Abstract

PURPOSE: A structure for an ornamental potted-plant is provided to manufacture a very fine structure. CONSTITUTION: A manufacturing method for a structure comprises:boiling a molding(6) in a temperature of 100°C or over for 1-5 hours for sloughing; drying the molding in 30-50°C for 20-50 hours in a drying chamber; completing an antiseptic treatment process of clothing an antiseptic; preparing a compound by mixing sand and resin for a ratio of 1:1 and adding a resin hardening agent; and settling the molding by using the compound.

Description

Structure for ornamental bonsai, etc. and construction method thereof {Construction for ornamental plant etc and its manufacturing method}

본 발명은 관상용 분재 등을 위한 구조물의 제조방법 및 그에 의한 구조물에 관한 것이다.The present invention relates to a method for producing a structure for ornamental bonsai, and the like thereby.

본 발명에 사용하는 조형물 구성의 한 예로는 다래나무를 사용하는데, 이 다래나무는 탈피하였을 경우, 그 나무의 표면 무늬결이 길이 방향으로 긴 꼬임이 휘감아 생기는 매우 미감이 우수한 형상의 무늬를 나타난다. 또한 다래나무 자체는 특히 상부로 갈수록 꼬임이 심하여 더욱 역동적인 형상을 나타내는 자연미가 매우 뛰어난 형상을 하고 있다.As an example of the configuration of the sculpture used in the present invention, a stalk is used. When the stalk is peeled off, the surface pattern of the wood shows a very aesthetically pleasing shape in which a long twist is formed in the longitudinal direction. In addition, the wood itself itself is very twisted toward the upper part of the natural beauty of the more dynamic shape showing a more dynamic shape.

이러한 다래나무 소재를 이용한 관상용 분재 등의 구조물에 관한 것으로는, 본 출원인에 의하여 선출원한 실용신안등록출원 번호 제 99 - 10184 호의 것이 있다.Regarding a structure such as an ornamental bonsai using such a material of a taupe, there is a utility model registration application No. 99-10184 filed by the present applicant.

본 발명은 상기한 본 출원인에 의하여 선출원한 것을 더욱 자연미가 나도록 개선한 것으로, 특히 상기한 다래나무의 형상을 이용하여 관상용 분재 등과 같은 구조물을 매우 미려하게 제조할 수 있는 방법을 제공한 것으로 이하, 첨부한 도면과 함께 본 발명을 상세히 설명한다.The present invention has been improved by the applicant of the present application to improve the natural beauty, in particular, by using the shape of the above-mentioned wood of the above to provide a method that can be very beautifully manufactured structures such as ornamental bonsai, The present invention will be described in detail with the accompanying drawings.

도 1a - 도 1c 는 본 발명에 따른 조형물(6)의 구조 예를 나타내는 도면1a-1c show a structural example of a sculpture 6 according to the invention

도 2 는 본 발명의 실시예를 보여 주는 요부 단면도2 is a cross-sectional view of main parts showing an embodiment of the present invention;

도 3 은 본 발명에 따른 조형물의 한 예를 도시한 사시도3 is a perspective view showing an example of a sculpture according to the present invention;

도 4a 및 도 4b 는 본 발명에 의하여 제작된 제품의 예를 보여 주는 것으로 수반에 아직 설치하지 않은 상태를 보여 주는 실물 사진이고, 도 4c 는 수반에 설치한 상태를 보여 주는 실물 사진이다.4a and 4b is a real picture showing a state of the product produced by the present invention showing the state not yet installed in the accompanying, Figure 4c is a real picture showing a state installed in the accompanying.

본 발명에 따른 관상용 분재 등을 위한 구조물의 제조방법은, 조형물(6)을 100 도 또는 그 이상의 온도에서 약 1 시간 내지 5 시간 동안 삶은 후 탈피하는 공정과, 탈피한 조형물을 건조실에서 약 30 - 50 도의 온도에서 약 20 - 50 시간 정도 건조시키는 공정과, 그리고 이를 방부제를 피복하는 방부처리 공정을 완료하여 조형물(6)을 준비하는 단계와; 모래와 수지를 약 1 : 1 비율로 혼합하고 또한 수지 경화제를 첨가하여 준비한 혼합물을 소정 형상의 틀에 부어 수지가 굳으면서 상기한 조형물(6)을 안착시키는 단계로 이루어지는 것을 특징으로 한다.Method for producing a structure for ornamental bonsai, etc. according to the present invention, the process of boiling the sculpture (6) at a temperature of 100 degrees or more for about 1 hour to 5 hours, and stripping the stripped sculpture in a drying chamber. Preparing a sculpture 6 by completing a drying process at a temperature of 50 degrees for about 20-50 hours, and a preservation process for coating the preservative; Sand and resin are mixed at a ratio of about 1: 1, and the mixture prepared by adding a resin curing agent is poured into a mold of a predetermined shape, and the resin is hardened, and the above-mentioned molding 6 is seated.

또한 그 구조는, 수지와 모래의 혼합물로 이루어지며 측단면상 사다리꼴 형상을 하는 좌대((1)와, 그리고 상기 좌대(1) 상에 고정 설치되는 다래나무로 이루어지는 조형물(6)로 구성되는 것을 특징으로 한다.In addition, the structure is characterized by consisting of a base (1) consisting of a mixture of resin and sand and having a trapezoidal shape on the side cross-section, and a sculpture (6) made of a stalk tree fixed on the base (1). It is done.

이하, 본 발명의 다른 특징 및 장점을 더욱 상세히 예를 들어가며 설명한다.Hereinafter, other features and advantages of the present invention will be described in more detail with examples.

먼저 본 발명에서는 예를 들어, 다래나무를 소정의 길이로 잘라 섭씨 100 도 또는 그 이상의 온도에서 삶는다. 삶는 시간은 약 1 시간 내지 5 시간 바람직하기로는 약 3 시간 정도 삶는다.First, in the present invention, for example, cut persimmon tree to a predetermined length and boil at a temperature of 100 degrees Celsius or more. Boil time is about 1 to 5 hours, preferably about 3 hours.

다래나무를 삶는 이유는 만약 삶지 않을 경우, 시간이 경과하면 나무의 건조에 따라 또는 경시적으로 변색되고 곰팽이가 발생하며 나무에 남아 있는 미생물등에 의하여 부식,부패되어 변형이 매우 심하게 된다.If you do not boil, if you do not boil over time, the color of the wood is dried or deteriorated over time, the mold occurs and the microorganisms remaining in the tree, such as decay, deterioration is very severe.

다래나무를 삶은 후엔 탈피한다. 그러면 탈피된 다래나무는 다래나무의 길이 방향 즉 세로로 매우 아름다운 줄무늬 꼬임 형상이 표면에 드러나게 된다.After boiling the perilla tree, peel off. Then, the stripped stalks will be exposed to the surface in the longitudinal direction of the stalks, that is, a very beautiful striped twisted shape.

그리고 이것을 건조실에서 약 30 - 50 도, 즉 한 예를 들면, 약 40 도 정도의 온도에서 약 20 - 50 시간, 즉 예를 들어 30 - 40 시간 정도 건조시키는 것이 적당하다.And it is suitable to dry it in a drying chamber at a temperature of about 30-50 degrees, i.e. about 40 degrees, for example about 20-50 hours, i.e. 30-40 hours.

건조가 완료되면 이를 방부제로 방부 처리한다. 방부제는 칠하거나 다른 방법으로 도포할 수도 있다. 또는 침지시킬 수도 있다.When drying is complete, it is preservative treated with a preservative. Preservatives may be applied or otherwise applied. Or dipping.

이와 같이 준비된 다래나무는 이것을 소정의 형상으로 굽혀 모양을 갖춘다. 예를 들어 둥글게 말은 형상으로 만든다. 그러나 굳이 변형시키지 않고 그대로 사용하여도 된다.Thus prepared wood is bent in a predetermined shape to have a shape. For example, round horses are made into shapes. However, it may be used as it is without deforming.

도 1a 의 형상과 같이 굽혀 좌대(1)에 고정시킬 경우, 상부가 벌어져 변형이 된다 하여도 크게 벌어지지 않는다. 또 도 2b 와 같이 똘똘 말은 형상으로 하여 원형상의 일부와 한쪽 단부가 좌대(1)에 심어져 고정되게 만들 수도 있다.When it is bent like the shape of FIG. 1A and is fixed to the base 1, even if an upper part opens and deforms, it does not open large. In addition, as shown in Fig. 2B, the horse may be made into a shape so that a part of a circular shape and one end thereof are planted in the pedestal 1 to be fixed.

또한 도 1c 와 같이 양단이 아치형으로 좌재(1)에 심어 고정되게 구성하여 변형이 전혀 없게 할 수도 있으며 또한 도 1c 와 같이 자연석(2)이나 조개(3) 등을 함께 고정시켜 둘 수도 있다.Also, as shown in FIG. 1C, both ends may be configured to be fixed by planting in the seat 1 in an arc shape so that there may be no deformation at all, and also natural stone 2 or shell 3 may be fixed together as shown in FIG.

한편 좌대(1)는 도 2 의 형상에서 보듯이 사다리꼴로 만드는 것이 바람직하다. 반대로 뒤집은 형상 즉, 상부가 크고 하부가 좁은 화분 형상으로 하면 불안정하며 여러가지로 불편하다. 즉 도 2 에 예시한 바와 같이 좌대(1)의 형상 보다 큰 수반(4)이라면 수반의 형상에 무관하게 이 좌대(1)를 수반(4)에 놓을 수 있으며, 매우 안정적으로 설치될 수 있다. 또한 이 좌대(1)와 수반(4) 사이에 모래 (5) 등을 깔아 두면 더욱 자연미가 살아나며 여기에 물을 뿌려두면 실내 가습 역할도 가능한 것이다.On the other hand, it is preferable to make the base 1 trapezoidal as shown in the shape of FIG. On the contrary, if the shape is inverted, that is, the upper part is large and the bottom part is instable, it is unstable and variously inconvenient. That is, as illustrated in FIG. 2, if the accommodating body 4 is larger than the shape of the accommodating body 1, the accommodating body 1 may be placed on the accommodating body 4 regardless of the shape of the accommodating body. In addition, if the sand (5) is laid between the base (1) and the head (4), natural beauty will be more lively, and if it is sprayed with water, it is also possible to act as an indoor humidification.

좌대(1)는 특히 바람직한 재질로는 모래를 사용하며 석분(돌가루) 등도 사용할 수 있다. 이의 바람직한 한 제조 방법은 다음과 같다.The pedestal 1 uses sand as a particularly preferable material, and may also use stone powder (stone) and the like. One preferred method for its preparation is as follows.

모래와 수지를 약 1 : 1 비율로 혼합한다. 모래가 수지 보다 많아도 된다. 모래 대신 석분을 사용할수도 있으나 모래가 입자가 더 크기 때문에 미관상 더 바람직하다. 수지엔 경화제를 첨가한다. 경화제의 한 예로는 불포화폴리에스털 수지를 사용한다. 그 수지 경화제의 성분은 스틸렌 40 - 55 중량%, 폴리에스털 45 - 60 중량% 그리고 키실렌 5 - 10 중량% 가 혼합된 것을 사용한다.Sand and resin are mixed at a ratio of about 1: 1. There may be more sand than resin. Stone powder may be used instead of sand, but sand is more desirable because of the larger particles. A curing agent is added to the resin. One example of the curing agent is an unsaturated polyester resin. The resin curing agent is a mixture of 40 to 55% by weight of styrene, 45 to 60% by weight of polyester and 5 to 10% by weight of xylene.

모래와 수지를 혼합하여 이를 틀에 부어서 제조하는 방법과 모래 또는 수지를 먼저 깔고 그 위에 모래 또는 수지를 적층하는 방법으로도 제조 가능하다. 좌대(1)는 도 2 에 예시한 바와 같이 컵을 엎어 놓은 형상의 속이 빈 형상으로 하는 것이 가볍고 재료도 덜 들어가므로 바람직하다. 이 좌대의 형상은 미리 만들어진 틀에서 제작된다.It is also possible to produce by mixing sand and resin and pouring it into a mold and by laying sand or resin first and laminating sand or resin thereon. As illustrated in FIG. 2, the seat 1 is preferably hollow and has a cup-like shape, and is preferably light and contains less material. The shape of this seat is made in a pre-made frame.

좌대(1)의 가장 상층엔 도 2 에 예시한 바와 같이 모래층(16)이 오도록 하는 것이 가장 자연미가 살아 난다.As illustrated in FIG. 2, the top layer of the pedestal 1 has a sand layer 16 that is most natural.

좌대(1)의 형상을 갖춘 틀에서 만들 경우, 모래와 수지의 혼합물을 부은 후, 여기에 상기한 조형물(6) 즉 예를 들어 다래나무로 이루어지는 조형물(6)을 안착하여 수지가 굳으면서 조형물이 고정되게 한다. 이때 조형물 외에 도 1c 에 예시한 바와 같이, 자연석(2)이나 조개(3) 등도 함께 좌대(1) 형상의 상층에 고정시켜 둘 수 있다.In the case of making the frame having the shape of the pedestal 1, after pouring a mixture of sand and resin, the above-mentioned moldings 6, that is, the moldings 6 made of, for example, wood, are placed thereon while the resin is hardened. To be fixed. At this time, in addition to the sculpture, as shown in Figure 1c, natural stone (2), shells (3) and the like can also be fixed to the upper layer of the pedestal (1) shape.

이런 구조물이 완성되면 예를 들어 착생란(7)을 접착제를 이용하여 살짝 다래나무(6)에 고정시켜 둔다. 그리고 수시로 이 착생란(7)에 수분을 분무하면 착생란(7)의 뿌리가 자라면서 이 다래나무에 고착하여 성장한다.When such a structure is completed, for example, the embryonic eggs (7) are slightly fixed to the rattan (6) using an adhesive. And if you spray water on the embryonic eggs 7 from time to time, the roots of the embryonic eggs 7 grow and adhere to the stye tree.

사진 실물에서 보듯이 매우 아름다운 자연미를 나타내고 있다.As you can see in the picture, it shows very beautiful natural beauty.

본 발명에서는 주요 구성 조형물을 다래나무로 특히 한정하여 설명하였지만, 본 발명은 이에 한정하는 것이 아니라 다른 유사한 나무 등의 자연물 또는 조형물을 이용하여 본 발명의 제조방법과 동일 또는 유사한 방법으로 사용할 경우에도 본 발명의 기술사상의 범위에 속한다고 보아야 함은 당연한 것이다.In the present invention, the main components of the present invention have been specifically limited to the above-mentioned wood, but the present invention is not limited thereto, and the present invention is also used when the same or similar method is used as the manufacturing method of the present invention using other similar trees or natural objects. It should be considered that it belongs to the technical idea of the invention.

또한 본 발명의 설명에서는 사용 식물을 착생란을 특히 한정하여 예로써, 설명하였으나 이에 한정되는 것을 결코 아니다. 다른 어떠한 식물 또는 식물이 아닌 조화 등으로도 본발명의 구조와 유사한 형상으로 만들 수 있음은 물론이다. 이와 같은 구성 모두 본 발명의 권리범위에 속하는 것으로 해석되어야 함은 당연하다.In addition, in the description of the present invention, the plant used was specifically described as an example by limiting the embryonated eggs, but the present invention is not limited thereto. Of course, any other plant or non-plant harmony can be made into a shape similar to the structure of the present invention. Naturally, such a configuration should be interpreted as falling within the scope of the present invention.

예를 들어, 다래나무 또는 다른 나무 또는 다른 구조물에 구멍을 뚫고, 여기에 조화 등을 고정시킬 수도 있지만 이러한 것들 역시 본 발명의 범위에 속하는 것으로 당연히 해석되어야 할 것이다. 즉 본원 발명의 권리범위는 특허 청구범위에 한정 해석하는 것이 아니라 상술한 본원 발명의 기술 사상에 속하는 것 모두 본원 발명의 권리범위에 속하는 것으로 해석하여야 할 것이다.For example, a hole may be drilled in a stalk or other tree or other structure, and the harmony may be fixed thereto, but these should also be naturally interpreted as falling within the scope of the present invention. That is, the scope of the present invention should not be construed as limited to the claims, but all belonging to the technical spirit of the present invention described above should be interpreted as belonging to the scope of the present invention.

이상과 같은 본 발명에 의하면, 예를 들어 도 3 및 도 4a, 도 4b, 도 4c 에 예시한 바와 같이, 매우 뛰어난 관상용 분재 구조물을 만들어 낼 수 있는 장점이 있다.According to the present invention as described above, as illustrated in Figs. 3 and 4a, 4b, 4c, for example, there is an advantage that can produce a very excellent ornamental bonsai structure.

또한 좌대(1)와 수반(4) 사이에 모래( 5) 또는 자갈이나 흙 등을 깔면 더욱 자연미를 한껏 뽐낼 수 있는 실내장식용 분재등의 구조물이 이루어 질수 있는 장점이 있다.In addition, when the sand (5) or gravel or soil is laid between the base (1) and the head (4), there is an advantage that a structure, such as bonsai for interior decoration that can exude more natural beauty.

Claims

In the method of manufacturing a structure for ornamental bonsai,

Boiling the wood sculpture (6) at a temperature of 100 degrees or more for about 1 to 5 hours, and then stripping it, and drying the stripped sculpture at a temperature of about 30 to 50 degrees in a drying room for about 20 to 50 hours. And to prepare a sculpture (6) by completing the antiseptic process to coat it with a preservative;

A mixture of sand and resin in a ratio of about 1: 1, and a mixture prepared by adding a resin curing agent is poured into a mold of a predetermined shape, and the resin solidifies, thereby seating the above-described molded article 6, etc. Method of manufacturing the structure for

The method according to claim 1, further comprising the step of further restoring other sculptures such as natural stones and shells when the sculptures 6 are seated, and further comprising attaching the complex eggs 7 with an adhesive after the sculptures are finished. Method of manufacturing a structure for ornamental bonsai, etc.

The method of manufacturing a structure for an ornamental bonsai, according to claim 1 or 2, characterized in that the above-mentioned sculpture (6) is a cork tree.

In the structure for ornamental bonsai, etc.,

A seat consisting of a mixture of resin and sand and having a trapezoidal shape in side section ((1), and

Structure for ornamental bonsai, etc., characterized in that consisting of a sculpture (6) consisting of the wood is fixed to the pedestal (1).