KR20080002721A

KR20080002721A - Processing method and manufactured goods of sand sculpture

Info

Publication number: KR20080002721A
Application number: KR1020070125861A
Authority: KR
Inventors: 황철현
Original assignee: 황철현
Priority date: 2007-12-04
Filing date: 2007-12-04
Publication date: 2008-01-04

Abstract

A manufacturing method of sand sculpture and a sand sculpture manufacture thereby are provided to maintain the artistic shape of sand sculpture for a long time by applying cold setting resin to the surface layer of the sand sculpture. A manufacturing method of sand sculpture includes the steps of: making sand sculpture by forming wet sand; drying the made sand sculpture to make the surface layer thereof have a moisture content of less than 15%; applying cold setting resin to the surface layer of the sand sculpture with a sprayer and making the cold setting resin permeating into the sand hardened; removing the sand inside the surface layer after the resin applied to the surface layer is hardened; and applying cold setting resin to the surface layer inside the sand sculpture from which the sand is removed and making the applied resin hardened.

Description

Processing method and manufactured goods of sand sculpture

도 1은 본 발명의 공정도1 is a process diagram of the present invention

본 발명은 모래조각품의 제조방법 및 그 모래조각품에 관한 것으로, 특히 젖은 모래로 조각품을 제작 한 후 그 표층을 건조시키고 그 표층에 상온경화수지를 분무기로 수회 도포하여 모래와 상온경화수지가 서로 결착하여 경화되도록 하는 단계, 그리고 모래조각품의 표층에 분무한 수지가 경화된 후 내부의 모래를 제거하는 단계, 그리고 내부의 모래를 제거한 모래조각품의 내부 표층에 다시 상온경화수지를 도포하는 단계에 의하여 쉽개 파손될 수 있는 모래조각품을 장기간 보존할 수 있고, 모래조각품 내부의 모래를 제거하여 중량을 줄임으로써 이동 및 취급이 편리하게 되도록 함을 특징으로 하는 모래조각품의 제조방법 및 그 모래조각품에 관한 것이다.The present invention relates to a method for producing a sand sculpture and its sand sculpture, and in particular, after the sculpture is made of wet sand, the surface layer is dried, and the surface layer is coated with a thermosetting resin several times with a sprayer to bind the sand and the room temperature curing resin to each other. By curing the resin sprayed on the surface layer of the sand sculpture, and then removing the sand inside, and applying the room temperature hardening resin to the inner surface layer of the sand sculpture from which the sand is removed. The present invention relates to a method for manufacturing a sand sculpture and its sand sculpture, which can be preserved for a long time, and the sand sculpture can be easily removed by removing sand in the sand sculpture to reduce weight.

종래에 만들어지는 모래조각은 모래를 물과 혼합하여 압착한 후 주걱이나 기타의 도구를 이용하여 아름다운 예술적인 형상을 조각한 것인데, 이러한 모래조각 은 모래입자가 수분에 의해 서로 결착되는 것이기 때문에 건조되면 바람이 세게 불어도 파손되고 강우에도 쉽게 부스러지므로 만든 후 2～3일만 방치하여도 쉽게 파손되거나 부서지며 운송 및 이동이 불가능하다는 문제점이 있었다.Conventional sand sculptures are made by squeezing sand by mixing it with water and then sculpting a beautiful artistic shape using a spatula or other tool. These sand flakes are sand particles that bind to each other by moisture. Even if the wind blows hard and breaks easily in the rain, it is easily broken or broken even after 2 or 3 days of making, and there is a problem that transportation and movement are impossible.

본 발명은 이러한 종래의 문제점을 해결하기 위하여 연출한 것으로, 특히 젖은 모래로 조각품을 제작한 후 모래조각품의 표층에 도포 후 상온에서 빠른 경화가 이루어지는 상온경화수지를 도포하여 모래의 질감을 잘 드러내면서도 모래조각품의 표층을 경화된 수지에 의해 단단히 결착시켜 조각의 예술적 형상을 장기보존 할 수 있도록 한 것이다.The present invention has been produced in order to solve the above problems, in particular, after making a sculpture with wet sand, and then applied to the surface layer of the sand sculptures by applying a room temperature hardening resin which is rapidly cured at room temperature, while the sand texture well exposed The surface layer of the sculpture is firmly bound by hardened resin to preserve the artistic shape of the sculpture for a long time.

이러한 본 발명의 구성을 첨부한 도면에 따라 상세히 설명하면 다음과 같다.The configuration of the present invention will be described in detail with reference to the accompanying drawings.

본 발명은 젖은 모래를 성형 또는 조각하여 모래조각품을 제작하는 단계와, 제작된 모래조각품의 표층이 수분함유량 15％ 이내가 되도록 건조시키는 단계와, 상기한 모래조각품의 표층에 상온경화수지(상온에서 경화제와 결합하여 화학반응으로 굳어지는 열결화성수지)를 분무기로 수회 도포하여 모래에 스며들어간 상온경화수지가 경화되도록 하는 단계와, 상기한 단계에 의해 모래조각품의 표층에 분무한 수지가 단단히 경화된 후 상온경화수지가 스며들지 않은 내부의 모래를 제거하는 단계와, 상기한 단계에 의해 내부의 모래를 제거한 모래조각품 내부의 표층에 다시 상온경화수지를 도포하여 경화시키는 단계를 포함하여서 된 것이다.The present invention comprises the steps of producing sand sculptures by molding or sculpting the wet sand, and drying the surface layer of the produced sand sculptures within 15% of water content, and at room temperature curing resin (at room temperature) The thermosetting resin hardened by a chemical reaction combined with a hardening agent is applied several times with a spray to harden the room temperature curing resin that has soaked into the sand, and the resin sprayed on the surface layer of the sand sculpture is hardened by the above steps. After the step of removing the sand inside the room temperature hardening resin is not impregnated with, and by applying the above-mentioned hardening of the room temperature hardening resin to the surface layer inside the sand sculpture from which the internal sand is removed by the above steps.

이하 본 발명의 실시예를 도면에 따라 상세히 설명한다.Hereinafter, embodiments of the present invention will be described in detail with reference to the drawings.

해변 또는 작업장에 선별된 젖은 모래를 모아놓고 틀로 성형되거나 조각도로 조각하여 모래조각품을 제작하는 제1단계(모래조각품의 제작)와,A first step (manufacturing sand sculpture) of collecting the wet sand selected on the beach or the workshop and forming sand sculpture by molding or carving into a frame;

제작된 모래조각품의 표층이 수분함유량 15％ 이내가 되도록 자연건조 또는 드라이어로 건조시키는 제2단계(모래조각품의 건조)와,A second step (drying the sand sculpture) of drying with a natural drying or a dryer so that the surface layer of the manufactured sand sculpture is within 15% of water content,

상기한 모래조각품의 표층에 상온경화수지(상온에서 경화제와 결합하여 화학반응으로 굳어지는 열경화성수지)의 한 종류인 호마이카를 경화제와 약 20:1정도로 혼합하여 분무기에 의해 수회 도포하여 모래에 스며들어간 상온경화수지가 경화되도록 하는 제3단계(모래조각품 표면에 상온경화수지를 도포하여 경화)와,On the surface layer of the sand sculptures, Homica, a kind of room temperature curing resin (a thermosetting resin which is hardened by a chemical reaction in combination with a curing agent at room temperature), is mixed with a curing agent at about 20: 1 and applied several times by a sprayer to seep into sand. A third step to cure the room temperature hardening resin (by curing the room temperature hardening resin on the surface of the sand sculpture);

상기한 단계에 의해 모래조각품의 표층에 분무한 상온경화수지가 단단히 경화된 후 상온경화수지가 스며들지 않은 내부의 모래를 제거하는 제4단계(모래조각품 내부의 모래 제거)와,A fourth step (removal of sand inside the sand sculpture) after removing the sand inside the room temperature hardening resin that is hardened by the room temperature hardening resin sprayed onto the surface layer of the sand sculpture by the above steps;

상기한 단계에 의해 내부의 모래를 제거한 모래조각품 내부의 표층에 다시 상온경화수지를 수히 도포하여 모래조각품의 내부도 역시 수지에 의해 경화시키는 제5단계(모래조각품 내부에 상온경화수지를 도포하여 경화)를 포함하여 이루어진 것이다.The fifth step of applying the room temperature hardening resin to the surface layer inside the sand piece from which the sand is removed by the above step again and curing the inside of the sand piece also by resin (coating the room temperature hardening resin inside the sand piece) ).

이와 같은 본 발명은 상술한 특정의 바람직한 실시예에 한정되지 않으며, 청구범위에 청구하는 본 발명의 요지를 벗어남이 없이 당해 발명이 속하는 기술 분야에서 통상의 지식을 갖은 자라면 누구든지 다양한 변형 실시가 가능한 것은 물론이고, 그와 같은 변경은 본 발명 청구범위 기재의 청구범위 이내에 있다고 할 수 있다.Such a present invention is not limited to the above-described specific preferred embodiments, and various modifications can be made by those skilled in the art without departing from the gist of the present invention as claimed in the claims. It goes without saying that such changes are within the scope of the claims of the present invention.

본 발명은 모래조각품의 표면에 상온경화수지가 스며들어 경화된 상태의 모래조각품을 제작함으로써 모래조각품의 변형 및 훼손이 방지되고 운송 및 이동이 가능해지도록 하는 특장점을 지닌 것이다.The present invention has the advantage of preventing the deformation and damage of the sand sculptures and transport and movement by making sand sculptures in the hardened state by infiltration of a room temperature hardening resin on the surface of the sand sculptures.

Claims

Forming sand sculptures by molding or sculpting wet sand; drying the sand sculptures so that the surface layer of the sand sculptures is within 15% of water content; and curing the room temperature with a curing agent at room temperature. The thermosetting resin hardened by a chemical reaction by a sprayer several times to harden the room temperature cured resin soaked into the sand, and the resin sprayed on the surface layer of the sand sculpture by the above step is hardened and then the room temperature cured resin. Removing the internal sand that has not been impregnated, and applying the above-mentioned hardening resin to the surface layer inside the sand sculpture from which the internal sand is removed by the above-mentioned step to harden the sand sculpture. Manufacturing method.

Sand sculptures, characterized in that produced by the manufacturing method of claim 1