KR200272111Y1 - Earthenware product structure - Google Patents

Abstract

The present invention is about 0.5% nov (Normal of Volume; normal) of the ceramic products of the heat-resistant base material 10 containing less than about 50% of heat resistance and shrinkage and light weight of feldspar (Petalite) is molded into a mold and baked About 90% of germanium (Ge) sol having a concentration), about 2% of iron chloride (FeCl _{3 ·} 6H ₂ O), about 6% of nickel chloride (NiCl _{2 ·} H ₂ O), and cobalt chloride (COCl _{2 ·)} H ₂ O) about 1%, copper chloride (CuCl _{2 ·} H ₂ O) about 1% mixed and stirred in a highly concentrated composite metal solute solution (21) and roasted by high concentration complex metal solute on the entire surface of the ceramic products Less than 7% germanium (Ge) sol and 3% titanium dioxide (TiO ₂ ) photocatalyst on the upper or inner surface of the ceramic product having a coating layer 20 formed thereon and the highly concentrated composite metal solute coating layer 20 formed on the entire surface thereof. Multi-functional coating agent (31) was prepared by mixing and stirring less than 90% of fluorine resin, followed by heat treatment and dry cooling to coat a highly concentrated composite metal solute. By forming the multi-functional coating layer 30 on the upper surface or the inner surface of the ceramic product having the layer 20 formed thereon, it is excellent in non-adhesion and heat resistance, fluorine resin, germanium (Ge) sol (sol) and titanium dioxide (TiO ₂ ) Highly efficient far-infrared radiation, antibacterial and deodorizing functions prevent the meat from sticking to the surface when grilling meat, preventing the meat from burning and preventing the attachment or penetration of bacteria and significantly destroying the nutrients of meat. It reduces the smell of the meat and gives it a fresh taste.

Description

Heat-resistant pottery product structure {Earthenware product structure}

The present invention relates to a heat-resistant ceramic product structure, and more specifically, high-concentration of a ceramic product in a state of forming a baking mold after forming a heat-resistant material containing less than about 50% of heat resistance and shrinkage and light weight of feldspar (Petalite) Dip the composite metal solute and roast the chaebol to form a highly concentrated composite metal solute coating layer on the entire surface of the ceramic product, and apply a multi-functional coating on the top or the inner surface of the ceramic product having the highly concentrated composite metal solution coating layer formed on the entire surface. As a heat-resistant ceramic product with a multi-functional coating agent coating layer formed on the upper surface or the inner surface of the ceramic product having a high concentration composite metal solution solution coating layer formed by heat treatment and dry cooling,

In particular, it is excellent in non-adhesion and heat resistance when applied to various roasted meat boards, and it has high-efficiency far-infrared radiation, antibacterial and deodorizing functions due to the properties of germanium sol and titanium oxide photocatalyst to prevent meat from sticking to the surface when grilling meat. Not only does it burn, but it also prevents the attachment and penetration of bacteria and significantly reduces the nutrient destruction of meat, and removes the unique smell of meat to make the meat fresh.

Fats contained in meat not only make meat taste, but also cause various adult diseases, and recently, recipes for removing fat from meat have been in the spotlight.

Charcoal-grilled, stone-grilled or barbecue grills, which have been used for a long time, are representative meat recipes that can remove fat.These recipes not only remove oil from the target roast, but also have a deodorant effect that removes fishy smell. Beef, pork, etc. are used to cook meat with a lot of fat and fishy smell.

Among them, charcoal grilling is a method of placing a grill-type iron grill on a charcoal grill and grilling meat on it. This recipe has the advantage of being able to taste fishy and light meat without fumigating with charcoal-specific aroma. A stone grill is a recipe that places a plate or square plate on a stove and bakes meat on it, allowing the meat to be grilled tenderly so that it does not stick to the plate, making the meat soft and removing grease. It was very easy to clean.

However, grill-type iron grills used for charcoal grilling are made by closely weaving a large number of iron slabs in the form of circular grilles, which frequently become dirty as meat is crushed quickly during grilling. It had trouble to use while replacing, and the problem was that the cleaning was also very difficult.

In addition, since various harmful ingredients contained in the alloy material in the iron ash is eluted by hot cooking heat, there is a problem that may cause a fatal adverse effect on the human body when ingesting meat with the eluted epidemic ingredients.

On the other hand, in the case of using the slab, since the meat is baked only by the hot heat of the heated slab, not by direct fire, there is a problem that there is no fumigation effect on the meat and thus it cannot produce a light meat taste.

The present invention was devised in view of the above-mentioned problems, and has excellent non-adhesion and heat resistance, and has high-efficiency far-infrared radiation due to the properties of fluorine resin, germanium (Ge) sol and titanium dioxide (TiO ₂ ) photocatalyst. Antibacterial and deodorizing function prevents meat from sticking to the surface when grilling meat, which prevents meat from burning, prevents bacteria from sticking or penetrates, and significantly reduces the destruction of nutrients. To give the fresh taste of the meat.

1 is an overall perspective view of a roasted meat plate which is a heat-resistant ceramic products of the present invention.

Figure 2 is an enlarged cross-sectional view showing the configuration of the roasting plate is a heat-resistant ceramic products of the present invention.

♣ Explanation of symbols for the main parts of the drawing

10: heat resistant

20: composite metal solute coating layer 21: composite metal solute

30: coating agent coating layer 31: coating agent

To achieve the above object, as shown in FIGS. 1 and 2, a heat-resistant base 10 containing at least about 50% of heat resistance, shrinkage, and light weight of feldspar (Petalite) is molded into a mold. In the first roasted ceramic product, about 90% of germanium (Ge) sol having a value of 0.5% nov (Normal of Volume), about 2% of iron chloride (FeCl _{3 ·} 6H ₂ O), and nickel chloride (NiCl) _{2 ·} H ₂ O) about 6%, cobalt chloride (COCl _{2 ·} H ₂ O) about 1%, copper chloride (CuCl _{2 ·} H ₂ O) about 1% mixed and stirred in a highly concentrated composite metal solute (21) Deep coating and chaebol to form a highly concentrated composite metal solution coating layer 20 on the entire surface of the ceramic products,

Less than 7% germanium (Ge) sol and less than 3% titanium dioxide (TiO ₂ ) photocatalyst on the upper or inner surface of the ceramic product having the highly concentrated composite metal solute coating layer 20 formed on the entire surface of the fluorine resin 90% The multifunctional coating agent 31 is mixed and stirred, and then heat-treated and dried to form the multifunctional coating agent layer 30 on the upper or inner surface of the ceramic product having the highly concentrated composite metal solute solution coating layer 20 formed thereon.

Referring to the manufacturing process of the heat-resistant ceramic products having a heat-resistant ceramic product structure of the present invention as described above in more detail.

[Step 1 (Material Selection Process)]

The heat-resistant material containing about 50% or more of low weight and low shrinkage effect and light weight petrite (Petalite) is selected. The feldspar (Petalite) is a kind of alkali alumina silicate, which is mainly used as a supporting agent to relieve thermal expansion. At around 1000 ° C, it turns into beta spodumene, which hardly changes in volume when heated or cooled.

[2nd process (molding process)]

The selected heat-resistant base is inserted into a mold to mold a ceramic product having a desired shape.

At this time, the mold can be produced in a circular or square or various shapes.

[3rd step (drying process)]

Pottery products molded to the desired shape are naturally dried in air at room temperature and pressure.

[4th process (primary roasting process)]

First firing of the naturally dried pottery product is baked.

[5th process (Deep coating process)]

About 90% of the germanium (Ge) sol having a 0.5% Normal of Volume value, about 2% of iron chloride (FeCl _{3 ·} 6H ₂ O), and nickel chloride (NiCl _{2 ·} H) were prepared. ₂ O) About 6%, cobalt chloride (COCl ₂ H ₂ O), about 1%, copper chloride (CuCl _{2 ·} H ₂ O) about 1% mixed and stirred in a highly concentrated composite metal solute formed and mixed to remove all the ceramic products Allow the highly concentrated complex metal solute to be applied.

[6th process (chaebol roasting process)]

Pottery products coated with the highly concentrated complex metal solute are oxidized and fired at a temperature of about 1240 ° C. for chaebol roasting.

[7th process (coating drafting process)]

A multifunctional coating formed by mixing and stirring less than 7% of 10,000 ppm of germanium (Ge) sol and less than 3% of titanium dioxide (TiO ₂ ) photocatalyst with 90% or more of a fluorine resin is applied to the top surface of the pottery roasted pottery product.

[Step 8 (Product Completion)]

A ceramic product coated with a multi-functional coating on the upper surface is heat-treated at about 430 ° C., dried, cooled and finished.

In this way, heat-resistant ceramic products emit non-tacky, high-efficiency infrared radiation, antibacterial, and deodorant.

Heat-resistant pottery products obtained in the present invention can be applied to kitchen ware products can be applied to a variety of products, such as pots, pots, grilled meat plate, fire plate.

Referring to the embodiment of the present invention as described above are as follows.

Example (Manufacture of roasted meat plate with kitchenware product)

In the present invention, a heat-resistant base containing less than about 50% of heat resistance and shrinkage effect and light weight of feldspar (Petalite) is used to form a curd plate having a desired shape using a molding frame.

The dried meat-dried plate formed as described above is naturally dried at room temperature and atmospheric pressure in air.

The roasted meat plate naturally dried at room temperature and pressure is first roasted in a kiln.

The first roasted roasted meat plate was about 90% germanium (Ge) sol having a value of 0.5% nov (Normal of Volume), about 2% iron chloride (FeCl _{3 ·} 6H ₂ O), and nickel chloride (NiCl ₂ H ₂ O) about 6%, cobalt chloride (COCl _{2 ·} H ₂ O) about 1%, copper chloride (CuCl _{2 ·} H ₂ O) about 1% in a highly concentrated composite metal solute formed by mixing and stirring Tip coating is performed to form a highly concentrated composite metal solution layer.

The high concentration composite metal solute solution is applied to roast the chaebol plate oxidized firing again at a temperature of about 1240 ℃.

The multifunctional coating agent is applied to the upper surface of the chaebol roasted meat plate.

At this time, the multifunctional coating agent is formed by mixing and stirring less than 7% of 10,000 ppm germanium (Ge) sol (sol) and less than 3% of titanium dioxide (TiO ₂ ) photocatalyst with 90% or more of fluorine resin.

Wherein the germanium (Ge) sol (sol) has a high efficiency and emitting far infrared rays, and titanium dioxide (TiO ₂₎ photocatalyst antibacterial and deodorization functions, the fluorine-based resin has a non-tacky.

The dried ceramic plate coated with the multifunctional coating agent is heat-treated again at a temperature of about 430 ° C., and then dried by cooling at room temperature.

The roasted meat plate 100 obtained according to the above embodiment uses a heat-resistant base 10 containing about 50% or more of feldspar (Petalite), which is light and low in heat resistance and shrinkage, as shown in FIG. 2. By forming the highly concentrated composite metal solute 21 is applied to the entire surface of the molded pottery product to form a highly concentrated composite metal solute layer 20.

Multifunctional coating agent 31 is applied to the upper surface or the inner surface of the ceramic product on which the highly concentrated complex metal solution coating layer 20 is formed as described above, followed by heat treatment and dry cooling to form the upper or inner surface of the ceramic product on which the highly concentrated composite metal solution solution coating layer 20 is formed. It will have a structure to form a multi-functional coating agent coating layer (30).

Therefore, when the meat is grilled using the roasted meat plate 100 as described above, the meat to be cooked is prevented from sticking to the upper surface, so that the meat does not burn, prevents the invasion of bacteria, and removes the peculiar smell of meat. The fresh taste of the meat makes it alive,

The present invention is not limited only to the above-described embodiment, and those skilled in the art will be able to easily change or replace.

As described above, the present invention forms a highly concentrated composite metal solute layer coated with a highly concentrated complex metal solute on the entire surface of a ceramic product, and a multi-functional coating agent is applied to the upper surface or the inner surface of the porcelain product having the highly concentrated composite metal solution coated thereon. Next, by heat treatment and dry cooling to form a multi-functional coating layer on the upper or inner surface of the ceramic product having a highly concentrated composite metal solute coating layer, excellent adhesion and heat resistance, fluorine resin and germanium (Ge) sol (sol) and titanium dioxide (TiO ₂ ) By the characteristics of photocatalyst, high-efficiency far-infrared radiation, antibacterial and deodorizing function prevents meat from sticking to the surface when grilling meat, which prevents meat from burning and also prevents bacteria from adhering or penetrating. Significantly reduced destruction and removes the peculiar smell of meat, making the meat fresh. There.

Claims (1)

0.5% nov (Normal of Volume) value for ceramic products in the state of forming a baking mold and forming a heat-resistant body (10) containing about 50% or more of lightweight, low-shrinkage and light-weight feldspar (Petalite) Germanium (Ge) sol having about 90%, iron chloride (FeCl _{3 ·} 6H ₂ O) about 2%, nickel chloride (NiCl _{2 ·} H ₂ O) about 6%, cobalt chloride (COCl _{2 ·} H ₂ O ) 1% and copper chloride (CuCl ₂ H ₂ O) is mixed and stirred in the highly concentrated composite metal solute (21), which is mixed and agitated. The highly concentrated composite metal solute coating layer (20) is coated on the entire surface of the ceramic product. ), Less than 7% germanium (Ge) sol and less than 3% titanium dioxide (TiO ₂ ) photocatalyst on the upper or inner surface of the ceramic product having the highly concentrated composite metal solute coating layer 20 formed on the entire surface of the fluorine resin 90% Heat-resistant pottery is characterized by forming a multi-functional coating agent coating layer 30 on the upper surface or the inner surface of the ceramic product having a highly concentrated composite metal solute coating layer 20 is formed by applying the mixed multi-function coating agent 31 by stirring and heat treatment and dry cooling Product structure.