KR20090025453A - The manufacturing method for metal decoration using master - Google Patents

The manufacturing method for metal decoration using master Download PDF

Info

Publication number
KR20090025453A
KR20090025453A KR1020070090317A KR20070090317A KR20090025453A KR 20090025453 A KR20090025453 A KR 20090025453A KR 1020070090317 A KR1020070090317 A KR 1020070090317A KR 20070090317 A KR20070090317 A KR 20070090317A KR 20090025453 A KR20090025453 A KR 20090025453A
Authority
KR
South Korea
Prior art keywords
master
copper
plating
corrosion
plated
Prior art date
Application number
KR1020070090317A
Other languages
Korean (ko)
Other versions
KR100901795B1 (en
Inventor
이우찬
Original Assignee
주식회사 엠.지.피
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 엠.지.피 filed Critical 주식회사 엠.지.피
Priority to KR1020070090317A priority Critical patent/KR100901795B1/en
Publication of KR20090025453A publication Critical patent/KR20090025453A/en
Application granted granted Critical
Publication of KR100901795B1 publication Critical patent/KR100901795B1/en

Abstract

A method for manufacturing a metal decoration product using a master is provided to improve quality of a plated product in a state corrosion resistance coating is not exfoliated from the master. A method for manufacturing a metal decoration product using a master comprises the following steps of: coating a corrosion resistance material on an upper part of the master for manufacturing the metal decoration product(S210a); coating Cu on the upper part of the master(S210b); coating the corrosion resistance material on a Cu coated plate(S210c); exfoliating the Cu coated plated from the master(S220); drying the exfoliated Cu coated plate(S230); and performing a punching process to produce a product from the dried plate(S240).

Description

마스터를 이용한 금속장식물 제조방법{The manufacturing method for metal decoration using master}The manufacturing method for metal decoration using master}

본 발명은 마스터를 이용한 금속장식물 제조방법에 관한 것으로, 보다 상세하게는 휴대단말기의 메탈키패드나 LCD액정의 둘레부를 감싸는 메탈윈도우, 케이스, 로그 등의 금속장식물 및/또는 다양한 패턴의 문양부에 대한 제품을 생산하기 위한 제조과정 중 마스터로부터 분리된 동(Cu)도금판으로부터 프레스를 통해 펀칭된 제품의 내식성도금을 위해 수작업으로 행거에 결착시키는 종래의 락킹작업을 제거함과 동시에 상기 동(Cu)도금판 제품의 내식성 도금을 마스터로부터 박리시키기 않은 상태에서 이루어지도록 구성함으로써, 상기한 종래 금속장식물의 제조방법에 비해 상기 제품에 대한 제조공정을 단축시킬 수 있음과 아울러 이에 대한 제품의 생산성을 향상시킬 수 있으며, 특히 상기 동(Cu)도금판 제품에 대한 내식성 도금이 마스터로부터 박리시키지 않은 상태에서 이루어지기 때문에 수작업을 통해 펀칭된 제품을 행거에 결착시켜 내식성 도금을 실행하였던 종래에 비해 도금된 제품의 품질 역시 향상시킬 수 있도록 한 마스터를 이용한 금속장식물 제조방법에 관한 것이다.The present invention relates to a method for manufacturing a metal ornament using a master, and more particularly, to a metal ornament such as a metal window, a case, a log, and / or a pattern of various patterns that surround a metal keypad of a portable terminal or an LCD liquid crystal. The copper plating at the same time as removing the conventional locking operation by manually binding to the hanger for the corrosion resistance plating of the product punched through the press from the copper plating plate separated from the master during the manufacturing process to produce the product By configuring the corrosion-resistant plating of the plate product in a state in which it is not peeled off from the master, it is possible to shorten the manufacturing process for the product as compared to the manufacturing method of the conventional metal ornaments as well as to improve the productivity of the product. In particular, when the corrosion-resistant plating on the copper plated product is peeled from the master The present invention relates to a method of manufacturing a metal ornament using a master to improve the quality of the plated product compared to the conventional practice of performing corrosion-resistant plating by binding the punched product to a hanger because it is made in a non-key state.

일반적으로, 휴대단말기의 메탈키패드나 LCD액정의 둘레부를 감싸는 메탈윈도우 등의 금속장식물을 제조하기 위한 방법으로서 전주도금(Electro Forming)방식이나 메탈스티커(Metal Sticker)제조 방식 등이 사용되고 있다.In general, as a method for manufacturing a metal decoration such as a metal keypad of a mobile terminal or a metal window surrounding the LCD liquid crystal, an electroforming method or a metal sticker manufacturing method is used.

이와 같은 금속장식물의 제조방법 중 상기 전주도금방식의 경우 도 1에 도시한 바와 같이 표면에 음각 또는 양각으로 다양한 패턴의 문양부가 형성된 장식물 제조용 마스터를 마련하는 단계(S100)와; 상기 장식물 제조용 마스터의 상단에 동(Cu)도금을 하는 단계(S110)와; 상기 마스터로부터 동(Cu)도금판을 박리시키는 단계(S120)와; 상기 박리된 동(Cu)도금판을 건조하는 단계(S130)와; 상기 건조된 동(Cu)도금판으로부터 제품 생산을 위한 프레스의 펀칭작업이 이루어지는 단계(S140)와; 상기 펀칭된 제품을 수작업으로 행거에 락킹시키는 단계(S150)와; 상기 행거에 락킹된 제품에 부식 방지를 위한 내식성 도금을 하는 단계(S160); 및 제품 생산 단계(S170)로 이루어져 있다.In the method of manufacturing the metal ornaments such as the pre-plated plating method as shown in Figure 1 providing a master for the decoration of the decorative pattern is formed in the pattern of the intaglio or embossed on the surface (S100); Copper plating (Cu) on the upper end of the decoration manufacturing master (S110); Peeling a copper (Cu) plated plate from the master (S120); Drying the peeled copper (Cu) plated plate (S130); A step (S140) of punching a press for producing a product from the dried copper (Cu) plated plate; Manually locking the punched product on a hanger (S150); Performing corrosion-resistant plating on the product locked to the hanger to prevent corrosion (S160); And it consists of a product production step (S170).

이 때, 상기 장식물 제조용 마스터의 상단에 직접 도금되는 동(Cu)도금의 경우 장식물 제조용 마스터의 상단에 도금 시 밀착성을 위한 1차 피로인산 동도금이 이루어지고, 그 상단에 내식성을 위한 2차 유산 동도금이 이루어지면서 제품화를 위한 동(Cu)도금판을 형성하게 된다.At this time, in the case of copper plating directly plated on the upper end of the decorative production master, primary pyrophosphate copper plating is performed for adhesion when plating on the upper end of the decorative production master, and the secondary lactic acid copper plating on the upper end for corrosion resistance. This is done to form a copper (Cu) plated plate for commercialization.

또한, 상기 행거에 락킹된 제품의 부식을 방지하기 위해 이루어지는 내식성 도금의 경우 파라듐(Pd)에 의한 1차 내식성 도금(S160a)이 이루어지고, 제품의 표면 색체 처리 효과를 향상시키기 위해 크롬(Cr)이나 니켈(Ni)에 의한 2차 내식성 도금(S160b)이 이루어지게 되는데, 이 때 상기 2차 내식성 도금을 크롬(Cr)으로 할 경우 상기 2차 내식성 도금부가 흰색을 띄게 된다.In addition, in the case of corrosion-resistant plating to prevent corrosion of the product locked to the hanger, the primary corrosion-resistant plating (S160a) is performed by palladium (Pd), and chromium (Cr) to improve the surface color treatment effect of the product. ) Or a secondary corrosion resistant plating (S160b) by nickel (Ni) is made, and when the secondary corrosion resistant plating is chromium (Cr), the secondary corrosion resistant plating becomes white.

그러나, 상기와 같은 전주도금방식의 경우 마스터에 200㎛ㅁ50㎛정도 동(Cu)을 도금하여 동(Cu)도금층을 형성한 후 마스터로부터 상기 동(Cu)도금층을 박리시켜 프레스의 펀칭공정을 통해 동(Cu)도금층으로부터 제품화되는 휴대단말기의 메탈키패드나 LCD액정의 둘레부를 감싸는 메탈윈도우 등의 금속장식물이나 다양한 패턴의 문양부를 천공한 다음 상기와 같이 천공된 금속장식물이나 다양한 패턴의 문양부에 대한 부식 방지를 위해 내식성 도금을 행할 수 있도록 상기 금속장식물이나 다양한 패턴의 문양부를 작업자가 일일이 수작업으로 행거에 결착시키는 락킹작업을 수행해야 하는 등의 번거로운 문제점과 아울러 이를 통한 제조공정의 작업시간이 오래 걸리게 되는 등의 커다란 문제점이 있었다.However, in the case of the above electroplating method, a copper plating layer is formed by plating copper (Cu) on the master about 200 μm ㅁ 50 μm, and then the punching process is performed by peeling the copper plating layer from the master. Through the metal decorative material such as metal keypad of the mobile terminal produced from the copper plating layer or the metal window surrounding the LCD liquid crystal, or the pattern of various patterns, and then the perforated metal decoration or the pattern of various patterns In order to prevent corrosion, the cumbersome problems such as the need for the worker to manually bind the hanger to the hanger by hand to the metal decoration or the pattern of various patterns, and also the long working time through the manufacturing process There was a big problem such as getting caught.

또한, 상기와 같이 프레스에 의해 펀칭된 제품에 대한 부식 방지를 위하여 상기 행거에 락킹된 제품들에 대한 내식성 도금을 실행할 경우 도포되는 내식성 도금소재의 분출압력에 의해 행거에 락킹된 제품들이 유동하거나 또는 작업자에 의한 내식성 도금을 균일하게 한다 하더라도 어느 한쪽의 제품들쪽으로 내식성 도금이 쏠리게 되어 상기 제품에 대한 내식성 도금이 균일하게 이루어지지 않게 되는 문제점과 아울러, 이를 통한 제품의 품질 역시 크게 저하되게 되는 등의 문제점도 있었다.In addition, in order to prevent corrosion of the products punched by the press as described above, when the corrosion-resistant plating on the products locked to the hanger is carried out by the ejecting pressure of the corrosion-resistant plating material applied to the hanger flows or Even if the corrosion-resistant plating by the operator is uniform, the corrosion-resistant plating is directed toward any one of the products, and the corrosion-resistant plating on the product is not uniformly performed, and the quality of the product is also greatly reduced. There was a problem.

상기와 같은 종래의 문제점을 해소하기 위하여 안출된 본 발명은, 휴대단말 기의 메탈키패드나 LCD액정의 둘레부를 감싸는 메탈윈도우, 케이스, 로그 등의 금속장식물 및/또는 다양한 패턴의 문양부에 대한 제품을 생산하기 위한 제조과정 중 마스터로부터 분리된 동(Cu)도금판으로부터 프레스를 통해 펀칭된 제품의 내식성도금을 위해 수작업으로 행거에 결착시키는 종래의 락킹작업을 제거함과 동시에 상기 동(Cu)도금판 제품의 내식성 도금을 마스터로부터 박리시키기 않은 상태에서 이루어지도록 구성함으로써, 상기한 종래 금속장식물의 제조방법에 비해 상기 제품에 대한 제조공정 및 작업시간을 단축시킬 수 있음과 아울러 이에 대한 제품의 생산성을 향상시킬 수 있도록 하는데 그 목적이 있다.The present invention has been made in order to solve the above-mentioned conventional problems, the product for metal ornaments and / or patterns of various patterns, such as metal windows, cases, logs surrounding the metal keypad of the mobile terminal or LCD liquid crystal The copper plated plate was removed from the copper plated plate separated from the master during the manufacturing process to remove the conventional locking work manually binding to the hanger for corrosion resistance of the product punched through the press. By constructing the corrosion-resistant plating of the product in a state in which it is not peeled from the master, it is possible to shorten the manufacturing process and working time for the product as well as to improve the productivity of the product compared to the conventional method of manufacturing a metal ornament. The purpose is to make it possible.

또한, 본 발명의 경우 상기와 같이 동(Cu)도금판 제품에 대한 내식성 도금이 마스터로부터 박리시키지 않은 상태에서 동(Cu)도금과 함께 이루어지기 때문에 수작업을 통해 펀칭된 제품을 행거에 결착시켜 내식성 도금을 실행하였던 종래에 비해 도금된 제품의 품질 역시 향상시킬 수 있도록 하는데 또 다른 목적이 있다.In addition, in the case of the present invention, since the corrosion-resistant plating on the copper plated product as described above is made together with the copper plating without peeling from the master, the product punched through manual work is bound to the hanger for corrosion resistance. Another object of the present invention is to improve the quality of plated products as compared with the conventional plating.

본 발명의 마스터를 이용한 금속장식물 제조방법은, 표면에 음각 또는 양각으로 다양한 패턴의 문양부가 형성된 장식물 제조용 마스터의 상단에 1차 내식성 도금을 하는 단계와;Method of manufacturing a metal ornament using the master of the present invention, the first corrosion-resistant plating on the top of the master for manufacturing a decorative pattern is formed in the pattern of the intaglio or embossed on the surface;

상기 1차 내식성 도금된 마스터의 상단에 동(Cu)도금을 하는 단계와;Copper (Cu) plating the upper end of the primary corrosion-resistant plated master;

상기 동(Cu)도금판의 상단에 2차 내식성 도금을 하는 단계와;Performing secondary corrosion resistant plating on an upper end of the copper (Cu) plated plate;

상기 1,2차 내식성 도금된 동(Cu)도금판을 마스터로부터 박리시키는 단계와;Peeling the first and second corrosion resistant plated copper (Cu) plated plates from the master;

상기 박리된 동(Cu)도금판을 건조하는 단계; 및Drying the peeled copper (Cu) plated plate; And

상기 건조된 동(Cu)도금판으로부터 제품 생산을 위한 프레스의 펀칭작업이 이루어지는 단계를 포함하여 이루어진 것을 특징으로 한다.It characterized in that it comprises a step of punching the press for producing a product from the dried copper (Cu) plated sheet.

본 발명의 마스터를 이용한 금속장식물 제조방법은, 휴대단말기의 메탈키패드나 LCD액정의 둘레부를 감싸는 메탈윈도우, 케이스, 로그 등의 금속장식물 및/또는 다양한 패턴의 문양부에 대한 제품을 생산하기 위한 제조과정 중 마스터로부터 분리된 동(Cu)도금판으로부터 프레스를 통해 펀칭된 제품의 내식성도금을 위해 수작업으로 행거에 결착시키는 종래의 락킹작업을 제거함과 동시에 상기 동(Cu)도금판 제품의 내식성 도금을 마스터로부터 박리시키기 않은 상태에서 이루어지도록 구성함으로써, 상기한 종래 금속장식물의 제조방법에 비해 상기 제품에 대한 제조공정 및 작업시간을 단축시킬 수 있음과 아울러 이에 대한 제품의 생산성을 향상시킬 수 있는 등의 탁월한 효과가 있다.Method of manufacturing a metal ornament using the master of the present invention, the production for producing a product for metal ornaments and / or patterns of various patterns, such as metal windows, cases, logs surrounding the metal keypad of the mobile terminal or LCD liquid crystal The corrosion-resistant plating of the copper plated product is eliminated while eliminating the conventional locking operation of manually binding the hanger for the corrosion-resistant plating of the product punched through the press from the copper plated plate separated from the master during the process. By being configured so as not to be peeled from the master, it is possible to shorten the manufacturing process and work time for the product compared to the conventional method of manufacturing the metal ornaments as well as to improve the productivity of the product, etc. Excellent effect

또한, 본 발명의 경우 상기와 같이 동(Cu)도금판 제품에 대한 내식성 도금이 마스터로부터 박리시키지 않은 상태에서 동(Cu)도금과 함께 이루어지기 때문에 수작업을 통해 펀칭된 제품을 행거에 결착시켜 내식성 도금을 실행하였던 종래에 비해 도금된 제품의 품질 역시 향상시킬 수 있는 등의 효과 역시 있다.In addition, in the case of the present invention, since the corrosion-resistant plating on the copper plated product as described above is made together with the copper plating without peeling from the master, the product punched through manual work is bound to the hanger for corrosion resistance. Compared with the conventional plating, the quality of the plated product can also be improved.

본 발명의 마스터를 이용한 금속장식물 제조방법을 도면과 대비하여 상세히 설명한다.The metal decoration method using the master of the present invention will be described in detail in comparison with the drawings.

도 2는 본 발명의 마스터를 이용한 금속장식물 도금과정을 개략적으로 나타 낸 공정도이고, 도 3은 도 2에 도시된 본 발명의 도금과정을 통해 제작된 금속장식물의 단면도를 나타낸 것이다.2 is a process diagram schematically showing a metal decoration plating process using the master of the present invention, Figure 3 shows a cross-sectional view of the metal decoration produced through the plating process of the present invention shown in FIG.

본 발명의 마스터를 이용한 금속장식물 제조방법은, 도 2에 도시한 바와 같이 표면에 음각 또는 양각으로 다양한 패턴의 문양부(12)가 형성된 장식물 제조용 마스터(10)의 상단에 1차 내식성 도금을 하는 단계(S210a)와; 상기 1차 내식성 도금된 마스터(10)의 상단에 동(Cu)도금을 하는 단계(S210b)와; 상기 동(Cu)도금판(30)의 상단에 2차 내식성 도금을 하는 단계(S210c)와; 상기 1,2차 내식성 도금된 동(Cu)도금판(30)을 마스터(10)로부터 박리시키는 단계(S220)와; 상기 박리된 동(Cu)도금판(30)을 건조하는 단계(S230); 및 상기 건조된 동(Cu)도금판(30)으로부터 제품 생산을 위한 프레스의 펀칭작업이 이루어지는 단계(S240)를 포함하여 이루어져 있다.In the method of manufacturing a metal ornament using the master of the present invention, as shown in FIG. 2, the first corrosion-resistant plating is performed on the upper end of the master for manufacturing ornaments 10 having the patterns 12 having various patterns in an intaglio or embossed surface. Step S210a; Copper plating (Cu) the upper end of the primary corrosion resistant plated master 10 (S210b); Performing a second corrosion resistant plating on an upper end of the copper (Cu) plated plate (S210c); Peeling the first and second corrosion-resistant plated copper (Cu) plated plates 30 from the master 10 (S220); Drying the peeled copper (Cu) plated plate (30) (S230); And a punching operation of a press for producing a product from the dried copper (Cu) plated plate 30 (S240).

여기서, 상기 1차 내식성 도금은 마스터(10)의 상단에 도금되는 동(Cu)도금의 하단부에 대한 부식을 방지하기 위한 파라듐(Pd)이나 삼원(주석(Sn),아연(Zn),동(Cu))합금에 의해 도금이 이루어진다.Here, the primary corrosion-resistant plating is palladium (Pd) or ternary (tin (Sn), zinc (Zn), copper to prevent corrosion to the lower end of the copper (Cu) plating to be plated on the top of the master 10) (Cu)) Plating is performed by alloy.

또한, 상기 2차 내식성 도금은 동(Cu)도금의 상단부에 대한 부식 방지 및 제품의 표면 색체 처리 효과를 향상시키기 위한 크롬(Cr)이나 니켈(Ni)로 도금이 이루어지되, 바람직하게는 크롬(Cr)에 의해 2차 내식성 도금이 이루어진다.In addition, the secondary corrosion-resistant plating is made of chromium (Cr) or nickel (Ni) to prevent the corrosion of the upper end of the copper (Cu) plating and improve the surface color treatment effect of the product, preferably chromium ( Secondary corrosion resistant plating).

이와 같이 구성된 본 발명의 마스터(10)를 이용한 금속장식물 제조방법에 대한 실시예를 도면과 대비하여 상세하게 설명하면 다음과 같다.When explaining the embodiment of the metal ornament manufacturing method using the master 10 of the present invention configured as described above in detail with reference to the drawings.

<실시예><Example>

먼저, 휴대단말기의 메탈키패드나 LCD액정의 둘레부를 감싸는 메탈윈도우, 케이스, 로그 등의 금속장식물(12) 및/또는 다양한 패턴의 문양부(12)가 표면에 음각 또는 양각으로 형성됨과 동시에 니켈(Ni) 또는 동(Cu) 재질로 이루어지면서 하단 및 테두리부분에 마스킹테이프(14) 처리된 장식물 제조용 마스터(10)를 준비(S200)한 다음 상기와 같이 표면에 음각 또는 양각으로 금속장식물(12)의 형상이나 다양한 패턴의 문양부(12)가 형성된 장식물 제조용 마스터(10)의 상단에 제품화되는 동(Cu)도금판(30)의 하단 부식을 방지하기 위하여 1차 내식성 도금(S210a)을 수행하게 되는데, 이 때 상기 1차 내식성 도금은 파라듐(Pd)을 이용해 도금이 이루어지며, 상기 파라듐(Pd) 대신 삼원(주석(Sn),아연(Zn),동(Cu))합금에 의해 도금이 이루어질 수도 있음을 미리 밝혀둔다.First, metal ornaments 12 such as a metal window, a case, a log, and / or a pattern 12 having various patterns and / or engraved portions are formed on the surface of the metal keypad of the mobile terminal or the LCD liquid crystal, and the nickel ( Made of Ni) or copper (Cu) to prepare a master (10) for manufacturing a decorative material treated with a masking tape (14) at the bottom and the rim portion (S200) and the metal ornament (12) in an intaglio or embossed surface as described above In order to prevent corrosion of the lower end of the copper (Cu) plated plate 30 to be commercialized on the top of the decorative manufacturing master 10 is formed in the shape or pattern 12 of various patterns (S210a) In this case, the first corrosion-resistant plating is performed by the use of palladium (Pd), plating by a three-way (tin (Sn), zinc (Zn), copper (Cu)) alloy instead of the palladium (Pd) Note that this may be done.

그리고, 상기와 같이 파라듐(Pd)이나 삼원(주석(Sn),아연(Zn),동(Cu))합금 등을 이용해 1차 내식성 도금이 이루어진 장식물 제조용 마스터(10)의 상단에 제품화를 위한 동(Cu)도금(S210b)이 이루어지는데, 이 때 상기 동(Cu)도금의 경우 전술한 종래 금속장식물 제조방법에 적용된 동(Cu)도금과정과 마찬가지로 파라듐(Pd)이나 삼원(주석(Sn),아연(Zn),동(Cu))합금 등에 의해 1차 내식성 도금된 장식물 제조용 마스터(10)의 상단에 도금 시 밀착성을 위한 1차 피로인산 동도금이 이루어지고, 그 상단에 내식성을 위한 2차 유산 동도금이 이루어지면서 제품화를 위한 동(Cu)도금판(30)을 형성하게 된다.And, as described above for the commercialization on the top of the master (10) for the manufacture of the decoration made of primary corrosion-resistant plating using palladium (Pd) or ternary (tin (Sn), zinc (Zn), copper (Cu)) alloy, etc. Copper (Cu) plating (S210b) is made, in the case of the copper (Cu) plating, such as the copper (Cu) plating process applied to the conventional method for manufacturing a metal ornament described above, such as palladium (Pd) or three-way (tin (Sn) ), Zinc (Zn), copper (Cu)) primary corrosion resistance plated by the alloy, etc. The primary pyrophosphate copper plating for adhesion at the top of the master (10) for the decoration is made, the upper 2 for corrosion resistance As the primary lactic acid copper plating is formed, copper (Cu) plated plate 30 is formed for commercialization.

또한, 상기와 같이 장식물 제조용 마스터(10)에 1차 내식성 도금과 함께 동(Cu)도금된 상기 동(Cu)도금판(30)의 상단에 2차 내식성 도금(S210c)을 수행하게 되는데, 이 때 상기 2차 내식성 도금은 동(Cu)도금판(30)의 상단부에 대한 부식 방지 및 제품의 표면 색체 처리 효과를 향상시키기 위한 크롬(Cr)이나 니켈(Ni)을 이용해 도금이 이루어지게 되며, 상기 2차 내식성 도금을 크롬(Cr)으로 할 경우 상기 2차 내식성 도금부가 흰색을 띄게 된다.In addition, the secondary corrosion-resistant plating (S210c) is performed on the upper end of the copper (Cu) plated plate 30 plated with copper (Cu) together with primary corrosion-resistant plating on the decorative material manufacturing master 10 as described above. At this time, the secondary corrosion resistant plating is performed using chromium (Cr) or nickel (Ni) to prevent corrosion on the upper end of the copper (Cu) plated plate 30 and improve the surface color treatment effect of the product. When the secondary corrosion resistant plating is chromium (Cr), the secondary corrosion resistant plating becomes white.

그리고, 상기와 같이 상기 1,2차 내식성 도금된 동(Cu)도금판(30)의 제품화를 위해 마스터(10) 즉, 상기 장식물 제조용 마스터(10)로부터 1,2차 내식성 도금된 동(Cu)도금판(30)을 박리(S220)시킨 다음 상기 박리된 동(Cu)도금판(30) 즉, 상하단에 1,2차 내식성 도금이 이루어진 동(Cu)도금판(30)을 건조기를 통해 50~60℃로 건조(S230)한 다음 상기 건조된 동(Cu)도금판(30)으로부터 휴대단말기의 메탈키패드나 LCD액정의 둘레부를 감싸는 메탈윈도우, 케이스, 로그 등의 금속장식물(12) 및/또는 다양한 패턴의 문양부(12)에 대한 제품을 생산하기 위하여 상기 제품과 스크랩부분을 분리시키기 위한 제품의 프레스 펀칭작업(S240)을 수행함으로써 도 3과 같은 단면의 제품 즉, 하단으로부터 1차 내식성 도금판(20), 동(Cu)도금판(30), 2차 내식성 도금판(40)이 적층된 상태의 금속장식물(12)이나 다양한 패턴의 문양부(12)에 대한 제품 생산(S250)이 이루어지면서 본 발명의 제조과정이 종료되게 된다.In addition, the first and second corrosion-resistant copper plated copper (Cu) plated plate 30 as described above for the commercialization of the master 10, that is, the first and second corrosion-resistant plated copper (Cu) Peeling the plate (30) (S220) and then the copper plated (Cu) plate 30, that is, the upper and lower copper plated copper (Cu) plate 30 made of the first and second corrosion-resistant plating through a dryer After drying (S230) at 50 ~ 60 ℃ (Cu) metal ornaments such as metal windows, cases, logs, etc. surrounding the circumference of the metal keypad or LCD liquid crystal of the mobile terminal from the copper plate (30) and And / or press punching operation (S240) of the product to separate the product from the scrap portion in order to produce a product for the pattern portion 12 of various patterns, that is, the product of the cross-section as shown in FIG. Metal decoration (12) in which the corrosion-resistant plated plate 20, copper (Cu) plated plate 30, the secondary corrosion-resistant plated plate 40 is laminated The production process of the present invention is terminated while producing the product (S250) for the pattern portion 12 of the various patterns.

이와 더불어, 상기 장식물 제조용 마스터(10)의 준비과정 및 상기 각 공정 중 1,2차 내식성 도금이 종료된 동(Cu)도금판(30)을 장식물 제조용 마스터(10)로부터 분리시킨 다음 각 공정 후 실행되는 수세과정은 금속장식물(12)이나 다양한 패턴의 문양부(12)를 제조하는 과정에서 통상적으로 실행되기 때문에 이에 대한 수세 과정의 설명은 생략하였으며, 상기한 수세과정이 생략되었다 하더라도 상기 장식물 제조용 마스터(10)의 준비과정이나 상기 각 공정 중 1,2차 내식성 도금이 종료된 동(Cu)도금판(30)을 장식물 제조용 마스터(10)로부터 분리시킨 다음 각 공정 후 수세과정이 이루어지는 것을 자명한 사실로서 본 발명의 기술사상을 벗어나지 않는다 할 것이다.In addition, after the preparation process of the decoration manufacturing master 10 and the first and second corrosion-resistant plating is finished in each of the copper plating plate 30 is separated from the decoration manufacturing master 10 and then after each process Since the washing process is usually performed in the process of manufacturing the metal ornament 12 or the pattern portion 12 of various patterns, the description of the washing process for this is omitted, even if the washing process is omitted for the decoration After the preparation of the master 10 or the above-mentioned processes, the copper plating plate 30 having the first and second corrosion resistant plating ends is separated from the master 10 for manufacturing a decoration, and then washing is performed after each step. As a matter of fact, the technical spirit of the present invention will not be exceeded.

이상에서와 같이 상술한 실시예는 본 발명의 가장 바람직한 예에 대하여 설명한 것이지만 상기 실시예에만 한정되는 것은 아니며, 본 발명의 기술사상을 벗어나지 않는 범위 내에서 다양한 변형이 가능하다는 것은 당업자에게 있어서 명백한 것이다.As described above, the above-described embodiments are described with reference to the most preferred examples of the present invention, but are not limited to the above embodiments, and it will be apparent to those skilled in the art that various modifications can be made without departing from the technical spirit of the present invention. .

도 1은 종래 마스터를 이용한 금속장식물 도금과정을 개략적으로 나타낸 공정도.1 is a process diagram schematically showing a metal plating process using a conventional master.

도 2는 본 발명의 마스터를 이용한 금속장식물 도금과정을 개략적으로 나타낸 공정도.Figure 2 is a process diagram schematically showing a metal decoration plating process using the master of the present invention.

도 3은 도 2에 도시된 본 발명의 도금과정을 통해 제작된 금속장식물의 단면도.3 is a cross-sectional view of the metal ornament produced through the plating process of the present invention shown in FIG.

* 도면의 주요 부분에 대한 보호의 설명 *Description of protection for the main parts of the drawing

10. 마스터10. Master

12. 금속장식물(문양부)12. Metal Ornaments (Glyphs)

14. 마스킹테이프14. Masking Tape

20. 1차 내식성 도금판20. Primary corrosion resistant plate

30. 동(Cu)도금판30. Copper plated plate

40. 2차 내식성 도금판40. Secondary corrosion resistant plate

Claims (2)

표면에 음각 또는 양각으로 다양한 패턴의 문양부가 형성된 장식물 제조용 마스터의 상단에 1차 내식성 도금을 하는 단계와;Performing a first corrosion resistant plating on the top of the master for producing a decoration having various patterns of patterns in an intaglio or embossed surface; 상기 1차 내식성 도금된 마스터의 상단에 동(Cu)도금을 하는 단계와;Copper (Cu) plating the upper end of the primary corrosion-resistant plated master; 상기 동(Cu)도금판의 상단에 2차 내식성 도금을 하는 단계와;Performing secondary corrosion resistant plating on an upper end of the copper (Cu) plated plate; 상기 1,2차 내식성 도금된 동(Cu)도금판을 마스터로부터 박리시키는 단계와;Peeling the first and second corrosion resistant plated copper (Cu) plated plates from the master; 상기 박리된 동(Cu)도금판을 건조하는 단계; 및Drying the peeled copper (Cu) plated plate; And 상기 건조된 동(Cu)도금판으로부터 제품 생산을 위한 프레스의 펀칭작업이 이루어지는 단계(S260)를 포함하여 이루어진 것을 특징으로 하는 마스터를 이용한 금속장식물 제조방법.Method of producing a metal decoration using a master, characterized in that it comprises a step (S260) of the punching operation of the press for producing a product from the dried copper (Cu) plated plate. 제 1 항에 있어서, 상기 1차 내식성 도금은 마스터의 상단에 도금되는 동(Cu)도금의 하단부에 대한 부식을 방지하기 위한 파라듐(Pd)이나 삼원(주석(Sn),아연(Zn),동(Cu))합금의 도금이 이루어지고,The method of claim 1, wherein the primary corrosion-resistant plating is palladium (Pd) or ternary (tin (Sn), zinc (Zn), to prevent corrosion to the lower end of the copper (Cu) plating to be plated on the top of the master) Copper (Cu) alloy is plated, 상기 2차 내식성 도금은 동(Cu)도금의 상단부에 대한 부식 방지 및 제품의 표면 색체 처리 효과를 향상시키기 위한 크롬(Cr)이나 니켈(Ni)로 도금이 이루어진 것을 특징으로 하는 마스터를 이용한 금속장식물 제조방법.The secondary corrosion-resistant plating is a metal decoration using a master, characterized in that the plating is made of chromium (Cr) or nickel (Ni) to prevent corrosion to the upper end of the copper (Cu) plating and improve the surface color treatment effect of the product Manufacturing method.
KR1020070090317A 2007-09-06 2007-09-06 The manufacturing method for metal decoration using master KR100901795B1 (en)