene Rubber), polybutene (Polybutene) and petroleum resin (Petroleum Resin) have.

본 발명에 있어서, 상기 가소제는 상기 고무 아스팔트 도막 방수재 조성물의 원료 혼화성과 유연성을 높이기 위한 첨가제로서 프로세스 오일(process oil), 글리콜유 및 미네랄 스프리트 오일(Mineral Spirit Oil)로 이루어진 군에서 1 또는 2 이상 선택될 수 있다. In the present invention, the plasticizer is one or two or more in the group consisting of process oil, glycol oil and mineral spirit oil as an additive for increasing the raw material miscibility and flexibility of the rubber asphalt coating waterproofing composition Can be selected.

더욱 구체적으로 상기 프로세스 오일(Process Oil)은 파라핀계 오일, 나프텐계 오일, 아로마틱계 오일 중에서 선택된 적어도 하나일 수 있다. More specifically, the process oil may be at least one selected from paraffinic oil, naphthenic oil, and aromatic oil.

상기 가소제의 첨가 비율이 2 중량% 미만일 경우, 혼화성이 떨어지고, 5 중량%를 초과하는 경우 고무 아스팔트 도막 방수재와 겔 상태에서 흘러내릴 문제점이 있다. When the addition ratio of the plasticizer is less than 2% by weight, miscibility is lowered, and when it exceeds 5% by weight, there is a problem of flowing down in a gel asphalt rubber waterproofing material and gel state.

본 발명에 있어서, 상기 요변성 증점제(Thixotropic Agent)는 로 벤토나이트 광물질을 2 중량% 내지 5 중량% 첨가하여 고무 아스팔트 도막 방수층의 수직 벽체면 도포 시 흘러내림성을 방지하는 역할을 나타낸다. In the present invention, the thixotropic agent is added to 2% by weight to 5% by weight of bentonite mineral exhibits a role of preventing the flow resistance when applying the vertical wall surface of the rubber asphalt coating waterproofing layer.

본 발명에 있어서, 상기 광물질 안정제는 고무 아스팔트 화합물의 점도 증대 효과, 흐름 방지효과, 저장 안정성 및 내구성 증대를 위한 것으로 해포석(Sepiolite), 프라이애쉬(Fly Ash), 탄산칼슘, 이산화규소 및 고령토로 이루어진 군에서 1 또는 2 이상 선택된다. In the present invention, the mineral stabilizer is to increase the viscosity of the rubber asphalt compound, flow prevention effect, storage stability and durability, and consists of haemulite (Sepiolite), fly ash, calcium carbonate, silicon dioxide and kaolin 1 or 2 or more selected from the group.

상기 광물제 안정제의 첨가 비율이 20 중량% 미만인 경우, 점도 증대 효과가 적으며 35 중량%를 초과하는 경우 고무 아스팔트 화합물의 유연성이 저하될 수 있다.When the addition ratio of the mineral stabilizer is less than 20% by weight, the effect of increasing viscosity is small, and when it exceeds 35% by weight, the flexibility of the rubber asphalt compound may be lowered.

본 발명에 있어서, 상기 산화방지제는 아민류 또는 페놀류이다. In the present invention, the antioxidant is amines or phenols.

복합 방수층의 시공방법Construction method of composite waterproof layer

본 발명은 또한, 바탕면을 정리하는 제1단계;The present invention also comprises a first step of arranging the base surface;

방수하자 발생 취약 부위의 방수층을 보강하는 제2단계; A second step of reinforcing a waterproof layer of a water-resistant flaw-prone area;

상기 바탕면에 고무 아스팔트 도막 방수재 조성물을 도포하여 고무 아스팔트 도막 방수층을 형성하는 제3단계; A third step of forming a rubber asphalt coating waterproofing layer by applying a rubber asphalt coating waterproofing composition to the base surface;

상기 고무 아스팔트 도막 방수층 상부면에 상기 방수시트를 부착하는 제4단계; 및 A fourth step of attaching the waterproof sheet to an upper surface of the rubber asphalt coating waterproofing layer; And

상기 제4단계는 상기 고무 아스팔트 도막 방수층 상부면에 2 이상의 방수시트를 부착하는 경우, 상기 방수시트의 연결 이음 부위의 수밀성을 보강하는 제5단계;를 포함하고, The fourth step includes a fifth step of reinforcing the watertightness of the connection joint portion of the waterproof sheet when the two or more waterproof sheets are attached to the upper surface of the rubber asphalt coating waterproofing layer.

상기 방수시트들은 겹침 이음으로 연결하며, 상기 겹침 폭은 50 ㎜ 이상인 것인 복합 방수층의 시공 방법을 제공한다. The waterproof sheets are connected by overlapping joints, and the overlapping width is 50 mm or more to provide a construction method of the composite waterproof layer.

본 명세서에서 상기 시공 방법에서 언급된 복합 방수층 및 방수시트는 전술한 내용과 동일하다. In the present specification, the composite waterproof layer and the waterproof sheet mentioned in the construction method are the same as described above.

이하에서는 각 단계에 대하여 상세하게 설명한다. Hereinafter, each step will be described in detail.

바탕면을 정리하는 제1단계는 콘크리트 바탕면의 레이턴스(Laitance), 흙, 먼지, 모래 등의 이물질 제거하고, 돌출 부위를 평활하게 조성하고, 깨끗하게 청소하여 바탕면을 정리한다. The first step of arranging the base surface is to remove foreign substances such as latent (Laitance), soil, dust, sand, etc. of the concrete base surface, to smooth the projections, and to clean the base surface by cleaning cleanly.

방수하자 발생 취약 부위의 방수층을 보강하는 제2단계는 시공 줄눈(Construction Joint) 부위, 콘크리트 균열 발생부위, 드레인, 파이프 배관주위 및 바닥과 벽체가 만나는 코너부위 등의 방수하자 발생 취약부위는 상기 고무 아스팔트 도막 방수재 도포(폭 200 ㎜/두께 1.0mm 내지 2.0 mm)와 동시에 200㎜ 폭의 폴리에스터 부직포를 부착하여 방수층을 보강할 수 있다. The second step of reinforcing the waterproof layer of the vulnerable areas where the waterproof flaw occurs is the waterproof flaw vulnerable areas such as construction joints, concrete cracking areas, drains, pipe pipes, and corners where floors and walls meet. At the same time as coating the asphalt coating waterproofing material (width 200 mm / thickness 1.0 mm to 2.0 mm), a nonwoven fabric of 200 mm width can be attached to reinforce the waterproof layer.

본 발명의 일 구현예에 있어서, 상기 바탕면을 정리하는 제1단계 후, 상기 방수하자 발생 취약 부위의 방수층을 보강하는 제2단계 전에 상기 바탕면 상부면에 프라이머층을 형성하는 단계를 추가로 포함할 수 있다. 상기 프라이머층을 형성하는 단계는 바탕면 전체에 로울러를 사용하여 프라이머를 도포할 수 있으며, 바탕면이 평활하고 깨끗하게 청소된 경우에는 겔 형상의 상기 고무 아스팔트 도막 방수재 조성물의 접착력이 뛰어나므로 생략이 가능하다. In one embodiment of the present invention, after the first step of arranging the base surface, before the second step of reinforcing the waterproof layer of the water-resistant flaw generation vulnerable region further comprises the step of forming a primer layer on the upper surface of the base surface It may include. The step of forming the primer layer can be applied to the primer using a roller on the entire base surface, when the base surface is smooth and clean, it can be omitted because the adhesive strength of the rubber asphalt coating waterproofing composition of the gel is excellent. Do.

상기 바탕면 상부면에 고무 아스팔트 도막 방수재 조성물을 도포하여 고무 아스팔트 도막 방수층을 형성하는 제3단계는 바탕면에 톱니 고무 흙손을 사용하여 타포린 시트 방수층을 상부 표면으로 하는 방수시트의 폭 정도 이상을 고무 아스팔트 도막 방수재 조성물을 1.0 mm 내지 2.0 mm 두께로 도포하는 방법으로 고무 아스팔트 도막 방수층을 형성할 수 있다. 다만, 앞서 설명한 프라이머층을 형성하는 단계를 포함하는 경우, 프라이머층 상부면에 고무 아스팔트 도막 방수재 조성물을 도포하여 고무 아스팔트 도막 방수층을 형성할 수 있다. The third step of forming a rubber asphalt coating waterproofing layer by applying a rubber asphalt coating waterproofing composition to the upper surface of the base surface rubber using a tooth rubber trowel on the base surface of the waterproof sheet having the tarpaulin sheet waterproof layer as the upper surface of the rubber or more A rubber asphalt coating waterproofing layer may be formed by applying the asphalt coating waterproofing composition to a thickness of 1.0 mm to 2.0 mm. However, in the case of including the step of forming a primer layer described above, by applying a rubber asphalt coating waterproofing composition to the upper surface of the primer layer can be formed a rubber asphalt coating waterproofing layer.

상기 고무 아스팔트 도막 방수층 상부면에 전술한 방수시트를 부착하는 제4단계는 상기 고무 아스팔트 도막 방수재 조성물을 도포와 동시에 상기 방수시트를 부착시킨다. 더욱 구체적으로, 수평 바닥면의 경우, 상기 고무 아스팔트 도막 방수재 조성물의 도포와 동시에 타포린 시트 방수층을 상부 표면으로 하고, 개질 아스팔트 콤파운드가 일정 두께로 피복되어 있으며, 폴리에스터 부직포가 부착된 방수시트를 깔아주어 상기 고무 아스팔트 도막 방수층에 밀착시킨다. In the fourth step of attaching the above-described waterproof sheet to the upper surface of the rubber asphalt coating waterproofing layer, the waterproof sheet is attached to the rubber asphalt coating waterproofing composition at the same time. More specifically, in the case of the horizontal bottom surface, the tarpaulin sheet waterproofing layer as the upper surface at the same time as the application of the rubber asphalt coating waterproofing material composition, the modified asphalt compound is coated with a certain thickness, the waterproof sheet with a polyester nonwoven fabric is laid To the rubber asphalt coating film waterproof layer.

또한, 수직 벽체면의 경우, 방수층 시공 후 토사 되메우기 과정에 토압에 의해 방수층이 탈락되거나 처지어 내림, 파손되는 현상이 발생되어 그로 인한 누수하자가 빈번하게 발생되고 있다. In addition, in the case of the vertical wall surface, the waterproof layer is dropped, sagging or broken due to earth pressure during the soil refilling process after construction of the waterproofing layer, which causes frequent water leakage.

따라서, 본 발명의 일 구현예에 있어서, 상기 복합 방수층을 시공한 후, 방수층 누름 철물로 상기 복합 방수층을 수직 벽체면에 고정하는 단계를 더 포함한다. Therefore, in one embodiment of the present invention, after the construction of the composite waterproof layer, further comprising the step of fixing the composite waterproof layer to the vertical wall surface with a waterproof layer pressing iron.

더욱 구체적으로 상기 복합 방수층을 시공한 후, 복합 방수층의 길이 방향 상단부에 방수층 누름 철물을 설치하여 못으로 벽체면에 고정함으로써, 토사 되메우기 과정에서 토압에 의한 방수층의 탈락 및 파손이나 처짐 현상을 완전하게 방지하고, 방수층 누름철물 위 못으로 고정부위의 공극은 고무 아스팔트 도막 방수재를 못 고정부위 주변에 덧칠하여 수밀성을 보강할 수 있다. More specifically, after constructing the composite waterproof layer, by installing a waterproofing layer pressing hardware on the upper end in the longitudinal direction of the composite waterproof layer and fixing it to the wall surface with a nail, completely eliminates the phenomenon of falling off, damage or sag of the waterproof layer by earth pressure during the soil refilling process. The air gap of the fixing part with the nail on the waterproofing layer pressing iron can be reinforced with watertightness by coating the rubber asphalt coating waterproofing material around the fixing part.

또한 수직 벽체면 방수층 설치 후 방수층 누름철물 사용 방수층을 벽체면에 고정시키는 방법은 벽체면 높이가 2 m 이상인 경우, 2m 높이마다 가로 방향으로 방수층 누름철물로 복합 방수층을 콘크리트 바탕면에 고정함이 바람직하다.In addition, after installing the vertical wall waterproofing layer, use the waterproofing layer pressing iron to fix the waterproofing layer on the wall surface. When the height of the wall surface is 2 m or more, it is preferable to fix the composite waterproofing layer on the concrete surface with the waterproofing layer pressing iron in the horizontal direction every 2m height. Do.

본 발명의 일 구현예에 따른 수평 바닥면에서의 복합 방수층의 시공 방법은, 바탕면을 정리하는 단계; 프라이머층을 형성하는 단계; 방수 하자 발생 취약 부위의 방수층을 보강하는 단계; 톱니 고무 흙손을 사용하여 1.0 mm 내지 2.0 mm 두께의 도포고무 아스팔트 도막 방수층을 형성하는 단계; 타포린 시트 방수층 및 개질 아스팔트 콤파운드 방수층을 포함하는 방수시트를 까는 단계; 및 방수시트의 연결 이음 부위에 방수 테이프를 부착하거나 고무 아스팔트 도막 방수재 조성물을 도포하여 보강하여 수밀성을 보강하는 단계를 포함한다. Construction method of the composite waterproof layer on the horizontal bottom surface according to an embodiment of the present invention, the step of cleaning the base surface; Forming a primer layer; Reinforcing the waterproof layer of the water-resistant flaw-prone area; Using a tooth rubber trowel to form a 1.0 mm to 2.0 mm thick coated rubber asphalt coating waterproofing layer; Covering the waterproof sheet including the tarpaulin sheet waterproof layer and the modified asphalt compound waterproof layer; And reinforcing watertightness by attaching a waterproof tape to the connection joint portion of the waterproof sheet or by applying a rubber asphalt coating waterproofing composition.

또한, 본 발명의 일 구현예에 따른 수직 벽체면에서의 복합 방수층의 시공 방법은, 바탕면을 정리하는 단계; 프라이머층을 형성하는 단계; 방수 하자 발생 취약 부위의 방수층을 보강하는 단계; 톱니 고무 흙손을 사용하여 1.0 mm 내지 2.0 mm 두께의 도포고무 아스팔트 도막 방수층을 형성하는 단계; 타포린 시트 방수층 및 개질 아스팔트 콤파운드 방수층을 포함하는 방수시트를 부착하는 단계; 방수시트의 연결 이음 부위에 방수 테이프를 부착하거나 고무 아스팔트 도막 방수재 조성물을 도포하여 보강하여 수밀성을 보강하는 단계; 및 벽체면 높이가 2 m 이상인 경우 2 m 마다 상기 방수시트 위에 가로방향으로 방수층 누름 철물을 이용하여 콘크리트 바탕면에 고정하는 단계를 포함한다. In addition, the construction method of the composite waterproof layer on the vertical wall surface according to an embodiment of the present invention, the step of arranging the base surface; Forming a primer layer; Reinforcing the waterproof layer of the water-resistant flaw-prone area; Using a tooth rubber trowel to form a 1.0 mm to 2.0 mm thick coated rubber asphalt coating waterproofing layer; Attaching a waterproof sheet comprising a tarpaulin sheet waterproof layer and a modified asphalt compound waterproof layer; Reinforcing watertightness by attaching a waterproof tape to the connection seam of the waterproof sheet or by applying a rubber asphalt coating waterproofing composition; And when the height of the wall surface is more than 2 m comprises a step of fixing to the concrete base surface by using the waterproof layer pressing iron in the horizontal direction on the waterproof sheet every 2 m.

도 7은 수직 벽체면 방수 공사에서 방수층 고정용 누름 철물의 형상도를 나타낸 도이다. 7 is a view showing the shape of the waterproofing layer fixing pressing hardware in the vertical wall surface waterproofing construction.

도 7에서 보는 바와 같이, 방수층 누름 철물은 도7에서와 같은 형상으로 제조되어 방수층 누름철물의 ① 중앙부위에 못을 박아 벽체 바탕면에 고정시킬 때, ④ 및 ⑤ 부위가 양 옆으로 펼치어지면서 ② 및 ③ 부위가 바탕면에 부착되어 방수층의 고정 역할을 하고, ④ 및 ⑤ 부위도 마찬가지로 벽체 바탕면에 부착됨으로서, ①, ②, ③, ④ 및 ⑤ 5개소 부위에서 방수층을 눌러주어 벽체면에 방수층을 완전하게 고정시키는 기능을 나타낼 수 있다. As shown in Figure 7, the waterproofing layer pressing hardware is manufactured in the same shape as in Figure 7 when nailing the ① central portion of the waterproofing layer pressing iron and fixed to the wall surface, while the ④ and ⑤ part unfolds to both sides ② and ③ parts are attached to the base surface to secure the waterproof layer, and ④ and ⑤ parts are similarly attached to the wall base surface, so that the waterproof layer is pressed on the wall surface by pressing the waterproof layer at 5 places of ①, ②, ③, ④ and ⑤. It can exhibit the function of completely fixing the waterproof layer.

본 발명의 일 구현예에 있어서, 상기 누름 철물의 폭은 30 mm 내지 40 mm이고, 상기 누름 철물의 재질은 알루미늄 또는 플라스틱이다. In one embodiment of the invention, the width of the pressing hardware is 30 mm to 40 mm, the material of the pressing hardware is aluminum or plastic.

또한, 고무 아스팔트 도막 방수층 상부면에 2 이상의 방수시트가 구비되는 경우, 방수시트는 겹침 이음으로 연결하고, 상기 방수시트의 겹침 폭은 50 mm 이상이며, 50 ~ 80mm일 수 있다. 방수시트의 겹침 연결 이음 폭 50 mm 상부에 고무 아스팔트 도막 방수재 조성물을 얇게 도포하여 접착 연결할 수 있다. In addition, when two or more waterproof sheets are provided on the upper surface of the rubber asphalt coating waterproof layer, the waterproof sheets are connected by overlapping joints, and the overlap width of the waterproof sheet is 50 mm or more, and may be 50 to 80 mm. Overlap joint of the waterproof sheet 50 mm thick rubber asphalt coating waterproofing composition can be applied by thin coating on the top.

방수시트의 연결 이음 부위를 보강하는 제5단계는 방수시트 겹침 연결 이음 부위 상부면에 100㎜ 폭의 방수테이프를 부착하거나, 연결 이음 끝단부위 상부에 고무 아스팔트 도막 방수재 조성물을 두께 2.0 mm 내지 3.0mm 및 폭 5.0 mm 정도로 도포하여 방수시트 연결 이음부위의 수밀성을 보강한다. The fifth step of reinforcing the joint portion of the waterproof sheet is to attach a 100 mm wide waterproof tape to the upper surface of the overlapping joint joint portion of the waterproof sheet, or to apply a rubber asphalt coating waterproofing composition thickness of 2.0 mm to 3.0 mm on the upper portion of the joint portion. And 5.0 mm wide to reinforce the watertightness of the joint portion of the waterproof sheet.

본 발명의 일 구현예에 있어서, 건물 옥상, 지하 주차장 상부 등의 인공지반 상부에 조경 녹화시설을 설치하게 될 경우 상기 복합 방수층을 형성한 후, 상기 복합 방수층 상부면에 방근층을 설치하는 단계를 더 포함하고, 상기 방근층은 방근시트; 및 상기 방근시트 상부면에 방근 보조필름이 구비되며, 상기 방근 보조필름은 고밀도 폴리에틸렌(HDPE)계 또는 폴리에틸렌테레프탈레이트(PET)계이다. In one embodiment of the present invention, when the landscaping greening facility is installed on the artificial ground, such as the roof of the building, the upper part of the underground parking lot, after forming the composite waterproofing layer, installing a barrier layer on the upper surface of the composite waterproofing layer. Further comprising, the barrier layer is a barrier sheet; And a weatherproof auxiliary film on the upper surface of the weatherproof sheet, wherein the weatherproof auxiliary film is a high density polyethylene (HDPE) or polyethylene terephthalate (PET) system.

도 5는 건물 옥상 또는 지하 주차장 상부 슬라브와 같은 수평 바닥면 방수 공사에서 본 발명에 따른 복합 방수층의 구성 시공 상세도를 나타낸 도이다. 5 is a view showing the detailed construction of the composite waterproof layer according to the present invention in the horizontal floor waterproofing construction, such as the roof of the building or the upper slab underground parking.

도 6은 지하철, 지하차도 및 공동구 등과 같은 지하 콘크리트 구조물의 수직 벽체면 방수 공사에서 본 발명에 따른 복합 방수층의 구성 시공 상세도를 나타낸 도이다. Figure 6 is a view showing the detailed construction of the composite waterproof layer according to the present invention in the vertical wall surface waterproofing construction of underground concrete structures, such as subway, underground roadway and cavities.

본 발명에 따른 복합 방수층은 방수시트와 콘크리트 바탕면 사이에 겔 형상의 고무 아스팔트 도막 방수층을 구비하여, 콘크리트 바탕면과 뛰어난 접착력으로 방수층의 들뜸이나 박리 현상없이 완전한 접착을 이룸과 동시에 방수시트의 개량 아스팔트 콤파운드 방수층과도 완전한 접합을 이루어 일체화된 복합 방수층을 형성할 수 있다. The composite waterproof layer according to the present invention includes a rubber-like rubber asphalt coating waterproof layer between the waterproof sheet and the concrete base surface, and achieves perfect adhesion without lifting or peeling of the waterproof layer with excellent adhesion to the concrete base surface and at the same time improving the waterproof sheet. It is also possible to form an integral composite waterproof layer by fully bonding with the asphalt compound waterproof layer.

본 발명에 따른 복합 방수층은 일반적인 단층 방수층에 비하여 인력에 의한 방수공사 시공과정에서 시공 부주의에 의한 방수하자 발생요인을 최소화하며, 만약의 시공 부주의에 의한 누수하자 발생 시에도 콘크리트 바탕면과 완전하게 접착된 복합 방수층 아래로 누수한 물이 흘러 다닐 수 없어, 누수 결함부위 발견이 용이하며, 부분적인 보수가 가능하다는 점이 커다란 장점이 될 수 있다. The composite waterproof layer according to the present invention minimizes the causes of waterproof defects caused by carelessness in the construction process of waterproof construction by manpower, compared to the general single-layer waterproof layer, and completely adheres to the concrete surface even when leakage occurs due to inadvertent construction. It can be a big advantage that the leaked water cannot flow under the composite waterproof layer, and it is easy to find the leaked part and the partial repair is possible.

또한 상기 복합 방수층은 인장 및 인열 강도가 뛰어나면서도 유성을 가지는 타포린 시트를 포함하는 타포린 시트 방수층을 상부면으로 하고, 그 하부면에 개질 아스팔트 콤파운드 방수층을 일정 두께로 피복시킨 방수시트는 방수층에 국부 하중 작용시의 패임 저항성과, 방수층의 충격에 대한 충격 저항성, 방수층 바탕판의 접합부 또는 바탕판에 발생한 균열의 움직임에 대한 방수층의 내피로성이 우수하여 복합 방수층의 보호기능을 가짐으로서 방수의 안전성과 내구성이 뛰어나다는 또 다른 효과를 나타낸다. In addition, the composite waterproof layer has a tarpaulin sheet waterproof layer including a tarpaulin sheet having excellent oiliness and tear strength as the upper surface, the waterproof sheet coated with a modified asphalt compound waterproof layer to a predetermined thickness on the lower surface is a local load on the waterproof layer Its waterproof resistance and impact resistance to the impact of the waterproof layer, the impact resistance of the waterproof layer against the joints of the waterproof layer base plate or the movement of the cracks on the base plate have excellent protection function of the composite waterproof layer, thereby ensuring the safety and durability of the waterproof. This excellence has another effect.

도 1은 본 발명의 일 구현예에 따른 복합 방수층의 단면도를 나타낸 도이다.
도 2는 본 발명의 일 구현예에 따른 복합 방수층의 구성도를 나타낸 도이다.
도 3은 본 발명의 일 구현예에 따른 방수시트의 구조도를 나타낸 도이다.
도 4는 본 발명의 일 구현예에 따른 방수시트의 형상도 및 단면도를 나타낸 도이다.
도 5는 건물 옥상 또는 지하 주차장 상부 슬라브와 같은 수평 바닥면 방수 공사에서 본 발명에 따른 복합 방수층의 구성 시공 상세도를 나타낸 도이다.
도 6은 지하철, 지하차도 및 공동구 등과 같은 지하 콘크리트 구조물의 수직 벽체면 방수 공사에서 본 발명에 따른 복합 방수층의 구성 시공 상세도를 나타낸 도이다.
도 7은 수직 벽체면 방수 공사에서 방수층 고정용 누름 철물의 형상도를 나타낸 도이다. 1 is a cross-sectional view of a composite waterproofing layer according to an embodiment of the present invention.
2 is a view showing the configuration of the composite waterproof layer according to an embodiment of the present invention.
3 is a view showing the structure of a waterproof sheet according to an embodiment of the present invention.
Figure 4 is a view showing the shape and cross-sectional view of the waterproof sheet according to an embodiment of the present invention.
5 is a view showing the detailed construction of the composite waterproof layer according to the present invention in the horizontal floor waterproofing construction, such as the roof of the building or the upper slab underground parking.
6 is a view showing the detailed construction of the composite waterproof layer according to the present invention in the vertical wall surface waterproofing construction of underground concrete structures such as subways, underground roads and cavities.
7 is a view showing the shape of the waterproofing layer fixing pressing hardware in the vertical wall surface waterproofing construction.

이하, 하기 실시예 및 실험예에 의해 본 발명을 보다 상세하게 설명한다. 그러나, 하기 실시예는 본 발명의 범위를 제한하는 것은 아니며, 이는 본 발명의 이해를 돕기 위한 것으로 해석되어야 할 것이다.Hereinafter, the present invention will be described in more detail with reference to the following Examples and Experimental Examples. However, the following examples are not intended to limit the scope of the present invention, which will be construed as to aid the understanding of the present invention.

실시예 1. 고무 아스팔트 도막 방수층의 제조 Example 1 Preparation of Rubber Asphalt Coating Waterproofing Layer

고무 아스팔트 도막 방수재 조성물은 전술한 성분의 재료 및 구성비로 조성되었으며, 본 발명에 따른 상기 고무 아스팔트 도막 방수재 조성물로 형성된 고무 아스팔트 도막 방수층의 품질 성능 기준은 하기 표 1과 같다. The rubber asphalt coating waterproofing composition is composed of the material and the composition ratio of the above-described components, and the quality performance standards of the rubber asphalt coating waterproofing layer formed of the rubber asphalt coating waterproofing composition according to the present invention are shown in Table 1 below.

시험항목Test Items 단위unit 품질성능기준Quality performance standard 비고Remarks 고형분Solid content %% 80이상80 or more 160±5℃, 24hr160 ± 5 ℃, 24hr 회분Ash %% 15이상, 30이하15 or more, 30 or less ASTM D 4586ASTM D 4586 흘러내림 저항성능Spill Resistance ㎜Mm 3매 모두 흐름길이가 2.0이하,
주름발생 등이 없을 것All three sheets have a flow length of 2.0 or less,
No wrinkles, etc. 온도조절 40℃, 24hrTemperature control 40 ℃, 24hr 내알카리성Alkali resistance -- 이상없을 것No abnormality 내열성(80℃)Heat resistance (80 ℃) -- 이상없을 것No abnormality 저온굴곡성(-15℃)Low Temperature Flexibility (-15 ℃) -- 이상없을 것No abnormality 수분함량Water content %% 1.0이하1.0 or less KS M 0010KS M 0010 부착성능Adhesive performance N/㎟N / mm2 0.7이상0.7 or more KS F 3211KS F 3211 아스팔트 함량Asphalt content %% 45이상, 65이하45 or more, 65 or less ASTM D 4586ASTM D 4586 지촉건조(불점착,2mm)Dry touch (non-sticking, 2mm) -- 6시간이내Within 6 hours 점도(25℃)Viscosity (25 ℃) cpscps 20,000~40,00020,000 ~ 40,000

상기 고무 아스팔트 도막 방수재 조성물로 형성된 고무 아스팔트 도막 방수층의 품질 성능을 측정한 결과는 표 2와 같다. Table 2 shows the results of measuring the quality performance of the rubber asphalt coating waterproofing layer formed of the rubber asphalt coating waterproofing composition.

시험항목Test Items 단위unit 시험·검사방법Test and inspection method 시험·검사결과Test and inspection result 고형분Solid content %% KS M 3705 - 2015KS M 3705-2015 81.781.7 회분Ash %% KS M 0009 - 2010KS M 0009-2010 23.023.0 흘러내림 저항성능Spill Resistance ㎜Mm KS F 3211 - 2015KS F 3211-2015 0 (이상없음)0 (no abnormality) 내알카리성Alkali resistance -- KS M ISO 2712 - 2012KS M ISO 2712-2012 이상없음 nothing strange 내열성(80℃)Heat resistance (80 ℃) -- KS F 4917 - 2016KS F 4917-2016 이상없음nothing strange 저온굴곡성(-15℃)Low Temperature Flexibility (-15 ℃) -- KS M 5000 - 2014KS M 5000-2014 이상없음nothing strange 부착성능Adhesive performance N/㎟N / mm2 KS F 3211 - 2015KS F 3211-2015 1.01.0 수분함량Water content %% LH 전문시방서(42531):2015LH Professional Specification (42531): 2015 0.20.2

실시예 2. 방수시트의 제조 Example 2 Preparation of Waterproof Sheet

전술한 방법으로 개질 아스팔트 콤파운드 방수층; 및 상기 개질 아스팔트 콤파운드 방수층 상부면에 구비된 타포린 시트를 포함하는 타포린 시트 방수층; 을 포함하는 방수시트를 제조하였다. A modified asphalt compound waterproofing layer in the manner described above; And a tarpaulin sheet including a tarpaulin sheet provided on an upper surface of the modified asphalt compound waterproof layer; To prepare a waterproof sheet comprising a.

본 발명에 따른 방수시트의 품질 성능 기준은 하기 표 3과 같다. Quality performance standards of the waterproof sheet according to the present invention are shown in Table 3 below.

시험항목Test Items 단위unit 품질성능기준Quality performance standard 비고Remarks 인장강도The tensile strength N/㎜N / mm 10.0이상10.0 or more KS F 4917
(개량 아스팔트 방수시트)KS F 4917
(Improved asphalt waterproof sheet) 신장율Elongation %% 20.0이상20.0 or more 인열강도Tear strength NN 40.0이상40.0 or more 내열성(흘러내림길이)Heat resistance (flowing length) ㎜Mm 5.0이하5.0 or less 저온굴곡성능(-15℃)Low temperature bending performance (-15 ℃) -- 잔금이 생기지 않을 것No balance 패임 저항성Dent resistance -- 이상없음
(패임 저항성4)clear
(Break resistance 4) KS F 2622
(멤브레인 방수층의 방수성능 평가시험)KS F 2622
(Waterproof performance evaluation test of membrane waterproof layer) 충격 저항성Shock resistant -- 이상없음
(충격 저항성4)clear
(Shock resistance 4) 내피로성 Fatigue resistance -- 이상없음
(내피로성4)clear
(Fatigue resistance 4)

상기 방수시트의 품질 성능을 측정한 결과는 하기 표 4와 같다. The results of measuring the quality performance of the waterproof sheet are shown in Table 4 below.

시험·검사 종목 Test / Inspection 단위unit 시험·검사 방법Test and inspection method 시험·검사 결과 Test and inspection result 길이방향Longitudinal direction 나비방향Butterfly direction 인장강도The tensile strength 무처리No treatment N/㎜N / mm KS F 4917 - 2016KS F 4917-2016 35.235.2 31.731.7 신장율Elongation 무처리No treatment %% 3131 3030 인열성능Tearing performance NN 8181 107107 내열성Heat resistance 흘러내림길이Descent length ㎜Mm 22 겉모양Appearance -- 이상없음nothing strange 굴곡성능Flexural performance 무처리
(길이, -15℃) No treatment
(Length, -15 degrees Celsius) -- 이상없음nothing strange 패임 저항성Dent resistance -- KS F 2622 - 2003KS F 2622-2003 패임 저항성4Recession Resistance 4 충격 저항성Shock resistant -- 충격 저항성4Shock Resistance 4 내피로성 Fatigue resistance -- 내피로성 4Fatigue Resistance 4

상기 표 4에서의 KS F 4917의 개량 아스팔트 방수시트의 품질 성능 기준은 하기 표 5와 같다. Quality performance standards of the improved asphalt waterproof sheet of KS F 4917 in Table 4 are as shown in Table 5.

시험항목Test Items 단위unit KS 규격 품질성능기준KS standard quality performance standard 인장강도The tensile strength N/㎜N / mm 5.0이상5.0 or more 신장율Elongation %% 15.0이상15.0 or more 인열강도Tear strength NN 20.0이상20.0 or more 내열성(흘러내림길이)Heat resistance (flowing length) ㎜Mm 5.0이하5.0 or less 저온굴곡성능(-15℃)Low temperature bending performance (-15 ℃) -- 잔금이 생기지 않을 것No balance

상기 표 4에 따른 실험 결과를 표 5의 품질 성능 기준과 대비하여 보면, 인장 강도의 경우, KS 규격 품질성능 기준인 5.0 이상 대비 634%, 신장율의 경우 KS 규격 품질성능 기준인 15.0 이상 대비 200%, 인열 성능의 경우 KS 규격 품질성능 기준인 20.0 이상 대비 405%, 내열성의 경우 KS 규격 품질성능 기준인 5.0 이하 대비 250%으로 본 발명에 따른 방수시트의 품질이 방수 성능이 우수함을 확인할 수 있다. When comparing the experimental results according to Table 4 with the quality performance criteria of Table 5, in the case of tensile strength, 634% compared to KS standard quality performance standard of 5.0 or more, elongation rate 200% compared to KS standard quality performance standard of 15.0 or more In the case of tearing performance, the quality of the waterproof sheet according to the present invention can be confirmed that the quality of the waterproof sheet according to the present invention is 405% compared to the KS standard quality performance standard of 20.0 or more and 250% compared to the KS standard quality performance standard of 5.0 or less.

또한, 상기 표 4에서의 KS F 2622의 멤브레인 방수층의 방수성능 평가의 시험 방법은 하기 표 6과 같다. In addition, the test method of evaluating the waterproof performance of the membrane waterproof layer of KS F 2622 in Table 4 is as shown in Table 6.

시험항목Test Items 시험목적Purpose of test 시험방법Test Methods 시험결과의 판정기준Criteria for testing results 패임
저항성
시험Defeat
Resistance
exam 방수층에 국부하중이 작용하는 경우의 패임 저항성을 평가Evaluation of the dent resistance when the local load is applied to the waterproof layer 방수층에 직경30㎜의 철구로 온도20℃, 60℃이하에서 24 시간 일정한 하중을 가해 공극의 유무율 조사(시험체3개)Investigate the presence or absence of voids by applying a constant load to the waterproofing layer at a temperature of 20 ° C and 60 ° C for 24 hours using a steel ball with a diameter of 30 mm (3 specimens). 1: 50N의 하중에서 공극이 있다
2: 150N의 하중에서 공극이 있다
3: 250N의 하중에서 공극이 있다
4: 공극이 없다1: there is air gap at 50N load
2: air gap at 150N load
3: air gap at load of 250N
4: no void 충격
저항성
시험Shock
Resistance
exam 방수층의 충격에 대한 저항성을 평가Evaluate the resistance of the waterproof layer to impact 선단이 10㎜Ø인 500g의 봉형태의 추를 0,20,60℃의 환경하에서 방수층에 낙하시켜 공극의 유무를 조사(시험체3개)A 500 g rod-shaped pendulum with a tip of 10 mm Ø is dropped to the waterproof layer under an environment of 0,20,60 ° C to investigate the presence of voids (3 specimens). 1: 높이0.5m에서 공극이 있다
2: 높이1.0m에서 공극이 있다
3: 높이1.5m에서 공극이 있다
4: 공극이 없다1: there is air gap at height 0.5m
2: there is void at height 1.0m
3: there is air gap at 1.5m height
4: no void 내피로성
시험Fatigue resistance
exam 방수층 바탕과의 접합부 또는 바탕에 발생한 균열의 움직임에 대한 저항성을 평가Evaluate the resistance to crack movement in the junction or the base of the waterproofing layer 플렉시블판에 방수층을 시공하고 그것을 휨에 의해 절단하여 접합부의 확대, 축소를 0,20℃의 환경하에서 400회 반복해서 방수층의 상태를 조사 (시험체2개) Construct a waterproof layer on the flexible plate, cut it by bending, and repeat the expansion and contraction of the joint 400 times in an environment of 0,20 ℃ to investigate the state of the waterproof layer (2 specimens) 1: 0.5↔1.0㎜에서 파단한다
2: 1.0↔2.0㎜에서 파단한다
3: 2.5↔5.0㎜에서 파단한다
4: 파단이 없다1: Break at 0.5↔1.0㎜
2: Break at 1.0↔2.0㎜
3: Break at 2.5↔5.0㎜
4: no break

본 발명에 따른 방수시트의 방수 성능 시험 평가에서도 패임저항성 시험은 시험체 3개 모두 250N의 국부하중에서도 공극이 전혀 발생되지 않았으며, 충격 저항성 시험도 시험체 3개 모두 방수층의 충격에 따른 공극 발생이 없었으며, 내피로성 시험에서도 시험체 2개 모두 바탕의 균열 움직임에 대한 저항성 시험 결과 방수층이 파단되지 않는 품질성능이 확인됨으로서 본 발명의 개질 아스팔트 콤파운드 방수층; 및 상기 개질 아스팔트 콤파운드 방수층 상부면에 구비된 타포린 시트를 포함하는 타포린 시트 방수층; 을 포함하는 방수시트의 품질 우수성은 검증되었다 볼 수 있다. In the evaluation of the waterproof performance test of the waterproof sheet according to the present invention, the pitting resistance test did not generate any voids even at the local load of 250 N in all three test specimens, and all three test specimens had no voids caused by the impact of the waterproof layer. In addition, in the fatigue resistance test, the modified asphalt compound waterproofing layer of the present invention was confirmed as the quality performance that the waterproofing layer was not broken as a result of resistance test against crack movement of both test specimens; And a tarpaulin sheet including a tarpaulin sheet provided on an upper surface of the modified asphalt compound waterproof layer; Quality excellence of the waterproof sheet including the can be seen that has been verified.

Claims (20)

개질 아스팔트 콤파운드 방수층; 및
상기 개질 아스팔트 콤파운드 방수층 상부면에 구비된 타포린 시트를 포함하는 타포린 시트 방수층;
을 포함하는 방수시트. Modified asphalt compound waterproofing layer; And
A tarpaulin sheet waterproof layer including a tarpaulin sheet provided on an upper surface of the modified asphalt compound waterproof layer;
Waterproof sheet comprising a. 제1항에 있어서, 상기 타포린 시트 방수층은,
폴리에스터 부직포;
상기 폴리에스터 부직포 상부면에 구비된 타포린 시트; 및
상기 타포린 시트 상부면에 구비된 폴리에틸렌 필름을 포함하고,
상기 폴리에스터 부직포는 상기 개질 아스팔트 콤파운드 방수층과 접하여 구비되는 것인 방수시트. According to claim 1, The tarpaulin sheet waterproof layer,
Polyester nonwovens;
A tarpaulin sheet provided on an upper surface of the polyester nonwoven fabric; And
It comprises a polyethylene film provided on the upper surface of the tarpaulin sheet,
The polyester non-woven fabric is waterproof sheet that is provided in contact with the modified asphalt compound waterproof layer. 제2항에 있어서,
상기 폴리에스터 부직포의 질량은 30 g/㎡ 내지 60 g/㎡ 이고,
상기 타포린 시트의 질량은 100 g/㎡ 내지 220 g/㎡인 것인 방수시트. The method of claim 2,
The mass of the polyester nonwoven fabric is 30 g / ㎡ to 60 g / ㎡,
The tarpaulin sheet is a waterproof sheet of 100 g / ㎡ to 220 g / ㎡. 제2항에 있어서,
상기 폴리에틸렌 필름의 두께는 30 μm 내지 60 μm인 것인 방수시트. The method of claim 2,
The polyethylene film has a thickness of 30 μm to 60 μm. 제1항에 있어서,
상기 개질 아스팔트 콤파운드 방수층 하부면에 폴리에스터 부직포 또는 이형 필름이 더 구비되는 것인 방수시트. The method of claim 1,
Waterproof sheet is further provided with a polyester non-woven fabric or a release film on the modified asphalt compound waterproof layer lower surface. 제5항에 있어서,
상기 개질 아스팔트 콤파운드 방수층 하부면에 폴리에스터 부직포가 구비되고,
상기 개질 아스팔트 콤파운드 방수층 하부면에 구비된 폴리에스터 부직포의 질량은 60 g/㎡ 내지 120 g/㎡인 것인 방수시트. The method of claim 5,
Polyester nonwoven fabric is provided on the lower surface of the modified asphalt compound waterproof layer,
The mass of the polyester nonwoven fabric provided on the lower surface of the modified asphalt compound waterproof layer is 60 g / ㎡ to 120 g / ㎡ waterproof sheet. 제5항에 있어서,
상기 개질 아스팔트 콤파운드 방수층 하부면에 이형 필름이 구비되고,
상기 복합 방수층은 자착식 구조(Self Adhesive Type)인 것인 방수시트. The method of claim 5,
Release film is provided on the lower surface of the modified asphalt compound waterproof layer,
The composite waterproof layer is a self-adhesive structure (Self Adhesive Type) is a waterproof sheet. 제1항 내지 제7항 중 어느 한 항에 따른 방수시트; 및
상기 방수시트 하부면에 구비된 고무 아스팔트 도막 방수층을 포함하는 복합 방수층. Waterproof sheet according to any one of claims 1 to 7; And
Composite waterproof layer comprising a rubber asphalt coating waterproof layer provided on the lower surface of the waterproof sheet. 제8항에 있어서, 상기 고무 아스팔트 도막 방수층은,
속건성 아스팔트 화합물 45 중량% 내지 70 중량%;
합성고무 개질제 3 중량% 내지 10 중량%;
가소제 2 중량% 내지 5 중량%;
요변성증점제 2 중량% 내지 5 중량%;
산화방지제 0.5 중량% 내지 1.0 중량%; 및
광물질안정제 20 중량% 내지 35 중량%;
를 포함하는 겔(gel) 형상의 고무 아스팔트 도막 방수재 조성물로 형성된 것인 복합 방수층. The method of claim 8, wherein the rubber asphalt coating waterproofing layer,
45% to 70% by weight quick-drying asphalt compound;
3 to 10 weight percent synthetic rubber modifier;
2 to 5 weight percent plasticizer;
2 to 5 weight percent of thixotropic thickener;
0.5 wt% to 1.0 wt% antioxidant; And
20 wt% to 35 wt% mineral stabilizer;
Composite waterproof layer formed of a gel-like rubber asphalt coating waterproofing composition comprising a. 제9항에 있어서,
상기 속건성 아스팔트 화합물은, 스트레이트 런 아스팔트(Straight Run Asphalt)와 석유용제의 혼합물; 및
블로운 아스팔트(Blown Asphalt)와 석유용제의 혼합물을,
혼합한 것인 복합 방수층. The method of claim 9,
The fast-drying asphalt compound, a mixture of straight run asphalt (Straight Run Asphalt) and petroleum solvent; And
A mixture of blown asphalt and a petroleum solvent,
Composite waterproofing layer that is mixed. 제9항에 있어서,
상기 속건성 아스팔트 화합물은, 상기 스트레이트 런 아스팔트와 석유용제의 혼합물과 상기 블로운 아스팔트와 석유용제의 혼합물을 60 중량% 내지 85 중량% : 15 중량% 내지 40 중량%의 비율로 혼합한 것인 복합 방수층. The method of claim 9,
The fast-drying asphalt compound, the composite waterproof layer is a mixture of the mixture of the straight run asphalt and petroleum solvent and the blown asphalt and petroleum solvent in a ratio of 60% by weight to 85% by weight: 15% by weight to 40% by weight. . 제9항에 있어서,
상기 합성고무 개질제는 이소부틸렌-이소프렌 고무(Isobutene-Isoprene Rubber), PIB고무(Poly Isobutylene Rubber), 폴리부텐(Polybutene) 및 석유수지(Petroleum Resin)로 이루어진 군에서 1 또는 2 이상 선택되는 것인 복합 방수층. The method of claim 9,
The synthetic rubber modifier is one or more selected from the group consisting of isobutene-isoprene rubber (Isobutene-Isoprene Rubber), PIB rubber (Poly Isobutylene Rubber), polybutene (Polybutene) and petroleum resin (Petroleum Resin) Composite waterproofing layer. 제9항에 있어서,
상기 가소제는 프로세스 오일(process oil), 글리콜유 및 미네랄 스프리트 오일(Mineral Spirit Oil)로 이루어진 군에서 1 또는 2 이상 선택되고,
상기 산화방지제는 아민류 또는 페놀류인 것인 복합 방수층. The method of claim 9,
The plasticizer is selected from the group consisting of process oil, glycol oil and mineral spirits oil (Mineral Spirit Oil) 1 or 2 or more,
The antioxidant is a composite waterproof layer is amines or phenols. 제9항에 있어서,
상기 광물질안정제는 해포석(Sepiolite), 프라이애쉬(Fly Ash), 탄산칼슘, 이산화규소 및 고령토로 이루어진 군에서 1 또는 2 이상 선택되고,
상기 요변성 증점제는 벤토나이트 광물질인 것인 복합 방수층. The method of claim 9,
The mineral stabilizer is selected from the group consisting of Sepolite, Fly Ash, Calcium Carbonate, Silicon Dioxide and Kaolin,
The thixotropic thickener is a bentonite mineral composite composite layer. 바탕면을 정리하는 제1단계;
방수하자 발생 취약 부위의 방수층을 보강하는 제2단계;
바탕면 상부면에 고무 아스팔트 도막 방수재 조성물을 도포하여 고무 아스팔트 도막 방수층을 형성하는 제3단계;
상기 고무 아스팔트 도막 방수층 상부면에 제1항 내지 제7항 중 어느 한 항에 따른 방수시트를 부착하는 제4단계; 및
상기 제4단계는 상기 고무 아스팔트 도막 방수층 상부면에 2 이상의 방수시트를 부착하는 경우, 상기 방수시트의 연결 이음 부위의 수밀성을 보강하는 제5단계;를 포함하고,
상기 방수시트들은 겹침 이음으로 연결하며, 상기 겹침 폭은 50 ㎜ 이상인 것인 복합 방수층의 시공 방법. A first step of arranging the base surface;
A second step of reinforcing a waterproof layer of a water-resistant flaw-prone area;
A third step of forming a rubber asphalt coating waterproofing layer by applying a rubber asphalt coating waterproofing composition to the upper surface of the base surface;
A fourth step of attaching the waterproof sheet according to any one of claims 1 to 7 on the upper surface of the rubber asphalt coating waterproofing layer; And
The fourth step includes a fifth step of reinforcing the watertightness of the joint portion of the waterproof sheet when the two or more waterproof sheets are attached to the upper surface of the rubber asphalt coating waterproofing layer.
The waterproof sheets are connected by overlapping joints, and the overlapping width is 50 mm or more construction method of the construction. 제15항에 있어서,
상기 바탕면을 정리하는 제1단계 후, 상기 방수하자 발생 취약 부위의 방수층을 보강하는 제2단계 전에 상기 바탕면 상부면에 프라이머층을 형성하는 단계를 추가로 포함하는 복합 방수층의 시공 방법. The method of claim 15,
After the first step of arranging the base surface, before the second step of reinforcing the waterproof layer of the water-resistant flaw generation vulnerable site further comprising the step of forming a primer layer on the base surface upper surface. 제15항에 있어서,
상기 고무 아스팔트 도막 방수층 상부면에 상기 방수시트를 부착하는 제4단계는, 상기 고무 아스팔트 도막 방수재 조성물을 도포와 동시에 상기 방수시트를 부착시키는 것인 복합 방수층의 시공방법. The method of claim 15,
The fourth step of attaching the waterproof sheet on the upper surface of the rubber asphalt coating waterproofing layer, coating the rubber asphalt coating waterproofing composition and the waterproof sheet at the same time the construction method of the construction. 제15항에 있어서,
상기 복합 방수층이 수직 벽체면 외부에 시공되는 경우,
상기 복합 방수층을 시공한 후, 방수층 누름 철물로 상기 복합 방수층을 수직 벽체면에 고정하는 단계를 더 포함하는 것인 복합 방수층의 시공방법. The method of claim 15,
When the composite waterproof layer is constructed outside the vertical wall surface,
After constructing the composite waterproof layer, further comprising the step of fixing the composite waterproof layer to the vertical wall surface with a waterproof layer pressing iron. 제18항에 있어서,
상기 누름 철물의 폭은 30 mm 내지 40 mm이고,
상기 누름 철물의 재질은 알루미늄 또는 플라스틱인 것인 복합 방수층의 시공방법. The method of claim 18,
The width of the pressing iron is 30 mm to 40 mm,
Construction of the composite waterproof layer is a material of the pressing iron is aluminum or plastic. 제15항에 있어서,
상기 복합 방수층을 형성한 후, 상기 복합 방수층 상부면에 방근층을 설치하는 단계를 더 포함하고,
상기 방근층은 방근시트; 및 상기 방근시트 상부면에 방근 보조필름이 구비되며,
상기 방근 보조필름은 고밀도 폴리에틸렌(HDPE)계 또는 폴리에틸렌테레프탈레이트(PET)계인 것인 복합 방수층의 시공방법.



The method of claim 15,
After forming the composite waterproof layer, further comprising the step of installing a root barrier layer on the upper surface of the composite waterproof layer,
The barrier layer is a barrier sheet; And a weatherproof auxiliary film on the top surface of the weatherproof sheet,
The waterproof auxiliary film is a high density polyethylene (HDPE) -based or polyethylene terephthalate (PET) -based construction method of the composite waterproof layer.



KR1020180066315A 2018-06-08 2018-06-08 Waterproof sheet, complex waterproofing layer comprising thereof and manufacturing method of the same KR20190139627A (en)