KR20070117515A - 숯 보드페널 - Google Patents
숯 보드페널 Download PDFInfo
- Publication number
- KR20070117515A KR20070117515A KR1020070114545A KR20070114545A KR20070117515A KR 20070117515 A KR20070117515 A KR 20070117515A KR 1020070114545 A KR1020070114545 A KR 1020070114545A KR 20070114545 A KR20070114545 A KR 20070114545A KR 20070117515 A KR20070117515 A KR 20070117515A
- Authority
- KR
- South Korea
- Prior art keywords
- powder
- charcoal
- weight
- mixing
- mixture
- Prior art date
Abstract
본 발명은 숯보드판에 관한것으로, 보드판을 숯과 탄소 및 흑연을 혼합하여 통상의 프라스틱수지와 혼합하여 압출, 또는사출하여 소정의 크기의 보드판을 성형하는 것이다,
따라서 본 발명에 따른 보드판은 숯과 탄소 기타 인체에 유익한 광석물과 기능들을 첨가함으로써 내, 외장용의 건축용 보드판을 이루고자 하는 것이다,
Description
본 발명은 숯, 보드 판에 관한 것으로 본 숯 보드의 용도는 숯과 열 전도성이 우수한 흑연을 결합한 것으로 이는 숯이 지니고 있는 기능인 원 적외선의 충만한 방출과 음이온 방출 그리고 탈취를 통한 공기정화, 습도조절, 등을 통하여 주거생활의 안정과 효능을 높이고 또한 열 전도가 우수하며 인체에 무해한 흑연을 효능을 높이고자 한 것이다, 따라서 통상의 숯 즉 참숯 및 대나무 숯등의 목질숯을 일정의 탄소 및 흑연 과 혼합하고 이에 흑운모 및 제오라이트, 토루마린,분말등을 소정량 혼합하여 용도에 따라서 통상의 플라스틱 수지를 선정하여 혼합한다, 즉 성형용 제품은 폴리에틸린(PE), 필름용제품은 폴리프로필렌(PP), 발포성 성형제품은 폴리스틸렌(PS),등을 혼합하고 이를 압출 또는 사출하여 소정의 구하고자하는 보드페널을 형성하는 것이다, 이때표면에 무뉘나 형상을 이루고자 할때에는 사출형식을 평면판을 이루고자할 때에는 압출로 하는 것이 바람직하다,
도한 상기의 숯, 흑연 및 분말소제들을 플라스틱소제와의 융합을 용이하게 하기위하여 상기의 첨가물들을 사전에 마스터배치를 형성하는 것이 바람직하다,
국내등록특허 제 10-0468442호의 경우에는 숯과 천연석 분말과 아크릴 수지를 포함하여 성형되는 내 외장재에 그치고 있으며 이또한 700-1200도의 가마에서 구워내어 유약으로 코팅한 것으로 되여있으나 통상의 숯분말 즉 목탄숯의 분말또는 일정의 알갱이 정도는 상기와 같은 온도에서는 그성분이 완전히 산화되여 유지할수 없음으로 통상의 목탄숯의 기능을 유지할수 없는 것이다,
또한 국내 공개특허 제 10-2006-0004580호와 같은경우에는 숯분말과 점토광물, 섬유보강제 및 접착제를 포함하여 가압 성형하여 숯보드를 제조하는 것으로 되여있어 건축용으로 응용하고자하나 이는 제품의 강도가 약하며 및 습기의 흡습력이 과다하여 표면에 변형현상이 발생함으로 장기적으로는 사용될 수 없는 결함이 있는것이다,
국내 공개특허 제 10-2007-0078644와 같은 경우에도 단순히 건축용 숯보드만을 제조하는 방법을 제시하고 있으나 이는 상기의 제 10-2006-0004580호와 같은 내용으로써 제품의 강도를 요구하는 마루바닥재 또는 벽면, 천정재 등에는 합당하게 사용되기가 어려운것이다,
따라서 현재 내, 외장재로 다수 사용되고 있는 마감재로는 합판, 목질을 압착한 MDF,등에 무뉘필름또는 무뉘목등을 접착한 것이 대부분이며 일부는 플라스틱을 압출하여 코팅한 제품을 사용하여 왔다,
따라서 상기의 제품들은 매우 화재에 위험하며 또한 인체에 유익한 기능들을 지니고 있지않은 것들이다,
따라서 목질탄의 숯기능이 함유된 내, 외장용 보드 페널을 제공하고자 하는 것이다,
위와같은 기술적인 문제에 있어서 현재 각 종의 많은 숯 보드와 또는 합판, MDF 등에 무뉘목, 또는 무뉘필름등을 응용한 보드나 페널이 있으나 이는 그용도와 기능들이 미흡하였다,
따라서 숯이 가지고 있는 상술한 바와같이 여러 가지 인체에 유익한 효능을 실 생활에서 가장많이 응용될수 있는 주거환경 및 생활 환경을 이루고자 하는 것으로써 기능성이 다양한 숯보드를 제공하는 것이다, 따라서 현재 국내에는 이를 위한 온전한 기술이 제공되지 않은 것으로 사료되는 것이다,
본 발명은 위와 같은 점들을 인식하여 구상된 것으로 기능성이 풍부한 즉 다량의 원적외방출과 음이온의 방출, 탈취효과, 세균침식방지효과, 흡습효과와, 조절기능이 우수한 숯보드를 건축물의 내, 외장에 적용하고자 하는 것이다,
따라서 상기의 목적을 달성하고 문재점들을 해결하기 위하여서는 숯의 다양한 기능성인 원적외선의 방출과 탈취효과 및 흡습효과등과 흑연, 탄소의 우수한 열 전도성과 토르마린의 음이온 발산기능을 효과적으로 결합하여 주거 및 건물내에서의 생활환경을 보다인체에 유익하게 하기위한 것으로, 본 숯 및 혼합물의 보드판을 형성하고자하는 과제의 해결수단으로써는 다음과 같은 실시의 예를 이루는 것이다,
최근 들어 생활의 여유와 더불어 건강에 대한 관심이 매우 깊어서 웰빙시대 를 이루며 이에 대하여 숯이 지니고 있는 효능과 가치에 대하여 많은 관심을 가져왔다, 따라서 숯이 여러 가지 형태로 실 생활에 응용되고있으나 아직은 단순한 숯 자체만을 응용한 것으로 그 기능성을 충분히 발휘하지 못하였다, 따라서 본 발명이 제시하는 바는 사람이 실생활에 가장많이 사용되는 주거환경에 응용함으로써 그 나타나는 효능으로 더불어 건강한 샐활환경을 제공하고자 하는 것이다,
따라서 본 발명은 상기에서 제시한 바와같이 숯이지니는 기능과 또다른 광물성들이 지니고 있는 기능들을 합하여 종합적인 기능성이 풍부한 보드 페널을 제공함으로써 사랑이 가장많이 거주하며 생활하는 주거환경 및 업무, 생활환경을 보다 효과적이며 쾌적한 환경을 이루고자 하는 것이다,
.
따라서 상기와 같은 목적을 달성하기 위하여서는 본 발명에 따르는 숯 보드의 제조방법은 몰비(M.R) 3.5인 액상 규산칼륨 또는 액상 규산나트륨,등의 일명 물유리용액, 또는 일반적인 액상의 난연제를 물과 희석하여 일정의 혼합액을 만들고 여기에 숯의 분말 또는 작은 알갱이와 일라이트, 제오라이트, 흑운모석, 토르마린등을 혼합하여 70도씨 이하의 온도에서 건조한다, 수분이 10％미만으로 건조된 재료는 그 숯의 입자들이 용도에 맞게 분쇄를 거치게 된다, 이는 성형작업시 숯을 높은 열로부터서 보호하고자 하는 것이다, 따라서 분쇄된 재료는 흑연과 함께 혼합하여 마스터배치를 형성하는 과정을 거치게 되는데 이때에는 용도에 합당한 플라스틱 수지를 포함하는 것이다,
따라서 건조가 완료된 재료는 압출기를 통하여 필요로 하는 두께의 보드판을 압출하여 성형하는 것이다, 또한 평면판이 요철의 형상을 이루는 제품은 프래스로 압착하거나 사출성형 할수 있는 것이다,
이때에 사용되는 숯은 참숯 또는 대나무숯으로 하며 흑연 탄소는 천연흑연으로 인상흑연, 고 결정질흑연, 미정질흑연, 인조흑연등이 있으나 고순도로 정재된 인상흑연을 사용하는 것이 바람직하다, 흑연은 그 자체가 탄소이며 소재로는 적당하며 또한 인체에 전혀 무해함으로 집접적인 접촉으로 부터서오는 분진 등의 피해를 없애면 좋은 생활의 도구로 응용할수 있는 것이다,
따라서 본 보드의 제조공정을 단계별로 정리하면 다음과 같다,
[1] 액상 규산 칼륨 또는 액상규산나트륨, 액상규산소다,또는 액상 난연재를 물과 희석한다, 이때 희석하는 물의 비율에 따라 농도와 열 저항성이 다르게된다, (10)
[2] 상기 [1]의 혼합액 20-40％중량에 숯분말 60％중량, 제오라이트 5％, 흑운모 20％중량, 토르마린15％중량을 혼합한다, (20)
[3] 상기[2]의 혼합물을 70도씨이하의 온도에서건조한다, (30)
[4] 건조된 재료를 용도에 따라 분쇄한다, (40)
[5] 분쇄된 재료15-30％ 중량에 흑연분말 15-30％중량에 프라스틱수지분말40-70％를 혼합한다,이때 제공되는 분말은 제품의 용도에 따라구성되나 분말의 고운 정도에 따라서 제품의 경도외 거칠기가 형성된다, (50)
[6] 상기[5] 의 혼합된 재료는 플라스틱 소재와 혼합하여 마스터배치를 형성한다, (60)
[7] 상기[6]의 재료를 발포제, 및 분산제와 유연제, 난연제를 혼합한다, (70)
[8] 상기의 혼합된 재료는 압출기,또는 사출기를 통하여 보드판을 형성한다, (80)
[9] 상기의 성형된 보드판넬은 그 표면을 무뉘종이또는 무뉘필름등으로 코팅처리하여 내,외장재로서 사용될수 있도록 미려한 형상을 제공한다,
상기와 같은 공정에 의하여 제조된 본 숯보드는 그 효능과 기능이 우수하여 건무의 내장제가 요구하는 기능들을 숯이가지는 다양한 기능들인 원적외선의 방출과 음이온의 방출, 습도조절, 냄새제거, 인체에 유해한 새균등의 번식억제 등의 효과를 발휘함으로써 실내환경또는 주거환경을 개선하고 나아가서는 새집증후군이나 아토피성 피부염등을 제어하는 효과를 나타냄으로써 실 생활 환경과 건강한 삶은 이루고자 하는 것이다,
.
Claims (6)
- 액상규산칼륨, 액상규산나트륨, 액상규산소다, 또는 액상의 난연재 용융액중 적어도하나를 물과 희석하는 액상 20-40％중량에 50매쉬 이상의 숯분말 60％중량과 제오라이트 분말10％중량과 흑운모분말 20％중량과 토르마린분말 10％중량을 혼합하여 건조하는 제조방법,
- 상기 제 1 항의 건조된 혼합물을 50메쉬이상 분쇄하는 제조방법, 이때 제품의 사양에 따라 분말의 정도를 조절한다,
- 분쇄된 숯 혼합물 15-30％중량과 흑연 15-30％중량에 플라스틱수지 40-70％ 중량을 교반하여 혼합하여 마스터배치를 형성하는 제조방법, 이때 제품의 용도에 따라 플라스틱수지의 종류를 선택한다, 바닥제 는 폴리에틸렌(PE), 벽제 및 천정제는 폴리스틸렌(PS), 등으로 선택한다,
- 상기 제 3항의 마스터배치를 제품의 사양에 따라 유연제, 발포제, 분산제, 난연제등을 혼합하여 플라스틱 압출기 또는 사출기를 통하여 성형하는 제조방법,
- 성형이 완료된 보드 판 위에 무뉘종이, 무뉘필름, 도료도장, 석분 몰타르로 및 열로 코팅하는 제조방법, 석분으로는 옥석, 맥반석, 대리석, 운모석, 미장석, 등의 분말인것,
- 상기의 제 5 항까지의 제조방법을 통하여 형성된숯 보드판넬,