KR20010109859A - A fine wool like yarn with latent crimp - Google Patents

A fine wool like yarn with latent crimp Download PDF

Info

Publication number
KR20010109859A
KR20010109859A KR1020000030546A KR20000030546A KR20010109859A KR 20010109859 A KR20010109859 A KR 20010109859A KR 1020000030546 A KR1020000030546 A KR 1020000030546A KR 20000030546 A KR20000030546 A KR 20000030546A KR 20010109859 A KR20010109859 A KR 20010109859A
Authority
KR
South Korea
Prior art keywords
yarn
area
crimp
polymer
latent
Prior art date
Application number
KR1020000030546A
Other languages
Korean (ko)
Other versions
KR100624369B1 (en
Inventor
윤준영
조대현
Original Assignee
구광시
주식회사 코오롱
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 구광시, 주식회사 코오롱 filed Critical 구광시
Priority to KR1020000030546A priority Critical patent/KR100624369B1/en
Publication of KR20010109859A publication Critical patent/KR20010109859A/en
Application granted granted Critical
Publication of KR100624369B1 publication Critical patent/KR100624369B1/en

Abstract

본 발명은 고유점도 특성 또는 열수 수축율이 서로 상이한 2종의 열가소성 폴리머(A,B)들이 사이드 바이 사이드(Side by side) 형태로 복합방사된 소모조 잠재 권축사에 관한 것으로서, 멀티필라멘트 다발을 구성하고 있는 모노필라멘트 내 열가소성 폴리머들의 면적구성비(A면적 : B면적)가 2:8 ~ 8:2인 것을 특징으로 한다. 본 발명은 모노필라멘트 들의 권축형태가 서로 상이하여 직편물 제조시 외관이 천연섬유처럼 자유스럽고, 반발탄성, 신축성, 드레이프성, 볼륨감이 우수하다.The present invention relates to a latent tank potential crimp yarn in which two kinds of thermoplastic polymers (A, B) having different intrinsic viscosity characteristics or hydrothermal shrinkage rates are different from each other in the form of side by side, constitute a multifilament bundle. The area composition ratio (area A: area B) of the thermoplastic polymers in the monofilament is characterized in that 2: 8 ~ 8: 2. The present invention is different in the crimped form of the monofilaments, the appearance is free when natural fabrics, such as natural fibers, resilience, elasticity, drape, excellent volume feeling.

Description

소모조 잠재 권축사 {A fine wool like yarn with latent crimp}Worn Tank Lay Downs {A fine wool like yarn with latent crimp}

본 발명은 직편물 제조시 외관이 자연스러우며 반발탄성, 신축성, 드레이프성, 볼륨감 등이 우수한 소모조 잠재 권축사에 관한 것이다.The present invention relates to a waste tank potential crimping yarn that is natural in appearance during fabric production and has excellent resilience, elasticity, drape, volume, and the like.

소모조(Fine wool like) 잠재 권축사는 신합성섬유의 주요한 한 분야를 이루고 있다. 소모조 잠재 권축사를 제조하는 방법으로는 수축율이 상이한 2종 이상의 원사를 가연 및 열처리하는 복합 사 가공 방법, 이성분 폴리머를 혼합방사하는 방법, 이성분 폴리머를 편심형 또는 접합형으로 복합 방사하는 방법 등이 있다.Fine wool like potential crimps form a major field of new synthetic fibers. As a method for producing a spent tank latent crimping yarn, a composite yarn processing method of combusting and heat treating two or more kinds of yarns having different shrinkage rates, a method of mixed spinning of two-component polymers, and a composite spinning of two-component polymers in an eccentric or bonded manner Method and the like.

먼저, 상기 복합 사 가공방법은 신장 특성 차이가 큰 2종 이상의 원사를 가연 복합한 후 이들 원사의 신장 회복력 차이를 이용하는 방법이다. 즉 가연 영역에서의 변형율과 해연후 잔류 변형율의 차이를 이용하는 방법이다.First, the composite yarn processing method is a method of using two or more kinds of yarns having a large difference in elongation characteristics, and then using the difference in the resilience of these yarns. In other words, the difference between the strain in the flammable region and the residual strain after disintegration.

가장 대표적인 방법으로 연신사와 자발 신장사를 합가연 하는 방법으로, 이 경우 변사인 자발 신장사가 상대적으로 심하게 변형되면서 심사인 연신사와 혼섬교락된 2층 구조의 복합 가연사가 제조된다.The most representative method is a method of combining twisted yarn and spontaneous elongated yarn. In this case, the spontaneous elongated yarn, which is a variant, is relatively deformed to produce a composite twisted yarn having a two-layered composite twisted yarn mixed with the examiner drawn yarn.

또다른 복합 사 가공방법으로는 자발 권축사에 연신사를 과공급하여 3층 구조사를 제조하는 방법, 연신사와 캐치온 가염사나 원착사를 가연, 복합하여 다층 구조의 혼색 권축사를 제조하는 방법, 식연사나 다중 다형사를 가연하거나 선연후 가연하여 단구간에서 랜덤한 원사길이 차이가 존재하며 수축 및 염착특성 차이가 발생되는 소모조 다층 구조사를 제조하는 방법 등이 있다.Another method for processing a composite yarn is to overfeed the spun yarn to spontaneous crimping yarns to produce a three-layer structured yarn, a method of producing a multi-layer mixed-colored crimping yarn by combusting and compounding the stretched yarns and the catch-on salted yarn or the original yarn, There is a method of manufacturing a multi-layered multi-layered yarn in which short yarn lengths are randomly varied in short sections by adding or twisting food or multi-polymorph yarns.

이러한 복합 사 가공 방법으로 소모조 잠재 권축사를 제조하는 경우 최소한 2종 이상의 원사를 각각 제조해야 하고, 그 이후에 이들의 가연, 합사, 연사하는 공정 등이 필요하여 공정이 복잡하고 제조원가가 상승하는 문제가 있다. 아울러 제조된 원사의 신축특성이 낮아 일반 자켓류와 같이 헐렁한 스타일의 의류용으로 용도가 한정되는 문제도 있다. 또한 2종의 원사를 합사해야하므로 직물의 편물이나 경편 등으로 용도를 확대 적용하기도 어렵다.When manufacturing latent tank crimps using such a composite yarn processing method, at least two or more kinds of yarns must be manufactured, and afterwards, the process of combusting, weaving, twisting, etc. is complicated, which leads to complicated process and increased manufacturing cost. there is a problem. In addition, there is a problem that the use is limited to the loose style of clothing, such as general jackets because of the low elastic properties of the manufactured yarn. In addition, since two types of yarn must be spliced together, it is difficult to expand the application to knitting or warp knitted fabrics.

한편, 잠재 권축사 개발에는 양모의 권축기구가 많이 참작되고 있다. 일본 특개평 2-22141호 및 특개평 2-22145호에서는 이(異)성분 폴리머를 혼합방사하여 잠재 권축사를 제조하는 방법이 기재되어 있고, 일본 특개평 4-136209호 등에서는 이(異)성분 폴리머를 접합형(사이드 바이 사이트 타입) 또는 편심형으로 복합방사 하여 잠재 권축사를 제조하는 방법이 기재되어 있다.On the other hand, the crimping mechanism of wool is taken into consideration in the development of a potential crimp. Japanese Laid-Open Patent Publication Nos. 2-22141 and 2-22145 disclose a method for producing latent crimp yarn by mixing and spun bicomponent polymers, and in Japanese Laid-Open Patent Publication No. 4-136209 and the like. A method of producing latent crimping yarns by complex spinning of component polymers in a bonded (side bisite type) or eccentric type is described.

이와 같은 혼합방사 또는 복합방사 방법은 복합 사 가공 방법에 비해 잠재 권축사의 신축 특성을 향상시킬 수 있는 장점이 있다.Such mixed spinning or composite spinning method has the advantage of improving the stretch characteristics of the potential crimping yarn compared to the composite yarn processing method.

종래에는 이성분 폴리머를 접합형(Side by side)으로 복합 방사하여 잠재 권축사를 제조하는 경우 연신 후 수축율차이 또는 열수축율 차이를 최대화 하여 권축 특성을 향상시킬 목적으로 모노필라멘트 단면내 상기 이성분 폴리머들의 면적비가 도 1과 같이 동일하게 하였다.Conventionally, when a latent crimp is manufactured by complex spinning of a bicomponent polymer in a side by side, the bicomponent polymer in a monofilament cross section for the purpose of maximizing shrinkage difference or thermal shrinkage difference after stretching to improve crimp characteristics. Area ratio was the same as in FIG.

그러나 상기의 경우 권축형태와 크기가 도 3과 같이 균일하여 직편물 제조시 자연스러운 권축이 일어나지 않고 필라멘트 다발 전체가 한가지 형태로 움직이게 되어 외관상 결점이 발생 하였다.However, in the above case, the crimp shape and size are uniform as shown in FIG. 3, and thus, the whole filament bundle moves in one form without producing a natural crimp.

본 발명의 목적은 이와 같은 종래 기술의 문제점들을 해결하므로서 직편물 제조시 외관이 자연스러우며 반발탄성 등이 우수한 소모조 잠재 권축사를 제조하기 위한 것이다.An object of the present invention is to manufacture a waste crimp potential crimping yarn having a natural appearance and excellent rebound elasticity when manufacturing a knitted fabric while solving the problems of the prior art.

본 발명은 종래 소모조 잠재 권축사 제조를 위해 이성분 폴리머를 사이드 바이 사이드 형으로 등성분 복합 방사할 때 발생되는 여러 문제를 해결하기 위하여 복합방사시 모노필라멘트 단면 내 이성분 폴리머들의 면적구성비를 다양하게 변화시킴으로서 직편물 상에서 자연스러운 권축을 발현하는 소모조 잠재 권축사를 제공하고자 한다.The present invention is to vary the area composition ratio of the bicomponent polymers in the monofilament cross section during the composite spinning in order to solve the various problems caused when the bicomponent polymer in the side-by-side type isotropic composite spinning for the production of latent tanks The present invention seeks to provide a spent tank potential crimp that expresses natural crimps on knitted fabrics.

도 1은 종래 잠재 권축사(사이드 바이 사이드 타입 복합사)의 단면 모식도 이다.1 is a schematic cross-sectional view of a conventional latent crimping yarn (side by side type composite yarn).

도 2는 본 발명 소모조 잠재 권축사의 단면 모식도 이다.Figure 2 is a schematic cross-sectional view of the present invention potential tank crimp.

도 3은 종래 잠재 권축사(사이드 바이 사이드 타입 복합사)의 길이방향 모식도 이다.3 is a longitudinal schematic diagram of a conventional latent crimping yarn (side by side type composite yarn).

도 4는 종래 이수축 혼섬사의 길이방향 모식도 이다.Figure 4 is a longitudinal schematic diagram of a conventional biaxial blended yarn.

도 5는 본 발명 소모조 잠재 권축사의 길이방향 모식도 이다.5 is a longitudinal schematic view of the present invention potable crimp yarn.

※도면 중 주요부분에 대한 부호설명※ Code description of main part of drawing

A : 고유점도 또는 열수 수축율이 상대적으로 높은 열가소성 폴리머A: Thermoplastic polymer with relatively high intrinsic viscosity or hydrothermal shrinkage

B : 고유점도 또는 열수 수축율이 상대적으로 낮은 열가소성 폴리머B: thermoplastic polymer having relatively low intrinsic viscosity or hydrothermal shrinkage

본 발명은 소모조 잠재 권축사에 관한 것이다.The present invention relates to a waste tank potential crimp.

더욱 구체적으로 본 발명은 고유점도 특성 또는 열수 수축율이 서로 상이한 2종의 열가소성 폴리머(A,B)들이 사이드 바이 사이드(Side by side) 형태로 복합방사된 잠재 권축사에 있어서, 멀티필라멘트 다발을 구성하고 있는 모노필라멘트 내 열가소성 폴리머들의 면적구성비(A면적 : B면적)가 2:8 ~ 8:2인 것을 특징으로 하는 소모조 잠재 권축사에 관한 것이다.More specifically, the present invention provides a multifilament bundle in a latent crimp yarn in which two kinds of thermoplastic polymers (A, B) having different intrinsic viscosity characteristics or hydrothermal shrinkage rates are different from each other in the form of side by side composite spinning. It relates to a waste tank potential crimping yarn, characterized in that the area composition ratio (area A: area B) of the thermoplastic polymer in the monofilament is 2: 8 ~ 8: 2.

이하 본 발명을 상세하게 설명한다.Hereinafter, the present invention will be described in detail.

먼저 본 발명은 고유점도 특성 또는 열수 수축율이 서로 상이한 2종의 열가소성 폴리머(A, B)를 사이드 바이 사이드 형태로 복합방사 할 때, 멀티필라멘트 다발을 구성하고 있는 모노필라멘트 내 폴리머들의 면적 구성비(A 폴리머 면적 : B 폴리머 면적)를 도 2와 같이 다양하게(일정하지 않게) 조절 한다.First, the present invention provides an area composition ratio (A) of polymers in monofilament constituting a multifilament bundle when composite spinning two kinds of thermoplastic polymers (A, B) having different intrinsic viscosity characteristics or hydrothermal shrinkage from each other in a side by side form. Polymer area: B polymer area) is adjusted (variably) as shown in FIG.

폴리머들의 면적 구성비는 2:8 ~ 8:2로 하며, 멀티필라멘트 내 열가소성 폴리머들의 전체 면적비는 서로 동일(5:5)하게 한다. 폴리머들의 면적 구성비가 상기 범위를 벗어날 경우 수축율 차이가 너무 심하여 공정성이 나빠지며 원사 물성도 저하된다.The area ratio of the polymers is 2: 8 to 8: 2, and the total area ratio of the thermoplastic polymers in the multifilament is the same (5: 5). If the area composition ratio of the polymers is out of the above range, the shrinkage difference is so severe that the processability is poor and the yarn properties are also lowered.

이때 멀티필라멘트(필라멘트 다발)을 구성하고 있는 전체 모노필라멘트 내에 폴리머 면적 구성비가 5:5인 모노필라멘트의 개수 비율이 40% 이하인 것이 바람직 하다. 상기 개수 비율이 40%를 초과하는 경우에는 권축형태 및 크기가 충분하게 다양화되지 않아 직편물 상에서 자연스러운 권축 발현 효과가 저하 될 우려가 있다.In this case, it is preferable that the ratio of the number of monofilaments having a polymer area composition ratio of 5: 5 in the total monofilaments constituting the multifilament (the filament bundle) is 40% or less. When the number ratio exceeds 40%, the crimp shape and size are not sufficiently diversified, and there is a concern that the natural crimp expression effect on the knitted fabric is lowered.

본 발명에서 사용하는 열가소성 폴리머는 폴리에틸렌테레프탈레이트 등이며, 2종의 폴리머간 고유점도 차이는 0.2 정도 또는 열수 수축율 차이가 10% 이상인 것이 바람직 하다.The thermoplastic polymer used in the present invention is polyethylene terephthalate or the like, and it is preferable that the difference in intrinsic viscosity between the two polymers is about 0.2 or 10% or more.

본 발명의 소모조 잠재 권축사는 모노필라멘트를 구성하는 폴리머(A, B)들의 면적 구성비가 일정 범위내에서 불균일하기 때문에 직편물 상에서 발현되는 권축의 크기와 형태가 도 5와 같이 다양하게 된다. 그 결과 직편물의 외관이 크게 향상되며, 반발탄성 및 신축성 등의 물성도 우수하게 된다.Potential crimps of the consumption tank of the present invention, since the area ratio of the polymer (A, B) constituting the monofilament is non-uniform within a certain range, the size and shape of the crimp is expressed on the knitted fabric is varied as shown in FIG. As a result, the appearance of the knitted fabric is greatly improved, and the physical properties such as resilience and elasticity are also excellent.

본 발명의 원사로 제조된 직편물을 100℃ 이상의 온도로 정련/염색하게 되면 다양한 형태의 루프가 발생하여 제직이나 제편시 발생 할 수 있는 필라멘트간 장력 편차로 인해 루프가 풀어지는 현상을 방지 할 수 있고, 다양한 형태의 루프가 겹쳐져 있어서 염색시 깊은 색조을 얻을 수도 있다.Refining / dying the knitted fabric made of the yarn of the present invention at a temperature of 100 ° C. or more can prevent loops from loosening due to tension variation between filaments that can occur during weaving or knitting. In addition, various types of loops are superimposed so that a deep color tone can be obtained during dyeing.

본 발명에 있어서 원사 및 원단의 각종 물성은 아래와 같은 방법으로 평가하였다.In the present invention, various physical properties of yarn and fabric were evaluated by the following method.

·방사성(%)Radioactivity (%)

미연신사 9kg 드럼을 160개 생산 할 때의 조업성(%)으로 평가 하였다.It evaluated the operability (%) when producing 160 undrawn 9kg drums.

·연신성(%)Elongation (%)

미연신사 3kg 드럼을 보빈으로 연신시 불량 및 절사 발생 빈도율(%)로 구한다.Unstretched 3kg drums are obtained by the percentage of occurrence of defects and cuts when stretching with bobbins.

·균제도(%)· Bacterial system (%)

유스터 밸뉴(Uster value)로 25m/분의 속력으로 시료의 질량변화를 3분간 10회 측정하여 그 평균치로 구한다.The change in the mass of the sample was measured 10 times for 3 minutes at a speed of 25 m / min using the Uster value, and the average value was obtained.

·수축율(%) 및 크림프율(%)Shrinkage (%) and Crimp Rate (%)

데니어 크릴에서 권회수를 10회로 하여 제작한 일정길이(L0)의 실타래를 100℃에서 15분간 열처리 한 후, 흡습지로 물을 제거한 후, 여기에 정하중+초하중을 달아 2분후 실타래 길이를 측정한다(이때 측정 길이를 L1이라고 한다). 계속해서 정하중을 제거하고 3분 후 실타래 길이를 측정한다(이때 측정 길이를 L2라고 한다). 측정값을 아래식에 대입하여 수축율과 크림프율을 구한다.After heat-treating a thread of constant length (L 0 ) made with 10 turns of denier krill for 15 minutes at 100 ° C, remove water with a damp paper, and then measure the length of the thread after 2 minutes with a static load + super load. (The measurement length is called L 1 ). Continue to remove the static load and measure the length of the thread three minutes later (the measurement length is called L 2 ). Substitute the measured value into the following formula to find the shrinkage and crimp rate.

수축율(%) =× 100Shrinkage (%) = × 100

크림프율(%) =× 100Crimp Rate (%) = × 100

여기서 정하중은 데니어당 2g 이고, 초하중은 데니어당 0.04g 이다.Here, the static load is 2g per denier and the super load is 0.04g per denier.

·권축수(CCrimp Number (C 1One 및 CAnd C 22 ))

시료를 단섬유 상태로 분리한 후 0.05g의 하중을 부여하여 단섬유 1인치당 외관 권축수를 측정한다(이때 측정값은 C1이라고 한다). 계속해서 하중을 제거한 상태에서 3분 경과후 단섬유 1인치당 외관 권축수를 측정한다(이때 측정값을 C2라고 한다).After separating the sample into a short fiber state, a weight of 0.05 g is applied to measure the number of appearance crimps per inch of short fiber (the measured value is called C 1 ). Subsequently, after three minutes with no load, measure the number of apparent crimps per inch of short fiber (the measurement is called C 2 ).

·원사 외관Yarn appearance

50인의 평가단을 선정하여 실시예 1과 비교실시예 1 ~ 비교실시예 3에서 각각 제조한 원단 샘플 4개에 대한 품평순위를 비교 평가하여 그 순위를 1~4등으로 구분 하였다.50 evaluation teams were selected to compare the evaluation ranks of four fabric samples prepared in Example 1 and Comparative Examples 1 to 3, respectively, and the rankings were classified into 1 to 4 and the like.

이하 실시예 및 비교실시예를 통하여 본 발명을 더욱 구체적으로 살펴본다. 그러나 본 발명이 아래 실시예에만 한정되는 것은 아니다.Hereinafter, the present invention will be described in more detail with reference to Examples and Comparative Examples. However, the present invention is not limited only to the following examples.

실시예 1Example 1

통상의 방법으로 제조한 고유점도 0.5의 폴리에틸렌테레프탈레이트(폴리머 A)와 고유점도 0.7의 폴리에틸렌테레프탈레이트(폴리머 B)를 모노필라멘트 내 폴리머 성분비가 일정하지 않은 사이드 바이 사이드형으로 280℃의 온도에서 1,350m/분의 방사속도로 복합방사 하고, 이를 100℃의 온도에서 3.4배의 연신비로 연신처리 하여 100데니어 24필라멘트의 잠재 권축사를 제조한다. 상기 24개 모노필라멘트 중 폴리머 A의 면적구성비가 60~80%인 것이 7개, 40~60%인 것이 12개, 20~40%인것이 5개 이다. 이와 같이 제조된 잠재 권축사를 경위사로 사용하여 생지기준 폭 65인치, 경사 10,800본, 위사 100본/인치인 3주자직 직물을 제조하고, 이를 가공하여 폭 44인치의 가공지를 제조한다. 제조한 잠재 권축사 및 가공지의 각종 물성을 평가한 결과는 표 1과 같다.A polyethylene terephthalate (polymer A) having an intrinsic viscosity of 0.5 and a polyethylene terephthalate (polymer B) having an intrinsic viscosity of 0.7, prepared by a conventional method, have a constant side-by-side ratio of polymer components in monofilament at a temperature of 1,350 at 280 ° C. Compound spinning at a spinning speed of m / min, and stretched to 3.4 times the draw ratio at a temperature of 100 ℃ to prepare a potential crimp yarn of 100 denier 24 filaments. Of the 24 monofilaments, the polymer A has an area composition ratio of 60 to 80% of 7, 40 to 60% of 12, and 20 to 40% of 5. Using the latent crimped yarn manufactured as described above, a three-week weaving fabric having a width of 65 inches, a slope of 10,800, and a weft yarn of 100 / inch is manufactured and processed to produce a processed paper having a width of 44 inches. The results of evaluating various physical properties of the manufactured latent crimps and processed paper are shown in Table 1.

비교실시예 1Comparative Example 1

전체 모노필라멘트 24개 중 폴리머 A의 면적 구성비가 80% 이상인 것이 2개, 60~80% 이상인 것이 2개, 60~80% 인 것이 5개, 40~60%인 것이 8개, 20~40%인 것이 6개, 80% 이하인 것이 3개가 되도록 모노필라멘트 내 폴리머 면적 구성비를 변경한 것을 제외 하고는 실시예 1과 동일한 공정 및 조건으로 잠재 권축사 및 가공지를 제조한다. 제조한 잠재권축사 및 가공지의 각종 물성을 평가한 결과는 표 1과 같다.Of the total 24 monofilaments, polymer A has an area composition ratio of at least 80%, two at 60-80%, two at 60-80%, eight at 40-60%, and 20-40% Latent crimps and processed paper were prepared in the same processes and conditions as in Example 1 except that the polymer area composition ratio in the monofilament was changed to 6 and 80% or less. Table 1 shows the results of evaluating various physical properties of the prepared latent livestock houses and processed paper.

비교실시예 2Comparative Example 2

모노필라멘트 24개 모두 폴리머 A의 면적 구성비가 50%가 되도록 모노필라멘트 내 폴리머 면적 구성비를 변경한 것을 제외 하고는 실시예 1과 동일한 공정 및 조건으로 잠재 권축사 및 가공지를 제조한다. 제조한 잠재권축사 및 가공지의 각종 물성을 평가한 결과는 표 1과 같다.All 24 monofilaments were manufactured with the potential crimps and processed paper in the same process and conditions as in Example 1 except that the polymer area ratio in the monofilament was changed such that the area ratio of polymer A was 50%. Table 1 shows the results of evaluating various physical properties of the prepared latent livestock houses and processed paper.

비교실시예 3Comparative Example 3

비등수 수축율이 25%인 40데니어 12필라멘트의 폴리에틸렌테레프탈레이트 원사와 비등수 수축율이 80%인 60데니어 12필라멘트의 폴리에틸렌테레프탈레이트 원사를 공기압 3kg/㎠으로 공기교락 하여 교락수가 30개/m인 100데니어 24필라멘트 원사를 제조한다. 이와 같이 제조된 원사를 경위사로 사용하여 생지기준 폭 65인치, 경사 10,800본, 위사 100본/인치인 3주자직 직물을 제조하고 이를 가공하여 폭 44인치의 가공지를 제조한다. 제조한 원사 및 가공지의 각종 물성을 평가한 결과는 표 1과 같다.A polyethylene terephthalate yarn of 40 denier 12 filaments having a boiling water shrinkage of 25% and a polyethylene terephthalate yarn of 60 denier 12 filaments having a boiling water shrinkage of 80% are air-interlaced at an air pressure of 3 kg / cm 2 and 100 with an interlock of 30 pieces / m. Denier 24 filament yarns are prepared. The yarn manufactured as described above is used as a weft yarn to manufacture a three-woven fabric having a width of 65 inches, a slope of 10,800, a weft yarn of 100 / inch, and processed to produce a processed paper having a width of 44 inches. The results of evaluating various physical properties of the manufactured yarn and processed paper are shown in Table 1.

원사 및 원단 물성Yarn and Fabric Properties 구 분division 실시예 1Example 1 비교실시예 1Comparative Example 1 비교실시예 2Comparative Example 2 비교실시예 3Comparative Example 3 방사성(%)Radioactivity (%) 9696 3232 7575 -- 연신성(%)Elongation (%) 1.21.2 2525 10.310.3 -- 균제도(%)Uniformity (%) 0.590.59 1.71.7 0.620.62 1.531.53 수축율(%)Shrinkage (%) 7.37.3 11.411.4 7.47.4 23.423.4 크림프율(%)Crimp Rate (%) 6363 3232 5656 4242 전축수(C1/C2)Total Axis Number (C 1 / C 2 ) 15/4215/42 5/125/12 13/3513/35 15/3615/36 원단외관Fabric appearance 1위1st 4위4th place 3위3rd place 2위2nd

본 발명은 모노필라멘트 단면 내 열가소성 폴리머들의 면적 구성비가 일정하지 않아 직편물 상에서 발현되는 권축 크기 및 형태가 다양하게 된다. 그 결과 직편물 제조시 외관이 자연스럽고, 반발특성, 신축성, 드레이프성, 볼륨감이 매우 양호하다.In the present invention, the area ratio of the thermoplastic polymers in the monofilament cross section is not constant, and thus the crimp size and shape expressed on the knitted fabric are varied. As a result, the appearance of the knitted fabric is natural, and the resilience, elasticity, drape and volume are very good.

Claims (3)

고유점도 특성 또는 열수 수축율이 서로 상이한 2종의 열가소성 폴리머(A,B)들이 사이드 바이 사이드(Side by side) 형태로 복합방사된 잠재 권축사에 있어서, 멀티필라멘트 다발을 구성하고 있는 모노필라멘트 내 열가소성 폴리머들의 면적구성비(A면적 : B면적)가 2:8 ~ 8:2인 것을 특징으로 하는 소모조 잠재 권축사.In latent crimping yarns in which two kinds of thermoplastic polymers (A, B) having different intrinsic viscosity characteristics or hydrothermal shrinkages are different from each other in the form of side by side, the thermoplastic in the monofilament constituting the multifilament bundle Potential crimp yarn of the consumption tank, characterized in that the area composition ratio (Area A: Area B) of the polymer is 2: 8 ~ 8: 2. 1항에 있어서, 전체 모노필라멘트 내에 열가소성 폴리머들의 면적구성비(A면적 : B면적)가 5:5인 모노필라멘트의 개수 비율이 40% 이하인 것을 특징으로 하는 소모조 잠재 권축사.The worsted crimp yarn according to claim 1, wherein the ratio of the number of monofilaments having an area composition ratio (area A to B area) of 5: 5 in the total monofilaments is 40% or less. 1항에 있어서, 열가소성 폴리머가 폴리에틸렌테레프탈레이트인 것을 특징으로 하는 소모조 잠재 권축사.The latex tank crimping yarn according to claim 1, wherein the thermoplastic polymer is polyethylene terephthalate.
KR1020000030546A 2000-06-03 2000-06-03 A fine wool like yarn with latent crimp KR100624369B1 (en)