KR101190333B1 - Mineral Composition for Enhancing Hair Growth and Skin Regeneration - Google Patents

Abstract

Five natural minerals composed of SiO2 (silicon dioxide), Al (aluminum), Mg (magnesium), K (potassium), Ca (calcium), and Na (sodium) in green pearls containing natural minerals that are beneficial to the human body Green mud, which contains a large amount of ingredients, is mixed with products such as dyes and shampoos. When used in combination with products such as dyes and shampoos, it absorbs deep into the skin with excellent adsorptive power. It removes blemishes, stimulates blood circulation, and provides oxygen to blood vessel cells to promote skin regeneration, removes caustic wrinkles due to the strong pore-constriction effect of strengthening collagen, and supplies nutrients to the skin membrane To keep the skin healthy and activate the metabolism of the skin to prevent roughening of the skin, relieve wounds and reinforcing the nutrients into the skin It discloses a mineral composition which can further promote hair growth and skin regeneration.
The mineral composition for promoting hair loss and skin regeneration of the present invention is 88.3-91.7 wt% of purified water, preferably 90.0 wt%, green pearl 7.5-10.5 wt%, preferably 9.0 wt%, green mud 0.4-0.6 wt%, Preferably 0.5 weight%, 0.2-0.3 weight% of pearl powders, Preferably 0.25 weight%, 0.2-0.3 weight% of clay, Preferably it consists of 0.25 weight%.

Description

Mineral composition for promoting hair growth and skin regeneration {Mineral Composition for Enhancing Hair Growth and Skin Regeneration}

The present invention relates to a mineral composition, and more particularly, SiO2 (silicon dioxide) and five natural mineral ingredients are mainly composed of green pearl which is used as a main ingredient for skin beauty and as a therapeutic agent for skin diseases by containing natural minerals that are beneficial to the human body. The present invention relates to a mineral composition in which green mud containing a large amount and pearl powder containing 18 amino acids other than calcium are mixed to enhance hair growth and skin regeneration promoting effects.

In general, hair loss is known to occur due to excessive stress, excessive production of DHT due to over-secretion of male hormones, and side effects of long-term use of chemical or oil shampoos.

It is also caused by polluted environments and eating habits. For example, excessive intake of sodium puts stress on the kidneys and heart, causing problems with blood circulation, causing hair loss, and sugary sweet foods can loosen the skin, weakening the scalp and causing hair loss. Spicy foods cause hair loss because the metabolic disorders are accelerated and the scalp ages and the cellular rhythm is reduced.

Therefore, the external medicine mainly applied to the scalp as the hair loss prevention and hair growth promoting agent developed to date has become mainstream, and some internal medicines such as testosterone secretion inhibitors have been sold, but conventionally known hair loss prevention and hair growth promoting products The reality is that it is difficult to use for a long time due to the small effect or severe side effects.

The present invention is to solve the conventional problems as described above, its purpose is to mix with products such as dyes, shampoos, soaps, BB cream and so on deeply penetrated deep into the skin with excellent adsorptive power, cosmetics are deposited in the deep pores The present invention provides a mineral composition capable of promoting hair growth and skin regeneration by removing residues and dead cells, excessive sebum secretion, acne, blemishes, and the like.

In addition, the present invention promotes skin regeneration by stimulating the blood circulation to provide oxygen to the blood vessel cells, remove the caustic wrinkles due to the strong pore contraction effect due to the strengthening of collagen, supplying nutrients to the skin membrane to healthy skin It provides a mineral composition that can promote hair growth and skin regeneration through the reinforcing action to prevent roughness of the skin, relieve wounds and permeate various nutrients to the skin by activating the metabolism of the skin.

The mineral composition for promoting hair loss and skin regeneration of the present invention for achieving the above object is purified water 88.3-9.7% by weight, green pearl 7.5-10.5% by weight, green mud 0.4-0.6% by weight, pearl powder 0.2-0.3% by weight And 0.2 to 0.3% by weight of clay.

In addition, the mineral composition is preferably made by mixing 90.0% by weight of purified water, 9.0% by weight of green pearl, 0.5% by weight of green mud, 0.25% by weight of pearl powder, and 0.25% by weight of clay.

The present invention having the above-described characteristic constitution includes SiO 2 (silicon dioxide) component, Al (aluminum), Mg (magnesium), K (potassium), and Ca (calcium) in green pearls containing natural minerals that are beneficial to the human body. Green mud containing 5 natural minerals consisting of Na (sodium) is mixed to promote far-infrared radiation of SiO2 (silicon dioxide) component, removal of wastes and sebum in skin, and to promote metabolism of Al (aluminum) component. Efficacy, waste excretion of Mg (magnesium) component, collagen binding effect, hormone secretion promoting effect of K (potassium) component, nerve function promoting effect of Ca (calcium) component, body tissue formation, skeletal strengthening effect of Na (calcium) component, Na ( Sodium) component of the body fluid, osmotic pressure control, to increase the effect of balancing the balance between the electrolyte in the body, thereby resulting in the effect of further promoting hair growth and skin regeneration.

In addition, the present invention is supplemented by 18 kinds of amino acids contained in the pearl powder in a very small amount of amino acids in green pearl and green mud to prevent hair damage, scalp irritation prevention, new hair root cells It can supplement hair loss prevention functions such as activation, and white clay softens dark green color by green pearl and green mud, and supplements SiO2 (silicon dioxide) component of green pearl and green mud to improve hair growth and skin regeneration. There is an effect to further increase.

Hereinafter, the preferred embodiment of the present invention will be described in detail.

The mineral composition of the present invention is made by mixing green pearl, which is a natural mud, green mud, which is a volcanic ash, a pearl powder obtained by grinding natural pearls, and white clay, for a long time, in purified water purified by removing impurities.

As for the said purified water, 88.3-91.7 weight% with respect to 100 weight% of mineral composition, Preferably 90 weight% is mixed.

The said green pearl is mixed as a main component of a mineral composition, and 7.5-10.5 weight% with respect to 100 weight% of mineral compositions, Preferably 9.0 weight% is mixed.

Green Pearl is a natural mineral pack containing more than 99% of clean seabed natural mud. Ancient volcanic ash combines with numerous nutrients in the sea, and has been matured for millions of years.There are a lot of minerals, mitamine, rare earth and salt that are essential for our body. It is known to have an excellent effect on skin beauty and skin troubles.

The main ingredients and functions of the green pearl are shown in Table 1 below.

main ingredient Ingredient Specific Functions content Fe (iron) Enzyme transport, energy metabolism, collagen binding, oxygen transport 20% SiO2 (silicon dioxide) Far infrared radiation, skin waste and sebum removal 20% Ca (calcium) Internal tissue formation, skeletal strengthening 10% K (potassium) Promotes Hormone Secretion, Promotes Nerve Function 10% Mg (magnesium) Waste excretion promotion, collagen binding One% Al (aluminum) Metabolism Promotion 10% Na (sodium) Body fluid, osmotic pressure regulation, balance of electrolytes in vitro One% S (sulfur) Purification One% Mn (manganese) Involved in lipid metabolism and bone formation One% Etc 26%

Next, the green mud is 0.4 to 0.6% by weight, preferably 0.5% by weight, based on 100% by weight of the mineral composition.

Green mud is a mineral produced by volcanic ash and lava from volcanic eruptions that has been deposited in the sea for a long time, and then raised to land due to crustal changes. It is a mineral with high concentration of natural minerals and used as a cosmetic and beauty material. The components are shown in Table 2 below.

SiO2 (silicon dioxide) 61.5% Ti (titanium) 0.3% Al (aluminum) 20.1% K (potassium) 4.5% Mg (magnesium) 4.7% Na (sodium) 1.1% Fe (iron) 7.1% Ca (calcium) 0.7%

As in the above main components, the green mud contains a large amount of SiO 2 (silicon dioxide). Therefore, among the major components of green pearl, the content of insufficient SiO2 (silicon dioxide) is further increased, thereby increasing the skin elasticity due to SiO2 (silicon dioxide), that is, increasing skin elasticity, moisturizing, and cation exchange method. It will further improve the supply, excellent hydrophilicity, pore reduction and acne soothing.

Next, the pearl powder is 0.2 to 0.3% by weight, preferably 0.25% by weight with respect to 100% by weight of the mineral composition.

Generally, pearl contains about 20 kinds of minerals and various physiologically active substances, so it absorbs human body very fast. Soluble in water keeps skin weakly acidic, enhances immunity of skin, prevents skin aging, moisturizing, blood circulation, It promotes cell regeneration, and has an excellent effect of clearing and clearing skin by whitening and washing. In particular, it treats senile blemishes, freckles, and pimples, and it is used for anti-inflammatory and fleshy skin where the skin is dry and rough, prevents skin aging, and where wounds do not heal well.

In particular, natural pearls contain 18 kinds of amino acids besides calcium, so the metaonine component of the amino acid has the function of preventing hair loss. Therefore, among the components of green pearl or green mud, it plays a role of improving the hair loss prevention function by supplementing the extremely weak amino acid component.

Subsequently, the said clay is 0.2-0.3 weight% with respect to 100 weight% of mineral compositions, Preferably 0.25 weight% is mixed.

White clay, also called kaolin, is called kaolin in our country. The clay contains 78% of SiO2 (silicon dioxide), so it has excellent whitening effect. Therefore, while weakening the dark green color by the green pearl and green mud, and serves to supplement the SiO2 (silicon dioxide) component of the green pearl.

This mineral composition is composed of SiO2 (silicon dioxide) component in green pearls containing natural minerals beneficial to the human body, and Al (aluminum), Mg (magnesium), K (potassium), and Ca (calcium), which are five natural mineral components. And green mud containing Na (sodium) in a large amount to remove impurities, cosmetic residues and dead cells, and excessive sebum secretion that penetrate deep into the skin with the excellent adsorption power of SiO2 (silicon dioxide). Efficacy in purifying acne and blemishes while rinsing, stimulating blood circulation of Al (aluminum) component, providing oxygen to blood vessel cells, helping skin regeneration, and strengthening collagen of Mg (magnesium) component. Due to the strong pore contraction effect, the lifting effect removes and spreads wrinkles that are not deeply spotted, and it nourishes the skin membrane of K (Potassium) ingredient and makes the skin healthy. It activates the skin metabolism of Ca (calcium) ingredients, prevents roughening of the skin and reduces wounds, and enhances the reinforcing function of injecting various nutrients of Na (sodium) into the skin.

In addition, the pearl powder contains a large amount of amino acids contained in green pearl and green mud, and the amino acid metaonine prevents hair loss, scalp irritation, and hair loss prevention by activating new hair root cells. In addition, the white clay softens the dark green color by green pearls and green muds, and at the same time, supplements the SiO 2 (silicon dioxide) component of green pearls and green muds to further increase its efficacy.

The mineral composition of the present invention was variously prepared as Examples and Comparative Examples to examine the efficacy.

≪ Example 1 >

After removing impurities, 90.0% by weight of purified water, 9.0% by weight of green pearl, 0.5% by weight of green mud, 0.25% by weight of pearl powder, and 0.25% by weight of clay were mixed with a mixer for 24 hours to prepare a mineral composition. It was used in combination with a conventional dye. At this time, the mixing ratio of the dye and the mineral composition was 10: 1.

<Example 2>

After removing impurities, 88.3 wt% of purified water, 10.5 wt% of green pearl, 0.6 wt% of green mud, 0.3 wt% of pearl powder, and 0.3 wt% of clay were mixed with a mixer for 24 hours to prepare a mineral composition. It was used in combination with a conventional dye. At this time, the mixing ratio of the dye and the mineral composition was 10: 1.

<Example 3>

After removing impurities, 91.7% by weight of purified water, 7.5% by weight of green pearl, 0.4% by weight of green mud, 0.2% by weight of pearl powder, and 0.2% by weight of clay were mixed with a mixer for 24 hours to prepare a mineral composition. It was used in combination with a conventional dye. At this time, the mixing ratio of the dye and the mineral composition was 10: 1.

&Lt; Comparative Example 1 &

After removing impurities, 87.6% by weight of purified water, 11% by weight of green pearl, 0.7% by weight of green mud, 0.35% by weight of pearl powder, and 0.35% by weight of clay were mixed with a mixer for 24 hours to prepare a mineral composition. It was used in combination with a conventional dye. At this time, the mixing ratio of the dye and the mineral composition was 10: 1.

Comparative Example 2

After removing impurities, 92.4% by weight of purified water, 7% by weight of green pearl, 0.3% by weight of green mud, 0.15% by weight of pearl powder, and 0.15% by weight of clay were mixed with a mixer for 24 hours to prepare a mineral composition. It was used in combination with a conventional dye. At this time, the mixing ratio of the dye and the mineral composition was 10: 1.

<Example 4>

After removing impurities, 90.0% by weight of purified water, 9.0% by weight of green pearl, 0.5% by weight of green mud, 0.25% by weight of pearl powder, and 0.25% by weight of clay were mixed with a mixer for 24 hours to prepare a mineral composition. It was mixed with a normal shampoo liquid and used. At this time, the mixing ratio of the shampoo liquid and the mineral composition was 10: 1.

<Example 5>

After removing impurities, 88.3 wt% of purified water, 10.5 wt% of green pearl, 0.6 wt% of green mud, 0.3 wt% of pearl powder, and 0.3 wt% of clay were mixed with a mixer for 24 hours to prepare a mineral composition. It was mixed with a normal shampoo liquid and used. At this time, the mixing ratio of the shampoo liquid and the mineral composition was 10: 1.

<Example 6>

After removing impurities, 91.7% by weight of purified water, 7.5% by weight of green pearl, 0.4% by weight of green mud, 0.2% by weight of pearl powder, and 0.2% by weight of clay were mixed with a mixer for 24 hours to prepare a mineral composition. It was mixed with a normal shampoo liquid and used. At this time, the mixing ratio of the shampoo liquid and the mineral composition was 10: 1.

&Lt; Comparative Example 3 &

After removing impurities, 87.6% by weight of purified water, 11% by weight of green pearl, 0.7% by weight of green mud, 0.35% by weight of pearl powder, and 0.35% by weight of clay were mixed with a mixer for 24 hours to prepare a mineral composition. It was mixed with a normal shampoo liquid and used. At this time, the mixing ratio of the shampoo liquid and the mineral composition was 10: 1.

&Lt; Comparative Example 4 &

After removing impurities, 92.4% by weight of purified water, 7% by weight of green pearl, 0.3% by weight of green mud, 0.15% by weight of pearl powder, and 0.15% by weight of clay were mixed with a mixer for 24 hours to prepare a mineral composition. It was mixed with a normal shampoo liquid and used. At this time, the mixing ratio of the shampoo liquid and the mineral composition was 10: 1.

In the case of the dyeing agent prepared by the above Examples and Comparative Examples, the dyeing once every 30 days to see the results after one year, in the case of the shampoo, the hair was washed once daily to see the results after one year. The results as shown in the table below were obtained.

division
dye Hair growth Scalp regeneration Dyeing Function Example 1 Promotion Promotion maintain Example 2 Promotion Promotion Slightly reduced Example 3 Lack of acceleration Lack of acceleration maintain Comparative Example 1 Promotion Promotion Very reduced Comparative Example 2 Very poor Very poor maintain

division
Shampoo Hair growth Scalp regeneration Shampoo function Example 4 Promotion Promotion maintain Example 5 Promotion Promotion Slightly reduced Example 6 Lack of acceleration Lack of acceleration maintain Comparative Example 3 Promotion Promotion Very reduced Comparative Example 4 Very poor Very poor maintain

As can be seen from Table 3, in the case of Example 1, it is possible to improve the hair growth and scalp regeneration while maintaining the dye function, it was found that the mixing amount of minerals in the purified water was made to the optimum composition ratio. In the case of Example 2, although the ratio of minerals to the purified water was slightly increased, the hair growth and scalp regeneration promotion were improved, but the original function of the dye was found to be slightly reduced. As the proportion of minerals decreased slightly, the dye function remained intact, but the effect of promoting hair growth and scalp regeneration was slightly insufficient.

On the other hand, as in the case of Comparative Example 1, as the ratio of minerals to the cleansing water increased more than the set range, it was possible to improve hair growth and scalp regeneration, but the original function of the dye was very difficult to apply, In the case of Comparative Example 2, the original function of the dye was maintained as the ratio of minerals to the purified water was lower than the set range, but the hair growth and scalp regeneration promoting efficacy was very weak and difficult to apply.

In addition, as can be seen from Table 4, in the case of Example 4, it is possible to improve hair growth and scalp regeneration while maintaining the function of the shampoo liquid, so that the mixing amount of minerals with purified water was made to the optimum composition ratio. Could know. In the case of Example 2, although the ratio of minerals to the purified water was slightly increased, it was possible to improve hair growth and scalp regeneration, but the original function of the shampoo liquid was found to decrease slightly. As the ratio of minerals slightly decreased, the original function of the shampoo liquid was maintained, but the effect of promoting hair growth and scalp regeneration was slightly insufficient.

On the other hand, as in the case of Comparative Example 3, as the ratio of minerals to the cleansing water increased more than the set range, it was possible to improve hair growth and scalp regeneration, but the original function of the shampoo solution was very difficult to apply In the case of Comparative Example 2, the original function of the shampoo liquid was maintained as the ratio of the mineral to the purified water was lower than the set range, but the hair growth and scalp regeneration promoting efficacy was very weak and difficult to apply.

It is to be understood that both the foregoing general description and the following detailed description of the present invention are exemplary and explanatory and are intended to be illustrative of the present invention and not to be construed as limiting the scope of the present invention as defined by the appended claims. It will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the invention as defined by the appended claims.

Claims (2)

88.3-91.7 wt% purified water, 7.5-10.5 wt% green pearl, 0.4-0.6 wt% green mud, 0.2-0.3 wt% pearl powder, 0.2-0.3 wt% clay Cosmetic composition for promoting hair growth and scalp regeneration. The method of claim 1, wherein the purified water is 90.0% by weight, the green pearl is 9.0% by weight, the green mud is 0.5% by weight, the pearl powder is 0.25% by weight, the clay is made by mixing 0.25% by weight Cosmetic composition for promoting hair growth and scalp reproduction containing a mineral composition to.