KR101459289B1 - Constructing method of multi layer air insulation waterproofing system - Google Patents

Constructing method of multi layer air insulation waterproofing system Download PDF

Info

Publication number
KR101459289B1
KR101459289B1 KR1020130047248A KR20130047248A KR101459289B1 KR 101459289 B1 KR101459289 B1 KR 101459289B1 KR 1020130047248 A KR1020130047248 A KR 1020130047248A KR 20130047248 A KR20130047248 A KR 20130047248A KR 101459289 B1 KR101459289 B1 KR 101459289B1
Authority
KR
South Korea
Prior art keywords
sheet
waterproof
layer
urethane
waterproofing
Prior art date
Application number
KR1020130047248A
Other languages
Korean (ko)
Other versions
KR20140128617A (en
Inventor
김재환
김충엽
Original Assignee
김재환
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김재환 filed Critical 김재환
Priority to KR1020130047248A priority Critical patent/KR101459289B1/en
Publication of KR20140128617A publication Critical patent/KR20140128617A/en
Application granted granted Critical
Publication of KR101459289B1 publication Critical patent/KR101459289B1/en

Abstract

본 발명은, 상하에 위치한 부재가 방수기능을 갖게 하고 상하 부재 사이를 잇으면서 일체로 형성된 격벽이 공간을 형성하고, 공간을 채운 공기층이 단열기능을 갖게 하여 방수시트와 단열재가 일체로 성형된 방수단열시트를 사용함으로써, 방수와 단열 및 결로현상을 동시에 해결할 수 있는 공기층이 형성된 방수단열시트 및 공기층 단열을 이용한 복합·복층·단열방수공법을 제공하기 위한 것이다.
본 발명에 따른 공기층이 형성된 방수단열시트는, 상부와 하부로 분리되어 있고, 상부와 하부 사이를 잇는 격벽이 일체로 형성되어, 격벽 사이사이가 공기층을 형성하고 있는 본체; 상기 본체의 상면과 하면에 열융착으로 접착된 부직포를 구비하여 구성되는 것을 특징으로 한다.
In the present invention, the upper and lower members have a waterproof function, the partition walls formed integrally with the upper and lower members form a space, the air layer filled with the space has a heat insulating function, The present invention is to provide a waterproof thermal insulation sheet having an air layer capable of simultaneously preventing waterproofing, adiabatic heat and condensation, and a composite, multi-layer, and waterproofing method using air layer insulation by using a heat insulation sheet.
A waterproof thermal insulation sheet having an air layer formed thereon according to the present invention is divided into an upper portion and a lower portion, a partition wall formed between the upper portion and the lower portion is integrally formed, and an air layer is formed between the partition walls. And a nonwoven fabric bonded to the upper surface and the lower surface of the body by thermal fusion bonding.

Description

공기층 단열을 이용한 복합·복층·단열방수공법{Constructing method of multi layer air insulation waterproofing system}{Construction method of multi layer air insulation waterproofing system using air layer insulation}

본 발명은 공기층 단열을 이용한 복합·복층·단열방수공법에 관한 것으로, 보다 상세하게는, 중간에 공기층을 형성함으로써 단열성 및 방수성을 동시에 갖는 방수단열시트를 사용하여 방수와 단열을 동시에 해결할 수 있는 공기층이 형성된 방수단열시트 및 공기층 단열을 이용한 복합·복층·단열방수공법에 관한 것이다.
The present invention relates to a composite, multi-layer, and heat insulating waterproofing method using an air layer insulation, and more particularly, to a waterproof and heat insulating waterproofing sheet having an air layer at an intermediate portion thereof, The present invention relates to a waterproof, heat insulating sheet having a waterproofing layer and a composite, multi-layer, and heat insulating waterproofing method using an air layer insulation.

일반적인 방수구조는 슬래브층 상면에 소정의 두께와 폭을 갖는 아스팔트시트의 이음부를 겹쳐지도록 위치시키고, 이음부에 토치 램프 등으로 열을 가하여 용융시켜서 상호 용착되게 하는 구조로 이루어졌다. 이와 같이 이루어진 방수구조는 각 낱장의 아스팔트시트 간에 겹쳐지는 이음부에 토치 램프 등을 이용하여 열로 용융시켜서 상호 용착되게 함으로써 어느 정도 방수효과가 있는 것이 사실이다. 그러나, 이러한 각 시트 간의 연결부분인 이음부를 토치 램프 등을 이용하여 열로 용융시켜서 용착하는 것이기 때문에 토치 램프의 과열로 인하여 구멍이 뚫려지거나 또는 미열로 인하여 용융되지 않은 채 시공되는 등 이음부가 균일하게 부착되지 못하는 경우가 있어서 누수 발생의 원인이 된다.
The general waterproof structure is constructed such that the joints of the asphalt sheets having a predetermined thickness and width are overlapped on the upper surface of the slab layer and the joints are welded to each other by applying heat with a torch lamp or the like to melt them. It is a fact that the waterproof structure having such a waterproof structure has a waterproof effect to a certain degree by melting the heat by using a torch lamp or the like in the joint portion overlapping each one of the asphalt sheets to mutually weld the same. However, since the joint part which is the connection part between the respective sheets is melted and fused by using a torch lamp or the like, holes are pierced due to the overheating of the torch lamp or they are applied without being melted due to low heat, It may cause leakage.

또한, 우레탄 도막방수공법은 콘크리트 슬래브층의 상면에 액상의 우레탄을 1차적으로 도포하고, 24시간이 경과된 후 2차우레탄층을 형성하며, 다시 24시간이 경과된 후 3차우레탄층을 형성하여 완료하는 방법이 있는데, 이와 같은 우레탄 도막방수공법은 우레탄이 방수재료로써 우수한 성질을 갖고 있어서 이음새 없는 방수층을 형성해 주며 상온반응의 냉공법으로서 큰 장점을 갖기는 하지만, 바닥 콘크리트면에 많은 요철이 있기 때문에 움푹 들어간 부분은 우레탄 수지가 많이 고여서 그 두께가 두껍게 형성되고, 볼록한 부분에는 얇게 형성되는 문제가 있으며, 콘크리트에 포함되어 있는 수분의 증기압에 의해 우레탄이 경화되기 전에 꽈리가 생기거나 들뜸이 생기는 등의 문제점이 있다.
In the urethane coating waterproofing method, a liquid urethane is first applied to the upper surface of the concrete slab layer, and after 24 hours, a secondary urethane layer is formed. After 24 hours, a third urethane layer is formed This urethane coating waterproofing method has excellent properties as urethane waterproofing material to form a seamless waterproof layer and has a great advantage as a cooling method of a room temperature reaction. However, there are many unevenness on the floor concrete surface There is a problem that the recessed portion is formed of a thick urethane resin due to a large amount of urethane resin and the thin portion is formed in the convex portion. When the urethane is hardened by the vapor pressure of water contained in the concrete, And the like.

상기와 같은 시트방수와 도막방수가 갖는 문제점을 해결하기 위하여 본 발명의 발명자는 특허등록 제180632호 "복합방수구조 및 그 시공방법", 특허등록 제238994호 "복합방수구조 및 그 시공방법", 특허등록 제334602호 "아스팔트 방수시트 및 이를 이용한 복합방수공법", 특허등록 제361582호 "방수단열용 바닥구조 및 시공방법", 특허등록 제362308호 "고무화 아스팔트 시트방수의 연결부 접합 방법 및 파라펫 처리 방법", 특허등록 제666080호 "쿨 루프 아스팔트 방수 시트 및 이의 연결부 접합 구조" 등 많은 기술을 개발하여 특허받았고, 그 이후로도 본 발명자가 경영하는 회사 명의로 특허등록 제785333호 "접합부 수밀성이 향상된 방수 시트재와 루프형 조인트시스템 및 이들을 이용한 복합방수공법", 특허등록 제1214810호 "방수·방근 일체형 시트 및 이를 이용한 방수·방근구조의 시공방법" 등 많은 기술을 개발하여 특허등록은 물론 시공을 해오고 있다.
In order to solve the problems of the waterproofing of the sheet and the waterproofing of the film, the inventor of the present invention has proposed the patent application No. 180632 entitled " Combined waterproof structure and construction method ", patent registration No. 238994 " Patent No. 334602 "Asphalt waterproof sheet and compound waterproofing method using same" Patent No. 361582 "Floor structure and construction method for waterproof insulation" Patent No. 362308 "Connection method of waterproofing of rubberized asphalt sheet Patent No. 666080, "Cool Loop Asphalt Waterproofing Sheet and Its Connection Structure" and many other technologies have been developed and patented since then. Patent No. 785333 entitled " Improved waterproof sheet material and loop type joint system, and complex waterproofing method using them ", Patent Registration No. 1214810" Waterproof / It developed a number of techniques, many banggeun structure construction method "and has been doing for the registration of patents, as well as construction.

하지만, 지금까지의 거의 모든 방수시공 및 구조는 방수 자체에 관한 것이고, 단열을 위해서는 방수와 별도로 단열재를 부설하여 시공하고 있는데, 구체적으로는 슬래브 위에 방수시공을 먼저 하고, 방수층 위에 단열재를 놓고, 단열재 위에 필름을 덮은 다음, 상부에 누름 콘크리트를 타설하여 시공하고 있다. 그런데 필름 상부로 작업자가 작업도구를 들고 걸어다니면서 콘크리트를 타설하다 보면 단열재 위에 덮힌 필름이 찢어지고 파손될 수밖에 없어서, 실제로 필름에 구멍이 뚫리거나 찢어지는 경우가 빈번하게 발생하게 되고 잇으며, 콘크리트 타설시 필름의 파손된 부위를 통해 많은 모르타르용 물이 들어가 단열재를 적시게 될 뿐만 아니라 단열재와 슬래브 사이에 물이 존재하게 되어 실질적인 단열효과는 거의 없어지고, 오히려 이 물이 동절기에 융해 및 동결되면서 팽창과 수축을 반복하게 되어 상부에 있는 누름 콘크리트 표면의 균열 원인으로 작용하게 된다는 문제가 있다.
However, almost all the waterproofing construction and structure to date have been related to the waterproofing itself, and the insulation is installed separately from the waterproofing for insulation. More specifically, the waterproofing work is first performed on the slab, the insulation material is placed on the waterproofing layer, After covering the film with the above, press concrete is put on the upper part. However, when the operator pours concrete while walking with the work tool on the upper part of the film, the film covered by the heat insulating material tends to be torn and broken, so that holes are frequently formed in the film and tearing occurs frequently. A large amount of water for mortar enters through the damaged portion of the film to wet the heat insulating material and water is present between the heat insulating material and the slab so that the thermal insulating effect is substantially eliminated and the water is melted and freezed in the winter season, It causes a problem of cracking of the surface of the pressed concrete on the upper part.

본 발명은 상기와 같은 문제를 해결하기 위하여 안출된 것으로, 본 발명의 목적은, 상하에 위치한 부재가 방수기능을 갖게 하고 상하 부재 사이를 잇으면서 일체로 형성된 격벽이 공간을 형성하고, 공간을 채운 공기층이 단열기능을 갖게 하여 방수시트와 단열재가 일체로 성형된 방수단열시트를 사용함으로써, 방수와 단열 및 결로현상을 동시에 해결할 수 있는 공기층이 형성된 방수단열시트 및 공기층 단열을 이용한 복합·복층·단열방수공법을 제공하기 위한 것이다.
SUMMARY OF THE INVENTION The present invention has been conceived in order to solve the above-mentioned problems, and an object of the present invention is to provide a water- A waterproof thermal insulation sheet in which an air layer has a heat insulating function and an airtight insulation sheet having a waterproof sheet and a heat insulating material integrally molded is used to form an airtight insulation layer capable of simultaneously solving waterproofing, So as to provide a waterproofing method.

상기와 같은 과제 해결을 위해 본 발명에 따른 공기층이 형성된 방수단열시트는, 상부와 하부로 분리되어 있고, 상부와 하부 사이를 잇는 격벽이 일체로 형성되어, 격벽 사이사이가 공기층을 형성하고 있는 본체; 상기 본체의 상면과 하면에 열융착으로 접착된 부직포를 구비하여 구성되는 것을 특징으로 한다.
In order to solve the above-mentioned problems, the waterproof thermal insulation sheet formed with the air layer according to the present invention is divided into an upper part and a lower part, and partition walls connecting the upper part and the lower part are integrally formed, ; And a nonwoven fabric bonded to the upper surface and the lower surface of the body by thermal fusion bonding.

본 발명에 따른 공기층 단열을 이용한 복합·복층·단열방수공법의 일실시예는, 바탕면 전체에 프라이머를 도포하는 단계; 프라이머가 도포된 콘크리트 슬래브 상면에 방수단열시트를 일정 간격으로 맞대서 놓는 단계; 상기 시트가 맞대진 부분의 하면에 일정 폭으로 우레탄을 도포하는 단계; 시트와 시트가 맞대지는 부분의 상면에 일정 폭의 부직포 또는 유리섬유를 접착시키는 단계; 우레탄이 시트와 시트 사이의 간격(틈)과 상기 부직포 또는 유리섬유를 덮도록 부직포 또는 유리섬유 위에 우레탄을 도포하여 조인트 부분을 처리하는 단계를 거쳐서 시공하며, 상기 방수단열시트는, 상부와 하부로 분리되어 있고, 상부와 하부 사이를 잇는 격벽이 일체로 형성되어, 격벽 사이사이가 공기층을 형성하고 있는 본체; 상기 본체의 상면과 하면에 열융착으로 접착된 부직포를 구비하여 구성되는 것을 특징으로 한다.
One embodiment of the composite, multi-layer, and thermal insulation method using air layer insulation according to the present invention comprises: applying a primer to the entire substrate; Placing the waterproof insulating sheet against the upper surface of the concrete slab coated with the primer at regular intervals; Applying urethane to a lower surface of the portion where the sheet is engaged with a predetermined width; Adhering a nonwoven fabric or glass fiber of a certain width to the upper surface of the portion where the sheet and the sheet meet; The urethane is applied through a step of applying a urethane on the nonwoven fabric or the glass fiber to cover the gap between the sheet and the sheet and the nonwoven fabric or the glass fiber to treat the joint portion, A main body in which partition walls which are separated from each other and which connect the upper part and the lower part are integrally formed and the spaces between the partition walls form an air layer; And a nonwoven fabric bonded to the upper surface and the lower surface of the body by thermal fusion bonding.

본 발명에 따른 공기층 단열을 이용한 복합·복층·단열방수공법의 다른 실시예는, 바탕면 전체에 프라이머를 도포하는 단계; 상기 프라이머층 상부 전체에 우레탄 또는 수용성 고무화아스팔트를 도포하여 방수층을 형성하는 단계; 상기 우레탄 또는 수용성 고무화아스팔트가 도포된 방수층 상부에 방수단열시트를 일정 간격으로 맞대서 접착시키는 단계; 시트와 시트가 맞대지는 부분의 상면에 일정 폭의 부직포 또는 유리섬유를 접착시키는 단계; 우레탄이 시트와 시트 사이의 간격(틈)과 상기 부직포 또는 유리섬유를 덮도록 부직포 또는 유리섬유 위에 우레탄을 도포하여 조인트 부분을 처리하는 단계; 상기 방수단열시트가 깔아진 면 전체에 우레탄을 도포하여 도막방수층을 형성하는 단계를 거쳐서 시공하며, 상기 방수단열시트는, 상부와 하부로 분리되어 있고, 상부와 하부 사이를 잇는 격벽이 일체로 형성되어 격벽 사이사이가 공기층을 형성하며, PP, PE, PVC, PET 중 어느 하나의 재질로 제작된 본체; 상기 본체의 상면과 하면에 열융착으로 접착된 부직포를 구비하여 구성되는 것을 특징으로 한다.
Another embodiment of the composite, multi-layer, and thermal insulation method using the air layer insulation according to the present invention includes: applying a primer to the entire substrate; Forming a waterproof layer by applying urethane or water-soluble rubberized asphalt to the entire upper surface of the primer layer; Adhering the waterproof insulation sheet to the upper part of the waterproof layer coated with the urethane or water-soluble rubberized asphalt at regular intervals; Adhering a nonwoven fabric or glass fiber of a certain width to the upper surface of the portion where the sheet and the sheet meet; Treating the joint portion by applying urethane on the nonwoven fabric or the glass fiber to cover the gap (gap) between the urethane sheet and the sheet and the nonwoven fabric or the glass fiber; The waterproof and heat insulating sheet is divided into an upper portion and a lower portion, and a partition wall connecting the upper portion and the lower portion is integrally formed A body formed of any one material of PP, PE, PVC and PET to form an air layer between the barrier ribs; And a nonwoven fabric bonded to the upper surface and the lower surface of the body by thermal fusion bonding.

삭제delete

상기와 같은 특징을 갖는 본 발명에 따른 공기층이 형성된 방수단열시트는 PP, PE, PVC, PET 등과 같은 플라스틱류로 된 상하에 위치한 판상(板狀)의 부재가 방수기능을 갖게 되고, 상하층 사이를 잇는 격벽을 일체로 형성하여 생긴 공간은 단면(斷面)이 사각형(□, 田), 육각형(honeycomb) 등 다양한 형상으로 형성되면서 공간이 공기층을 형성하여 단열 및 차음기능을 갖게 되므로, 방수시트와 단열재가 일체로 성형되어 방수와 단열 뿐만 아니라 차음문제를 동시에 해결할 수 있다.
The waterproof and heat-insulating sheet having the air layer according to the present invention having the above-described features has a function of waterproofing the upper and lower plate members made of plastics such as PP, PE, PVC, PET and the like, The space formed by integrally forming the partition walls connecting the partition walls is formed into various shapes such as a rectangular shape (square), a hexagonal shape (honeycomb), and the space forms an air layer, And the heat insulating material are integrally formed, so that it is possible to solve not only the waterproofing and the insulation but also the sound insulation problem at the same time.

또한 상기와 같은 방수단열시트를 이용하는 본 발명에 따른 공기층 단열을 이용한 복합·복층·단열방수공법은, 지금까지 방수시트와 단열재를 별도로 시공하던 것을 한번의 시공으로 끝낼 수 있을 뿐만 아니라 중간에 공기층이 형성되어 있으므로 결로현상 및 아음문제를 근원적으로 방지할 수 있다.
In addition, the composite, multi-layer, and thermal insulation method using the above-described waterproof and heat-insulating sheet according to the present invention can finish the construction of the waterproof sheet and the heat insulation material by one time, It is possible to fundamentally prevent the condensation phenomenon and the sublimation problem.

도 1은 본 발명에 따른 단열방수시트의 여러 실시예를 도시한 도면이다.
도 2는 본 발명에 따른 복합·복층·단열방수공법의 제1실시예를 도시한 도면이다.
도 3은 본 발명에 따른 복합·복층·단열방수공법의 제2실시예를 도시한 도면이다.
도 4는 본 발명에 따른 복합·복층·단열방수공법의 제3실시예를 도시한 도면이다.
1 is a view showing various embodiments of the heat insulating waterproof sheet according to the present invention.
FIG. 2 is a view showing a first embodiment of the composite multi-layer waterproofing method according to the present invention.
3 is a view showing a second embodiment of the composite multi-layer waterproofing method according to the present invention.
FIG. 4 is a view showing a third embodiment of the composite, multilayer, and adiabatic waterproofing method according to the present invention.

본 발명에 따른 공기층이 형성된 방수단열시트 및 공기층 단열을 이용한 복합·복층·단열방수공법의 가장 큰 기술적 특징은, 상하에 위치한 판상(板狀)의 부재가 방수기능을 갖게 하고, 상하층 사이를 잇는 격벽 사이의 공간에 차있는 공기에 의해 형성된 공기층이 단열기능을 갖게 하여, 방수시트와 단열재가 하나의 시트에 일체로 형성되게 함으로써, 한번의 시공으로 방수와 단열 및 결로현상을 동시에 해결할 수 있게 했다는 점이다.
The most significant technical feature of the waterproof thermal insulation sheet with the air layer according to the present invention and the composite, multi-layer, and thermal insulation method using the air layer insulation is that the plate members located on the upper and lower sides have a waterproof function, The air layer formed by the air present in the space between the partition walls is provided with a heat insulating function and the waterproof sheet and the heat insulating material are integrally formed in one sheet so that the waterproofing, .

본 발명에 따른 방수단열시트(10)는 방수기능과 공기층에 의한 단열기능을 동시에 구비하게 되는데, 방수단열시트(10)는, 판상(板狀)의 부재가 상부와 하부로 분리되어 있고, 상부와 하부 사이를 잇는 격벽이 일체로 형성되어, 격벽 사이사이에 채워진 공기가 공기층(12)을 형성하고 있는 본체(11)와, 본체(11)의 상면과 하면에 열융착으로 접착된 부직포(13)를 구비하여 구성된 것이다.
The waterproof and heat insulating sheet 10 according to the present invention is provided with a waterproof function and a heat insulating function by an air layer. The waterproof and heat insulating sheet 10 has a plate-shaped member separated into an upper part and a lower part, And an air layer 12 formed between the partition walls to form an air layer 12. The nonwoven fabric 13 bonded to the lower surface of the upper surface of the main body 11 by heat fusion ).

본체(11)의 재질은 PP, PE, PVC, PET 등과 같은 플라스틱류이면 어느 것이나 상관없으며, 상부와 하부층 사를 잇는는 격벽을 일체로 형성하여 격벽에 의해 단면(斷面)이 사각형(□, 田), 육각형(honeycomb) 등 다양한 형상으로 공간을 형성하면, 공간에 공기가 채워지면서 공기층이 단열기능을 갖게 될 뿐만 아니라 시공후 결로현상 및 차음문제를 근원적으로 방지 및 해결해 준다.
The main body 11 may be made of any plastic material such as PP, PE, PVC, PET, etc., and a partition wall for connecting the upper and lower layers may be integrally formed. The partition wall may have a rectangular cross- ), Hexagonal (honeycomb), etc., the space is filled with air so that the air layer not only has a heat insulating function, but also prevents and resolves the problem of condensation and sound insulation after construction.

또한, 본체(11)의 상면과 하면에는 부직포(13)가 열융착되어 접착되어 있기 때문에 방수단열시트(10)를 접착제 또는 방수층이 형성된 슬래브의 바닥면에 접착시킨다거나, 시트 사이의 조인트 부위에 우레탄 등으로 아이조인트(I-joint)를 형성한다든가, 또는 시트의 상면에 도막방수층을 형성할 때 시트와 도막제가 잘 접착되게 된다.
Since the nonwoven fabric 13 is bonded to the upper surface and the lower surface of the main body 11 by thermal fusion, the waterproof thermal insulation sheet 10 is bonded to the bottom surface of the slab on which the adhesive or waterproof layer is formed, The sheet and the coating film are adhered well when an eye joint (I-joint) is formed with urethane or the like, or when a waterproof layer is formed on the top surface of the sheet.

본 발명에 따른 공기층 단열을 이용한 복합·복층·단열방수공법은 지금까지 설명한 공기층이 형성된 방수단열시트(10)를 사용하여 시공한다.
In the composite, multi-layer, and thermal insulation method using the air layer insulation according to the present invention, the waterproof insulation sheet 10 having the air layer formed as described above is used.

도 2를 참조하여 복합·복층·단열방수공법의 제1실시예에 대하여 설명하면, 바탕면 전체에 프라이머를 도포하는 단계; 프라이머가 도포된 콘크리트 슬래브 상면에 방수단열시트(10)를 일정 간격으로 맞대서 놓는 단계; 상기 길이방향을 따라 시트의 단부를 들어올리고 시트가 맞대진 부분의 하면에 일정 폭으로 우레탄을 도포하는 단계; 들어올린 시트를 다시 내려서 슬래브 상면에 도포된 우레탄에 시트가 접착되고 나면, 시트와 시트가 맞대지는 부분의 상면에 일정 폭의 부직포 또는 유리섬유(21)를 접착시키는 단계; 우레탄이 시트와 시트 사이의 간격(틈)과 상기 부직포 또는 유리섬유를 덮도록 부직포 또는 유리섬유(21) 위에 우레탄을 도포하여 조인트 부분(20)의 단면(斷面)이 I자 형태가 되도록 조인트 부분(20)을 처리하는 단계를 거쳐서 시공한다. 물론 방수단열시트(10)를 바닥면에 접착시킬 때는 시트의 양단이 슬래브의 상부에 도포된 우레탄에 접착되도록 시공해야 한다.
Referring to FIG. 2, the first embodiment of the composite multi-layer waterproofing method will be described. Placing the waterproof insulating sheet 10 on the upper surface of the concrete slab coated with the primer at regular intervals; A step of lifting an end portion of the sheet along the longitudinal direction and applying a urethane to the lower surface of the portion where the sheet is engaged with a predetermined width; After the lifted sheet is lowered again, the sheet is adhered to the urethane coated on the upper surface of the slab, thereby adhering a nonwoven fabric or glass fiber (21) having a certain width to the upper surface of the portion where the sheet and the sheet meet; Urethane is applied on the nonwoven fabric or the glass fiber 21 so as to cover the gap (gap) between the sheet and the sheet and the nonwoven fabric or the glass fiber so that the cross section of the joint portion 20 forms an I- (20). Of course, when the waterproof and heat-insulating sheet 10 is adhered to the floor, both ends of the sheet must be adhered to the urethane coated on the upper part of the slab.

도 3을 참조하여 복합·복층·단열방수공법의 제2실시예에 대하여 설명하면, 바탕면 전체에 프라이머를 도포하는 단계; 상기 프라이머층 상부에 우레탄 또는 수용성 고무화아스팔트를 도포하여 방수층(30)을 형성하는 단계; 상기 우레탄 또는 수용성 고무화아스팔트가 도포된 방수층 상부에 방수단열시트(10)를 일정 간격으로 맞대서 접착시키는 단계; 시트와 시트가 맞대지는 부분의 상면에 일정 폭의 부직포 또는 유리섬유(21)를 접착시키는 단계; 우레탄이 시트와 시트 사이의 간격(틈)과 상기 부직포 또는 유리섬유를 덮도록 부직포 또는 유리섬유 위에 우레탄을 도포하여 조인트 부분(20)을 처리하는 단계를 거쳐서 시공한다.
Referring to FIG. 3, the second embodiment of the composite, multi-layer, and heat insulating waterproofing method will be described. Forming a waterproof layer (30) by applying urethane or water-soluble rubberized asphalt on the primer layer; Adhering the waterproof insulation sheet 10 to the upper part of the waterproof layer coated with the urethane or the water-soluble rubberized asphalt at regular intervals; Adhering a nonwoven fabric or glass fiber (21) having a certain width to an upper surface of a portion where the sheet and the sheet abut against each other; The urethane is applied on the nonwoven fabric or the glass fiber to cover the gap (gap) between the sheet and the sheet and the nonwoven fabric or the glass fiber to treat the joint portion 20.

본 발명에 따른 복합·복층·단열방수공법의 제3실시예는, 제2실시예에서 시트의 상면 전체에 걸쳐 도막방수층(30')을 형성하는 공법인데, 방수단열시트(10)가 맞대지는 부분 상부에 일정 폭으로 우레탄을 도포하는 단계 후에 방수단열시트(10)가 깔아진 면 전체에 우레탄을 도포하여 도막방수층(30')을 형성하는 단계를 더 거치는 공법이다.
The third embodiment of the composite multi-layer waterproofing method according to the present invention is a method of forming a waterproof film layer 30 'over the entire upper surface of the sheet in the second embodiment, A step of applying urethane to the entire surface on which the waterproof thermal insulating sheet 10 is formed to form the coating film waterproof layer 30 'after the step of applying the urethane at a predetermined width to the upper portion.

이상의 설명은 본 발명을 예시적으로 설명한 것이고, 명세서에 게시된 실시예는 본 발명의 기술사상을 한정하기 위한 것이 아니라 설명하기 위한 것이므로 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자라면 본 발명의 기술사상을 벗어나지 않는 범위에서 다양한 수정 및 변형이 가능할 것이다. 그러므로 본 발명의 보호범위는 청구범위에 기재된 사항에 의해 해석되고, 그와 균등한 범위 내에 있는 기술적 사항도 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.
It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit or scope of the present invention. Various modifications and variations will be possible without departing from the spirit of the invention. Therefore, the scope of the present invention should be construed as being covered by the scope of the appended claims, and technical scope within the scope of equivalents thereof should be construed as being included in the scope of the present invention.

10 : 방수단열시트
20 : 조인트 부분
21 : 부직포(또는 유리섬유)
30, 30' 도막방수층
10: Waterproof insulation sheet
20: joint part
21: nonwoven fabric (or glass fiber)
30, 30 'Thick film waterproof layer

Claims (5)

삭제delete 삭제delete 삭제delete 바탕면 전체에 프라이머를 도포하는 단계;
상기 프라이머층 상부 전체에 우레탄 또는 수용성 고무화아스팔트를 도포하여 방수층을 형성하는 단계;
상기 우레탄 또는 수용성 고무화아스팔트가 도포된 방수층 상부에 방수단열시트를 일정 간격으로 맞대서 접착시키는 단계;
시트와 시트가 맞대지는 부분의 상면에 일정 폭의 부직포 또는 유리섬유를 접착시키는 단계;
우레탄이 시트와 시트 사이의 간격(틈)과 상기 부직포 또는 유리섬유를 덮도록 부직포 또는 유리섬유 위에 우레탄을 도포하여 조인트 부분을 처리하는 단계;
상기 방수단열시트가 깔아진 면 전체에 우레탄을 도포하여 도막방수층을 형성하는 단계;
를 거쳐서 시공하며, 상기 방수단열시트는,
상부와 하부로 분리되어 있고, 상부와 하부 사이를 잇는 격벽이 일체로 형성되어 격벽 사이사이가 공기층을 형성하며, PP, PE, PVC, PET 중 어느 하나의 재질로 제작된 본체;
상기 본체의 상면과 하면에 열융착으로 접착된 부직포;
를 구비하여 구성되는 것을 특징으로 하는 공기층 단열을 이용한 복합·복층·단열방수공법.
Applying a primer to the entire substrate;
Forming a waterproof layer by applying urethane or water-soluble rubberized asphalt to the entire upper surface of the primer layer;
Adhering the waterproof insulation sheet to the upper part of the waterproof layer coated with the urethane or water-soluble rubberized asphalt at regular intervals;
Adhering a nonwoven fabric or glass fiber of a certain width to the upper surface of the portion where the sheet and the sheet meet;
Treating the joint portion by applying urethane on the nonwoven fabric or the glass fiber to cover the gap (gap) between the urethane sheet and the sheet and the nonwoven fabric or the glass fiber;
Applying urethane to the entire surface of the waterproofing and heat insulating sheet to form a waterproof coating layer;
Wherein the waterproofing and heat-insulating sheet is made of a water-
A main body made of any one of PP, PE, PVC, and PET, wherein the partition wall is divided into an upper portion and a lower portion and a partition wall is formed between the upper portion and the lower portion so as to form an air layer therebetween.
A nonwoven fabric bonded to the upper surface and the lower surface of the body by thermal fusion;
The method of claim 1, further comprising:
삭제delete
KR1020130047248A 2013-04-29 2013-04-29 Constructing method of multi layer air insulation waterproofing system KR101459289B1 (en)