KR20010071653A - 항균성과 방취성을 가지는 합포용 내피 직물 및 그 제조방법 - Google Patents
항균성과 방취성을 가지는 합포용 내피 직물 및 그 제조방법 Download PDFInfo
- Publication number
- KR20010071653A KR20010071653A KR1020010036921A KR20010036921A KR20010071653A KR 20010071653 A KR20010071653 A KR 20010071653A KR 1020010036921 A KR1020010036921 A KR 1020010036921A KR 20010036921 A KR20010036921 A KR 20010036921A KR 20010071653 A KR20010071653 A KR 20010071653A
- Authority
- KR
- South Korea
- Prior art keywords
- antibacterial
- fabric
- adhesive
- antimicrobial agent
- deodorizing
- Prior art date
Abstract
본 발명은 항균성과 방취성을 가지는 합포용 내피 직물 및 그 제조방법에 관한 것으로, 더욱 상세하게는 신발, 의류, 정화필터 등을 제조할 때 외피 등에 부착하는 내피에 항균성, 방취성, 살균성을 가지는 환경친화성 무기물질을 접착제와 함께 점적 도포하여 외피와 합포 사용시 살균, 탈취, 항균효과를 얻을 수 있도록 한 항균성과 방취성을 가지는 합포용 내피 직물 및 그 제조방법에 관한 것이다.
Description
본 발명은 항균성과 방취성을 가지는 합포용 내피 직물 및 그 제조방법에 관한 것으로, 더욱 상세하게는 신발, 의류, 정화필터 등을 제조할 때 외피 등에 부착하는 내피에 항균성, 방취성, 살균성을 가지는 환경친화성 무기물질을 접착제와 함께 점적 도포하여 외피와 합포 사용시 살균, 탈취, 항균효과를 얻을 수 있도록 한 항균성과 방취성을 가지는 합포용 내피 직물 및 그 제조방법에 관한 것이다.
일반적으로 신발의 갑피, 안창표면이나 침구류, 의복류 및 공기청정기, 자동차용 에어콘 필터에는 부직포, 면, 나일론 등으로 된 원단 즉 내피가 접착제에 의해 부착 사용된다.
이러한 내피는 직접적으로 사람의 신체에 접촉되거나 사람의 거주공간에 설치되기 때문에 사람의 몸으로부터 발생하는 땀 내지는 외부의 수분을 다량 흡수하게 된다.
따라서, 땀과 수분 그리고 오물이 침투된 외피와 내피를 빠른 시간에 살균, 세척하지 않으면 각종 세균의 번식을 활성화시켜 악취를 발생시키게 되고 더욱이 이와같은 오염물질과 세균류는 사람의 피부에 발생하는 각종 질병의 원인이 되며, 신발류의 경운는 제대로 통풍이 되지 않기 때문에 더욱 심한 악취를 발생시키고 무좀균과 같은 각종 유해한 세균을 증식시키게 되는 문제점이 더욱 크다.
특히, 내피와 외피는 접착제로서 합포되기 때문에 접착제가 내피 표면 또는 외피의 이면에서 불투과성 박막층을 형성하여 투습성과 통기성이 완전히 차단되므로 땀과 수분 등이 내피까지는 통과하나 전기 불투과성 박막층에 의해 차단되어 습한 상태를 지속적으로 유지시키므로서 불쾌감을 주고 세균의 번식이 쉽게 이루어지며 악취의 발생이 가중되는 문제점이 있었다.
본 발명의 목적은 내피의 표면에 접착하는 열가소성 점착제에 살균 또는 항균 및 탈취효과가 탁월한 천연 무기물질을 혼합하여 보존력이 탁월하게 도포하므로서 항균과 탈취효과를 얻을 수 있는 항균성과 방취성을 가지는 내피직물을 제공하는 데 있다.
본 발명의 또 다른 목적은 천연 무기물질을 혼합한 열가소성 점착제를 내피의 표면에 균정하게 점적 도포하여 단위면적당 효율적인 기공면을 보유케하므로서 투습성과 통기성이 부여되는 항균성과 방취성을 가지는 내피직물의 제조방벙을 제공하는 데 있다.
이와같은 목적을 달성하기 위한 본 발명의 내피직물은 내피로 사용되는 기지의 표면에 외피와 합지를 위해 도포되는 점착제와 살균, 항균, 탈취기능을 발휘하는 항균제를 배합한 항균 방취점착제를 점적 도포하고 가열 용융시켜 고착시키는 방법으로 가공처리 됨을 특징으로 한다.
도 1 은 항균 무기물질의 도포예시를 나타낸 본 발명의 내피의 예시도
도 2 는 본 발명의 내피를 외피와 합포한 예시 사시도
<도면의 주요부분에 대한 부호의 설명>
100 : 내피 1 : 기지 2 : 점줄무늬
3 : 외피
이하 본 발명을 실시예에 의거 상세히 설명하면 다음과 같다.
본 발명의 내피직물은 내피(100)을 구성하는 기지(1)의 표면에 저온용 고밀도 분말상태인 열가소성 점착제 90∼97%와 살균성, 항균성, 탈취성, 제습성이 뛰어난 천연 무기물질의 항균제 3∼10%를 혼합하여 점줄무늬(2) 이를 테면 바둑판 모양, 연속 평행사변형 모양, 기타 지그재그 모양 등의 모양이 현출되게 점적상으로 도포하고 가열 용융시켜서 이루어진다.
여기서 열가소성 점착제는 폴리아미드, 폴리에틸렌, 폴리에스터, 폴리프로필렌, 폴리우레탄, EVA, 에틸렌 초산비닐 또는 그 공중합물의 단독 또는 2종 이상이분말상태(300∼1,000 mesh)로서 90∼97% 가 사용되는 데 이는 피도포자재 즉 나일론, 면, 부직포등 기지(1)의 특성에 따라 다양하게 선택 사용된다.
항균제는 살균, 항균 및 탈취효과가 우수한 천연 무기물질로서 견운모 (Sericite), 백운모, 흑운모와 게껍질에서 추출하여 항균제로서 널리 사용되고 있는 키토산이 선택적으로 3∼10%가 혼합된다.
견운모와, 백운모, 흑운모는 미세한 입자로 된 백운모족의 점토광물로서, SoO2, Al2O3, Fe2O3, CaO, MgO, K2O 의 성분으로 조성되어 있으며 이들 성분 함량의 대소의 차이에 따라 서로 구별되는 데 이들은 모두 FINE 세라믹이나 알류미나계의 세라믹 소재로 씌여 왔으나 최근 과학의 발달로, 본 광물에 함유되어 있는 TiO2, Ge, P, K, Na 등의 미네랄이 인체의 각 부분을 활성화 시키고, 이에 따라 인체의 건강유지와 활성을 촉진 또는 증진 시키는 작용을 하는 것으로 밝혀지고 있다. 특히 우리 광산의 흑운모(Biotite), 세리사이트는 그 품위가 매우 높고 중금속등 인체에 해가 있는 성분이 전혀 없을 뿐 아니라 '氣'의 방출과 원적외선의 방사량이 매우 높아 그 이용도는 전래의 일반 세라믹의 개념에서 진일보한 생체의 활성화, 환경 친화적 요소, 건강의 증진에 이르기까지(건축,미용, 환경, 건강 제품) 그 용도가 매우 다양하다.
그리고 흑운모는 그 성상이 백운모와는 달리 검은 색을 띠고 있으나, 백운모(견운모)에 비하여 게르마늄의 함유량이 높고 원적외선의 상온대(39-40℃) 방사율이 0.93-0.95에 이르고 있으며 탈취, 항균, 생체에너지(氣), 열전도율이 매우 높은 등의 기능이 우수한 것으로 알려져 있다.
상기의 열가소성 점착제와 항균제는 소정의 비율로 혼합되어 내피(100)로 사용되는 기지(1)의 표면에 점줄무늬(2)로 균정하게 점적 도포되는 데 상기 항균 점착제를 기지의 표면에 일정량으로 균정한 점적 도포를 위해서는 여러 가지의 방식을 채택할 수 있지만 바람직하게는 미세한 셀의 음각무늬 갖는 엠보스로울이나 미세한 망목의 스크린 로울에 의한 롤 프린터식으로 도포될 수 있다.
예로서, 엠보스 로울 방식을 채택할 경우 셀의 구경, 간격, 인치당 셀의 수를 적정하게 구성하여 사용되는 데 가열 프레스로울을 통과한 기지(1)의 표면에 항균 점착제가 주입되는 엠보스로울을 통과하면서 일정량의 점착제 분말이 균정하게 점적 도포되고 도포된 기지는 히터 등의 가열장치를 통과하여 가열 건조되고 냉각되므로서 일정량의 항균 방취 점착제가 내피(100)의 표면에 점적 도포되는 것이다.
이와같이 항균 방취 점착제가 점적 도포된 내피(100)는 외피(3)와 점착 프레스기에 의해 점착되어 신발, 의류, 침구류, 필터류등 다양한 용도로 사용되는 데 외피와 내피는 이를 접착한 항균 점착제의 점적 도포로서 이루어져 합지작업이 간편하고 특히, 도트의 사이로 통기성과 투습성이 원활히 이루어지게 되므로 악취가 제거되고 항균제의 항균 및 살균작용으로 각종 세균이 제거되므로서 인체에 유익하고 보다 청결한 거주환경을 제공할 수 있는 것이다.
실시예
열가소성 점착제 분말과 천연 광물질로 된 항균제 분말의 혼합 비율을 97:3,95:5, 93:7, 91:9의 4가지 혼합비율로 내피에 균정하게 점적 도포하고 건조후 외피와 열접착으로 합지를 실시하여 공정상의 제약이 있는 지를 조사한 결과 광물질의 항균제의 혼합비가 9% 이상시 도포의 품질과 합지후 접착강도가 떨어질 우려가 있고, 3% 미만시는 혼합시 균등한 혼합이 이루어지지 않을 위험이 내포되어 있어 항균제의 혼합비가 3%에서 9%가 가장 이상적이라는 시험결과가 나왔다.
한편, 본 발명에 따른 실제 작용효과를 검증하기 위한 살균성과 탈취성의 시험이 시행되었다. (의뢰일시 2001. 4. 19. 접수번호 930141-01418)
시험재료는 항균제로서 백운모(Sericite) 9%와 점착제 폴리아미드 91%를 혼합하여 이를 나일론 직물에 도포하여 내피를 제조하고 이를 천연가죽에 합지한 것을 시험재료로 하여 한국원사직물시험연구원에서 실시되었다.
이에 따른 시험결과가 2001. 04. 25일자로 통보되었다.
이 시험결과에 따르면, 항균력을 아래와 같이 두가지 접종균으로 각각 SHAKE FLASK 법으로 시험한 결과 24시간 경과후 약 99.9% 살균력 보유가 입증되었다.
(1) 항균력(Shake flask법) : 세균수/㎖, 세균감소율:%
시험결과
#Blank #1 Sample #2 Sample
초기균수 1.6 ×1051.6 ×1051.6 ×105
24시간후 6.2 ×106<10 <10
감소율(%) 99.9 99.9
* 증가율 : 39배
* 접종균 농도 : 1.6 ±0.1 ×105/㎖
* 비이온 계면활성제 종류 : Tween 80(0.05%)
주) ㆍ시험조건
- 시험균액을 35±1℃에서 24시간 진탕 배양후 균수 측정(진탕회수
150회/분).
- 시료표면적 : 60㎠
- 중화용액 : 인산완충용액(ph 7.0±0.2)
-사용공시균주 : Staphylococcus aureus ATCC 6538
- 시료 : #Blank 일반직물, #1 본발명의 도포직물 국산, #2 이태리
(2) 항균력(Shake flask법) : 세균수/㎖, 세균감소율:%
시험결과
#Blank #1 Sample #2 Sample
초기균수 1.3 ×1051.3 ×1051.3 ×105
24시간후 5.6 ×106<10 <10
감소율(%) 99.9 99.9
* 증가율 : 43배
* 접종균 농도 : 1.3 ±0.1 ×105/㎖
* 비이온 계면활성제 종류 : Tween 80(0.05%)
주) ㆍ시험조건
- 시험균액을 35±1℃에서 24시간 진탕 배양후 균수 측정(진탕회수
150회/분).
- 시료표면적 : 60㎠
- 중화용액 : 인산완충용액(ph 7.0±0.2)
- 사용공시균주 : Escherichia coli ATCC 25922
- 시료 : 상기와 동일
또 탈취율 시험은 가스검지관법으로 암모니아 가스를 사용하여 두가지 방법, 즉, %와 ppm으로 실시하여 5분, 15분, 30분, 60분 단위로 측정하여 최저 97.7%, 최고 98.8%와 최저 10ppm, 최고 5ppm 미만의 탈취율이 입증되었다.
(3) 탈취율(가스검지관법) : (%)
주) ㆍ시료무게 : 100㎠
ㆍ시험가스 : 암노니아가스.
ㆍ탈취율(%) = (Cb - Cs)/Cb ×100.
- Cb : Blank 각 시간 경과후 측정 농도 (ppm)
- Cs : 시료 각 시간 경과후 측정 농도 (ppm).
ㆍ> : ∼ 이상
(4) 탈취율(가스검지관법) : (ppm)
주) ㆍ시험가스 : 암노니아가스.
ㆍ시료무게 : 100㎠
ㆍ> : ∼ 이상
상기의 시험에서 입증되듯이 본 발명의 내피가 외피와 접착되어 제품으로 사용될 경우 점진적으로 시간이 지나면서 탈취효과가 상승되는 것을 알 수 있다.
이와같이 본 발명은 환경친화적이고 인체에 무해한 천연무기물질의 항균제를 열가소성 점착제와 혼합하여 이를 내피에 균등하게 점적 도포하므로서 외피와 합지하여 제품으로 사용시 살균력과 항균력을 가지게 되고 탈취기능이 수행되어 위생적이고, 악취 발생이 억제되며 통기성과 투습성이 매우 우수한 등 그 효과가 매우 크다.
Claims (5)
- 내피(100)로 사용되는 기지(1)의 표면에 점착기능을 발휘하는 열가소성 점착제와, 살균, 항균, 탈취기능을 수행하는 항균제를 소정 비율로 배합한 것을 점줄무늬(2)가 현출되게 균정하게 점적 도포하고 가열 용융시켜서 고착시키는 방법으로 가공처리 함을 특징으로 하는 항균성과 방취성을 가지는 합포용 내피 직물의 제조방법.
- 내피(100)를 구성하는 기지(1)의 표면에 열가소성 점착제와 항균제의 혼합물이 균정하게 점적 도포되고 가열 용융 고착되어 점줄무늬(2)를 현출하는 항균성과 방취성을 가지는 합포용 내피 직물.
- 제 1항 또는 제 2 항에 있어서, 열가소성 점착제가 90∼97%의 비율로 포함되고 천연 무기물질의 항균제가 3∼10%이 비율로 혼합되어 이루어진 것을 특징으로 하는 항균성과 방취성을 가지는 합포용 내피 직물 및 그 제조방법.
- 제 1 항 또는 제 2 항에 있어서, 열가소성 점착제가 폴리아미드, 폴리에틸렌, 폴리에스터, 폴리프로필렌, 폴리우레탄, EVA, 에틸렌 초산비닐 또는 그 공중합물 중에서 선택 사용되는 항균성과 방취성을 가지는 합포용 내피 직물 및 그 제조방법.
- 제 1 항 또는 제 2 항에 있어서, 항균제가 견운모, 백운모, 흑운모, 키토산중에서 선택 사용되는 항균성과 방취성을 가지는 합포용 내피 직물 및 그 제조방법.