CN102758510B - Surface processing method for aluminum gusset plates - Google Patents
Surface processing method for aluminum gusset plates Download PDFInfo
- Publication number
- CN102758510B CN102758510B CN201110110849.0A CN201110110849A CN102758510B CN 102758510 B CN102758510 B CN 102758510B CN 201110110849 A CN201110110849 A CN 201110110849A CN 102758510 B CN102758510 B CN 102758510B
- Authority
- CN
- China
- Prior art keywords
- plates
- paint
- sheet material
- engraving
- wire drawing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a surface processing method for gusset plates. The surface processing method comprises the following procedures: 1) engraving plates and spraying paint on the plates, namely performing screen printing and then performing corrosion engraving on the surfaces of the plates or directly engraving the surfaces by means of a laser engraving machine, and spraying paint on the plates of which the surfaces are engraved; 2) drawing wires on the surfaces, namely drawing wires on the surfaces of the plates sprayed with the paint, performing wiredrawing on the paint on the bulged surfaces of the plates to remove the paint, and reserving the paint on the concave parts on the surfaces of the plates; 3) printing patterns on the surfaces, coloring the bulged surfaces of the plates, namely painting, printing, performing transfer printing, oxidizing, baking paint, and coating protective films on the surfaces of the plates of which the surface patterns are printed; 4) performing punch forming on the gusset plates, namely putting the processed plates into a punch die, and punching the plates into the required gusset plates; and 5) spraying varnish on the surfaces, namely spraying matte or specular varnish on the punched surfaces of the gusset plates. The surface processing method has the characteristics that: a processing process is simple; a processing effect is obvious; and the surfaces of the plates can be processed to meet the requirements on the surfaces of the present gusset plates.
Description
Technical field
What the present invention relates to is a kind of surfacing processing method that is specifically designed to aluminum-pinch, belongs to the process of surface treatment of aluminium plate.
Background technology
As a kind of metal decorative material, the surfacing quality of aluminium sheet will be directly connected to quality and the aesthetic measure of interior decoration.Along with improving constantly of people's living standard, people are more and more higher to the attention of interior decoration quality and aesthetic measure, but the Surface Machining of aluminum current plate material is processed and has substantially been continued to use conventional processing technology, as surperficial pattern printing, spraying paint of surface processed etc., especially day by day universal along with Integral ceiling product, aluminum-pinch surface can not meet simple true qualities and be only surperficial concave-convex design and produced, be badly in need of a kind of surface color and polish pattern rich and varied, the aluminium sheet material that can match with indoor other decoration.
Summary of the invention
The object of the invention is to overcome the deficiency that prior art exists, and provide a kind of improved, and processing technology is simple, and processing effect is obvious, can carry out Surface Machining processing to aluminium sheet material, to meet the Surface Machining treating method of aluminum-pinch of aluminum current buckle surface needs.
The object of the invention is to complete by following technical solution, the surfacing processing method of described aluminum-pinch, its aluminium, copper material are made sheet material, and described processing and treating method comprises following a few procedure:
It comprises following a few procedure:
1) engraving of sheet material, the processing of spraying paint, it refers to first carries out serigraphy post-etching engraving to the surface of sheet material, or laser engraving machine directly carves, and then effects on surface carries out the sheet material that Carving Machining crosses and sprays paint;
2) surperficial wire drawing processing, it is that the sheet material after spraying paint is carried out to surperficial wire drawing processing, the paint of sheet material upper convex surface is carried out removing after wire drawing, and the paint at the recessed place of plate surface still retains;
3) picture on surface is printed, and carries out color treatments in sheet material convex surfaces, comprises air brushing, printing, transfer printing, oxidation, paint baking, and be covered with diaphragm at plate surface after picture on surface has been printed;
4) buckle punch forming, puts into above-mentioned sheet material after treatment on punching machine mold plate stamping is become to required buckle;
5) surface spray varnish, more sub-light or high light varnish are sprayed in buckle surface after punching press.
Erosion carving of the present invention comprises serigraphy and erosion carving, and wherein said engraving is that liquid medicine corrosion is carried out in the place that silk screen is not printed onto, thereby occurs Z-Correct bump mapping Z-correct; Selected liquid medicine is ferric trichloride; The described processing of spraying paint, especially selects spray silver paint and gold lacquer, to show as bronzing effect; Described surperficial wire drawing is treated to be loaded onto rubber and carries out wire drawing on rubber machine, and wire drawing thickness depends on a rubber material size and selects.
It is simple that the present invention has processing technology, and processing effect is obvious, can carry out Surface Machining processing to sheet material, waits feature to meet current buckle surface needs.
The specific embodiment
Below in conjunction with specific embodiment, the present invention will be described in detail: the surfacing processing method of described aluminum-pinch, and its aluminium, copper material are made sheet material, and described processing and treating method comprises following a few procedure:
1) engraving of sheet material, the processing of spraying paint, it refers to first carries out serigraphy post-etching engraving to the surface of sheet material, or laser engraving machine directly carves, and then effects on surface carries out the sheet material that Carving Machining crosses and sprays paint;
2) surperficial wire drawing processing, it is that the sheet material after spraying paint is carried out to surperficial wire drawing processing, the paint of sheet material upper convex surface is carried out removing after wire drawing, and the paint at the recessed place of plate surface still retains;
3) picture on surface is printed, and carries out color treatments in sheet material convex surfaces, comprises air brushing, printing, transfer printing, oxidation, paint baking, and be covered with diaphragm at plate surface after picture on surface has been printed;
4) buckle punch forming, puts into above-mentioned sheet material after treatment on punching machine mold aluminium sheet is struck out to required buckle;
5) surface spray varnish, then buckle surface after punching press sprays sub-light or high light varnish, it not only can make buckle surface more be rich in quality, and is more prone to clean.
Erosion carving of the present invention comprises serigraphy and erosion carving, and wherein said engraving is that liquid medicine corrosion is carried out in the place that silk screen is not printed onto, thereby occurs Z-Correct bump mapping Z-correct; Selected liquid medicine is ferric trichloride; The described processing of spraying paint, especially selects spray silver paint and gold lacquer, to show as bronzing effect; Described surperficial wire drawing is treated to be loaded onto rubber and carries out wire drawing on rubber machine, and wire drawing thickness depends on a rubber material size and selects.
Claims (2)
1. a surface treatment method for buckle, its aluminium, copper material are made sheet material, it is characterized in that described processing and treating method comprises following a few procedure:
1) engraving of sheet material, the processing of spraying paint, it refers to first carries out serigraphy post-etching engraving to the surface of sheet material, or laser engraving machine directly carves, and then effects on surface carries out the sheet material that Carving Machining crosses and sprays paint;
2) surperficial wire drawing processing, it is that the sheet material after spraying paint is carried out to surperficial wire drawing processing, the paint of sheet material upper convex surface is carried out removing after wire drawing, and the paint at the recessed place of plate surface still retains;
3) picture on surface is printed, and carries out color treatments in sheet material convex surfaces, comprises air brushing, printing, transfer printing, oxidation, paint baking, and be covered with diaphragm at plate surface after picture on surface has been printed;
4) buckle punch forming, puts into above-mentioned sheet material after treatment on punching machine mold plate stamping is become to required buckle;
5) surface spray varnish, more sub-light or high light varnish are sprayed in buckle surface after punching press.
2. the surface treatment method of buckle according to claim 1, the engraving that it is characterized in that described sheet material comprises the erosion carving after serigraphy, wherein said erosion carving is that liquid medicine corrosion is carried out in the place that silk screen is not printed onto, thereby occurs Z-Correct bump mapping Z-correct; Selected liquid medicine is ferric trichloride; The described processing of spraying paint comprises spray silver paint and gold lacquer, to show as bronzing effect; Described surperficial wire drawing is treated to be loaded onto rubber and carries out wire drawing on rubber machine, and wire drawing thickness depends on the size of a rubber material.