Abstract

PURPOSE: A manufacturing method of a vitamin solid for a filter interposed in a shower is provided to supply harmless water to the skin and hairs by removing chlorine in tap water, to prevent the skin from aging and to supply moisture to the skin by removing active oxygen causing the aging of the skin. CONSTITUTION: The manufacturing method of a vitamin solid for a filter interposed in a shower comprises the steps of: dissolving powered vitamins in purified water; putting and stirring powered plaster in a mixture containing the vitamins; pouring a mixture mixed with the powered plaster in a frame of an appointed shape; stripping the hardened solid off from the frame after 1-3 minutes; and drying by a warm breeze of 40-70 degrees for 15 minutes or more.

Description

Vitamine solid body for filter in shower apparatus and manufacturing method

본 발명은 샤워기내 삽입되는 필터용 비타민 고형체 및 그 제조방법에 관한 것으로, 보다 상세하게는 수도물 속의 염소를 제거하고 피부미용을 위해 샤워기의 유로에 삽입되는 비타민 고형체에 관한 것이다.The present invention relates to a vitamin solid for a filter inserted into the shower and a method for manufacturing the same, and more particularly to a vitamin solid to be inserted into the flow path of the shower for removing chlorine in the tap water and skin care.

우리나라의 수도물은 치아염소나트륨을 이용하여 염소살균을 하고 있다. 즉,정수장에서 1차 염소처리를 통해 살균과 함께 유기화합물을 제거하고, 가정에 급수하기 직전에 다시 2차 염소를 투여하여 잔류 염소를 보존 유지함으로써 수행성 병원균으로부터의 질병을 예방한다.Tap water in Korea is chlorine sterilized using sodium chlorine. In other words, by removing the organic compound with sterilization through the first chlorine treatment in the water purification plant, the second chlorine is administered again just before water supply to the home to preserve the residual chlorine to prevent diseases from the performance pathogens.

그러나 염소는 할로겐 원소의 하나로서 산화제, 표백제, 소독제 등의 용도로 쓰이는 유독성 물질이며 수도물 속의 염소도 유기 화합물과 반응하여 유기염소 화합물(환경 호르몬)을 생성하여 건강이나 환경에 좋지 않은 영향을 주며, 특히 인체의 피부를 구성하는 피부단백질과 반응하여 파괴함으로써 살결을 거칠게 하고 피부 노화나 각종 피부 드러블의 원인이 되기도 한다.However, chlorine is a toxic substance used as an oxidant, bleach, disinfectant, etc. as a halogen element, and chlorine in tap water reacts with organic compounds to produce organic chlorine compounds (environmental hormones), which have an adverse effect on health or the environment. In particular, it reacts with and destroys the skin proteins that make up the human skin, resulting in rough skin texture and aging or skin bleeding.

또한 염소는 피부와 마찬가지로 모발 단백질을 파괴하고 푸석푸석한 머리결의 원인이 되며, 두피의 건강을 해쳐 탈모의 영향을 줄 뿐 아니라 아토피성 피부염을 악화시키는 원인이 되는 등 문제점이 많았다.In addition, chlorine, like the skin, destroys hair proteins and causes loose hair, and damages the scalp's health, affecting hair loss, and causing atopic dermatitis.

그렇다고 해서 염소성분을 거르기 위해 정수기의 물을 사용하는 것은 경제적이지 못하므로 이에 대한 대책이 요구되어 왔다.However, it is not economical to use water from a water purifier to filter chlorine components, so measures have been required.

이를 개선하기 위하여 샤워기의 내부에 교체가 가능한 필터를 설치하고 이 필터에 고형체의 비타민을 넣어 수도물이 샤워기 내부의 유로를 흐르면서 비타민을 녹임으로써 수도물 속에 첨가되어 있는 염소를 제거함과 동시에 피부보습 등 미용에도 효과를 얻을 수 있도록 한 고안이 본 출원인에 의해 실용신안으로 출원된 바, 비타민C는 수도물 속의 염소를 중화시키고 수도물을 알칼리 상태로부터 피부에 좋은 약산성으로 변화시킨다.To improve this, install a replaceable filter inside the shower, and put a solid vitamin into the filter to remove the chlorine added to the tap by dissolving the vitamin while the tap water flows through the inside of the shower. Designed to achieve the Edo effect has been filed as a utility model by the present applicant, vitamin C neutralizes the chlorine in tap water and changes the tap water from the alkaline state to weak acidity good for the skin.

따라서, 비타민C에 의해 염소가 중화된 상태의 수도물을 이용하여 샤워 및 목욕을 하면 피부와 모발, 두피 등에 좋을 뿐 아니라 피부 보습의 효과도 있게 된다.Therefore, showering and bathing with tap water in a state in which chlorine is neutralized by vitamin C is not only good for skin, hair, and scalp, but also moisturizes the skin.

또한 피부 노화의 원인이 되는 활성산소를 제거하여 피부 노화를 방지할 수 있으므로 비타민C가 들어간 필터를 통해 적극적인 스킨 케어와 모발관리를 할 수 있게 된다.In addition, by removing the free radicals that cause skin aging to prevent skin aging, active skin care and hair care through a filter containing vitamin C.

이를 화학식으로 나타내면,If this is represented by the formula,

C₆H₈O₆(Vitamin-C) + HClO(치아염소산) = C₆H₈O₆H₂O + HCl(염산)C ₆ H ₈ O ₆ (Vitamin-C) + HClO (HCl) = C ₆ H ₈ O ₆ H ₂ O + HCl (HCl)

이다.to be.

그러나 비타민을 함유한 필터를 만들기 위해서는 비타민을 고형체로 만들어야 하고 이 고형체가 수도물의 유속에 의해 적당량이 녹아지어 적절한 비율의 비타민이 수도물속에 포함되도록 하여야 하므로 본 발명에서는 상기와 같이 수도물 속의 염소를 제거하면서도 적당한 비율로 수도물에 녹아지도록 하는 비타민 고형체 및 그 제조방법을 제공하는 데 그 목적이 있다.However, in order to make a filter containing vitamins, the vitamins must be made into solids, and the solids must be dissolved in an appropriate amount due to the flow rate of tap water so that an appropriate proportion of vitamins can be contained in tap water. It is an object of the present invention to provide a vitamin solid and a method for preparing the same, which are dissolved while being dissolved in tap water at an appropriate ratio.

상기와 같은 목적을 달성하기 위하여 비타민 분말을 정수된 물에 적정비율로 넣어 녹이는 단계와, 상기 비타민이 녹은 혼합액에 석고가루를 적정비율로 넣은 후 잘 섞어지도록 저어주는 단계와, 상기 석고가루가 혼합된 액을 일정한 모양의 틀에 붓는 단계와, 1-3분 후 굳어진 고형체를 상기 틀에서 떼어낸 후 40-70℃의 온풍으로 15분 이상 건조시키는 단계로 제조되는 샤워기 필터용 비타민 고형체가 제공된다.In order to achieve the above object, the vitamin powder is dissolved in purified water at an appropriate ratio, and the gypsum powder is stirred in a mixed solution in which the vitamin is dissolved in an appropriate ratio, followed by stirring to mix well. The vitamin solids for the shower filter are prepared by pouring the prepared liquid into a mold of a predetermined shape, and removing the solidified body from the mold after 1-3 minutes and drying it for at least 15 minutes by warm air at 40-70 ° C. Is provided.

이하 본 발명의 샤워기내 삽입되는 필터용 비타민 고형체 및 그 제조방법을 상세히 설명한다.Hereinafter will be described in detail a vitamin solid for a filter and a manufacturing method inserted into the shower of the present invention.

먼저, 약간의 온수가 섞인 정수된 물을 용기에 담고, 비타민C 분말을 정량으로 혼합하여 잘 녹인다.First, put the purified water mixed with some hot water in a container, mix the vitamin C powder in a quantitative manner and dissolve well.

이에 향을 첨가한 후 저어준다.Add flavor and stir.

향이 첨가된 상기 혼합액에 석고(CaSO₄)가루를 조금씩 투여하여 침전되도록한 후 약 1~3분 정도 저어주어 잘 섞어준다.Gypsum (CaSO ₄ ) powder is added little by little to the mixed solution added to the fragrance to stir and stir for about 1 to 3 minutes to mix well.

상기 혼합물을 일정한 틀에 붓는다. 이때 석고가 굳고 있으므로 틀을 미리 준비하여 빨리 넣어야 한다. 이후 약 5~7분이 지나면 굳어진 비타민 고형체를 조심스럽게 틀에서 떼어낸다.Pour the mixture into a regular mold. At this time, the plaster is hardening, so the mold should be prepared in advance and put in quickly. After about 5-7 minutes, carefully remove the solid vitamin solid from the mold.

이때 굳은 고형체가 깨지거나 그 표면에 지문 자국이 나지 않도록 주의하여야 한다.At this time, care should be taken not to crack hard solids or to mark fingerprints on the surface.

틀에서 떼어낸 비타민 고형체를 온풍으로 40~70℃를 가하여 15분 이상 건조시킨다.Vitamin solids removed from the mold are added to 40 ~ 70 ℃ with warm air and dried for at least 15 minutes.

이후 은은한 온풍으로 약 40분 ~1시간 정도 건조시킨다.Then dry for about 40 minutes to 1 hour with a gentle warm air.

이 완성된 비타민 고형체를 진공 포장함으로써 모든 제조공정이 종료된다.All the manufacturing processes are completed by vacuum-packing this completed vitamin solid.

여기서, 상기 혼합물을 붓는 틀의 형상에 따라 비타민 고형체의 모양이 결정되며 필요에 따라 봉형상이나 구형상의 비타민 고형체를 만들수 있다.Here, the shape of the vitamin solid is determined according to the shape of the pouring frame of the mixture, and a rod-shaped or spherical vitamin solid may be made as necessary.

아래의 [표1]은 본 발명에서 제시하는 비타민 고형체의 성분비를 나타낸 것이다.Table 1 below shows the component ratios of the vitamin solids presented in the present invention.

물(H₂O)Water (H ₂ O) 반수석고(CaSO₄½H₂0)Half-water gypsum (CaSO ₄ ½H ₂ 0) 비타민C(C₆H₈O₆)Vitamin C (C ₆ H ₈ O ₆ ) 오렌지향Orange flavor 합계Sum 중량(g)Weight (g) 1717 2424 77 0.70.7 48.7(g)48.7 (g) 혼합율Mixing ratio 34.9%34.9% 49.3%49.3% 14.4%14.4% 1.4%1.4% 진류율Flow rate 31.1%31.1% 52.2%52.2% 15.2%15.2% 1.5%1.5% 46(g)46 (g)

총중량 : 46g(수분 loss : 2.7g)Gross weight: 46g (moisture loss: 2.7g)

이와 같은 방법에 의해 제조된 비타민 고형체를 샤워기 내의 필터에 충진시켜 사용하면 수도물의 유속에 의해 비타민이 조금씩 녹게 되어 물속에 용해되어 있는 염소성분을 제거하게 되므로 순수 무공해 상태의 청결수를 살수하게 되는 것이다.When the vitamin solid produced by the above method is filled and used in the filter in the shower, the vitamin dissolves little by little due to the flow rate of tap water to remove the chlorine component dissolved in the water. will be.

또한, 상술한 예에서와 같이 비타민C 뿐 만 아니라 비타민A 분말을 혼합하여 비타민 고형체를 만들면 노화방지와 주름방지에 크게 효과가 있다.In addition, as in the above-described example, if a vitamin solid is prepared by mixing not only vitamin C but also vitamin A powder, it is greatly effective in preventing aging and preventing wrinkles.

위와 같은 본 발명의 비타민C를 이용한 비타민 고형체는 오렌지 100개 분량의 천연 비타민C를 함유하고 있기 때문에 수도물 속의 염소를 제거하여 피부와 머리카락에 해롭지 않은 물을 제공하며, 피부 노화의 원인이 되는 활성산소를 제거하어 피부 노화를 방지하고 피부 보습에 큰 효과가 있다.Vitamin solids using vitamin C of the present invention as described above contains 100 vitamins of natural vitamin C orange, so it removes chlorine in the tap water to provide water that is not harmful to the skin and hair, and active to cause skin aging. It removes oxygen and prevents skin aging and has a great effect on skin moisturizing.

Claims

Dissolving the vitamin powder in purified water at an appropriate ratio, and adding gypsum powder to the mixed solution of the vitamin at an appropriate ratio and stirring the mixture so that the mixture is well mixed. After pouring, and solidifying the solidified body after 1-3 minutes from the mold and dried in a warm air at 40-70 ℃ 15 minutes or more, the method for producing a vitamin solid body for a shower filter.

For shower filters, characterized in that the purified water, gypsum powder, vitamin powder, fragrance liquid 30-35% by weight: 45-50% by weight: 10-15% by weight: 1-2% by weight and mixed Vitamin solids.