KR20060082112A - Manufacture method of infrared ray cut off filter for small size optical instrument - Google Patents
Manufacture method of infrared ray cut off filter for small size optical instrument Download PDFInfo
- Publication number
- KR20060082112A KR20060082112A KR1020050002556A KR20050002556A KR20060082112A KR 20060082112 A KR20060082112 A KR 20060082112A KR 1020050002556 A KR1020050002556 A KR 1020050002556A KR 20050002556 A KR20050002556 A KR 20050002556A KR 20060082112 A KR20060082112 A KR 20060082112A
- Authority
- KR
- South Korea
- Prior art keywords
- product
- disc
- original
- plate
- cut filter
- Prior art date
Abstract
본 발명은 소형 광학기기에 사용되는 적외선 차단 필터에 관한 것으로서, 종래 적외선 차단 필터의 제조공정을 보면 적외선 차단 필터가 만들어지기 까지 다수회의 반복된 작업공정이 필요하고, 작업시간이 오래 걸리며, 비용이 많이 소모되어 생산성이 저하되는 문제점이 있었다.The present invention relates to an infrared cut filter used in a small optical device, the conventional manufacturing process of the infrared cut filter requires a number of repeated work process until the infrared cut filter is made, takes a long time, cost There was a problem that a lot of consumption is reduced productivity.
따라서 본 발명은 원판의 표면 검사 단계와, 원판의 코팅막 검사단계와, 원판의 1차 절단가공 단계와, 원판의 2차 절단가공 단계와, 제품의 치수 확인 단계와, 제품의 표면 클리닝 단계와, 제품의 표면 검사 단계를 통해 완성품인 적외선 차단 필터를 제조함에 있어서,Therefore, the present invention provides a surface inspection step of the original plate, a coating film inspection step of the original plate, a primary cutting process of the original plate, a secondary cutting process of the original plate, a dimension checking step of the product, a surface cleaning step of the product, In manufacturing the finished infrared cut filter through the surface inspection step of the product,
상기 원판의 1차 절단가공 단계와, 제품의 치수 확인 단계의 사이에, Between the first cutting process step of the disc, and the dimension check step of the product,
적외선 차단 필터의 원판(10) 다수개를 적층시키되 적층되는 각 원판(10)의 사이에 원판(10)을 보호하기 위한 종이(20)와 접착수단(30)을 설치한 다음 상기 적층된 원판(10)을 가열판(50)에 올려놓아 가열판(50)의 열에 의해 상기 접착수단(30)이 녹으면서 적층된 원판(10)이 서로 고정될 수 있도록 한 원판의 가열판 적층 단계와; A plurality of discs 10 of the infrared cut filter are stacked, and a paper 20 and an adhesive means 30 for protecting the disc 10 are installed between each disc 10 to be stacked, and then the laminated disc ( A step of laminating a heating plate of the original plate such that the original plates 10 are fixed to each other by melting the adhesive means 30 by the heat of the heating plate 50 by placing the plate 10 on the heating plate 50;
상기 원판의 가열판 적층 단계를 통해 적층된 원판(10)을 필요로 하는 치수 및 형상에 상응하도록 동시에 절단하여 가공된 원판(10)이 적층된 상태의 제품(60)으로 만들어지는 원판의 2차 절단가공 단계와;Secondary cutting of a disc made of a product 60 in which the processed disc 10 is laminated at the same time by cutting simultaneously to correspond to the required dimensions and shapes of the laminated disc 10 laminated through the heating plate lamination step of the disc. Processing step;
상기 원판의 2차 절단가공 단계를 통해 가공된 제품(60)을 가열된 상태의 트 리클로로에틸렌 용액에 집어넣어 상기 가공된 원판(10)을 고정시키고 있는 접착수단(30)을 녹여 제품(60)을 이루고 있는 가공된 원판(10)이 서로 분리되도록 하는 제품의 세척 단계와;The product 60 through the secondary cutting process of the disc is put into a trichloroethylene solution in a heated state to melt the adhesive means 30 which fixes the processed disc 10 and the product 60 And a washing step of the product to make the processed disk (10) separated from each other;
상기 제품의 세척 단계에 의해 제품(60)이 가공된 원판(10)과 종이(20)로 분리되고 상기 종이(20)는 제거하고 가공된 원판(10)만을 선택하여 선별해내는 제품의 분리 단계;Separation step of the product is separated by the product 60 is processed into the original plate 10 and the paper 20 by the washing step of the product, and the paper 20 is removed and selected by selecting only the processed original plate 10 ;
가 순차적으로 수행될 수 있도록 구성함에 따라 적외선 차단 필터를 짧은 시간동안 다량으로 제작할 수 있어, 제작성 및 생산성을 더욱 향상시킬 수 있는 것이다.As it is configured to be performed sequentially, the infrared cut filter can be produced in a large amount for a short time, it is possible to further improve the manufacturability and productivity.
광학기기, 적외선 차단 필터, 카메라, 가열판, 접착수단, 트리클로로에틸렌Optics, infrared cut filter, camera, heating plate, adhesive means, trichloroethylene
Description
도 1 은 종래의 적외선 차단 필터 제조공정을 도시한 순서도.1 is a flow chart showing a conventional infrared cut filter manufacturing process.
도 2 는 본 발명에 따른 적외선 차단 필터의 제조공정을 예시한 순서도.Figure 2 is a flow chart illustrating a manufacturing process of the infrared cut filter according to the present invention.
도 3 은 본 발명에 따라 적외선 차단 필터의 원판이 적층된 상태를 예시한 요부 확대 단면도.Figure 3 is an enlarged cross-sectional view of the main portion illustrating a state in which the original plate of the infrared cut filter is stacked in accordance with the present invention.
도 4a 는 본 발명에 따라 적층된 원판이 사각형상으로 가공된 상태를 예시한 요부 사시도.Figure 4a is a perspective view of the main portion illustrating a state in which the original plate laminated in accordance with the present invention processed into a square shape.
도 4b 는 본 발명에 따라 적층된 원판이 원형으로 각공된 상태를 예시한 요부 사시도.Figure 4b is a perspective view of the main portion illustrating a state in which the circle stacked in accordance with the present invention in a circular hole.
도면의 주요 부분에 대한 부호의 설명Explanation of symbols for the main parts of the drawings
10 : 원판 20 : 종이10: disc 20: paper
30 : 접착수단 40 : 보호유리30: bonding means 40: protective glass
50 : 가열판 60 : 제품50: heating plate 60: product
본 발명은 소형의 광학기기에 사용되는 적외선 차단 필터에 관한 것으로서, 더욱 상세히는 적외선 차단 필터로 만들기 위한 원판을 절단 가공하여 일정한 치수와 형상을 가지는 다수개의 적외선 차단 필터로 제작함에 있어서, 동시에 많은 갯수의 적외선 차단 필터를 신속하면서 용이하게 만들어낼 수 있도록 구성함에 따라 적외선 차단 필터의 제작성을 향상시키고 생산성을 더욱 늘릴 수 있도록 한 소형 광학기기에 사용되는 적외선 차단 필터의 제조공법에 관한 것이다.The present invention relates to an infrared cut filter used in a compact optical device, and more particularly, to fabricate a plurality of infrared cut filter having a certain dimension and shape by cutting the original plate for making the infrared cut filter, a large number at the same time The present invention relates to a method for manufacturing an infrared cut filter used in a small optical device that can improve the manufacturing ability of the infrared cut filter and increase productivity by configuring the cut off filter of the infrared cut filter quickly and easily.
일반적으로 광학기기(Optical Instrument)는 태양이나 전등에서 복사되는 빛의 특성인 반사, 굴절, 흡수, 간섭, 회절 등을 이용하여 공간에 있는 물체의 상을 형성시키거나, 어떤 물체에서 발사되는 방사선을 분석하여 그 물체의 성질을 연구하는 장치이다.In general, an optical instrument forms an image of an object in space by using reflection, refraction, absorption, interference, and diffraction, which are characteristics of light radiated from the sun or an electric light, or emit radiation emitted from an object. It is a device to analyze and study the properties of the object.
이러한 광학기기를 크게 분류해보면 안경, 쌍안경, 망원경, 현미경 등과 같이 눈의 시각력을 증강시키기 위한 목적의 것과; 카메라, 영화, 텔레비젼, 비디오촬영기, 투영기 등과 같이 렌즈에 의해 생긴 상의 기록과 그 재현을 목적으로 하는 것과; 거리계, 트랜싯, 간섭계, 고도계, 분광계, 렌즈미터 등의 광학적인 측정을 목적으로 하는 것과; 파이버스코프, 가스트로스코프 등과 같이 상의 전파, 정보전달 등 광학섬유속에 의한 상의 전송을 하는 것 등으로 분류할 수 있으며, 이러한 광학기기의 영역과 그 용용은 다방면에 걸쳐 개발되고 있는 실정이다.To broadly classify such optical devices, such as glasses, binoculars, telescopes, microscopes and the like for the purpose of enhancing the visual power of the eye; For the purpose of recording and reproducing images produced by lenses such as cameras, movies, televisions, video cameras, projectors, etc .; For optical measurement of rangefinders, transits, interferometers, altimeters, spectrometers, lens meters, etc .; Such as fiber scopes, gastroscopes, and the like can be classified into optical fiber bundles such as image propagation, information transmission, and the like. The scope and application of such optical devices are being developed in various fields.
이러한 광학기기에 있어서, 렌즈에 의해 생긴 상의 기록과 그 재현을 목적으 로 하는 이미지 인식 광학기기는 위에서도 언급한 바와 같이 캠코더, 디지털 카메라, PDA, 감시카메라, 차량용 카메라, 화상캠, 휴대폰 카메라 등과 같이 다양하며, 아날로그 방식보다는 디지털 방식의 이미저가 사용되고 있고, 그러한 디지털 방식의 이미저로는 상보성 금속 산화막 반도체인 CMOS(Complementary Metal Oxide Semiconductor)나, 고체촬상소자인 CCD(Charged Coupled Device)가 사용되고 있다.In such optics, image recognition optics for the purpose of recording and reproducing images caused by the lens, such as camcorders, digital cameras, PDAs, surveillance cameras, car cameras, image cams, mobile phone cameras, etc., as mentioned above. Various types of digital imagers are used rather than analog methods. Complementary metal oxide semiconductors (CMOS), which are complementary metal oxide semiconductors, or charged coupled devices (CCDs), which are solid-state imaging devices, are used as the digital imagers.
그리고 최근에는 디지털 이미저인 CMOS 및 CCD 등 촬상에 관련된 부품이 점차로 소형화되면서 이미지 인식 광학기기가 소형화되어 휴대가 용이해지고 있으며, 휴대폰에 소형의 디지털 카메라가 접목시켜 사용하기도 한다.Recently, as components related to imaging such as CMOS and CCD, which are digital imagers, are gradually miniaturized, image recognition optical devices have been miniaturized, making it easy to carry, and a small digital camera is also incorporated into a mobile phone.
한편, 상기와 같은 디지털 이미저에는 적외선 차단 필터(Infrared Ray Cut Off Filter)가 장착되는데, 상기 적외선 차단 필터는 디지털 이미저로 도달하는 가시광선(Visible)만을 투과시켜 광학적인 이미지 정보를 전기신호로 바꾸어 주고, 적외선은 반사 혹은 흡수하여 디지털 이미저인 CCD 또는 CMOS에 적외선이 도달되지 못하도록 해주는 역할을 하며, 그 두께는 주로 0.05mm 및 0.4mm 또는 그 이상으로 만들어지고, 그 형상은 디지털 이미저가 설치되는 제품의 설치부 형상에 따라 원형 또는 사각 및 그 외 다양한 형상으로 만들어진다.On the other hand, such an imager is equipped with an infrared ray cut off filter (Infrared Ray Cut Off Filter), the infrared cut filter transmits only visible light (Visible) reaching the digital imager to convert the optical image information into an electrical signal Infrared rays are reflected or absorbed to prevent infrared rays from reaching the digital imager CCD or CMOS, and the thickness is mainly made of 0.05mm and 0.4mm or more, and the shape is installed by the digital imager. Depending on the shape of the installation part of the product to be made of round or square and other various shapes.
이와 같은 적외선 차단 필터의 제조공정을 도 1 을 통해 살펴보면 다음과 같다.Looking at the manufacturing process of such an infrared cut filter as shown in FIG.
즉, 적외선 차단 필터의 원판이 소정의 형상과 크기로 가공되어 완성품이 되는 과정을 단계별로 보면, In other words, if the original plate of the infrared cut filter is processed into a predetermined shape and size to become a finished product step by step,
60W의 백열등이나 삼파장을 이용하여 적외선 차단 필터의 원판 표면에 흠집 이 있거나 이물질 등이 부착되어 있는지 파악하는 원판의 표면 검사 단계와;A surface inspection step of a disc using a 60 W incandescent lamp or a three-wavelength to determine whether the disc surface of the infrared cut filter is scratched or foreign matter is attached;
접착력이 강한 테이프를 원판의 5곳 이상 지점에 붙였다가 떼어내면서 코팅막의 박리현상을 검사하는 원판의 코팅막 검사 단계와;A coating film inspection step of inspecting a peeling phenomenon of the coating film while attaching and detaching the adhesive strong tape to five or more points of the disk;
원판의 크기를 고려하여 광학용 유리칼로 원판을 등분하되 등분되는 수가 많아질 수록 자재의 낭비가 많아지므로 최소한의 등분으로 가공하는 원판의 1차 절단가공 단계와;Dividing the original plate with an optical glass knife in consideration of the size of the original plate, but as the number of equal parts increases, waste of materials increases, so that the first cutting processing step of the original plate is processed with a minimum amount;
상기 등분된 원판을 만들고자 하는 형상과 치수에 맞도록 절단기로 절단하여 완성품의 전단계인 다수개의 제품으로 가공하는 원판의 2차 절단가공 단계와;A secondary cutting processing step of the disc for cutting into a plurality of products which are the previous stages of the finished product by cutting with a cutter to match the shape and dimensions to make the equalized disc;
상기 2차 절단가공을 통해 만들어진 제품을 버니어캘리퍼스와 같은 측정공구를 이용하여 전체적인 치수를 확인하는 제품의 치수 확인 단계와;A dimension checking step of checking the overall dimension of the product made through the second cutting process using a measuring tool such as a vernier caliper;
광학용 티슈와 아세톤 등을 이용하여 상기 제품의 양면에 묻어 있는 이물질을 제거하는 제품의 표면 클리닝 단계와;A surface cleaning step of the product for removing foreign matters on both sides of the product by using an optical tissue and acetone;
제품의 표면을 60W 백열등이나 삼파장을 이용하여 육안으로 검사하거나 제품의 사양에 따라 현미경을 이용하여 검사하는 제품의 표면 검사 단계;Inspecting the surface of the product by visual inspection using a 60 W incandescent lamp or a three-wavelength or by using a microscope according to the specification of the product;
를 거쳐 완성품인 적외선 차단 필터가 만들어지는 것이다.After that, the finished infrared cut filter is made.
그러나 상기와 같은 종래 적외선 차단 필터의 제조공정을 보면 적외선 차단 필터의 원판이 원판의 1차 절단가공 단계에 의해 수개로 등분된 상태에서 원하는 형상과 치수에 따라 원판의 2차 절단가공 단계를 통해 완성품 전단계인 다수개의 제품으로 만들어지는 것인데, 종래에는 원판의 1차 절단가공 단계를 통해 만들어진 등분된 원판을 개별적으로 2차 절단가공하여 만들고자 하는 형상과 치수로 된 다수 개의 제품으로 만들기 때문에 제품으로 만들어지기까지 다수회의 반복된 작업공정이 필요하게 되고, 이에 따라 작업시간 및 비용이 많이 소모되어 작업성 및 생산성이 저하되는 문제점이 있었다.However, in the manufacturing process of the conventional infrared cut filter as described above, the final cut through the second cut processing step of the disc according to the desired shape and dimensions in the state that the original plate of the infrared cut filter is divided into several parts by the first cutting step of the original plate. It is made of a plurality of products, which are the previous stages, but conventionally, it is made of a product because it is made of a plurality of products having the shape and dimensions to be made by individually cutting the equally divided disks made through the first cutting process step of the original plates. Repeated work process is required until a number of times, accordingly there was a problem that the work time and cost are consumed and workability and productivity are lowered.
따라서 본 발명의 목적은 상기와 같은 문제점을 해결하기 위한 것으로서, 적외선 차단 필터의 원판을 원하는 치수와 형상으로 가공하여 완성품 전단계인 제품으로 만들때 동시에 많은 수의 제품을 신속하면서 용이하게 만들어 낼 수 있도록 구성함에 따라 전체적인 작업성이 향상될 수 있고, 작업시간이 단축되면서 경제적인 효과와 함께 생산성이 더욱 향상될 수 있도록 한 소형 광학기기에 사용되는 적외선 차단 필터의 제조방법을 제공하는데 있다.Therefore, an object of the present invention is to solve the problems described above, and to process a disc of the infrared cut filter to a desired dimension and shape to make a large number of products at the same time when making a product that is a preliminary step of the finished product. According to the configuration, the overall workability can be improved, and the work time can be shortened, thereby providing a manufacturing method of an infrared cut filter used for a compact optical device that can further improve productivity and economic effects.
이와 같은 본 발명의 목적은 원판의 표면 검사 단계와, 원판의 코팅막 검사단계와, 원판의 1차 절단가공 단계와, 원판의 2차 절단가공 단계와, 제품의 치수 확인 단계와, 제품의 표면 클리닝 단계와, 제품의 표면 검사 단계를 거쳐 완성품인 적외선 차단 필터를 제조함에 있어서,The object of the present invention is to inspect the surface of the disc, the coating film inspection step of the disc, the primary cutting process of the disc, the secondary cutting process of the disc, confirm the dimensions of the product, and clean the surface of the product In the step and the surface inspection step of the product to produce the finished infrared cut filter,
상기 원판의 표면 검사 단계와, 원판의 코팅막 검사단계와, 원판의 1차 절단가공 단계를 수행한 다음,After performing the surface inspection step of the disc, the coating film inspection step of the disc, and the first cutting processing step of the disc,
상기 원판의 1차 절단가공 단계를 거쳐 등분된 다수개의 원판이 서로 적층되도록 하되 각각의 원판 사이에 종이와 함께 파라핀과 송진으로 이루어진 접착수단을 설치한 다음 상기 서로 적층된 다수개의 원판을 가열판에 올려놓아 가열판의 열에 의해 상기 접착수단이 녹으면서 적층된 원판이 서로 고정될 수 있도록 한 가열판 적층 단계와; A plurality of discs divided into equal parts are laminated to each other through the first cutting processing step of the discs, and an adhesive means made of paraffin and rosin together with paper is installed between each disc, and then the plurality of discs stacked on each other are placed on a heating plate. A heating plate laminating step in which the laminated plates are fixed to each other while the adhesive means is melted by the heat of the heating plate;
상기 원판의 가열판 적층 단계를 통해 적층된 원판을 필요로 하는 치수 및 형상에 상응하도록 동시에 절단하여 가공하는 원판의 2차 절단가공 단계와;A secondary cutting processing step of the original plate which is simultaneously cut and processed to correspond to the required size and shape of the original plate laminated by the heating plate lamination step of the original plate;
상기 원판의 2차 절단가공 단계를 통해 가공된 제품을 가열된 상태의 트리클로로에틸렌 용액에 집어넣어 상기 트리클로로에틸렌 용액에 의해 접착수단이 녹으면서 제품을 이루고 있는 각각의 가공된 원판이 분리되도록 한 제품의 세척 단계와;Put the processed product through the secondary cutting process of the disc into the heated trichloroethylene solution so that each processed disc forming the product is separated by melting the adhesive means by the trichloroethylene solution. Washing the product;
상기 제품의 세척 단계에 의해 분리되는 가공된 원판만을 선택해서 골라내는 제품의 분리 단계;Separating the product by selecting and selecting only the processed disc separated by the washing step of the product;
를 순차적으로 수행한 다음 나머지 제품의 치수 확인 단계와, 제품의 표면 클리닝 단계와, 제품의 표면 검사 단계를 거쳐 완성품이 만들어질 수 있도록 구성하므로서 달성되는 것이다.This is achieved by sequentially performing the configuration of the final product after the dimensional confirmation step of the remaining product, the surface cleaning step of the product, and the surface inspection step of the product.
이러한 본 발명은 원판을 일정한 치수와 형상을 가지는 다수개의 적외선 차단 필터로 가공할 때 다수개의 원판을 순차적으로 적층시켜 고정시킨 상태에서 절단하여 가공한 후 적층된 원판을 서로 분리시킴에 따라 단시간에 많은 수량의 적외선 차단 필터 제조할 수 있으며, 작업성 및 생산성을 더욱 향상시킬 수 있으므로 상기 목적을 달성할 수 있는 것이다.
In the present invention, when the disc is processed with a plurality of infrared cut filter having a certain dimension and shape, the plurality of discs are sequentially stacked and cut and processed in a fixed state, thereby separating the stacked discs from each other in a short time. The number of infrared cut filter can be produced, and the above object can be achieved because workability and productivity can be further improved.
이하, 본 발명의 특징을 효과적으로 달성할 수 있는 바람직한 실시 예로서 그 기술구성 및 작용효과를 첨부된 도면에 의하여 상세히 설명하면 다음과 같다.Hereinafter, with reference to the accompanying drawings, the technical configuration and operational effects as a preferred embodiment that can effectively achieve the features of the present invention will be described.
즉, 도 2 은 본 발명에 따른 적외선 차단 필터의 제조공정을 예시한 순서도이고, 도 3 은 본 발명에 따라 적외선 차단 필터의 원판이 종이와 접착수단을 사이에 두고 적층된 상태를 예시한 요부 확대 단면도이며, 도 4a 는 본 발명에 따라 적층된 원판이 사각형상의 제품으로 절단된 상태를 예시한 요부 사시도이고, 도 4b 는 본 발명에 따라 적층된 원판이 원형의 제품으로 절단된 상태를 예시한 요부 사시도이다.That is, Figure 2 is a flow chart illustrating a manufacturing process of the infrared cut filter according to the present invention, Figure 3 is an enlarged main portion illustrating a state in which the original plate of the infrared cut filter is laminated between the paper and the adhesive means in accordance with the present invention 4A is a perspective view illustrating a state in which a laminated disc according to the present invention is cut into a rectangular product, and FIG. 4B is a main part illustrating a state in which a laminated disc according to the present invention is cut into a circular product. Perspective view.
이에 예시한 바와 같이 본 발명은 원판의 표면 검사 단계와, 원판의 코팅막 검사단계와, 원판의 1차 절단가공 단계와, 원판의 2차 절단가공 단계와, 제품의 치수 확인 단계와, 제품의 표면 클리닝 단계와, 제품의 표면 검사 단계를 거쳐 완성품이 되는 적외선 차단 필터의 제조방법에 있어서,As illustrated in the present invention, the present invention provides a surface inspection step of a disc, a coating film inspection step of a disc, a primary cutting process of a disc, a secondary cutting process of a disc, a step of confirming a dimension of a product, and a surface of a product. In the manufacturing method of the infrared cut filter to be a finished product through the cleaning step and the surface inspection step of the product,
상기 원판의 표면 검사 단계와, 원판의 코팅막 검사단계와, 원판의 1차 절단가공 단계를 수행한 다음, After performing the surface inspection step of the disc, the coating film inspection step of the disc, and the first cutting processing step of the disc,
상기 원판의 1차 절단가공 단계를 거쳐 등분된 다수개의 원판(10)을 서로 겹쳐지도록 적층시키되 상기 적층된 각각의 원판(10) 사이에 원판(10)을 보호하기 위한 종이(20)와 원판(10)을 서로 고정시키기 위한 접착수단(30)을 설치하고, 적층된 원판(10)중 아래쪽 저면과 위쪽 상면 또한 종이(20)와 접착수단(30)을 이용하여 보호유리(40)를 설치한 다음 이를 가열판(50)에 올려놓아 상기 가열판(50)의 열에 의해 상기 접착수단(30)이 녹으면서 적층된 각 원판(10)과 종이(20)와 보호유리(40) 가 서로 고정될 수 있도록 한 원판의 가열판 적층 단계와;By stacking the plurality of
상기 원판의 가열판 적층 단계를 통해 적층된 각 원판(10)과 종이(20)와 보호유리(40)를 필요로 하는 치수 및 형상에 상응하도록 절단하여 가공하는 원판의 2차 절단가공 단계와;A secondary cutting processing step of the
상기 원판의 2차 절단가공 단계를 통해 가공된 원판(10)이 적층된 상태로 고정되어 있는 제품(60)을 트리클로로에틸렌 용액에 집어넣어 상기 가공된 원판(10)을 서로 고정시키고 있는 접착수단(30)을 녹여 가공된 원판(10)과 종이(20)와 보호유리(40)가 서로 분리될 수 있도록 한 제품의 세척 단계와;Adhesion means for fixing the processed
상기 제품의 세척 단계에 의해 분리되는 가공된 원판(10)과 종이(20)와 보호유리(40)중 종이(20)와 보호유리(40)는 제거하고 가공된 원판(10)만을 선택해서 골라내는 제품의 분리 단계;Remove the
를 순차적으로 수행한 다음 나머지 제품의 치수 확인 단계와, 제품의 표면 클리닝 단계와, 제품의 표면 검사 단계를 통해 완성품인 적외선 차단 필터가 제조될 수 있도록 한 것을 특징으로 하는 것이다.After sequentially performing the step of confirming the dimensions of the remaining product, the surface cleaning step of the product, and the surface inspection step of the product is characterized in that the finished infrared cut filter can be manufactured.
이러한 본 발명은 적외선 차단 필터의 원판이 여러 단계를 거치면서 일정한 치수와 형상을 가지는 다수개의 적외선 차단 필터로 제작함에 있어서, 상기 원판(10)을 일정한 치수와 형상으로 절단가공할 때 원판(10)을 하나씩 절단가공 하지 않고 다수개의 원판(10)을 적층하여 고정시킨 상태에서 절단가공한 후 간단히 분리시킬 수 있도록 구성함에 따라 단시간에 많은 수량의 적외선 차단 필터를 효과적으로 제작할 수 있도록 한 것이다.The present invention in the manufacture of a plurality of infrared cut filter having a predetermined size and shape while the disc of the infrared cut filter has a plurality of steps, the
즉, 도 2 는 본 발명에 따른 적외선 차단 필터의 제조방법을 단계적으로 나타낸 순서도로서, 제조과정의 특징을 단계별로 살펴보면 다음과 같다.That is, Figure 2 is a flow chart showing a step-by-step manufacturing method of the infrared cut filter according to the present invention, looking at the characteristics of the manufacturing process step by step as follows.
우선 적외선 차단 필터로 제작하기 위한 일정한 크기의 원판이 입고된 후, 코팅의 종류나 두께에 따라 분류되어 보관되어 있다가 주문이 들어오면 주문에 필요한 량의 원판이 원판의 표면 검사 단계로 이동되고, 원판의 표면 검사 단계에서는 60W의 백열등 또는 삼파장 등을 이용하여 원판의 표면에 발생될 수도 있는 흠집 및 오염 또는 이물질의 유무를 검사하게 된다.First, a disk of a certain size for making an infrared cut filter is received, and then classified and stored according to the type or thickness of the coating, and when the order is placed, the quantity of the disk required for the order is moved to the surface inspection step of the disk, In the surface inspection step of the disc, a 60W incandescent lamp or a three-wavelength, etc. is used to check the presence of scratches, contamination or foreign matter that may occur on the surface of the disc.
그리고 상기 원판의 표면 검사 단계를 통과한 원판은 이후 원판 표면에 코팅되어 있는 코팅막의 상태를 검사하는 원판의 코팅막 검사 단계를 거치게 되는데, 상기 원판의 코팅막 검사 단계는 접착력이 강한 테이프를 원판 표면에 붙였다 떼어내면서 원판으로부터 코팅막의 박리 여부를 판단하게 되는 것이며, 통상적으로 원판의 5개 이상의 지점을 선택하여 검사하게 된다.Then, the disc that passed the surface inspection step of the disc is subjected to a coating film inspection step of the disc to examine the state of the coating film coated on the disc surface, the coating film inspection step of the disc was attached to the disc surface with a strong adhesive tape It is to determine whether the coating film is peeled off from the original plate while removing it, and typically five or more points of the original plate are selected and inspected.
그리고 상기 원판의 코팅막 검사 단계를 통과한 원판은 원판의 1차 절단가공 단계를 거치게 되는데, 이는 상기 원판을 가공하기 용이하도록 적절한 크기로 등분을 하기 위한 것이며, 이때 등분되는 수가 많을 수록 낭비되는 부분이 많아지므로 최소한의 갯수로 등분을 하는게 바람직 하다.In addition, the original plate that passes the coating film inspection step of the original plate is subjected to the first cutting processing step of the original plate, which is intended to be equally divided into appropriate sizes so as to easily process the original plate. It is preferable to divide the food into a minimum number of pieces.
여기서 상기 원판의 표면 검사단계와, 원판의 코팅막 검사 단계와, 원판의 1차 절단가공 단계는 종래와 동일하고, 상기 원판의 1차 절단가공 단계를 거친 원판이 원판의 가열판 적층 단계와, 원판의 2차 절단가공 단계와, 제품의 세척 단계와, 제품의 분리 단계를 순차적으로 거치도록 한 것이 본 발명의 특징이며, 상기 제품 의 분리 단계 이후 제품의 치수 확인 단계와, 제품의 표면 클리닝 단계와, 제품의 표면 검사 단계를 거쳐 완성품이 만들어지는 단계 또한 종래와 동일한 것이다.Here, the surface inspection step of the original plate, the coating film inspection step of the original plate, and the first cutting process of the original plate is the same as the conventional one, and the original plate undergoing the primary cutting process of the original plate is a hot plate lamination step of the original plate, It is a feature of the present invention to sequentially pass through the secondary cutting process, the washing step of the product, and the separation step of the product, and after the separation step of the product to confirm the dimensions of the product, the surface cleaning step of the product, The step of producing the finished product through the surface inspection step of the product is also the same as the conventional one.
따라서 본 발명의 특징이라고 할 수 있는 원판의 가열판 적층 단계와, 원판의 2차 절단가공 단계와, 제품의 세척 단계와, 제품의 분리 단계를 상세히 살펴보면 다음과 같다.Therefore, the heating plate lamination step of the original plate, which is a feature of the present invention, the secondary cutting process of the original plate, the washing step of the product, and the separation step of the product are described in detail as follows.
즉, 원판의 1차 절단가공 단계를 통과하면서 가공하기 용이한 크기로 등분된 원판(10)은 원판의 가열판 적층 단계로 이동되는데, 상기 원판의 가열판 적층 단계는 상기 등분된 원판(10)을 서로 겹쳐 적층시키되 하나의 원판(10) 상면에 얇은 종이(20)를 올려놓고, 상기 종이(20) 위에는 접착수단(30)을 도포한 다음 상기 접착수단(30)의 위로 다른 원판(10)을 올려놓고, 상기 다른 원판(10)의 상면 역시 얇은 종이(20)를 올려놓은 다음 접착수단(30)을 도포하는 방식으로 다수개의 원판(10)을 서로 적층시키는 것이다.That is, the
이때 상기 종이(20)의 역할은 서로 겹쳐되는 원판(10)의 표면을 보호하기 위한 것이고, 접착수단(30)은 일정한 온도에 의해 녹을수 있도록 파라핀과 송진을 혼합하여 만든 것이며, 상기와 같이 적층된 제일 아래쪽 원판(10)의 바닥면과 제일 위쪽 원판(10)의 표면에는 적층되는 원판(10)의 상면과 저면을 보호할 수 있도록 상기 종이(20)와 접착수단(30)과 함께 보호유리를 설치한 것이다.At this time, the role of the
그리고 이와 같이 적층된 다수개의 원판(10)은 일정한 온도로 가열된 가열판(50)에 놓여지게 되는데, 상기 가열판(50)의 온도는 적층된 각 원판(10) 사이에 도포되어 있던 접착수단(30)이 녹을 수 있는 온도로서 가열된 가열판(50)에 적층된 원판(10)이 놓여지게 되면 상기 원판(10) 사이 도포된 접착수단(30)이 가열판(50)의 열에 의해 녹게 되고, 이후 상기 가열판(50)이 냉각되면 상기 녹은 접착수단(30) 또한 굳어져 적층된 각 원판(10)이 상기 접착수단(30)에 의해 서로 고정될 수 있는 것이다.And the plurality of
따라서 상기 가열판(50)의 온도가 적층된 각 원판(10)에 전달되는 범위에 상응하도록 적층되는 원판(10)의 갯수가 정해질 수 있는 것인데, 원판(10)의 두께에 따라 차이는 있지만 일반적으로 원판(10)을 16장에서 20장까지 적층하여 고정시킬 수 있다.Therefore, the number of the
이와 같이 원판의 가열판 적층 단계를 통해 다수개로 적층되어 서로 고정된 원판(10)은 원판의 2차 절단가공 단계로 이동되는데, 주문된 치수와 형상에 따라 적층된 상태의 원판(10)이 가공되는 것이며, 이때 상기 가열판(50)이 충분히 냉각되지 않은 상태에서는 적층된 원판(10)의 접착수단(30) 또한 충분히 굳은 상태가 아니므로 이러한 상태에서 절단가공을 할 경우 적층된 원판(10)이 서로 유동되면서 오차가 생기거나 적층된 원판(10)이 서로 분리될 수 있어 가열판(50)이 충분히 냉각시킨 후 절단가공을 하는 것이 바람직 한 것이다.As described above, a plurality of
따라서 상기 원판의 2차 절단가공 단계를 통해 일정한 크기와 형상으로 가공된 원판(10)이 서로 적층된 상태로 고정되어 있는 다수개의 제품(60)은 마치 하나의 덩어리 형태이며, 이러한 덩어리 형태의 제품(60)은 다음 단계인 제품의 세척단계를 통해 서로 분리될 수 있도록 한 것이다.Therefore, the plurality of
즉, 상기 제품(60)을 에틸렌의 수소원자 3개를 염소원자로 치환한 화합물인 트리클로로에틸렌(trichloroethylene) 용액에 집어넣고, 상기 트리클로로에틸렌 용액을 가열하므로서 상기 용액에 의해 가공된 원판(10)을 적층된 상태로 고정시켜주던 접착수단(30)이 녹게되면서 가공된 원판(10)이 각각 분리되는 것이다.That is, the
따라서 상기와 같이 덩어리의 형태였던 제품(60)이 트리클로로에틸렌 용액에 의해 서로 분리되면 다음 단계인 제품의 분리 단계로 이동되는데, 제품의 분리 단계에서는 녹은 상태의 접착수단(30)이 함유된 트리클로로에틸렌 용액은 제거되고, 이에 따라 가공된 원판(10)과 가공된 원판(10) 사이에 설치되었던 종이(20)와 보호유리(40)중 가공된 원판(10)만을 선별하여 분리시키게 된다.Therefore, when the
이후 상기 제품의 분리 단계를 통해 분리되어진 가공된 원판(10)은 종래와 동일한 형상 및 치수를 확인하는 제품의 치수 확인 단계와, 제품의 표면에 생긴 얼룩이나 먼지 또는 이물질을 제거하는 제품의 표면 클리닝 단계와, 제품의 표면을 육안 또는 현미경을 이용한 검사를 하는 제품의 표면 검사 단계를 거쳐 완성품인 적외선 차단 필터로 만들어지는 것이다.Then, the processed
이상과 같이 본 발명의 바람직한 실시 예를 설명하였으나 본 발명은 다양한 변화와 변경 및 균등물을 사용할 수가 있으며, 상기 실시 예를 적절히 변형하여 동일하게 응용할 수 있음이 명확하다. 따라서 상기 기재 내용은 하기 특허청구범위의 한계에 의해 정해지는 본 발명의 범위를 한정하는 것은 아니다.As described above, the preferred embodiment of the present invention has been described, but the present invention may use various changes, modifications, and equivalents. Therefore, the above description does not limit the scope of the invention defined by the limitations of the following claims.
이상에서 상술한 바와 같이 본 발명은 소형 광학기기에 사용되는 적외선 차 단 필터를 제조함에 있어서, 다수개의 원판을 적층시켜 고정시킨 상태에서 주문된 형상 및 치수에 따라 상기 적층되어 고정된 원판을 동시에 가공하므로서, 다량의 적외선 차단 필터를 신속하면서 효과적으로 제작할 수 있는 것이며, 작업성 및 생산성을 더욱 향상시킬 수 있는 것이다.
As described above, according to the present invention, in manufacturing an infrared cut filter used for a small optical device, the laminated and fixed original plates are simultaneously processed according to the ordered shape and dimensions in a state where a plurality of original plates are laminated and fixed. Therefore, a large amount of infrared cut filter can be manufactured quickly and effectively, and workability and productivity can be further improved.
Claims (3)