KR100744727B1 - Expoused double waterproof plus film of paint and sheet in the building and construction method of the same - Google Patents
Expoused double waterproof plus film of paint and sheet in the building and construction method of the same Download PDFInfo
- Publication number
- KR100744727B1 KR100744727B1 KR1020070034433A KR20070034433A KR100744727B1 KR 100744727 B1 KR100744727 B1 KR 100744727B1 KR 1020070034433 A KR1020070034433 A KR 1020070034433A KR 20070034433 A KR20070034433 A KR 20070034433A KR 100744727 B1 KR100744727 B1 KR 100744727B1
- Authority
- KR
- South Korea
- Prior art keywords
- asphalt
- sheet
- waterproof
- coating
- layer
- Prior art date
Abstract
Description
도1은 종래기술에 따른 개량 아스팔트 방수시트의 구성도.1 is a block diagram of an improved asphalt waterproof sheet according to the prior art.
도2는 본 발명에 의한 건축 구조물의 도막 및 시트 이중 노출방수공법을 개략적으로 나타낸 단면도.Figure 2 is a cross-sectional view schematically showing the coating film and sheet double exposure waterproofing method of the building structure according to the present invention.
도3은 본 발명에 사용되는 아스팔트 노출형 아스팔트 방수시트의 구성을 나타낸 사시도.Figure 3 is a perspective view showing the configuration of the asphalt exposed asphalt waterproof sheet used in the present invention.
도4는 본 발명이 신축공사에 적용된 예시도.4 is an exemplary view of the present invention applied to new construction.
도5는 본 발명이 보수공사에 적용된 예시도.5 is an exemplary view of the present invention applied to the repair work.
*도면의 주요 부분에 대한 부호의 설명* Explanation of symbols for the main parts of the drawings
20: 콘크리트 구조물 바탕면 30: 프라이머층20: ground surface of the concrete structure 30: primer layer
40: 고무 아스팔트 도막 방수층 50: 시트층40: rubber asphalt coating film waterproof layer 50: sheet layer
60: 착색그래뉼 입자층 70: 노출방수시트60: colored granule particle layer 70: exposed waterproof sheet
본 발명은 건축물의 옥상이나 주차장의 상부 등의 방수를 위한 건축 구조물의 도막 및 시트 이중 노출방수공법에 관한 것으로, 특히 콘크리트 피도체에 대한 강력한 접착력 및 탄력성, 신축성으로 콘크리트 크랙에 따른 저항력을 갖는 도막방수층과 자외선에 강한 착색그래뉼 입자층을 상부 노출층으로 형성한 방수시트층을 결합함으로써 도막 및 시트이중 방수효과를 극대화한 건축 구조물의 도막 및 시트 이중 노출방수재 및 그의 시공방법에 관한 것이다. The present invention relates to a double-layer waterproofing method of the coating and sheet of the building structure for waterproofing the roof of the building or the upper part of the parking lot, in particular a coating film having a strong adhesive force, elasticity, elasticity to the concrete object, according to the concrete crack The present invention relates to a coating and sheet double exposure waterproofing material for a building structure that maximizes the coating and sheet double waterproofing effect by combining a waterproof sheet and a waterproof sheet layer formed of an upper exposed layer of colored granule particle layers resistant to ultraviolet rays, and a construction method thereof.
일반적으로, 콘크리트 건물 특히 옥상의 경우는 외부적 요인과 가장 많이 접촉하는 곳으로, 강수에 대한 방어를 위한 방수기능, 태양광선에 의한 일사 열량의 열부하를 경감시키며 내부의 열을 보온·단열시키기 위한 기능, 적설하중과 풍화하중에 의해 지붕면에 작용하는 적재하중을 감당할 수 있는 기능을 고려하여 적절한 방수공법 및 방수재료를 선택하여야 한다.In general, concrete buildings, especially rooftops, are the ones that are most in contact with external factors. They are waterproof to prevent precipitation, reduce the heat load of solar radiation caused by sunlight, and insulate and insulate the heat inside. Appropriate waterproofing method and waterproofing material should be selected in consideration of the ability to handle the loading load acting on the roof surface by function, snow load and weathering load.
건물 옥상방수의 보수공사에는 기존의 방수층 보호 누름 콘크리트층과 방수층까지 철거 후 새로운 방수층(비노출 방수층)을 형성하고, 다시 방수층 보호 누름 콘크리트층을 설치하는 기존 방수층 철거방식과, 기존의 방수층과 방수층 보호 누름 콘크리트층을 철거하지 않고 그 위에 새로운 방수층(노출방수층)을 덮어씌우는 방식으로 구분할 수 있으며, 이들 방식의 장,단점은 다음과 같다.For the renovation of the rooftop waterproofing of the building, after removing the existing waterproof layer protection pressed concrete and waterproof layers, form a new waterproof layer (non-exposed waterproof layer) and press the waterproof layer protection again. Press It can be classified by covering the new waterproof layer (exposure waterproof layer) on top of it without removing the concrete layer. The advantages and disadvantages of these methods are as follows.
전자의 노후화된 기존 방수층 철거방식에 적용되는 비노출 방수층은 방수층에 대한 충격을 방지하여 한냉, 적설에 대한 방수층을 보호하고, 자외선, 산성비에 대한 방수층의 안전성으로 내후성, 내구성이 우수한 반면에, 공사비가 많이 들며 공사기간이 길고, 기존 방수층과 방수층 보호 누름 콘크리트층 철거 작업시 소음과 분진발생에 철거 잔재 폐기물 처리에 따른 공해가 발생한다.The non-exposed waterproof layer applied to the deterioration of the existing waterproof layer of the former prevents the impact on the waterproof layer to protect the waterproof layer against cold and snow, and has excellent weather resistance and durability due to the safety of the waterproof layer against UV rays and acid rain, It takes a lot of work, and the construction period is long, and the existing waterproof layer and the waterproof layer are pressed. When the concrete layer is removed, noise and dust are generated.
후자의 덮어씌우는 방식의 노출 방수층은 보수가 간단하여 보수기간이 짧으며 보수비가 경제적이고, 새로운 방수층 형성에 따른 슬라브 위 하중부하가 미미한 장점이 있는 반면에, 옥상위에 중량물을 놓을 수 없으며, 옥상사용에 다소 제약을 받는다. The latter covering waterproof layer has simple advantages such as simple repair period, short repair period, economical cost of maintenance, and minimal load on the slab due to the formation of a new waterproof layer, while it is not possible to place heavy materials on the rooftop. Are somewhat restricted to
한편, 건축 구조물의 옥상과 같이 노출된 부위에는 수분이 내부로 스며드는 것을 방지하기 위하여 구조물의 표면에 불투수성의 방수층을 형성하는데, 이러한 방수층을 형성시키는 방법으로는 노출형 아스팔트 시트방수, 액체방수, 에폭시방수, 폴리우레탄방수 등과 같은 다양한 방법이 사용되고 있다.Meanwhile, in order to prevent moisture from penetrating into the exposed areas such as the roof of the building structure, an impermeable waterproof layer is formed on the surface of the structure, and the method of forming such a waterproof layer is exposed asphalt sheet waterproof, liquid waterproof, epoxy Various methods such as waterproofing and polyurethane waterproofing are used.
여기서, 상기 노출형 아스팔트 시트방수공법은 작업자가 방수시트 하부면을 토우치 램프로 가열하여 고무아스팔트를 용융시키면서 콘크리트 바탕면에 접착하는 열융착공법이다. 상기 공법은 인력에 의존하여 토우치 램프로 아스팔트 방수시트를 가열하기 때문에 상기 아스팔트 방수시트의 균일한 가열을 이룰 수가 없다. 이로 인해 콘크리트 바탕면과의 완전한 접착이 이루어지지 않아 부분적으로 시트방수층의 들뜸현상이 발생되는 문제점이 있다. 특히 방수시트의 하부면 또는 방수시트의 연결이음부를 가열하는 과정에서 아스팔트 콤파운드의 연소산화에 따른 수밀성이 약화되어 누수사고와 같은 하자가 빈번해지는 문제점이 있다.
또한, 상기 공법에 적용되는 노출형 아스팔트 방수시트는 하절기에 태양광선에 장기간 노출되거나 또는 동절기의 추운 영하의 날씨에 의해 여러 해에 걸쳐 수축 팽창이 반복되면 갈라지거나 들뜨는 다른 문제점이 있었다.Here, the exposure-type asphalt sheet waterproofing method is a heat fusion method for the operator to heat the lower surface of the waterproof sheet with a torch lamp to melt the rubber asphalt while adhering to the concrete base surface. The method does not achieve uniform heating of the asphalt waterproof sheet because the asphalt waterproof sheet is heated by the torch lamp depending on the attraction force. Due to this, there is a problem in that the full adhesion with the concrete base surface is not made, thereby partially lifting the sheet waterproof layer. In particular, in the process of heating the bottom surface of the waterproof sheet or the connection joint of the waterproof sheet, the watertightness due to the combustion oxidation of the asphalt compound is weakened, so that there are frequent problems such as leakage accidents.
In addition, the exposed asphalt waterproof sheet applied to the above method had another problem of cracking or lifting after repeated expansion and contraction for many years due to long-term exposure to sunlight in the summer or cold and freezing weather in winter.
도막 방수는 폴리우레탄 또는 아크릴 고무를 주원료로 하는 액상의 도막방수재를 수차례 도포하여 피막을 형성하는 것으로서, 이음새없는 방수층을 형성할 수 있고 협소한 시공 부위도 간단히 시공할 수 있으나, 액상의 도막방수재를 여러 겹으로 순차 도포할 때, 한 겹당 각기 약 24시간 이상의 경화 시간을 요구하므로 시공시간이 길어지며, 구조물에 균열이 발생되면 도막재 또한 파단되어 누수의 원인이 되는 단점이 있었다.Coating waterproofing is to form a coating by applying a liquid coating waterproofing material, which is mainly made of polyurethane or acrylic rubber, several times, which can form a seamless waterproofing layer and can easily construct narrow construction sites, but it is a liquid coating waterproofing material. When sequentially applying a plurality of layers, each time requires a curing time of more than about 24 hours each, so the construction time is long, and if a crack occurs in the structure, the coating material also breaks, causing a leak.
최근에는 옥상 슬래브에 행해지는 방수공법으로서, 아스팔트 시트방수와 폴리우레탄 도막방수를 결합한 복합방수공법이 제안되어 사용되고 있다. 이러한 종래의 복합방수공법은 특허 등록 제0590854호에서 제시된 것이다. 상기 복합방수공법은 도1에 도시한 바와 같이 콘크리트 바탕면 또는 프라이머층(110)상에 아스팔트 시트(120)를 깔고 상기 아스팔트 시트(120)의 상부에 부직포층(130)을 형성하고, 상기 부직포층(130) 위에 노출면으로서의 폴리우레탄 도막 방수층(140)을 설치함으로써 이질재료인 아스팔트 시트층(120)과 도막방수층(140)간의 결합을 이룰 수 있도록 한 구조(100)이다.Recently, as a waterproof method performed on a rooftop slab, a composite waterproof method combining an asphalt sheet waterproof and a polyurethane coating waterproof has been proposed and used. This conventional composite waterproof method is presented in Patent Registration No. 0590854. In the composite waterproof method, as shown in FIG. 1, the
상기한 복합방수구조(100)에서 폴리우레탄층은 내열성과 내신축성이 우수하기 때문에 하절기에 태양광선에 장기간 노출되거나 동절기의 추운 영하날씨에도 수축팽창이 되지 않는 물성을 가지고 있어, 노출면 방수에 적합하게 사용되고 있다. In the composite
그러나, 상기 아스팔트 시트 및 폴리우레탄 조합의 복합방수구조(100)는 콘크리트 바탕면과 아스팔트 방수시트층(120)이 부분적으로 접합되어 시트 방수층이 콘크리트 바탕면으로부터 띄워지는 절연방수층을 형성하게 되므로, 콘크리트 바탕면과 다소의 습윤상태에서도 시공할 수 있는 장점이 있으나, 만약의 시공부주의에 의한 하자발생시 방수층 아래에서 누수된 물이 흘러다니게 되므로 부분적 보수가 불가능한 커다란 문제점이 있다.
특히, 상기 구조는 폴리우레탄 도막방수층과 아스팔트 방수시트층이 이질재료로 이루어져 있기 때문에 오랜 시간이 경과한 후에 폴리우레탄층이 아스팔트 방수시트층으로부터 분리되는 현상이 발생되어 방수 하자로 이어질 수 있고, 상기에서 제안된 공법은 방수공사 시공의 대부분이 작업 인부들의 인력에 의한 시공으로 이루어지고 있어 시공상의 부주의에 의한 하자발생이 빈번한 원론적인 문제점을 그대로 내포하고 있다.However, the composite
Particularly, since the polyurethane coating waterproof layer and the asphalt waterproof sheet layer are made of heterogeneous materials, the structure may cause the polyurethane layer to be separated from the asphalt waterproof sheet layer after a long time, leading to a waterproof defect. The construction method proposed in the above is made up of most of the waterproof construction work by manpower of workers, and thus contains the fundamental problem of frequent defects caused by inadvertent construction.
따라서, 본 발명은 상기의 제반 문제점을 해결하기 위하여 제안된 것으로서, 건축물의 옥상이나, 지하주차장 상부 등의 도막 방수를 목적으로 하는 아스팔트 매스틱 도막방수재와 노출면에 착색그래뉼 입자를 도포하여 제작된 노출 방수시트를 부착하는 시공방법으로 물과 습기의 침투를 방지함은 물론 알카리나 산성물질의 영향을 전혀 받지 않으며, 높은 항장력, 탄성력 및 내구성이 뛰어나고, 콘크리트 균열에 대한 저항력을 가지고 영구방수를 행할 수 있는 건축 구조물의 도막 및 시트 이중 노출방수재 및 그의 시공방법을 제공함에 그 목적이 있다.Therefore, the present invention has been proposed to solve the above problems, it is produced by applying colored granule particles to the asphalt mastic coating waterproofing material and the exposed surface for the purpose of waterproofing the coating film, such as the roof of the building or the upper part of the underground parking lot. As a method of attaching the exposed waterproof sheet, it prevents the penetration of water and moisture, and is not affected by alkali or acidic materials, and has high tensile strength, elasticity and durability, and resistance to concrete cracking. The purpose of the present invention is to provide a coating and sheet double exposure waterproofing material and a construction method thereof of the building structure.
또한, 본 발명은 겔 상태의 아스팔트 매스틱 도막방수재를 이용함으로써 시공이 까다로운 부위에도 쉽게 시공할 수 있으며, 하자발생 부위 발견 및 보수시공이 간단할 뿐만 아니라, 동절기 시공이 가능한 건축 구조물의 도막 및 시트 이중 노출방수재 및 그의 시공방법을 제공함에 다른 목적이 있다.In addition, the present invention can be easily applied to the difficult construction site by using a gel-like asphalt mastic coating waterproofing, and easy to find and repair the defect site, as well as coating and sheet of the building structure that can be built in winter Another object is to provide a double exposure waterproofing material and its construction method.
또한, 본 발명은 보호방수층으로서의 보호몰탈이나 누름콘크리트를 타설하지 않고도 외부자외선에 강한 착색그래뉼 입자층이 도포된 방수시트를 도막방수층에 까는 작업만으로 마감공정을 수행할 수 있어 시공공정이 감소되고, 이에 따른 공사비 절감 및 공사기간을 단축할 수 있는 건축 구조물의 도막 및 시트 이중 노출방수재 및 그의 시공방법을 제공함에 또 다른 목적이 있다.In addition, the present invention can perform the finishing process only by covering the waterproof sheet coated with a layer of granulated granules strong to external ultraviolet rays to the coating waterproof layer without placing protective mortar or pressed concrete as a protective waterproof layer, thereby reducing the construction process. It is another object of the present invention to provide a double-coated waterproofing material and a method of constructing a coating and sheet of a building structure that can reduce the construction cost and shorten the construction period.
상기 목적을 달성하기 위하여 본 발명은, 속건성 아스팔트 화합물(Quick Drying Asphalt Compound)을 주원료로 하되, 상기 물질에 합성고분자 수지 접착제, 천연 광물질 섬유, 석유수지 및 이소부틸렌 또는 폴리 이소부틸렌계 합성수지중 하나의 물질을 혼합하여 제조되며, 건축 구조물 바탕면 또는 프라이머층과 결합되는 고무 아스팔트 도막 방수층; 및 상기 도막 방수재상에 적층되어 부착되며, 합성수지 양면에 고무 아스팔트 혼합물이 도포되고 상부 노출면에 자외선 차단제(Ultraviolet material)가 코팅된 착색그래뉼 입자가 도포된 노출형 아스팔트 방수시트층을 포함하는 건축 구조물의 도막 및 시트 이중 노출방수재를 제공한다.In order to achieve the above object, the present invention, a quick-drying asphalt compound (Quick Drying Asphalt Compound) as the main raw material, the synthetic polymer resin adhesive, natural mineral fiber, petroleum resin and isobutylene or poly isobutylene-based synthetic resin to the material It is prepared by mixing the materials of, rubber asphalt coating waterproofing layer is bonded to the building surface or primer layer; And an exposed asphalt waterproof sheet layer laminated on the coating waterproof material, and having a rubber asphalt mixture coated on both sides of a synthetic resin and coated with granulated granules coated with an ultraviolet ray material on an upper exposed surface. It provides a coating film and a sheet double exposed waterproof material.
또한, 본 발명은 속건성 아스팔트 화합물(Quick Drying Asphalt Compound)을 주원료로 하되, 상기 물질에 합성고분자 수지 접착제, 천연 광물질 섬유, 석유수지 및 이소부틸렌 또는 폴리 이소부틸렌계 합성수지중 하나의 물질을 혼합하여 제조된 도막방수재를 시공할 모체 표면에 도포하는 제1 단계; 합성수지 양면에 고무 아스팔트 혼합물이 도포되고, 하부표면에 이형필름이 부착되고, 상부 노출면에 자외선 차단제(Ultraviolet material)가 코팅된 착색그래뉼 입자가 도포되어 제작된 롤 형상의 노출형 아스팔트 방수시트를 상기 도막방수재상에 깔아 접착하는 제2 단계; 및 상기 노출형 아스팔트 방수시트의 일단부측 상부에 소정 폭만큼 상기 1차 도막방수재와 동일하게 이루어진 2차 도막방수재를 도포하고, 그 위에 다른 노출형 아스팔트 방수시트를 중첩되게 깔아주어 이음매부위를 연결하고 마감하는 제3 단계를 포함하는 건축 구조물의 도막 및 시트 이중 노출방수재의 시공방법을 제공한다. In addition, the present invention is a quick drying asphalt compound (Quick Drying Asphalt Compound) as a main raw material, by mixing a material of one of synthetic polymer resin adhesive, natural mineral fiber, petroleum resin and isobutylene or poly isobutylene-based synthetic resin to the material A first step of applying the prepared coating waterproofing material to the surface of the mother body to be constructed; A rubber asphalt mixture is coated on both sides of the synthetic resin, a release film is attached to the lower surface, and colored granule particles coated with an ultraviolet ray material (ultraviolet material) are coated on the upper exposed surface. A second step of adhering onto the coating waterproofing material; And applying a secondary coating waterproofing material having the same width as that of the primary coating waterproofing material on a top of one end side of the exposed asphalt waterproofing sheet, spreading the other exposed asphalt waterproofing sheet on it and connecting the joint portions. Provided is a method of constructing a double exposure waterproofing coating and sheet of a building structure comprising a third step of finishing.
이하, 첨부된 도2 내지 도5를 참조하여 본 발명의 실시예를 상세히 설명한다. Hereinafter, embodiments of the present invention will be described in detail with reference to FIGS. 2 to 5.
본 발명에 의한 건축 구조물의 도막 및 시트 이중 노출방수재 및 그의 시공방법은 콘크리트 피도체에 대한 강력한 접착력 및 탄력성, 신축성으로 콘크리트 크랙에 따른 저항력을 갖는 도막방수층과 자외선 차단제가 코팅된 착색그래뉼 입자층을 노출층으로 형성한 아스팔트 방수시트를 적층시공함으로서 도막 및 시트의 이중방수로 탁월한 방수효과를 나타내며, 간편하게 시공할 수 있도록 구현한 것이다.Double-coated waterproofing material and sheet of the building structure according to the present invention and its construction method is exposed to the coating layer and the layer of granulated granules coated with a sunscreen having a strong adhesive strength, elasticity, elasticity to the concrete coating, resistance to concrete cracks By stacking the asphalt waterproof sheet formed of a layer, it shows an excellent waterproof effect by double waterproofing of the coating film and the sheet, and is implemented to be easily constructed.
본 발명에 따른 건축 구조물의 도막 및 시트 이중 노출방수재는 도2 및 도3에 도시된 바와 같이, 속건성 아스팔트 화합물(Quick Drying Asphalt Compound)을 주원료로 하되, 상기 물질에 합성고분자 수지 접착제, 천연 광물질 섬유, 석유수지 및 이소부틸렌 또는 폴리 이소부틸렌계 합성수지중 하나의 물질을 혼합하여 제조되며, 건축 구조물의 바탕면(20) 또는 프라이머층(30)과 결합되는 고무 아스팔트 매스틱(이하, '고무 아스팔트 도막 방수재' 라 칭함)(40)와; 합성수지 양면에 고무 아스팔트 혼합물이 소정 두께로 균일하게 도포된 시트층(50)과 상부 노출면에 자외선 차단제(Ultraviolet material)가 코팅된 착색그래뉼 입자층(60)으로 이루어지며, 상기 도막방수재 상부에 적층된 상태로 부착되는 자착식 노출형 아스팔트 방수시트(70)를 포함한다.As shown in FIGS. 2 and 3, the coating film and the sheet double exposed waterproofing material of the building structure according to the present invention are made of a quick drying asphalt compound as a main raw material, and the synthetic polymer resin adhesive and the natural mineral fiber are applied to the material. , A rubber asphalt mastic (hereinafter referred to as 'rubber asphalt') manufactured by mixing a material of petroleum resin and one of isobutylene or poly isobutylene-based synthetic resin and combined with a
본 발명의 실시예에서, 상기 노출형 아스팔트 방수시트는 하부에 아스팔트 혼합물로부터 쉽게 박리되도록 하기 위한 이형필름이 부착되어 있는 자착식 방수시트이다. 상기 이형필름은 방수시트가 롤(roll) 형태로 감겨질 때 방수시트의 감겨지는 면과 그의 대응면이 상호 접착되는 것을 방지하기 위한 것이며, 도막방수층상에 방수시트를 깔아 부착할 때에 이형필름을 박리시킨 후 시공하게 된다. In an embodiment of the present invention, the exposed asphalt waterproof sheet is a self-supporting waterproof sheet is attached to the release film to be easily peeled off from the asphalt mixture at the bottom. The release film is to prevent the surface and the corresponding surface of the waterproof sheet is bonded to each other when the waterproof sheet is wound in a roll (roll) form, and the release film when the waterproof sheet is attached to the waterproof layer After peeling off, it is constructed.
상기 노출형 아스팔트 방수시트는 하부의 고무 아스팔트 혼합물 표면에 폴리에스테르 장섬유 부직포를 접착성형시켜 형성할 수도 있다. 이 경우에 상기 부직포가 도막방수재에 함침됨으로써 도막방수재와 방수시트가 일체화되어 견고한 부착력을 유지할 수 있게 된다.The exposed asphalt waterproof sheet may be formed by adhesively molding a polyester long fiber nonwoven fabric on the surface of the rubber asphalt mixture below. In this case, the nonwoven fabric is impregnated with the coating waterproof material, thereby the coating waterproof material and the waterproof sheet are integrated to maintain a firm adhesive force.
상기 도막방수층은 도막방수기능과 함께 방수시트와 콘크리트 표면을 접착시키기 위한 접착제로서의 기능을 겸비하는 것으로, 도포후 1시간내에 탄성을 나타내는 상태의 지촉(指燭)건조상태로 경화되어야 한다. The coating film waterproofing layer combines the waterproofing film with the function of an adhesive for adhering the waterproof sheet and the concrete surface, and should be cured to a dry condition in a state showing elasticity within 1 hour after application.
도막방수기능을 부여하는 고무 아스팔트 도막 방수층의 기본 조건은 콘크리트 바탕면에 도포하여 콘크리트 표면과의 부착성을 높이고, 콘크리트 바탕면과 방수시트층간의 접합강도를 증가시키는 역할을 해야 한다. The basic condition of the waterproof layer of rubber asphalt coating which provides waterproofing function should be applied to concrete surface to increase adhesion to concrete surface and to increase the bonding strength between concrete surface and waterproof sheet layer.
이러한 조건을 충족하기 위해 미국 ASTM D2823에서 규정하는 아스팔트 루프 시멘트의 품질성능 기준은 하기의 <표1>과 같다.In order to meet these conditions, the quality performance standards of asphalt roof cement prescribed in the US ASTM D2823 are shown in Table 1 below.
<표1><Table 1>
상기 <표1>과 같은 기준을 만족시키기 위한 본 발명의 고무 아스팔트 도막 방수층은 속건성 아스팔트 화합물(Quick Drying Asphalt Compound) 40 ~ 57wt%를 주원료로 하되, 상기 물질에 합성고분자 수지 접착제(Synthetic Rubber Adhesives) 15 ~ 25wt%, 천연 광물질 섬유(Asbestos fibers, Modified Cellulose fibers) 12 ~ 16wt%, 석유수지 5 ~ 10wt% 및 이소부틸렌 또는 폴리 이소부틸렌계 합성수지중 어느 하나의 물질 3 ~ 10wt%를 혼합하여 제조된다.Rubber asphalt coating waterproofing layer of the present invention for satisfying the criteria as shown in Table 1, the main material is 40 ~ 57wt% of Quick Drying Asphalt Compound, Synthetic Rubber Adhesives 15 ~ 25wt%, natural mineral fibers (Asbestos fibers, Modified Cellulose fibers) 12 ~ 16wt%, petroleum resin 5 ~ 10wt% and isobutylene or poly isobutylene synthetic resin 3 ~ 10wt% of the mixed material do.
또한, 상기에서 혼합된 혼합물질에 보조첨가제로서, 내구성과 유연성을 보강하기 위하여 스테아린산 아연 0.2 ~ 0.6wt%이 첨가되고, 점도조절과 작업성 및 분산성을 용이하게 하기 위하여 석유용제 5 ~ 7wt%를 포함하고, 기타 분산제, 산화방지제, 가소제중 선택된 적어도 하나 이상의 물질 0.2 ~ 0.4wt%를 첨가하여 제조된다.In addition, 0.2 ~ 0.6 wt% of zinc stearate is added as a co-additive to the mixture material mixed above to enhance durability and flexibility, and 5 to 7 wt% of petroleum solvent to facilitate viscosity control, workability and dispersibility. It is prepared by adding 0.2 to 0.4 wt% of at least one material selected from other dispersants, antioxidants, and plasticizers.
상기 아스팔트 화합물은 컷백 아스팔트(Cutback Asphalt)나 블로운 아스팔트(Blown Asphalt) 또는 이들 컷백 아스팔트와 블로운 아스팔트를 혼합한 물질로서 아스팔트 고형분이 80%, 석유용제 (Solvent)가 20%로 이루어져 있다.The asphalt compound is cutback asphalt (Cutback Asphalt) or blown asphalt (Blown Asphalt) or a mixture of these cutback asphalt and blown asphalt, composed of 80% asphalt solids, 20% petroleum solvent (Solvent).
상기 합성고분자 수지 접착제는 크랙에 대한 대응력과, 내열성 및 접착성을 부여하기 위한 것으로, 15wt%이하로 첨가될 경우 신장률과 접착강도가 저하되고, 25wt%이상으로 첨가될 경우에는 신장률이 너무 커져 오히려 접착강도가 저하됨과 동시에 제조비용이 상승하는 문제점이 있다.The synthetic polymer resin adhesive is to impart a coping force, heat resistance and adhesion to cracks, and when it is added below 15wt%, the elongation rate and adhesive strength decrease, and when it is added above 25wt%, the elongation rate becomes too large. At the same time the adhesive strength is lowered, there is a problem that the manufacturing cost increases.
상기 천연광물질 섬유는 합성고무 접착제와 혼합되어 크랙에 대한 대응력을 부여하고, 또 접착강도를 증가시킬 수 있도록 하기 위한 것으로, 12wt%이하로 첨가될 경우에는 본 발명에서 요구하는 접착강도를 얻을 수 없고, 16wt%이상으로 첨가될 경우에는 내구성이 나빠지게 되는 문제점이 있다.The natural mineral fiber is to be mixed with the synthetic rubber adhesive to give a crack resistance and to increase the adhesive strength, when added to less than 12wt% can not obtain the adhesive strength required by the present invention When added in more than 16wt%, there is a problem that the durability is worse.
상기 석유수지는 접착력을 보강하고, 인장강도, 내열성을 증가시키기 위한 것으로, 5wt%이하로 첨가될 경우, 인장강도와 내열성이 저하되는 문제점이 있으며, 10wt%이상으로 첨가될 경우에는 강도가 너무 커서 크랙의 발생 가능성이 매우 큰 문제점이 있다.The petroleum resin is for reinforcing adhesive strength, increasing tensile strength and heat resistance, and when added to 5wt% or less, there is a problem that the tensile strength and heat resistance are lowered, and when added to 10wt% or more, the strength is too large. There is a problem that is very likely to occur cracks.
상기 천연광물질 섬유로는 석면(Asbestos Fibers) 또는 천연석을 가공한 무기질 휠러(Modified Cellulose Fibers)등으로 이루어질 수 있다. The natural mineral fiber may be made of asbestos fibers or inorganic wheelers processed with natural stone.
상기와 같은 조성으로 제조된 고무 아스팔트 도막 방수재는 기존의 아스팔트 시트 방수공법에서 시행되었던 프라이머층에 더하여 소정 두께(본 실시예에서는 1.0 ∼ 2.0mm정도)의 도포작업만으로 도막 및 접착기능을 신뢰적으로 이룰 수 있기 때문에, 도막방수기능과 함께 무기질인 콘크리트 바탕면과 유기질인 스트레치 아스팔트 펠트간의 완전한 접착을 수행할 수 있게 된다. 또한, 상기 도막방수재는 겔상으로 이루어져 있어 로울러나 붓등을 이용하여 콘크리트 바탕면 또는 프라이머층 뿐만 아니라, 벽체면에도 도포작업을 쉽고 균일하게 실시할 수 있다. 또한, 도막방수재 도포와 동시에 노출방수시트 깔기의 연속작업을 수행함으로써 시공을 간단히 행할 수 있을 뿐만 아니라, 시공인건비가 과다하게 소요되는 문제점을 해소할 수 있고, 작업인부의 시공부주의에 따른 방수하자를 방지할 수 있다. The rubber asphalt coating waterproofing material manufactured with the composition described above, in addition to the primer layer used in the existing asphalt sheet waterproofing method, the coating film and the adhesion function can be reliably only by applying a predetermined thickness (about 1.0 to 2.0 mm in this embodiment). As a result, it is possible to perform a complete adhesion between the inorganic concrete base surface and the organic stretch asphalt felt together with the waterproofing function of the film. In addition, the coating film waterproofing material is made of a gel, it can be easily and uniformly applied to not only the concrete base surface or primer layer, but also the wall surface using a roller or a brush. In addition, by carrying out the continuous operation of laying the exposed waterproof sheet at the same time as coating the coating waterproofing material can not only perform the construction, but also solve the problem of excessive labor cost, and the waterproofing of the worker due to the care of the construction You can prevent it.
상기에서 제시된 조성으로 이루어진 고무 아스팔트 도막 방수재는 특유의 강한 접착성에 의해 콘크리트 바탕면과 자착식 노출형 아스팔트 방수시트간의 완전한 접착을 이룬다.Rubber asphalt coating waterproofing material composed of the above-described composition is a perfect adhesion between the concrete base surface and self-exposed exposed asphalt waterproof sheet by the unique strong adhesion.
상기 노출형 아스팔트 방수시트에서 합성수지는 폴리프로필렌 직포와 폴리에스테르 부직포중 어느 하나로 이루어지며, 상기 합성수지의 양면에 도포되는 아스팔트 화합물은 아스팔트와 혼합성이 뛰어난 SBS(Styrene-Butadiene-Styrene)개량 아스팔트 화합물이나, 아스팔트와 혼합시 내열성 및 내후성이 뛰어난 APP(Atactic Polypropylene)개질 아스팔트 화합물로 형성된다. In the exposed asphalt waterproof sheet, the synthetic resin is made of any one of a polypropylene woven fabric and a polyester nonwoven fabric, and the asphalt compound coated on both sides of the synthetic resin is SBS (Styrene-Butadiene-Styrene) improved asphalt compound having excellent mixing properties with asphalt. When mixed with asphalt, it is formed of APP (Atactic Polypropylene) modified asphalt compound with excellent heat resistance and weather resistance.
상기 노출형 아스팔트 방수시트는 일반 방수시트와는 달리 시트 하부면, 즉 도막방수재와의 접착면에 폴리에스테르 부직포가 부착될 경우, 이 부직포가 콘크리트 모체의 표면에 도포된 도막 방수재를 함침함으로써 접착효과를 극대화시킴과 동시에 누름 콘크리트 타설작업시에도 시트의 밀림현상을 방지할 수 있고 겔 상태인 도막방수재의 유동성을 방지할 수 있는 것이다. Unlike the general waterproof sheet, the exposed asphalt waterproof sheet has an adhesive effect by impregnating the coating waterproof material coated on the surface of the concrete matrix when the polyester nonwoven fabric is attached to the lower surface of the sheet, that is, the adhesive surface with the coating waterproof material. At the same time, it is possible to prevent the rolling phenomenon of the sheet and to prevent the fluidity of the coating waterproofing material in the gel state even during pressing concrete pouring work.
그리고, 노출형 아스팔트 방수시트의 저면의 아스팔트 화합물에 부착되는 폴리에스테르 부직포는 상기 도막방수재를 함침시키기가 용이하고, 내구성이 뛰어나며 인장력이 크도록 하기 위하여 최소한 60g/㎡이상을 가진다. 상기 노출형 아스팔트 방수시트는 최소한 4mm이상의 두께를 갖는 것을 사용하며, 도막방수재상에 쉽게 깔수 있도록 통상 롤(roll) 형태로 제조된다. In addition, the polyester nonwoven fabric attached to the asphalt compound of the bottom surface of the exposed asphalt waterproof sheet has at least 60 g / ㎡ or more in order to easily impregnate the coating waterproofing material, excellent durability and high tensile force. The exposed asphalt waterproof sheet is used to have a thickness of at least 4mm or more, and is usually manufactured in a roll form so as to be easily spread on the coating waterproofing material.
본 발명에서의 상기 노출형 아스팔트 방수시트는 하기 <표2>의 품질성능 기준에 충족하는 것을 사용한다.The exposed asphalt waterproof sheet in the present invention is used to meet the quality performance criteria of the following <Table 2>.
<표2><Table 2>
상기와 같이 구성된 아스팔트 역청질계 도막방수재와 방수시트를 이용한 시공방법을 도4 및 도5에 도시된 바닥면 방수시공의 예를 들어 설명하면 다음과 같다. Referring to the construction method using the asphalt bitumen-based waterproof film and the waterproof sheet configured as described above with reference to the waterproof construction of the floor shown in Figures 4 and 5 as follows.
도4는 신축공사시의 시공상세도이고, 도5는 보수공사시의 시공상세도를 각각 나타낸다.4 is a detailed construction drawing at the time of new construction, and FIG. 5 is a detailed construction drawing at the time of repair work.
먼저, 신축공사에서는 도4에 도시한 바와 같이 방수공사를 시공할 콘크리트 모체 표면(슬라브)을 깨끗하고 편평하게 한다. 이때, 철선이나 못등이 돌출되지 않도록 처리하는 것이 바람직하며, 요철부분은 편평하게 쇠흙손으로 마감처리하거나 또는 고름몰탈을 시공한 후, 흙, 먼지, 모래 등을 깨끗하게 청소한다. 또한, 콘크리트 타설 이음매부위, 드레인부위, 바닥과 벽체의 모서리부위, 코너부위, 파이프연결부위등의 방수하자가 발생되기 쉬운 취약부분에 도막방수재를 2∼3mm두께로 먼저 도포하여 보강한 후에 아스팔트 프라이머를 도포(0.4ℓ/㎡)하고, 1차도막방수재를 2mm정도의 두께로 도포한다.First, in the new construction, the concrete matrix surface (slab) to be waterproofed as shown in Figure 4 to clean and flatten. At this time, it is preferable to treat the wires or nails so as not to protrude, and the uneven parts are flattened with iron trowels or after the pus mortar is applied, the soil, dust, sand, etc. are cleaned cleanly. In addition, after coating and reinforcing the film waterproofing material with a thickness of 2 to 3 mm on the fragile areas where water-proof defects such as concrete pouring seams, drains, floors and wall edges, corners, and pipe joints are easily generated, asphalt primer (0.4 L / m 2), and the primary coating waterproofing material is applied to a thickness of about 2 mm.
여기서, 상기 1차 도막방수재(아스팔트 매스틱; 도막용)가 액상 또는 겔상으로 바닥면에 도포되어 견고히 부착되기 때문에 상기 프라이머 도포공정은 생략할 수도 있다. Here, the primer coating process may be omitted because the primary coating waterproofing material (asphalt mastic; coating film) is applied to the bottom surface in a liquid or gel form and adheres firmly.
상기 1차 도막방수층을 방수시트의 폭만큼 톱니흙손을 사용하여 낮은 곳에서 높은 쪽으로 2mm 정도의 두께로 골고루 도포한다.The first coating waterproof layer is evenly applied to the thickness of about 2mm from the lower place to the high place using the toothed trowel as the width of the waterproof sheet.
그리고, 상기 1차 도포된 도막방수재위에 롤 형상으로 말려진 노출방수시트를 깔고, 롤러로 가볍게 눌러줌으로써 도막방수재와 방수시트가 이중으로 방수를 수행하기 때문에 방수성을 극대화할 수 있으며, 또한 방수시트를 도막방수층위에 까는 작업만으로 마감작업을 병행할 수 있으므로, 방수시공공정을 간략화할 수 있게 된다. And, by spreading the exposed waterproof sheet rolled in a roll shape on the first coating film waterproofing material, by pressing lightly with a roller, the waterproofing material and the waterproof sheet can be doubled to maximize the waterproofness, and also the waterproof sheet Since the finishing work can be performed only by covering the waterproof layer, the waterproof construction process can be simplified.
다음, 노출 방수시트간의 연결부분(이음매) 시공은 먼저 깔린 방수시트의 끝단측에 폭 10cm정도로 2차 도막방수재(아스팔트 매스틱; 보강용)를 1∼2mm두께로 도포한 후, 그 위에 노출 방수시트를 중첩시켜 깔아주면서 롤러로 가볍게 눌러주어 아래시트와 윗시트를 접착한다. 상기 2차 도막방수재는 1차 도막방수재와 동일한 성분으로 이루어진 것을 사용한다.Next, the connection part (seam) between the exposed waterproof sheets is first coated with a 1 ~ 2mm thickness of the secondary coating waterproofing material (asphalt mastic; reinforcing) on the end side of the waterproof sheet, and then exposed and waterproofed thereon. Gently press down on the rollers while overlapping the sheets to bond the lower and upper sheets. The secondary coating waterproofing material is made of the same components as the primary coating waterproofing material.
상기 공정 수행후, 상기 방수시트가 중첩된 이음매부위에서 접합 끝단부위 좌,우폭 5cm 정도에 3차 아스팔트 매스틱을 1∼2mm두께만큼 쇠흙손을 사용하여 보강 도포하므로서 상기 이음매부위로 물이나 습기등이 침투되는 것을 방지한다.After performing the process, water or moisture is applied to the joint portion by reinforcing and applying the third asphalt mastic by using a trowel as much as 1 to 2 mm in the left and right width of the joint at the joint end portion where the waterproof sheet is overlapped. Prevent it from penetrating.
상기와 같이 도막방수재의 도포 및 노출 방수시트 깔기 작업으로 방수시공을 완료한다.Complete the waterproof construction by applying the coating waterproofing material and laying the exposed waterproof sheet as described above.
상기 방수시공공정에서, 이음매 보강용인 2차 및 3차 아스팔트 매스틱은 4∼5시간 경과후 완전경화되는 경화성 아스팔트 매스틱을 사용한다.In the waterproof construction process, the secondary and tertiary asphalt mastic for seam reinforcement uses a curable asphalt mastic which is completely cured after 4 to 5 hours.
상기와 같이 구성되어 시공되는 본 발명은 아래의 실시예와 같이 건축 구조물의 옥상, 지하주차장 슬라브등의 방수가 필요한 모든 구조물의 외부방수에 적용할 수 있다.The present invention constructed and constructed as described above can be applied to the external waterproofing of all structures requiring waterproofing, such as a rooftop of a building structure, an underground parking lot slab, and the like, as in the following embodiments.
도5에 도시한 바와 같이 보수공사에서는 기존 방수층위에 형성된 누름 콘크리트의 바탕면을 정리한 후 전술한 도4와 같은 동일한 방법으로 시공을 행한다. As shown in FIG. 5, the repair work is carried out by arranging the base surface of the pressed concrete formed on the existing waterproof layer and then performing the same construction as in FIG.
한편, 수직벽체방수 시공의 경우, 전술한 바닥면 방수시공의 경우와 동일하다. 특히 바닥과 벽체의 모서리 부위는 바닥의 방수시트를 수직벽면 쪽으로 10cm정도 올려 붙이고, 또한 수직벽에서 내려오는 방수시트는 바닥면쪽으로 10cm정도 내려 붙여서 두겹으로 중첩되도록 한다. On the other hand, in the case of vertical wall waterproofing construction, it is the same as the case of the above-described waterproof floor construction. Particularly, the edges of the floor and the wall attach the bottom waterproof sheet about 10cm to the vertical wall surface, and the waterproof sheet down from the vertical wall attach about 10cm to the floor surface so that they overlap in two layers.
이상에서 설명한 본 발명은 전술한 실시예 및 첨부된 도면에 의해 한정되는 것은 아니고, 본 발명의 기술적 사상을 벗어나지 않는 범위내에서 여러가지 치환, 변형 및 변경이 가능함은 본 발명이 속하는 기술분야에서 통상의 지식을 가진자에게 있어 명백할 것이다.The present invention described above is not limited to the above-described embodiment and the accompanying drawings, and various substitutions, modifications, and changes are possible within the scope without departing from the technical spirit of the present invention. It will be apparent to those who have knowledge.
전술한 바와 같이 본 발명에 따르면, 다음과 같은 효과를 구현한다.As described above, according to the present invention, the following effects are realized.
첫째, 아스팔트 도막 및 접착제 기능을 겸비하는 고무 아스팔트 도막방수재와 착색그래뉼 입자층이 노출면으로 구성된 노출형 아스팔트 방수시트에 의한 이중방수층 형성으로 수밀성이 뛰어나 방수의 안전성ㆍ신뢰성을 확보할 수 있고, 바탕의 거동에 대한 대응성, 내화학성, 내구성, 내후성이 우수하다.First, it is possible to secure safety and reliability of waterproofing with excellent watertightness by forming a double waterproof layer by the exposed asphalt waterproof sheet composed of the exposed surface of rubber asphalt coating waterproofing material and colored granule particle layer having both asphalt coating and adhesive function. Excellent responsiveness to behavior, chemical resistance, durability and weather resistance.
둘째, 상온공법 시공으로서, 수직 벽체면 시공이 가능하며, 자재의 취급 및 운반 작업 위험성이 없고, 고무 아스팔트 도막 방수재의 상온 도포시공과 노출형 아스팔트 방수시트의 연속 작업으로 시공성이 양호하고 별도의 마감공정을 생략할 수 있다. Second, as a room temperature construction method, vertical wall construction is possible, there is no risk of material handling and transportation work, and the workability is good and continuous finish by the room temperature application of rubber asphalt coating waterproofing material and continuous work of exposed asphalt waterproof sheet. The process can be omitted.
셋째, 고무 아스팔트 도막 방수재의 강한 접착력에 의해 콘크리트 바탕면과의 들뜸이나 박리현상 없이, 콘크리트 바탕면과 노출형 아스팔트 방수시트를 완전하게 접착할 수 있는 고무 아스팔트 도막층을 형성함으로써, 만약의 시공 부주의에 의한 방수하자 발생시에도 방수층 아래로 누수된 물이 흘러다닐 수 없으므로 하자발생시 결함부위 발견이 용이하며 부분 보수시공이 간편하다. Third, due to the strong adhesion of the rubber asphalt coating waterproofing material, by forming a rubber asphalt coating layer that can completely adhere the concrete surface and the exposed asphalt waterproof sheet without lifting or peeling from the concrete ground surface. Water leaks under the waterproofing layer cannot flow even when water-resistant defects occur. Therefore, defects are easily found and partial repair work is easy.
삭제delete
Claims (9)