KR20030089620A - Manufacturing method of yellow soil a flowerpot - Google Patents

Abstract

PURPOSE: A method of producing a loess flowerpot by mixing germanium, charcoal and loess as a main material is provided. Thus obtained flowerpot has a good appearance and enhanced stiffness while preventing the growth of moss and improving the growth of plants. CONSTITUTION: A mixture of 0.5 to 1.5% by weight of germanium, 1.5 to 2.5% by weight of jade, 0.5 to 1.5% by weight of charcoal and 94.5 to 97.5% by weight of loess is agitated with water and formed into a flowerpot having various shapes. Then, the molded product is dried for about 24hr in the shade, coated with a lacquer and dried for about 30min in the shade. The dried product also is coated with a mixture of lacquer, urethane and a curing agent and dried for about 1hr in the shade.

Description

Manufacturing method of ocher pollen {MANUFACTURING METHOD OF YELLOW SOIL A FLOWERPOT}

The present invention relates to a manufacturing method of ocher pots. Emission of germanium, jade, charcoal and ocher mixed in the mixing process by manufacturing ocher pots by mixing, molding, primary drying, coating lamination, secondary drying, surface treatment and tertiary drying The present invention relates to a method for producing ocher pots, which can improve the growth state of plants planted by ocher pots by far-infrared rays, prevent moss caught and obtain clean and beautiful pots, and obtain more potted pots.

The conventional method for producing ocher pots is molded by the shape of the pot using one ocher material and dried to be shipped.

Since the pot was manufactured using only one ocher material as described above, there was a problem that the strength was very weak and easily broken.

In addition, since the growth of the moss on the surface of the conventional ocher potted plants well, there was also an uncomfortable and cumbersome problem that the moss of the potted plants must be removed periodically.

The purpose of the present invention for solving and solving these conventional problems,

It is possible to improve the growth state of plants planted by ocher pots and to prevent moss pinching, to obtain clean and beautiful pots, and to provide a more robust pot.

In order to achieve the above object, the present invention,

Mixing process of mixing germanium, jade, charcoal, ocher, molding process to form into a potted shape, primary drying process, paint lamination process of laminating paint (lacquer), secondary drying process, lacquer, urethane, hardener The manufacture of ocher pots by the surface treatment process, tertiary drying process to paint the surface of the pot can achieve the object of the present invention.

1 is a flute chart showing a manufacturing method of the loess pollen of the present invention

The manufacturing method of the present invention will be described in detail by the accompanying drawings for each process.

A mixing process of adding an appropriate amount of water to 0.5-1.5% by weight of germanium, 1.5-2.5% by weight of jade, 0.5-1.5% by weight of charcoal, and 94.5-97.5% by weight of ocher, and mixing in a stirrer;

A molding process of molding the mixture obtained in the mixing process into flower pots of various shapes;

A primary drying process of drying the molded product obtained in the molding process in a shaded place at room temperature for about 24 hours,

A paint lamination process of laminating paint (lacquer) on the surface of the molded article dried in the first drying process,

A secondary drying process of drying the paint in the paint lamination process in a shady place at room temperature for about 30 minutes;

A surface treatment process of coating the surface of the molded article obtained in the second drying process by coating a paint mixture mixed with lacca, urethane, and hardener in a ratio of about 4: 4: 2;

After the surface treatment process, the molded article is dried in a shaded place at room temperature for about 1 hour to obtain a completed ocher pollen to obtain a tertiary drying process.

The operation of the present invention thus described is as follows.

Firstly, in the mixing process, 0.5-1.5% by weight of germanium, 1.5-2.5% by weight of jade, 0.5-1.5% by weight of charcoal, and 94.5-97.5% by weight of ocher are put in an appropriate amount of water to make a dough.

Then, the mixture obtained in the mixing process, that is, using the dough is molded in the molding process of the flower pots of various shapes.

In addition, the molded article obtained in the molding process is dried for about 24 hours in the shade of room temperature by the primary drying process.

In addition, the surface of the molded article dried in the first drying process is laminated with a paint (lacquer) by the paint lamination process.

In addition, the paint in the paint lamination process is dried for about 30 minutes in the shade of room temperature by the secondary drying process.

In addition, the molded article obtained in the secondary drying process is subjected to a surface treatment by coating a paint mixture of lacquer, urethane, and hardener in a ratio of about 4: 4: 2 to the surface of the molded article by surface treatment.

In addition, the molded product after the surface treatment is dried for about 1 hour in a shaded place at room temperature by a tertiary drying process to obtain a completed ocher pots.

Thus, the present invention is a mixing process of mixing germanium, jade, charcoal, ocher, molding process to form into a potted shape, primary drying process, paint lamination process of laminating paint (lacquer), secondary drying process, lacquer, The ocher pollen is manufactured by mixing the urethane and hardener to the surface of the flowerpot and tertiary drying process to improve the growth of the plants planted by the ocher flowerpot. Pollen can be obtained and has a useful effect of obtaining a more robust pollen.

Claims (1)

A mixing process of adding an appropriate amount of water to 0.5-1.5% by weight of germanium, 1.5-2.5% by weight of jade, 0.5-1.5% by weight of charcoal, and 94.5-97.5% by weight of ocher, and mixing in a stirrer; A molding process of molding the mixture obtained in the mixing process into flower pots of various shapes; A primary drying process of drying the molded product obtained in the molding process in a shaded place at room temperature for about 24 hours, A paint lamination process of laminating paint (lacquer) onto the surface of the molded article dried in the first drying process, A secondary drying process of drying the paint in the paint lamination process in a shady place at room temperature for about 30 minutes; A surface treatment process of coating the surface of the molded article obtained in the second drying process by coating a paint mixture mixed with lacca, urethane, and hardener in a ratio of about 4: 4: 2; The method for producing ocher pots, characterized in that consisting of a tertiary drying process to obtain the finished ocher pots by drying the molded article after the surface treatment in a shade of room temperature for about 1 hour.