KR20000063990A - 일회용 반창고 - Google Patents
일회용 반창고 Download PDFInfo
- Publication number
- KR20000063990A KR20000063990A KR1020000047067A KR20000047067A KR20000063990A KR 20000063990 A KR20000063990 A KR 20000063990A KR 1020000047067 A KR1020000047067 A KR 1020000047067A KR 20000047067 A KR20000047067 A KR 20000047067A KR 20000063990 A KR20000063990 A KR 20000063990A
- Authority
- KR
- South Korea
- Prior art keywords
- woven fabric
- sodium polyacrylate
- tree oil
- aid
- wound
- Prior art date
Abstract
본 발명은 항균 기능을 갖는 고흡수성 일회용 반창고에 관한 것으로, 더욱 상세하게는 지지체층과 그 위에 형성된 점착층과 그 위에 형성된 2 층의 패드부 및 박리지로 이루어진 일회용 반창고에 있어서, 상기 패드부가 소디움폴리아크릴레이트 및 티트리오일을 포함하는 부직포와 그의 표면에 라미네이팅 되어 있는 상처 박리용 필름으로 이루어져 있는 것을 특징으로 하는 일회용 반창고에 관한 것이다. 본 발명에 따른 반창고는 상처에서 분비되는 분비물을 충분히 흡수하고 항균 기능으로 인해 상처의 빠른 치유를 유도하고 위생적으로 사용할 수 있는 효과가 있는 것이다.
Description
본 발명은 항균기능을 갖는 고흡수성 반창고에 관한 것으로, 더욱 상세하게는 가벼운 절상, 찰과상 및 관통상에 사용할 경우, 상처에서 분비되는 분비물을 고흡수성 수지가 충분히 흡수하고, 티트리오일이 항균 기능으로 인해 상처의 소독을 촉진시켜 빠른 치유를 할 수 있는 일회용 반창고를 제공하는 것을 특징으로 한다.
종래의 반창고중 잘 알려진 시판품은, 죤슨 앤드 죤슨(Johnson & Johnson)사의 얇은 스트립(strip), 패취(patch), 스포트(spot), 가소성 스트립 형태의 밴드-에이드(BAND-AID*) 상표 반창고(막대형이 아닌 쿠션 패드를 함유하는) ; 콜게이트-팔몰리브 컴퍼니[Colgate-Palmolive Co.(Kendall)]의 큐리티 큐러드*(CurityCURAD*)" (오우취리스(Ouchless)" 반창고 ; 및 어메리컨 화이트 크로스 래보러토리즈, 인코퍼레이티드(American WhiteCross Laboratories, Inc.)의 스틱-타이트*(STIK-TITE*) 탄성 스트립등이 있다.
상기와 같이 종래에 사용되어 온 일회용 반창고는, 일반적으로 지지체 층과 지지체층 위에 형성되어 상처 부위에 부착될 수 있도록 해주는 점착층과, 점착층 위에 형성되어 상처에서 분비되는 분비물을 흡수해 주는 패드부와 패드부를 덮고 있는 박리지로 구성되어 있다. 그러나, 이러한 종래의 일회용 반창고는 패드부가 가제 혹은 부직포만으로 이루어져 있어 분비물이 누출되거나 이들이 상처에 들러붙는 단점이 있었다. 패드부에 아크리놀, 벤잘코니움클로라이드, 도데실피리딘니움클로라이드 등의 약물이 부가되어 있는 경우에는 멸균작용을 나타낼 수 있으나, 상처부위 분비물이 과량일 때에는 이를 억제할 수 있는 능력이 떨어지고, 약물에 대한 알레르기도 배제할 수 없었다. 일반적인 멸균방법으로는 세균 차단 물질로 제조된 낱개 밀봉 포장 속에 낱개의 지혈 반창고를 넣고 에틸렌 멸균을 행하여 반창고를 사용하려고 할 때까지 멸균상태로 유지시킨다. 이 경우, 사용자는 멸균 포장을 뜯고 반창고를 꺼낸 다음, 2 개의 박리필름을 벗겨내고, 패드 구조물을 상처부분에 고정 시켜 사용하게 된다.
한편, 대한민국 특허 공고 제 95-5335 호에는 패드부에 혈액 응고를 돕는 풀리에틸렌옥사이드를 사용하여 지혈 효과를 증대 시킨 일회용 반창고가 개시되어 있다. 또한, 미합중국 특허 제 3,328,259 호에서는 " 지혈제를 함유하는 상처용 드레싱(Dressing)" 이라는 발명의 명칭으로 카르복시메틸셀룰로이스의 나트륨염을 사용하여 지혈제 함유 상처용 드레싱을 제조하는 방법이 기술되어 있다.
또한, 티트리오일을 사용한 기술은 미합중국 특허 제 5,610,189 호에서와 같이 티펜과 혼합하여 소독제로 사용한 예가 있다. 미합중국특허 제 5,958,420 호에서와 같이 화상치료제로 젤상태의 제형에 티트리오일을 사용한 예와 화상치료제로 티트리오일 혼합물을 이용하는 방법이 미합중국특허 제 5,009,890 호, 제 5,384,125 호, 제 5,529,784 호, 제 5,753,257 호, 제 6,033,675 호에 기술되어 있다.
그러나, 상기와 같은 종래 기술에서는 지혈 효과에만 중점을 두어 반창고를 개발한 결과 상처에서 분비되는 분비물이나 오염물을 흡수하는 능력이 떨어지거나 상처의 소독을 통한 치유에만 중점을 두어 분비물의 흡수가 부족하였다. 이에 본 발명자들은 고흡수성 물질인 소디움폴리아크릴레이트와 티트리오일을 사용하여 종래의 일회용 반창고에 비하여 분비물이나 오염물을 훨씬 빠른 흡수속도로 흡수하고 항균기능을 갖고 상처의 소독 기능을 갖는 일회용 반창고를 완성 할 수 있었다.
다량의 혈액을 흡수할 수 있는 고흡수성 수지인 소디움폴리아크릴레이트와 티트리오일을 함침시킨 층의 2 층으로 구성된 일회용 반창고가 이에 부합되는 효과를 나타낸다는 사실을 알아내어 본 발명을 완성하게 되었다.
따라서, 본 발명의 목적은, 상처에서 배출되는 혈액, 진물, 화농 등의 분비물이나 오염물을 빠르게, 다량 흡수함과 동시에 상처부위의 빠른 치유를 유도하는 다기능 일회용 반창고를 제공 하는 것이다.
이를 위하여 본 발명에서는 지지체층과 그 위에 형성된 점착층과 그 위에 형성된 패드부 및 박리지로 이루어진 일회용 반창고에 있어서, 상기 패드부가 소디움폴리아크릴레이트 및 티트리오일을 포함하는 부직포와 그의 표면에 라미네이팅되어 있는 상처 박리용 필름으로 이루어져 있는 것을 특징으로 한다.
이하, 본 발명의 내용을 보다 상세히 설명한다.
본 발명에 있어서 지지체층의 소재로는 통기성 PVC 필름, 폴리우레탄 필름, 신축성 레이온, 폴리에틸렌, 폴리프로필렌 또는 폴리에스테르를 사용하는 것이 바람직하며, 이의 상부 표면에 의료용 점착제를 도포하여 점착층을 형성시킨다. 의료용 점착제로는 천연 고무, 합성 고무 수지, 아크릴 수지 등에 디펜히드라민, 말레인산클로로페닐아민 등의 항알레르기성 약물을 첨가하여 사용할 수 있다.
본 발명의 특징인 패드부는 소디움폴리아크릴레이트층으로 이루어진 부직포로 된 흡수 패드층과 티트리오일이 함침된 층을 포함하고 있는 부직포와 이의 표면에 라미네이팅되어 있는 상처 박리용 필름으로 구성된다. 상기 부직포는 비스코스레이온 60∼100%의 부직포나 폴리에스테르 부직포인 것이 바람직하고, 상처 박리용 필름으로는 통기성 저밀도 폴리에틸렌계 필름을 사용하는 것이 바람직하다.
부직포에 함침할 소디움롤리아크릴레이트는 가교 결합하지 않은 상태이고, 흡수능이 70∼100 ㎖/g 인 것으로서, 초기에는 겔상태가 아니지만, 수분이 흡수되면 겔상태로 되는데 초기 수분함량은 5 중량% 이하로 충분한 흡수량을 가지는 것이 바람직하다. 이러한 소디움폴리아크릴레이트의 함량은 부직포 전체의 중량을 기준으로 1.0 내지 15%(w/w)가 되도록 하는 것이 바람직하다. 부직포에 함침시킨 소디움폴리아크릴레이트는 혈액이나 오염물 등을 다량, 신속하게 흡수하는데, 이와 같이 수분성분을 흡수하여 겔상태가 되었을 때의 pH 는 상처부위를 자극하지 않도록 하기 위해 6.5-7.5 정도의 상태를 유지해야 한다. 소디움폴리아크릴레이트를 부직포에 함침시키기 위해 살포할 때에는 물이나. 물-에탄올 혼합액등의 용매에 분산시켜 살포한다.
부직포에 함침시킨 티트리오일은 천연상태에서 얻은 오일을 사용하거나 티트리 혼합오일(Melaleuca alternifolia, Melaleuca lineariifolia, Melaleuca leucadendron)을 사용 할 수 있다. 티트리오일의 함량은 부직포 전체의 중량을 기준으로 1.0 내지 15%(w/w)가 되도록 하는 것이 바림직하다. 티트리오일은 가연성의 성질을 갖고 있어 20% 이상을 사용하지 않는 것이 바람직하다. 또한 티트리오일은 가스크로마토그래피로 분석한 결과 다음과 같은 유효성분으로 구성된 혼합물도 사용 할 수 도 있다.
본 발명에 있어서. 패드부를 덮고 있는 상처 박리용 필름은 부직포가 상처 부위에 눌러 붙는 것을 방지해 준다.
마지막으로 패드부와 점착층 위에는 박리지를 적층하여 패드부와 점착층을 오염 등으로부터 보호한다. 박리지로는 실리콘 종이나 폴리프로필렌 등을 사용할 수 있는데, 반창고 사용시에는 이 박리지를 제거한 후 사용한다.
본 발명에 따른 고흡수성 일회용 반창고는 상처부위의 혈액, 진물, 화농 등의 분비물이나 오염물을 다량, 신속하게 흡수하므로, 종래의 일회용 반창고에 비해 훨씬 빠른 흡수효과를 나타내어 상처부위를 청결하게 유지하고 항균효과로 인해 신속한 치료를 유도하게 된다.
본 발명을 이하의 제조예와 실시예에 의하여 더욱 구체적으로 설명한다. 이들 실시예는 본 발명을 예시하기 위하여 제공되는 것으로, 어떠한 형태로든 본 발명의 범위가 이에 의하여 제한되는 것은 아니다.
[실시예 1]
용해조에 소디움폴리아크릴레이트 1 kg, 물과 에탄올(무게 혼합비 1:1) 10 kg을 넣고, 3 시간 교반하여 분산을 확인한 다음 혼합물을 균일액으로 한 후, 레이온사 부직포 제조시 함께 살포하여 함침시켰다. 오븐터널에서 용매를 증발시켜 부직포내에 소디움폴리아크릴레이트 부직포올 사이에 재침전 형성시킨 후 부직포를 감아 올렸다. 부직포에 대한 소디움폴리아크릴레이트 농도가 3.0 %(w/w)가 되게 조절하였다. 다음 용해조에 천연 티트리오일 2 kg을 넣고 균일하게 교반한 후 레이온사 부직포 제조시 살포하여 함침 시킨 후 부직포에 대한 티트리오일 농도가 2.0 %(w/w)가 되게 조절하였다. 소디움폴리아크릴레이트 성분이 함침되어 있는 부직포와 티트리오일 성분이 함침된 부직포를 통기성 저밀도 풀리에틸렌계 필름에 라미네이팅시킨 다음, 절단하여 의료용 점착제가 도포된 통기성 지지체에 절단 부착시켰다. 모든 공정은 통상적으로 사용되는 반창고 제조 기계와 일회용 반창고 제작기계 및 포장기를 사용하여 시행되며, 특별히 명기되지 않은 세부적인 시행 공정은 공지의 방법에 따랐다.
[실시예 2]
부직포내에 소디움폴리아크릴레이트 농도가 6.0 %(w/w)가 되게 조절하고 부직포내에 티트리오일 농도가 4.0 %(w/w)가 되게 조절하는 것을 제외하고는 실시예 1 과 같은 방법으로 일회용 반창고를 제조하였다.
[비교예 1]
티트리오일을 사용하는 공정을 제외하고 실시예 1 에서와 같은 방법으로 일회용 반창고를 제조하였다.
[비교예 2]
티트리오일을 사용하는 공정을 제외하고 실시예 2 에서와 같은 방법으로 일회용 반창고를 제조하였다.
[비교예 3]
대한약전에 수재된 가아제를 사용하여 일회용 반창고를 제조하였다.
[흡수시험]
실시예 1 및 비교예 1 내지 3 에 따른 일회용 반창고의 흡수효과를, 실험실에서 0.9% 생리식염수를 조제하여 다음과 같은 시험법에 의해 평가하였다.
1. 실시예 1 및 비교예 1 내지 3 에 따라 제조된 일회용 반창고를 각각 10 개씩 샘플로 사용하여, 샘플의 번호를 기록하고, 패드부분의 박리필름을 절개하였다.
2. 상기 샘플을 제조 후 실리카겔이 들어있는 데시케이타에서 24 시간 보관 후, 항온 항습실에서 샘플별로 중량을 달고 기록하였다.
3. 0.9% 생리식염수에 1시간 침적 시켰다.
4. 각 샘플을 동시에 식염수에서 꺼낸 후 길이방향을 지면에서 수직으로 세우고 잔류액을 스스로 흘러내리게 한 후, 필름에 남아 있는 잔류액을 탈지면으로 제거하였다.
5. 상기와 같은 방법으로 완료된 샘플을 번호별로 중량을 정밀하게 측정하였다.
6. 5의 측정값에서 2의 측정값을 뺀 후 각각의 평균값과 표준편차를 구하였다.
상기 방법을 사용하여 얻은 결과, 흡수효과[패드 부분에 흡수되는 생리식염수 흡수율(%)]를 표 1 에 나타내었다. 흡수에 대한 시험 중 흡수량(㎎)을 흡수율(%)로 환산한 것은 샘플별 규격이 서로 상이함에 따른 것이며, 값은 아래의 식으로 구하였다.
[항균 효능평가]
항균성 효능 측정방법으로 후광 영역 시험법(halo zone test)을 사용하였는데, 멸균된 페리디쉬(peri dish, 직경 10cm)에 감자 덱스트로스(potato dextrose)의 한천 배지를 제조한 후, 실시예와 비교예에서 사용한 각각의 샘플 위에 아스퍼질러스 니거 (Aspergillus niger, A. niger)포자액을 얇게 도포하였다. 증류수 용액 20 마이크로리터를 지름 1cm 의 천위에 떨어뜨린 후, 자외선하의 클린 벤치에서 1 시간 방치 하였다. 이것을 아스퍼질러스 니거 (Aspergillus niger, A. niger )가 도포된 한천 배지의 중앙에 올려 놓고 30。C 항온 배양기에서 72 시간 배양한 후, 주위에서 아스퍼질러스 니거(Aspergillus niger, A. niger)의 성장여부를 육안으로 관찰하였다.
[표 1] 흡수율과 항균시험 결과
이상에서와 같이 소디움폴리아크릴레이트와 티트리오일이 함침된 부직포를 사용한 본 발명은 수용성 물질에 대한 흡수력이 뛰어나 신체의 상처부위에서 분비물이나 오염물을 다량, 신속하게 흡수하므로, 종래의 일회용 반창고에 비해 훨씬 분비물에 대한 빠른 흡수효과를 나타내어 상처부위를 청결하게 유지하고 항균효과로 인해 상처부위에서 일회용 밴드를 위생적으로 사용할 수 있는 효과가 있는 것을 확인 할 수 있었다.
.
제 1 도는 본 발명에 따른 항균기능을 갖는 고흡수성 일회용 반창고의 단면도를 나타낸 것이다
* 도면의 주요부분에 대한 부호의 설명
1 :PVC 필름, 풀리우레탄계 필름, 신축성레이온면, 폴리에틸렌, 폴리프로필렌, 또는 폴리에스테르의 지지체
2 : 아크릴레이트 공중합체 점착층
3 : 티트리오일 함침층
4 : 소디움풀리아크릴레이트 함침층
5 : 상처 박리용 필름
.
.
Claims (3)
- 지지층위에 코팅된 점착층과 그 위에 형성된 패드부 및 박리지로 이루어진 일회용 반창고에 있어서, 상기 패드부가 소디움폴리아크릴레이트 및 티트리오일을 포함하는 부직포와 그의 표면에 라미네이팅 되어 있는 상처 박리용 필름으로 이루어져 있는 것을 특징으로 하는 일회용 반창고.
- 제 1 항에 있어서, 상기 소디움폴리아크릴레이트는 흡수율이 70∼100 ㎖/g 이고, 수분함량이 5 중량% 이하이며, 부직포에 대한 농도가 1.0 내지 15 %(w/w)인 것을 특징으로 하는 일회용 반창고,
- 제 1 항에 있어서, 상기 티트리오일은 천연의 것이나 다음표와 같은 성분이 포함된 것을 특징으로 하고 부직포에 대한 농도가 1.0 내지 15 %(w/w)인 것을 특징으로 하는 일회용 반창고.